WO2023032794A1 - 感活性光線性又は感放射線性樹脂組成物、感活性光線性又は感放射線性膜、パターン形成方法、電子デバイスの製造方法、及び化合物 - Google Patents

感活性光線性又は感放射線性樹脂組成物、感活性光線性又は感放射線性膜、パターン形成方法、電子デバイスの製造方法、及び化合物 Download PDF

Info

Publication number
WO2023032794A1
WO2023032794A1 PCT/JP2022/031954 JP2022031954W WO2023032794A1 WO 2023032794 A1 WO2023032794 A1 WO 2023032794A1 JP 2022031954 W JP2022031954 W JP 2022031954W WO 2023032794 A1 WO2023032794 A1 WO 2023032794A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
sensitive
groups
radiation
acid
Prior art date
Application number
PCT/JP2022/031954
Other languages
English (en)
French (fr)
Inventor
太朗 三好
修平 山口
知昭 吉岡
英治 福▲崎▼
悠花 上農
Original Assignee
富士フイルム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社 filed Critical 富士フイルム株式会社
Priority to KR1020247006526A priority Critical patent/KR20240040785A/ko
Priority to JP2023545501A priority patent/JPWO2023032794A1/ja
Publication of WO2023032794A1 publication Critical patent/WO2023032794A1/ja

Abstract

本発明は、（Ａ）酸の作用により分解し極性が増大する樹脂、及び（Ｃ）活性光線又は放射線の照射によって酸を発生する化合物であって、特定の一般式で表される、化合物を含有する感活性光線性又は感放射線性樹脂組成物であって、上記樹脂（Ａ）が特定の一般式（ＡＩ）で表される繰り返し単位を含む、感活性光線性又は感放射線性樹脂組成物、これを用いた感活性光線性又は感放射線性膜、パターン形成方法、電子デバイスの製造方法、及び、化合物を提供する。

