WO2024070577A1 - 造粒体およびその製造方法 - Google Patents

造粒体およびその製造方法 Download PDF

Info

Publication number
WO2024070577A1
WO2024070577A1 PCT/JP2023/032780 JP2023032780W WO2024070577A1 WO 2024070577 A1 WO2024070577 A1 WO 2024070577A1 JP 2023032780 W JP2023032780 W JP 2023032780W WO 2024070577 A1 WO2024070577 A1 WO 2024070577A1
Authority
WO
WIPO (PCT)
Prior art keywords
aliphatic polyester
powder
hydroxybutyrate
granules
poly
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2023/032780
Other languages
English (en)
French (fr)
Inventor
竜輝 安成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kaneka Corp
Original Assignee
Kaneka Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kaneka Corp filed Critical Kaneka Corp
Priority to JP2024549971A priority Critical patent/JPWO2024070577A1/ja
Priority to CN202380066506.XA priority patent/CN119948084A/zh
Publication of WO2024070577A1 publication Critical patent/WO2024070577A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

嵩密度が高く、流動性が高い脂肪族ポリエステルを含む造粒体を提供することを課題とする。脂肪族ポリエステルを含み、かつ嵩密度が０．３０ｇ／ｃｍ３～０．５０ｇ／ｃｍ３の粉体を圧縮造粒する工程を含む脂肪族ポリエステルを含む造粒体の製造方法により、前記課題を解決する。

Description

造粒体およびその製造方法
　本発明は、造粒体およびその製造方法に関する。
　ポリヒドロキシアルカン酸（ＰＨＡ）等の生分解性樹脂は生分解性を有することから、種々の用途への利用が進んでいる。例えば、ＰＨＡはその利用に際して、乾燥させた粉体等として輸送や加工に供される。従来、ＰＨＡ懸濁液を噴霧乾燥することによりＰＨＡ粉体を製造する方法が開発されている（例えば、特許文献１）。
　ところで、少なくとも１つのポリエステル、ポリエステル分解活性を有する生物学的エンティティ及び少なくとも１つの制酸フィラーを含むプラスチック組成物であって、生物学的エンティティがプラスチック組成物の総重量を基準として１１％（重量換算）未満を占める、プラスチック組成物を調製するためのプロセスであって、混合工程として、ポリエステルが部分的若しくは全体的に溶融した状態にある温度、かつ／又は、押出機、好ましくは二軸スクリュー押出機、より好ましくは共回転式二軸スクリュー押出機中で実施する技術が知られている（例えば、特許文献２）。
国際公開第２０１８／０７０４９２号明細書 特開２０２１－１１９２４０号公報
　しかし、特許文献１に記載の噴霧乾燥によって得られたＰＨＡ粉体は嵩密度が低く、流動性が悪くなる場合があるため、改善の余地があった。
　また、特許文献２に記載の技術は押出機を用いて混合する技術であるため、脂肪族ポリエステルの分子量が低下する等の問題があった。
　本発明の一態様は、嵩密度が高く、流動性が高い脂肪族ポリエステルを含む造粒体を実現することを目的とする。
　本発明者らは、前記課題を解決すべく鋭意検討を行った。その結果、脂肪族ポリエステルを含み、かつ嵩密度が特定の範囲である粉体を圧縮造粒する工程を含むことにより、嵩密度および流動性が高い脂肪族ポリエステルを製造できることを見出し、本発明を完成するに至った。
　したがって、本発明の一態様は、嵩密度が０．３０ｇ／ｃｍ３～０．５０ｇ／ｃｍ３である、脂肪族ポリエステルを含む粉体を圧縮造粒する工程を含む、脂肪族ポリエステルを含む造粒体の製造方法（以下、「本発明の一実施形態に係る脂肪族ポリエステルを含む造粒体の製造方法」を、「本製造方法」と称する。）である。
　また、本発明の別の一態様は、嵩密度が０．５０ｇ／ｃｍ３超、０．７０ｇ／ｃｍ３以下であり、かつ脂肪族ポリエステルの含有量が９０重量％以上である、造粒体（以下、「本造粒体」と称する。）である。
　本発明の一態様によれば、嵩密度が高く、流動性が高い脂肪族ポリエステルを含む造粒体を実現できる。
　本発明の実施の一形態について、以下に詳細に説明する。なお、本明細書において特記しない限り、数値範囲を表す「Ａ～Ｂ」は、「Ａ以上、Ｂ以下」を意味する。また、本明細書中に記載された文献の全てが、本明細書中において参考文献として援用される。
　〔１．本発明の概要〕
　特許文献１に記載されているような噴霧乾燥等により得られたＰＨＡ粉体は、その後コンパウンド工程等によりペレット化される。ＰＨＡ粉体をペレット化することにより、成型機に供給する場合のハンドリング性が向上し、見かけの嵩密度が上昇することにより輸送性が向上する。しかしながら、本発明者らは特許文献１に記載されている従来の方法では、得られるＰＨＡ粉体の嵩密度が低いため、ＰＨＡ粉体の流動性が低くなり、前記コンパウンド工程等における生産効率が低下するという問題が生じることを見出した。また、ＰＨＡ粉体の流動性が低下すると、粉体の輸送性が悪くなるという問題も生じる。
