WO2022220655A1 - 이차전지 - Google Patents

이차전지 Download PDF

Info

Publication number
WO2022220655A1
WO2022220655A1 PCT/KR2022/005502 KR2022005502W WO2022220655A1 WO 2022220655 A1 WO2022220655 A1 WO 2022220655A1 KR 2022005502 W KR2022005502 W KR 2022005502W WO 2022220655 A1 WO2022220655 A1 WO 2022220655A1
Authority
WO
WIPO (PCT)
Prior art keywords
vent member
secondary battery
case
outside
comonomer
Prior art date
Application number
PCT/KR2022/005502
Other languages
English (en)
French (fr)
Inventor
임훈희
김상훈
강민형
송대웅
유형균
황수지
Original Assignee
주식회사 엘지에너지솔루션
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지에너지솔루션 filed Critical 주식회사 엘지에너지솔루션
Priority to JP2023526646A priority Critical patent/JP2023548505A/ja
Priority to CN202280007436.6A priority patent/CN116529943A/zh
Priority to EP22788510.0A priority patent/EP4224612A1/en
Priority to US18/035,232 priority patent/US20240014506A1/en
Publication of WO2022220655A1 publication Critical patent/WO2022220655A1/ko

Abstract

본 발명은 벤트 부재를 가지는 이차전지를 개시한다. 본 발명의 일 실시양태에 따른 이차전지는, 전극 조립체; 상기 전극 조립체를 수납하는 케이스; 및 벤트 부재를 포함하고, 상기 벤트 부재가 상기 케이스 외부로 돌출되고, 상기 케이스 외부로 돌출된 벤트 부재의 일단이 상기 케이스에 접합된다.

Description

이차전지
본 출원은 2021년 4월 15일에 출원된 한국특허출원 제10-2021-0049364호에 기초한 우선권을 주장한다.
본 발명은 이차전지에 관한 것으로서, 보다 상세하게는, 벤트 부재를 구비한 이차전지에 관한 것이다.
이차전지는 다양한 제품에 적용이 가능하며 높은 에너지 밀도 등 전기적 특성이 우수하다. 이차전지는 휴대용 기기뿐만 아니라 전력으로 구동되는 전기자동차(EV)나 하이브리드 전기자동차(HEV)에도 많이 사용된다. 이차전지는 화석연료의 사용을 크게 줄일 수 있고 에너지 소비 과정에서 부산물이 발생하지 않는다는 점에서 환경 친화성 및 에너지 효율 향상을 위한 새로운 에너지원으로 주목받고 있다.
현재 널리 사용되는 이차전지로는 리튬 이온 전지, 리튬 폴리머 전지, 니켈 카드뮴 전지, 니켈 수소 전지, 니켈 아연 전지 등이 있다.
이차전지는 일반적으로 양극/분리막/음극 구조를 갖는 적어도 하나의 단위 셀을 포함하는 전극 조립체가 외층, 금속 배리어층, 실란트층이 순차적으로 적층된 라미네이트 시트의 케이스에 수납되고, 상기 실란트층의 실란트 수지를 융착하여 전극 조립체가 밀봉된 구조를 갖는다.
종래의 이차전지에서는 이차전지 내부의 단락, 과충전 또는 과방전, 온도 조절 등 다양한 원인에 의해 전지가 발화될 수 있다. 이때, 이차전지 내부의 온도가 급격히 상승함과 동시에 인접 셀로 열이 전달되는 열 폭주 현상(Thermal Propagation)이 발생하여 화재가 더욱 커질 수 있다.
열 폭주 현상 발생 시, 즉 이차전지 내부 온도가 상승할 때, 가스에 의한 전극의 손상을 최소화하기 위해, 가스를 한 방향으로 배출하는 디렉셔널 벤팅(Directional Venting) 특성이 요구된다. 그러나, 종래의 이차전지는 특정 방향으로 가스 배출을 유도하기 어려운 문제점이 있다.
따라서, 본 발명은 특정 방향으로 가스 배출을 유도하여 안전성이 향상된 이차전지를 제공하는 것을 목적으로 한다.
따라서 본 발명이 해결하고자 하는 과제는, 특정 방향으로 가스 배출을 유도할 수 있어 안전성이 향상된 이차전지를 제공하는 것이다.
