WO2024053510A1 - 織物および繊維製品 - Google Patents

織物および繊維製品 Download PDF

Info

Publication number
WO2024053510A1
WO2024053510A1 PCT/JP2023/031499 JP2023031499W WO2024053510A1 WO 2024053510 A1 WO2024053510 A1 WO 2024053510A1 JP 2023031499 W JP2023031499 W JP 2023031499W WO 2024053510 A1 WO2024053510 A1 WO 2024053510A1
Authority
WO
WIPO (PCT)
Prior art keywords
fiber
woven fabric
fibers
flame
composite
Prior art date
Application number
PCT/JP2023/031499
Other languages
English (en)
French (fr)
Inventor
篤男 田村
Original Assignee
帝人株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 帝人株式会社 filed Critical 帝人株式会社
Publication of WO2024053510A1 publication Critical patent/WO2024053510A1/ja

Abstract

課題は、難燃性だけでなく優れた伸縮性と抗ピリング性と良好な外観品位をも有する織物、および該織物を用いてなる繊維製品を提供することであり、解決手段は、ＪＩＳ　Ｋ７２０１により測定される限界酸素指数が２５以上の難燃性繊維を含む紡績糸と、２成分がサイドバイサイド型または偏心芯鞘型に貼り合わされた複合繊維からなる糸条とを含む複合糸を用いてなる織物において、前記複合糸に含まれる複合繊維からなる糸条の重量比率を４０～６０重量％とし、前記複合糸に、撚係数Ｋが２７０～４００で撚りを施すことである。

Description

織物および繊維製品
　本発明は、難燃性だけでなく優れた伸縮性と抗ピリング性と良好な外観品位をも有する織物、および該織物を用いてなる繊維製品に関する。
　従来、消防、電力、化学会社など火炎に晒される可能性のある作業に従事する人々が着用する作業服として難燃布帛が用いられている。この難燃布帛は、メタ系アラミド繊維やパラ系アラミド繊維をはじめとする難燃繊維を主体として使用しており、一般的には伸縮性の付与は難しいとされている。
　難燃繊維を使った布帛に伸縮性を付与する方法としては、弾性糸を用いる方法（例えば、特許文献１～３参照）や難燃繊維に撚りをかけた後に熱セットし解撚する方法（例えば、特許文献４～６参照）などが提案されている。
　しかしながら、弾性糸を用いた布帛では、耐熱性や難燃性だけでなく、耐薬品性、特に、耐塩素性が低いことによる通常の使用および洗濯時の伸縮性の急激な低下などの問題があった。
　一方、撚りをかけた後に熱セットし解撚した難燃繊維を用いた布帛では、製織および後加工工程、さらには着用中に伸縮性が低下し布帛として十分な性能と品質が得られないという問題や、コストが高くなるという問題点があった。
　上記問題を解決するため、２成分がサイドバイサイド型または偏心芯鞘型に貼り合わされた複合繊維を含む複合糸を用いて製織し、加熱収縮により伸縮性を付与した布帛が提案されているが、抗ピリング性の点でまだ満足とはいえなかった（例えば、特許文献７参照）。