　また、本発明者らは特許文献２に記載の押出機を使用する技術では、流動性の悪い脂肪族ポリエステルを使用した場合、押出機内へ入りにくく、生産速度が低下するという問題が生じることを見出した。さらに、生産速度を上げるために押出機のスクリュー回転数を増加させると温度が過剰に上昇するため、脂肪族ポリエステルが熱分解され、分子量が低下するという問題が生じることも見出した。特に、上述したＰＨＡは融点と分解温度が近いため、流動性を上げるために加熱すると分子量が低下しやすい。
　そこで、本発明者らは上記問題を解決するために鋭意検討を行った結果、以下の知見を得ることに成功した。
・脂肪族ポリエステルを含む嵩密度が低い粉体を圧縮造粒することにより、嵩密度が高く、流動性に優れる造粒体を得られること。
・本製造方法により得られる造粒体は、嵩密度が高いため、輸送性にも優れること。
・本製造方法によれば、バインダーを使用することなく、脂肪族ポリエステルを含む造粒体を製造できること。
・本製造方法によれば、圧縮造粒時に可塑剤等を使用する必要がないため、不純物が少なくなり、脂肪族ポリエステルの含有量が高い造粒体が得られること。
　特に、嵩密度が低い脂肪族ポリエステルを含む粉体を圧縮造粒して、嵩密度の高い造粒体を得るとの技術思想はこれまでになく、本発明は極めて優れている。本製造方法により得られる本造粒体は、嵩密度が高く、流動性にも優れるため、脂肪族ポリエステルを含む造粒体原料として、有利に使用できる。
　本明細書において、「粉体」とはメジアン径が０．５ｍｍ未満のものを意図し、「造粒体」とは粉体を造粒してなる粒子であって、特に、メジアン径が０．５ｍｍ～１０．０ｍｍのものを意図する。
　上述したような構成によれば、効率的にプラスチック製品を製造でき、これにより、例えば、目標１２「持続可能な消費生産形態を確保する」や目標１４「持続可能な開発のために、海・海洋資源を保全し、持続可能な形で利用する」等の持続可能な開発目標（ＳＤＧｓ）の達成に貢献できる。以下、本製造方法の構成について詳説する。
　〔２．脂肪族ポリエステル造粒体の製造方法〕
　本製造方法は、嵩密度が０．３０ｇ／ｃｍ３～０．５０ｇ／ｃｍ３である、脂肪族ポリエステルを含む粉体を圧縮造粒する工程を含む。本製造方法は、前記構成を有することにより、嵩密度が高く、流動性に優れる脂肪族ポリエステル造粒体を得ることができる。
　（２－１．脂肪族ポリエステルを含む粉体）
　本製造方法における脂肪族ポリエステルを含む粉体は、嵩密度が０．３０ｇ／ｃｍ３～０．５０ｇ／ｃｍ３である。前記粉体の嵩密度は、好ましくは０．３２ｇ／ｃｍ３～０．４８ｇ／ｃｍ３であり、より好ましくは０．３４ｇ／ｃｍ３～０．４６ｇ／ｃｍ３、さらに好ましくは０．３６ｇ／ｃｍ３～０．４４ｇ／ｃｍ３である。本製造方法において、嵩密度が前記範囲の脂肪族ポリエステルを含む粉体を用いることにより、嵩密度が高く、流動性に優れる脂肪族ポリエステル造粒体を得ることができる。本明細書において、前記嵩密度は、後述する実施例に記載の方法により測定される値である。
　前記粉体は、脂肪族ポリエステルを含む。脂肪族ポリエステルとしては、特に限定されないが、例えば、ポリ（３－ヒドロキシアルカノエート）（以下、「Ｐ３ＨＡ」とも称する。）、ポリ乳酸（ＰＬＡ）、ポリブチレンサクシネート（ＰＢＳ）、ポリブチレンサクシネートアジペート、ポリブチレンアジペートテレフタレート、ポリブチレンサクシネートテレフタレート、ポリカプロラクトン等が挙げられる。中でも、脂肪族ポリエステルは、工業的な生産性の観点から、Ｐ３ＨＡが好ましい。前記粉体は、前記脂肪族ポリエステルを１種含んでもよいし、２種以上含んでもよい。
　前記粉体に含まれる脂肪族ポリエステルは、当該脂肪族ポリエステル１００重量％中、Ｐ３ＨＡを５０重量％以上含むことが好ましく、６０重量％以上含むことがより好ましく、７０重量％以上含むことがより好ましく、８０重量％以上含むことがより好ましく、９０重量％以上含むことがさらに好ましく、９５重量％以上含むことがよりさらに好ましい。前記粉体に含まれる脂肪族ポリエステルは、当該脂肪族ポリエステル１００重量％中、Ｐ３ＨＡを１００重量％含むことが特に好ましい。
　前記粉体のメジアン径は、６０～２００μｍが好ましく、８０～１８０μｍがより好ましく、１００～１７０μｍがさらに好ましい。前記粉体の黄色度（ＹＩ）は、４０以下が好ましく、３５以下がより好ましく、３０以下がさらに好ましい。なお、ＹＩは低いほど黄色度が低いことになり、下限値は特に限定されないが、例えば、５以上であればよい。前記粉体の熱安定性は、７０～１００％が好ましく、７５～９５％がより好ましく、７７～８５％がさらに好ましい。これらのメジアン径、ＹＩ、熱安定性は、後述する実施例に記載の方法により測定することができる。
　本製造方法における脂肪族ポリエステルを含む粉体は、脂肪族ポリエステルを好ましくは９０重量％以上含み、より好ましくは９５重量％以上、さらに好ましくは９７重量％以上、最も好ましくは９９重量％以上含む。前記粉体における脂肪族ポリエステルの含有量の上限は特に限定されず、例えば、１００重量％以下であり、１００重量％であってもよい。
　前記粉体に含まれる脂肪族ポリエステルの融点は、好ましくは５０～２００℃でありより、好ましくは６０～１８０℃、さらに好ましくは７０～１７０℃であり、特に好ましくは８０～１６０℃である。脂肪族ポリエステルの融点が上述した範囲であれば、圧縮造粒時に加熱することなく粉体を融着させることが可能となるため、後述するバインダーの使用量を低減することができる。
　本発明の一実施形態において、脂肪族ポリエステルを含む粉体は、バインダーを含まない。本製造方法では、脂肪族ポリエステルを含む粉体を、圧縮造粒する工程を含むことにより、バインダーを使用することなく、脂肪族ポリエステルを含む造粒体を製造できる。本明細書において、「バインダー」とは、可塑剤、セルロース、水等の脂肪族ポリエステル同士を接着させる、またはその接着を促進する物質を意図する。また、本明細書において、脂肪族ポリエステルを含む粉体が、「バインダーを含まない」とは、脂肪族ポリエステルを含む粉体が、バインダーを全く含まないことの他、バインダーを実質的に含まない場合も意図する。脂肪族ポリエステルを含む粉体が、「バインダーを実質的に含まない」とは、バインダーを、脂肪族ポリエステルを含む粉体１００重量％に対して、例えば、１重量％以下含み、より好ましくは０．１重量％以下含み、さらに好ましくは０．０１重量％以下含むことを意図する。バインダーの含有量が少ない程、製造コストを低減することができる。
　以下、脂肪族ポリエステルの一例として、ポリ（３－ヒドロキシアルカノエート）を挙げて、脂肪族ポリエステルを含む粉末の製造方法を含めて、本製造方法の一態様について詳細に説明する。
　＜Ｐ３ＨＡ＞
　本製造方法におけるＰ３ＨＡは、３－ヒドロキシアルカノエート単位を構成単位（モノマー単位）として有する重合体である。本明細書において、「３－ヒドロキシアルカノエート」を「３ＨＡ」と称する場合もある。Ｐ３ＨＡとしては、具体的には、下記一般式（１）で示される繰り返し単位を含む重合体が好ましい：
　［－ＣＨＲ－ＣＨ２－ＣＯ－Ｏ－］・・・（１）。
　一般式（１）中、ＲはＣｎＨ２ｎ＋１で表されるアルキル基を示し、ｎは１～１５の整数を示す。Ｒとしては、例えば、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、ｔ－ブチル基、ペンチル基、ヘキシル基等の直鎖または分岐鎖状のアルキル基が挙げられる。ｎとしては、１～１０が好ましく、１～８がより好ましい。
　より詳しくは、ＰＨＡとしては、例えば、ポリ（３－ヒドロキシブチレート）（Ｐ３ＨＢ）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシプロピオネート）（Ｐ３ＨＢ３ＨＰ）ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシヘキサノエート）（Ｐ３ＨＢ３ＨＨ）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシバリレート）（Ｐ３ＨＢ３ＨＶ）、ポリ（３－ヒドロキシブチレート－コ－４－ヒドロキシブチレート）（Ｐ３ＨＢ４ＨＢ）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシオクタノエート）（Ｐ３ＨＢ３ＨＯ）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシオクタデカノエート）（Ｐ３ＨＢ３ＨＯＤ）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシデカノエート）（Ｐ３ＨＢ３ＨＤ）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシバリレート－コ－３－ヒドロキシヘキサノエート）（Ｐ３ＨＢ３ＨＶ３ＨＨ）等が挙げられる。中でも、工業的に生産が容易であることから、Ｐ３ＨＢ、Ｐ３ＨＢ３ＨＨ、Ｐ３ＨＢ３ＨＶ、Ｐ３ＨＢ４ＨＢ、Ｐ３ＨＢ３ＨＰが好ましい。
　また、繰り返し単位の組成比を変えることで、融点、結晶化度を変化させ、結果として、ヤング率、耐熱性等の物性を変化させることができ、かつ、ポリプロピレンとポリエチレンとの間の物性を付与することが可能であること、および上記したように工業的に生産が容易であり、物性的に有用なプラスチックであるという観点から、３－ヒドロキシ酪酸と３－ヒドロキシヘキサン酸の共重合体であるＰ３ＨＢ３ＨＨがより好ましい。
　より具体的に、Ｐ３ＨＡは、３－ヒドロキシブチレート単位とコモノマー単位とを有する共重合体であり、共重合体における全繰り返し単位１００モル％中の３ＨＢ単位とコモノマー単位との比率（３ＨＢ単位／コモノマー単位）が、好ましくは７０／３０（ｍｏｌ％／ｍｏｌ％）～９９／１（ｍｏｌ％／ｍｏｌ％）であり、７５／２５（ｍｏｌ％／ｍｏｌ％）～９７／３（ｍｏｌ％／ｍｏｌ％）がより好ましく、８０／２０（ｍｏｌ％／ｍｏｌ％）～９５／５（ｍｏｌ％／ｍｏｌ％）がさらに好ましい。
　このような各モノマー単位の比率を有するＰ３ＨＡは、当業者に公知の方法、例えば国際公開第２００９／１４５１６４号に記載の方法に準拠して作製することができる。Ｐ３ＨＡ中の各モノマー単位の比率（すなわち、上述した（３ＨＢ単位／コモノマー単位））は、実施例に記載の方法により求めることができる。
　＜Ｐ３ＨＡを含む粉末の製造方法＞
　本発明の一実施形態において、Ｐ３ＨＡを含む粉末（以下、「Ｐ３ＨＡ粉末」と称する場合がある。）の製造方法は特に限定されず、化学合成による製造方法であってもよいし、微生物による製造方法であってもよい。中でも、微生物による製造方法が好ましい。Ｐ３ＨＡ粉末の微生物による製造方法については、公知の方法を適用できるが、培養工程、精製工程、乾燥工程を含むことが好ましい。
　培養工程でＰ３ＨＡを生産する微生物を培養する方法は特に限定されず、例えば、国際公開第２０１９／１４２７１７号に記載の方法を使用することができる。
　Ｐ３ＨＡを生産する微生物は、細胞内にＰＨＡを生成し得る微生物である限り、特に限定されない。例えば、天然から単離された微生物および菌株の寄託機関（例えば、ＩＦＯ、ＡＴＣＣ等）に寄託されている微生物、またはそれらから調製し得る変異体および形質転換体等を使用できる。例えば、ＰＨＡの一例であるＰ３ＨＢを生成する菌体としては、１９２５年に発見されたＢａｃｉｌｌｕｓ　ｍｅｇａｔｅｒｉｕｍが最初で、他にもカプリアビダス・ネカトール（Ｃｕｐｒｉａｖｉｄｕｓ　ｎｅｃａｔｏｒ）（旧分類：アルカリゲネス・ユートロファス（Ａｌｃａｌｉｇｅｎｅｓ　ｅｕｔｒｏｐｈｕｓ）、ラルストニア・ユートロフア（Ｒａｌｓｔｏｎｉａ　ｅｕｔｒｏｐｈａ））、アルカリゲネス・ラタス（Ａｌｃａｌｉｇｅｎｅｓ　ｌａｔｕｓ）等の天然微生物が挙げられる。これらの微生物ではＰＨＡが菌体内に蓄積されることが知られている。
