WO2024018993A1 - Film de démoulage à couche antistatique - Google Patents

Film de démoulage à couche antistatique Download PDF

Info

Publication number
WO2024018993A1
WO2024018993A1 PCT/JP2023/025924 JP2023025924W WO2024018993A1 WO 2024018993 A1 WO2024018993 A1 WO 2024018993A1 JP 2023025924 W JP2023025924 W JP 2023025924W WO 2024018993 A1 WO2024018993 A1 WO 2024018993A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
antistatic
antistatic layer
mass
less
Prior art date
Application number
PCT/JP2023/025924
Other languages
English (en)
Japanese (ja)
Inventor
良太 粂井
由佳 天野
悠介 柴田
充晴 中谷
Original Assignee
東洋紡株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東洋紡株式会社 filed Critical 東洋紡株式会社
Publication of WO2024018993A1 publication Critical patent/WO2024018993A1/fr

Abstract

La présente invention vise à proposer un excellent film de démoulage pour la production d'une feuille verte de céramique, le film de démoulage permettant à la fois de réduire la charge électrostatique pendant le déroulement et d'éviter les trous d'épingle, les variations locales d'épaisseur et autres, même si une feuille verte de céramique est amincie.　À cet effet, la présente invention concerne un film de démoulage ayant une couche antistatique, le film de démoulage comprenant un matériau de base, une couche antistatique qui est disposée sur une surface du matériau de base avec une première couche fonctionnelle interposée entre les deux, et une couche de démoulage qui est disposée sur l'autre côté de surface du matériau de base. En ce qui concerne ce film de démoulage ayant une couche antistatique, la couche antistatique est formée d'une composition de formation de couche antistatique qui contient un agent antistatique et une résine liante thermodurcissable ; l'agent antistatique contient un polymère conducteur ; et le côté sur lequel la couche antistatique est disposée a une résistivité superficielle (logΩ/□) de 3 à 10.
PCT/JP2023/025924 2022-07-19 2023-07-13 Film de démoulage à couche antistatique WO2024018993A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2022-114715 2022-07-19
JP2022114715 2022-07-19

Publications (1)

Publication Number Publication Date
WO2024018993A1 true WO2024018993A1 (fr) 2024-01-25

Family

ID=89617662

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2023/025924 WO2024018993A1 (fr) 2022-07-19 2023-07-13 Film de démoulage à couche antistatique

Country Status (1)

Country Link
WO (1) WO2024018993A1 (fr)

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016133092A1 (fr) * 2015-02-18 2016-08-25 リンテック株式会社 Film de démoulage
JP2017218507A (ja) * 2016-06-07 2017-12-14 三菱ケミカル株式会社 積層ポリエステルフィルム

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016133092A1 (fr) * 2015-02-18 2016-08-25 リンテック株式会社 Film de démoulage
JP2017218507A (ja) * 2016-06-07 2017-12-14 三菱ケミカル株式会社 積層ポリエステルフィルム

Similar Documents

Publication Publication Date Title
JP6791329B2 (ja) セラミックグリーンシート製造用離型フィルム
JP7306395B2 (ja) 離型フィルム
JP6610810B2 (ja) セラミックグリーンシート製造用離型フィルム
JP7417878B2 (ja) 離型フィルム
JP2024028476A (ja) セラミックグリーンシート製造用離型フィルム
JP7338233B2 (ja) セラミックグリーンシート製造用離型フィルム
JP7310289B2 (ja) セラミックグリーンシート製造用離型フィルム
TWI792241B (zh) 離型膜、離型膜之製造方法、陶瓷生胚之製造方法以及陶瓷電容器之製造方法
WO2024018993A1 (fr) Film de démoulage à couche antistatique
JP7327602B2 (ja) 離型フィルム
WO2022004784A1 (fr) Film de traitement

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23842916

Country of ref document: EP

Kind code of ref document: A1