特開２００３－１９３３１４号公報 特開２００６－１２４８６５号公報 特開２００７－９３７８号公報 特開２００１－２４８０２７号公報 特開２００５－３０７４２９号公報 特開２００８－１９０１０３号公報 特開２０１４－２４０５３２号公報
　本発明は上記の背景に鑑みなされたものであり、その目的は、難燃性だけでなく優れた伸縮性と抗ピリング性と良好な外観品位をも有する織物、および該織物を用いてなる繊維製品を提供することにある。
　本発明者は上記の課題を達成するため鋭意検討した結果、２成分がサイドバイサイド型または偏心芯鞘型に貼り合わされた複合繊維を含む複合糸を含む布帛において、複合繊維の重量比率が小さすぎると、布帛を十分に収縮させることができず、伸縮性が得られないばかりか、布帛に緻密さが欠け抗ピリング性が低下することを見出し、さらに鋭意検討を重ねることにより本発明を完成するに至った。かくして、本発明によれば以下の発明が提供される。
１．ＪＩＳ　Ｋ７２０１により測定される限界酸素指数が２５以上の難燃性繊維を含む紡績糸と、２成分がサイドバイサイド型または偏心芯鞘型に貼り合わされた複合繊維からなる糸条とを含む複合糸を用いてなる織物であり、前記複合糸において、前記複合繊維からなる糸条の重量比率が４０～６０重量％であり、前記複合糸に、下記式で定義する撚係数Ｋが２７０～４００で撚りが施されていることを特徴とする織物。
撚係数Ｋ＝Ｔ×√Ｄ
ただし、Ｔは撚数（回／２．５４ｃｍ）、Ｄは複合糸の総繊度（ｄｔｅｘ）である。
２．織物において、前記難燃性繊維の重量比率が織物重量に対して６５～８４重量％の範囲内であり、かつ前記複合繊維の重量比率が織物重量に対して１６～３５重量％の範囲内である、上記１に記載の織物。
３．前記難燃性繊維が、メタ系アラミド繊維、パラ系アラミド繊維、ポリパラフェニレンベンズオキサゾール繊維、ポリベンゾイミダゾール繊維、ポリイミド繊維、ポリエーテルイミド繊維、ポリアミドイミド繊維、炭素繊維、ポリフェニレンサルファイド繊維、ポリ塩化ビニル繊維、難燃レーヨン、モダアクリル繊維、難燃アクリル繊維、難燃ポリエステル繊維、難燃ビニロン繊維、メラミン繊維、フッ素繊維、難燃ウール、および難燃コットンからなる群から選ばれた１種類以上の繊維である、上記１または２に記載の織物。
４．前記複合繊維からなる糸条が、単繊維繊度０．５～１０．０ｄｔｅｘ、かつ総繊度２０～２００ｄｔｅｘのマルチフィラメントである、上記１～３のいずれかに記載の織物。
５．前記複合繊維を構成する成分の少なくとも１成分がリサイクル由来または植物由来である、上記１～４のいずれかに記載の織物。
６．前記難燃性繊維が難燃剤を含むメタ系アラミド繊維であり、かつ前記複合繊維が難燃剤を含む、上記１～５のいずれかに記載の織物。
７．前記複合糸が織物の緯糸に配され、緯方向の伸長率が1０～５０％の範囲内である、上記１～６のいずれかに記載の織物。
８．前記複合糸が織物の緯糸に配され、緯方向の伸長回復率が７０％以上である、上記１～６のいずれかに記載の織物。
９．ＪＩＳ　Ｌ１０７６－２０１２　Ａ法　ＩＣＩ型１０時間で測定される抗ピリング性が４級以上である、上記１～８のいずれかに記載の織物。
１０．表面に前記複合繊維の収縮に起因する凹凸がない、上記１～９のいずれかに記載の織物。
１１．織物において、ＪＩＳ　Ｋ７２０１により測定される限界酸素指数が２５以上である、上記１～１０のいずれかに記載の織物。
１２．上記１～１１のいずれかに記載された織物を用いてなり、消防服、防火服、執務服、モータースポーツ用レーシングスーツ、作業服、手袋、帽子、ベスト、シート、テント、膜材、幌、建築資材、住宅材、および車両内装材からなる群より選択される繊維製品。
　本発明によれば、難燃性だけでなく優れた伸縮性と抗ピリング性と良好な外観品位をも有する織物、および該織物を用いてなる繊維製品が得られる。