　また、ＰＨＡの一例である、ヒドロキシブチレートとその他のヒドロキシアルカノエートとの共重合体を生成する菌体としては、Ｐ３ＨＢ３ＨＶおよびＰ３ＨＢ３ＨＨ生産菌であるアエロモナス・キヤビエ（Ａｅｒｏｍｏｎａｓ　ｃａｖｉａｅ）、Ｐ３ＨＢ４ＨＢ生産菌であるアルカリゲネス・ユートロファス（Ａｌｃａｌｉｇｅｎｅｓ　ｅｕｔｒｏｐｈｕｓ）等が挙げられる。特に、Ｐ３ＨＢ３ＨＨに関し、Ｐ３ＨＢ３ＨＨの生産性を上げるために、ＰＨＡ合成酵素群の遺伝子を導入したアルカリゲネス・ユートロファス　ＡＣ３２株（Ａｌｃａｌｉｇｅｎｅｓ　ｅｕｔｒｏｐｈｕｓ　ＡＣ３２，　ＦＥＲＭ　ＢＰ－６０３８）（Ｔ．Ｆｕｋｕｉ，Ｙ．Ｄｏｉ，Ｊ．Ｂａｔｅｒｉｏｌ．，１７９，ｐ４８２１－４８３０（１９９７））等がより好ましい。また、菌体は、上記以外にも、生産したいＰＨＡに合わせて、各種ＰＨＡ合成関連遺伝子を導入した遺伝子組換え微生物であっても良い。
　精製工程で微生物培養により得られたＰ３ＨＡを精製する方法は特に限定されず、公知の物理学的処理、および／または化学的処理、および／または生物学的処理を適用することができ、例えば、国際公開第２０１０／０６７５４３号に記載の精製方法を好ましく適用できる。
　乾燥工程で微生物培養、精製により得られたＰ３ＨＡを乾燥する方法は、特に限定されず、噴霧乾燥、流動層乾燥、気流乾燥、回転乾燥、振動乾燥、バンド乾燥、プレート乾燥等を適用することができ、例えば、国際公開２０１８／０７０４９２号に記載の乾燥方法を好ましく適用できる。
　噴霧乾燥の方法としては、例えば、Ｐ３ＨＡを含む水性懸濁液（以下、「Ｐ３ＨＡ水性懸濁液」と称する。）を微細な液滴の状態として乾燥機内に供給し、該乾燥機内で熱風と接触させながら乾燥する方法が挙げられる。Ｐ３ＨＡ水性懸濁液を微細な液滴の状態で乾燥機内に供給する方法（アトマイザー）は、特に限定されず、回転ディスクを用いる方法、ノズルを用いる方法等の公知の方法が挙げられる。乾燥機内における液滴と熱風の接触方式は、特に限定されず、並流式、向流式、これらを併用する方式等が挙げられる。
　前記噴霧乾燥の際の乾燥温度は、Ｐ３ＨＡ水性懸濁液の液滴から水性媒体の大半を除去できる温度であればよく、目的とする含水率まで乾燥させることができ、なおかつ品質悪化（分子量低下、色調低下）や溶融を極力生じさせないような条件で適宜設定できる。また、乾燥機内の熱風の風量についても、例えば乾燥機のサイズ等に応じて適宜設定できる。
　Ｐ３ＨＡ粉末の製造方法では、前記噴霧乾燥の後に、得られたＰ３ＨＡをさらに乾燥させる工程を含んでいても良い。また、Ｐ３ＨＡの製造方法では、その他の工程（例えば、Ｐ３ＨＡ水性懸濁液に各種添加物を添加する工程等）を含んでいても良い。
　（２－２．圧縮造粒工程）
　本製造方法は、上述した脂肪族ポリエステルを含む粉体を、圧縮造粒する工程（以下、「圧縮造粒工程」とも記載する）を含む。前記粉体を圧縮造粒することにより、嵩密度が高く、流動性に優れる脂肪族ポリエステルを含む造粒体を得ることができる。前記造粒体の流動性が向上することにより、装置に供給された原料（本製造方法においては脂肪族ポリエステルを含む粉体）が、すでに供給された原料により押し戻される、「フィードネック」と呼ばれる現象を発生しにくくできるため、製品の製造効率が向上する。また、圧縮造粒する工程により、前記粉体が上述したバインダーを含んでいない場合でも造粒することが可能であるため、製造コストを低減することができる。
　本発明者らは、圧縮造粒工程により嵩密度が高い脂肪族ポリエステルを含む造粒体が得られる理由として、前記圧縮造粒工程において生じる熱（摩擦熱）により脂肪族ポリエステル同士が融着して固形化されると推定している。このように、本製造方法によれば、加熱することなく粉体を固形化することが可能となるため、上述したバインダーを使用する必要がなくなる。これにより、製造コストを低減できるとの利点も有する。
　前記圧縮造粒工程において、圧縮時の圧力は、１０ｋＮ～６０ｋＮが好ましく、１５ｋＮ～５０ｋＮがより好ましく、１７ｋＮ～４７ｋＮがさらに好ましい。圧力が１０ｋＮ以上であれば、前記粉体を十分に融着させることができる。また、圧力が６０ｋＮ以下であれば、造粒機のトルクオーバーが発生しにくく、かつ原料が完全に溶融することを防ぐことができる。
　本製造方法では、前記圧縮造粒工程において加熱を行うことなく、嵩密度の高い造粒体を製造することができる。したがって、本発明の一実施形態において、前記圧縮造粒工程は、好ましくは５０℃以下で実施され、より好ましくは４０℃以下、さらに好ましくは３０℃以下で実施される。また、温度の下限は特に限定されないが、例えば０℃以上であってもよい。前記圧縮造粒工程が、前記温度範囲内で実施されることにより、脂肪族ポリエステルの熱分解が発生しにくくなるため、脂肪族ポリエステルの分子量の低下を抑制できる。
　圧縮造粒工程における原料の温度は特に限定されない。原料の温度は例えば、０～１００℃であってもよい。また、原料は加熱されていてもよいし、非加熱であってもよい。すなわち、本製造方法は原料の温度に関わらず、粉体の造粒を行うことができる。脂肪族ポリエステルの熱分解が発生しにくくなる観点から、原料は加熱されていないことが好ましい。
　本製造方法において、圧縮造粒する方法は特に限定されず、例えば公知の圧縮造粒装置を使用して実施することができる。圧縮造粒装置の種類は特に限定されず、例えば板状型、タブレット型、ブリケット型、コンパクティング型、スクリュー押出型、ロール足出し型、ブレード押出型、移動ダイス型、ラム押出型等が挙げられる。これらの中でも、脂肪族ポリエステルを含む造粒体の品質と生産性を両立させる観点から、ブリケット型造粒機であることが好ましい。ブリケット型造粒機としては、ブリケットマシン（ホソカワミクロン社製）、ブリケッタ（登録商標）ＢＳＳ型（新東工業製）、ＢＭ－２型（ケイハン）等を使用することができる。
　前記圧縮造粒装置に原料である前記粉体を供給する方法は特に限定されないが、例えば前記粉体をホッパーに貯蔵し、ホッパーに付帯した搬送コンベアより造粒装置に直接供給してもよいし、あるいはホッパー搬送コンベアからベルトコンベア、バケットコンベア等を経由して圧縮造粒装置へ供給することができる。