Description

感活性光線性又は感放射線性樹脂組成物、感活性光線性又は感放射線性膜、パターン形成方法、電子デバイスの製造方法、及び化合物
　本発明は、感活性光線性又は感放射線性樹脂組成物、感活性光線性又は感放射線性膜、パターン形成方法、電子デバイスの製造方法、及び化合物に関する。
　ＩＣ（Ｉｎｔｅｇｒａｔｅｄ　Ｃｉｒｃｕｉｔ、集積回路）及びＬＳＩ（ＬａｒｇｅＳｃａｌｅ　Ｉｎｔｅｇｒａｔｅｄ　ｃｉｒｃｕｉｔ、大規模集積回路）等の半導体デバイスの製造プロセスにおいては、感光性組成物を用いたリソグラフィーによる微細加工が行われている。
　リソグラフィーの方法として、感光性組成物によりレジスト膜を形成した後、得られた膜を露光して、その後、現像する方法が挙げられる。特に、近年、露光の際に、ＡｒＦエキシマレーザーに加えて、ＥＢ（Ｅｌｅｃｔｒｏｎ　Ｂｅａｍ）、ＥＵＶ（Ｅｘｔｒｅｍｅ　ｕｌｔｒａｖｉｏｌｅｔ）光を用いる検討がなされており、ＥＵＶ露光に適した感活性光線性又は感放射線性樹脂組成物の開発がなされている。
　微細なパターン形成を目的としたＥＵＶ（波長１３．５ｎｍ）、又は電子線を用いたレジストパターンの形成においては、従来のＡｒＦ（波長１９３ｎｍ）光等を用いた場合よりも各種性能において求められる要求が厳しくなっている。
　例えば、特許文献１には、（Ａ）酸解離性基含有樹脂と、（Ｃ）特定の一般式で表される化合物と、を含有する感放射線性樹脂組成物が開示されている。
　特許文献２には、フェノール性水酸基を有する構造単位を含む樹脂、及び特定の式で表される化合物を含む感放射線性樹脂組成物が開示されている。
国際公開第２０１０／１３４４７７号 国際公開第２０２０／１９５４２８号
　近年、ＥＵＶ光又は電子線を用いて形成されるパターンの微細化に伴い、レジスト組成物を一定時間保存した後（経時後）のラフネス性能等の諸性能等において、更なる向上が求められている。しかしながら、従来のレジスト組成物により達成することは非常に困難である。
　そこで本発明は、経時に伴うラフネス性能の変動が抑制され、経時に伴う現像欠陥性能の変動が抑制される感活性光線性又は感放射線性樹脂組成物を提供することを課題とする。
　また、本発明は、上記感活性光線性又は感放射線性樹脂組成物を用いる感活性光線性又は感放射線性膜、パターン形成方法、電子デバイスの製造方法、及び化合物を提供することを課題とする。
　本発明者らは、以下の構成により上記課題を解決できることを見出した。
［１］
（Ａ）酸の作用により分解し極性が増大する樹脂、及び
（Ｃ）活性光線又は放射線の照射によって酸を発生する化合物であって、下記一般式（Ｉ）で表される、化合物を含有する感活性光線性又は感放射線性樹脂組成物であって、
　上記樹脂（Ａ）が下記一般式（ＡＩ）で表される繰り返し単位を含む、感活性光線性又は感放射線性樹脂組成物。
Figure JPOXMLDOC01-appb-C000005
一般式（ＡＩ）中、
ＲＡ、ＲＢ、及びＲＣは、それぞれ独立に、水素原子、アルキル基、シクロアルキル基、ハロゲン原子、シアノ基、又はアルコキシカルボニル基を表す。但し、ＲＣはＡｒＡと結合して環を形成していてもよく、その場合のＲＣは単結合又はアルキレン基を表す。
ＬＡは、単結合又は２価の連結基を表す。
ＡｒＡは、（ｎ＋１）価の芳香環基を表す。ＡｒＡがＲＣと結合して環を形成する場合には、ＡｒＡは、（ｎ＋２）価の芳香環基を表す。
ｎは、１～５の整数を表す。
Figure JPOXMLDOC01-appb-C000006
一般式（Ｉ）中、
Ｒ０は置換基を表す。
ｐは０～４の整数である。
ｑは０～３の整数である。ｐ＋ｑ≧１である。
ｑが０の場合、全てのＲ０において、炭素原子の総数と酸素原子の総数を足した合計が３以上である。
ｐが２以上の整数の場合、複数のＲ０は同一であってもよく、異なっていても良い。
Ｍ＋はカチオンを表す。
［２］
　上記一般式（Ｉ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、アルキル基、－Ｃ（＝Ｏ）Ｒ１、又はアリール基を表し、Ｒ１は有機基を表す、［１］に記載の感活性光線性又は感放射線性樹脂組成物。
［３］
　活性光線又は放射線の照射によって、上記化合物（Ｃ）が発生する酸よりも強い酸を発生する化合物（Ｂ）を含有する、［１］又は［２］に記載の感活性光線性又は感放射線性樹脂組成物。
［４］
　上記樹脂（Ａ）が、活性光線又は放射線の照射により分解して酸を発生する基を有する繰り返し単位を有する、［１］～［３］のいずれかに記載の感活性光線性又は感放射線性樹脂組成物。
［５］
　上記活性光線又は放射線の照射により分解して酸を発生する基を有する繰り返し単位が、下記一般式（Ｓ－１）で表される繰り返し単位である、［４］に記載の感活性光線性又は感放射線性樹脂組成物。
Figure JPOXMLDOC01-appb-C000007
一般式（Ｓ－１）中、
Ｒ２１は、水素原子、アルキル基、アリール基、又はハロゲン原子を表す。
Ｘ１は、単結合又は２価の連結基を表す。
Ｒｃ１～Ｒｃ３は、それぞれ独立に、アルキル基、アリール基、又はヘテロアリール基を表す。Ｒｃ１～Ｒｃ３のうち２つが結合して環構造を形成してもよい。
［６］
　上記一般式（Ｉ）中、ｐが３又は４を表す、［１］～［５］のいずれか１項に記載の感活性光線性又は感放射線性樹脂組成物。
［７］
　上記一般式（Ｉ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、－Ｃ（＝Ｏ）Ｒ１を表す、［１］～［６］のいずれか１項に記載の感活性光線性又は感放射線性樹脂組成物。
［８］
　上記一般式（Ｉ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、アリール基を表す、［１］～［７］のいずれか１項に記載の感活性光線性又は感放射線性樹脂組成物。
［９］
　［１］～［８］のいずれか１項に記載の感活性光線性又は感放射線性樹脂組成物により形成された、感活性光線性又は感放射線性膜。
［１０］
　［１］～［８］のいずれか１項に記載の組成物により基板上に感活性光線性又は感放射線性膜を形成する工程と、上記感活性光線性又は感放射線性膜を露光する工程と、上記露光された感活性光線性又は感放射線性膜を現像液を用いて現像する工程と、を有する、パターン形成方法。
［１１］
　［１０］に記載のパターン形成方法を含む、電子デバイスの製造方法。
［１２］
　下記一般式（ＩＡ）で表される化合物。
Figure JPOXMLDOC01-appb-C000008
一般式（ＩＡ）中、
Ｒ０はアルキル基、－Ｃ（＝Ｏ）Ｒ１、又はアリール基を表す。Ｒ１は有機基を表す。
ｐは０～４の整数である。ｑは０～３の整数である。ｐ＋ｑ≧１である。
ｑが０の場合、全てのＲ０において、炭素原子の総数と酸素原子の総数を足した合計が３以上である。
ｐが２以上の整数の場合、複数のＲ０は同一であってもよく、異なっていても良い。
Ｍ＋はカチオンを表す。
［１３］
　上記一般式（ＩＡ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、アルキル基、－Ｃ（＝Ｏ）Ｒ１、又はアリール基を表し、Ｒ１は有機基を表す、［１２］に記載の化合物。
［１４］
　上記一般式（ＩＡ）中、ｐが３又は４を表す、［１２］又は［１３］に記載の化合物。
［１５］
　上記一般式（ＩＡ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、－Ｃ（＝Ｏ）Ｒ１を表す、［１２］～［１４］のいずれか１項に記載の化合物。
［１６］
　上記一般式（ＩＡ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、アリール基を表す、［１２］～［１５］のいずれか１項に記載の化合物。
　本発明により、経時に伴うラフネス性能の変動が抑制され、経時に伴う現像欠陥性能の変動が抑制される感活性光線性又は感放射線性樹脂組成物を提供することができる。また、本発明によれば、上記感活性光線性又は感放射線性樹脂組成物を用いた感活性光線性又は感放射線性膜、パターン形成方法、電子デバイスの製造方法、及び化合物を提供することができる。
　以下、本発明について詳細に説明する。
　以下に記載する構成要件の説明は、本発明の代表的な実施態様に基づいてなされる場合があるが、本発明はそのような実施態様に限定されない。
　本明細書中における基（原子団）の表記について、本発明の趣旨に反しない限り、置換及び無置換を記していない表記は、置換基を有さない基と共に置換基を含む基をも包含する。例えば、「アルキル基」とは、置換基を有さないアルキル基（無置換アルキル基）のみならず、置換基を有するアルキル基（置換アルキル基）をも包含する。また、本明細書中において、「有機基」とは、少なくとも１個の炭素原子を含む基をいう。
　置換基としては、特に断らない限り、１価の置換基が好ましい。
　本明細書において、「活性光線」又は「放射線」とは、例えば、水銀灯の輝線スペクトル、エキシマレーザーに代表される遠紫外線、極紫外線（ＥＵＶ光：　Ｅｘｔｒｅｍｅ　Ｕｌｔｒａｖｉｏｌｅｔ）、Ｘ線、及び、電子線（ＥＢ：Ｅｌｅｃｔｒｏｎ　Ｂｅａｍ）を意味する。
　本明細書において、「光」とは、活性光線又は放射線を意味する。
　本明細書において、「露光」とは、特に断らない限り、水銀灯の輝線スペクトル、エキシマレーザーに代表される遠紫外線、極紫外線（ＥＵＶ：Ｅｘｔｒｅｍｅ　ｕｌｔｒａｖｉｏｌｅｔ）、及び、Ｘ線等による露光のみならず、電子線、及び、イオンビーム等の粒子線による描画も含む。
　本明細書において、「～」とは、その前後に記載される数値を下限値及び上限値として含む意味で使用される。
　本明細書において、表記される２価の連結基の結合方向は、特に断らない限り制限されない。例えば、「Ｘ－Ｙ－Ｚ」なる式で表される化合物中の、Ｙが－ＣＯＯ－である場合、Ｙは、－ＣＯ－Ｏ－であってもよく、－Ｏ－ＣＯ－であってもよい。上記化合物は「Ｘ－ＣＯ－Ｏ－Ｚ」であってもよく、「Ｘ－Ｏ－ＣＯ－Ｚ」であってもよい。
　本明細書において、（メタ）アクリレートはアクリレート及びメタクリレートを表し、（メタ）アクリルはアクリル及びメタクリルを表す。
　本明細書において、重量平均分子量（Ｍｗ）、数平均分子量（Ｍｎ）、及び、分散度（以下「分子量分布」ともいう。）（Ｍｗ／Ｍｎ）は、ＧＰＣ（Ｇｅｌ　Ｐｅｒｍｅａｔｉｏｎ　Ｃｈｒｏｍａｔｏｇｒａｐｈｙ）装置（東ソー社製ＨＬＣ－８１２０ＧＰＣ）によるＧＰＣ測定（溶媒：テトラヒドロフラン、流量（サンプル注入量）：１０μＬ、カラム：東ソー社製ＴＳＫ　ｇｅｌ　Ｍｕｌｔｉｐｏｒｅ　ＨＸＬ－Ｍ、カラム温度：４０℃、流速：１．０ｍＬ／分、検出器：示差屈折率検出器（Ｒｅｆｒａｃｔｉｖｅ　Ｉｎｄｅｘ　Ｄｅｔｅｃｔｏｒ））によるポリスチレン換算値として定義される。
　本明細書において、酸解離定数（ｐＫａ）とは、水溶液中でのｐＫａを表し、具体的には、下記ソフトウェアパッケージ１を用いて、ハメットの置換基定数及び公知文献値のデータベースに基づいた値を、計算により求められる値である。
　ソフトウェアパッケージ１：　Ａｄｖａｎｃｅｄ　Ｃｈｅｍｉｓｔｒｙ　Ｄｅｖｅｌｏｐｍｅｎｔ　（ＡＣＤ／Ｌａｂｓ）　Ｓｏｆｔｗａｒｅ　Ｖ８．１４　ｆｏｒ　Ｓｏｌａｒｉｓ　（１９９４－２００７　ＡＣＤ／Ｌａｂｓ）。
　ｐＫａは、分子軌道計算法によっても求められる。具体的な方法としては、熱力学サイクルに基づいて、水溶液中におけるＨ＋解離自由エネルギーを計算することで算出する手法が挙げられる。Ｈ＋解離自由エネルギーの計算方法については、例えばＤＦＴ（密度汎関数法）により計算することができるが、他にも様々な手法が文献等で報告されており、これに制限されない。なお、ＤＦＴを実施できるソフトウェアは複数存在するが、例えば、Ｇａｕｓｓｉａｎ１６が挙げられる。
　本明細書中において、ｐＫａとは、上述した通り、ソフトウェアパッケージ１を用いて、ハメットの置換基定数及び公知文献値のデータベースに基づいた値を計算により求められる値を指すが、この手法によりｐＫａが算出できない場合には、ＤＦＴ（密度汎関数法）に基づいてＧａｕｓｓｉａｎ１６により得られる値を採用するものとする。
　本明細書中において、ｐＫａは、上述した通り「水溶液中でのｐＫａ」を指すが、水溶液中でのｐＫａが算出できない場合には、「ジメチルスルホキシド（ＤＭＳＯ）溶液中でのｐＫａ」を採用するものとする。
　「固形分」とは、感活性光線性又は感放射線性膜を形成する成分を意味し、溶剤は含まれない。また、感活性光線性又は感放射線性膜を形成する成分であれば、その性状が液体状であっても、固形分とみなす。
　以下、本発明の感活性光線性又は感放射線性樹脂組成物について詳細に説明する。
　感活性光線性又は感放射線性樹脂組成物は、好ましくはレジスト組成物であり、ポジ型のレジスト組成物であっても、ネガ型のレジスト組成物であってもよい。レジスト組成物は、アルカリ現像用のレジスト組成物であっても、有機溶剤現像用のレジスト組成物であってもよい。
　レジスト組成物は、化学増幅型のレジスト組成物であっても、非化学増幅型のレジスト組成物であってもよい。レジスト組成物は、典型的には、化学増幅型のレジスト組成物である。
　本発明の感活性光線性又は感放射線性樹脂組成物（以下、「本発明の組成物」ともいう）は、（Ａ）酸の作用により分解し極性が増大する樹脂、及び（Ｃ）活性光線又は放射線の照射によって酸を発生する化合物であって、下記一般式（Ｉ）で表される、化合物を含有する感活性光線性又は感放射線性樹脂組成物であって、
　上記樹脂（Ａ）が下記一般式（ＡＩ）で表される繰り返し単位を含む、感活性光線性又は感放射線性樹脂組成物である。
Figure JPOXMLDOC01-appb-C000009
一般式（ＡＩ）中、
ＲＡ、ＲＢ、及びＲＣは、それぞれ独立に、水素原子、アルキル基、シクロアルキル基、ハロゲン原子、シアノ基、又はアルコキシカルボニル基を表す。但し、ＲＣはＡｒＡと結合して環を形成していてもよく、その場合のＲＣは単結合又はアルキレン基を表す。
ＬＡは、単結合又は２価の連結基を表す。
ＡｒＡは、（ｎ＋１）価の芳香環基を表す。ＡｒＡがＲＣと結合して環を形成する場合には、ＡｒＡは、（ｎ＋２）価の芳香環基を表す。
ｎは、１～５の整数を表す。
Figure JPOXMLDOC01-appb-C000010
一般式（Ｉ）中、
Ｒ０は置換基を表す。
ｐは０～４の整数である。ｑは０～３の整数である。ｐ＋ｑ≧１である。
ｑが０の場合、全てのＲ０において、炭素原子の総数と酸素原子の総数を足した合計が３以上である。
ｐが２以上の整数の場合、複数のＲ０は同一であってもよく、異なっていても良い。
Ｍ＋はカチオンを表す。
　本発明の組成物により、経時に伴うラフネス性能の変動が抑制され、経時に伴う現像欠陥性能の変動が抑制される理由については、完全には明らかになってはいないが、本発明者らは以下のように推定している。
　一般式（Ｉ）で表される化合物において、ｑが０の場合、全てのＲ０において、炭素原子の総数と酸素原子の総数を足した合計が３以上である。このように、全てのＲ０において、炭素原子の総数と酸素原子の総数を足した合計が３以上であると、（ｉ）Ｒ０が結合されたアリール基が嵩高くなる（例えば、Ｒ０が、酸素原子を含まず、例えば、アルキル基である場合など）、及び、（ｉｉ）Ｒ０がＡｒＡ－ＯＨと相互作用する基（例えば、アシル基、アリール基など）を有するのいずれか少なくとも一方を満たす。
　上記（ｉ）の場合、Ｒ０が結合されたアリール基は、本発明の組成物における一般式（Ｉ）で表される化合物同士の凝集において、立体障害し得る構造となるから、組成物中における一般式（Ｉ）で表される化合物同士の凝集を抑制することができるため、経時に伴うラフネス性能の変動が抑制され、経時に伴う現像欠陥性能の変動が抑制されるものと考えられる。
　上記（ｉｉ）の場合、Ｒ０としての、Ａｒａ－ＯＨと相互作用する基が炭素原子と酸素原子とから構成される極性基（例えばアシル基など）である場合、上記極性基は、樹脂（Ａ）が有する一般式（ＡＩ）で表される繰り返し単位における「ＡｒＡで－表される芳香環基に結合する水酸基」と相互作用しやすく、上記（ｉ）の場合と同様に、組成物中における一般式（Ｉ）で表される化合物同士の凝集を抑制することができるため、経時に伴うラフネス性能の変動が抑制され、経時に伴う現像欠陥性能の変動が抑制されるものと考えられる。
　上記（ｉｉ）の場合、Ｒ０としての、Ａｒａ－ＯＨと相互作用する基がアリール基（例えばアシル基など）である場合、上記（ｉ）の場合にも相当し、上記アリール基は、樹脂（Ａ）が有する一般式（ＡＩ）で表される繰り返し単位における「ＡｒＡで－表される芳香環基」と相互作用しやすく、上記（ｉ）の場合と同様に、組成物中における一般式（Ｉ）で表される化合物同士の凝集を抑制することができるため、経時に伴うラフネス性能の変動が抑制され、経時に伴う現像欠陥性能の変動が抑制されるものと考えられる。
　また、一般式（Ｉ）で表される化合物において、ｑが１以上である場合、多環芳香族環が存在する。このような多環芳香族環は、樹脂（Ａ）における一般式（ＡＩ）で表される繰り返し単位のＡｒＡで表される芳香環基と相互作用しやすいことにより、一般式（Ｉ）で表される化合物同士の凝集を抑制することができるため、経時に伴うラフネス性能の変動が抑制され、経時に伴う現像欠陥性能の変動が抑制されるものと考えられる。
　また、詳細は不明であるが、一般式（Ｉ）のアニオン部における芳香環に結合する－ＣＯＯ－と、－ＣＯＯ－と結合する芳香環の炭素原子に隣接する炭素原子に結合する－ＯＨの関係も一般式（Ｉ）で表される化合物同士の凝集を抑制に寄与するものと推測される。
　以上により、本発明の組成物により、経時に伴うラフネス性能の変動が抑制され、経時に伴う現像欠陥性能の変動が抑制されるものと考えられる。
　以下において、まず、感活性光線性又は感放射線性樹脂組成物の各種成分について詳述する。
＜（Ｃ）活性光線又は放射線の照射によって酸を発生する化合物であって、下記一般式（Ｉ）で表される、化合物＞
　本発明の組成物は、（Ｃ）活性光線又は放射線の照射によって酸を発生する化合物であって、下記一般式（Ｉ）で表される、化合物（以下、「化合物（Ｃ）」ともいう）を含有する。
（一般式（Ｉ）で表される化合物）
Figure JPOXMLDOC01-appb-C000011
一般式（Ｉ）中、
Ｒ０は置換基を表す。
ｐは０～４の整数である。ｑは０～３の整数である。ｐ＋ｑ≧１である。
ｑが０の場合、全てのＲ０において、炭素原子の総数と酸素原子の総数を足した合計が３以上である。
ｐが２以上の整数の場合、複数のＲ０は同一であってもよく、異なっていても良い。
Ｍ＋はカチオンを表す。
　Ｒ０の置換基は、特に限定されないが、例えば、有機基、水酸基、ハロゲン原子、シアノ基等が挙げられる。
　有機基としては、特に限定されないが、炭素数１～３０の有機基が挙げられ、具体的には、アルキル基、シクロアルキル基、アルコキシ基、アリール基、又は－Ｃ（＝Ｏ）Ｒ１が挙げられる。Ｒ１は有機基を表す。
　アルキル基としては、特に限定されないが、直鎖状又は分岐鎖状であってもよく、炭素数１～１５のアルキル基が好ましく、炭素数１～１０のアルキル基がより好ましい。
　シクロアルキル基は、特に限定されないが、単環型でも、多環型でもよく、炭素数３～１５のシクロアルキル基が好ましく、炭素数３～１０のシクロアルキル基がより好ましい。
　アルコキシ基としては、特に限定されないが、直鎖状又は分岐鎖状であってもよく、炭素数１～１５のアルコキシ基が好ましく、炭素数１～１０のアルコキシ基がより好ましい。
　アリール基としては、特に限定されないが、単環でも、多環型でもよく、炭素数６～１０のアリール基が好ましく、例えば、フェニル基、ナフチル基、及びアントリル基等が挙げられる。
　アルキル基、シクロアルキル基、アルコキシ基、アリール基は、さらに置換基を有していても良い。置換基としては、特に限定されないが、例えば、アルキル基、アルコキシ基、水酸基、ハロゲン原子、シアノ基等が挙げられる。
　Ｒ１の有機基としては、特に限定されないが、炭素数１～３０の有機基が挙げられ、具体的には、アルキル基、シクロアルキル基、アルコキシ基、アリール基等を挙げることができる。アルキル基、シクロアルキル基、アルコキシ基、アリール基は、それぞれ、上述したＲ０の有機基としてのアルキル基、シクロアルキル基、アルコキシ基、アリール基と同様のものを挙げることができ、また好ましい範囲も同様である。
　ｐは０～４の整数である。ｑは０～３の整数である。ｐ＋ｑ≧１である。
　ｐは好ましくは１～４の整数であり、より好ましくは、３又は４を表す。
　ｑは、好ましくは、０～２の整数であり、より好ましくは０又は１である。
　好ましい一態様として、ｑが０の場合、ｐは３又は４を表すことが好ましい。
　一般式（Ｉ）において、ｑが０の場合、全てのＲ０において、炭素原子の総数と酸素原子の総数を足した合計が３以上である。全てのＲ０における炭素原子の総数及び酸素原子の総数の合計は３以上である。
　この要件を満たす例として、例えば、下記の態様１、態様２、態様３を挙げることができる。
（態様１）　ｑ＝０、ｐ＝３で、Ｒ０が全てメチル基の態様
（態様２）　ｑ＝０、ｐ＝１で、Ｒ０がメチルカルボニル基の態様
（態様３）　ｑ＝０、ｐ＝１で、Ｒ０がプロピル基の態様
　このように、「一般式（Ｉ）において、ｑが０の場合、全てのＲ０において、炭素原子の総数と酸素原子の総数を足した合計が３以上である」とは、存在する各々のＲ０について、それぞれ炭素原子の総数及び酸素原子の総数を算出して、全てのＲ０において、炭素原子の総数及び酸素原子の総数を足した合計が３以上であることを意味する。
　ｐが２以上の整数の場合、複数のＲ０は同一であってもよく、異なっていても良い。
　一般式（Ｉ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、アルキル基、－Ｃ（＝Ｏ）Ｒ１、又はアリール基を表すことが好ましい。
　一般式（Ｉ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、－Ｃ（＝Ｏ）Ｒ１を表すことが好ましい。
　一般式（Ｉ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、アリール基を表すことが好ましい。
　Ｍ＋で表されるカチオンは、特に限定されないが、有機カチオンが好ましい。
　なかでも、上記有機カチオンとしては、式（ＺａＩ）で表されるカチオン（以下「カチオン（ＺａＩ）」ともいう。）、又は、式（ＺａＩＩ）で表されるカチオン（以下「カチオン（ＺａＩＩ）」ともいう。）が好ましい。
Figure JPOXMLDOC01-appb-C000012
　上記式（ＺａＩ）において、Ｒ２０１、Ｒ２０２、及びＲ２０３は、それぞれ独立に、有機基を表す。
　Ｒ２０１、Ｒ２０２、及びＲ２０３としての有機基の炭素数は、１～３０が好ましく、１～２０がより好ましい。Ｒ２０１～Ｒ２０３のうち２つが結合して環構造を形成してもよく、環内に酸素原子、硫黄原子、エステル基、アミド基、又はカルボニル基を含んでいてもよい。Ｒ２０１～Ｒ２０３の内の２つが結合して形成する基としては、例えば、アルキレン基（例えば、ブチレン基及びペンチレン基）、及び－ＣＨ２－ＣＨ２－Ｏ－ＣＨ２－ＣＨ２－が挙げられる。
　式（ＺａＩ）における有機カチオンの好適な態様としては、後述する、カチオン（ＺａＩ－１）、カチオン（ＺａＩ－２）、カチオン（ＺａＩ－３ｂ）、カチオン（ＺａＩ－４ｂ）が挙げられる。
　まず、カチオン（ＺａＩ－１）について説明する。
　カチオン（ＺａＩ－１）は、上記式（ＺａＩ）のＲ２０１～Ｒ２０３の少なくとも１つがアリール基である、アリールスルホニウムカチオンである。
　アリールスルホニウムカチオンは、Ｒ２０１～Ｒ２０３の全てがアリール基でもよいし、Ｒ２０１～Ｒ２０３の一部がアリール基であり、残りがアルキル基又はシクロアルキル基であってもよい。
　Ｒ２０１～Ｒ２０３のうちの１つがアリール基であり、Ｒ２０１～Ｒ２０３のうちの残りの２つが結合して環構造を形成してもよく、環内に酸素原子、硫黄原子、エステル基、アミド基、又はカルボニル基を含んでいてもよい。Ｒ２０１～Ｒ２０３のうちの２つが結合して形成する基としては、例えば、１つ以上のメチレン基が酸素原子、硫黄原子、エステル基、アミド基、及び／又はカルボニル基で置換されていてもよいアルキレン基（例えば、ブチレン基、ペンチレン基、及び－ＣＨ２－ＣＨ２－Ｏ－ＣＨ２－ＣＨ２－）が挙げられる。
　アリールスルホニウムカチオンとしては、トリアリールスルホニウムカチオン、ジアリールアルキルスルホニウムカチオン、アリールジアルキルスルホニウムカチオン、ジアリールシクロアルキルスルホニウムカチオン、及びアリールジシクロアルキルスルホニウムカチオンが挙げられる。
　アリールスルホニウムカチオンに含まれるアリール基としては、フェニル基又はナフチル基が好ましく、フェニル基がより好ましい。アリール基は、酸素原子、窒素原子、又は硫黄原子等を有するヘテロ環構造を有するアリール基であってもよい。ヘテロ環構造としては、ピロール残基、フラン残基、チオフェン残基、インドール残基、ベンゾフラン残基、及びベンゾチオフェン残基が挙げられる。アリールスルホニウムカチオンが２つ以上のアリール基を有する場合に、２つ以上あるアリール基は同一であっても異なっていてもよい。
　アリールスルホニウムカチオンが必要に応じて有しているアルキル基又はシクロアルキル基は、炭素数１～１５の直鎖状アルキル基、炭素数３～１５の分岐鎖状アルキル基、又は炭素数３～１５のシクロアルキル基が好ましく、メチル基、エチル基、プロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ｔ－ブチル基、シクロプロピル基、シクロブチル基、又はシクロヘキシル基がより好ましい。
　Ｒ２０１～Ｒ２０３のアリール基、アルキル基、及びシクロアルキル基が有していてもよい置換基としては、アルキル基（例えば、炭素数１～１５）、シクロアルキル基（例えば、炭素数３～１５）、アリール基（例えば、炭素数６～１４）、アルコキシ基（例えば、炭素数１～１５）、シクロアルキルアルコキシ基（例えば、炭素数１～１５）、ハロゲン原子（例えば、フッ素及びヨウ素）、水酸基、カルボキシル基、エステル基、スルフィニル基、スルホニル基、アルキルチオ基、又はフェニルチオ基が好ましい。
　上記置換基は可能な場合更に置換基を有していてもよく、上記アルキル基が置換基としてハロゲン原子を有して、トリフルオロメチル基等のハロゲン化アルキル基となっていることも好ましい。
　上記置換基は任意の組み合わせにより、酸分解性基を形成することも好ましい。
　なお、酸分解性基とは、酸の作用により分解して極性基を生じる基を意図し、酸の作用により脱離する基で極性基が保護された構造であることが好ましい。上記の極性基及び脱離基としては、上述の通りである。
　次に、カチオン（ＺａＩ－２）について説明する。
　カチオン（ＺａＩ－２）は、式（ＺａＩ）におけるＲ２０１～Ｒ２０３が、それぞれ独立に、芳香環を有さない有機基を表すカチオンである。芳香環とは、ヘテロ原子を含む芳香族環も包含する。
　Ｒ２０１～Ｒ２０３としての芳香環を有さない有機基の炭素数は、１～３０が好ましく、１～２０がより好ましい。
　Ｒ２０１～Ｒ２０３としては、それぞれ独立に、アルキル基、シクロアルキル基、アリル基、又はビニル基が好ましく、直鎖状又は分岐鎖状の２－オキソアルキル基、２－オキソシクロアルキル基、又はアルコキシカルボニルメチル基がより好ましく、直鎖状又は分岐鎖状の２－オキソアルキル基が更に好ましい。
　Ｒ２０１～Ｒ２０３のアルキル基及びシクロアルキル基は、例えば、炭素数１～１０の直鎖状アルキル基又は炭素数３～１０の分岐鎖状アルキル基（例えば、メチル基、エチル基、プロピル基、ブチル基、及びペンチル基）、並びに、炭素数３～１０のシクロアルキル基（例えば、シクロペンチル基、シクロヘキシル基、及びノルボルニル基）が挙げられる。
　Ｒ２０１～Ｒ２０３は、ハロゲン原子、アルコキシ基（例えば、炭素数１～５）、水酸基、シアノ基、又はニトロ基によって更に置換されていてもよい。
　Ｒ２０１～Ｒ２０３の置換基は、それぞれ独立に、置換基の任意の組み合わせにより、酸分解性基を形成することも好ましい。
　次に、カチオン（ＺａＩ－３ｂ）について説明する。
　カチオン（ＺａＩ－３ｂ）は、下記式（ＺａＩ－３ｂ）で表されるカチオンである。
Figure JPOXMLDOC01-appb-C000013
　式（ＺａＩ－３ｂ）中、Ｒ１ｃ～Ｒ５ｃは、それぞれ独立に、水素原子、アルキル基、シクロアルキル基、アリール基、アルコキシ基、アリールオキシ基、アルコキシカルボニル基、アルキルカルボニルオキシ基、シクロアルキルカルボニルオキシ基、ハロゲン原子、水酸基、ニトロ基、アルキルチオ基、又はアリールチオ基を表す。
　Ｒ６ｃ及びＲ７ｃは、それぞれ独立に、水素原子、アルキル基（例えば、ｔ－ブチル基等）、シクロアルキル基、ハロゲン原子、シアノ基、又はアリール基を表す。
　Ｒｘ及びＲｙは、それぞれ独立に、アルキル基、シクロアルキル基、２－オキソアルキル基、２－オキソシクロアルキル基、アルコキシカルボニルアルキル基、アリル基、又はビニル基を表す。
　Ｒ１ｃ～Ｒ７ｃ、並びに、Ｒｘ及びＲｙの置換基は、それぞれ独立に、置換基の任意の組み合わせにより、酸分解性基を形成することも好ましい。
　Ｒ１ｃ～Ｒ５ｃ中のいずれか２つ以上、Ｒ５ｃとＲ６ｃ、Ｒ６ｃとＲ７ｃ、Ｒ５ｃとＲｘ、及びＲｘとＲｙは、それぞれ互いに結合して環を形成してもよく、この環は、それぞれ独立に、酸素原子、硫黄原子、ケトン基、エステル結合、又はアミド結合を含んでいてもよい。
　上記環としては、芳香族又は非芳香族の炭化水素環、芳香族又は非芳香族のヘテロ環、及びこれらの環が２つ以上組み合わされてなる多環縮合環が挙げられる。環としては、３～１０員環が挙げられ、４～８員環が好ましく、５又は６員環がより好ましい。
　Ｒ１ｃ～Ｒ５ｃ中のいずれか２つ以上、Ｒ６ｃとＲ７ｃ、及びＲｘとＲｙが結合して形成する基としては、ブチレン基及びペンチレン基等のアルキレン基が挙げられる。このアルキレン基中のメチレン基が酸素原子等のヘテロ原子で置換されていてもよい。
　Ｒ５ｃとＲ６ｃ、及びＲ５ｃとＲｘが結合して形成する基としては、単結合又はアルキレン基が好ましい。アルキレン基としては、メチレン基及びエチレン基が挙げられる。
　Ｒ１ｃ～Ｒ５ｃ、Ｒ６ｃ、Ｒ７ｃ、Ｒｘ、Ｒｙ、並びに、Ｒ１ｃ～Ｒ５ｃ中のいずれか２つ以上、Ｒ５ｃとＲ６ｃ、Ｒ６ｃとＲ７ｃ、Ｒ５ｃとＲｘ、及びＲｘとＲｙがそれぞれ互いに結合して形成する環は、置換基を有していてもよい。
　次に、カチオン（ＺａＩ－４ｂ）について説明する。
　カチオン（ＺａＩ－４ｂ）は、下記式（ＺａＩ－４ｂ）で表されるカチオンである。
Figure JPOXMLDOC01-appb-C000014
　式（ＺａＩ－４ｂ）中、ｌは０～２の整数を表し、ｒは０～８の整数を表す。
　Ｒ１３は、水素原子、ハロゲン原子(例えば、フッ素原子及びヨウ素原子等)、水酸基、アルキル基、ハロゲン化アルキル基、アルコキシ基、カルボキシル基、アルコキシカルボニル基、又はシクロアルキル基を含む基（シクロアルキル基そのものであってもよく、シクロアルキル基を一部に含む基であってもよい）を表す。これらの基は置換基を有してもよい。
　Ｒ１４は、水酸基、ハロゲン原子(例えば、フッ素原子及びヨウ素原子等)、アルキル基、ハロゲン化アルキル基、アルコキシ基、アルコキシカルボニル基、アルキルカルボニル基、アルキルスルホニル基、シクロアルキルスルホニル基、又はシクロアルキル基を含む基（シクロアルキル基そのものであってもよく、シクロアルキル基を一部に含む基であってもよい）を表す。これらの基は置換基を有してもよい。Ｒ１４は、複数存在する場合は、それぞれ独立して、水酸基等の上記基を表す。
　Ｒ１５は、それぞれ独立して、アルキル基、シクロアルキル基、又はナフチル基を表す。２つのＲ１５が互いに結合して環を形成してもよい。２つのＲ１５が互いに結合して環を形成するとき、環骨格内に、酸素原子、又は窒素原子等のヘテロ原子を含んでもよい。
　一態様において、２つのＲ１５がアルキレン基であり、互いに結合して環構造を形成することが好ましい。なお、上記アルキル基、上記シクロアルキル基、及び上記ナフチル基、並びに、２つのＲ１５が互いに結合して形成する環は置換基を有してもよい。
　式（ＺａＩ－４ｂ）において、Ｒ１３、Ｒ１４、及びＲ１５のアルキル基は、直鎖状又は分岐鎖状であってもよい。アルキル基の炭素数は、１～１０が好ましい。アルキル基は、メチル基、エチル基、ｎ－ブチル基、又はｔ－ブチル基等が好ましい。
　Ｒ１３～Ｒ１５、並びに、Ｒｘ及びＲｙの各置換基は、それぞれ独立に、置換基の任意の組み合わせにより、酸分解性基を形成することも好ましい。
　次に、式（ＺａＩＩ）について説明する。
　式（ＺａＩＩ）中、Ｒ２０４及びＲ２０５は、それぞれ独立に、アリール基、アルキル基又はシクロアルキル基を表す。
　Ｒ２０４及びＲ２０５のアリール基としては、フェニル基、又はナフチル基が好ましく、フェニル基がより好ましい。Ｒ２０４及びＲ２０５のアリール基は、酸素原子、窒素原子、又は硫黄原子等を有するヘテロ環を有するアリール基であってもよい。ヘテロ環を有するアリール基の骨格としては、例えば、ピロール、フラン、チオフェン、インドール、ベンゾフラン、及びベンゾチオフェンが挙げられる。
　Ｒ２０４及びＲ２０５のアルキル基及びシクロアルキル基としては、炭素数１～１０の直鎖状アルキル基又は炭素数３～１０の分岐鎖状アルキル基（例えば、メチル基、エチル基、プロピル基、ブチル基、又はペンチル基）、又は炭素数３～１０のシクロアルキル基（例えばシクロペンチル基、シクロヘキシル基、又はノルボルニル基）が好ましい。
　Ｒ２０４及びＲ２０５のアリール基、アルキル基、及びシクロアルキル基は、それぞれ独立に、置換基を有していてもよい。Ｒ２０４及びＲ２０５のアリール基、アルキル基、及びシクロアルキル基が有していてもよい置換基としては、例えば、アルキル基（例えば、炭素数１～１５）、シクロアルキル基（例えば、炭素数３～１５）、アリール基（例えば、炭素数６～１５）、アルコキシ基（例えば、炭素数１～１５）、ハロゲン原子、水酸基、及びフェニルチオ基が挙げられる。また、Ｒ２０４及びＲ２０５の置換基は、それぞれ独立に、置換基の任意の組み合わせにより、酸分解性基を形成することも好ましい。
　以下に有機カチオンの具体例を示すが、本発明は、これに限定されない。
Figure JPOXMLDOC01-appb-C000015
Figure JPOXMLDOC01-appb-C000016
Figure JPOXMLDOC01-appb-C000017
　化合物（Ｃ）の好ましい例を以下に示すが、本発明はこれらに限定されるものではない。Ｍｅはメチル基を表す。また、以下の化合物において、カチオンとアニオンの組み合わせを変更することができる。
Figure JPOXMLDOC01-appb-C000018
Figure JPOXMLDOC01-appb-C000019
　化合物（Ｃ）は、活性光線又は放射線の照射により酸を発生する化合物（光酸発生剤）である。
　化合物（Ｃ）は、酸拡散制御剤として使用される場合においては、化合物（Ｃ）から生じる酸に対して、露光部における樹脂の反応に必要な酸を発生する光酸発生剤より生じる酸が相対的に強酸となるような光酸発生剤を併用することが好ましい。
　また、化合物（Ｃ）は、酸拡散制御剤として使用される場合においては、化合物（Ｃ）から生じる酸に対して、露光部における樹脂の反応に必要な酸を発生する光酸発生剤より生じる酸が相対的に強酸となるような繰り返し単位を有する樹脂（Ａ）を併用することが好ましい。樹脂（Ａ）については後述する。
　化合物（Ｃ）は、公知の方法を参照して合成することができる。一般式（Ｉ）で表される化合物の具体的な合成例は後述する実施例で示す。
　上記化合物（Ｃ）の分子量は、３００～３０００が好ましく、３００～２０００がより好ましく、３００～１５００が更に好ましい。
　化合物（Ｃ）は、１種単独で使用してもよいし、２種以上を併用してもよい。