　以下、本発明の実施の形態について詳細に説明する。本発明において、複合糸は紡績糸と複合繊維からなる糸条とを含む。そして、前記紡績糸は、ＪＩＳ　Ｋ７２０１により測定される限界酸素指数が２５以上の難燃性繊維（以下、単に「難燃性繊維」ということもある。）を含む。
　かかる難燃性繊維としては、メタ系アラミド繊維（メタ型全芳香族ポリアミド繊維）、パラ系アラミド繊維（パラ型全芳香族ポリアミド繊維）、ポリパラフェニレンベンズオキサゾール繊維、ポリベンゾイミダゾール繊維、ポリイミド繊維、ポリエーテルイミド繊維、ポリアミドイミド繊維、炭素繊維、ポリフェニレンサルファイド繊維、ポリ塩化ビニル繊維、難燃レーヨン、モダアクリル繊維、難燃アクリル繊維、難燃ポリエステル繊維、難燃ビニロン繊維、メラミン繊維、フッ素繊維、難燃ウール、難燃コットンなどが例示される。これらの難燃性繊維を１種または２種以上用いることができる。
　なかでも、優れた限界酸素指数を示しかつ優れた機械的物性の点から、メタ系アラミド繊維すなわちメタフェニレンイソフタルアミド繊維（市販品では、帝人株式会社製「コーネックス」（商標名）、デュポン社製「ノーメックス」（商標名）など）は有用である。さらには、パラ系アラミド繊維すなわちパラフェニレンテレフタルアミド繊維（市販品では、テイジンアラミド社製「トワロン」（商標名）、東レ・デュポン株式会社製「ケブラー」（商標名）など）、コパラフェニレン・３、４’オキシジフェニレンテレフタルアミド繊維（市販品では、帝人株式会社製「テクノーラ」（商標名）など）を混合させることも好ましい。
　これらの難燃性繊維は、本発明の目的を損なわない範囲で、酸化防止剤、紫外線吸収剤、熱安定剤、難燃剤、酸化チタン、着色剤、不活性微粒子などの添加剤を含有してもよい。
　なかでも難燃剤を含むメタ系アラミド繊維が好ましい。その際、かかる難燃剤としては特開平１０－２５１９８１号公報に記載されたものや、無機系の金属および担体、金属含有担体の表面を被覆したものなどが例示されるが、優れた難燃性を得る上でリン系難燃剤が好ましい。含有量としては繊維重量対比１～１５重量％が好ましい。また、難燃剤の付与方法としては、繊維の製造段階で紡糸ドープ中に添加する方法が好ましい。
　また、前記難燃性繊維において、繊維長としては３５～１１０ｍｍの範囲が好ましい。
　前記紡績糸において、総繊度は、用途に応じて、表面外観、耐熱性、熱防護性、伸縮性、風合いなどを考慮して適宜選択すればよく、特に紡績糸の総繊度は５８ｄｔｅｘ（英式綿番手１００番単糸相当）～５８０ｄｔｅｘ（英式綿番手１０番手相当）の範囲が好ましい。
　また、前記紡績糸の単繊維繊度は、良好な紡績工程通過性、柔軟性の求められている衣料用途への使用の観点から、０．６～５．５ｄｔｅｘの範囲が好ましい。
　前記紡績糸において、撚係数Ｋは布帛の物性および柔軟性の点から１９０～３５０の範囲内であることが好ましい。ただし、撚係数Ｋ＝Ｔ×√Ｄであり、Ｔは撚数（回／２．５４ｃｍ）、Ｄは紡績糸の総繊度（ｄｔｅｘ）である。また、前記紡績糸は単糸であってもよいし双糸であってもよい。
　本発明において、複合繊維は２成分がサイドバイサイド型または偏心芯鞘型に貼り合わされた複合繊維である。本発明の織物に含まれる複合糸が、前記の紡績糸だけでなくかかる複合繊維からなる糸条をも含むことにより、布帛の熱処理工程で複合繊維からなる糸条が３次元コイル捲縮の形態をとり、複合糸に伸縮性が付与され、その結果、織物にも伸縮性が付与される。
　ここで、前記複合繊維を形成する２成分としては、ポリエステル／ポリエステル、ポリエステル／ナイロンなどの組合せが例示される。より具体的には、ポリトリメチレンテレフタレート／ポリトリメチレンテレフタレート、ポリトリメチレンテレフタレート／ポリエチレンテレフタレート、ポリエチレンテレフタレート／ポリエチレンテレフタレートなどの組合せが好ましい。その際、固有粘度を互いに異ならせることが好ましい。また、酸化防止剤、紫外線吸収剤、熱安定剤、難燃剤、酸化チタン、着色剤、不活性微粒子などの添加剤を含有してもよい。
　特に、前記複合繊維が難燃剤を含むことが好ましい。その際、難燃剤としては、リン系難燃剤が好ましい。また、難燃剤の付与方法としては、吸尽法や、バインダー樹脂とともに付与する方法などが好ましい。
　前記複合繊維からなる糸条において、その形状は特に限定されず、長繊維（マルチフィラメント）でもよいし短繊維（紡績糸）でもよいが、優れた伸縮性を得る上で長繊維（マルチフィラメント）が好ましい。また、前記複合繊維を構成する成分の少なくとも１成分がリサイクル由来または植物由来であることが好ましい。例えば、リサイクル由来のポリエチレンテレフタレートや植物由来のポリトリメチレンテレフタレートなどが例示される。
　前記複合繊維からなる糸条において、総繊度、単繊維繊度は用途に応じて適宜選定され、総繊度２０～２００ｄｔｅｘ、単繊維繊度０．５～１０．０ｄｔｅｘの範囲が好ましい。
　本発明において、複合糸には前記の紡績糸と前記の複合繊維からなる糸条とが含まれる。その際、複合糸に含まれる複合繊維からなる糸条の重量比率としては、難燃性と伸縮性とを両立させる上で、複合繊維からなる糸条の重量比率が、複合糸重量対比４０～６０重量％（より好ましくは４５～５５重量％）の範囲内であることが重要である。なお、複合糸に他の繊維を含ませてもよい。
　前記複合糸において、合撚糸条であることが重要である。より具体的には、前記の紡績糸と前記の複合繊維からなる糸条とを用いて、市販のアップツイスタ、イタリ式撚糸機、ダブルツイスタなどを使用して、合撚することが好ましい。その際、撚数は撚係数Ｋが２７０～４００であることが重要である。ただし、撚係数Ｋ＝Ｔ×√Ｄであり、Ｔは撚数（回／２．５４ｃｍ）、Ｄは複合糸の総繊度（ｄｔｅｘ）である。撚係数が２７０を下回ると、複合繊維の収縮による凹凸が織物表面に発現し、外観品位が悪化するとともに抗ピリング性が悪化するおそれがある。逆に４００を上回ると、複合糸の熱収縮が阻害され、伸長率が悪化するおそれがある。
　撚り止めセットは要求される品質により実施してもよい。複合糸（合撚糸）の撚り止めセットは、通常の紡績糸のセットに用いられる真空スチームセットを用いることができる。複合合撚糸のセット時の温度は、５０～９５℃（より好ましくは５０～８５℃）の範囲が好ましい。複合糸（合撚糸）の撚り止めセット温度が高過ぎると、最終的に得られる布帛の伸縮性が損なわれるおそれがある。
　本発明の織物はかかる複合糸を用いてなる織物である。その際、前記複合糸が織物の経糸および緯糸に配されていてもよいが、経糸および緯糸のうちどちらか一方のみ（好ましくは緯糸）に配されることが好ましい。特に、緯糸に前記複合糸が全量配され、経糸には、前記のような紡績糸が配されることが好ましい。
　ここで、優れた難燃性を得る上で、前記難燃性繊維の重量比率が織物重量に対して６０重量％以上（より好ましくは６５～８４重量％）の範囲内であることが好ましい。前記難燃性繊維の重量比率が６０重量％未満の場合、難燃性が低下するおそれがある。
　また、前記複合繊維の重量比率が織物重量に対して１６重量％以上（より好ましくは１６～３５重量％）であることが好ましい。前記複合繊維の重量比率が織物重量に対して３０重量％を越える場合、炎が複合繊維に沿って伝わりやすく燃焼しやすくなるおそれがある。逆に、前記複合繊維の重量比率が２０重量％未満の場合、織物の伸縮性が低下するばかりか、抗ピリング性が悪化するおそれがある。
　織物の組織としては、平組織、綾組織、朱子組織などが例示される。特に、平組織、２／１綾、２／２綾組織などが好ましい。これ以上浮数の多い組織では、伸縮率は高いものの、抗ピリング性が悪化するおそれがある。
　次いで、かかる織物に、精錬、リラックス、染色処理、セットなどの熱処理を施すことにより、織物に含まれる、前記複合繊維からなる糸条が３次元コイル捲縮の形態をとり、布帛に伸縮性が付与される。特に染色において液流染色機にて１３０℃まで昇温し織物を循環させることは、織物を幅方向に収縮させ、高い伸縮性を与えるため好ましいことである。
　かかる織物には、吸水加工、撥水加工、起毛加工、難燃加工、紫外線遮蔽あるいは抗菌剤、消臭剤、防虫剤、蓄光剤、再帰反射剤、マイナスイオン発生剤等の機能を付与する各種加工を付加適用してもよい。
　ここで、吸尽法やバインダー樹脂により、織物に難燃加工を施し、前記複合繊維に難燃剤を含ませることは好ましいことである。特に、前記難燃性繊維がリン系難燃剤などの難燃剤を含むメタ系アラミド繊維であり、かつ前記複合繊維がリン系難燃剤などの難燃剤を含むと、織物の難燃性がさらに向上し好ましい。
　かくして得られた織物は、前記の構成を有するので、難燃性だけでなく優れた伸縮性と抗ピリング性と良好な外観品位をも有する。
　ここで、織物の伸縮性としては、緯方向の伸長率が１０～５０％の範囲内であることが好ましい。また、織物の伸長回復率としては、緯方向の伸長回復率が７０％以上（より好ましくは７３～９９％）であることが好ましい。また、難燃性としては、織物において、ＪＩＳ Ｋ７２０１により測定される限界酸素指数が２５以上（より好ましくは２５～４０）であることが好ましい。また、残炎時間（秒）が２秒以下（より好ましくは０～１秒）であることが好ましい。また、抗ピリング性としては、ＪＩＳ　Ｌ１０７６－２０１２　Ａ法（ＩＣＩ １０ｈｒ）にしたがって測定し、４級以上（より好ましくは４．５～５級）であることが好ましい。また、外観品位としては、北窓太陽光線を約４５°の角度で織物の表面に当て、試験者が織物の表面に対して垂直に見て、複合繊維の収縮に起因する凹凸（シボ）が判別できない程度であることが好ましい。
　また、優れた難燃性を得る上で目付けは１８０ｇ／ｍ２以上（より好ましくは２００～５００ｇ／ｍ２、特に好ましくは２２０～２６０ｇ／ｍ２）であることが好ましい。
　次に、本発明の繊維製品は前記の織物を用いてなるものである。かかる繊維製品は前記の織物を用いているので、難燃性だけでなく優れた伸縮性と抗ピリング性と良好な外観品位をも有する。かかる繊維製品には、消防服、防火服、執務服、モータースポーツ用レーシングスーツ、作業服、手袋、帽子、ベスト、各種産業資材（シート、テント、膜材、幌、建築資材、住宅材、車両内装材など）などが含まれる。また、前記作業服には、製鉄所や鉄鋼工場の作業用作業服、溶接作業用作業服、防爆エリアにおける作業服などが含まれる。また、前記手袋には、精密部品を取り扱う航空機産業、情報機器産業、精密機器産業などで使用される作業手袋などが含まれる。
　次に本発明の実施例および比較例を詳述するが、本発明はこれらによって限定されるものではない。なお、実施例中の各測定項目は下記の方法で測定した。
（１）難燃性
　ＪＩＳ　Ｋ７２０１：１９９９（酸素指数法による高分子材料の燃焼試験法）により限界酸素指数（ＬＯＩ）を測定し、難燃性の指標とした。
（２）伸縮性
　ＪＩＳ　Ｌ１０９６－２０１０（Ｂ法、定荷重法）にしたがって、伸長率および伸長回復率を測定した。
（３）燃焼性
　ＪＩＳ　Ｌ１０９１－１９９９　Ａ－４法付属書８にしたがって、残炎時間（秒）、残じん時間（秒）、炭化長（ｃｍ）を測定し、燃焼性の指標とした。