　ブリケット型の圧縮造粒装置では、供給された前記粉体をスクリューにより縦方向に押しこみ、押し込まれた該粉体を左右から一対のローラーを使用して圧縮することによって、造粒体を製造する。ローラーの種類としては、例えば、リングロール、セグメントロール、コンパクトロール等が挙げられる。
　前記ブリケット型の圧縮造粒装置を使用する場合、ロール回転数は５ｒｐｍ～２０ｒｐｍが好ましく、７ｒｐｍ～１５ｒｐｍがより好ましく、１０ｒｐｍ～１４ｒｐｍがさらに好ましい。圧縮力は１０ｋＮ～６０ｋＮが好ましく、１５ｋＮ～５０ｋＮがより好ましく、１７ｋＮ～４７ｋＮがさらに好ましい。ロール支持圧は３ＭＰａ～１５ＭＰａが好ましく、４ＭＰａ～１０ＭＰａがより好ましく、４．５ＭＰａ～９ＭＰａがさらに好ましい。
　前記圧縮造粒工程は、圧縮する工程と、破砕（造粒）する工程を別々に行ってもよい。すなわち、前記粉体を圧縮した後、破砕することにより造粒を行ってもよい。具体的には、例えば前記粉体を圧縮することにより脂肪族ポリエステルを含む圧縮シートを製造した後、該圧縮シートを破砕してもよい。
　本発明の一実施形態において、前記圧縮造粒工程は、以下の工程を含み得る：
（ａ）嵩密度が０．３０ｇ／ｃｍ３～０．５０ｇ／ｃｍ３である、脂肪族ポリエステルを含む粉体を圧縮してシート状の脂肪族ポリエステルを得る工程、および
（ｂ）前記（ａ）で得られたシート状の脂肪族ポリエステルを破砕する工程。
　前記破砕工程の方法は、得られた圧縮造粒物を破砕することができれば特に限定されず、公知の破砕機によって実施することができる。破砕工程に使用可能な装置としては、例えば、ジョークラッシャー、ロールクラッシャー、フレーククラッシャー等の各種クラッシャー、ローラーミル、カッティングミル、カッターミル等の各種ミル、および破砕メディアを添加した振動篩等が好ましく用いられる。また、これらの破砕機を組み合わせ用いることも可能である。前記フレーククラッシャーとしては、例えばフェザーミル（ホソカワミクロン社製）、ロートプレックス（ホソカワミクロン社製）等を使用することができる。
　本製造方法は必要に応じて、得られた造粒体を整粒、および分級する工程をさらに含んでもよい。整粒機を使用した整粒工程、および分級機を用いた分級工程は、公知の方法によって実施することができる。
　各工程における前記粉体および前記造粒体の輸送方法に制限はないが、自然落下、コンベア輸送、風送等を用いることが可能である。例えば、コンベア輸送で原料を造粒機に輸送した後、自然落下で破砕機・整粒機・分級機へ輸送する方法が好ましい。
　〔３．脂肪族ポリエステルを含む造粒体〕
　本造粒体は、嵩密度が０．５０ｇ／ｃｍ３超、０．７０ｇ／ｃｍ３以下であり、かつ脂肪族ポリエステルの含有量が９０重量％以上である。本造粒体が前記構成を有することにより、流動性、輸送性等が向上する。なお、「脂肪族ポリエステル」については、〔２．脂肪族ポリエステル造粒体の製造方法〕に記載した事項を、適宜援用することができる。
　本造粒体の嵩密度は、０．５０ｇ／ｃｍ３超、０．７０ｇ／ｃｍ３以下であり、好ましくは０．５１ｇ／ｃｍ３～０．６５ｇ／ｃｍ３であり、より好ましくは０．５２ｇ／ｃｍ３～０．６０ｇ／ｃｍ３であり、さらに好ましくは０．５３ｇ／ｃｍ３～０．５７ｇ／ｃｍ３である。本造粒体の嵩密度が前記範囲であれば、本造粒体が流動性および輸送性に優れる。
　本造粒体における脂肪族ポリエステルの含有量は９０重量％以上であり、好ましくは９５重量％以上、より好ましくは９７重量％以上、さらに好ましくは９９重量％以上である。本造粒体における脂肪族ポリエステルの含有量が前記範囲であれば、加工性に優れる。本造粒体における脂肪族ポリエステルの含有量の上限は特に限定されず、例えば、１００％であってもよい。
　本造粒体のメジアン径は、０．５ｍｍ～４．０ｍｍが好ましく、０．７ｍｍ～３．８ｍｍがより好ましく、１．０ｍｍ～３．５ｍｍがさらに好ましく、１．３ｍｍ～３．２ｍｍが特に好ましい。本造粒体のメジアン径が０．５ｍｍ以上であれば、本造粒体の流動性が向上する。また、本造粒体のメジアン径が４．０ｍｍ以下であれば、配管等における詰まりが抑制され、加工時に押し出し機等のスクリューに噛み込みやすくなることから、生産性を向上させることができる。造粒体のメジアン径は、後述する実施例に記載の方法により測定することができる。
　本造粒体の硬度は、５ｋｇｆ～３５ｋｇｆが好ましく、７ｋｇｆ～３０ｋｇｆがより好ましく、１０ｋｇｆ～２５ｋｇｆがさらに好ましい。本造粒体の硬度が５ｋｇｆ以上であれば、輸送中の破損を抑制できるため輸送性および流動性が向上する。また、３５ｋｇｆ以下であれば、スクリュー等により破砕することが容易になるため、加工性に優れる。造粒体の硬度は、後述する実施例に記載の方法により測定することができる。
　本造粒体の含水率は、５％以下が好ましく、１％以下がより好ましく、０．５％以下がさらに好ましく、０．３％以下が特に好ましい。含水率は低いほどよく、例えば、０％であってもよい。本造粒体の含水率が前記範囲であれば、得られる造粒体の硬度、および流動性が向上する。
　本造粒体の黄色度（ＹＩ）は、例えば、４０以下であることが好ましく、３５以下であることがより好ましく、３０以下であることがさらに好ましい。なお、ＹＩは低いほど黄色度が低いことになり、下限値は特に限定されないが、例えば、５以上であればよい。本造粒体のＹＩが前記範囲であれば、不純物の混入が一定量以下に抑えられている評価でき、一定の品質を担保できる。ＹＩは、後述する実施例に記載の方法により測定することができる。
　本造粒体の熱安定性は、例えば、７０％以上であり、７３％以上が好ましく、７５％以上がより好ましい。熱安定性が前記範囲であれば、熱安定性に優れた造粒体原料として使用できる。熱安定性は高いほどよく、例えば、１００％であってもよい。
　本発明の一実施形態において、本造粒体は、本製造方法により製造される。
　本造粒体は、紙、フィルム、シート、チューブ、板、棒、容器（例えば、ボトル容器等）、袋、部品等、種々の用途に利用できる。
　本発明は上述した各実施形態に限定されるものではなく、請求項に示した範囲で種々の変更が可能であり、異なる実施形態にそれぞれ開示された技術的手段を適宜組み合わせて得られる実施形態についても本発明の技術的範囲に含まれる。
　すなわち、本発明の一実施形態は、以下である。
＜１＞嵩密度が０．３０ｇ／ｃｍ３～０．５０ｇ／ｃｍ３である、脂肪族ポリエステルを含む粉体を圧縮造粒する工程を含む、脂肪族ポリエステルを含む造粒体の製造方法。
＜２＞前記圧縮造粒する工程が、５０℃以下で実施される、＜１＞に記載の造粒体の製造方法。
＜３＞前記圧縮造粒する工程が、ブリケット型造粒機を用いて実施される、＜１＞または＜２＞に記載の造粒体の製造方法。
＜４＞前記圧縮造粒する工程において、圧縮時の圧力が１０ｋＮ～６０ｋＮである、＜１＞～＜３＞に記載の造粒体の製造方法。
＜５＞前記脂肪族ポリエステルが、ポリ（３－ヒドロキシアルカノエート）である、＜１＞～＜４＞のいずれかに記載の造粒体の製造方法。
＜６＞前記脂肪族ポリエステルが、ポリ（３－ヒドロキシブチレート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシプロピオネート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシヘキサノエート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシバリレート）およびポリ（３－ヒドロキシブチレート－コ－４－ヒドロキシブチレートからなる群より選択される１種類以上である、＜１＞～＜５＞のいずれかに記載の造粒体の製造方法。
＜７＞嵩密度が０．５０ｇ／ｃｍ３超、０．７０ｇ／ｃｍ３以下であり、かつ脂肪族ポリエステルの含有量が９０重量％以上である、脂肪族ポリエステルを含む造粒体。
＜８＞前記脂肪族ポリエステルが、ポリ（３－ヒドロキシアルカノエート）である、＜７＞に記載の造粒体。
＜９＞前記脂肪族ポリエステルが、ポリ（３－ヒドロキシブチレート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシプロピオネート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシヘキサノエート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシバリレート）およびポリ（３－ヒドロキシブチレート－コ－４－ヒドロキシブチレートからなる群より選択される１種類以上である、＜７＞または＜８＞に記載の造粒体。
＜１０＞メジアン径が０．５ｍｍ～４．０ｍｍである、＜７＞～＜９＞のいずれかに記載の造粒体。
＜１１＞硬度が５ｋｇｆ～３５ｋｇｆである、＜７＞～＜１０＞のいずれかに記載の造粒体。
＜１２＞含水率が５％以下である、＜７＞～＜１１＞のいずれかに記載の造粒体。
　以下、本発明を実施例に基づいてより詳細に説明するが、本発明はこれら実施例に限定されるものではない。
　〔測定方法〕
　（含水率）
　脂肪族ポリエステル粉体および造粒体の含水率は、加熱乾燥式水分計（商品名：ＭＳ－７０、Ａ＆Ｄ社製）を使用して測定した。
　〔組成比率〕
　脂肪族ポリエステル粉体中の脂肪族ポリエステル（共重合体）における３ＨＢ単位とコモノマー単位との組成比率（上述した（３ＨＢ単位／コモノマー単位））は以下のように算出した。脂肪族ポリエステル粉体を生産するために培養した乾燥菌体約２０ｍｇに１ｍｌの硫酸－メタノール混液（１５：８５）と１ｍｌのクロロホルムを添加して密栓し、１００℃で１４０分間加熱することでＰＨＡ分解物のメチルエステルを得た。冷却後、これに０．５ｍｌの脱イオン水を加えてよく混合した後、水層と有機層が分離するまで放置した。その後、分取した有機層中のＰＨＡ分解物のモノマー単位組成をキャピラリーガスクロマトグラフィーにより分析した。ガスクロマトグラフは島津製作所ＧＣ－１７Ａ、キャピラリーカラムはＧＬサイエンス社製ＮＥＵＴＲＡ　ＢＯＮＤ－１（カラム長２５ｍ、カラム内径０．２５ｍｍ、液膜厚０．４μｍ）を用いた。キャリアガスとしてＨｅを用い、カラム入口圧１００ｋＰａとし、サンプルは１μｌを注入した。温度条件は、初発温度５０～２００℃まで８℃／分の速度で昇温し、さらに２００～２９０℃まで３０℃／分の速度で昇温した。
　（黄色度）
　脂肪族ポリエステル粉体および造粒体の黄色度（ＹＩ）は、ＪＩＳ　Ｋ　７３７３に基づき、色彩色差計（商品名：ＣＭ－５、コニカミノルタ社製）を使用して測定した。
　（分子量）
　脂肪族ポリエステル粉体中の、および造粒体中の脂肪族ポリエステルの重量平均分子量は、ゲル浸透クロマトグラフィー（ＧＰＣ）（昭和電工製「Ｓｈｏｄｅｘ　ＧＰＣ－１０１」）によって、カラムにポリスチレンゲル（昭和電工製「Ｓｈｏｄｅｘ　Ｋ－８０４」）を用い、クロロホルムを移動相とし、ポリスチレン換算した場合の重量平均分子量として求めた。
　（嵩密度）
　脂肪族ポリエステル粉体および造粒体の嵩密度は、ＪＩＳ　Ｋ　７３６５：１９９９に基づき、嵩比重測定器（商品名：規格形カサ比重測定器、蔵特科学器械製）を用いて測定した。
　（硬度）
　脂肪族ポリエステル造粒体の硬度は、硬度計（商品名：木屋式硬度計、藤原製作所製）を使用して測定した。
　（脂肪族ポリエステル粉体のメジアン径）
　脂肪族ポリエステル粉体のメジアン径は、レーザ回折／散乱式粒子径分布測定装置ＬＡ－９５０（ＨＯＲＩＢＡ社製）を用いて測定した。イオン交換水２０ｍＬに、界面活性剤としてドデシル硫酸ナトリウム０．０５ｇを加えて、界面活性剤水溶液を得た。次いで、上記界面活性剤水溶液に、測定対象の脂肪族ポリエステル粉体０．２ｇを加えて、上記脂肪族ポリエステル粉体を上記界面活性剤水溶液中に分散させ、測定用の分散液を得た。調製した分散液を、上記レーザ回折／散乱式粒子径分布測定装置に導入し、測定を行った。
　（造粒体のメジアン径）
　脂肪族ポリエステル造粒体のメジアン径は、ＪＩＳ　Ｚ　８８０１－１：２０００に基づき、金属製網ふるいを用いて測定した。
　（熱安定性）
