WO2023089480A1 - Échangeur de chaleur et procédé de fabrication - Google Patents

Échangeur de chaleur et procédé de fabrication Download PDF

Info

Publication number
WO2023089480A1
WO2023089480A1 PCT/IB2022/060983 IB2022060983W WO2023089480A1 WO 2023089480 A1 WO2023089480 A1 WO 2023089480A1 IB 2022060983 W IB2022060983 W IB 2022060983W WO 2023089480 A1 WO2023089480 A1 WO 2023089480A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
thickness
heat exchanger
plates
brazing
Prior art date
Application number
PCT/IB2022/060983
Other languages
English (en)
Inventor
Giorgio Girondi
Original Assignee
Ufi Innovation Center S.R.L.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from IT102021000029129A external-priority patent/IT202100029129A1/it
Application filed by Ufi Innovation Center S.R.L. filed Critical Ufi Innovation Center S.R.L.
Publication of WO2023089480A1 publication Critical patent/WO2023089480A1/fr

Abstract

L'invention concerne un échangeur de chaleur (1) pouvant être relié fluidiquement à un système de circulation de fluide de travail, de préférence à base d'huile, et à un système de circulation d'eau. L'échangeur de chaleur (1) s'étend le long d'un axe vertical (V-V) et de deux axes longitudinaux (X-X ; Y-Y) comprenant, le long dudit axe vertical (V-V), une plaque supérieure (2), une pluralité de plaques intermédiaires (3) et une plaque inférieure (4), l'empilement desdites plaques délimitant une zone d'écoulement d'eau (5), dans laquelle circule de l'eau, et une zone d'écoulement de fluide de travail (6), dans laquelle circule un fluide de travail. Lesdites plaques sont mutuellement reliées au moyen d'un procédé de brasage sous vide. En outre, les plaques intermédiaires (3) faisant face à la zone d'écoulement d'eau (5) comprennent une face en regard de l'eau respective et lesdites plaques intermédiaires (3) comprennent un film (35) délimitant ladite face d'eau, ledit film (35) ayant une épaisseur de 19 % à 22 % de l'épaisseur de la plaque intermédiaire (3) et étant constitué d'un alliage d'aluminium contenant du zinc.
PCT/IB2022/060983 2021-11-17 2022-11-15 Échangeur de chaleur et procédé de fabrication WO2023089480A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
IT102021000029129 2021-11-17
IT102021000029129A IT202100029129A1 (it) 2021-11-17 2021-11-17 Scambiatore di calore e metodo di produzione
IT202022000001142 2022-03-21
IT202200001142 2022-03-21

Publications (1)

Publication Number Publication Date
WO2023089480A1 true WO2023089480A1 (fr) 2023-05-25

Family

ID=84286157

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2022/060983 WO2023089480A1 (fr) 2021-11-17 2022-11-15 Échangeur de chaleur et procédé de fabrication

Country Status (1)

Country Link
WO (1) WO2023089480A1 (fr)

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2355683A (en) * 1999-09-30 2001-05-02 Denso Corp Brazed heat exchanger
EP1211473B1 (fr) * 2000-11-29 2004-02-04 Denso Corporation Echangeur de chaleur en aluminium
US7648776B2 (en) * 2005-10-13 2010-01-19 Behr Gmbh & Co. Kg Multi-layered brazing sheet
US20180017333A1 (en) * 2016-07-14 2018-01-18 Modine Manufacturing Company Brazeable Metal Sheet Material, and Heat Exchanger with Components Made of the Same
EP3414089B1 (fr) * 2016-02-09 2019-12-04 Aleris Rolled Products Germany GmbH Produit en feuille multicouches brasée en aluminium et procédé de brasage sans flux
US20210114144A1 (en) * 2018-04-16 2021-04-22 Constellium Neuf-Brisach Multlayer brazing sheet

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2355683A (en) * 1999-09-30 2001-05-02 Denso Corp Brazed heat exchanger
EP1211473B1 (fr) * 2000-11-29 2004-02-04 Denso Corporation Echangeur de chaleur en aluminium
US7648776B2 (en) * 2005-10-13 2010-01-19 Behr Gmbh & Co. Kg Multi-layered brazing sheet
EP3414089B1 (fr) * 2016-02-09 2019-12-04 Aleris Rolled Products Germany GmbH Produit en feuille multicouches brasée en aluminium et procédé de brasage sans flux
US20180017333A1 (en) * 2016-07-14 2018-01-18 Modine Manufacturing Company Brazeable Metal Sheet Material, and Heat Exchanger with Components Made of the Same
US20210114144A1 (en) * 2018-04-16 2021-04-22 Constellium Neuf-Brisach Multlayer brazing sheet

Similar Documents

Publication Publication Date Title
US6298910B1 (en) Aluminum-made heat exchanger with brazed joint portion
US5429183A (en) Plate-type heat exchanger and method of producing the same
EP1211473B1 (fr) Echangeur de chaleur en aluminium
US20070256822A1 (en) Heat exchanger
JP7485611B2 (ja) 多層ブレージングシート
US20070228113A1 (en) Method of manufacturing metallic foam based heat exchanger
US20180045469A1 (en) Heat exchanger device
JPH10185462A (ja) ハウジングレス式オイルクーラ
WO2023089480A1 (fr) Échangeur de chaleur et procédé de fabrication
US7077193B2 (en) Compound type heat exchanger
CN115038546A (zh) 多层铝钎焊板材料
CN117190757A (zh) 热交换器及其制造方法以及一种适用于钎焊的板材
JP3716887B2 (ja) オイルクーラ
IT202100029129A1 (it) Scambiatore di calore e metodo di produzione
JP3753794B2 (ja) 真空ろう付用アルミニウム材料及び該材料を用いた耐食性に優れたドロンカップ型熱交換器
JP3704178B2 (ja) ろう付用アルミニウム材料及び該材料を用いた耐食性に優れたドロンカップ型熱交換器
WO2004068055A1 (fr) Echangeur de chaleur et procede de fabrication dudit echangeur
JP2012112562A (ja) ドロンカップ型熱交換器
WO2020132202A1 (fr) Échangeur de chaleur avec tube plaqué d'alliage d'aluminium et son procédé de fabrication
JP3850082B2 (ja) アルミニウム合金製熱交換器
US5676203A (en) Heat exchanger
WO2022054558A1 (fr) Échangeur de chaleur et procédé de fabrication d'un tel échangeur de chaleur
JPH08303988A (ja) 耐食性に優れた積層型アルミニウム熱交換器
WO2021261005A1 (fr) Échangeur de chaleur et son procédé de fabrication
EP4342624A1 (fr) Module d'échangeur de chaleur, procédé de soudage d'échangeur de chaleur et ensemble échangeur de chaleur

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22809915

Country of ref document: EP

Kind code of ref document: A1