WO2023106097A1 - Adhésif réactif, film stratifié et emballage - Google Patents

Adhésif réactif, film stratifié et emballage Download PDF

Info

Publication number
WO2023106097A1
WO2023106097A1 PCT/JP2022/043264 JP2022043264W WO2023106097A1 WO 2023106097 A1 WO2023106097 A1 WO 2023106097A1 JP 2022043264 W JP2022043264 W JP 2022043264W WO 2023106097 A1 WO2023106097 A1 WO 2023106097A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
adhesive
reactive adhesive
polyol
acid
Prior art date
Application number
PCT/JP2022/043264
Other languages
English (en)
Japanese (ja)
Inventor
常行 手島
寛知 永田
千勇 徳永
Original Assignee
Dic株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dic株式会社 filed Critical Dic株式会社
Priority to JP2023514036A priority Critical patent/JPWO2023106097A1/ja
Publication of WO2023106097A1 publication Critical patent/WO2023106097A1/fr

Abstract

L'invention concerne un adhésif réactif satisfaisant à (1) et (2) ; et un film stratifié dans lequel une pluralité de films de base contenant une résine oléfinique sont stratifiés et collés à l'aide d'un adhésif réactif, l'adhésif réactif satisfaisant à (1) et (2). (1) Après qu'une résine polyoléfinique et l'adhésif réactif sont mélangés selon un rapport de 96:4 et malaxés à l'état fondu à 240 °C pendant 3 minutes, la granulométrie de l'adhésif est de 20 μm ou moins. (2) L'E' à 200 °C d'un film durci obtenu par durcissement de l'adhésif réactif à 40 °C pendant 72 heures est compris dans la plage 1,0×105-3,0×106.
PCT/JP2022/043264 2021-12-09 2022-11-24 Adhésif réactif, film stratifié et emballage WO2023106097A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2023514036A JPWO2023106097A1 (fr) 2021-12-09 2022-11-24

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2021199940 2021-12-09
JP2021-199940 2021-12-09

Publications (1)

Publication Number Publication Date
WO2023106097A1 true WO2023106097A1 (fr) 2023-06-15

Family

ID=86730364

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2022/043264 WO2023106097A1 (fr) 2021-12-09 2022-11-24 Adhésif réactif, film stratifié et emballage

Country Status (2)

Country Link
JP (1) JPWO2023106097A1 (fr)
WO (1) WO2023106097A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7499395B1 (ja) 2023-10-13 2024-06-13 日本マタイ株式会社 積層シートの製造方法

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2006008160A (ja) * 2004-06-24 2006-01-12 Nissan Motor Co Ltd 多層容器
KR101492789B1 (ko) * 2013-08-14 2015-02-23 전승호 재활용성 폴리올레핀계 다기능성 식품포장재 및 이의 제조방법
WO2018096377A2 (fr) * 2016-11-28 2018-05-31 "Jáger Invest" Kereskedelmi, Szolgáltató És Ingatlanhasznosító Kft. Agglomérat polymère homogène contenant du caoutchouc broyé, des déchets plastiques thermodurcis renforcés et des déchets thermoplastiques
JP2018154701A (ja) * 2017-03-16 2018-10-04 東ソー株式会社 樹脂組成物及びこれよりなる積層体
WO2021060308A1 (fr) * 2019-09-24 2021-04-01 株式会社クラレ Stratifié
JP2021088184A (ja) * 2019-11-25 2021-06-10 東洋インキＳｃホールディングス株式会社 包装材及び包装容器

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2006008160A (ja) * 2004-06-24 2006-01-12 Nissan Motor Co Ltd 多層容器
KR101492789B1 (ko) * 2013-08-14 2015-02-23 전승호 재활용성 폴리올레핀계 다기능성 식품포장재 및 이의 제조방법
WO2018096377A2 (fr) * 2016-11-28 2018-05-31 "Jáger Invest" Kereskedelmi, Szolgáltató És Ingatlanhasznosító Kft. Agglomérat polymère homogène contenant du caoutchouc broyé, des déchets plastiques thermodurcis renforcés et des déchets thermoplastiques
JP2018154701A (ja) * 2017-03-16 2018-10-04 東ソー株式会社 樹脂組成物及びこれよりなる積層体
WO2021060308A1 (fr) * 2019-09-24 2021-04-01 株式会社クラレ Stratifié
JP2021088184A (ja) * 2019-11-25 2021-06-10 東洋インキＳｃホールディングス株式会社 包装材及び包装容器

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7499395B1 (ja) 2023-10-13 2024-06-13 日本マタイ株式会社 積層シートの製造方法

Also Published As

Publication number Publication date
JPWO2023106097A1 (fr) 2023-06-15

Similar Documents

Publication Publication Date Title
WO2023106097A1 (fr) Adhésif réactif, film stratifié et emballage
JP6763499B1 (ja) 反応性接着剤、積層体、及び包装体
JP2022055658A (ja) 反応性接着剤、積層フィルム、及び包装材
WO2023112687A1 (fr) Agent de revêtement durcissable à deux composants, corps stratifié et matériau d'emballage
JP6892020B1 (ja) 反応性接着剤、積層フィルム、及び包装体
JP6733835B1 (ja) 反応性接着剤、積層体、及び包装体
JP7332075B1 (ja) 接着剤、積層体、包装材
JP7173389B2 (ja) 反応型接着剤、積層体及び包装体
JP7347708B2 (ja) 積層フィルム及び包装材
JP7396547B2 (ja) 接着剤、積層体、積層体の製造方法、包装材
JP7036293B1 (ja) 接着剤、積層体、包装材
JP7364122B1 (ja) 積層フィルム及び包装材
JP7184181B2 (ja) 接着剤組成物、積層体、及び包装体
WO2022138188A1 (fr) Corps multicouche barrière aux gaz et matériau d'emballage
WO2023112688A1 (fr) Adhésif, stratifié et matériau d'emballage
WO2024122292A1 (fr) Agent adhésif, stratifié et matériau d'emballage
WO2024101165A1 (fr) Composition de barrière contre les gaz, agent de revêtement et corps multicouche
WO2024135514A1 (fr) Adhésif durcissable en deux parties, corps multicouche et emballage
CN110894418A (zh) 双组份型粘接剂、层叠体和包装材料

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 2023514036

Country of ref document: JP

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22904028

Country of ref document: EP

Kind code of ref document: A1