　本発明の組成物中、化合物（Ｃ）の含有量（複数種存在する場合はその合計）は、組成物の全固形分を基準として、３～５０質量％が好ましく、５～３０質量％がより好ましく、５～２５質量％が更に好ましく、５～２０質量％が特に好ましい。
＜（Ａ）酸の作用により分解し極性が増大する樹脂＞
　本発明の組成物は、（Ａ）酸の作用により分解し極性が増大する樹脂（以下、「樹脂（Ａ）」又は「酸分解性樹脂」ともいう。）を含む。
　樹脂（Ａ）は、通常、酸の作用により分解し極性が増大する基（以下「酸分解性基」ともいう。）を含み、酸分解性基を有する繰り返し単位を含むことが好ましい。
　樹脂（Ａ）が酸分解性基を有する場合、本明細書におけるパターン形成方法において、典型的には、現像液としてアルカリ現像液を採用した場合には、ポジ型パターンが好適に形成され、現像液として有機系現像液を採用した場合には、ネガ型パターンが好適に形成される。
　酸分解性基を有する繰り返し単位としては、後述する酸分解性基を有する繰り返し単位以外に、不飽和結合を含む酸分解性基を有する繰り返し単位が好ましい。
　以下において、樹脂（Ａ）が含み得る繰り返し単位について説明する。
（一般式（ＡＩ）で表される繰り返し単位）
　上記樹脂（Ａ）は、下記一般式（ＡＩ）で表される繰り返し単位（以下、「繰り返し単位（ａ）」ともいう）を含む。
Figure JPOXMLDOC01-appb-C000020
一般式（ＡＩ）中、
ＲＡ、ＲＢ、及びＲＣは、それぞれ独立に、水素原子、アルキル基、シクロアルキル基、ハロゲン原子、シアノ基、又はアルコキシカルボニル基を表す。但し、ＲＣはＡｒＡと結合して環を形成していてもよく、その場合のＲＣは単結合又はアルキレン基を表す。
ＬＡは、単結合又は２価の連結基を表す。
ＡｒＡは、（ｎ＋１）価の芳香環基を表す。ＡｒＡがＲＣと結合して環を形成する場合には、ＡｒＡは、（ｎ＋２）価の芳香環基を表す。
ｎは、１～５の整数を表す。
　一般式（ＡＩ）におけるＲＡ、ＲＢ、及びＲＣのアルキル基としては、メチル基、エチル基、プロピル基、イソプロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ヘキシル基、２－エチルヘキシル基、オクチル基、及びドデシル基等の炭素数２０以下のアルキル基が好ましく、炭素数８以下のアルキル基がより好ましく、炭素数３以下のアルキル基が更に好ましい。
　一般式（ＡＩ）におけるＲＡ、ＲＢ、及びＲＣのシクロアルキル基としては、単環型でも、多環型でもよい。なかでも、シクロプロピル基、シクロペンチル基、及びシクロヘキシル基等の炭素数３～８個で単環型のシクロアルキル基が好ましい。
　一般式（ＡＩ）におけるＲＡ、ＲＢ、及びＲＣのハロゲン原子としては、フッ素原子、塩素原子、臭素原子、及びヨウ素原子が挙げられ、フッ素原子が好ましい。
　一般式（ＡＩ）におけるＲＡ、ＲＢ、及びＲＣのアルコキシカルボニル基に含まれるアルキル基としては、上記ＲＡ、ＲＢ、及びＲＣにおけるアルキル基と同様のものが好ましい。
　上記各基は、置換基を有していてもよい。上記各基における好ましい置換基としては、特に限定されないが、例えば、アルキル基、シクロアルキル基、アリール基、アミノ基、アミド基、ウレイド基、ウレタン基、水酸基、カルボキシ基、ハロゲン原子、アルコキシ基、チオエーテル基、アシル基、アシロキシ基、アルコキシカルボニル基、シアノ基、及びニトロ基が挙げられる。置換基の炭素数は８以下が好ましい。
　ＡｒＡは、（ｎ＋１）価の芳香環基を表す。ｎが１である場合における２価の芳香環基は、例えば、フェニレン基、トリレン基、ナフチレン基、及びアントラセニレン基等の炭素数６～１８のアリーレン基、又はチオフェン環、フラン環、ピロール環、ベンゾチオフェン環、ベンゾフラン環、ベンゾピロール環、トリアジン環、イミダゾール環、ベンゾイミダゾール環、トリアゾール環、チアジアゾール環、及びチアゾール環等のヘテロ環を含む２価の芳香環基が好ましい。なお、上記芳香環基は、置換基を有していてもよい。
　ｎが２以上の整数である場合における（ｎ＋１）価の芳香環基の具体例としては、２価の芳香環基の上記した具体例から、（ｎ－１）個の任意の水素原子を除してなる基が挙げられる。
　（ｎ＋１）価の芳香環基は、更に置換基を有していてもよい。
　上述したアルキル基、シクロアルキル基、アルコキシカルボニル基、及び（ｎ＋１）価の芳香環基が有し得る置換基としては、特に限定されないが、例えば、一般式（Ｉ）におけるＲＡ、ＲＢ、及びＲＣで挙げたアルキル基；メトキシ基、エトキシ基、ヒドロキシエトキシ基、プロポキシ基、ヒドロキシプロポキシ基、及びブトキシ基等のアルコキシ基；フェニル基等のアリール基；ハロゲン原子；一般式（Ｉ）におけるＲＡ、ＲＢ、及びＲＣで挙げたアルコキシカルボニル基等が挙げられる。
　ＬＡの２価の連結基としては、特に限定されないが、－ＣＯＯ－、－ＣＯＮＲ６４－、アルキレン基、又はこれらの基の２種以上を組み合わせてなる基が挙げられる。Ｒ６４は、水素原子又はアルキル基を表す。
　アルキレン基としては、特に限定されないが、メチレン基、エチレン基、プロピレン基、ブチレン基、ヘキシレン基、及びオクチレン基等の炭素数１～８のアルキレン基が好ましい。
　Ｒ６４のアルキル基としては、メチル基、エチル基、プロピル基、イソプロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ヘキシル基、２－エチルヘキシル基、オクチル基、及びドデシル基等の炭素数２０以下のアルキル基が挙げられ、炭素数８以下のアルキル基が好ましい。
　ＡｒＡとしては、炭素数６～１８の芳香環基が好ましく、ベンゼン環基、ナフタレン環基、及びビフェニレン環基がより好ましい。
　一般式（ＡＩ）で表される繰り返し単位は、ヒドロキシスチレン構造を備えていることが好ましい。即ち、ＡｒＡは、ベンゼン環基であることが好ましい。
　ｎは、１～３の整数であることが好ましく、１又は２であることがより好ましい。
　以下、一般式（ＡＩ）で表される繰り返し単位を以下に例示する。式中、ａは１、２又は３を表す。
Figure JPOXMLDOC01-appb-C000021
Figure JPOXMLDOC01-appb-C000022
Figure JPOXMLDOC01-appb-C000023
Figure JPOXMLDOC01-appb-C000024
　なお、一般式（ＡＩ）で表される繰り返し単位は、以下に具体的に記載する繰り返し単位が好ましい。式中、Ｒは水素原子又はメチル基を表し、ａは、１、２又は３を表す。
Figure JPOXMLDOC01-appb-C000025
　また、好ましい一態様として、一般式（ＡＩ）で表される繰り返し単位に相当するモノマーを以下に例示する。
Figure JPOXMLDOC01-appb-C000026
　一般式（ＡＩ）で表される繰り返し単位の含有量は、樹脂（Ａ）中の全繰り返し単位に対し、３０モル％以上が好ましく、４０モル％以上がより好ましい。また、その上限値としては、９０モル％以下が好ましく、８５モル％以下がより好ましく、８０モル％以下が更に好ましい。
（酸分解性基を有する繰り返し単位）
　酸分解性基とは、酸の作用により分解し極性が増大する基、すなわち、酸の作用により分解し極性基を生じる基をいう。酸分解性基は、酸の作用により脱離する基(脱離基)で極性基が保護された構造を有することが好ましい。つまり、樹脂（Ａ）は、酸の作用により分解し、極性基を生じる基を有する繰り返し単位を有する。この繰り返し単位を有する樹脂は、酸の作用により極性が増大してアルカリ現像液に対する溶解度が増大し、有機溶剤に対する溶解度が減少する。
　極性基としては、アルカリ可溶性基が好ましく、例えば、カルボキシル基、フェノール性水酸基、フッ素化アルコール基、スルホン酸基、リン酸基、スルホンアミド基、スルホニルイミド基、（アルキルスルホニル）（アルキルカルボニル）メチレン基、（アルキルスルホニル）（アルキルカルボニル）イミド基、ビス（アルキルカルボニル）メチレン基、ビス（アルキルカルボニル）イミド基、ビス（アルキルスルホニル）メチレン基、ビス（アルキルスルホニル）イミド基、トリス（アルキルカルボニル）メチレン基、及び、トリス（アルキルスルホニル）メチレン基等の酸性基、並びに、アルコール性水酸基が挙げられる。
　なかでも、極性基としては、カルボキシル基、フェノール性水酸基、フッ素化アルコール基（好ましくはヘキサフルオロイソプロパノール基）、又は、スルホン酸基が好ましい。
　酸の作用により脱離する基としては、例えば、式（Ｙ１）～（Ｙ４）で表される基が挙げられる。
式（Ｙ１）：－Ｃ（Ｒｘ１）（Ｒｘ２）（Ｒｘ３）
式（Ｙ２）：－Ｃ（＝Ｏ）ＯＣ（Ｒｘ１）（Ｒｘ２）（Ｒｘ３）
式（Ｙ３）：－Ｃ（Ｒ３６）（Ｒ３７）（ＯＲ３８）
式（Ｙ４）：－Ｃ（Ｒｎ）（Ｈ）（Ａｒ）
　式（Ｙ１）及び式（Ｙ２）中、Ｒｘ１～Ｒｘ３は、それぞれ独立に、アルキル基（直鎖状又は分岐鎖状）、シクロアルキル基（単環又は多環）、アルケニル基（直鎖状又は分岐鎖状）、又は、アリール基（単環又は多環）を表す。なお、Ｒｘ１～Ｒｘ３の全てがアルキル基（直鎖状又は分岐鎖状）である場合、Ｒｘ１～Ｒｘ３のうち少なくとも２つはメチル基であることが好ましい。
　なかでも、Ｒｘ１～Ｒｘ３は、それぞれ独立に、直鎖状又は分岐鎖状のアルキル基を表すことが好ましく、Ｒｘ１～Ｒｘ３は、それぞれ独立に、直鎖状のアルキル基を表すことがより好ましい。
　Ｒｘ１～Ｒｘ３の２つが結合して、単環又は多環を形成してもよい。
　Ｒｘ１～Ｒｘ３のアルキル基としては、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ｎ－ブチル基、イソブチル基、及び、ｔ－ブチル基等の炭素数１～５のアルキル基が好ましい。
　Ｒｘ１～Ｒｘ３のシクロアルキル基としては、シクロペンチル基、及び、シクロヘキシル基等の単環のシクロアルキル基、並びに、ノルボルニル基、テトラシクロデカニル基、テトラシクロドデカニル基、及び、アダマンチル基等の多環のシクロアルキル基が好ましい。
　Ｒｘ１～Ｒｘ３のアリール基としては、炭素数６～１０のアリール基が好ましく、例えば、フェニル基、ナフチル基、及び、アントリル基が挙げられる。
　Ｒｘ１～Ｒｘ３のアルケニル基としては、ビニル基が好ましい。
　Ｒｘ１～Ｒｘ３の２つが結合して形成される環としては、シクロアルキル基が好ましい。Ｒｘ１～Ｒｘ３の２つが結合して形成されるシクロアルキル基としては、シクロペンチル基、若しくは、シクロヘキシル基等の単環のシクロアルキル基、又は、ノルボルニル基、テトラシクロデカニル基、テトラシクロドデカニル基、若しくは、アダマンチル基等の多環のシクロアルキル基が好ましく、炭素数５～６の単環のシクロアルキル基がより好ましい。
　Ｒｘ１～Ｒｘ３の２つが結合して形成されるシクロアルキル基は、環を構成するメチレン基の１つが、酸素原子等のヘテロ原子、カルボニル基等のヘテロ原子を含む基、又は、ビニリデン基で置き換わっていてもよい。これらのシクロアルキル基は、シクロアルカン環を構成するエチレン基の１つ以上が、ビニレン基で置き換わっていてもよい。
　式（Ｙ１）又は式（Ｙ２）で表される基は、例えば、Ｒｘ１がメチル基又はエチル基であり、Ｒｘ２とＲｘ３とが結合して上述のシクロアルキル基を形成している態様が好ましい。
　本発明の組成物が、例えば、ＥＵＶ露光用レジスト組成物である場合、Ｒｘ１～Ｒｘ３で表されるアルキル基、シクロアルキル基、アルケニル基、アリール基、及び、Ｒｘ１～Ｒｘ３の２つが結合して形成される環は、更に、置換基として、フッ素原子又はヨウ素原子を有していることも好ましい。
　式（Ｙ３）中、Ｒ３６～Ｒ３８は、それぞれ独立に、水素原子又は１価の有機基を表す。Ｒ３７とＲ３８とは、互いに結合して環を形成してもよい。１価の有機基としては、アルキル基、シクロアルキル基、アリール基、アラルキル基、及び、アルケニル基が挙げられる。Ｒ３６は水素原子であることも好ましい。
　なお、上記アルキル基、シクロアルキル基、アリール基、及び、アラルキル基には、酸素原子等のヘテロ原子及び／又はカルボニル基等のヘテロ原子を含む基が含まれていてもよい。例えば、上記アルキル基、シクロアルキル基、アリール基、及び、アラルキル基において、メチレン基の１つ以上が、酸素原子等のヘテロ原子及び／又はカルボニル基等のヘテロ原子を含む基で置き換わっていてもよい。
　Ｒ３８は、繰り返し単位の主鎖が有する別の置換基と互いに結合して、環を形成してもよい。Ｒ３８と繰り返し単位の主鎖が有する別の置換基とが互いに結合して形成する基は、メチレン基等のアルキレン基が好ましい。
　レジスト組成物が、例えば、ＥＵＶ露光用レジスト組成物である場合、Ｒ３６～Ｒ３８で表される１価の有機基、及び、Ｒ３７とＲ３８とが互いに結合して形成される環は、更に、置換基として、フッ素原子又はヨウ素原子を有していることも好ましい。
　式（Ｙ３）としては、下記式（Ｙ３－１）で表される基が好ましい。
Figure JPOXMLDOC01-appb-C000027
　ここで、Ｌ１及びＬ２は、それぞれ独立に、水素原子、アルキル基、シクロアルキル基、アリール基、又は、これらを組み合わせた基（例えば、アルキル基とアリール基とを組み合わせた基）を表す。
　Ｍは、単結合又は２価の連結基を表す。
　Ｑは、ヘテロ原子を含んでいてもよいアルキル基、ヘテロ原子を含んでいてもよいシクロアルキル基、ヘテロ原子を含んでいてもよいアリール基、アミノ基、アンモニウム基、メルカプト基、シアノ基、アルデヒド基、又は、これらを組み合わせた基（例えば、アルキル基とシクロアルキル基とを組み合わせた基）を表す。
　アルキル基及びシクロアルキル基は、例えば、メチレン基の１つが、酸素原子等のヘテロ原子、又は、カルボニル基等のヘテロ原子を含む基で置き換わっていてもよい。
　なお、Ｌ１及びＬ２のうち一方は水素原子であり、他方はアルキル基、シクロアルキル基、アリール基、又は、アルキレン基とアリール基とを組み合わせた基であることが好ましい。
　Ｑ、Ｍ、及びＬ１の少なくとも２つが結合して環（好ましくは、５員若しくは６員環）を形成してもよい。
　パターンの微細化の点では、Ｌ２が２級又は３級アルキル基であることが好ましく、３級アルキル基であることがより好ましい。２級アルキル基としては、イソプロピル基、シクロヘキシル基、及び、ノルボルニル基が挙げられ、３級アルキル基としては、ｔｅｒｔ－ブチル基、及び、アダマンタン基が挙げられる。これらの態様では、Ｔｇ（ガラス転移温度）及び活性化エネルギーが高くなるため、膜強度の担保に加え、かぶりの抑制ができる。
　本発明の組成物が、例えば、ＥＵＶ露光用レジスト組成物である場合、Ｌ１及びＬ２で表される、アルキル基、シクロアルキル基、アリール基、及び、これらを組み合わせた基は、更に、置換基として、フッ素原子又はヨウ素原子を有していることも好ましい。上記アルキル基、シクロアルキル基、アリール基、及び、アラルキル基には、フッ素原子及びヨウ素原子以外に、酸素原子等のヘテロ原子が含まれていることも好ましい。具体的には、上記アルキル基、シクロアルキル基、アリール基、及び、アラルキル基は、例えば、メチレン基の１つが、酸素原子等のヘテロ原子、又は、カルボニル基等のヘテロ原子を含む基で置き換わっていてもよい。
　本発明の組成物が、例えば、ＥＵＶ露光用レジスト組成物である場合、Ｑで表されるヘテロ原子を含んでいてもよいアルキル基、ヘテロ原子を含んでいてもよいシクロアルキル基、ヘテロ原子を含んでいてもよいアリール基、アミノ基、アンモニウム基、メルカプト基、シアノ基、アルデヒド基、及び、これらを組み合わせた基において、ヘテロ原子としては、フッ素原子、ヨウ素原子及び酸素原子からなる群から選択されるヘテロ原子であることも好ましい。
　式（Ｙ４）中、Ａｒは、芳香環基を表す。Ｒｎは、アルキル基、シクロアルキル基、又は、アリール基を表す。ＲｎとＡｒとは互いに結合して非芳香族環を形成してもよい。Ａｒとしては、アリール基が好ましい。
　レジスト組成物が、例えば、ＥＵＶ露光用レジスト組成物である場合、Ａｒで表される芳香環基、並びに、Ｒｎで表されるアルキル基、シクロアルキル基、及び、アリール基は、置換基としてフッ素原子又はヨウ素原子を有していることも好ましい。
　繰り返し単位の酸分解性が優れる点から、極性基を保護する脱離基において、極性基（又はその残基）に非芳香族環が直接結合している場合、上記非芳香族環中の、上記極性基（又はその残基）と直接結合している環員原子に隣接する環員原子は、置換基としてフッ素原子等のハロゲン原子を有さないことも好ましい。
　酸の作用により脱離する基は、他にも、３－メチル－２－シクロペンテニル基のような置換基（アルキル基等）を有する２－シクロペンテニル基、及び、１，１，４，４－テトラメチルシクロヘキシル基のような置換基（アルキル基等）を有するシクロヘキシル基でもよい。
　酸分解性基を有する繰り返し単位としては、式（Ａ）で表される繰り返し単位も好ましい。
Figure JPOXMLDOC01-appb-C000028
　Ｌ１は、フッ素原子又はヨウ素原子を有していてもよい２価の連結基を表し、Ｒ１は水素原子、フッ素原子、ヨウ素原子、フッ素原子若しくはヨウ素原子を有していてもよいアルキル基、又は、フッ素原子若しくはヨウ素原子を有していてもよいアリール基を表し、Ｒ２は酸の作用によって脱離し、フッ素原子又はヨウ素原子を有していてもよい脱離基を表す。ただし、Ｌ１、Ｒ１、及びＲ２のうち少なくとも１つは、フッ素原子又はヨウ素原子を有する。
　Ｌ１で表される、フッ素原子又はヨウ素原子を有していてもよい２価の連結基としては、－ＣＯ－、－Ｏ－、－Ｓ－、－ＳＯ－、－ＳＯ２－、フッ素原子又はヨウ素原子を有していてもよい炭化水素基（例えば、アルキレン基、シクロアルキレン基、アルケニレン基、及び、アリーレン基等）、及び、これらの複数が連結した連結基が挙げられる。なかでも、Ｌ１としては、－ＣＯ－、アリーレン基、又は、－アリーレン基－フッ素原子若しくはヨウ素原子を有するアルキレン基－が好ましく、－ＣＯ－、又は、－アリーレン基－フッ素原子若しくはヨウ素原子を有するアルキレン基－がより好ましい。
　アリーレン基としては、フェニレン基が好ましい。
　アルキレン基は、直鎖状であっても、分岐鎖状であってもよい。アルキレン基の炭素数は特に制限されないが、１～１０が好ましく、１～３がより好ましい。
　フッ素原子又はヨウ素原子を有するアルキレン基に含まれるフッ素原子及びヨウ素原子の合計数は特に制限されないが、２以上が好ましく、２～１０がより好ましく、３～６が更に好ましい。
　Ｒ１で表されるアルキル基は、直鎖状であっても、分岐鎖状であってもよい。アルキル基の炭素数は特に制限されないが、１～１０が好ましく、１～３がより好ましい。
　Ｒ１で表される、フッ素原子又はヨウ素原子を有するアルキル基に含まれる、フッ素原子及びヨウ素原子の合計数は特に制限されないが、１以上が好ましく、１～５がより好ましく、１～３が更に好ましい。
　Ｒ１で表されるアルキル基は、ハロゲン原子以外の酸素原子等のヘテロ原子を含んでいてもよい。
　Ｒ２で表される、フッ素原子又はヨウ素原子を有していてもよい脱離基としては、上述した式（Ｙ１）～（Ｙ４）で表され、かつ、フッ素原子又はヨウ素原子を有する脱離基が挙げられる。
　酸分解性基を有する繰り返し単位としては、式（ＡＩ）で表される繰り返し単位も好ましい。
Figure JPOXMLDOC01-appb-C000029
　式（ＡＩ）において、Ｘａ１は、水素原子、又は、置換基を有していてもよいアルキル基を表す。Ｔは、単結合、又は、２価の連結基を表す。Ｒｘ１～Ｒｘ３は、それぞれ独立に、アルキル基（直鎖状又は分岐鎖状）、シクロアルキル基（単環又は多環）、アルケニル基（直鎖状又は分岐鎖状）、又は、アリール（単環又は多環）基を表す。ただし、Ｒｘ１～Ｒｘ３の全てがアルキル基（直鎖状、又は分岐鎖状）である場合、Ｒｘ１～Ｒｘ３のうち少なくとも２つはメチル基であることが好ましい。
　Ｒｘ１～Ｒｘ３の２つが結合して、単環又は多環（単環又は多環のシクロアルキル基等）を形成してもよい。
　Ｘａ１により表される、置換基を有していてもよいアルキル基としては、例えば、メチル基又は－ＣＨ２－Ｒ１１で表される基が挙げられる。Ｒ１１は、ハロゲン原子（フッ素原子等）、水酸基、又は、１価の有機基を表す。Ｒ１１で表される１価の有機基としては、例えば、ハロゲン原子が置換していてもよい炭素数５以下のアルキル基、ハロゲン原子が置換していてもよい炭素数５以下のアシル基、及び、ハロゲン原子が置換していてもよい炭素数５以下のアルコキシ基が挙げられ、炭素数３以下のアルキル基が好ましく、メチル基がより好ましい。Ｘａ１としては、水素原子、メチル基、トリフルオロメチル基、又は、ヒドロキシメチル基が好ましい。
　Ｔの２価の連結基としては、アルキレン基、芳香環基、－ＣＯＯ－Ｒｔ－基、及び、－Ｏ－Ｒｔ－基が挙げられる。式中、Ｒｔは、アルキレン基、又は、シクロアルキレン基を表す。
　Ｔは、単結合又は－ＣＯＯ－Ｒｔ－基が好ましい。Ｔが－ＣＯＯ－Ｒｔ－基を表す場合、Ｒｔとしては、炭素数１～５のアルキレン基が好ましく、－ＣＨ２－基、－（ＣＨ２）２－基、又は、－（ＣＨ２）３－基がより好ましい。
　Ｒｘ１～Ｒｘ３のアルキル基としては、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ｎ－ブチル基、イソブチル基、及び、ｔ－ブチル基等の炭素数１～４のアルキル基が好ましい。
　Ｒｘ１～Ｒｘ３のシクロアルキル基としては、シクロペンチル基、及び、シクロヘキシル基等の単環のシクロアルキル基、又は、ノルボルニル基、テトラシクロデカニル基、テトラシクロドデカニル基、及び、アダマンチル基等の多環のシクロアルキル基が好ましい。
　Ｒｘ１～Ｒｘ３のアリール基としては、炭素数６～１０のアリール基が好ましく、例えば、フェニル基、ナフチル基、及び、アントリル基が挙げられる。
　Ｒｘ１～Ｒｘ３のアルケニル基としては、ビニル基が好ましい。
　Ｒｘ１～Ｒｘ３の２つが結合して形成されるシクロアルキル基としては、シクロペンチル基、及び、シクロヘキシル基等の単環のシクロアルキル基が好ましい。また、ノルボルニル基、テトラシクロデカニル基、テトラシクロドデカニル基、及び、アダマンチル基等の多環のシクロアルキル基も好ましい。なかでも、炭素数５～６の単環のシクロアルキル基が好ましい。
　Ｒｘ１～Ｒｘ３の２つが結合して形成されるシクロアルキル基は、例えば、環を構成するメチレン基の１つが、酸素原子等のヘテロ原子、カルボニル基等のヘテロ原子を含む基、又は、ビニリデン基で置き換わっていてもよい。また、これらのシクロアルキル基は、シクロアルカン環を構成するエチレン基の１つ以上が、ビニレン基で置き換わっていてもよい。
　式（ＡＩ）で表される繰り返し単位は、例えば、Ｒｘ１がメチル基又はエチル基であり、Ｒｘ２とＲｘ３とが結合して上述のシクロアルキル基を形成している態様が好ましい。
　上記各基が置換基を有する場合、置換基としては、例えば、アルキル基（炭素数１～４）、ハロゲン原子、水酸基、アルコキシ基（炭素数１～４）、カルボキシル基、及び、アルコキシカルボニル基（炭素数２～６）が挙げられる。置換基中の炭素数は、８以下が好ましい。
　式（ＡＩ）で表される繰り返し単位としては、酸分解性（メタ）アクリル酸３級アルキルエステル系繰り返し単位（Ｘａ１が水素原子又はメチル基を表し、かつ、Ｔが単結合を表す繰り返し単位）が好ましい。
　酸分解性基を有する繰り返し単位の具体例を以下に示すが、これに限定されない。なお、式中、Ｘａ１は、Ｈ、ＣＨ３、ＣＦ３、又は、ＣＨ２ＯＨを表し、Ｒｘａ及びＲｘｂは、それぞれ独立に、炭素数１～５の直鎖状又は分岐鎖状のアルキル基を表す。
Figure JPOXMLDOC01-appb-C000030
Figure JPOXMLDOC01-appb-C000031
Figure JPOXMLDOC01-appb-C000032
Figure JPOXMLDOC01-appb-C000033
Figure JPOXMLDOC01-appb-C000034
　樹脂（Ａ）は、酸分解性基を有する繰り返し単位として、不飽和結合を含む酸分解性基を有する繰り返し単位を有していてもよい。
　不飽和結合を含む酸分解性基を有する繰り返し単位としては、式（Ｂ）で表される繰り返し単位が好ましい。
Figure JPOXMLDOC01-appb-C000035
　式（Ｂ）において、Ｘｂは、水素原子、ハロゲン原子、又は、置換基を有していてもよいアルキル基を表す。Ｌは、単結合、又は、置換基を有してもよい２価の連結基を表す。Ｒｙ１～Ｒｙ３は、それぞれ独立に、直鎖状若しくは分岐鎖状のアルキル基、単環状若しくは多環状のシクロアルキル基、アルケニル基、アルキニル基、又は、単環若しくは多環のアリール基を表す。ただし、Ｒｙ１～Ｒｙ３のうち少なくとも１つはアルケニル基、アルキニル基、単環若しくは多環のシクロアルケニル基、又は、単環若しくは多環のアリール基を表す。
　Ｒｙ１～Ｒｙ３の２つが結合して、単環又は多環（単環又は多環のシクロアルキル基、シクロアルケニル基等）を形成してもよい。
　Ｘｂにより表される、置換基を有していてもよいアルキル基としては、例えば、メチル基又は－ＣＨ２－Ｒ１１で表される基が挙げられる。Ｒ１１は、ハロゲン原子（フッ素原子等）、水酸基、又は、１価の有機基を表し、例えば、ハロゲン原子が置換していてもよい炭素数５以下のアルキル基、ハロゲン原子が置換していてもよい炭素数５以下のアシル基、及び、ハロゲン原子が置換していてもよい炭素数５以下のアルコキシ基が挙げられ、炭素数３以下のアルキル基が好ましく、メチル基がより好ましい。Ｘｂとしては、水素原子、フッ素原子、メチル基、トリフルオロメチル基、又は、ヒドロキシメチル基が好ましい。
　Ｌの２価の連結基としては、－Ｒｔ－基、－ＣＯ－基、－ＣＯＯ－Ｒｔ－基、－ＣＯＯ－Ｒｔ－ＣＯ－基、－Ｒｔ－ＣＯ－基、及び、－Ｏ－Ｒｔ－基が挙げられる。式中、Ｒｔは、アルキレン基、シクロアルキレン基、又は、芳香環基を表し、芳香環基が好ましい。
　Ｌとしては、－Ｒｔ－基、－ＣＯ－基、－ＣＯＯ－Ｒｔ－ＣＯ－基、又は、－Ｒｔ－ＣＯ－基が好ましい。Ｒｔは、ハロゲン原子、水酸基、アルコキシ基等の置換基を有していてもよい。
　Ｒｙ１～Ｒｙ３のアルキル基としては、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ｎ－ブチル基、イソブチル基、及び、ｔ－ブチル基等の炭素数１～４のアルキル基が好ましい。
　Ｒｙ１～Ｒｙ３のシクロアルキル基としては、シクロペンチル基、及び、シクロヘキシル基等の単環のシクロアルキル基、又はノルボルニル基、テトラシクロデカニル基、テトラシクロドデカニル基、及び、アダマンチル基等の多環のシクロアルキル基が好ましい。
　Ｒｙ１～Ｒｙ３のアリール基としては、炭素数６～１０のアリール基が好ましく、例えば、フェニル基、ナフチル基、及び、アントリル基が挙げられる。
　Ｒｙ１～Ｒｙ３のアルケニル基としては、ビニル基が好ましい。
　Ｒｙ１～Ｒｙ３のアルキニル基としては、エチニル基が好ましい。
　Ｒｙ１～Ｒｙ３のシクロアルケニル基としては、シクロペンチル基、及び、シクロヘキシル基等の単環のシクロアルキル基の一部に二重結合を含む構造が好ましい。
　Ｒｙ１～Ｒｙ３の２つが結合して形成されるシクロアルキル基としては、シクロペンチル基、及び、シクロヘキシル基等の単環のシクロアルキル基、又は、ノルボルニル基、テトラシクロデカニル基、テトラシクロドデカニル基、及び、アダマンチル基等の多環のシクロアルキル基が好ましい。なかでも、炭素数５～６の単環のシクロアルキル基がより好ましい。
　Ｒｙ１～Ｒｙ３の２つが結合して形成されるシクロアルキル基、又は、シクロアルケニル基は、例えば、環を構成するメチレン基の１つが、酸素原子等のヘテロ原子、カルボニル基、－ＳＯ２－基及び－ＳＯ３－基等のヘテロ原子を含む基、ビニリデン基、又は、それらの組み合わせで置き換わっていてもよい。また、これらのシクロアルキル基又はシクロアルケニル基は、シクロアルカン環又はシクロアルケン環を構成するエチレン基の１つ以上が、ビニレン基で置き換わっていてもよい。
　式（Ｂ）で表される繰り返し単位は、例えば、Ｒｙ１がメチル基、エチル基、ビニル基、アリル基、又は、アリール基であり、Ｒｙ２とＲｙ３とが結合して上述のシクロアルキル基又はシクロアルケニル基を形成している態様が好ましい。
　上記各基が置換基を有する場合、置換基としては、例えば、アルキル基（炭素数１～４）、ハロゲン原子、水酸基、アルコキシ基（炭素数１～４）、カルボキシル基、及び、アルコキシカルボニル基（炭素数２～６）が挙げられる。置換基中の炭素数は、８以下が好ましい。
　式（Ｂ）で表される繰り返し単位としては、好ましくは、酸分解性（メタ）アクリル酸３級エステル系繰り返し単位（Ｘｂが水素原子又はメチル基を表し、かつ、Ｌが－ＣＯ－基を表す繰り返し単位）、酸分解性ヒドロキシスチレン３級アルキルエーテル系繰り返し単位（Ｘｂが水素原子又はメチル基を表し、かつ、Ｌがフェニル基を表す繰り返し単位）、酸分解性スチレンカルボン酸３級エステル系繰り返し単位（Ｘｂが水素原子又はメチル基を表し、かつ、Ｌが－Ｒｔ－ＣＯ－基（Ｒｔは芳香族基）を表す繰り返し単位）である。
　不飽和結合を含む酸分解性基を有する繰り返し単位の含有量は、樹脂（Ａ）中の全繰り返し単位に対して、１５モル％以上が好ましく、２０モル％以上がより好ましく、３０モル％以上が更に好ましい。また、その上限値としては、樹脂（Ａ）中の全繰り返し単位に対して、８０モル％以下が好ましく、７０モル％以下がより好ましく、６０モル％以下が更に好ましい。
　不飽和結合を含む酸分解性基を有する繰り返し単位の具体例を以下に示すが、これに限定されない。なお、式中、Ｘｂ及びＬ１は上記記載の置換基、連結基のいずれかを表し、Ａｒは芳香族基を表し、Ｒは、水素原子、アルキル基、シクロアルキル基、アリール基、アラルキル基、アルケニル基、水酸基、アルコキシ基、アシロキシ基、シアノ基、ニトロ基、アミノ基、ハロゲン原子、エステル基（－ＯＣＯＲ’’’又は－ＣＯＯＲ’’’、Ｒ’’’は炭素数１～２０のアルキル基又はフッ素化アルキル基）、又は、カルボキシル基等の置換基を表し、Ｒ’は直鎖状若しくは分岐鎖状のアルキル基、単環状若しくは多環状のシクロアルキル基、アルケニル基、アルキニル基、又は、単環若しくは多環のアリール基を表し、Ｑは酸素原子等のヘテロ原子、カルボニル基、－ＳＯ２－基及び－ＳＯ３－基等のヘテロ原子を含む基、ビニリデン基、又はそれらの組み合わせを表し、ｎ、ｍ及びｌは０以上の整数を表す。
Figure JPOXMLDOC01-appb-C000036
Figure JPOXMLDOC01-appb-C000037
Figure JPOXMLDOC01-appb-C000038
Figure JPOXMLDOC01-appb-C000039
　酸分解性基を有する繰り返し単位の含有量は、樹脂（Ａ）中の全繰り返し単位に対して、１５モル％以上が好ましく、２０モル％以上がより好ましく、３０モル％以上が更に好ましい。また、その上限値としては、樹脂（Ａ）中の全繰り返し単位に対して、９０モル％以下が好ましく、８０モル％以下がより好ましく、７０モル％以下が更に好ましく、６０モル％以下が特に好ましい。
　樹脂（Ａ）は、以下のＡ群からなる群から選択される少なくとも１種の繰り返し単位、及び／又は、以下のＢ群からなる群から選択される少なくとも１種の繰り返し単位を含んでいてもよい。
Ａ群：以下の（２０）～（２５）の繰り返し単位からなる群。
（２０）後述する、酸基を有する繰り返し単位
（２１）後述する、酸分解性基及び酸基のいずれも有さず、フッ素原子、臭素原子又はヨウ素原子を有する繰り返し単位
（２２）後述する、ラクトン基、スルトン基、又はカーボネート基を有する繰り返し単位
（２３）後述する、光酸発生基を有する繰り返し単位
（２４）後述する、式（Ｖ－１）又は下記式（Ｖ－２）で表される繰り返し単位
（２５）主鎖の運動性を低下させるための繰り返し単位
　尚、後述する、式（Ａ）～式（Ｅ）で表される繰り返し単位は、（２５）主鎖の運動性を低下させるための繰り返し単位に相当する。
Ｂ群：以下の（３０）～（３２）の繰り返し単位からなる群。
（３０）後述する、ラクトン基、スルトン基、カーボネート基、水酸基、シアノ基、及びアルカリ可溶性基から選ばれる少なくとも１種類の基を有する繰り返し単位
（３１）後述する、脂環式炭化水素構造を有し、酸分解性を示さない繰り返し単位
（３２）後述する、水酸基及びシアノ基のいずれも有さない、式（ＩＩＩ）で表される繰り返し単位
　樹脂（Ａ）は上記Ａ群からなる群から選択される少なくとも１種の繰り返し単位を有してもよい。本発明の組成物がＥＵＶ露光用の感活性光線性又は感放射線性樹脂組成物として用いられる場合、樹脂（Ａ）は上記Ａ群からなる群から選択される少なくとも１種の繰り返し単位を有することが好ましい。
　樹脂（Ａ）は、フッ素原子及びヨウ素原子の少なくとも一方を含んでもよい。本発明の組成物がＥＵＶ露光用の感活性光線性又は感放射線性樹脂組成物として用いられる場合、樹脂（Ａ）は、フッ素原子及びヨウ素原子の少なくとも一方を含むことが好ましい。樹脂（Ａ）がフッ素原子及びヨウ素原子の両方を含む場合、樹脂（Ａ）は、フッ素原子及びヨウ素原子の両方を含む１つの繰り返し単位を有していてもよいし、樹脂（Ａ）は、フッ素原子を有する繰り返し単位とヨウ素原子を含む繰り返し単位との２種を含んでいてもよい。
　樹脂（Ａ）は、芳香族基を有する繰り返し単位を有してもよい。本発明の組成物がＥＵＶ露光用の感活性光線性又は感放射線性樹脂組成物として用いられる場合、樹脂（Ａ）が、芳香族基を有する繰り返し単位を有することも好ましい。
　樹脂（Ａ）は上記Ｂ群からなる群から選択される少なくとも１種の繰り返し単位を有してもよい。本発明の組成物がＡｒＦ用の感活性光線性又は感放射線性樹脂組成物として用いられる場合、樹脂（Ａ）は上記Ｂ群からなる群から選択される少なくとも１種の繰り返し単位を有することが好ましい。
　なお、本発明の組成物がＡｒＦ用の感活性光線性又は感放射線性樹脂組成物として用いられる場合、樹脂（Ａ）は、フッ素原子及び珪素原子のいずれも含まないことが好ましい。
（酸基を有する繰り返し単位）
　樹脂（Ａ）は、繰り返し単位（ａ）に相当しない酸基を有する繰り返し単位を有していてもよい。
　酸基としては、ｐＫａが１３以下の酸基が好ましい。上記酸基の酸解離定数は、１３以下が好ましく、３～１３がより好ましく、５～１０が更に好ましい。
　樹脂（Ａ）が、ｐＫａが１３以下の酸基を有する場合、樹脂（Ａ）中における酸基の含有量は特に制限されないが、０．２～６．０ｍｍｏｌ／ｇの場合が多い。なかでも、０．８～６．０ｍｍｏｌ／ｇが好ましく、１．２～５．０ｍｍｏｌ／ｇがより好ましく、１．６～４．０ｍｍｏｌ／ｇが更に好ましい。酸基の含有量が上記範囲内であれば、現像が良好に進行し、形成されるパターン形状に優れ、解像性にも優れる。
　酸基としては、例えば、カルボキシル基、フェノール性水酸基、フッ化アルコール基（好ましくはヘキサフルオロイソプロパノール基）、スルホン酸基、スルホンアミド基、又はイソプロパノール基が好ましい。
　上記ヘキサフルオロイソプロパノール基は、フッ素原子の１つ以上（好ましくは１～２つ）が、フッ素原子以外の基（アルコキシカルボニル基等）で置換されてもよい。酸基としては、このように形成された－Ｃ（ＣＦ３）（ＯＨ）－ＣＦ２－も好ましい。また、フッ素原子の１つ以上がフッ素原子以外の基に置換されて、－Ｃ（ＣＦ３）（ＯＨ）－ＣＦ２－を含む環を形成してもよい。
　酸基を有する繰り返し単位は、上述の酸の作用により脱離する基で極性基が保護された構造を有する繰り返し単位、及び後述するラクトン基、スルトン基、又はカーボネート基を有する繰り返し単位とは異なる繰り返し単位であることが好ましい。
　酸基を有する繰り返し単位は、フッ素原子又はヨウ素原子を有していてもよい。
　酸基を有する繰り返し単位としては、以下の繰り返し単位が挙げられる。
Figure JPOXMLDOC01-appb-C000040
Figure JPOXMLDOC01-appb-C000041
　酸基を有する繰り返し単位の含有量は、樹脂（Ａ）中の全繰り返し単位に対して、１０モル％以上が好ましく、１５モル％以上がより好ましい。また、その上限値としては、樹脂（Ａ）中の全繰り返し単位に対して、７０モル％以下が好ましく、６５モル％以下がより好ましく、６０モル％以下が更に好ましい。
（酸分解性基及び酸基のいずれも有さず、フッ素原子、臭素原子又はヨウ素原子を有する繰り返し単位）
　樹脂（Ａ）は、上述した＜酸分解性基を有する繰り返し単位＞及び＜酸基を有する繰り返し単位＞とは別に、酸分解性基及び酸基のいずれも有さず、フッ素原子、臭素原子又はヨウ素原子を有する繰り返し単位（以下、単位Ｘともいう。）を有していてもよい。ここで言う＜酸分解性基及び酸基のいずれも有さず、フッ素原子、臭素原子又はヨウ素原子を有する繰り返し単位＞は、後述の＜ラクトン基、スルトン基、又はカーボネート基を有する繰り返し単位＞、及び＜光酸発生基を有する繰り返し単位＞等の、Ａ群に属する他の種類の繰り返し単位とは異なることが好ましい。
　単位Ｘとしては、式（Ｃ）で表される繰り返し単位が好ましい。
Figure JPOXMLDOC01-appb-C000042
　Ｌ５は、単結合、又はエステル基を表す。Ｒ９は、水素原子、又はフッ素原子若しくはヨウ素原子を有していてもよいアルキル基を表す。Ｒ１０は、水素原子、フッ素原子若しくはヨウ素原子を有していてもよいアルキル基、フッ素原子若しくはヨウ素原子を有していてもよいシクロアルキル基、フッ素原子若しくはヨウ素原子を有していてもよいアリール基、又はこれらを組み合わせた基を表す。
　フッ素原子又はヨウ素原子を有する繰り返し単位を以下に例示する。
Figure JPOXMLDOC01-appb-C000043
　単位Ｘの含有量は、樹脂（Ａ）中の全繰り返し単位に対して、０モル％以上が好ましく、５モル％以上がより好ましく、１０モル％以上が更に好ましい。また、その上限値としては、樹脂（Ａ）中の全繰り返し単位に対して、５０モル％以下が好ましく、４５モル％以下がより好ましく、４０モル％以下が更に好ましい。
　樹脂（Ａ）の繰り返し単位のうち、フッ素原子、臭素原子及びヨウ素原子の少なくとも１つを含む繰り返し単位の合計含有量は、樹脂（Ａ）の全繰り返し単位に対して、１０モル％以上が好ましく、２０モル％以上がより好ましく、３０モル％以上が更に好ましく、４０モル％以上が特に好ましい。上限値は特に制限されないが、例えば、樹脂（Ａ）の全繰り返し単位に対して、１００モル％以下である。
　なお、フッ素原子、臭素原子及びヨウ素原子の少なくとも１つを含む繰り返し単位としては、例えば、フッ素原子、臭素原子又はヨウ素原子を有し、かつ、酸分解性基を有する繰り返し単位、フッ素原子、臭素原子又はヨウ素原子を有し、かつ、酸基を有する繰り返し単位、及びフッ素原子、臭素原子又はヨウ素原子を有する繰り返し単位が挙げられる。
（ラクトン基、スルトン基、又はカーボネート基を有する繰り返し単位）
　樹脂（Ａ）は、ラクトン基、スルトン基、及びカーボネート基からなる群から選択される少なくとも１種を有する繰り返し単位（以下、「単位Ｙ」ともいう。）を有していてもよい。
　単位Ｙは、水酸基、及びヘキサフルオロプロパノール基等の酸基を有さないことも好ましい。
　ラクトン基又はスルトン基としては、ラクトン構造又はスルトン構造を有していればよい。ラクトン構造又はスルトン構造は、５～７員環ラクトン構造又は５～７員環スルトン構造が好ましい。なかでも、ビシクロ構造若しくはスピロ構造を形成する形で５～７員環ラクトン構造に他の環構造が縮環しているもの、又はビシクロ構造若しくはスピロ構造を形成する形で５～７員環スルトン構造に他の環構造が縮環しているものがより好ましい。
　樹脂（Ａ）は、下記式（ＬＣ１－１）～（ＬＣ１－２１）のいずれかで表されるラクトン構造、又は下記式（ＳＬ１－１）～（ＳＬ１－３）のいずれかで表されるスルトン構造の環員原子から、水素原子を１つ以上引き抜いてなるラクトン基又はスルトン基を有する繰り返し単位を有することが好ましく、ラクトン基又はスルトン基が主鎖に直接結合していてもよい。例えば、ラクトン基又はスルトン基の環員原子が、樹脂（Ａ）の主鎖を構成してもよい。
Figure JPOXMLDOC01-appb-C000044
　上記ラクトン構造又はスルトン構造は、置換基（Ｒｂ２）を有していてもよい。好ましい置換基（Ｒｂ２）としては、炭素数１～８のアルキル基、炭素数４～７のシクロアルキル基、炭素数１～８のアルコキシ基、炭素数１～８のアルコキシカルボニル基、カルボキシル基、ハロゲン原子、シアノ基、及び酸分解性基が挙げられる。ｎ２は、０～４の整数を表す。ｎ２が２以上の時、複数存在するＲｂ２は、異なっていてもよく、複数存在するＲｂ２同士が結合して環を形成してもよい。
　式（ＬＣ１－１）～（ＬＣ１－２１）のいずれかで表されるラクトン構造、又は式（ＳＬ１－１）～（ＳＬ１－３）のいずれかで表されるスルトン構造を含む基を有する繰り返し単位としては、例えば、下記式（ＡＩ）で表される繰り返し単位が挙げられる。
Figure JPOXMLDOC01-appb-C000045
　式（ＡＩ）中、Ｒｂ０は、水素原子、ハロゲン原子、又は炭素数１～４のアルキル基を表す。Ｒｂ０のアルキル基が有していてもよい好ましい置換基としては、水酸基、及びハロゲン原子が挙げられる。
　Ｒｂ０のハロゲン原子としては、フッ素原子、塩素原子、臭素原子、及びヨウ素原子が挙げられる。Ｒｂ０は、水素原子又はメチル基が好ましい。
　Ａｂは、単結合、アルキレン基、単環又は多環の脂環式炭化水素構造を有する２価の連結基、エーテル基、エステル基、カルボニル基、カルボキシル基、又はこれらを組み合わせた２価の連結基を表す。なかでも、Ａｂとしては、単結合、又は－Ａｂ１－ＣＯ２－で表される連結基が好ましい。Ａｂ１は、直鎖状若しくは分岐鎖状のアルキレン基、又は単環若しくは多環のシクロアルキレン基であり、メチレン基、エチレン基、シクロヘキシレン基、アダマンチレン基、又はノルボルニレン基が好ましい。
　Ｖは、式（ＬＣ１－１）～（ＬＣ１－２１）のいずれかで表されるラクトン構造の環員原子から水素原子を１つ引き抜いてなる基、又は式（ＳＬ１－１）～（ＳＬ１－３）のいずれかで表されるスルトン構造の環員原子から水素原子を１つ引き抜いてなる基を表す。
　ラクトン基又はスルトン基を有する繰り返し単位に、光学異性体が存在する場合、いずれの光学異性体を用いてもよい。また、１種の光学異性体を単独で用いても、複数の光学異性体を混合して用いてもよい。１種の光学異性体を主に用いる場合、その光学純度（ｅｅ）は９０以上が好ましく、９５以上がより好ましい。
　カーボネート基としては、環状炭酸エステル基が好ましい。
　環状炭酸エステル基を有する繰り返し単位としては、下記式（Ａ－１）で表される繰り返し単位が好ましい。
Figure JPOXMLDOC01-appb-C000046
　式（Ａ－１）中、ＲＡ １は、水素原子、ハロゲン原子、又は１価の有機基（好ましくはメチル基）を表す。ｎは０以上の整数を表す。ＲＡ ２は、置換基を表す。ｎが２以上の場合、複数存在するＲＡ ２は、それぞれ同一でも異なっていてもよい。Ａは、単結合又は２価の連結基を表す。上記２価の連結基としては、アルキレン基、単環又は多環の脂環式炭化水素構造を有する２価の連結基、エーテル基、エステル基、カルボニル基、カルボキシル基、又はこれらを組み合わせた２価の連結基が好ましい。Ｚは、式中の－Ｏ－ＣＯ－Ｏ－で表される基と共に単環又は多環を形成する原子団を表す。
　単位Ｙを以下に例示する。式中、Ｒｘは、水素原子、－ＣＨ３、－ＣＨ２ＯＨまたは－ＣＦ３を表す。
Figure JPOXMLDOC01-appb-C000047
Figure JPOXMLDOC01-appb-C000048
Figure JPOXMLDOC01-appb-C000049
　単位Ｙの含有量は、樹脂（Ａ）中の全繰り返し単位に対して、１モル％以上が好ましく、１０モル％以上がより好ましい。また、その上限値としては、樹脂（Ａ）中の全繰り返し単位に対して、８５モル％以下が好ましく、８０モル％以下がより好ましく、７０モル％以下が更に好ましく、６０モル％以下が特に好ましい。
（光酸発生基を有する繰り返し単位）
　樹脂（Ａ）は、活性光線又は放射線の照射により分解して酸を発生する基（以下、「光酸発生基」ともいう）を有する繰り返し単位を有していてもよい。
　光酸発生基を有する繰り返し単位としては、式（４）で表される繰り返し単位が挙げられる。
Figure JPOXMLDOC01-appb-C000050
　Ｒ４１は、水素原子又はメチル基を表す。Ｌ４１は、単結合、又は２価の連結基を表す。Ｌ４２は、２価の連結基を表す。Ｒ４０は、活性光線又は放射線の照射により分解して側鎖に酸を発生させる構造部位を表す。
　また、光酸発生基を有する繰り返し単位は、下記一般式（Ｓ－１）で表される繰り返し単位であることが好ましい。
Figure JPOXMLDOC01-appb-C000051
一般式（Ｓ－１）中、
Ｒ２１は、水素原子、アルキル基、アリール基、又はハロゲン原子を表す。
Ｘ１は、単結合又は２価の連結基を表す。
Ｒｃ１～Ｒｃ３は、それぞれ独立に、アルキル基、アリール基、又はヘテロアリール基を表す。Ｒｃ１～Ｒｃ３のうち２つが結合して環構造を形成してもよい。
　一般式（Ｓ－１）中、Ｒ２１は水素原子、アルキル基、アリール基、又はハロゲン原子を表す。
　Ｒ２１のアルキル基としては、好ましくは置換基を有していても良いメチル基、エチル基、プロピル基、イソプロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ヘキシル基、２－エチルヘキシル基、オクチル基、ドデシル基など炭素数２０以下のアルキル基が挙げられ、より好ましくは炭素数８以下のアルキル基が挙げられる。
　アリール基としては、置換基を有していても良い炭素数６～１４個の単環、多環の芳香族基が好ましく、具体的にはフェニル基、トリル基、クロロフェニル基、メトキシフェニル基、ナフチル基等が挙げられる。またアリール基同士が結合して、複環を形成していてもよい。
　ハロゲン原子としては、フッ素原子、塩素原子、臭素原子及びヨウ素原子が挙げられ、フッ素原子がより好ましい。
　Ｒ２１は水素原子又はアルキル基であることが好ましく、水素原子又は炭素数８以下のアルキル基であることがより好ましく、水素原子又はメチル基であることが更に好ましい。
　Ｘ１が２価の連結基を表す場合の２価の連結基としては、アリーレン基、ヘテロアリーレン基、アルキレン基、シクロアルキレン基、－Ｏ－、－ＳＯ２－、－ＣＯ－、－Ｎ（Ｒ３３）－又はこれらの複数を組み合わせた２価の連結基が好ましい。
　Ｒ３３は、水素原子、アルキル基、シクロアルキル基、アルケニル基、アリール基又はアラルキル基を表す。
　Ｒ３３のアルキル基としては、好ましくは置換基を有していても良いメチル基、エチル基、プロピル基、イソプロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ヘキシル基、２－エチルヘキシル基、オクチル基、ドデシル基など炭素数２０以下のアルキル基が挙げられ、より好ましくは炭素数８以下のアルキル基が挙げられる。
　Ｘ１のアリーレン基は、置換基を有していても良い炭素数６～１４個のものが好ましく、具体的にはフェニレン基、トリレン基、ナフチレン基等が挙げられる。
　Ｘ１のヘテロアリーレン基は、環員としてヘテロ原子を含む２価の芳香族基（２価の芳香族ヘテロ環基）であり、ヘテロ原子としては、酸素原子、硫黄原子、窒素原子などが挙げられる。ヘテロアリーレン基の炭素数は４～２０が好ましく、５～１２がより好ましい。ヘテロアリーレン基としては、例えば、ピロール、フラン、チオフェン、インドール、ベンゾフラン、ベンゾチオフェン等から２つの水素原子を除してなる基が挙げられる。
　Ｘ１のアルキレン基としては、好ましくはメチレン基、エチレン基、プロピレン基、ブチレン基、ヘキシレン基、オクチレン基等の炭素数１～８個のものが挙げられる。
　Ｘ１のシクロアルキレン基としては、好ましくは置換基を有していても良いシクロペンチレン基、シクロヘキシレン基等の炭素数５～８個のものが挙げられる。
　Ｘ１はアリーレン基であることが好ましい。
　一般式（Ａ－１）中、Ｒｃ１～Ｒｃ３はそれぞれ独立にアルキル基、アリール基、又はヘテロアリール基を表す。
　Ｒｃ１～Ｒｃ３のアルキル基としては、好ましくは、炭素数１～２０の直鎖又は分岐アルキル基を挙げることができ、炭素数１～１２の直鎖又は分岐アルキル基がより好ましい。好ましい一態様として、アルキル基として、より好ましくは２－オキソアルキル基、アルコキシカルボニルメチル基を挙げることができる。
　Ｒｃ１～Ｒｃ３のアリール基としては、置換基を有していても良い炭素数６～２０個の単環、多環の芳香族基が好ましく、具体的にはフェニル基、トリル基、クロロフェニル基、メトキシフェニル基、ナフチル基等が挙げられる。またアリール基同士が結合して、複環を形成していてもよい。
　Ｒｃ１～Ｒｃ３のヘテロアリール基は、環員としてヘテロ原子を含む芳香族基（芳香族ヘテロ環基）であり、ヘテロ原子としては、酸素原子、硫黄原子、窒素原子などが挙げられる。ヘテロアリール基の炭素数は４～２０が好ましく、５～１２がより好ましい。ヘテロアリール基としては、例えば、ピロール、フラン、チオフェン、インドール、ベンゾフラン、ベンゾチオフェン等から１つの水素原子を除してなる基が挙げられる。
　Ｒｃ１～Ｒｃ３のアルキル基、アリール基、及びヘテロアリール基は置換基を有していてもよい。好ましい置換基としては、水酸基、ハロゲン原子（例えば、フッ素原子、塩素原子、臭素原子、ヨウ素原子）、ニトロ基、シアノ基、アミド基、スルホンアミド基、アルキル基、アルコキシ基（例えば、メトキシ基、エトキシ基、ヒドロキシエトキシ基、プロポキシ基、ヒドロキシプロポキシ基、ブトキシ基等）、アルコキシカルボニル基（例えば、メトキシカルボニル基、エトキシカルボニル基等）、ホルミル基、アセチル基、ベンゾイル基等のアシル基、アセトキシ基、ブチリルオキシ基等のアシロキシ基、カルボキシ基、並びに、フェニル基及びナフチル基などの芳香環基が挙げられる。
　Ｒｃ１～Ｒｃ３はアルキル基又はアリール基であることが好ましく、アリール基であることがより好ましい。
　アルキル基としては、炭素数１～１０の直鎖又は分岐アルキル基（例えば、メチル基、エチル基、プロピル基、ブチル基、ペンチル基）が好ましい。また、２－オキソアルキル基、アルコキシカルボニルメチル基も好ましい例として挙げることができる。２－オキソアルキル基は、直鎖又は分岐のいずれであってもよく、好ましくは、上記のアルキル基の２位に＞Ｃ＝Ｏを有する基を挙げることができる。
　アリール基としては、炭素数６～１４のアリール基（例えば、フェニル基、ナフチル基）が好ましい。
　光酸発生基を有する繰り返し単位を以下に例示する。
Figure JPOXMLDOC01-appb-C000052
　光酸発生基を有する繰り返し単位に相当するモノマーを以下に例示する。Ｍｅはメチル基を表す。
Figure JPOXMLDOC01-appb-C000053
　そのほか、式（４）で表される繰り返し単位としては、例えば、特開２０１４－０４１３２７号公報の段落［００９４］～［０１０５］に記載された繰り返し単位、及び国際公開第２０１８／１９３９５４号公報の段落［００９４］に記載された繰り返し単位が挙げられる。
　光酸発生基を有する繰り返し単位の含有量は、樹脂（Ａ）中の全繰り返し単位に対して、１モル％以上が好ましく、５モル％以上がより好ましい。また、その上限値としては、樹脂（Ａ）中の全繰り返し単位に対して、４０モル％以下が好ましく、３５モル％以下がより好ましく、３０モル％以下が更に好ましい。
（式（Ｖ－１）又は下記式（Ｖ－２）で表される繰り返し単位）
　樹脂（Ａ）は、下記式（Ｖ－１）、又は下記式（Ｖ－２）で表される繰り返し単位を有していてもよい。
　下記式（Ｖ－１）、及び下記式（Ｖ－２）で表される繰り返し単位は上述の繰り返し単位とは異なる繰り返し単位であることが好ましい。
Figure JPOXMLDOC01-appb-C000054
　式中、
　Ｒ６及びＲ７は、それぞれ独立に、水素原子、水酸基、アルキル基、アルコキシ基、アシロキシ基、シアノ基、ニトロ基、アミノ基、ハロゲン原子、エステル基（－ＯＣＯＲ又は－ＣＯＯＲ：Ｒは炭素数１～６のアルキル基又はフッ素化アルキル基）、又はカルボキシル基を表す。アルキル基としては、炭素数１～１０の直鎖状、分岐鎖状又は環状のアルキル基が好ましい。
　ｎ３は、０～６の整数を表す。
　ｎ４は、０～４の整数を表す。
　Ｘ４は、メチレン基、酸素原子、又は硫黄原子である。
　式（Ｖ－１）又は（Ｖ－２）で表される繰り返し単位を以下に例示する。
　式（Ｖ－１）又は（Ｖ－２）で表される繰り返し単位としては、例えば、国際公開第２０１８／１９３９５４号の段落［０１００］に記載された繰り返し単位が挙げられる。
（主鎖の運動性を低下させるための繰り返し単位）
　樹脂（Ａ）は、発生酸の過剰な拡散又は現像時のパターン崩壊を抑制できる点から、ガラス転移温度（Ｔｇ）が高い方が好ましい。Ｔｇは、９０℃より大きいことが好ましく、１００℃より大きいことがより好ましく、１１０℃より大きいことが更に好ましく、１２５℃より大きいことが特に好ましい。なお、現像液への溶解速度が優れる点から、Ｔｇは４００℃以下が好ましく、３５０℃以下がより好ましい。
　なお、本明細書において、樹脂（Ａ）等のポリマーのガラス転移温度（Ｔｇ）（以下「繰り返し単位のＴｇ」）は、以下の方法で算出する。まず、ポリマー中に含まれる各繰り返し単位のみからなるホモポリマーのＴｇを、Ｂｉｃｅｒａｎｏ法によりそれぞれ算出する。次に、ポリマー中の全繰り返し単位に対する、各繰り返し単位の質量割合（％）を算出する。次に、Ｆｏｘの式（Ｍａｔｅｒｉａｌｓ　Ｌｅｔｔｅｒｓ　６２（２００８）３１５２等に記載）を用いて各質量割合におけるＴｇを算出して、それらを総和して、ポリマーのＴｇ（℃）とする。
　Ｂｉｃｅｒａｎｏ法は、Ｐｒｅｄｉｃｔｉｏｎ　ｏｆ　ｐｏｌｙｍｅｒ　ｐｒｏｐｅｒｔｉｅｓ，　Ｍａｒｃｅｌ　Ｄｅｋｋｅｒ　Ｉｎｃ，　Ｎｅｗ　Ｙｏｒｋ（１９９３）に記載されている。Ｂｉｃｅｒａｎｏ法によるＴｇの算出は、ポリマーの物性概算ソフトウェアＭＤＬ　Ｐｏｌｙｍｅｒ（ＭＤＬ　Ｉｎｆｏｒｍａｔｉｏｎ　Ｓｙｓｔｅｍｓ，　Ｉｎｃ．）を用いて行うことができる。
　樹脂（Ａ）のＴｇを大きくする（好ましくは、Ｔｇを９０℃超とする）には、樹脂（Ａ）の主鎖の運動性を低下させることが好ましい。樹脂（Ａ）の主鎖の運動性を低下させる方法は、以下の（ａ）～（ｅ）の方法が挙げられる。
（ａ）主鎖への嵩高い置換基の導入
（ｂ）主鎖への複数の置換基の導入
（ｃ）主鎖近傍への樹脂（Ａ）間の相互作用を誘発する置換基の導入
（ｄ）環状構造での主鎖形成
（ｅ）主鎖への環状構造の連結
　なお、樹脂（Ａ）は、ホモポリマーのＴｇが１３０℃以上を示す繰り返し単位を有することが好ましい。
　なお、ホモポリマーのＴｇが１３０℃以上を示す繰り返し単位の種類は特に制限されず、Ｂｉｃｅｒａｎｏ法により算出されるホモポリマーのＴｇが１３０℃以上である繰り返し単位であればよい。なお、後述する式（Ａ）～式（Ｅ）で表される繰り返し単位中の官能基の種類によっては、ホモポリマーのＴｇが１３０℃以上を示す繰り返し単位に該当する。
　上記（ａ）の具体的な達成手段の一例としては、樹脂（Ａ）に式（Ａ）で表される繰り返し単位を導入する方法が挙げられる。
Figure JPOXMLDOC01-appb-C000055
　式（Ａ）、ＲＡは、多環構造を含む基を表す。Ｒｘは、水素原子、メチル基、又はエチル基を表す。多環構造を含む基とは、複数の環構造を含む基であり、複数の環構造は縮合していても、縮合していなくてもよい。
　式（Ａ）で表される繰り返し単位の具体例としては、国際公開第２０１８/１９３９５４号の段落［０１０７］～［０１１９］に記載のものが挙げられる。
　上記（ｂ）の具体的な達成手段の一例としては、樹脂（Ａ）に式（Ｂ）で表される繰り返し単位を導入する方法が挙げられる。
Figure JPOXMLDOC01-appb-C000056
　式（Ｂ）中、Ｒｂ１～Ｒｂ４は、それぞれ独立に、水素原子又は有機基を表し、Ｒｂ１～Ｒｂ４のうち少なくとも２つ以上が有機基を表す。
　有機基の少なくとも１つが、繰り返し単位中の主鎖に直接環構造が連結している基である場合、他の有機基の種類は特に制限されない。
　また、有機基のいずれも繰り返し単位中の主鎖に直接環構造が連結している基ではない場合、有機基の少なくとも２つ以上は、水素原子を除く構成原子の数が３つ以上である置換基である。
　式（Ｂ）で表される繰り返し単位の具体例としては、国際公開第２０１８/１９３９５４号の段落［０１１３］～［０１１５］に記載のものが挙げられる。
　上記（ｃ）の具体的な達成手段の一例としては、樹脂（Ａ）に式（Ｃ）で表される繰り返し単位を導入する方法が挙げられる。
Figure JPOXMLDOC01-appb-C000057
　式（Ｃ）中、Ｒｃ１～Ｒｃ４は、それぞれ独立に、水素原子又は有機基を表し、Ｒｃ１～Ｒｃ４のうち少なくとも１つが、主鎖炭素から原子数３以内に水素結合性の水素原子を含む基である。なかでも、樹脂（Ａ）の主鎖間の相互作用を誘発するうえで、原子数２以内（より主鎖近傍側）に水素結合性の水素原子を有することが好ましい。
　式（Ｃ）で表される繰り返し単位の具体例としては、国際公開第２０１８／１９３９５４号の段落［０１１９］～［０１２１］に記載のものが挙げられる。
　上記（ｄ）の具体的な達成手段の一例としては、樹脂（Ａ）に式（Ｄ）で表される繰り返し単位を導入する方法が挙げられる。
Figure JPOXMLDOC01-appb-C000058
　式（Ｄ）中、「Ｃｙｃｌｉｃ」は、環状構造で主鎖を形成している基を表す。環の構成原子数は特に制限されない。
　式（Ｄ）で表される繰り返し単位の具体例としては、国際公開第２０１８/１９３９５４号の段落［０１２６］～［０１２７］に記載のものが挙げられる。
　上記（ｅ）の具体的な達成手段の一例としては、樹脂（Ａ）に式（Ｅ）で表される繰り返し単位を導入する方法が挙げられる。
Figure JPOXMLDOC01-appb-C000059
　式（Ｅ）中、Ｒｅは、それぞれ独立に、水素原子又は有機基を表す。有機基としては、例えば、置換基を有してもよい、アルキル基、シクロアルキル基、アリール基、アラルキル基、及びアルケニル基が挙げられる。
　「Ｃｙｃｌｉｃ」は、主鎖の炭素原子を含む環状基である。環状基に含まれる原子数は特に制限されない。
　式（Ｅ）で表される繰り返し単位の具体例としては、国際公開第２０１８／１９３９５４号の段落［０１３１］～［０１３３］に記載のものが挙げられる。
（ラクトン基、スルトン基、カーボネート基、水酸基、シアノ基、及びアルカリ可溶性基から選ばれる少なくとも１種類の基を有する繰り返し単位）
　樹脂（Ａ）は、ラクトン基、スルトン基、カーボネート基、水酸基、シアノ基、及びアルカリ可溶性基から選ばれる少なくとも１種類の基を有する繰り返し単位を有していてもよい。
　樹脂（Ａ）が有するラクトン基、スルトン基、又はカーボネート基を有する繰り返し単位としては、上述した＜ラクトン基、スルトン基、又はカーボネート基を有する繰り返し単位＞で説明した繰り返し単位が挙げられる。好ましい含有量も上述した＜ラクトン基、スルトン基、又はカーボネート基を有する繰り返し単位＞で説明した通りである。
　樹脂（Ａ）は、水酸基又はシアノ基を有する繰り返し単位を有していてもよい。これにより基板密着性、現像液親和性が向上する。
　水酸基又はシアノ基を有する繰り返し単位は、水酸基又はシアノ基で置換された脂環式炭化水素構造を有する繰り返し単位であることが好ましい。
　水酸基又はシアノ基を有する繰り返し単位は、酸分解性基を有さないことが好ましい。水酸基又はシアノ基を有する繰り返し単位としては、特開２０１４－０９８９２１号公報の段落［００８１］～［００８４］に記載のものが挙げられる。
　樹脂（Ａ）は、アルカリ可溶性基を有する繰り返し単位を有していてもよい。
　アルカリ可溶性基としては、カルボキシル基、スルホンアミド基、スルホニルイミド基、ビススルホニルイミド基、及びα位が電子求引性基で置換された脂肪族アルコール基（例えば、ヘキサフルオロイソプロパノール基）が挙げられ、カルボキシル基が好ましい。樹脂（Ａ）がアルカリ可溶性基を有する繰り返し単位を含むことにより、コンタクトホール用途での解像性が増す。アルカリ可溶性基を有する繰り返し単位としては、特開２０１４－０９８９２１号公報の段落［００８５］及び［００８６］に記載のものが挙げられる。
（脂環式炭化水素構造を有し、酸分解性を示さない繰り返し単位）
　樹脂（Ａ）は、脂環式炭化水素構造を有し、酸分解性を示さない繰り返し単位を有してもよい。これにより液浸露光時にレジスト膜から液浸液への低分子成分の溶出が低減できる。脂環式炭化水素構造を有し、酸分解性を示さない繰り返し単位として、例えば、１－アダマンチル（メタ）アクリレート、ジアマンチル（メタ）アクリレート、トリシクロデカニル（メタ）アクリレート、又はシクロヘキシル（メタ）アクリレート由来の繰り返し単位が挙げられる。
（水酸基及びシアノ基のいずれも有さない、式（ＩＩＩ）で表される繰り返し単位）
　樹脂（Ａ）は、水酸基及びシアノ基のいずれも有さない、式（ＩＩＩ）で表される繰り返し単位を有していてもよい。
Figure JPOXMLDOC01-appb-C000060
　式（ＩＩＩ）中、Ｒ５は少なくとも１つの環状構造を有し、水酸基及びシアノ基のいずれも有さない炭化水素基を表す。
　Ｒａは水素原子、アルキル基又は－ＣＨ２－Ｏ－Ｒａ２基を表す。式中、Ｒａ２は、水素原子、アルキル基又はアシル基を表す。
　水酸基及びシアノ基のいずれも有さない、式（ＩＩＩ）で表される繰り返し単位としては、特開２０１４－０９８９２１号公報の段落［００８７］～［００９４］に記載のものが挙げられる。
（その他の繰り返し単位）
　更に、樹脂（Ａ）は、上述した繰り返し単位以外のその他の繰り返し単位を有してもよい。
　例えば樹脂（Ａ）は、オキサチアン環基を有する繰り返し単位、オキサゾロン環基を有する繰り返し単位、ジオキサン環基を有する繰り返し単位、及びヒダントイン環基を有する繰り返し単位からなる群から選択される繰り返し単位を有していてもよい。
　上述した繰り返し単位以外のその他の繰り返し単位の具体例を以下に例示する。
Figure JPOXMLDOC01-appb-C000061
　樹脂（Ａ）は、上記の繰り返し構造単位以外に、ドライエッチング耐性、標準現像液適性、基板密着性、レジストプロファイル、解像性、耐熱性、及び感度等を調節する目的で様々な繰り返し構造単位を有していてもよい。
　樹脂（Ａ）としては、特に、組成物がＡｒＦ用の感活性光線性又は感放射線性樹脂組成物として用いられる場合、繰り返し単位の全てが、エチレン性不飽和結合を有する化合物に由来する繰り返し単位で構成されることが好ましい。特に、繰り返し単位の全てが（メタ）アクリレート系繰り返し単位で構成されることも好ましい。繰り返し単位の全てが（メタ）アクリレート系繰り返し単位で構成される場合、繰り返し単位の全てがメタクリレート系繰り返し単位であるもの、繰り返し単位の全てがアクリレート系繰り返し単位であるもの、繰り返し単位の全てがメタクリレート系繰り返し単位とアクリレート系繰り返し単位とによるもののいずれのものでも用いることができ、アクリレート系繰り返し単位が全繰り返し単位の５０モル％以下であることが好ましい。
　樹脂（Ａ）は、常法に従って（例えばラジカル重合）合成できる。
　ＧＰＣ法によりポリスチレン換算値として、樹脂（Ａ）の重量平均分子量は、３０，０００以下が好ましく、１，０００～３０，０００がより好ましく、３，０００～３０，０００が更に好ましく、５，０００～１５，０００が特に好ましい。
　樹脂（Ａ）の分散度（分子量分布）は、１～５が好ましく、１～３がより好ましく、１．２～３．０が更に好ましく、１．２～２．０が特に好ましい。分散度が小さいものほど、解像度、及びレジスト形状がより優れ、更に、レジストパターンの側壁がよりスムーズであり、ラフネス性にもより優れる。
　本発明の組成物において、樹脂（Ａ）の含有量は、組成物の全固形分に対して、４０．０～９９．９質量％が好ましく、６０．０～９０．０質量％がより好ましい。
　樹脂（Ａ）は、１種で使用してもよいし、複数併用してもよい。
＜光酸発生剤＞
　本発明の組成物は、活性光線又は放射線の照射によって酸を発生する化合物（Ｂ）（以下、光酸発生剤（Ｂ）、又は化合物（Ｂ）ともいう）を含有していても良い。
　化合物（Ｂ）は、化合物（Ｃ）に相当しない化合物であり、活性光線又は放射線の照射によって、化合物（Ｃ）が発生する酸よりも強い酸を発生する化合物であることが好ましい。
　「化合物（Ｃ）が発生する酸よりも強い酸を発生する」は、化合物（Ｃ）が発生する酸の酸強度よりも、化合物（Ｂ）が発生する酸の酸強度が強いことを示し、典型的には、化合物（Ｂ）が発生する酸の酸解離定数が（ｐＫａ）が、化合物（Ｃ）が発生する酸のｐＫａよりも低いことを示すものである。
　化合物（Ｂ）より発生した酸は、通常、樹脂（Ａ）における酸分解性基と反応する。
　光酸発生剤（Ｂ）は、低分子化合物の形態であってもよく、重合体（例えば、後述する樹脂（Ａ））の一部に組み込まれた形態であってもよい。また、低分子化合物の形態と重合体（例えば、後述する樹脂（Ａ））の一部に組み込まれた形態とを併用してもよい。
　光酸発生剤（Ｂ）が、低分子化合物の形態である場合、光酸発生剤の分子量は３０００以下が好ましく、２０００以下がより好ましく、１０００以下が更に好ましい。下限は特に制限されないが、１００以上が好ましい。
　光酸発生剤（Ｂ）が、重合体の一部に組み込まれた形態である場合、樹脂（Ａ）の一部に組み込まれてもよく、樹脂（Ａ）とは異なる樹脂に組み込まれてもよい。
　本明細書において、光酸発生剤（Ｂ）は、低分子化合物の形態であることが好ましい。
　光酸発生剤（Ｂ）としては、例えば、「Ｍ＋　Ｘ－」で表される化合物（オニウム塩）が挙げられ、露光により有機酸を発生する化合物であることが好ましい。
　上記有機酸として、例えば、スルホン酸（脂肪族スルホン酸、芳香族スルホン酸、及びカンファースルホン酸等）、カルボン酸（脂肪族カルボン酸、芳香族カルボン酸、及びアラルキルカルボン酸等）、カルボニルスルホニルイミド酸、ビス（アルキルスルホニル）イミド酸、及びトリス（アルキルスルホニル）メチド酸が挙げられる。
　「Ｍ＋　Ｘ－」で表される化合物において、Ｍ＋は、有機カチオンを表す。
　有機カチオンとしては特に制限されない。有機カチオンの価数は、１又は２価以上であってもよい。
　なかでも、上記有機カチオンとしては、上記式（ＺａＩ）で表されるカチオン（以下「カチオン（ＺａＩ）」ともいう。）、又は、上記式（ＺａＩＩ）で表されるカチオン（以下「カチオン（ＺａＩＩ）」ともいう。）が好ましい。
　「Ｍ＋　Ｘ－」で表される化合物において、Ｘ－は、有機アニオンを表す。
　有機アニオンとしては、特に制限されず、１又は２価以上の有機アニオンが挙げられる。
　有機アニオンとしては、求核反応を起こす能力が著しく低いアニオンが好ましく、非求核性アニオンがより好ましい。
　非求核性アニオンとしては、例えば、スルホン酸アニオン（脂肪族スルホン酸アニオン、芳香族スルホン酸アニオン、及びカンファースルホン酸アニオン等）、カルボン酸アニオン（脂肪族カルボン酸アニオン、芳香族カルボン酸アニオン、及びアラルキルカルボン酸アニオン等）、スルホニルイミドアニオン、ビス（アルキルスルホニル）イミドアニオン、及びトリス（アルキルスルホニル）メチドアニオンが挙げられる。
　脂肪族スルホン酸アニオン及び脂肪族カルボン酸アニオンにおける脂肪族部位は、直鎖状又は分岐鎖状のアルキル基であっても、シクロアルキル基であってもよく、炭素数１～３０の直鎖状又は分岐鎖状のアルキル基、又は、炭素数３～３０のシクロアルキル基が好ましい。
　上記アルキル基は、例えば、フルオロアルキル基（フッ素原子以外の置換基を有していてもよい。パーフルオロアルキル基であってもよい）であってもよい。
　芳香族スルホン酸アニオン及び芳香族カルボン酸アニオンにおけるアリール基としては、炭素数６～１４のアリール基が好ましく、例えば、フェニル基、トリル基、及び、ナフチル基が挙げられる。
　上記で挙げたアルキル基、シクロアルキル基、及び、アリール基は、置換基を有していてもよい。置換基としては特に制限されないが、例えば、ニトロ基、フッ素原子及び塩素原子等のハロゲン原子、カルボキシル基、水酸基、アミノ基、シアノ基、アルコキシ基（炭素数１～１５が好ましい）、アルキル基（炭素数１～１０が好ましい）、シクロアルキル基（炭素数３～１５が好ましい）、アリール基（炭素数６～１４が好ましい）、アルコキシカルボニル基（炭素数２～７が好ましい）、アシル基（炭素数２～１２が好ましい）、アルコキシカルボニルオキシ基（炭素数２～７が好ましい）、アルキルチオ基（炭素数１～１５が好ましい）、アルキルスルホニル基（炭素数１～１５が好ましい）、アルキルイミノスルホニル基（炭素数１～１５が好ましい）、及び、アリールオキシスルホニル基（炭素数６～２０が好ましい）が挙げられる。
　アラルキルカルボン酸アニオンにおけるアラルキル基としては、炭素数７～１４のアラルキル基が好ましい。
　炭素数７～１４のアラルキル基としては、例えば、ベンジル基、フェネチル基、ナフチルメチル基、ナフチルエチル基、及び、ナフチルブチル基が挙げられる。
　スルホニルイミドアニオンとしては、例えば、サッカリンアニオンが挙げられる。
　ビス（アルキルスルホニル）イミドアニオン、及び、トリス（アルキルスルホニル）メチドアニオンにおけるアルキル基としては、炭素数１～５のアルキル基が好ましい。これらのアルキル基の置換基としては、ハロゲン原子、ハロゲン原子で置換されたアルキル基、アルコキシ基、アルキルチオ基、アルキルオキシスルホニル基、アリールオキシスルホニル基、及び、シクロアルキルアリールオキシスルホニル基が挙げられ、フッ素原子又はフッ素原子で置換されたアルキル基が好ましい。
　また、ビス（アルキルスルホニル）イミドアニオンにおけるアルキル基は、互いに結合して環構造を形成してもよい。これにより、酸強度が増加する。
　その他の非求核性アニオンとしては、例えば、フッ素化燐（例えば、ＰＦ６ －）、フッ素化ホウ素（例えば、ＢＦ４ －）、及び、フッ素化アンチモン（例えば、ＳｂＦ６ －）が挙げられる。
　非求核性アニオンとしては、スルホン酸の少なくともα位がフッ素原子で置換された脂肪族スルホン酸アニオン、フッ素原子若しくはフッ素原子を有する基で置換された芳香族スルホン酸アニオン、アルキル基がフッ素原子で置換されたビス（アルキルスルホニル）イミドアニオン、又は、アルキル基がフッ素原子で置換されたトリス（アルキルスルホニル）メチドアニオンが好ましい。なかでも、パーフルオロ脂肪族スルホン酸アニオン（炭素数４～８が好ましい）、又は、フッ素原子を有するベンゼンスルホン酸アニオンがより好ましく、ノナフルオロブタンスルホン酸アニオン、パーフルオロオクタンスルホン酸アニオン、ペンタフルオロベンゼンスルホン酸アニオン、又は、３，５－ビス（トリフルオロメチル）ベンゼンスルホン酸アニオンが更に好ましい。
　非求核性アニオンとしては、下記式（ＡＮ１）で表されるアニオンも好ましい。
Figure JPOXMLDOC01-appb-C000062
　式（ＡＮ１）中、Ｒ１及びＲ２は、それぞれ独立に、水素原子、又は置換基を表す。
　置換基は特に制限されないが、電子求引性基ではない基が好ましい。電子求引性基ではない基としては、例えば、炭化水素基、水酸基、オキシ炭化水素基、オキシカルボニル炭化水素基、アミノ基、炭化水素置換アミノ基、及び、炭化水素置換アミド基が挙げられる。
　電子求引性基ではない基としては、それぞれ独立に、－Ｒ’、－ＯＨ、－ＯＲ’、－ＯＣＯＲ’、－ＮＨ２、－ＮＲ’２、－ＮＨＲ’、又は、－ＮＨＣＯＲ’が好ましい。Ｒ’は、１価の炭化水素基である。
　上記Ｒ’で表される１価の炭化水素基としては、例えば、メチル基、エチル基、プロピル基、及びブチル基等のアルキル基；エテニル基、プロペニル基、及びブテニル基等のアルケニル基；エチニル基、プロピニル基、及びブチニル基等のアルキニル基等の１価の直鎖状又は分岐鎖状の炭化水素基；シクロプロピル基、シクロブチル基、シクロペンチル基、シクロヘキシル基、ノルボルニル基、及びアダマンチル基等のシクロアルキル基；シクロプロペニル基、シクロブテニル基、シクロペンテニル基、及びノルボルネニル基等のシクロアルケニル基等の１価の脂環炭化水素基；フェニル基、トリル基、キシリル基、メシチル基、ナフチル基、メチルナフチル基、アントリル基、及びメチルアントリル基等のアリール基；ベンジル基、フェネチル基、フェニルプロピル基、ナフチルメチル基、及びアントリルメチル基等のアラルキル基等の１価の芳香族炭化水素基が挙げられる。