상기 과제를 해결하기 위하여, 본 발명의 일 측면에 따르면, 하기 구현예들의 이차전지가 제공된다.
제1 구현예는,
전극 조립체; 상기 전극 조립체를 수납하는 케이스; 및 벤트 부재를 포함하고, 상기 벤트 부재가 상기 케이스 외부로 돌출되고, 상기 케이스 외부로 돌출된 벤트 부재의 일단이 상기 케이스 외측에 접합되는 것을 특징으로 하는 이차전지에 관한 것이다.
제2 구현예는, 제1 구현예에 있어서,
상기 벤트 부재가 케이스 외부로 돌출된 부분이 절곡되어 상기 케이스 외부로 돌출된 벤트 부재의 일단이 상기 케이스 외측에 접합될 수 있다.
제3 구현예는, 제1 구현예 또는 제2 구현예에 있어서,
상기 케이스는 상기 전극 조립체를 수납하는 수납부 및 실란트 수지를 포함하고 상기 전극 조립체를 밀봉하기 위해 형성된 실링부를 구비할 수 있고, 상기 케이스 외부로 돌출된 벤트 부재의 일단이 상기 수납부 내에서 전극 조립체가 위치하지 않는 부분과 대응하는 케이스 외측에 접합될 수 있다.
제4 구현예는, 제3 구현예에 있어서,
상기 벤트 부재의 타단이 상기 실링부에 위치할 수 있다.
제5 구현예는, 제4 구현예에 있어서,
상기 전극 조립체에 전극 리드가 부착될 수 있고, 상기 벤트 부재의 타단이 상기 전극 리드가 외부로 노출되는 측의 실링부에 위치할 수 있다.
제6 구현예는, 제4 구현예 또는 제5 구현예에 있어서,
상기 전극 조립체에 전극 리드가 부착될 수 있고, 상기 벤트 부재의 타단이 상기 전극 리드가 외부로 노출되는 측의 코너 측 실링부에 위치할 수 있다.
제7 구현예는, 제3 구현예 내지 제6 구현예 중 어느 한 구현예에 있어서,
상기 벤트 부재의 융점이 상기 실란트 수지의 융점보다 낮을 수 있다.
제8 구현예는, 제1 구현예 내지 제7 구현예 중 어느 한 구현예에 있어서,
상기 벤트 부재가 100℃ 내지 120℃에서 벤팅될 수 있다.
제9 구현예는, 제8 구현예에 있어서,
상기 벤트 부재가 1.5 atm 이상의 압력에서 벤팅될 수 있다.
제10 구현예는, 제1 구현예 내지 제9 구현예 중 어느 한 구현예에 있어서,
상기 벤트 부재의 100℃ 이상에서의 최대 실링 강도가 6 kgf/15 mm 미만일 수 있다.
제11 구현예는, 제1 구현예 내지 제10 구현예 중 어느 한 구현예에 있어서,
상기 벤트 부재의 100℃ 이상에서의 평균 실링 강도가 4.5 kgf/15 mm 미만일 수 있다.
제12 구현예는, 제1 구현예 내지 제11 구현예 중 어느 한 구현예에 있어서,
상기 벤트 부재의 상온 내지 60℃에서의 최대 실링 강도가 6 kgf/15 mm 이상일 수 있다.
제13 구현예는, 제1 구현예 내지 제12 구현예 중 어느 한 구현예에 있어서,
상기 벤트 부재의 상온 내지 60℃에서의 평균 실링 강도가 4.5 kgf/15 mm 이상일 수 있다.
제14 구현예는, 제1 구현예 내지 제13 구현예 중 어느 한 구현예에 있어서,
상기 벤트 부재가 탄소수 6 이상의 코모노머(comonomer)를 가지는 선형 저밀도 폴리에틸렌을 포함할 수 있다.
제15 구현예는, 제14 구현예에 있어서,
상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌이 메탈로센 촉매의 존재 하에 중합된 것일 수 있다.
제16 구현예는, 제14 구현예 또는 제15 구현예에 있어서,
상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌에서 상기 탄소수 6 이상의 코모노머의 함량이 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌 100 중량% 대비 15 중량% 이하일 수 있다.
제17 구현예는, 제14 구현예 내지 제16 구현예 중 어느 한 구현예에 있어서,
상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 다분산성 지수(Poly Dispersity Index; PDI)가 4 이하일 수 있다.
제18 구현예는, 제14 구현예 내지 제17 구현예 중 어느 한 구현예에 있어서,
상기 케이스는 실란트 수지를 포함하고 상기 전극 조립체를 밀봉하기 위해 형성된 실링부를 구비할 수 있고, 상기 실란트 수지의 결정화 온도와 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 결정화 온도의 차이가 10℃ 이하일 수 있다.
제19 구현예는, 제18 구현예에 있어서,
상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 결정화 온도가 90℃ 내지 115℃일 수 있다.
제20 구현예는, 제14 구현예 내지 제19 구현예 중 어느 한 구현예에 있어서,
상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 중량평균분자량이 10만 g/mol 내지 40만 g/mol일 수 있다.
제21 구현예는, 제1 구현예 내지 제20 구현예 중 어느 한 구현예에 있어서,
상기 벤트 부재가 100℃ 내지 130℃의 융점을 가질 수 있다.
제22 구현예는, 제1 구현예 내지 제21 구현예 중 어느 한 구현예에 있어서,
상기 이차전지가 파우치형 이차전지일 수 있다.
본 발명의 일 실시형태에 따른 이차전지는 일단이 케이스 외부로 돌출되어 케이스 외측에 접합된 벤트 부재가 전지가 스웰링 되었을 때 당겨져, 보다 빠르게 벤트를 유도할 수 있다. 이에 따라, 전지의 안전성이 향상될 수 있다.
본 명세서에 첨부되는 다음의 도면들은 본 발명의 바람직한 실시예를 예시하는 것이며, 전술한 발명의 내용과 함께 본 발명의 기술사상을 더욱 이해시키는 역할을 하는 것이므로, 본 발명은 그러한 도면에 기재된 사항에만 한정되어 해석되어서는 아니 된다.
도 1은, 본 발명의 일 실시양태에 따른 이차전지를 나타낸 평면도이다.
도 2는, 도 1의 A-A`의 단면도를 나타낸 도이다.
도 3은, 본 발명의 일 실시양태에 따른 이차전지에서 벤트가 일어나는 양상을 나타낸 도이다.
이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세히 설명하기로 한다. 이에 앞서, 본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.
따라서, 본 명세서에 기재된 실시예와 도면에 도시된 구성은 본 발명의 가장 바람직한 일 실시예에 불과할 뿐이고 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형예들이 있을 수 있음을 이해하여야 한다.
본 발명의 일 측면에 따른 이차전지는, 전극 조립체; 상기 전극 조립체를 수납하는 케이스; 및 벤트 부재를 포함하고, 상기 벤트 부재가 상기 케이스 외부로 돌출되고, 상기 케이스 외부로 돌출된 벤트 부재의 일단이 상기 케이스 외측에 접합된다.
도 1은 본 발명의 일 실시양태에 따른 이차전지를 나타낸 것이다.
이차전지(10)는 전극 리드(11)가 부착된 전극 조립체(12), 및 케이스(13)를 구비한다.
상기 전극 조립체(12)는 양극판, 음극판 및 분리막을 포함한다. 전극 조립체(12)는 분리막을 사이에 두고 양극판과 음극판이 순차적으로 적층될 수 있다.
양극판은 도전성이 우수한 금속 박판, 예를 들면 알루미늄(Al) 호일(foil)로 이루어진 양극 집전체와 이의 적어도 일면에 코팅된 양극 활물질층을 포함할 수 있다. 또한, 상기 양극판은 일측 단부에 금속 재질, 이를테면 알루미늄(Al) 재질로 이루어진 양극탭을 포함할 수 있다. 상기 양극탭은 양극판의 일측 단부로부터 돌출될 수 있다. 상기 양극탭은 양극판의 일측 단부에 용접되거나 도전성 접착제를 이용하여 접합될 수 있다.
음극판은 도전성 금속 박판, 예를 들면 구리(Cu) 호일로 이루어진 음극 집전체와, 이의 적어도 일면에 코팅된 음극 활물질층을 포함할 수 있다. 또한, 상기 음극판은 일측 단부에 금속 재질, 이를테면 니켈(Ni) 재질로 형성된 음극탭을 포함할 수 있다. 상기 음극탭은 음극판의 일측 단부로부터 돌출될 수 있다. 상기 음극탭은 음극판의 일측 단부에 용접되거나 도전성 접착제를 이용하여 접합될 수 있다.