（４）抗ピリング性試験
　ＪＩＳ　Ｌ１０７６－２０１２　Ａ法（ＩＣＩ １０ｈｒ）にしたがって、抗ピリング性(級)の測定を行った。
（５）外観品位
　北窓太陽光線を約４５°の角度で織物の表面に当て、試験者が織物の表面に対して垂直に見て、複合繊維の収縮に起因する凹凸（シボ）が判別できない程度であれば外観品位を「良い」、判別できる場合は外観品位を「悪い」、の２段階で判定した。
（６）繊度
　ＪＩＳ　Ｌ１０１３－２０１０　正量繊度により測定した。
（７）沸水収縮率
　ＪＩＳ　Ｌ１０１３－２０１０　Ｂ法によりＢＷＳ（％）を測定した。
（８）固有粘度
　オルソクロロフェノール溶媒中において、温度３０℃にて測定した。
（９）織物の目付け
　ＪＩＳ　Ｌ１０９６：２０１０ Ａ法に従って測定した。
（紡績糸１）
　紡績工程において、単繊維繊度２．２ｄｔｅｘ、カット長（繊維長）５１ｍｍ、ＬＯＩが３３のポリメタフェニレンイソフタルアミド繊維（帝人株式会社製「コーネックス」（商標名））からなる短繊維と、単繊維繊度１．７ｄｔｅｘ、カット長（繊維長）５１ｍｍ、ＬＯＩが２５のコパラフェニレン・３、４’オキシジフェニレンテレフタルアミド繊維（帝人株式会社製「テクノーラ」（商標名））からなる短繊維を重量割合（前者：後者）９５：５の割合で混紡し、Ｚ方向撚数２４回／２．５４ｃｍ（撚係数＝２９２）、英式綿番手で４０番単糸（総繊度１４７．６ｄｔｅｘ）を得た。
（紡績糸２）
　紡績工程において、単繊維繊度２．２ｄｔｅｘ、カット長（繊維長）５１ｍｍ、ＬＯＩが３３であるポリメタフェニレンイソフタルアミド繊維（帝人株式会社製「コーネックス」（商標名））からなる短繊維と、単繊維繊度１．７ｄｔｅｘ、カット長（繊維長）５１ｍｍ、ＬＯＩが２５であるコパラフェニレン・３、４’オキシジフェニレンテレフタルアミド繊維（帝人株式会社製「テクノーラ」（商標名））からなる短繊維を重量割合（前者：後者）９５：５の割合で混紡し、Ｚ方向撚数１９．８回／２．５４ｃｍ（撚係数＝２５４）、英式綿番手で３６番単糸（総繊度１６４ｄｔｅｘ）を得た。
（複合繊維１）
　複合繊維からなる糸条として、ポリトリメチレンテレフタレートとポリエチレンテレフタレートとを偏心芯鞘型に貼り合せた総繊度１６７ｄｔｅｘ／７２フィラメント、伸度２６％、沸水収縮率５５．０％のマルチフィラメント（長繊維）を用意した。
（複合繊維２）
　複合繊維からなる糸条として、固有粘度１．２６のポリトリメチレンテレフタレートと、固有粘度０．９２のポリトリメチレンテレフタレートとを、常法によりサイドバイサイド型紡糸口金にて紡糸、延伸してサイドバイサイド型に貼り合せた総繊度４０ｄｔｅｘ／２４フィラメント、伸度２６％、沸水収縮率５５．０％のマルチフィラメント（長繊維）を用意した。
（複合繊維３）
　複合繊維からなる糸条として、固有粘度１．２６のポリトリメチレンテレフタレートと、固有粘度０．９２のポリトリメチレンテレフタレートとを、常法によりサイドバイサイド型紡糸口金にて紡糸、延伸してサイドバイサイド型に貼り合せた総繊度８４ｄｔｅｘ／２４フィラメント、伸度２６％、沸水収縮率５５．０％のマルチフィラメント（長繊維）を用意した。
　　［実施例１］
　紡績糸１を２本合糸し、ダブルツイスタ―にて表１に記載の上撚数にてS方向に撚糸した後、真空スチームセット機にてセット温度１２０℃、セット時間２０分の条件で撚り止めセットし、経糸を得た。
　一方、紡績糸１と複合繊維１を合糸し、ダブルツイスタ―にて表３に記載の撚数でS方向に撚糸した後、真空スチームセット機にてセット温度７０℃、セット時間２０分の条件で撚り止めセットし緯糸を得た。