　なかでも、Ｒ１及びＲ２は、それぞれ独立に、炭化水素基（シクロアルキル基が好ましい）又は水素原子が好ましい。
　Ｌは、２価の連結基を表す。
　Ｌが複数存在する場合、Ｌは、それぞれ同一でも異なっていてもよい。
　２価の連結基としては、例えば、－Ｏ－ＣＯ－Ｏ－、－ＣＯＯ－、－ＣＯＮＨ－、－ＣＯ－、－Ｏ－、－Ｓ－、－ＳＯ－、－ＳＯ２－、アルキレン基（炭素数１～６が好ましい）、シクロアルキレン基（炭素数３～１５が好ましい）、アルケニレン基（炭素数２～６が好ましい）、及び、これらの複数を組み合わせた２価の連結基が挙げられる。なかでも、２価の連結基としては、－Ｏ－ＣＯ－Ｏ－、－ＣＯＯ－、－ＣＯＮＨ－、－ＣＯ－、－Ｏ－、－ＳＯ２－、－Ｏ－ＣＯ－Ｏ－アルキレン基－、－ＣＯＯ－アルキレン基－、又は、－ＣＯＮＨ－アルキレン基－が好ましく、－Ｏ－ＣＯ－Ｏ－、－Ｏ－ＣＯ－Ｏ－アルキレン基－、－ＣＯＯ－、－ＣＯＮＨ－、－ＳＯ２－、又は、－ＣＯＯ－アルキレン基－がより好ましい。
　Ｌとしては、例えば、下記式（ＡＮ１－１）で表される基が好ましい。
　＊ａ－（ＣＲ２ａ ２）Ｘ－Ｑ－（ＣＲ２ｂ ２）Ｙ－＊ｂ　　　（ＡＮ１－１）
　式（ＡＮ１－１）中、＊ａは、式（ＡＮ１）におけるＲ３との結合位置を表す。
　＊ｂは、式（ＡＮ１）における－Ｃ（Ｒ１）（Ｒ２）－との結合位置を表す。
　Ｘ及びＹは、それぞれ独立に、０～１０の整数を表し、０～３の整数が好ましい。
　Ｒ２ａ及びＲ２ｂは、それぞれ独立に、水素原子又は置換基を表す。
　Ｒ２ａ及びＲ２ｂがそれぞれ複数存在する場合、複数存在するＲ２ａ及びＲ２ｂは、それぞれ同一でも異なっていてもよい。
　ただし、Ｙが１以上の場合、式（ＡＮ１）における－Ｃ（Ｒ１）（Ｒ２）－と直接結合するＣＲ２ｂ ２におけるＲ２ｂは、フッ素原子以外である。
　Ｑは、＊Ａ－Ｏ－ＣＯ－Ｏ－＊Ｂ、＊Ａ－ＣＯ－＊Ｂ、＊Ａ－ＣＯ－Ｏ－＊Ｂ、＊Ａ－Ｏ－ＣＯ－＊Ｂ、＊Ａ－Ｏ－＊Ｂ、＊Ａ－Ｓ－＊Ｂ、又は、＊Ａ－ＳＯ２－＊Ｂを表す。
　ただし、式（ＡＮ１－１）中のＸ＋Ｙが１以上、かつ、式（ＡＮ１－１）中のＲ２ａ及びＲ２ｂのいずれもが全て水素原子である場合、Ｑは、＊Ａ－Ｏ－ＣＯ－Ｏ－＊Ｂ、＊Ａ－ＣＯ－＊Ｂ、＊Ａ－Ｏ－ＣＯ－＊Ｂ、＊Ａ－Ｏ－＊Ｂ、＊Ａ－Ｓ－＊Ｂ、又は、＊Ａ－ＳＯ２－＊Ｂを表す。
　＊Ａは、式（ＡＮ１）におけるＲ３側の結合位置を表し、＊Ｂは、式（ＡＮ１）における－ＳＯ３ －側の結合位置を表す。
　式（ＡＮ１）中、Ｒ３は、有機基を表す。
　上記有機基は、炭素原子を１以上有していれば特に制限はなく、直鎖状の基（例えば、直鎖状のアルキル基）でも、分岐鎖状の基（例えば、ｔ－ブチル基等の分岐鎖状のアルキル基）でもよく、環状の基であってもよい。上記有機基は、置換基を有していても、有していなくてもよい。上記有機基は、ヘテロ原子（酸素原子、硫黄原子、及び／又は、窒素原子等）を有していても、有してなくてもよい。
　なかでも、Ｒ３は、環状構造を有する有機基であることが好ましい。上記環状構造は、単環でも多環でもよく、置換基を有していてもよい。環状構造を含む有機基における環は、式（ＡＮ１）中のＬと直接結合していることが好ましい。
　上記環状構造を有する有機基は、例えば、ヘテロ原子（酸素原子、硫黄原子、及び／又は、窒素原子等）を有していても、有してなくてもよい。ヘテロ原子は、環状構造を形成する炭素原子の１つ以上と置換していてもよい。
　上記環状構造を有する有機基は、例えば、環状構造の炭化水素基、ラクトン環基、及び、スルトン環基が好ましい。なかでも、上記環状構造を有する有機基は、環状構造の炭化水素基が好ましい。
　上記環状構造の炭化水素基は、単環又は多環のシクロアルキル基が好ましい。これらの基は、置換基を有していてもよい。
　上記シクロアルキル基は、単環（シクロヘキシル基等）でも多環（アダマンチル基等）でもよく、炭素数は５～１２が好ましい。
　上記ラクトン基及びスルトン基としては、例えば、上述した式（ＬＣ１－１）～（ＬＣ１－２１）で表される構造、及び、式（ＳＬ１－１）～（ＳＬ１－３）で表される構造のいずれかにおいて、ラクトン構造又はスルトン構造を構成する環員原子から、水素原子を１つ除いてなる基が好ましい。
　非求核性アニオンとしては、ベンゼンスルホン酸アニオンであってもよく、分岐鎖状のアルキル基又はシクロアルキル基によって置換されたベンゼンスルホン酸アニオンであることが好ましい。
　非求核性アニオンとしては、下記式（ＡＮ２）で表されるアニオンも好ましい。
Figure JPOXMLDOC01-appb-C000063
　式（ＡＮ２）中、ｏは、１～３の整数を表す。ｐは、０～１０の整数を表す。ｑは、０～１０の整数を表す。
　Ｘｆは、水素原子、フッ素原子、少なくとも１つのフッ素原子で置換されたアルキル基、又はフッ素原子を有さない有機基を表す。このアルキル基の炭素数は、１～１０が好ましく、１～４がより好ましい。少なくとも１つのフッ素原子で置換されたアルキル基としては、パーフルオロアルキル基が好ましい。
　Ｘｆは、フッ素原子又は炭素数１～４のパーフルオロアルキル基であることが好ましく、フッ素原子又はＣＦ３であることがより好ましく、双方のＸｆがフッ素原子であることが更に好ましい。
　Ｒ４及びＲ５は、それぞれ独立に、水素原子、フッ素原子、アルキル基、又は、少なくとも１つのフッ素原子で置換されたアルキル基を表す。Ｒ４及びＲ５が複数存在する場合、Ｒ４及びＲ５は、それぞれ同一でも異なっていてもよい。
　Ｒ４及びＲ５で表されるアルキル基は、炭素数１～４が好ましい。上記アルキル基は置換基を有していてもよい。Ｒ４及びＲ５としては、水素原子が好ましい。
　Ｌは、２価の連結基を表す。Ｌの定義は、式（ＡＮ１）中のＬと同義である。
　Ｗは、環状構造を含む有機基を表す。なかでも、環状の有機基であることが好ましい。
　環状の有機基としては、例えば、脂環基、アリール基、及び、複素環基が挙げられる。
　脂環基は、単環であってもよく、多環であってもよい。単環の脂環基としては、例えば、シクロペンチル基、シクロヘキシル基、及び、シクロオクチル基等の単環のシクロアルキル基が挙げられる。多環の脂環基としては、例えば、ノルボルニル基、トリシクロデカニル基、テトラシクロデカニル基、テトラシクロドデカニル基、及び、アダマンチル基等の多環のシクロアルキル基が挙げられる。なかでも、ノルボルニル基、トリシクロデカニル基、テトラシクロデカニル基、テトラシクロドデカニル基、及び、アダマンチル基等の炭素数７以上の嵩高い構造を有する脂環基が好ましい。
　アリール基は、単環又は多環であってもよい。上記アリール基としては、例えば、フェニル基、ナフチル基、フェナントリル基、及び、アントリル基が挙げられる。
　複素環基は、単環又は多環であってもよい。なかでも、多環の複素環基である場合、より酸の拡散を抑制できる。複素環基は、芳香族性を有していてもよいし、芳香族性を有していなくてもよい。芳香族性を有している複素環としては、例えば、フラン環、チオフェン環、ベンゾフラン環、ベンゾチオフェン環、ジベンゾフラン環、ジベンゾチオフェン環、及び、ピリジン環が挙げられる。芳香族性を有していない複素環としては、例えば、テトラヒドロピラン環、ラクトン環、スルトン環、及び、デカヒドロイソキノリン環が挙げられる。複素環基における複素環としては、フラン環、チオフェン環、ピリジン環、又は、デカヒドロイソキノリン環が好ましい。
　上記環状の有機基は、置換基を有していてもよい。上記置換基としては、例えば、アルキル基（直鎖状及び分岐鎖状のいずれであってもよく、炭素数１～１２が好ましい）、シクロアルキル基（単環、多環、及び、スピロ環のいずれであってもよく、炭素数３～２０が好ましい）、アリール基（炭素数６～１４が好ましい）、水酸基、アルコキシ基、エステル基、アミド基、ウレタン基、ウレイド基、チオエーテル基、スルホンアミド基、及び、スルホン酸エステル基が挙げられる。なお、環状の有機基を構成する炭素（環形成に寄与する炭素）はカルボニル炭素であってもよい。
　式（ＡＮ２）で表されるアニオンとしては、ＳＯ３ －－ＣＦ２－ＣＨ２－ＯＣＯ－（Ｌ）ｑ’－Ｗ、ＳＯ３ －－ＣＦ２－ＣＨＦ－ＣＨ２－ＯＣＯ－（Ｌ）ｑ’－Ｗ、ＳＯ３ －－ＣＦ２－ＣＯＯ－（Ｌ）ｑ’－Ｗ、ＳＯ３ －－ＣＦ２－ＣＦ２－ＣＨ２－ＣＨ２－（Ｌ）ｑ－Ｗ、又は、ＳＯ３ －－ＣＦ２－ＣＨ（ＣＦ３）－ＯＣＯ－（Ｌ）ｑ’－Ｗが好ましい。ここで、Ｌ、ｑ及びＷは、式（ＡＮ２）と同様である。ｑ’は、０～１０の整数を表す。
　非求核性アニオンとしては、下記式（ＡＮ３）で表される芳香族スルホン酸アニオンも好ましい。
Figure JPOXMLDOC01-appb-C000064
　式（ＡＮ３）中、Ａｒは、アリール基（フェニル基等）を表し、スルホン酸アニオン、及び、－（Ｄ－Ｂ）基以外の置換基を更に有していてもよい。更に有してもよい置換基としては、例えば、フッ素原子及び水酸基が挙げられる。
　ｎは、０以上の整数を表す。ｎとしては、１～４が好ましく、２～３がより好ましく、３が更に好ましい。
　Ｄは、単結合又は２価の連結基を表す。２価の連結基としては、エーテル基、チオエーテル基、カルボニル基、スルホキシド基、スルホン基、スルホン酸エステル基、エステル基、及び、これらの２種以上の組み合わせからなる基が挙げられる。
　Ｂは、炭化水素基を表す。
　Ｂとしては、脂肪族炭化水素基が好ましく、イソプロピル基、シクロヘキシル基、又は更に置換基を有してもよいアリール基（トリシクロヘキシルフェニル基等）がより好ましい。
　非求核性アニオンとしては、ジスルホンアミドアニオンも好ましい。
　ジスルホンアミドアニオンは、例えば、Ｎ－（ＳＯ２－Ｒｑ）２で表されるアニオンである。
　ここで、Ｒｑは置換基を有していてもよいアルキル基を表し、フルオロアルキル基が好ましく、パーフルオロアルキル基がより好ましい。２個のＲｑは互いに結合して環を形成してもよい。２個のＲｑが互いに結合して形成される基は、置換基を有していてもよいアルキレン基が好ましく、フルオロアルキレン基が好ましく、パーフルオロアルキレン基が更に好ましい。上記アルキレン基の炭素数は２～４が好ましい。
　また、非求核性アニオンとしては、下記式（ｄ１－１）～（ｄ１－４）で表されるアニオンも挙げられる。
Figure JPOXMLDOC01-appb-C000065
Figure JPOXMLDOC01-appb-C000066
　式（ｄ１－１）中、Ｒ５１は置換基（例えば、水酸基）を有していてもよい炭化水素基（例えば、フェニル基等のアリール基）を表す。
　式（ｄ１－２）中、Ｚ２ｃは置換基を有していてもよい炭素数１～３０の炭化水素基（ただし、Ｓに隣接する炭素原子にはフッ素原子が置換されない）を表す。
　Ｚ２ｃにおける上記炭化水素基は、直鎖状でも分岐鎖状でもよく、環状構造を有していてもよい。また、上記炭化水素基における炭素原子（好ましくは、上記炭化水素基が環状構造を有する場合における、環員原子である炭素原子）は、カルボニル炭素（－ＣＯ－）であってもよい。上記炭化水素基としては、例えば、置換基を有していてもよいノルボルニル基を有する基が挙げられる。上記ノルボルニル基を形成する炭素原子は、カルボニル炭素であってもよい。
　式（ｄ１－２）中の「Ｚ２ｃ－ＳＯ３ －」は、上述の式（ＡＮ１）～（ＡＮ３）で表されるアニオンとは異なることが好ましい。例えば、Ｚ２ｃは、アリール基以外が好ましい。例えば、Ｚ２ｃにおける、－ＳＯ３ －に対してα位及びβ位の原子は、置換基としてフッ素原子を有する炭素原子以外の原子が好ましい。例えば、Ｚ２ｃは、－ＳＯ３ －に対してα位の原子及び／又はβ位の原子は環状基中の環員原子であることが好ましい。
　式（ｄ１－３）中、Ｒ５２は有機基（好ましくはフッ素原子を有する炭化水素基）を表し、Ｙ３は直鎖状、分岐鎖状、若しくは、環状のアルキレン基、アリーレン基、又は、カルボニル基を表し、Ｒｆは炭化水素基を表す。
　式（ｄ１－４）中、Ｒ５３及びＲ５４は、それぞれ独立に、有機基（好ましくはフッ素原子を有する炭化水素基）を表す。Ｒ５３及びＲ５４は互いに結合して環を形成していてもよい。
　有機アニオンは、１種単独で使用してもよく、２種以上を使用してもよい。
　光酸発生剤は、化合物（Ｉ）～（ＩＩ）からなる群から選択される少なくとも１つであることも好ましい。
（化合物（Ｉ））
　化合物（Ｉ）は、１つ以上の下記構造部位Ｘ及び１つ以上の下記構造部位Ｙを有する化合物であって、活性光線又は放射線の照射によって、下記構造部位Ｘに由来する下記第１の酸性部位と下記構造部位Ｙに由来する下記第２の酸性部位とを含む酸を発生する化合物である。
　　構造部位Ｘ：アニオン部位Ａ１ －とカチオン部位Ｍ１ ＋とからなり、且つ活性光線又は放射線の照射によって、ＨＡ１で表される第１の酸性部位を形成する構造部位
　　構造部位Ｙ：アニオン部位Ａ２ －とカチオン部位Ｍ２ ＋とからなり、且つ活性光線又は放射線の照射によって、ＨＡ２で表される第２の酸性部位を形成する構造部位
　上記化合物（Ｉ）は、下記条件Ｉを満たす。
　条件Ｉ：上記化合物（Ｉ）において上記構造部位Ｘ中の上記カチオン部位Ｍ１ ＋及び上記構造部位Ｙ中の上記カチオン部位Ｍ２ ＋をＨ＋に置き換えてなる化合物ＰＩが、上記構造部位Ｘ中の上記カチオン部位Ｍ１ ＋をＨ＋に置き換えてなるＨＡ１で表される酸性部位に由来する酸解離定数ａ１と、上記構造部位Ｙ中の上記カチオン部位Ｍ２ ＋をＨ＋に置き換えてなるＨＡ２で表される酸性部位に由来する酸解離定数ａ２とを有し、且つ、上記酸解離定数ａ１よりも上記酸解離定数ａ２の方が大きい。
　以下において、条件Ｉをより具体的に説明する。
　化合物（Ｉ）が、例えば、上記構造部位Ｘに由来する上記第１の酸性部位を１つと、上記構造部位Ｙに由来する上記第２の酸性部位を１つ有する酸を発生する化合物である場合、化合物ＰＩは「ＨＡ１とＨＡ２とを有する化合物」に該当する。
　化合物ＰＩの酸解離定数ａ１及び酸解離定数ａ２とは、より具体的に説明すると、化合物ＰＩの酸解離定数を求めた場合において、化合物ＰＩが「Ａ１ －とＨＡ２とを有する化合物」となる際のｐＫａが酸解離定数ａ１であり、上記「Ａ１ －とＨＡ２とを有する化合物」が「Ａ１ －とＡ２ －とを有する化合物」となる際のｐＫａが酸解離定数ａ２である。
　化合物（Ｉ）が、例えば、上記構造部位Ｘに由来する上記第１の酸性部位を２つと、上記構造部位Ｙに由来する上記第２の酸性部位を１つと有する酸を発生する化合物である場合、化合物ＰＩは「２つのＨＡ１と１つのＨＡ２とを有する化合物」に該当する。
　化合物ＰＩの酸解離定数を求めた場合、化合物ＰＩが「１つのＡ１ －と１つのＨＡ１と１つのＨＡ２とを有する化合物」となる際の酸解離定数、及び「１つのＡ１ －と１つのＨＡ１と１つのＨＡ２とを有する化合物」が「２つのＡ１ －と１つのＨＡ２とを有する化合物」となる際の酸解離定数が、上述の酸解離定数ａ１に該当する。「２つのＡ１ －と１つのＨＡ２とを有する化合物」が「２つのＡ１ －とＡ２ －を有する化合物」となる際の酸解離定数が酸解離定数ａ２に該当する。つまり、化合物ＰＩの場合、上記構造部位Ｘ中の上記カチオン部位Ｍ１ ＋をＨ＋に置き換えてなるＨＡ１で表される酸性部位に由来する酸解離定数を複数有する場合、複数の酸解離定数ａ１のうち最も大きい値よりも、酸解離定数ａ２の値の方が大きい。なお、化合物ＰＩが「１つのＡ１ －と１つのＨＡ１と１つのＨＡ２とを有する化合物」となる際の酸解離定数をａａとし、「１つのＡ１ －と１つのＨＡ１と１つのＨＡ２とを有する化合物」が「２つのＡ１ －と１つのＨＡ２とを有する化合物」となる際の酸解離定数をａｂとしたとき、ａａ及びａｂの関係は、ａａ＜ａｂを満たす。
　酸解離定数ａ１及び酸解離定数ａ２は、上述した酸解離定数の測定方法により求められる。
　上記化合物ＰＩとは、化合物（Ｉ）に活性光線又は放射線を照射した場合に、発生する酸に該当する。
　化合物（Ｉ）が２つ以上の構造部位Ｘを有する場合、構造部位Ｘは、それぞれ同一であっても異なっていてもよい。また、２つ以上の上記Ａ１ －、及び２つ以上の上記Ｍ１ ＋は、それぞれ同一であっても異なっていてもよい。
　化合物（Ｉ）中、上記Ａ１ －及び上記Ａ２ －、並びに、上記Ｍ１ ＋及び上記Ｍ２ ＋は、それぞれ同一であっても異なっていてもよいが、上記Ａ１ －及び上記Ａ２ －は、それぞれ異なっていることが好ましい。
　上記化合物ＰＩにおいて、酸解離定数ａ１（酸解離定数ａ１が複数存在する場合はその最大値）と酸解離定数ａ２との差（絶対値）は、０．１以上が好ましく、０．５以上がより好ましく、１．０以上が更に好ましい。なお、酸解離定数ａ１（酸解離定数ａ１が複数存在する場合はその最大値）と酸解離定数ａ２との差（絶対値）の上限値は特に制限されないが、例えば、１６以下である。
　上記化合物ＰＩにおいて、酸解離定数ａ２は、２０以下が好ましく、１５以下がより好ましい。なお、酸解離定数ａ２の下限値としては、－４．０以上が好ましい。
　上記化合物ＰＩにおいて、酸解離定数ａ１は、２．０以下が好ましく、０以下がより好ましい。なお、酸解離定数ａ１の下限値としては、－２０．０以上が好ましい。
　アニオン部位Ａ１ －及びアニオン部位Ａ２ －は、負電荷を帯びた原子又は原子団を含む構造部位であり、例えば、以下に示す式（ＡＡ－１）～（ＡＡ－３）及び式（ＢＢ－１）～（ＢＢ－６）からなる群から選ばれる構造部位が挙げられる。
　アニオン部位Ａ１ －としては、酸解離定数の小さい酸性部位を形成し得るものが好ましく、なかでも、式（ＡＡ－１）～（ＡＡ－３）のいずれかであることがより好ましく、式（ＡＡ－１）及び（ＡＡ－３）のいずれかであることが更に好ましい。
　また、アニオン部位Ａ２ －としては、アニオン部位Ａ１ －よりも酸解離定数の大きい酸性部位を形成し得るものが好ましく、式（ＢＢ－１）～（ＢＢ－６）のいずれかであることがより好ましく、式（ＢＢ－１）及び（ＢＢ－４）のいずれかであることが更に好ましい。
　なお、以下の式（ＡＡ－１）～（ＡＡ－３）及び式（ＢＢ－１）～（ＢＢ－６）中、＊は、結合位置を表す。
　式（ＡＡ－２）中、ＲＡは、１価の有機基を表す。ＲＡで表される１価の有機基は特に制限されないが、例えば、シアノ基、トリフルオロメチル基、及びメタンスルホニル基が挙げられる。
Figure JPOXMLDOC01-appb-C000067
Figure JPOXMLDOC01-appb-C000068
　カチオン部位Ｍ１ ＋及びカチオン部位Ｍ２ ＋は、正電荷を帯びた原子又は原子団を含む構造部位であり、例えば、電荷が１価の有機カチオンが挙げられる。なお、有機カチオンとしては、例えば、上述したＭ＋で表される有機カチオンが挙げられる。
　化合物（Ｉ）の具体的な構造としては特に制限されないが、例えば、後述する式（Ｉａ－１）～式（Ｉａ－５）で表される化合物が挙げられる。
－式（Ｉａ－１）で表される化合物－
　以下において、まず、式（Ｉａ－１）で表される化合物について述べる。
　Ｍ１１ ＋　Ａ１１ －－Ｌ１－Ａ１２ －　Ｍ１２ ＋　　　　（Ｉａ－１）
　式（Ｉａ－１）で表される化合物は、活性光線又は放射線の照射によって、ＨＡ１１－Ｌ１－Ａ１２Ｈで表される酸を発生する。
　式（Ｉａ－１）中、Ｍ１１ ＋及びＭ１２ ＋は、それぞれ独立に、有機カチオンを表す。
　Ａ１１ －及びＡ１２ －は、それぞれ独立に、１価のアニオン性官能基を表す。
　Ｌ１は、２価の連結基を表す。
　Ｍ１１ ＋及びＭ１２ ＋は、それぞれ同一であっても異なっていてもよい。
　Ａ１１ －及びＡ１２ －は、それぞれ同一であっても異なっていてもよいが、互いに異なっていることが好ましい。
　但し、上記式（Ｉａ－１）において、Ｍ１１ ＋及びＭ１２ ＋で表されるカチオンをＨ＋に置き換えてなる化合物ＰＩａ（ＨＡ１１－Ｌ１－Ａ１２Ｈ）において、Ａ１２Ｈで表される酸性部位に由来する酸解離定数ａ２は、ＨＡ１１で表される酸性部位に由来する酸解離定数ａ１よりも大きい。なお、酸解離定数ａ１と酸解離定数ａ２との好適値については、上述した通りである。化合物ＰＩａと、活性光線又は放射線の照射によって式（Ｉａ－１）で表される化合物とから発生する酸は同じである。
　また、Ｍ１１ ＋、Ｍ１２ ＋、Ａ１１ －、Ａ１２ －、及びＬ１の少なくとも１つが、置換基として、酸分解性基を有していてもよい。
　式（Ｉａ－１）中、Ｍ１１ ＋及びＭ１２ ＋で表される有機カチオンとしては、それぞれ上述したＭ＋で表される有機カチオンが挙げられる。
　Ａ１１ －で表される１価のアニオン性官能基とは、上述したアニオン部位Ａ１ －を含む１価の基を意図する。また、Ａ１２ －で表される１価のアニオン性官能基とは、上述したアニオン部位Ａ２ －を含む１価の基を意図する。
　Ａ１１ －及びＡ１２ －で表される１価のアニオン性官能基としては、上述した式（ＡＡ－１）～（ＡＡ－３）及び式（ＢＢ－１）～（ＢＢ－６）のいずれかのアニオン部位を含む１価のアニオン性官能基であるのが好ましく、式（ＡＸ－１）～（ＡＸ－３）、及び式（ＢＸ－１）～（ＢＸ－７）からなる群から選ばれる１価のアニオン性官能基であることがより好ましい。Ａ１１ －で表される１価のアニオン性官能基としては、なかでも、式（ＡＸ－１）～（ＡＸ－３）のいずれかで表される１価のアニオン性官能基であることが好ましい。Ａ１２ －で表される１価のアニオン性官能基としては、なかでも、式（ＢＸ－１）～（ＢＸ－７）のいずれかで表される１価のアニオン性官能基が好ましく、式（ＢＸ－１）～（ＢＸ－６）のいずれかで表される１価のアニオン性官能基がより好ましい。
Figure JPOXMLDOC01-appb-C000069
　式（ＡＸ－１）～（ＡＸ－３）中、ＲＡ１及びＲＡ２は、それぞれ独立に、１価の有機基を表す。＊は、結合位置を表す。
　ＲＡ１で表される１価の有機基は特に制限されないが、例えば、シアノ基、トリフルオロメチル基、及びメタンスルホニル基が挙げられる。
　ＲＡ２で表される１価の有機基としては、直鎖状、分岐鎖状、若しくは環状のアルキル基、又はアリール基が好ましい。
　上記アルキル基の炭素数は１～１５が好ましく、１～１０がより好ましく、１～６が更に好ましい。
　上記アルキル基は、置換基を有していてもよい。置換基としては、フッ素原子又はシアノ基が好ましく、フッ素原子がより好ましい。上記アルキル基が置換基としてフッ素原子を有する場合、パーフルオロアルキル基であってもよい。
　上記アリール基としては、フェニル基又はナフチル基が好ましく、フェニル基がより好ましい。
　上記アリール基は、置換基を有していてもよい。置換基としては、フッ素原子、ヨウ素原子、パーフルオロアルキル基（例えば、炭素数１～１０が好ましく、炭素数１～６がより好ましい。）、又はシアノ基が好ましく、フッ素原子、ヨウ素原子、又は、パーフルオロアルキル基がより好ましい。
　式（ＢＸ－１）～（ＢＸ－４）及び式（ＢＸ－６）中、ＲＢは、１価の有機基を表す。＊は、結合位置を表す。
　ＲＢで表される１価の有機基としては、直鎖状、分岐鎖状、若しくは環状のアルキル基、又はアリール基が好ましい。
　上記アルキル基の炭素数は１～１５が好ましく、１～１０がより好ましく、１～６が更に好ましい。
　上記アルキル基は、置換基を有していてもよい。置換基として特に制限されないが、置換基としては、フッ素原子又はシアノ基が好ましく、フッ素原子がより好ましい。上記アルキル基が置換基としてフッ素原子を有する場合、パーフルオロアルキル基であってもよい。
　なお、アルキル基において結合位置となる炭素原子が置換基を有する場合、フッ素原子又はシアノ基以外の置換基であることも好ましい。ここで、アルキル基において結合位置となる炭素原子とは、例えば、式（ＢＸ－１）及び（ＢＸ－４）の場合、アルキル基中の式中に明示される－ＣＯ－と直接結合する炭素原子が該当し、式（ＢＸ－２）及び（ＢＸ－３）の場合、アルキル基中の式中に明示される－ＳＯ２－と直接結合する炭素原子が該当し、式（ＢＸ－６）の場合、アルキル基中の式中に明示されるＮ－と直接結合する炭素原子が該当する。
　上記アルキル基は、炭素原子がカルボニル炭素で置換されていてもよい。
　上記アリール基としては、フェニル基又はナフチル基が好ましく、フェニル基がより好ましい。
　上記アリール基は、置換基を有していてもよい。置換基としては、フッ素原子、ヨウ素原子、パーフルオロアルキル基（例えば、炭素数１～１０が好ましく、炭素数１～６がより好ましい。）、シアノ基、アルキル基（例えば、炭素数１～１０が好ましく、炭素数１～６がより好ましい。）、アルコキシ基（例えば、炭素数１～１０が好ましく、炭素数１～６がより好ましい。）、又はアルコキシカルボニル基（例えば、炭素数２～１０が好ましく、炭素数２～６がより好ましい。）が好ましく、フッ素原子、ヨウ素原子、パーフルオロアルキル基、アルキル基、アルコキシ基、又はアルコキシカルボニル基がより好ましい。
　式（Ｉａ－１）中、Ｌ１で表される２価の連結基としては特に制限されず、－ＣＯ－、－ＮＲ－、－Ｏ－、－Ｓ－、－ＳＯ－、－ＳＯ２－、アルキレン基（好ましくは炭素数１～６、直鎖状でも分岐鎖状でもよい）、シクロアルキレン基（好ましくは炭素数３～１５）、アルケニレン基（好ましくは炭素数２～６）、２価の脂肪族複素環基（少なくとも１つのＮ原子、Ｏ原子、Ｓ原子、又はＳｅ原子を環構造内に有する５～１０員環が好ましく、５～７員環がより好ましく、５～６員環が更に好ましい。）、２価の芳香族複素環基（少なくとも１つのＮ原子、Ｏ原子、Ｓ原子、又はＳｅ原子を環構造内に有する５～１０員環が好ましく、５～７員環がより好ましく、５～６員環が更に好ましい。）、２価の芳香族炭化水素環基（６～１０員環が好ましく、６員環が更に好ましい。）、及びこれらの複数を組み合わせた２価の連結基が挙げられる。上記Ｒは、水素原子又は１価の有機基が挙げられる。１価の有機基としては特に制限されないが、例えば、アルキル基（好ましくは炭素数１～６）が好ましい。
　上記アルキレン基、上記シクロアルキレン基、上記アルケニレン基、上記２価の脂肪族複素環基、２価の芳香族複素環基、及び２価の芳香族炭化水素環基は、置換基を有していてもよい。置換基としては、例えば、ハロゲン原子（好ましくはフッ素原子）が挙げられる。
　なかでも、Ｌ１で表される２価の連結基としては、式（Ｌ１）で表される２価の連結基であることが好ましい。
Figure JPOXMLDOC01-appb-C000070
　式（Ｌ１）中、Ｌ１１１は、単結合又は２価の連結基を表す。
　Ｌ１１１で表される２価の連結基としては特に制限されず、例えば、－ＣＯ－、－ＮＨ－、－Ｏ－、－ＳＯ－、－ＳＯ２－、置換基を有していてもよいアルキレン基（好ましくは炭素数１～６がより好ましい。直鎖状及び分岐鎖状のいずれでもよい）、置換基を有していてもよいシクロアルキレン基（好ましくは炭素数３～１５）、置換基を有していてもよいアリール基（好ましくは炭素数６～１０）、及びこれらの複数を組み合わせた２価の連結基が挙げられる。置換基としては特に制限されず、例えば、ハロゲン原子が挙げられる。
　ｐは、０～３の整数を表し、１～３の整数を表すことが好ましい。
　ｖは、０又は１の整数を表す。
　Ｘｆ１は、それぞれ独立に、フッ素原子、又は少なくとも１つのフッ素原子で置換されたアルキル基を表す。このアルキル基の炭素数は、１～１０が好ましく、１～４がより好ましい。少なくとも１つのフッ素原子で置換されたアルキル基としては、パーフルオロアルキル基が好ましい。
　Ｘｆ２は、それぞれ独立に、水素原子、置換基としてフッ素原子を有していてもよいアルキル基、又はフッ素原子を表す。このアルキル基の炭素数は、１～１０が好ましく、１～４がより好ましい。Ｘｆ２としては、なかでも、フッ素原子、又は少なくとも１つのフッ素原子で置換されたアルキル基を表すのが好ましく、フッ素原子、又はパーフルオロアルキル基がより好ましい。
　なかでも、Ｘｆ１及びＸｆ２としては、それぞれ独立に、フッ素原子又は炭素数１～４のパーフルオロアルキル基であることが好ましく、フッ素原子又はＣＦ３であることがより好ましい。特に、Ｘｆ１及びＸｆ２が、いずれもフッ素原子であることが更に好ましい。
　＊は結合位置を表す。
　式（Ｉａ－１）中のＬ１１が式（Ｌ１）で表される２価の連結基を表す場合、式（Ｌ１）中のＬ１１１側の結合手（＊）が、式（Ｉａ－１）中のＡ１２ －と結合することが好ましい。
－式（Ｉａ－２）～（Ｉａ－４）で表される化合物－
　次に、式（Ｉａ－２）～（Ｉａ－４）で表される化合物について説明する。
Figure JPOXMLDOC01-appb-C000071
　式（Ｉａ－２）中、Ａ２１ａ －及びＡ２１ｂ －は、それぞれ独立に、１価のアニオン性官能基を表す。ここで、Ａ２１ａ －及びＡ２１ｂ －で表される１価のアニオン性官能基とは、上述したアニオン部位Ａ１ －を含む１価の基を意図する。Ａ２１ａ －及びＡ２１ｂ －で表される１価のアニオン性官能基としては特に制限されないが、例えば、上述の式（ＡＸ－１）～（ＡＸ－３）からなる群から選ばれる１価のアニオン性官能基が挙げられる。
　Ａ２２ －は、２価のアニオン性官能基を表す。ここで、Ａ２２ －で表される２価のアニオン性官能基とは、上述したアニオン部位Ａ２ －を含む２価の連結基を意図する。Ａ２２ －で表される２価のアニオン性官能基としては、例えば、以下に示す式（ＢＸ－８）～（ＢＸ－１１）で表される２価のアニオン性官能基が挙げられる。
Figure JPOXMLDOC01-appb-C000072
　Ｍ２１ａ ＋、Ｍ２１ｂ ＋、及びＭ２２ ＋は、それぞれ独立に、有機カチオンを表す。Ｍ２１ａ ＋、Ｍ２１ｂ ＋、及びＭ２２ ＋で表される有機カチオンとしては、上述のＭ１１ ＋と同義であり、好適態様も同じである。
　Ｌ２１及びＬ２２は、それぞれ独立に、２価の有機基を表す。
　上記式（Ｉａ－２）において、Ｍ２１ａ ＋、Ｍ２１ｂ ＋、及びＭ２２ ＋で表される有機カチオンをＨ＋に置き換えてなる化合物ＰＩａ－２において、Ａ２２Ｈで表される酸性部位に由来する酸解離定数ａ２は、Ａ２１ａＨに由来する酸解離定数ａ１－１及びＡ２１ｂＨで表される酸性部位に由来する酸解離定数ａ１－２よりも大きい。なお、酸解離定数ａ１－１と酸解離定数ａ１－２とは、上述した酸解離定数ａ１に該当する。
　なお、Ａ２１ａ －及びＡ２１ｂ －は、互いに同一であっても異なっていてもよい。Ｍ２１ａ ＋、Ｍ２１ｂ ＋、及びＭ２２ ＋は、互いに同一であっても異なっていてもよい。
　Ｍ２１ａ ＋、Ｍ２１ｂ ＋、Ｍ２２ ＋、Ａ２１ａ －、Ａ２１ｂ －、Ｌ２１、及びＬ２２の少なくとも１つが、置換基として、酸分解性基を有していてもよい。
　式（Ｉａ－３）中、Ａ３１ａ －及びＡ３２ －は、それぞれ独立に、１価のアニオン性官能基を表す。なお、Ａ３１ａ －で表される１価のアニオン性官能基の定義は、上述した式（Ｉａ－２）中のＡ２１ａ －及びＡ２１ｂ －と同義であり、好適態様も同じである。
　Ａ３２ －で表される１価のアニオン性官能基は、上述したアニオン部位Ａ２ －を含む１価の基を意図する。Ａ３２ －で表される１価のアニオン性官能基としては特に制限されないが、例えば、上述の式（ＢＸ－１）～（ＢＸ－７）からなる群から選ばれる１価のアニオン性官能基が挙げられる。
　Ａ３１ｂ －は、２価のアニオン性官能基を表す。ここで、Ａ３１ｂ －で表される２価のアニオン性官能基とは、上述したアニオン部位Ａ１ －を含む２価の連結基を意図する。Ａ３１ｂ －で表される２価のアニオン性官能基としては、例えば、以下に示す式（ＡＸ－４）で表される２価のアニオン性官能基が挙げられる。
Figure JPOXMLDOC01-appb-C000073
　Ｍ３１ａ ＋、Ｍ３１ｂ ＋、及びＭ３２ ＋は、それぞれ独立に、１価の有機カチオンを表す。Ｍ３１ａ ＋、Ｍ３１ｂ ＋、及びＭ３２ ＋で表される有機カチオンとしては、上述のＭ１１ ＋と同義であり、好適態様も同じである。
　Ｌ３１及びＬ３２は、それぞれ独立に、２価の有機基を表す。
　上記式（Ｉａ－３）において、Ｍ３１ａ ＋、Ｍ３１ｂ ＋、及びＭ３２ ＋で表される有機カチオンをＨ＋に置き換えてなる化合物ＰＩａ－３において、Ａ３２Ｈで表される酸性部位に由来する酸解離定数ａ２は、Ａ３１ａＨで表される酸性部位に由来する酸解離定数ａ１－３及びＡ３１ｂＨで表される酸性部位に由来する酸解離定数ａ１－４よりも大きい。なお、酸解離定数ａ１－３と酸解離定数ａ１－４とは、上述した酸解離定数ａ１に該当する。
　なお、Ａ３１ａ －及びＡ３２ －は、互いに同一であっても異なっていてもよい。また、Ｍ３１ａ ＋、Ｍ３１ｂ ＋、及びＭ３２ ＋は、互いに同一であっても異なっていてもよい。
　Ｍ３１ａ ＋、Ｍ３１ｂ ＋、Ｍ３２ ＋、Ａ３１ａ －、Ａ３２ －、Ｌ３１、及びＬ３２の少なくとも１つが、置換基として、酸分解性基を有していてもよい。
　式（Ｉａ－４）中、Ａ４１ａ －、Ａ４１ｂ －、及びＡ４２ －は、それぞれ独立に、１価のアニオン性官能基を表す。なお、Ａ４１ａ －及びＡ４１ｂ －で表される１価のアニオン性官能基の定義は、上述した式（Ｉａ－２）中のＡ２１ａ －及びＡ２１ｂ －と同義である。Ａ４２ －で表される１価のアニオン性官能基の定義は、上述した式（Ｉａ－３）中のＡ３２ －と同義であり、好適態様も同じである。
　Ｍ４１ａ ＋、Ｍ４１ｂ ＋、及びＭ４２ ＋は、それぞれ独立に、有機カチオンを表す。Ｍ４１ａ ＋、Ｍ４１ｂ ＋、及びＭ４２ ＋で表される有機カチオンとしては、上述のＭ１１ ＋と同義であり、好適態様も同じである。
　Ｌ４１は、３価の有機基を表す。
　上記式（Ｉａ－４）において、Ｍ４１ａ ＋、Ｍ４１ｂ ＋、及びＭ４２ ＋で表される有機カチオンをＨ＋に置き換えてなる化合物ＰＩａ－４において、Ａ４２Ｈで表される酸性部位に由来する酸解離定数ａ２は、Ａ４１ａＨで表される酸性部位に由来する酸解離定数ａ１－５及びＡ４１ｂＨで表される酸性部位に由来する酸解離定数ａ１－６よりも大きい。なお、酸解離定数ａ１－５と酸解離定数ａ１－６とは、上述した酸解離定数ａ１に該当する。
　なお、Ａ４１ａ －、Ａ４１ｂ －、及びＡ４２ －は、互いに同一であっても異なっていてもよい。また、Ｍ４１ａ ＋、Ｍ４１ｂ ＋、及びＭ４２ ＋は、互いに同一であっても異なっていてもよい。
　Ｍ４１ａ ＋、Ｍ４１ｂ ＋、Ｍ４２ ＋、Ａ４１ａ －、Ａ４１ｂ －、Ａ４２ －、及びＬ４１の少なくとも１つが、置換基として、酸分解性基を有していてもよい。
　式（Ｉａ－２）中のＬ２１及びＬ２２、並びに、式（Ｉａ－３）中のＬ３１及びＬ３２で表される２価の有機基としては特に制限されず、例えば、－ＣＯ－、－ＮＲ－、－Ｏ－、－Ｓ－、－ＳＯ－、－ＳＯ２－、アルキレン基（好ましくは炭素数１～６、直鎖状でも分岐鎖状でもよい）、シクロアルキレン基（好ましくは炭素数３～１５）、アルケニレン基（好ましくは炭素数２～６）、２価の脂肪族複素環基（少なくとも１つのＮ原子、Ｏ原子、Ｓ原子、又はＳｅ原子を環構造内に有する５～１０員環が好ましく、５～７員環がより好ましく、５～６員環が更に好ましい。）、２価の芳香族複素環基（少なくとも１つのＮ原子、Ｏ原子、Ｓ原子、又はＳｅ原子を環構造内に有する５～１０員環が好ましく、５～７員環がより好ましく、５～６員環が更に好ましい。）、２価の芳香族炭化水素環基（６～１０員環が好ましく、６員環が更に好ましい。）、及びこれらの複数を組み合わせた２価の有機基が挙げられる。上記－ＮＲ－におけるＲは、水素原子又は１価の有機基が挙げられる。１価の有機基としては特に制限されないが、例えば、アルキル基（好ましくは炭素数１～６）が好ましい。
　上記アルキレン基、上記シクロアルキレン基、上記アルケニレン基、上記２価の脂肪族複素環基、２価の芳香族複素環基、及び２価の芳香族炭化水素環基は、置換基を有していてもよい。置換基としては、例えば、ハロゲン原子（好ましくはフッ素原子）が挙げられる。
　式（Ｉａ－２）中のＬ２１及びＬ２２、並びに、式（Ｉａ－３）中のＬ３１及びＬ３２で表される２価の有機基としては、例えば、下記式（Ｌ２）で表される２価の有機基であることも好ましい。
Figure JPOXMLDOC01-appb-C000074
　式（Ｌ２）中、ｑは、１～３の整数を表す。＊は結合位置を表す。
　Ｘｆは、それぞれ独立に、フッ素原子、又は少なくとも１つのフッ素原子で置換されたアルキル基を表す。このアルキル基の炭素数は、１～１０が好ましく、１～４がより好ましい。少なくとも１つのフッ素原子で置換されたアルキル基としては、パーフルオロアルキル基が好ましい。
　Ｘｆは、フッ素原子又は炭素数１～４のパーフルオロアルキル基であることが好ましく、フッ素原子又はＣＦ３であることがより好ましい。特に、双方のＸｆがフッ素原子であることが更に好ましい。
　ＬＡは、単結合又は２価の連結基を表す。
　ＬＡで表される２価の連結基としては特に制限されず、例えば、－ＣＯ－、－Ｏ－、－ＳＯ－、－ＳＯ２－、アルキレン基（好ましくは炭素数１～６。直鎖状でも分岐鎖状でもよい）、シクロアルキレン基（好ましくは炭素数３～１５）、２価の芳香族炭化水素環基（６～１０員環が好ましく、６員環が更に好ましい。）、及びこれらの複数を組み合わせた２価の連結基が挙げられる。
　上記アルキレン基、上記シクロアルキレン基、及び２価の芳香族炭化水素環基は、置換基を有していてもよい。置換基としては、例えば、ハロゲン原子（好ましくはフッ素原子）が挙げられる。
　式（Ｌ２）で表される２価の有機基としては、例えば、＊－ＣＦ２－＊、＊－ＣＦ２－ＣＦ２－＊、＊－ＣＦ２－ＣＦ２－ＣＦ２－＊、＊－Ｐｈ－Ｏ－ＳＯ２－ＣＦ２－＊、＊－Ｐｈ－Ｏ－ＳＯ２－ＣＦ２－ＣＦ２－＊、＊－Ｐｈ－Ｏ－ＳＯ２－ＣＦ２－ＣＦ２－ＣＦ２－＊、及び、＊－Ｐｈ－ＯＣＯ－ＣＦ２－＊が挙げられる。なお、Ｐｈとは、置換基を有していてもよいフェニレン基であり、１，４－フェニレン基であることが好ましい。置換基としては特に制限されないが、アルキル基（例えば、炭素数１～１０が好ましく、炭素数１～６がより好ましい。）、アルコキシ基（例えば、炭素数１～１０が好ましく、炭素数１～６がより好ましい。）、又はアルコキシカルボニル基（例えば、炭素数２～１０が好ましく、炭素数２～６がより好ましい。）が好ましい。
　式（Ｉａ－２）中のＬ２１及びＬ２２が式（Ｌ２）で表される２価の有機基を表す場合、式（Ｌ２）中のＬＡ側の結合手（＊）が、式（Ｉａ－２）中のＡ２１ａ －及びＡ２１ｂ －と結合することが好ましい。
　式（Ｉａ－３）中のＬ３１及びＬ３２が式（Ｌ２）で表される２価の有機基を表す場合、式（Ｌ２）中のＬＡ側の結合手（＊）が、式（Ｉａ－３）中のＡ３１ａ －及びＡ３２ －と結合することが好ましい。
－式（Ｉａ－５）で表される化合物－
　次に、式（Ｉａ－５）について説明する。
Figure JPOXMLDOC01-appb-C000075
　式（Ｉａ－５）中、Ａ５１ａ －、Ａ５１ｂ －、及びＡ５１ｃ －は、それぞれ独立に、１価のアニオン性官能基を表す。ここで、Ａ５１ａ －、Ａ５１ｂ －、及びＡ５１ｃ －で表される１価のアニオン性官能基とは、上述したアニオン部位Ａ１ －を含む１価の基を意図する。Ａ５１ａ －、Ａ５１ｂ －、及びＡ５１ｃ －で表される１価のアニオン性官能基としては特に制限されないが、例えば、上述の式（ＡＸ－１）～（ＡＸ－３）からなる群から選ばれる１価のアニオン性官能基が挙げられる。
　Ａ５２ａ －及びＡ５２ｂ －は、２価のアニオン性官能基を表す。ここで、Ａ５２ａ －及びＡ５２ｂ －で表される２価のアニオン性官能基とは、上述したアニオン部位Ａ２ －を含む２価の連結基を意図する。Ａ２２ －で表される２価のアニオン性官能基としては、例えば、上述の式（ＢＸ－８）～（ＢＸ－１１）からなる群から選ばれる２価のアニオン性官能基が挙げられる。
　Ｍ５１ａ ＋、Ｍ５１ｂ ＋、Ｍ５１ｃ ＋、Ｍ５２ａ ＋、及びＭ５２ｂ ＋は、それぞれ独立に、有機カチオンを表す。Ｍ５１ａ ＋、Ｍ５１ｂ ＋、Ｍ５１ｃ ＋、Ｍ５２ａ ＋、及びＭ５２ｂ ＋で表される有機カチオンとしては、上述のＭ１１ ＋と同義であり、好適態様も同じである。
　Ｌ５１及びＬ５３は、それぞれ独立に、２価の有機基を表す。Ｌ５１及びＬ５３で表される２価の有機基としては、上述した式（Ｉａ－２）中のＬ２１及びＬ２２と同義であり、好適態様も同じである。
　Ｌ５２は、３価の有機基を表す。Ｌ５２で表される３価の有機基としては、上述した式（Ｉａ－４）中のＬ４１と同義であり、好適態様も同じである。
　上記式（Ｉａ－５）において、Ｍ５１ａ ＋、Ｍ５１ｂ ＋、Ｍ５１ｃ ＋、Ｍ５２ａ ＋、及びＭ５２ｂ ＋で表される有機カチオンをＨ＋に置き換えてなる化合物ＰＩａ－５において、Ａ５２ａＨで表される酸性部位に由来する酸解離定数ａ２－１及びＡ５２ｂＨで表される酸性部位に由来する酸解離定数ａ２－２は、Ａ５１ａＨに由来する酸解離定数ａ１－１、Ａ５１ｂＨで表される酸性部位に由来する酸解離定数ａ１－２、及びＡ５１ｃＨで表される酸性部位に由来する酸解離定数ａ１－３よりも大きい。なお、酸解離定数ａ１－１～ａ１－３は、上述した酸解離定数ａ１に該当し、酸解離定数ａ２－１及びａ２－２は、上述した酸解離定数ａ２に該当する。
　なお、Ａ５１ａ －、Ａ５１ｂ －、及びＡ５１ｃ －は、互いに同一であっても異なっていてもよい。また、Ａ５２ａ －及びＡ５２ｂ －は、互いに同一であっても異なっていてもよい。Ｍ５１ａ ＋、Ｍ５１ｂ ＋、Ｍ５１ｃ ＋、Ｍ５２ａ ＋、及びＭ５２ｂ ＋は、互いに同一であっても異なっていてもよい。
　Ｍ５１ｂ ＋、Ｍ５１ｃ ＋、Ｍ５２ａ ＋、Ｍ５２ｂ ＋、Ａ５１ａ －、Ａ５１ｂ －、Ａ５１ｃ －、Ｌ５１、Ｌ５２、及びＬ５３の少なくとも１つが、置換基として、酸分解性基を有していてもよい。
（化合物（ＩＩ））
　化合物（ＩＩ）は、２つ以上の上記構造部位Ｘ及び１つ以上の下記構造部位Ｚを有する化合物であって、活性光線又は放射線の照射によって、上記構造部位Ｘに由来する上記第１の酸性部位を２つ以上と上記構造部位Ｚとを含む酸を発生する化合物である。
　構造部位Ｚ：酸を中和可能な非イオン性の部位
　化合物（ＩＩ）中、構造部位Ｘの定義、並びに、Ａ１ －及びＭ１ ＋の定義は、上述した化合物（Ｉ）中の構造部位Ｘの定義、並びに、Ａ１ －及びＭ１ ＋の定義と同義であり、好適態様も同じである。
　上記化合物（ＩＩ）において上記構造部位Ｘ中の上記カチオン部位Ｍ１ ＋をＨ＋に置き換えてなる化合物ＰＩＩにおいて、上記構造部位Ｘ中の上記カチオン部位Ｍ１ ＋をＨ＋に置き換えてなるＨＡ１で表される酸性部位に由来する酸解離定数ａ１の好適範囲については、上記化合物ＰＩにおける酸解離定数ａ１と同じである。
　なお、化合物（ＩＩ）が、例えば、上記構造部位Ｘに由来する上記第１の酸性部位を２つと上記構造部位Ｚとを有する酸を発生する化合物である場合、化合物ＰＩＩは「２つのＨＡ１を有する化合物」に該当する。この化合物ＰＩＩの酸解離定数を求めた場合、化合物ＰＩＩが「１つのＡ１ －と１つのＨＡ１とを有する化合物」となる際の酸解離定数、及び「１つのＡ１ －と１つのＨＡ１とを有する化合物」が「２つのＡ１ －を有する化合物」となる際の酸解離定数が、酸解離定数ａ１に該当する。
　酸解離定数ａ１は、上述した酸解離定数の測定方法により求められる。
　上記化合物ＰＩＩとは、化合物（ＩＩ）に活性光線又は放射線を照射した場合に、発生する酸に該当する。
　なお、上記２つ以上の構造部位Ｘは、それぞれ同一であっても異なっていてもよい。２つ以上の上記Ａ１ －、及び２つ以上の上記Ｍ１ ＋は、それぞれ同一であっても異なっていてもよい。
　構造部位Ｚ中の酸を中和可能な非イオン性の部位としては特に制限されず、例えば、プロトンと静電的に相互作用し得る基、又は、電子を有する官能基を含む部位であることが好ましい。
　プロトンと静電的に相互作用し得る基、又は、電子を有する官能基としては、環状ポリエーテル等のマクロサイクリック構造を有する官能基、又は、π共役に寄与しない非共有電子対をもった窒素原子を有する官能基が挙げられる。π共役に寄与しない非共有電子対を有する窒素原子とは、例えば、下記式に示す部分構造を有する窒素原子である。
Figure JPOXMLDOC01-appb-C000076
　プロトンと静電的に相互作用し得る基又は電子を有する官能基の部分構造としては、例えば、クラウンエーテル構造、アザクラウンエーテル構造、１～３級アミン構造、ピリジン構造、イミダゾール構造、及びピラジン構造が挙げられ、なかでも、１～３級アミン構造が好ましい。
　化合物（ＩＩ）としては特に制限されないが、例えば、下記式（ＩＩａ－１）及び下記式（ＩＩａ－２）で表される化合物が挙げられる。
Figure JPOXMLDOC01-appb-C000077
　上記式（ＩＩａ－１）中、Ａ６１ａ －及びＡ６１ｂ －は、それぞれ上述した式（Ｉａ－１）中のＡ１１ －と同義であり、好適態様も同じである。また、Ｍ６１ａ ＋及びＭ６１ｂ ＋は、それぞれ上述した式（Ｉａ－１）中のＭ１１ ＋と同義であり、好適態様も同じである。
　上記式（ＩＩａ－１）中、Ｌ６１及びＬ６２は、それぞれ上述した式（Ｉａ－１）中のＬ１と同義であり、好適態様も同じである。
　式（ＩＩａ－１）中、Ｒ２Ｘは、１価の有機基を表す。Ｒ２Ｘで表される１価の有機基としては特に制限されず、アルキル基（好ましくは炭素数１～１０、直鎖状でも分岐鎖状でもよい）、シクロアルキル基（好ましくは炭素数３～１５）、又はアルケニル基（好ましくは炭素数２～６）が挙げられる。Ｒ２Ｘで表される１価の有機基におけるアルキル基、シクロアルキル基、及びアルケニル基に含まれる－ＣＨ２－は、－ＣＯ－、－ＮＨ－、－Ｏ－、－Ｓ－、－ＳＯ－、及び－ＳＯ２－からなる群より選ばれる１種又は２種以上の組み合わせで置換されていてもよい。
　上記アルキレン基、上記シクロアルキレン基、及び上記アルケニレン基は、置換基を有していてもよい。置換基としては、特に制限されないが、例えば、ハロゲン原子（好ましくはフッ素原子）が挙げられる。
　上記式（ＩＩａ－１）において、Ｍ６１ａ ＋及びＭ６１ｂ ＋で表される有機カチオンをＨ＋に置き換えてなる化合物ＰＩＩａ－１において、Ａ６１ａＨで表される酸性部位に由来する酸解離定数ａ１－７及びＡ６１ｂＨで表される酸性部位に由来する酸解離定数ａ１－８は、上述した酸解離定数ａ１に該当する。
　なお、上記化合物（ＩＩａ－１）において上記構造部位Ｘ中の上記カチオン部位Ｍ６１ａ ＋及びＭ６１ｂ ＋をＨ＋に置き換えてなる化合物ＰＩＩａ－１は、ＨＡ６１ａ－Ｌ６１－Ｎ（Ｒ２Ｘ）－Ｌ６２－Ａ６１ｂＨが該当する。また、化合物ＰＩＩａ－１と、活性光線又は放射線の照射によって式（ＩＩａ－１）で表される化合物から発生する酸は同じである。
　Ｍ６１ａ ＋、Ｍ６１ｂ ＋、Ａ６１ａ －、Ａ６１ｂ －、Ｌ６１、Ｌ６２、及びＲ２Ｘの少なくとも１つが、置換基として、酸分解性基を有していてもよい。
　上記式（ＩＩａ－２）中、Ａ７１ａ －、Ａ７１ｂ －、及びＡ７１ｃ －は、それぞれ上述した式（Ｉａ－１）中のＡ１１ －と同義であり、好適態様も同じである。Ｍ７１ａ ＋、Ｍ７１ｂ ＋、及び、Ｍ７１ｃ ＋は、それぞれ上述した式（Ｉａ－１）中のＭ１１ ＋と同義であり、好適態様も同じである。
　上記式（ＩＩａ－２）中、Ｌ７１、Ｌ７２、及びＬ７３は、それぞれ上述した式（Ｉａ－１）中のＬ１と同義であり、好適態様も同じである。
　上記式（ＩＩａ－２）において、Ｍ７１ａ ＋、Ｍ７１ｂ ＋、及び、Ｍ７１ｃ ＋で表される有機カチオンをＨ＋に置き換えてなる化合物ＰＩＩａ－２において、Ａ７１ａＨで表される酸性部位に由来する酸解離定数ａ１－９、Ａ７１ｂＨで表される酸性部位に由来する酸解離定数ａ１－１０、及びＡ７１ｃＨで表される酸性部位に由来する酸解離定数ａ１－１１は、上述した酸解離定数ａ１に該当する。
　なお、上記化合物（ＩＩａ－１）において上記構造部位Ｘ中の上記カチオン部位Ｍ７１ａ ＋、Ｍ７１ｂ ＋、及び、Ｍ７１ｃ ＋をＨ＋に置き換えてなる化合物ＰＩＩａ－２は、ＨＡ７１ａ－Ｌ７１－Ｎ（Ｌ７３－Ａ７１ｃＨ）－Ｌ７２－Ａ７１ｂＨが該当する。また、化合物ＰＩＩａ－２と、活性光線又は放射線の照射によって式（ＩＩａ－２）で表される化合物から発生する酸は同じである。
　Ｍ７１ａ ＋、Ｍ７１ｂ ＋、Ｍ７１ｃ ＋、Ａ７１ａ －、Ａ７１ｂ －、Ａ７１ｃ －、Ｌ７１、Ｌ７２、及びＬ７３の少なくとも１つが、置換基として、酸分解性基を有していてもよい。
　化合物（Ｉ）及び化合物（ＩＩ）が有し得る、カチオン以外の部位を例示する。
Figure JPOXMLDOC01-appb-C000078
Figure JPOXMLDOC01-appb-C000079
　以下に光酸発生剤の具体例を示すが、これに限定されない。
Figure JPOXMLDOC01-appb-C000080
Figure JPOXMLDOC01-appb-C000081
Figure JPOXMLDOC01-appb-C000082
　本発明の組成物が光酸発生剤（Ｂ）を含む場合、その含有量は特に制限されないが、組成物の全固形分に対して、０．５質量％以上が好ましく、１．０質量％以上がより好ましい。上記含有量は、組成物の全固形分に対して、５０．０質量％以下が好ましく、３０．０質量％以下がより好ましく、２５．０質量％以下が更に好ましい。
　光酸発生剤（Ｂ）は、１種単独で使用してもよく、２種以上を使用してもよい。
＜酸拡散制御剤（Ｃ１）＞
　本発明の組成物は、化合物（Ｃ）に相当しない酸拡散制御剤を含んでいてもよい。
　酸拡散制御剤は、露光時に光酸発生剤等から発生する酸をトラップし、余分な発生酸による、未露光部における酸分解性樹脂の反応を抑制するクエンチャーとして作用する。
　酸拡散制御剤の種類は特に制限されず、例えば、塩基性化合物（ＣＡ）、窒素原子を有し、酸の作用により脱離する基を有する低分子化合物（ＣＢ）、及び、活性光線又は放射線の照射により酸拡散制御能が低下又は消失する化合物（ＣＣ）が挙げられる。
　化合物（ＣＣ）としては、光酸発生剤に対して相対的に弱酸となるオニウム塩化合物（ＣＤ）、及び、活性光線又は放射線の照射により塩基性が低下又は消失する塩基性化合物（ＣＥ）が挙げられる。
　塩基性化合物（ＣＡ）の具体例としては、例えば、国際公開第２０２０／０６６８２４号の段落［０１３２］～［０１３６］に記載のものが挙げられ、活性光線又は放射線の照射により塩基性が低下又は消失する塩基性化合物（ＣＥ）の具体例としては、国際公開第２０２０／０６６８２４号の段落［０１３７］～［０１５５］に記載のものが挙げられ、窒素原子を有し、酸の作用により脱離する基を有する低分子化合物（ＣＢ）の具体例としては、国際公開第２０２０／０６６８２４号の段落［０１５６］～［０１６３］に記載のものが挙げられ、カチオン部に窒素原子を有するオニウム塩化合物（ＣＥ）の具体例としては、国際公開第２０２０／０６６８２４号公報の段落［０１６４］に記載のものが挙げられる。
　光酸発生剤に対して相対的に弱酸となるオニウム塩化合物（ＣＤ）の具体例としては、例えば、国際公開第２０２０／１５８３３７号の段落［０３０５］～［０３１４］に記載のものが挙げられる。
　上記以外にも、例えば、米国特許出願公開２０１６／００７０１６７Ａ１号の段落［０６２７］～［０６６４］、米国特許出願公開２０１５／０００４５４４Ａ１号の段落［００９５］～［０１８７］、米国特許出願公開２０１６／０２３７１９０Ａ１号の段落［０４０３］～［０４２３］、及び米国特許出願公開２０１６／０２７４４５８Ａ１号の段落［０２５９］～［０３２８］に開示された公知の化合物を酸拡散制御剤として好適に使用できる。
　本発明の組成物に酸拡散制御剤が含まれる場合、酸拡散制御剤の含有量（複数種存在する場合はその合計）は、レジスト組成物の全固形分に対して、０．１～１５．０質量％が好ましく、１．０～１５．０質量％がより好ましい。
　本発明の組成物において、酸拡散制御剤は１種単独で使用してもよいし、２種以上を併用してもよい。
＜疎水性樹脂（Ｄ）＞
　本発明の組成物は、更に、樹脂（Ａ）とは異なる疎水性樹脂を含んでいてもよい。
　疎水性樹脂はレジスト膜の表面に偏在するように設計されることが好ましいが、界面活性剤とは異なり、必ずしも分子内に親水基を有する必要はなく、極性物質及び非極性物質の均一な混合に寄与しなくてもよい。
　疎水性樹脂の添加による効果として、水に対するレジスト膜表面の静的及び動的な接触角の制御、並びに、アウトガスの抑制が挙げられる。
　疎水性樹脂は、膜表層への偏在化の点から、フッ素原子、珪素原子、及び、樹脂の側鎖部分に含まれたＣＨ３部分構造のいずれか１種以上を有するのが好ましく、２種以上を有することがより好ましい。上記疎水性樹脂は、炭素数５以上の炭化水素基を有することが好ましい。これらの基は樹脂の主鎖中に有していても、側鎖に置換していてもよい。
　疎水性樹脂としては、国際公開第２０２０／００４３０６号の段落［０２７５］～［０２７９］に記載される化合物が挙げられる。
　本発明の組成物が疎水性樹脂を含む場合、疎水性樹脂の含有量は、組成物の全固形分に対して、０．０１～２０．０質量％が好ましく、０．１～１５．０質量％がより好ましい。
＜界面活性剤（Ｅ）＞
　本発明の組成物は、界面活性剤を含んでいてもよい。界面活性剤を含むと、密着性により優れ、現像欠陥のより少ないパターンを形成することができる。
　界面活性剤は、フッ素系及び／又はシリコン系界面活性剤が好ましい。
　フッ素系及び／又はシリコン系界面活性剤としては、国際公開第２０１８／１９３９５４号の段落［０２１８］及び［０２１９］に開示された界面活性剤が挙げられる。
　これら界面活性剤は、１種を単独で用いてもよく、２種以上を使用してもよい。
　本発明の組成物が界面活性剤を含む場合、界面活性剤の含有量は、組成物の全固形分に対して、０．０００１～２．０質量％が好ましく、０．０００５～１．０質量％がより好ましく、０．１～１．０質量％が更に好ましい。
＜溶剤（Ｆ）＞
　本発明の組成物は、溶剤を含むことが好ましい。
　溶剤は、（Ｍ１）プロピレングリコールモノアルキルエーテルカルボキシレート、並びに、（Ｍ２）プロピレングリコールモノアルキルエーテル、乳酸エステル、酢酸エステル、アルコキシプロピオン酸エステル、鎖状ケトン、環状ケトン、ラクトン、及びアルキレンカーボネートからなる群より選択される少なくとも１つの少なくとも一方を含んでいることが好ましい。なお、上記溶剤は、成分（Ｍ１）及び（Ｍ２）以外の成分を更に含んでいてもよい。
　上述した溶剤と上述した樹脂とを組み合わせると、組成物の塗布性の向上、及び、パターンの現像欠陥数の低減の観点で好ましい。上述した溶剤は、上述した樹脂の溶解性、沸点及び粘度のバランスが良いため、レジスト膜の膜厚のムラ及びスピンコート中の析出物の発生等を抑制することができる。
　成分（Ｍ１）及び成分（Ｍ２）の詳細は、国際公開第２０２０／００４３０６号の段落［０２１８］～［０２２６］に記載され、これらの内容は本明細書に組み込まれる。
　溶剤が成分（Ｍ１）及び（Ｍ２）以外の成分を更に含む場合、成分（Ｍ１）及び（Ｍ２）以外の成分の含有量は、溶剤の全量に対して、５～３０質量％が好ましい。
　本発明の組成物中の溶剤の含有量は、固形分濃度が０．５～３０質量％となるように定めるのが好ましく、１～２０質量％となるように定めることがより好ましい。こうすると、本発明の組成物の塗布性を更に向上させられる。
　なお、固形分とは、溶剤以外の全ての成分を意味するものであり、上述の通り、感活性光線性又は感放射線性膜を形成する成分を意味する。
　固形分濃度とは、本発明の組成物の総質量に対する、溶剤を除く他の成分の質量の質量百分率である。
　「全固形分」とは、本発明の組成物の全組成から溶剤を除いた成分の総質量をいう。また、「固形分」とは、上述のように、溶剤を除いた成分であり、例えば、２５℃において固体であっても、液体であってもよい。
＜その他の添加剤＞
　本発明の組成物は、溶解阻止化合物、染料、可塑剤、光増感剤、光吸収剤、及び／又は、現像液に対する溶解性を促進させる化合物（例えば、分子量１０００以下のフェノール化合物、又は、カルボキシル基を含んだ脂環族若しくは脂肪族化合物）を更に含んでいてもよい。
　上記「溶解阻止化合物」とは、酸の作用により分解して有機系現像液中での溶解度が減少する、分子量３０００以下の化合物である。
　本明細書の組成物は、ＥＵＶ露光用感光性組成物として好適に用いられる。
　ＥＵＶ光は波長１３．５ｎｍであり、ＡｒＦ（波長１９３ｎｍ）光等に比べて、より短波長であるため、同じ感度で露光された際の入射フォトン数が少ない。そのため、確率的にフォトンの数がばらつく“フォトンショットノイズ”の影響が大きく、ＬＥＲの悪化及びブリッジ欠陥を招く。フォトンショットノイズを減らすには、露光量を大きくして入射フォトン数を増やす方法があるが、高感度化の要求とトレードオフとなる。
　また、本発明は、以下の化合物にも関する。
　下記一般式（ＩＡ）で表される化合物。
Figure JPOXMLDOC01-appb-C000083
一般式（ＩＡ）中、
Ｒ０は、アルキル基、－Ｃ（＝Ｏ）Ｒ１、又はアリール基を表す。Ｒ１は有機基を表す。
ｐは０～４の整数である。ｑは０～３の整数である。ｐ＋ｑ≧１である。
ｑが０の場合、全てのＲ０において、炭素原子の総数と酸素原子の総数を足した合計が３以上である。
ｐが２以上の整数の場合、複数のＲ０は同一であってもよく、異なっていても良い。
Ｍ＋はカチオンを表す。
　一般式（ＩＡ）中、Ｒ０のアルキル基、－Ｃ（＝Ｏ）Ｒ１及びアリール基としては、それぞれ、本発明の組成物における上記一般式（Ｉ）中のＲ０の置換基におけるアルキル基、－Ｃ（＝Ｏ）Ｒ１及びアリール基と同様のものが挙げられ、また、好ましい範囲も同様である。
　一般式（ＩＡ）中、ｐ及びｑは、それぞれ、本発明の組成物における上記一般式（Ｉ）中のｐ及びｑと同義である。
　なお、「ｑが０の場合、全てのＲ０において、炭素原子の総数と酸素原子の総数を足した合計が３以上である。」は、本発明の組成物における上記一般式（Ｉ）において記載した「ｑが０の場合、全てのＲ０において、炭素原子の総数と酸素原子の総数を足した合計が３以上である。」と同様である。
　一般式（Ｉ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、アルキル基、－Ｃ（＝Ｏ）Ｒ１、又はアリール基を表すことが好ましい。
　一般式（Ｉ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、－Ｃ（＝Ｏ）Ｒ１を表すことが好ましい。
　一般式（Ｉ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、アリール基を表すことが好ましい。
　好ましい一態様として、ｑが０の場合、ｐは３又は４を表すことが好ましい。
＜感活性光線性又は感放射線性膜、パターン形成方法＞
　上記組成物を用いたパターン形成方法の手順は特に制限されないが、以下の工程を有することが好ましい。
工程１：感活性光線性又は感放射線性樹脂組成物により基板上に感活性光線性又は感放射線性膜を形成する工程
工程２：感活性光線性又は感放射線性膜を露光する工程
工程３：露光された感活性光線性又は感放射線性膜を現像液を用いて現像する工程
　以下、上記それぞれの工程の手順について詳述する。
（工程１：感活性光線性又は感放射線性膜形成工程）
　工程１は、本発明の組成物により基板上に感活性光線性又は感放射線性膜を形成する工程である。
　感活性光線性又は感放射線性樹脂組成物により基板上に感活性光線性又は感放射線性膜を形成する方法としては、例えば、感活性光線性又は感放射線性樹脂組成物を基板上に塗布する方法が挙げられる。
　なお、塗布前に感活性光線性又は感放射線性樹脂組成物を必要に応じてフィルター濾過することが好ましい。フィルターのポアサイズは、０．１μｍ以下が好ましく、０．０５μｍ以下がより好ましく、０．０３μｍ以下が更に好ましい。フィルターは、ポリテトラフルオロエチレン製、ポリエチレン製、又は、ナイロン製が好ましい。
　感活性光線性又は感放射線性樹脂組成物は、集積回路素子の製造に使用されるような基板（例：シリコン、二酸化シリコン被覆）上に、スピナー又はコーター等の適当な塗布方法により塗布できる。塗布方法は、スピナーを用いたスピン塗布が好ましい。スピナーを用いたスピン塗布をする際の回転数は、１０００～３０００ｒｐｍが好ましい。
　感活性光線性又は感放射線性樹脂組成物の塗布後、基板を乾燥し、レジスト膜を形成してもよい。なお、必要により、レジスト膜の下層に、各種下地膜（無機膜、有機膜、反射防止膜）を形成してもよい。
　乾燥方法としては、例えば、加熱して乾燥する方法が挙げられる。加熱は通常の露光機、及び／又は、現像機に備わっている手段で実施でき、ホットプレート等を用いて実施してもよい。加熱温度は８０～１５０℃が好ましく、８０～１４０℃がより好ましく、８０～１３０℃が更に好ましい。加熱時間は３０～１０００秒が好ましく、６０～８００秒がより好ましく、６０～６００秒が更に好ましい。
　感活性光線性又は感放射線性樹脂膜（典型的には、レジスト膜）の膜厚は特に制限されないが、より高精度な微細パターンを形成できる点から、１０～１２０ｎｍが好ましい。なかでも、ＥＵＶ露光とする場合、レジスト膜の膜厚としては、１０～６５ｎｍがより好ましく、１５～５０ｎｍが更に好ましい。ＡｒＦ液浸露光とする場合、レジスト膜の膜厚としては、１０～１２０ｎｍがより好ましく、１５～９０ｎｍが更に好ましい。
　なお、感活性光線性又は感放射線性膜の上層にトップコート組成物を用いてトップコートを形成してもよい。
　トップコート組成物は、レジスト膜と混合せず、更にレジスト膜上層に均一に塗布できることが好ましい。トップコートは、特に限定されず、従来公知のトップコートを、従来公知の方法によって形成でき、例えば、特開２０１４－０５９５４３号公報の段落［００７２］～［００８２］の記載に基づいてトップコートを形成できる。
　例えば、特開２０１３－６１６４８号公報に記載されたような塩基性化合物を含むトップコートを、レジスト膜上に形成することが好ましい。トップコートが含み得る塩基性化合物の具体的な例は、レジスト組成物が含んでいてもよい塩基性化合物が挙げられる。
　トップコートは、エーテル結合、チオエーテル結合、水酸基、チオール基、カルボニル結合、及びエステル結合からなる群より選択される基又は結合を少なくとも１つ含む化合物を含むことも好ましい。
（工程２：露光工程）
　工程２は、感活性光線性又は感放射線性膜を露光する工程である。
　露光の方法としては、形成した感活性光線性又は感放射線性膜に所定のマスクを通して活性光線又は放射線を照射する方法が挙げられる。
　活性光線又は放射線としては、赤外光、可視光、紫外光、遠紫外光、極紫外光、Ｘ線、及び電子線が挙げられ、２５０ｎｍ以下が好ましく、２２０ｎｍ以下がより好ましく、１～２００ｎｍの波長の遠紫外光、具体的には、ＫｒＦエキシマレーザー（２４８ｎｍ）、ＡｒＦエキシマレーザー（１９３ｎｍ）、Ｆ２エキシマレーザー（１５７ｎｍ）、ＥＵＶ（１３．５ｎｍ）、Ｘ線、及び電子ビームが特に好ましい。
　露光後、現像を行う前にベーク（加熱）を行うことが好ましい。ベークにより露光部の反応が促進され、感度及びパターン形状がより良好となる。
　加熱温度は８０～１５０℃が好ましく、８０～１４０℃がより好ましく、８０～１３０℃が更に好ましい。
　加熱時間は１０～１０００秒が好ましく、１０～１８０秒がより好ましく、３０～１２０秒が更に好ましい。
　加熱は通常の露光機及び／又は現像機に備わっている手段で実施でき、ホットプレート等を用いて行ってもよい。
　この工程は露光後ベークともいう。
（工程３：現像工程）
　工程３は、現像液を用いて、露光された感活性光線性又は感放射線性膜を現像し、パターンを形成する工程である。
　現像液は、アルカリ現像液であっても、有機溶剤を含有する現像液（以下、有機系現像液ともいう）であってもよい。
　現像方法としては、例えば、現像液が満たされた槽中に基板を一定時間浸漬する方法（ディップ法）、基板表面に現像液を表面張力によって盛り上げて一定時間静置して現像する方法（パドル法）、基板表面に現像液を噴霧する方法（スプレー法）、及び一定速度で回転している基板上に一定速度で現像液吐出ノズルをスキャンしながら現像液を吐出しつづける方法（ダイナミックディスペンス法）が挙げられる。
　また、現像を行う工程の後に、他の溶剤に置換しながら、現像を停止する工程を実施してもよい。
　現像時間は未露光部の樹脂が十分に溶解する時間であれば特に制限はなく、１０～３００秒が好ましく、２０～１２０秒がより好ましい。
　現像液の温度は０～５０℃が好ましく、１５～３５℃がより好ましい。
　アルカリ現像液は、アルカリを含むアルカリ水溶液を用いることが好ましい。アルカリ水溶液の種類は特に制限されないが、例えば、テトラメチルアンモニウムヒドロキシドに代表される４級アンモニウム塩、無機アルカリ、１級アミン、２級アミン、３級アミン、アルコールアミン、又は、環状アミン等を含むアルカリ水溶液が挙げられる。中でも、アルカリ現像液は、テトラメチルアンモニウムヒドロキシド（ＴＭＡＨ）に代表される４級アンモニウム塩の水溶液であることが好ましい。アルカリ現像液には、アルコール類、界面活性剤等を適当量添加してもよい。アルカリ現像液のアルカリ濃度は、通常、０．１～２０質量％であることが好ましい。アルカリ現像液のｐＨは、通常、１０．０～１５．０であることが好ましい。
　有機系現像液は、ケトン系溶剤、エステル系溶剤、アルコール系溶剤、アミド系溶剤、エーテル系溶剤、及び炭化水素系溶剤からなる群より選択される少なくとも１種の有機溶剤を含有する現像液であることが好ましい。
　上記の溶剤は、複数混合してもよいし、上記以外の溶剤又は水と混合してもよい。現像液全体としての含水率は、５０質量％未満が好ましく、２０質量％未満がより好ましく、１０質量％未満が更に好ましく、実質的に水分を含有しないのが特に好ましい。
　有機系現像液に対する有機溶剤の含有量は、現像液の全量に対して、５０質量％以上１００質量％以下が好ましく、８０質量％以上１００質量％以下がより好ましく、９０質量％以上１００質量％以下が更に好ましく、９５質量％以上１００質量％以下が特に好ましい。
（他の工程）
　上記パターン形成方法は、工程３の後に、リンス液を用いて洗浄する工程を含むことが好ましい。
　アルカリ現像液を用いて現像する工程の後のリンス工程に用いるリンス液としては、例えば、純水が挙げられる。なお、純水には、界面活性剤を適当量添加してもよい。
　リンス液には、界面活性剤を適当量添加してもよい。
　有機系現像液を用いた現像工程の後のリンス工程に用いるリンス液は、パターンを溶解しないものであれば特に制限はなく、一般的な有機溶剤を含む溶液を使用できる。リンス液は、炭化水素系溶剤、ケトン系溶剤、エステル系溶剤、アルコール系溶剤、アミド系溶剤、及びエーテル系溶剤からなる群より選択される少なくとも１種の有機溶剤を含有するリンス液を用いることが好ましい。
　リンス工程の方法は特に限定されず、例えば、一定速度で回転している基板上にリンス液を吐出しつづける方法（回転塗布法）、リンス液が満たされた槽中に基板を一定時間浸漬する方法（ディップ法）、及び基板表面にリンス液を噴霧する方法（スプレー法）が挙げられる。
　また、パターン形成方法は、リンス工程の後に加熱工程（Ｐｏｓｔ　Ｂａｋｅ）を含んでいてもよい。本工程により、ベークによりパターン間及びパターン内部に残留した現像液及びリンス液が除去される。また、本工程により、レジストパターンがなまされ、パターンの表面荒れが改善される効果もある。リンス工程の後の加熱工程は、通常４０～２５０℃（好ましくは９０～２００℃）で、通常１０秒間～３分間（好ましくは３０秒間～１２０秒間）行う。
　また、形成されたパターンをマスクとして、基板のエッチング処理を実施してもよい。つまり、工程３にて形成されたパターンをマスクとして、基板（又は、下層膜及び基板）を加工して、基板にパターンを形成してもよい。
　基板（又は、下層膜及び基板）の加工方法は特に限定されないが、工程３で形成されたパターンをマスクとして、基板（又は、下層膜及び基板）に対してドライエッチングを行うことにより、基板にパターンを形成する方法が好ましい。ドライエッチングは、酸素プラズマエッチングが好ましい。
　本明細書の組成物、及び本明細書のパターン形成方法において使用される各種材料（例えば、溶剤、現像液、リンス液、反射防止膜形成用組成物、トップコート形成用組成物等）は、金属等の不純物を含まないことが好ましい。これら材料に含まれる不純物の含有量は、１質量ｐｐｍ以下が好ましく、１０質量ｐｐｂ以下がより好ましく、１００質量ｐｐｔ以下が更に好ましく、１０質量ｐｐｔ以下が特に好ましく、１質量ｐｐｔ以下が最も好ましい。下限は特に制限させず、０質量ｐｐｔ以上が好ましい。ここで、金属不純物としては、例えば、Ｎａ、Ｋ、Ｃａ、Ｆｅ、Ｃｕ、Ｍｇ、Ａｌ、Ｌｉ、Ｃｒ、Ｎｉ、Ｓｎ、Ａｇ、Ａｓ、Ａｕ、Ｂａ、Ｃｄ、Ｃｏ、Ｐｂ、Ｔｉ、Ｖ、Ｗ、及びＺｎが挙げられる。
　各種材料から金属等の不純物を除去する方法としては、例えば、フィルターを用いた濾過が挙げられる。フィルターを用いた濾過の詳細は、国際公開第２０２０／００４３０６号の段落［０３２１］に記載される。
　各種材料に含まれる金属等の不純物を低減する方法としては、例えば、各種材料を構成する原料として金属含有量が少ない原料を選択する方法、各種材料を構成する原料に対してフィルター濾過を行う方法、及び装置内をテフロン（登録商標）でライニングする等してコンタミネーションを可能な限り抑制した条件下で蒸留を行う方法が挙げられる。
　フィルター濾過の他、吸着材による不純物の除去を行ってもよく、フィルター濾過と吸着材とを組み合わせて使用してもよい。吸着材としては、公知の吸着材を使用でき、例えば、シリカゲル及びゼオライト等の無機系吸着材、並びに、活性炭等の有機系吸着材を使用できる。上記各種材料に含まれる金属等の不純物を低減するためには、製造工程における金属不純物の混入を防止する必要がある。製造装置から金属不純物が十分に除去されたかどうかは、製造装置の洗浄に使用された洗浄液中に含まれる金属成分の含有量を測定して確認できる。使用後の洗浄液に含まれる金属成分の含有量は、１００質量ｐｐｔ（ｐａｒｔｓ　ｐｅｒ　ｔｒｉｌｌｉｏｎ）以下が好ましく、１０質量ｐｐｔ以下がより好ましく、１質量ｐｐｔ以下が更に好ましい。下限は特に制限させず、０質量ｐｐｔ以上が好ましい。
　リンス液等の有機系処理液には、静電気の帯電、引き続き生じる静電気放電に伴う、薬液配管及び各種パーツ（フィルター、Ｏ－リング、及び、チューブ等）の故障を防止するため、導電性の化合物を添加してもよい。導電性の化合物は特に制限されないが、例えば、メタノールが挙げられる。添加量は特に制限されないが、好ましい現像特性又はリンス特性を維持する点で、１０質量％以下が好ましく、５質量％以下がより好ましい。下限は特に制限させず、０．０１質量％以上が好ましい。
　薬液配管としては、例えば、ＳＵＳ（ステンレス鋼）、又は、帯電防止処理の施されたポリエチレン、ポリプロピレン、若しくは、フッ素樹脂（ポリテトラフルオロエチレン、又は、パーフルオロアルコキシ樹脂等）で被膜された各種配管を使用できる。フィルター及びＯ－リングに関しても同様に、帯電防止処理の施されたポリエチレン、ポリプロピレン、又は、フッ素樹脂（ポリテトラフルオロエチレン、又は、パーフルオロアルコキシ樹脂等）を使用できる。
＜電子デバイスの製造方法＞
　本明細書は、上記したパターン形成方法を含む、電子デバイスの製造方法、及びこの製造方法により製造された電子デバイスにも関する。
　本明細書の電子デバイスの好適態様としては、電気電子機器（家電、ＯＡ（Ｏｆｆｉｃｅ　Ａｕｔｏｍａｔｉｏｎ）、メディア関連機器、光学用機器及び通信機器等）に搭載される態様が挙げられる。
　以下に実施例に基づいて本発明を更に詳細に説明する。以下の実施例に示す材料、使用量、割合、処理内容、及び処理手順等は、本発明の趣旨を逸脱しない限り適宜変更することができる。したがって、本発明の範囲は以下に示す実施例により限定的に解釈されるべきものではない。
　＜樹脂（Ａ）＞
　使用した樹脂（Ａ）の繰り返し単位の種類及び含有量（含有比率（モル％比）、重量平均分子量（Ｍｗ）、及び分散度（Ｍｗ／Ｍｎ）を表１に示す。
　なお、樹脂（Ａ）の重量平均分子量（Ｍｗ）及び分散度（Ｍｗ／Ｍｎ）はＧＰＣ（溶媒：テトラヒドロフラン（ＴＨＦ））により測定した。また、樹脂の組成比（モル％比）は、１３Ｃ－ＮＭＲ（ｎｕｃｌｅａｒ　ｍａｇｎｅｔｉｃ　ｒｅｓｏｎａｎｃｅ）により測定した。
Figure JPOXMLDOC01-appb-T000084
  
　表１に示される各繰り返し単位の構造式を以下に示す。なお、各繰り返し単位については、対応する原料モノマーの構造式として示す。Ｍｅはメチル基を表す。
Figure JPOXMLDOC01-appb-C000085
Figure JPOXMLDOC01-appb-C000086
Figure JPOXMLDOC01-appb-C000087
Figure JPOXMLDOC01-appb-C000088
＜化合物（Ｃ）＞
＜合成例１：化合物（Ｃ－１）の合成＞
　３－ヒドロキシ－２－ナフトエ酸２０．１ｇに、塩化メチレン５３０ｇ、次いでトリフェニルスルホニウム炭酸塩の２０％水溶液１８１ｇを加え、室温（２３℃）で３０分間撹拌した。水層を除去した後、蒸留水２０．０ｇを加え、分液操作を４回繰り返した。有機層の溶媒を減圧留去し、アセトン２００ｇを加え、溶解させた。酢酸エチル４００ｇを加え、室温で撹拌し、得られた固体をろ過し、化合物（Ｃ－１）２９．９ｇを得た。
　得られた化合物（Ｃ－１）についてＮＭＲ測定を行い、以下の測定結果からその構造を同定した。
１Ｈ－ＮＭＲ（ＤＭＳＯ－ｄ６）δ（ｐｐｍ）＝８．２８（ｓ，１Ｈ），７．８９－７．７４（ｍ，１６Ｈ），７．５６（ｄ，２Ｈ），７．３２（ｍ，１Ｈ），７．１５（ｍ，１Ｈ），６．９４（ｓ，１Ｈ）．
＜合成例３：化合物（Ｃ－７）の合成＞
　５－アセチルサリチル酸５．００ｇに、塩化メチレン４０．０ｇ、次いでトリフェニルスルホニウム炭酸塩の２０％水溶液４７．２ｇを加え、室温で３０分間撹拌した。水層を除去した後、蒸留水２０ｇを加え、分液操作を４回繰り返した。有機層の溶媒を減圧留去し、アセトニトニル２０．０ｇを加え、４０℃に加熱し溶解させた。ジイソプロピルエーテル２０．０ｇを加え、室温で撹拌し、得られた固体をろ過し、化合物（Ｃ－７）２．９２ｇを得た。
　得られた化合物（Ｃ－７）についてＮＭＲ測定を行い、以下の測定結果からその構造を同定した。
１Ｈ－ＮＭＲ（ＤＭＳＯ－ｄ６）δ（ｐｐｍ）＝８．２８（ｄ，１Ｈ），７．８９－７．７３（ｍ，１６Ｈ），６．６２（ｄ，１Ｈ），２．４０（ｓ，３Ｈ）．
　同様にして、化合物Ｃ－２～Ｃ－６、Ｃ－８～Ｃ－１３を合成した。
　化合物Ｃ－１～Ｃ－１３の構造を以下に記載する。なお、化合物ＣＣ－１～ＣＣ－３は、化合物（Ｃ）の範囲外であるが、便宜上、化合物（Ｃ）として記載する。Ｍｅはメチル基を表す。
Figure JPOXMLDOC01-appb-C000089
Figure JPOXMLDOC01-appb-C000090
＜光酸発生剤（Ｂ）＞
　使用した光酸発生剤（Ｂ）の構造を以下に示す。
Figure JPOXMLDOC01-appb-C000091
＜界面活性剤＞
　界面活性剤としては、下記Ｗ－１～Ｗ－４を用いた。
　Ｗ－１：メガファックＲ０８（ＤＩＣ（株）製；フッ素及びシリコン系）
　Ｗ－２：メガファックＦ１７６（大日本インキ化学工業（株）製；フッ素系）
　Ｗ－３：トロイゾルＳ－３６６（トロイケミカル（株）製；フッ素系）
　Ｗ－４：ＰＦ６５６（ＯＭＮＯＶＡ社製；フッ素系）
＜溶剤＞
　使用した溶剤を以下に示す。
　Ｓ－１：プロピレングリコールモノメチルエーテルアセテート（ＰＧＭＥＡ：１－メトキシ－２－アセトキシプロパン）
　Ｓ－２：プロピレングリコールモノメチルエーテル（ＰＧＭＥ：１－メトキシ－２－プロパノール）
　Ｓ－３：シクロヘキサノン
　Ｓ－４：乳酸エチル
　Ｓ－５：γ－ブチロラクトン
（実施例１－１～１－１４、２－１～２－１４、３－１～３－１４、４－１～４－１４、比較例１－１～１－３、２－１～２－３、３－１～３－３、及び４－１～４－３）
＜レジスト組成物の調製＞
（実施例１－１～１－１４、２－１～２－１４、比較例１－１～１－３、２－１～２－３）
　表２に示す成分を表２に示す溶剤に溶解させ、固形分濃度が３．０質量％の溶液を調製し、これを０．０２μｍのポアサイズを有するポリエチレンフィルターでろ過して、レジスト組成物を調製した。
　なお、固形分とは、溶剤以外の全ての成分を意味する。得られたレジスト組成物を、実施例及び比較例で使用した。
　また、表中、「量」欄は、各成分の、レジスト組成物中の全固形分に対する含有量（質量％）を示す。また、表には用いた溶剤の使用量（質量部）を記載した。
＜パターン形成方法（１）：ＥＢ露光、アルカリ現像（ポジ）＞
　上記のレジスト組成物を、予めヘキサメチルジシラザン（ＨＭＤＳ）処理を施した６インチＳｉウェハ上に東京エレクトロン製スピンコーターＭａｒｋ８を用いて塗布し、１００℃、６０秒間ホットプレート上で乾燥して、膜厚１００ｎｍのレジスト膜を得た。ここで、１インチは、０．０２５４ｍである。
　なお、上記Ｓｉウェハをクロム基板に変更しても、同様の結果が得られるものである。
　上記で得られたレジスト膜が塗布されたウェハを、電子線描画装置（（株）日立製作所製ＨＬ７５０、加速電圧５０ＫｅＶ）を用いて、パターン照射を行った。この際、１：１のラインアンドスペースが形成されるように描画を行った。電子線描画後、ホットプレート上で、１００℃で６０秒間加熱した後、２．３８質量％のテトラメチルアンモニウムハイドロオキサイド水溶液で３０秒間現像し、純水でリンスをした後、４０００ｒｐｍの回転数で３０秒間ウェハを回転させた後、９５℃で６０秒間加熱を行うことにより、線幅５０ｎｍの１：１ラインアンドスペースパターンのレジストパターンを得た。
＜性能評価＞
［経時に伴うラフネス性能の変動］
　経時に伴うラフネス性能の変動は、経時に伴うＬＥＲ（Ｌｉｎｅ　Ｅｄｇｅ　Ｒｏｕｇｈｎｅｓｓ）の変動により評価した。
　上記の方法で作成した線幅５０ｎｍ１：１ラインアンドスペースパターンを走査型電子顕微鏡（（株）日立製作所製Ｓ－４３００）を用いて観察した。そして、その長さ方向５０μｍに含まれる等間隔の３０点について、エッジがあるべき基準線と実際のエッジとの間の距離を測定した。そして、この距離の標準偏差を求め、３σを算出した。そして、この３σを「ＬＥＲ（ｎｍ）」とした。
　製造してから４℃の環境で１週間以内のレジスト組成物（レジスト組成物（Ａ））を使用して上記のようにパターン形成し、ＬＥＲ（ｎｍ）算出した。
　製造してから、４℃の環境で３か月間放置した後のレジスト組成物（レジスト組成物（Ｂ））を使用して上記のようにパターンを形成し、ＬＥＲ（ｎｍ）を算出した。
　レジスト組成物（Ａ）に基づくＬＥＲとレジスト組成物（Ｂ）に基づくＬＥＲの差（ｎｍ）を経時に伴うラフネス性能の変動（「ラフネス性能の変動」ともいう）とした。値が小さいほど良好な性能であることを示す。
［経時に伴う現像欠陥性能の変動（現像欠陥性能の変動）］
　上記の方法で作成した線幅５０ｎｍの１：１ラインアンドスペースパターンをケー・エル・エー・テンコール社製の欠陥検査装置ＫＬＡ２３６０（商品名）を用い、欠陥検査装置のピクセルサイズを０．１６μｍに、また閾値を２０に設定して、比較イメージとピクセル単位の重ね合わせによって生じる差異から抽出される欠陥（個数／ｃｍ２）を検出して、単位面積あたりの欠陥数（個／ｃｍ２）を算出した。その後、欠陥レビューを行うことで全欠陥の中から現像欠陥を分類抽出し、単位面積あたりの現像欠陥数（個／ｃｍ２）を算出した。
　製造してから４℃の環境で１週間以内のレジスト組成物（レジスト組成物（Ａ））を使用して上記のようにパターン形成し、単位面積あたりの現像欠陥数（個／ｃｍ２）を算出した。
　製造してから、４℃の環境で３か月間放置した後のレジスト組成物（レジスト組成物（Ｂ））を使用して上記のようにパターンを形成し、単位面積あたりの現像欠陥数（個／ｃｍ２）を算出した。
　レジスト組成物（Ａ）に基づく単位面積あたりの現像欠陥数（個／ｃｍ２）とレジスト組成物（Ｂ）に基づく単位面積あたりの現像欠陥数（個／ｃｍ２）の差（個／ｃｍ２）が０．５未満のものをＡ、０．５以上１．０未満のものをＢ、１．０以上５．０未満のものをＣ、５．０以上のものをＤとした。値が小さいほど良好な性能であることを示す。
＜パターン形成方法（２）：ＥＢ露光、有機溶剤現像（ネガ）＞
　上記のレジスト組成物を、予めヘキサメチルジシラザン（ＨＭＤＳ）処理を施した６インチＳｉウェハ上に東京エレクトロン製スピンコーターＭａｒｋ８を用いて塗布し、１００℃、６０秒間ホットプレート上で乾燥して、膜厚１００ｎｍのレジスト膜を得た。
　なお、上記Ｓｉウェハをクロム基板に変更しても、同様の結果が得られるものである。
　上記で得られたレジスト膜が塗布されたウェハを、電子線描画装置（（株）日立製作所製ＨＬ７５０、加速電圧５０ＫｅＶ）を用いて、パターン照射を行った。この際、１：１のラインアンドスペースが形成されるように描画を行った。電子線描画後、ホットプレート上で、１００℃で６０秒間加熱した後、酢酸ｎ－ブチルで３０秒間現像し、これをスピン乾燥し、９５℃で６０秒間加熱を行うことにより、線幅５０ｎｍの１：１ラインアンドスペースパターンのレジストパターンを得た。
＜性能評価＞
［経時に伴うラフネス性能の変動］
　経時に伴うラフネス性能の変動は、経時に伴うＬＥＲ（Ｌｉｎｅ　Ｅｄｇｅ　Ｒｏｕｇｈｎｅｓｓ）の変動により評価した。
　上記の方法で作成した線幅５０ｎｍ１：１ラインアンドスペースパターンを走査型電子顕微鏡（（株）日立製作所製Ｓ－４３００）を用いて観察した。そして、その長さ方向５０μｍに含まれる等間隔の３０点について、エッジがあるべき基準線と実際のエッジとの間の距離を測定した。そして、この距離の標準偏差を求め、３σを算出した。そして、この３σを「ＬＥＲ（ｎｍ）」とした。
　製造してから４℃の環境で１週間以内のレジスト組成物（レジスト組成物（Ａ））を使用して上記のようにパターン形成し、ＬＥＲ（ｎｍ）算出した。
　製造してから、４℃の環境で３か月間放置した後のレジスト組成物（レジスト組成物（Ｂ））を使用して上記のようにパターンを形成し、ＬＥＲ（ｎｍ）を算出した。
　レジスト組成物（Ａ）に基づくＬＥＲとレジスト組成物（Ｂ）に基づくＬＥＲの差（ｎｍ）を経時に伴うラフネス性能の変動（「ラフネス性能の変動」ともいう）とした。値が小さいほど良好な性能であることを示す。
［経時に伴う現像欠陥性能の変動（現像欠陥性能の変動）］
　上記の方法で作成した線幅５０ｎｍの１：１ラインアンドスペースパターンをケー・エル・エー・テンコール社製の欠陥検査装置ＫＬＡ２３６０（商品名）を用い、欠陥検査装置のピクセルサイズを０．１６μｍに、また閾値を２０に設定して、比較イメージとピクセル単位の重ね合わせによって生じる差異から抽出される欠陥（個数／ｃｍ２）を検出して、単位面積あたりの欠陥数（個／ｃｍ２）を算出した。その後、欠陥レビューを行うことで全欠陥の中から現像欠陥を分類抽出し、単位面積あたりの現像欠陥数（個／ｃｍ２）を算出した。
　製造してから４℃の環境で１週間以内のレジスト組成物（レジスト組成物（Ａ））を使用して上記のようにパターン形成し、単位面積あたりの現像欠陥数（個／ｃｍ２）を算出した。
　製造してから、４℃の環境で３か月間放置した後のレジスト組成物（レジスト組成物（Ｂ））を使用して上記のようにパターンを形成し、単位面積あたりの現像欠陥数（個／ｃｍ２）を算出した。
　レジスト組成物（Ａ）に基づく単位面積あたりの現像欠陥数（個／ｃｍ２）とレジスト組成物（Ｂ）に基づく単位面積あたりの現像欠陥数（個／ｃｍ２）の差（個／ｃｍ２）が０．５未満のものをＡ、０．５以上１．０未満のものをＢ、１．０以上５．０未満のものをＣ、５．０以上のものをＤとした。値が小さいほど良好な性能であることを示す。
　得られた評価結果を表３に示す。
（ＥＵＶ露光）
（実施例３－１～３－１４、４－１～４－１４、比較例３－１～３－３、４－１～４－３）
＜パターン形成方法（３）：ＥＵＶ露光、アルカリ現像（ポジ）＞
　シリコンウエハ上に下層膜形成用組成物ＡＬ４１２（Ｂｒｅｗｅｒ　Ｓｃｉｅｎｃｅ社製）を塗布し、２０５℃で６０秒間ベークして、膜厚２０ｎｍの下地膜を形成した。その上に、表４に示すレジスト組成物を塗布し、１００℃で６０秒間ベークして、膜厚４０ｎｍのレジスト膜を形成した。
　ＥＵＶ露光装置（Ｅｘｉｔｅｃｈ社製、Ｍｉｃｒｏ　Ｅｘｐｏｓｕｒｅ　Ｔｏｏｌ、ＮＡ０．３、Ｑｕａｄｒｕｐｏｌ、アウターシグマ０．６８、インナーシグマ０．３６）を用いて、得られたレジスト膜を有するシリコンウエハに対してパターン照射を行った。なお、レクチルとしては、ラインサイズ＝５０ｎｍであり、且つ、ライン：スペース＝１：１であるマスクを用いた。
　露光後のレジスト膜を９０℃で６０秒間ベークした後、テトラメチルアンモニウムハイドロオキサイド水溶液（２．３８質量％）で３０秒間現像し、次いで純水で３０秒間リンスした。その後、これをスピン乾燥してポジ型のパターンを得た。
＜性能評価＞
［経時に伴うラフネス性能の変動］
　経時に伴うラフネス性能の変動は、経時に伴うＬＥＲ（Ｌｉｎｅ　Ｅｄｇｅ　Ｒｏｕｇｈｎｅｓｓ）の変動により評価した。
　上記の方法で作成した線幅５０ｎｍ１：１ラインアンドスペースパターンを走査型電子顕微鏡（（株）日立製作所製Ｓ－４３００）を用いて観察した。そして、その長さ方向５０μｍに含まれる等間隔の３０点について、エッジがあるべき基準線と実際のエッジとの間の距離を測定した。そして、この距離の標準偏差を求め、３σを算出した。そして、この３σを「ＬＥＲ（ｎｍ）」とした。
　製造してから４℃の環境で１週間以内のレジスト組成物（レジスト組成物（Ａ））を使用して上記のようにパターン形成し、ＬＥＲ（ｎｍ）算出した。
　製造してから、４℃の環境で３か月間放置した後のレジスト組成物（レジスト組成物（Ｂ））を使用して上記のようにパターンを形成し、ＬＥＲ（ｎｍ）を算出した。
　レジスト組成物（Ａ）に基づくＬＥＲとレジスト組成物（Ｂ）に基づくＬＥＲの差（ｎｍ）を経時に伴うラフネス性能の変動（「ラフネス性能の変動」ともいう）とした。値が小さいほど良好な性能であることを示す。
［経時に伴う現像欠陥性能の変動（現像欠陥性能の変動）］
　上記の方法で作成した線幅５０ｎｍの１：１ラインアンドスペースパターンをケー・エル・エー・テンコール社製の欠陥検査装置ＫＬＡ２３６０（商品名）を用い、欠陥検査装置のピクセルサイズを０．１６μｍに、また閾値を２０に設定して、比較イメージとピクセル単位の重ね合わせによって生じる差異から抽出される欠陥（個数／ｃｍ２）を検出して、単位面積あたりの欠陥数（個／ｃｍ２）を算出した。その後、欠陥レビューを行うことで全欠陥の中から現像欠陥を分類抽出し、単位面積あたりの現像欠陥数（個／ｃｍ２）を算出した。
　製造してから４℃の環境で１週間以内のレジスト組成物（レジスト組成物（Ａ））を使用して上記のようにパターン形成し、単位面積あたりの現像欠陥数（個／ｃｍ２）を算出した。
　製造してから、４℃の環境で３か月間放置した後のレジスト組成物（レジスト組成物（Ｂ））を使用して上記のようにパターンを形成し、単位面積あたりの現像欠陥数（個／ｃｍ２）を算出した。
　レジスト組成物（Ａ）に基づく単位面積あたりの現像欠陥数（個／ｃｍ２）とレジスト組成物（Ｂ）に基づく単位面積あたりの現像欠陥数（個／ｃｍ２）の差（個／ｃｍ２）が０．５未満のものをＡ、０．５以上１．０未満のものをＢ、１．０以上５．０未満のものをＣ、５．０以上のものをＤとした。値が小さいほど良好な性能であることを示す。
＜パターン形成方法（４）：ＥＵＶ露光、有機溶剤現像（ネガ）＞
　シリコンウエハ上に下層膜形成用組成物ＡＬ４１２（Ｂｒｅｗｅｒ　Ｓｃｉｅｎｃｅ社製）を塗布し、２０５℃で６０秒間ベークして、膜厚２０ｎｍの下地膜を形成した。その上に、表４に示すレジスト組成物を塗布し、１００℃で６０秒間ベークして、膜厚４０ｎｍのレジスト膜を形成した。
　ＥＵＶ露光装置（Ｅｘｉｔｅｃｈ社製、Ｍｉｃｒｏ　Ｅｘｐｏｓｕｒｅ　Ｔｏｏｌ、ＮＡ０．３、Ｑｕａｄｒｕｐｏｌ、アウターシグマ０．６８、インナーシグマ０．３６）を用いて、得られたレジスト膜を有するシリコンウエハに対してパターン照射を行った。なお、レクチルとしては、ラインサイズ＝５０ｎｍであり、且つ、ライン：スペース＝１：１であるマスクを用いた。
　露光後のレジスト膜を９０℃で６０秒間ベークした後、酢酸ｎ－ブチルで３０秒間現像し、これをスピン乾燥してネガ型のパターンを得た。
＜性能評価＞
［経時に伴うラフネス性能の変動］
　経時に伴うラフネス性能の変動は、経時に伴うＬＥＲ（Ｌｉｎｅ　Ｅｄｇｅ　Ｒｏｕｇｈｎｅｓｓ）の変動により評価した。
　上記の方法で作成した線幅５０ｎｍ１：１ラインアンドスペースパターンを走査型電子顕微鏡（（株）日立製作所製Ｓ－４３００）を用いて観察した。そして、その長さ方向５０μｍに含まれる等間隔の３０点について、エッジがあるべき基準線と実際のエッジとの間の距離を測定した。そして、この距離の標準偏差を求め、３σを算出した。そして、この３σを「ＬＥＲ（ｎｍ）」とした。
　製造してから４℃の環境で１週間以内のレジスト組成物（レジスト組成物（Ａ））を使用して上記のようにパターン形成し、ＬＥＲ（ｎｍ）算出した。
　製造してから、４℃の環境で３か月間放置した後のレジスト組成物（レジスト組成物（Ｂ））を使用して上記のようにパターンを形成し、ＬＥＲ（ｎｍ）を算出した。
　レジスト組成物（Ａ）に基づくＬＥＲとレジスト組成物（Ｂ）に基づくＬＥＲの差（ｎｍ）を経時に伴うラフネス性能の変動（「ラフネス性能の変動」ともいう）とした。値が小さいほど良好な性能であることを示す。
［経時に伴う現像欠陥性能の変動（現像欠陥性能の変動）］
　上記の方法で作成した線幅５０ｎｍの１：１ラインアンドスペースパターンをケー・エル・エー・テンコール社製の欠陥検査装置ＫＬＡ２３６０（商品名）を用い、欠陥検査装置のピクセルサイズを０．１６μｍに、また閾値を２０に設定して、比較イメージとピクセル単位の重ね合わせによって生じる差異から抽出される欠陥（個数／ｃｍ２）を検出して、単位面積あたりの欠陥数（個／ｃｍ２）を算出した。その後、欠陥レビューを行うことで全欠陥の中から現像欠陥を分類抽出し、単位面積あたりの現像欠陥数（個／ｃｍ２）を算出した。
　製造してから４℃の環境で１週間以内のレジスト組成物（レジスト組成物（Ａ））を使用して上記のようにパターン形成し、単位面積あたりの現像欠陥数（個／ｃｍ２）を算出した。
　製造してから、４℃の環境で３か月間放置した後のレジスト組成物（レジスト組成物（Ｂ））を使用して上記のようにパターンを形成し、単位面積あたりの現像欠陥数（個／ｃｍ２）を算出した。
　レジスト組成物（Ａ）に基づく単位面積あたりの現像欠陥数（個／ｃｍ２）とレジスト組成物（Ｂ）に基づく単位面積あたりの現像欠陥数（個／ｃｍ２）の差（個／ｃｍ２）が０．５未満のものをＡ、０．５以上１．０未満のものをＢ、１．０以上５．０未満のものをＣ、５．０以上のものをＤとした。値が小さいほど良好な性能であることを示す。
　得られた評価結果を表４に示す。
Figure JPOXMLDOC01-appb-T000092
  