분리막은 양극판과 음극판 사이에 위치하여, 양극판과 음극판을 서로 전기적으로 절연시킨다. 상기 분리막은 양극판과 음극판 사이에서 리튬 이온이 서로 통과할 수 있도록 다공성 막일 수 있다. 상기 분리막은, 예를 들어 폴리에틸렌(PE), 또는 폴리프로필렌(PP), 또는 이들의 복합필름을 사용한 다공성 막을 포함할 수 있다.
분리막의 표면에는 무기물 코팅층이 구비될 수 있다. 무기물 코팅층은 무기물 입자들이 바인더에 의해 서로 결합되어 입자들 사이에 기공 구조(interstitial volume)를 형성한 구조를 가질 수 있다.
전극 조립체(12)는 긴 시트형의 양극들과 음극들을 분리막이 개재된 상태에서 권취한 구조의 젤리-롤(권취형) 전극 조립체, 소정 크기의 단위로 절취한 다수의 양극과 음극들을 분리막을 개재한 상태로 순차적으로 적층한 스택형(적층형) 전극 조립체, 소정 단위의 양극과 음극들을 분리막을 개재한 상태로 적층한 바이셀(Bi-cell) 또는 풀 셀(Full dell)들을 권취한 구조의 스택/폴딩형 전극 조립체 등일 수 있다.
상기 케이스(13)는 전극 조립체(12)를 수납하는 역할을 한다.
본 발명의 일 실시양태에서, 상기 케이스(13)는 도 1에 도시된 바와 같이, 전극 조립체(12)를 수납하는 수납부(13a), 및 전극 조립체(12)를 밀봉하기 위해 형성된 실링부(13b)를 구비할 수 있다.
상기 실링부(13b)는 실란트 수지를 포함할 수 있고, 상기 실란트 수지가 상기 수납부(13a)의 외주면을 따라 융착하여 전극 조립체(12)를 밀봉할 수 있다.
본 발명의 일 실시양태에서, 상기 케이스(13)는 외부 충격 보호를 위한 외층, 수분을 차단하는 금속 배리어층, 및 케이스를 밀봉하는 실란트층의 다층 구조의 필름 형태로 구비될 수 있다.
상기 외층은, 폴리(에틸렌테레프탈레이트)(Poly(ethylene terephthalate); PET), 폴리부틸렌테레프타레이트, 폴리에틸렌나프탈레이트, 폴리부틸렌나프탈레이트, 공중합 폴리에스테르, 폴리카보네이트, 나일론 등을 사용한 폴리에스터계 필름을 포함할 수 있고, 단일층 또는 다층으로 구성될 수 있다.
상기 금속 배리어층은, 알루미늄, 구리 등을 포함할 수 있다.
상기 실란트층은 실란트 수지를 포함할 수 있고, 단일층 또는 다층으로 구성될 수 있다.
상기 실란트 수지는 폴리프로필렌(PP), 산 변성 폴리프로필렌(Acid modified polypropylene; PPa), 랜덤 폴리프로필렌(random polypropylene), 에틸렌 프로필렌 공중합체, 또는 이들 중 2 이상을 포함할 수 있다. 상기 에틸렌 프로필렌 공중합체는 에틸렌 프로필렌 고무(ethylene-propylene rubber), 에틸렌-프로필렌 블록 공중합체 등을 포함할 수 있으나, 이에 한정되지는 않는다.
본 발명의 일 실시양태에서, 상기 케이스(13)는 파우치 형태일 수 있다.
파우치 형태의 케이스(13)는 상부 파우치와 하부 파우치를 포함할 수 있다. 케이스(13)가 상부 파우치와 하부 파우치를 포함하는 경우, 실란트 수지가 서로 대향하도록 상부 파우치와 하부 파우치를 배치한 후, 대향하는 실란트 수지가 열과 압력에 의해 상호 융착됨으로써 전지를 밀봉하는 구조를 가질 수 있다.
실링부(13b)의 융착은 열융착, 초음파에 의한 융착 등일 수 있으나, 실링부(13b)를 융착시킬 수 있다면 특별히 제한되지는 않는다.