　脂肪族ポリエステル粉体および造粒体の熱安定性は、小型熱プレス機（商品名：Ｈ３００－０１、アズワン社製）を使用して測定した。１６０℃、１３ＭＰａで２０分間プレスを行い、加熱前と後で分子量が変化した割合を熱安定性とした。
　（流動性）
　脂肪族ポリエステル粉体および造粒体の流動性は押出機、ＴＥＭ２６ＳＳ（東芝機械製）を用いて測定した。一定量の粉体または造粒体を押出機に供給し、フィードネックが発生するまでのスクリューの回転数を測定し、さらに回転数当たりの処理量を算出して、比較することで流動性を評価した。
　〔実施例１〕
　（圧縮造粒）
　国際公開第２０２１／０８５５３４号の実施例１に記載の方法により、表１に記載の３ＨＨ比率を有するＰ３ＨＢ３ＨＨ粉体（乾燥粉体）を得た。得られた粉体を、縦スクリューと２つの回転ロールを有するブリケット型造粒機であるブリケットマシン（ホソカワミクロン社製）に供給して圧縮し、圧縮シートを得た。得られた圧縮シートを、縦スクリューと回転ロールを備えたフェザーミル（ホソカワミクロン社製）で破砕することにより造粒して、造粒体を得た。圧縮造粒機のロール回転数は１４ｒｐｍ、圧縮力は４０ｋＮ、ロール支持圧は９ＭＰａとした。また、造粒体の製造は室温（２３℃）で実施し、原料温度は２２℃であった。造粒体の含水率は０．２１％、分子量は４２万、嵩密度は０．５７、メジアン径は１．８ｍｍ、ＹＩは１４、硬度は１０ｋｇｆ、熱安定性は８５％、Ｐ３ＨＢ３ＨＨ含有量は９９重量％であった。
　〔実施例２〕
　国際公開第２０２２／０９１６８５号の実施例１に記載の方法により、表１に記載の３ＨＨ（コモノマー単位）比率を有するＰ３ＨＢ３ＨＨ粉体（乾燥粉体）を得た。得られた粉体を、前記ブリケットマシン（ホソカワミクロン社製）に供給して、圧縮シートを得た。得られたシートを、前記フェザーミル（ホソカワミクロン社製）で破砕し、造粒体を得た。圧縮造粒機のロール回転数は１０ｒｐｍ、圧縮力は１７ｋＮ、ロール支持圧は４．５ＭＰａとした。また、造粒体の製造は室温（２３℃）で実施し、原料温度は２２℃であった。造粒体の含水率は０．０９％、分子量は６５万、嵩密度は０．５３、メジアン径は３．２ｍｍ、ＹＩは２６、硬度は１８ｋｇｆ、熱安定性は７７％、Ｐ３ＨＢ３ＨＨ含有量は９９重量％であった。
　〔実施例３〕
　菌体の培養方法を国際公開第２０１９／１４２８４５号の実施例２に記載の方法に変更したこと以外は、実施例１と同様の方法により、表１に記載の３ＨＨ比率を有するＰ３ＨＢ３ＨＨ粉体（乾燥粉体）を得た。得られた粉体を、前記ブリケットマシン（ホソカワミクロン社製）に供給して、シートを得た。得られたシートを、縦スクリューと回転ロールを備えたフェザーミル（ホソカワミクロン社製）で破砕し、造粒体を得た。圧縮造粒機のロール回転数は１４ｒｐｍ、圧縮力は４５ｋＮ、ロール支持圧は９ＭＰａとした。また、造粒体の製造は室温（２３℃）で実施し、原料温度は２２℃であった。造粒体の含水率は０．２０％、分子量は６５万、嵩密度は０．５３、メジアン径は３．２ｍｍ、硬度は１４ｋｇｆ、熱安定性は５５％、Ｐ３ＨＢ３ＨＨ含有量は９９重量％であった。
　〔実施例４〕
　菌体の培養方法を国際公開第２０１９／１４２８４５号の実施例２に記載の方法に変更したこと以外は、実施例１と同様の方法により、表１に記載の３ＨＨ比率を有するＰ３ＨＢ３ＨＨ粉体（乾燥粉体）を得た。得られた粉体を、前記ブリケットマシン（ホソカワミクロン社製）に供給して、シートを得た。得られたシートを、固定刃と回転刃を有するロートプレックス（ホソカワミクロン社製）で破砕し、造粒体を得た。圧縮造粒機のロール回転数は１０．７ｒｐｍ、圧縮力は２５ｋＮ、ロール支持圧は４．５ＭＰａとした。また、造粒体の製造は室温（２７℃）で実施し、原料温度は２６℃であった。造粒体の含水率は０．０９％、分子量は６５万、嵩密度は０．５４、メジアン径は２．８ｍｍ、ＹＩは２６、硬度は２０ｋｇｆ、熱安定性は８０％、Ｐ３ＨＢ３ＨＨ含有量は９９重量％であった。
　〔実施例５〕
　国際公開第２０２２／０９１６８５号の実施例１の（洗浄２）までと同様の方法により、分散スラリーを得た。これを濾布で脱水し、プレートドライヤー（Andritz社製）を用いて乾燥し、表１に記載の３ＨＨ比率を有するＰ３ＨＢ３ＨＨ粉体（乾燥粉体）を得た。得られた粉体を、前記ブリケットマシン（ホソカワミクロン社製）に供給して、シートを得た。得られたシートを、固定刃と回転刃を有するロートプレックス（ホソカワミクロン社製）で破砕し、造粒体を得た。圧縮造粒機のロール回転数は１１．５ｒｐｍ、圧縮力は３６ｋＮ、ロール支持圧は９ＭＰａとした。また、造粒体の製造は室温（２８℃）で実施し、原料温度は２８℃であった。造粒体の含水率は０．１７％、分子量は４５万、嵩密度は０．５７、メジアン径は２．５ｍｍ、ＹＩは１４、硬度は１４ｋｇｆ、熱安定性は８３％、Ｐ３ＨＢ３ＨＨ含有量は９９重量％であった。
　〔実施例６〕
　国際公開第２０２２／０９１６８５号の実施例１の（洗浄２）までと同様の方法により、分散スラリーを得た。これを濾布で脱水し、プレートドライヤー（Andritz社製）を用いて乾燥し、表１に記載の３ＨＨ比率を有するＰ３ＨＢ３ＨＨ粉体（乾燥粉体）を得た。得られた粉体を、前記ブリケットマシン（ホソカワミクロン社製）に供給して、シートを得た。得られたシートを、固定刃と回転刃を有するロートプレックス（ホソカワミクロン社製）で破砕し、造粒体を得た。圧縮造粒機のロール回転数は１４．４ｒｐｍ、圧縮力は１３ｋＮ、ロール支持圧は４．１ＭＰａとした。また、造粒体の製造は室温（１１℃）で実施し、原料温度は６０℃であった。造粒体の含水率は０．２８％、分子量は７０万、嵩密度は０．５２、メジアン径は２．５ｍｍ、ＹＩは２３、硬度は２４ｋｇｆ、熱安定性は８３％、Ｐ３ＨＢ３ＨＨ含有量は９９重量％であった。
　〔比較例１〕
　実施例１の粉体（乾燥粉体）を比較例１とした。比較例１の粉体は、コモノマーとして３ＨＨを含み、含水率が０．２１％、（３ＨＢ単位／３ＨＨ単位）は９４．８／５．２（ｍｏｌ％／ｍｏｌ％）、重量平均分子量が４２万、嵩密度が０．４２、メジアン径が１６３μｍ、ＹＩが１４、熱安定性は８４％であった。