Figure JPOXMLDOC01-appb-T000093
  
Figure JPOXMLDOC01-appb-T000094
  
Figure JPOXMLDOC01-appb-T000095
  
Figure JPOXMLDOC01-appb-T000096
　上記表３、表４に示すように、本発明のレジスト組成物によれば、アルカリ現像又は有機溶剤現像で微細のパターンを形成した場合に、経時に伴うラフネス性能の変動が抑制され、経時に伴う現像欠陥性能の変動が抑制される一方で、比較例のレジスト組成物では、これら性能が不十分であった。
　本発明によれば、経時に伴うラフネス性能の変動が抑制され、経時に伴う現像欠陥性能の変動が抑制される感活性光線性又は感放射線性樹脂組成物を提供することができる。また、本発明によれば、上記感活性光線性又は感放射線性樹脂組成物を用いた感活性光線性又は感放射線性膜、パターン形成方法、電子デバイスの製造方法、及び化合物を提供することができる。
　本発明を詳細にまた特定の実施態様を参照して説明したが、本発明の精神と範囲を逸脱することなく様々な変更や修正を加えることができることは当業者にとって明らかである。
　本出願は、本出願は、２０２１年８月３１日出願の日本特許出願（特願２０２１－１４２００４）に基づくものであり、その内容はここに参照として取り込まれる。

 

Claims (16)

  1. （Ａ）酸の作用により分解し極性が増大する樹脂、及び
    （Ｃ）活性光線又は放射線の照射によって酸を発生する化合物であって、下記一般式（Ｉ）で表される、化合物を含有する感活性光線性又は感放射線性樹脂組成物であって、
    　前記樹脂（Ａ）が下記一般式（ＡＩ）で表される繰り返し単位を含む、感活性光線性又は感放射線性樹脂組成物。
    Figure JPOXMLDOC01-appb-C000001
    一般式（ＡＩ）中、
    ＲＡ、ＲＢ、及びＲＣは、それぞれ独立に、水素原子、アルキル基、シクロアルキル基、ハロゲン原子、シアノ基、又はアルコキシカルボニル基を表す。但し、ＲＣはＡｒＡと結合して環を形成していてもよく、その場合のＲＣは単結合又はアルキレン基を表す。
    ＬＡは、単結合又は２価の連結基を表す。
    ＡｒＡは、（ｎ＋１）価の芳香環基を表す。ＡｒＡがＲＣと結合して環を形成する場合には、ＡｒＡは、（ｎ＋２）価の芳香環基を表す。
    ｎは、１～５の整数を表す。
    Figure JPOXMLDOC01-appb-C000002
    一般式（Ｉ）中、
    Ｒ０は置換基を表す。
    ｐは０～４の整数である。ｑは０～３の整数である。ｐ＋ｑ≧１である。
    ｑが０の場合、全てのＲ０において、炭素原子の総数と酸素原子の総数を足した合計が３以上である。
    ｐが２以上の整数の場合、複数のＲ０は同一であってもよく、異なっていても良い。
    Ｍ＋はカチオンを表す。
  2. 　前記一般式（Ｉ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、アルキル基、－Ｃ（＝Ｏ）Ｒ１、又はアリール基を表し、Ｒ１は有機基を表す、請求項１に記載の感活性光線性又は感放射線性樹脂組成物。
  3. 　活性光線又は放射線の照射によって、前記化合物（Ｃ）が発生する酸よりも強い酸を発生する化合物（Ｂ）を含有する、請求項１又は２に記載の感活性光線性又は感放射線性樹脂組成物。
  4. 　前記樹脂（Ａ）が、活性光線又は放射線の照射により分解して酸を発生する基を有する繰り返し単位を有する、請求項１又は２に記載の感活性光線性又は感放射線性樹脂組成物。
  5. 　前記活性光線又は放射線の照射により分解して酸を発生する基を有する繰り返し単位が、下記一般式（Ｓ－１）で表される繰り返し単位である、請求項４に記載の感活性光線性又は感放射線性樹脂組成物。
    Figure JPOXMLDOC01-appb-C000003
    一般式（Ｓ－１）中、
    Ｒ２１は、水素原子、アルキル基、アリール基、又はハロゲン原子を表す。
    Ｘ１は、単結合又は２価の連結基を表す。
    Ｒｃ１～Ｒｃ３は、それぞれ独立に、アルキル基、アリール基、又はヘテロアリール基を表す。Ｒｃ１～Ｒｃ３のうち２つが結合して環構造を形成してもよい。
  6. 　前記一般式（Ｉ）中、ｐが３又は４を表す、請求項１又は２に記載の感活性光線性又は感放射線性樹脂組成物。
  7. 　前記一般式（Ｉ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、－Ｃ（＝Ｏ）Ｒ１を表す、請求項１又は２に記載の感活性光線性又は感放射線性樹脂組成物。
  8. 　前記一般式（Ｉ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、アリール基を表す、請求項１又は２に記載の感活性光線性又は感放射線性樹脂組成物。
  9. 　請求項１又は２に記載の感活性光線性又は感放射線性樹脂組成物により形成された、感活性光線性又は感放射線性膜。
  10. 　請求項１又は２に記載の組成物により基板上に感活性光線性又は感放射線性膜を形成する工程と、前記感活性光線性又は感放射線性膜を露光する工程と、前記露光された感活性光線性又は感放射線性膜を現像液を用いて現像する工程と、を有する、パターン形成方法。
  11. 　請求項１０に記載のパターン形成方法を含む、電子デバイスの製造方法。
  12. 　下記一般式（ＩＡ）で表される化合物。
    Figure JPOXMLDOC01-appb-C000004
    一般式（ＩＡ）中、
    Ｒ０はアルキル基、－Ｃ（＝Ｏ）Ｒ１、又はアリール基を表す。Ｒ１は有機基を表す。
    ｐは０～４の整数である。ｑは０～３の整数である。ｐ＋ｑ≧１である。
    ｑが０の場合、全てのＲ０において、炭素原子の総数と酸素原子の総数を足した合計が３以上である。
    ｐが２以上の整数の場合、複数のＲ０は同一であってもよく、異なっていても良い。
    Ｍ＋はカチオンを表す。
  13. 　前記一般式（ＩＡ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、アルキル基、－Ｃ（＝Ｏ）Ｒ１、又はアリール基を表し、Ｒ１は有機基を表す、請求項１２に記載の化合物。
  14. 　前記一般式（ＩＡ）中、ｐが３又は４を表す、請求項１２又は１３に記載の化合物。
  15. 　前記一般式（ＩＡ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、－Ｃ（＝Ｏ）Ｒ１を表す、請求項１２又は１３に記載の化合物。
  16. 　前記一般式（ＩＡ）中、ｐが１におけるＲ０、及びｐが２～４における複数のＲ０のうちの少なくとも一つは、アリール基を表す、請求項１２又は１３に記載の化合物。
     

     
PCT/JP2022/031954 2021-08-31 2022-08-24 感活性光線性又は感放射線性樹脂組成物、感活性光線性又は感放射線性膜、パターン形成方法、電子デバイスの製造方法、及び化合物 WO2023032794A1 (ja)