　次いで、前記の経糸と緯糸を用い、表１に記載の組織、経緯密度で製織し、織物を毛焼－精練‐セット（温度１５０℃×時間３０秒）し、液流染色機により常温から２℃／分の速度で昇温し、１３０℃で３０分間染色処理した。染色後、乾燥し、そのままの幅でセット（温度１８０℃×時間３０秒）した。評価結果を表１に示す。
　　［実施例２～５、比較例１～７］
　実施例１において、表１、表２の通り、糸種や撚り係数を変えること以外は実施例１と同様にした。評価結果を表１、表２に示す。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
　本発明によれば、難燃性だけでなく優れた伸縮性と抗ピリング性と良好な外観品位をも有する織物、および該織物を用いてなる繊維製品が提供され、その工業的価値は極めて大である。
 

Claims (12)

  1. 　ＪＩＳ　Ｋ７２０１により測定される限界酸素指数が２５以上の難燃性繊維を含む紡績糸と、２成分がサイドバイサイド型または偏心芯鞘型に貼り合わされた複合繊維からなる糸条とを含む複合糸を用いてなる織物であり、
    　前記複合糸において、前記複合繊維からなる糸条の重量比率が４０～６０重量％であり、
    　前記複合糸に、下記式で定義する撚係数Ｋが２７０～４００で撚りが施されていることを特徴とする織物。
    撚係数Ｋ＝Ｔ×√Ｄ
    ただし、Ｔは撚数（回／２．５４ｃｍ）、Ｄは複合糸の総繊度（ｄｔｅｘ）である。
  2. 　織物において、前記難燃性繊維の重量比率が織物重量に対して６５～８４重量％の範囲内であり、かつ前記複合繊維の重量比率が織物重量に対して１６～３５重量％の範囲内である、請求項１に記載の織物。
  3. 　前記難燃性繊維が、メタ系アラミド繊維、パラ系アラミド繊維、ポリパラフェニレンベンズオキサゾール繊維、ポリベンゾイミダゾール繊維、ポリイミド繊維、ポリエーテルイミド繊維、ポリアミドイミド繊維、炭素繊維、ポリフェニレンサルファイド繊維、ポリ塩化ビニル繊維、難燃レーヨン、モダアクリル繊維、難燃アクリル繊維、難燃ポリエステル繊維、難燃ビニロン繊維、メラミン繊維、フッ素繊維、難燃ウール、および難燃コットンからなる群から選ばれた１種類以上の繊維である、請求項1に記載の織物。
  4. 　前記複合繊維からなる糸条が、単繊維繊度０．５～１０．０ｄｔｅｘ、かつ総繊度２０～２００ｄｔｅｘのマルチフィラメントである、請求項1に記載の織物。
  5. 　前記複合繊維を構成する成分の少なくとも１成分がリサイクル由来または植物由来である、請求項1に記載の織物。
  6. 　前記難燃性繊維が難燃剤を含むメタ系アラミド繊維であり、かつ前記複合繊維が難燃剤を含む、請求項１に記載の織物。
  7. 　前記複合糸が織物の緯糸に配され、緯方向の伸長率が1０～５０％の範囲内である、請求項１に記載の織物。
  8. 　前記複合糸が織物の緯糸に配され、緯方向の伸長回復率が７０％以上である、請求項１に記載の織物。
  9. 　ＪＩＳ　Ｌ１０７６－２０１２　Ａ法　ＩＣＩ型１０時間で測定される抗ピリング性が４級以上である、請求項１に記載の織物。
  10. 　表面に前記複合繊維の収縮に起因する凹凸がない、請求項１に記載の織物。
  11. 　織物において、ＪＩＳ　Ｋ７２０１により測定される限界酸素指数が２５以上である、請求項１に記載の織物。
  12. 　請求項１～１１のいずれかに記載された織物を用いてなり、消防服、防火服、執務服、モータースポーツ用レーシングスーツ、作業服、手袋、帽子、ベスト、シート、テント、膜材、幌、建築資材、住宅材、および車両内装材からなる群より選択される繊維製品。
     
PCT/JP2023/031499 2022-09-05 2023-08-30 織物および繊維製品 WO2024053510A1 (ja)