WO2024063872A1 - Système de récupération d'énergie et de neutre en carbone pour recyclage de batterie ev ultra-efficace - Google Patents

Système de récupération d'énergie et de neutre en carbone pour recyclage de batterie ev ultra-efficace Download PDF

Info

Publication number
WO2024063872A1
WO2024063872A1 PCT/US2023/029571 US2023029571W WO2024063872A1 WO 2024063872 A1 WO2024063872 A1 WO 2024063872A1 US 2023029571 W US2023029571 W US 2023029571W WO 2024063872 A1 WO2024063872 A1 WO 2024063872A1
Authority
WO
WIPO (PCT)
Prior art keywords
electrode
membrane
solid electrolyte
ions
lithium
Prior art date
Application number
PCT/US2023/029571
Other languages
English (en)
Inventor
Jesse Baucom
Sanjeev Kolli
Original Assignee
Lyten, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US17/948,030 external-priority patent/US11827991B1/en
Priority claimed from US17/948,055 external-priority patent/US11779886B1/en
Application filed by Lyten, Inc. filed Critical Lyten, Inc.
Publication of WO2024063872A1 publication Critical patent/WO2024063872A1/fr

Abstract

Les concepts présentement divulgués concernent des techniques améliorées pour l'extraction de métal alcalin et des systèmes de recyclage de batterie EV ultra-efficaces. En utilisant un électrolyte solide incorporé dans une matrice, un métal alcalin (tel que le lithium) peut être séparé plus efficacement des solutions d'alimentation. L'énergie utilisée pour extraire initialement le lithium d'une solution d'alimentation est stockée en tant qu'énergie électrochimique, laquelle énergie électrochimique est récupérée dans des étapes de traitement d'extraction ultérieures. Le présent stockage d'énergie et cette récupération d'énergie sont effectués dans des cycles en cours ultra-efficaces continus. Puisque les pertes d'énergie irrécupérables engendrées dans chaque cycle sont limitées à des quantités négligeables de chauffage par effet Joule des composants du système et de la solution d'alimentation, le système peut être alimenté de manière durable à l'aide d'une énergie renouvelable générée localement.
PCT/US2023/029571 2022-09-19 2023-08-04 Système de récupération d'énergie et de neutre en carbone pour recyclage de batterie ev ultra-efficace WO2024063872A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US17/948,030 US11827991B1 (en) 2022-09-19 2022-09-19 Energy reclamation and carbon-neutral system for ultra-efficient EV battery recycling
US17/948,030 2022-09-19
US17/948,055 US11779886B1 (en) 2022-09-19 2022-09-19 Water-impermeable carbon-based electrolyte and separation membrane and fabrication thereof
US17/948,055 2022-09-19

Publications (1)

Publication Number Publication Date
WO2024063872A1 true WO2024063872A1 (fr) 2024-03-28

Family

ID=90455100

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2023/029571 WO2024063872A1 (fr) 2022-09-19 2023-08-04 Système de récupération d'énergie et de neutre en carbone pour recyclage de batterie ev ultra-efficace

Country Status (2)

Country Link
TW (1) TW202413272A (fr)
WO (1) WO2024063872A1 (fr)

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7488409B1 (en) * 2001-10-05 2009-02-10 Scimist, Inc. Mediated electrochemical oxidation of animal waste materials
US20130186760A1 (en) * 2010-11-19 2013-07-25 Central South University Method and device for extracting and enriching lithium
US20150171455A1 (en) * 2012-05-21 2015-06-18 Blacklight Power Inc. Ciht power system
US20150197830A1 (en) * 2012-07-31 2015-07-16 Research Institute Of Industrial Science & Technology Method for Extracting Lithium from Solution Containing Lithium
US20210391605A1 (en) * 2018-10-26 2021-12-16 National University Of Singapore A lithium ion battery materials recycling method
US20220223885A1 (en) * 2021-01-14 2022-07-14 Palo Alto Research Center Incorporated Electrochemical device with efficient ion exchange membranes

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7488409B1 (en) * 2001-10-05 2009-02-10 Scimist, Inc. Mediated electrochemical oxidation of animal waste materials
US20130186760A1 (en) * 2010-11-19 2013-07-25 Central South University Method and device for extracting and enriching lithium
US20150171455A1 (en) * 2012-05-21 2015-06-18 Blacklight Power Inc. Ciht power system
US20150197830A1 (en) * 2012-07-31 2015-07-16 Research Institute Of Industrial Science & Technology Method for Extracting Lithium from Solution Containing Lithium
US20210391605A1 (en) * 2018-10-26 2021-12-16 National University Of Singapore A lithium ion battery materials recycling method
US20220223885A1 (en) * 2021-01-14 2022-07-14 Palo Alto Research Center Incorporated Electrochemical device with efficient ion exchange membranes

Also Published As

Publication number Publication date
TW202413272A (zh) 2024-04-01

Similar Documents

Publication Publication Date Title
Lu et al. Carbon materials for stable Li metal anodes: challenges, solutions, and outlook
Kim et al. An electrochemical cell for selective lithium capture from seawater
CN110537269B (zh) 预锂化储能装置
Liu et al. Bipolar electrodes for next‐generation rechargeable batteries
US9748616B2 (en) Regeneration of cathode material of lithium-ion batteries
CN107579235B (zh) 一种应用于锂硫电池正极的氧化Mxene/S复合物的制备方法
US9057139B2 (en) Method for manufacturing electrode module for recovery of metal ions, electrode module for recovery of metal ions, and apparatus for recovery of metal ions including the same
CN105761941B (zh) 不含金属的含水电解质能量存储装置
Ming et al. The binder effect on an oxide-based anode in lithium and sodium-ion battery applications: the fastest way to ultrahigh performance
US12110603B2 (en) Energy reclamation and carbon-neutral system for ultra-efficient EV battery recycling
US20140287305A1 (en) Ion conducting batteries with solid state electrolyte materials
TW201442324A (zh) 用於製造較厚電極之多層電池電極設計
CN102754247A (zh) 用于高能量锂离子电池的分段电极技术
CN112189266A (zh) 具有改善的离子电导率的电化学电池
Shi et al. Exploration of energy storage materials for water desalination via next-generation capacitive deionization
US11779886B1 (en) Water-impermeable carbon-based electrolyte and separation membrane and fabrication thereof
JP6827657B2 (ja) 電気化学デバイス及びその作製方法
TW201436340A (zh) 蓄電元件與其製造方法以及蓄電裝置
JP2020047572A (ja) 亜鉛二次電池用電極活物質及びこれを含む二次電池
Pan et al. A functional separator modified by synergistic MoS2 and activated carbon for improved-performance lithium sulfur batteries
Wang et al. Direct recycling for advancing sustainable battery solutions
Tiwari et al. Exploring advances in sulfur composite cathodes for lithium-sulfur batteries: A comprehensive review
Wang et al. Direct Lithium Extraction Using Intercalation Materials
Panda et al. Acidity‐Aided Surface Modification Strategy to Enhance In Situ MnO2 Deposition for High Performance Zn‐MnO2 Battery Prototypes
EP3398221B1 (fr) Cathode d'oxyde de metal

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23868768

Country of ref document: EP

Kind code of ref document: A1