WO2023037930A1 - Matériau à dilatation thermique négative, son procédé de production et pâte - Google Patents
Matériau à dilatation thermique négative, son procédé de production et pâte Download PDFInfo
- Publication number
- WO2023037930A1 WO2023037930A1 PCT/JP2022/032588 JP2022032588W WO2023037930A1 WO 2023037930 A1 WO2023037930 A1 WO 2023037930A1 JP 2022032588 W JP2022032588 W JP 2022032588W WO 2023037930 A1 WO2023037930 A1 WO 2023037930A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- thermal expansion
- negative thermal
- hydrogen peroxide
- expansion material
- particles
- Prior art date
Abstract
Le but de la présente invention est de fournir un matériau à dilatation thermique négative comprenant du phosphotungstate de zirconium, à partir duquel une pâte ayant une viscosité appropriée peut être produite lorsque du carbonate de propylène est utilisé comme solvant. La présente invention concerne un matériau à dilatation thermique négative caractérisé en ce qu'il comprend au moins des particules de phosphotungstate de zirconium modifiées en surface qui comprennent des particules de phosphotungstate de zirconium et du peroxyde d'hydrogène présent sur les surfaces des particules de phosphotungstate de zirconium.
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2021145641 | 2021-09-07 | ||
JP2021-145641 | 2021-09-07 | ||
JP2022-116580 | 2022-07-21 | ||
JP2022116580A JP2023038904A (ja) | 2021-09-07 | 2022-07-21 | 負熱膨張材、その製造方法及びペースト |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2023037930A1 true WO2023037930A1 (fr) | 2023-03-16 |
Family
ID=85506683
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2022/032588 WO2023037930A1 (fr) | 2021-09-07 | 2022-08-30 | Matériau à dilatation thermique négative, son procédé de production et pâte |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2023037930A1 (fr) |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2011122218A1 (fr) * | 2010-03-29 | 2011-10-06 | 日本電気硝子株式会社 | Matériau d'étanchéité et pâte utilisant ce matériau |
WO2017061403A1 (fr) * | 2015-10-07 | 2017-04-13 | 日本化学工業株式会社 | Matériau à dilatation thermique négative et matériau composite le comprenant |
WO2018116890A1 (fr) * | 2016-12-22 | 2018-06-28 | ニッタ・ハース株式会社 | Composition de polissage |
JP2019067590A (ja) * | 2017-09-29 | 2019-04-25 | 日立化成株式会社 | リチウムイオン二次電池用負極材、リチウムイオン二次電池用負極及びリチウムイオン二次電池 |
WO2019087722A1 (fr) * | 2017-10-31 | 2019-05-09 | 日本化学工業株式会社 | Tungstate de phosphate de zirconium modifié, charge à expansion thermique négative et composition polymère |
WO2020091000A1 (fr) * | 2018-11-01 | 2020-05-07 | 日産化学株式会社 | Composition de polissage faisant appel à des particules de polissage ayant une haute affinité pour l'eau |
WO2020179703A1 (fr) * | 2019-03-07 | 2020-09-10 | 日本化学工業株式会社 | Tungstate de phosphate de zirconium modifié, charge de dilatation thermique négative et composition polymère |
-
2022
- 2022-08-30 WO PCT/JP2022/032588 patent/WO2023037930A1/fr unknown
Patent Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2011122218A1 (fr) * | 2010-03-29 | 2011-10-06 | 日本電気硝子株式会社 | Matériau d'étanchéité et pâte utilisant ce matériau |
WO2017061403A1 (fr) * | 2015-10-07 | 2017-04-13 | 日本化学工業株式会社 | Matériau à dilatation thermique négative et matériau composite le comprenant |
WO2018116890A1 (fr) * | 2016-12-22 | 2018-06-28 | ニッタ・ハース株式会社 | Composition de polissage |
JP2019067590A (ja) * | 2017-09-29 | 2019-04-25 | 日立化成株式会社 | リチウムイオン二次電池用負極材、リチウムイオン二次電池用負極及びリチウムイオン二次電池 |
WO2019087722A1 (fr) * | 2017-10-31 | 2019-05-09 | 日本化学工業株式会社 | Tungstate de phosphate de zirconium modifié, charge à expansion thermique négative et composition polymère |
WO2020091000A1 (fr) * | 2018-11-01 | 2020-05-07 | 日産化学株式会社 | Composition de polissage faisant appel à des particules de polissage ayant une haute affinité pour l'eau |
WO2020179703A1 (fr) * | 2019-03-07 | 2020-09-10 | 日本化学工業株式会社 | Tungstate de phosphate de zirconium modifié, charge de dilatation thermique négative et composition polymère |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP6105140B1 (ja) | 負熱膨張材及びそれを含む複合材料 | |
WO2017061403A1 (fr) | Matériau à dilatation thermique négative et matériau composite le comprenant | |
Karimi et al. | Synthesis and characterization of nanoparticles and nanocomposite of ZnO and MgO by sonochemical method and their application for zinc polycarboxylate dental cement preparation | |
DE112005000930T5 (de) | Oxynitridpulver und Verfahren zur Herstellung davon | |
US9982191B2 (en) | Suspensions of phosphates of at least one rare earth element selected from among cerium and terbium and optionally lanthanum and luminophores produced therefrom | |
KR20070015427A (ko) | 산화칼슘 분산액 및 이의 제조 방법 | |
TW201922612A (zh) | 改質磷酸鎢酸鋯、負熱膨脹填料和高分子組成物 | |
JP2020002000A (ja) | 負熱膨張材、その製造方法及び複合材料 | |
WO2017061402A1 (fr) | Procédé de production de phosphate de tungstène et de zirconium | |
CN113121228A (zh) | 黑色混合氧化物材料及其制造方法 | |
WO2013039108A1 (fr) | Procédé de production d'oxalate de baryum titanyle et procédé de production de titanate de baryum | |
JP7259231B2 (ja) | 粒子状シリカ及びその製造方法 | |
WO2023037930A1 (fr) | Matériau à dilatation thermique négative, son procédé de production et pâte | |
JP2023038904A (ja) | 負熱膨張材、その製造方法及びペースト | |
JP6839767B2 (ja) | セリウム系研磨材用原料の製造方法、及びセリウム系研磨材の製造方法 | |
JP2009138081A (ja) | 微粒子分散溶液、当該微粒子分散溶液の製造方法、及びLnOX−LnX3複合体粒子の製造方法 | |
Jaiswal et al. | Fabrication and luminescent studies of near-spherical phosphor embedded epoxy-resin nanocomposite beads | |
KR20110002445A (ko) | 실리케이트계 산화물 형광체 및 상기의 분말 제조 방법 | |
JP2008174690A (ja) | ユーロピウム賦活酸化イットリウム蛍光材料及びその製造方法 | |
Toy et al. | A colloidal method for manganese oxide addition to alumina powder and investigation of properties | |
CN116409991A (zh) | 黑色混合氧化物材料及其制造方法 | |
JP7427058B2 (ja) | 負熱膨張材、その製造方法及び複合材料 | |
JP2023038905A (ja) | 表面改質粒子及びその製造方法 | |
JP5594747B2 (ja) | 微粒子分散溶液の製造方法、及びLnOX−LnX3複合体粒子の製造方法 | |
JPH01234490A (ja) | 蛍光体および蛍光ランプ |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 22867252 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |