WO2024000919A1 - Procédé et système de préparation de poudre de titane ou d'alliage de titane ayant un degré élevé de sphéricité et un faible incrément d'oxygène - Google Patents

Procédé et système de préparation de poudre de titane ou d'alliage de titane ayant un degré élevé de sphéricité et un faible incrément d'oxygène Download PDF

Info

Publication number
WO2024000919A1
WO2024000919A1 PCT/CN2022/124577 CN2022124577W WO2024000919A1 WO 2024000919 A1 WO2024000919 A1 WO 2024000919A1 CN 2022124577 W CN2022124577 W CN 2022124577W WO 2024000919 A1 WO2024000919 A1 WO 2024000919A1
Authority
WO
WIPO (PCT)
Prior art keywords
titanium alloy
powder
titanium
atomization
wire
Prior art date
Application number
PCT/CN2022/124577
Other languages
English (en)
Chinese (zh)
Inventor
王健
赵博深
任志豪
李永华
张生滨
陈小龙
Original Assignee
南京尚吉增材制造研究院有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from CN202210774191.1A external-priority patent/CN115283683B/zh
Priority claimed from CN202221686145.8U external-priority patent/CN218283735U/zh
Application filed by 南京尚吉增材制造研究院有限公司 filed Critical 南京尚吉增材制造研究院有限公司
Publication of WO2024000919A1 publication Critical patent/WO2024000919A1/fr

Abstract

La présente invention concerne un procédé et un système de préparation de poudre de titane ou d'alliage de titane ayant un degré élevé de sphéricité et un faible incrément d'oxygène. Un matériau de fil en alliage de titane à haute propreté et un matériau en barre sont utilisés en tant que matières premières ; une source de chaleur à plasma à haute énergie chauffe le matériau de fil sous la protection d'une atmosphère inerte ; des gouttelettes de métal fondu tombent sur une surface d'extrémité du matériau en barre en rotation à grande vitesse et sont projetées par force centrifuge, et subissent séquentiellement des étapes telles qu'une étape de sphéroïdisation, une étape de solidification et une étape de refroidissement le long d'une piste de vol, de telle sorte que des défauts tels qu'une poudre satellite, une poudre de forme spéciale et une poudre creuse provoqués par un refroidissement rapide de particules et une interférence de flux de gaz secondaire sont efficacement évités sans impact d'écoulement de jet à grande vitesse. L'ensemble du processus de préparation de poudre et de post-traitement de criblage est effectué sous la protection d'une atmosphère inerte, et l'incrément d'oxygène de poudre est efficacement limité, ce qui facilite l'obtention de la poudre de titane ou de l'alliage de titane ayant un degré élevé de sphéricité et un faible incrément d'oxygène.
PCT/CN2022/124577 2022-07-01 2022-10-11 Procédé et système de préparation de poudre de titane ou d'alliage de titane ayant un degré élevé de sphéricité et un faible incrément d'oxygène WO2024000919A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
CN202210774191.1A CN115283683B (zh) 2022-07-01 2022-07-01 高球形度及低氧增量钛合金粉末的制备方法及系统
CN202221686145.8U CN218283735U (zh) 2022-07-01 2022-07-01 高球形度及低氧增量钛或钛合金粉末的制备系统
CN202221686145.8 2022-07-01
CN202210774191.1 2022-07-01

Publications (1)

Publication Number Publication Date
WO2024000919A1 true WO2024000919A1 (fr) 2024-01-04

Family

ID=89383795

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2022/124577 WO2024000919A1 (fr) 2022-07-01 2022-10-11 Procédé et système de préparation de poudre de titane ou d'alliage de titane ayant un degré élevé de sphéricité et un faible incrément d'oxygène

Country Status (1)

Country Link
WO (1) WO2024000919A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6280205A (ja) * 1985-10-01 1987-04-13 Kobe Steel Ltd 金属微粉末の製造方法
CN105618775A (zh) * 2016-04-11 2016-06-01 西安欧中材料科技有限公司 一种制备Ti-6Al-7Nb医用钛合金球形粉末的方法
CN106378460A (zh) * 2016-09-22 2017-02-08 成都优材科技有限公司 制备纯钛或钛合金粉末的等离子雾化方法及设备
CN109676148A (zh) * 2019-01-28 2019-04-26 深圳微纳增材技术有限公司 3d打印用金属粉末的制备装置
CN114226740A (zh) * 2021-12-27 2022-03-25 南京尚吉增材制造研究院有限公司 离心雾化制粉的方法及装置

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6280205A (ja) * 1985-10-01 1987-04-13 Kobe Steel Ltd 金属微粉末の製造方法
CN105618775A (zh) * 2016-04-11 2016-06-01 西安欧中材料科技有限公司 一种制备Ti-6Al-7Nb医用钛合金球形粉末的方法
CN106378460A (zh) * 2016-09-22 2017-02-08 成都优材科技有限公司 制备纯钛或钛合金粉末的等离子雾化方法及设备
CN109676148A (zh) * 2019-01-28 2019-04-26 深圳微纳增材技术有限公司 3d打印用金属粉末的制备装置
CN114226740A (zh) * 2021-12-27 2022-03-25 南京尚吉增材制造研究院有限公司 离心雾化制粉的方法及装置

Similar Documents

Publication Publication Date Title
CN106378460B (zh) 制备球形纯钛或钛合金粉末的等离子雾化方法及设备
CN110480024B (zh) 一种基于VIGA工艺制备CuCrZr球形粉的方法
CN107096925B (zh) 一种新型的等离子体雾化制备球型粉末系统
CN107900366B (zh) 气雾化连续制备3d打印用钛或钛合金粉末的装置及方法
JP5837731B2 (ja) 清浄で急速凝固された合金を製造するための装置及び方法
CN106166617A (zh) 一种3d打印用钛合金粉末的制备方法
CN107900367B (zh) 一种3d打印用钛及钛合金粉末的新型雾化器
US11839918B2 (en) Method and apparatus for producing high purity spherical metallic powders at high production rates from one or two wires
CN106623959A (zh) 一种增材制造用Waspalloy球形粉末的制备方法
CN105689730A (zh) 一种制备Inconel 625合金球形粉末的方法
CN106956008A (zh) 一种3D打印用Hastelloy X合金粉末的制备方法
CN110405220A (zh) 一种基于等离子旋转雾化法制备GRCop-84球形粉的方法
CN106964782B (zh) 一种制备球形铌合金粉末的方法
CN113145855A (zh) 一种电弧制备高熔点合金粉末的装置和方法
CA1233307A (fr) Methode et installation pour la fabrication de poudres d'alliages
CN102950293A (zh) 纳米铝粉的生产方法
CN113414398A (zh) 一种等离子体制备金属粉末的设备及其方法
US5120352A (en) Method and apparatus for making alloy powder
CN108380895A (zh) 一种Ti-Al-V-Fe-O合金粉末的制备方法及应用
CN114226740B (zh) 离心雾化制粉的方法及装置
CN114054775B (zh) 时效强化型镍基高温合金3d打印工艺及制得的3d打印件
KR20210071150A (ko) 금속 분말 및 이의 가공장치, 가공방법
CN208696304U (zh) 一种低压直流等离子枪制备3d打印用钛粉的装置
CN112658271B (zh) 一种高效复合式气雾化制粉装置及方法
WO2024000919A1 (fr) Procédé et système de préparation de poudre de titane ou d'alliage de titane ayant un degré élevé de sphéricité et un faible incrément d'oxygène

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22949004

Country of ref document: EP

Kind code of ref document: A1