실링부(13b)는 일부 실시양태에서 케이스(13)의 테두리에서 4면 실링 또는 3면 실링될 수 있다. 3면 실링 구조에서, 상부 파우치와 하부 파우치가 하나의 파우치 시트에 형성된 후 상부 파우치 및 하부 파우치의 경계면을 절곡시켜 상부 파우치 및 하부 파우치에 형성된 수납부(13a)들이 포개지도록 한 상태에서 절곡부를 제외한 나머지 3면의 테두리가 실링된다.
상기 전극 리드(11)는 도 1에 도시된 바와 같이, 전극 리드(11)의 일부가 상기 케이스(13)의 외부로 노출되도록 케이스(13)에 수납될 수 있다.
본 발명의 일 실시양태에 따른 이차전지(10)는 리드 필름(14)을 구비한다. 상기 리드 필름(14)은 상기 전극 리드(11)의 외면의 일부를 감싸고, 전극 리드(11)와 케이스(13) 사이에 개재된다. 예컨대, 리드 필름(14)이 전극 리드(11)와, 전극 리드(11)가 케이스(13)로부터 돌출되거나 연장되는 부분의 케이스(13)의 실링부(13b) 사이에 개재되어 전극 리드(11)와 상기 케이스(13)의 결착을 도울 수 있다.
도 1을 참조하면, 본 발명의 일 실시양태에 따른 이차전지(10)는 벤트 부재(15)를 포함한다. 열 폭주 현상 발생 시, 상기 벤트 부재(15)는 특정한 방향으로 가스의 배출을 유도하여 전지의 안전성을 향상시킬 수 있다.
도 2는 도 1의 A-A`의 단면도를 나타낸 도이다.
도 2를 참조하면, 벤트 부재(15)는 케이스(13) 외부로 돌출되고, 상기 케이스(13) 외부로 돌출된 벤트 부재(15)의 일단이 케이스 외측(16)에 접합된다. 여기서, "케이스 외측"은 벤트 부재(15)가 돌출된 부근의 케이스(13) 부분과는 구별되는 것으로, 벤트 부재(15)가 돌출된 부근의 케이스(13) 부분과는 소정 간격으로 이격되어 있다. 이 때, 벤트 부재(15)가 케이스(13) 외부로 돌출된 부분이 절곡되어 케이스(13) 외부로 돌출된 벤트 부재(15)의 일단이 상기 케이스 외측(16)에 접합될 수 있다.
도 1 및 도 2를 참조하면, 케이스(13) 외부로 돌출된 벤트 부재(15)의 일단이 수납부(13a) 내에서 전극 조립체(12)가 위치하지 않는 부분과 대응하는 케이스 외측(16)에 접합될 수 있다. 즉, 수납부(13a) 내에서 전극 조립체(12)가 위치하지 않는 부분 상에 위치한 케이스 외측(16)에 상기 케이스(13) 외부로 돌출된 벤트 부재(15)의 일단이 접합될 수 있다.
도 3은 본 발명의 일 실시양태에 따른 이차전지에서 벤트가 발생하는 상태를 나타낸 도면이다. 구체적으로, 도 3은 본 발명의 일 실시양태에 따른 이차전지에서 벤트 부재를 도시한 단면도이다.
도 3을 참조하면, 전지가 정상적으로 작동하는 온도에서, 벤트 부재는 케이스를 외부로부터 밀봉하는 역할을 한다. 전지의 비정상적인 작동으로 인해 전지의 온도가 과도하게 상승하면 전지 내부에서 가스가 발생됨에 따라 전지가 스웰링 되었을 때, 케이스(13) 역시 스웰링 된다. 케이스(13) 외부로 돌출된 벤트 부재(15)의 일단이 케이스 외측(16)에 접합됨에 따라, 스웰링된 케이스(13)에 의해 벤트 부재(15)가 당겨져 벤트 부재(15)가 삽입된 부분의 실링 강도가 저하된다. 이에 따라, 벤트 부재(15)가 삽입된 부분의 밀봉 강도가 떨어지게 되면서 이 부분으로 벤트가 유도될 수 있다.