　〔比較例２〕
　実施例２の粉体（乾燥粉体）を比較例２とした。比較例２の粉体は、コモノマーとして３ＨＨを含み、含水率が０．０９％、（３ＨＢ単位／３ＨＨ単位）は８２／１８（ｍｏｌ％／ｍｏｌ％）、重量平均分子量が６５万、嵩密度が０．４４、メジアン径が１６３μｍ、ＹＩが２６、熱安定性は７７％であった。
　〔比較例３〕
　実施例３の粉体（乾燥粉体）を比較例３とした。比較例３の粉体は、コモノマーとして３ＨＨを含み、含水率が０．２０％、（３ＨＢ単位／３ＨＨ単位）は９６．３／３．７（ｍｏｌ％／ｍｏｌ％）、重量平均分子量が３３万、嵩密度が０．３６、メジアン径が１１３μｍ、熱安定性は５５％であった。
　〔比較例４〕
　実施例４の粉体（乾燥粉体）を比較例４とした。比較例４の粉体は、コモノマーとして３ＨＨを含み、含水率が０．０９％、（３ＨＢ単位／３ＨＨ単位）は８２／１８（ｍｏｌ％／ｍｏｌ％）、重量平均分子量が６５万、嵩密度が０．４４、メジアン径が１６３μｍ、ＹＩが２６、熱安定性は７７％であった。
　〔比較例５〕
　実施例５の粉体（乾燥粉体）を比較例５とした。比較例５の粉体は、コモノマーとして３ＨＨを含み、含水率が０．１７％、（３ＨＢ単位／３ＨＨ単位）は９４．９／５．１（ｍｏｌ％／ｍｏｌ％）、重量平均分子量が４５万、嵩密度が０．３２、メジアン径が２．９μｍ、ＹＩが１４、熱安定性は８３％であった。
　〔比較例６〕
　実施例６の粉体（乾燥粉体）を比較例６とした。比較例６の粉体は、コモノマーとして３ＨＨを含み、含水率が０．２８％、（３ＨＢ単位／３ＨＨ単位）は８７．５／１２．５（ｍｏｌ％／ｍｏｌ％）、重量平均分子量が７０万、嵩密度が０．３５、メジアン径が２６．１μｍ、ＹＩが２３、熱安定性は８３％であった。
　実施例１～６の造粒体、および比較例１～６の粉体の物性を表１に示す。なお、比較例１～６の粉体は手で押しつぶせるほど柔らかかったため、硬度の測定は行わなかった。
Figure JPOXMLDOC01-appb-T000001
　実施例１、３、ならびに比較例１、３の流動性試験の結果を表２に示す。表２中、「ＦＮ」はフィードネックを意味する。
Figure JPOXMLDOC01-appb-T000002
　〔結果〕
　表１より、実施例１～６のいずれの造粒体も嵩密度が０．５０ｇ／ｃｍ３を超えており、比較例１～６の粉体よりも高い嵩密度を有していた。また表２より、実施例１および３の造粒体は、比較例１、３の粉体と比較して、ＦＮが発生するスクリューの回転数が低く、処理量が向上しているため、優れた流動性を有していることが分かる。また、実施例と比較例の間では、熱安定性、およびＹＩに大きな変化はなかった。したがって、圧縮造粒で製造された本発明の造粒体は、噴霧乾燥で製造された乾燥粉体に比して、品質面で差異がないことが示された。以上より、本発明の一実施形態に係る製造方法によれば、嵩密度が高く、流動性が高い脂肪族ポリエステルを含む造粒体を製造できることが示された。
　本発明の製造方法により得られた造粒体は、農業、漁業、林業、園芸、医学、衛生品、衣料、非衣料、包装、自動車、建材、その他の分野に好適に利用することができる。

 

Claims (12)

  1. 　嵩密度が０．３０ｇ／ｃｍ３～０．５０ｇ／ｃｍ３である、脂肪族ポリエステルを含む粉体を圧縮造粒する工程を含む、脂肪族ポリエステルを含む造粒体の製造方法。
  2. 　前記圧縮造粒する工程が、５０℃以下で実施される、請求項１に記載の造粒体の製造方法。
  3. 　前記圧縮造粒する工程が、ブリケット型造粒機を用いて実施される、請求項１に記載の造粒体の製造方法。
  4. 　前記圧縮造粒する工程において、圧縮時の圧力が１０ｋＮ～６０ｋＮである、請求項１に記載の造粒体の製造方法。
  5. 　前記脂肪族ポリエステルが、ポリ（３－ヒドロキシアルカノエート）である、請求項１～４のいずれか１項に記載の造粒体の製造方法。
  6. 　前記脂肪族ポリエステルが、ポリ（３－ヒドロキシブチレート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシプロピオネート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシヘキサノエート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシバリレート）およびポリ（３－ヒドロキシブチレート－コ－４－ヒドロキシブチレートからなる群から選択される１種類以上である、請求項５に記載の造粒体の製造方法。
  7. 　嵩密度が０．５０ｇ／ｃｍ３超、０．７０ｇ／ｃｍ３以下であり、かつ脂肪族ポリエステルの含有量が９０重量％以上である、脂肪族ポリエステルを含む造粒体。
  8. 　前記脂肪族ポリエステルが、ポリ（３－ヒドロキシアルカノエート）である、請求項７に記載の造粒体。
  9. 　前記脂肪族ポリエステルが、ポリ（３－ヒドロキシブチレート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシプロピオネート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシヘキサノエート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシバリレート）およびポリ（３－ヒドロキシブチレート－コ－４－ヒドロキシブチレートからなる群から選択される１種類以上である、請求項８に記載の造粒体。
  10. 　メジアン径が、０．５ｍｍ～４．０ｍｍである、請求項７～９のいずれか１項に記載の造粒体。
  11. 　硬度が、５ｋｇｆ～３５ｋｇｆである、請求項７～９のいずれか１項に記載の造粒体。
  12. 　含水率が５％以下である、請求項７～９のいずれか１項に記載の造粒体。

     
PCT/JP2023/032780 2022-09-26 2023-09-08 造粒体およびその製造方法 Ceased WO2024070577A1 (ja)