전극 리드(11)가 케이스(13) 외부로 노출되는 쪽에서는 전극 조립체(12)와 전극 리드(11) 사이에 일정부분 빈 공간이 형성되게 된다. 전지 내부에서 가스가 발생하는 경우, 이러한 빈 공간으로 가스가 집중될 수 있다. 상기 케이스(13) 외부로 돌출된 벤트 부재(15)의 일단이 수납부(13a) 내에서 전극 조립체(12)가 위치하지 않는 부분과 대응하는 케이스 외측(16)에 접합되는 경우, 수납부(13a) 내에서 전극 조립체(12)가 위치하지 않는 부분과 대응하는 케이스 외측(16)이 특히 더 많이 스웰링됨에 따라 스웰링된 케이스 외측(16)에 의해 벤트 부재(15)가 당겨져 벤트 부재(15)가 삽입된 부분의 실링 강도가 더욱 저하될 수 있다. 이에 따라 벤트가 유도되기 더욱 용이할 수 있다.
도 1 및 도 2를 참조하면, 벤트 부재(15)의 타단이 실링부(13b)에 위치할 수 있다.
도 1 및 도 2를 참조하면, 상기 벤트 부재(15)가 상기 전극 리드(11)가 외부로 노출되는 측의 실링부(13b)에 위치할 수 있다. 이 때, 벤트 부재(15)가 전극 리드들(11)의 사이를 제외한 전극 리드(11) 옆의 실링부(13b)에 위치할 수 있다. 구체적으로, 상기 벤트 부재(15)가 상기 전극 리드(11)가 외부로 노출되는 측의 코너 측 실링부(13b)에 위치할 수 있다.
상기 벤트 부재(15)가 전극 리드들(11)의 사이를 제외한 전극 리드(11) 옆의 실링부(13b)에 위치하는 경우, 전극 리드(11)의 사이드 부분을 향하는 방향으로 벤트되는 가스의 양을 최소화할 수 있어 전지의 안전성을 더욱 향상시킬 수 있다. 전극 리드(11)는 과충전이나 내부단락 등의 이상 상황에서 온도가 빠르게 상승하는 부품이다. 따라서, 벤트되는 가스와 전극 리드(11)의 직접적 접촉을 최소화하면 안전성이 개선될 수 있다.
상기 벤트 부재(15)와 케이스(13)는 열융착을 통해 중첩될 수 있다. 다른 예에서, 상기 벤트 부재(15)와 케이스(13)는 글루 등의 접착제를 통해 중첩될 수 있다. 또 다른 예에서, 상기 벤트 부재(15)와 케이스(13)는 클립 등을 통해 물리적으로 상호 결합될 수 있다. 또 다른 예에서, 케이스(13)를 구성하는 필름, 예컨대, 실란트 수지 내에 벤트 부재(15)의 적어도 일부가 매립(embedding)될 수 있다.
본 발명의 일 실시양태에서, 상기 벤트 부재(15)가 상기 실란트 수지보다 융점이 낮을 수 있다. 상기 벤트 부재(15)가 실란트 수지보다 융점이 낮은 경우, 고온에서 벤트 부재가 실란트 수지보다 더 빨리 용융될 수 있다. 벤트 부재(15)가 삽입된 부분의 실링 강도가 실란트 수지를 포함하는 케이스 부분의 실링 강도보다 더 저하됨에 따라 벤트 특성이 구현되기 더욱 용이할 수 있다.
본 발명의 일 실시양태에서, 상기 벤트 부재(15)가 100℃ 내지 130℃, 또는 105℃ 내지 125℃, 또는 110℃ 내지 120℃의 융점을 가지는 것일 수 있다. 상기 벤트 부재(15)의 융점이 전술한 범위를 만족하는 경우, 고온, 예컨대 100℃ 이상에서 벤트 부재(15)가 삽입된 케이스(13) 부분의 실링 강도가 저하되어 벤트 특성이 구현되기 더욱 용이할 수 있다.
상기 벤트 부재(15)의 융점은 시차 주사 열량계(Differential scanning calorimeter; DSC)를 이용하여 측정할 수 있다. 예컨대, 시료의 온도를 30℃로부터 10℃/min으로 280℃까지 증가시킨 후, 280℃에서 10분 간 유지하고, 10℃/min으로 30℃까지 냉각한 후, 30℃에서 10분간 유지한다. 이후, 시료의 온도를 30℃로부터 10℃/min으로 280℃까지 증가시킨 후 280℃에서 10분간 온도를 유지하여 융점을 측정할 수 있다.
본 발명의 일 실시양태에서, 상기 벤트 부재(15)는 100℃ 내지 120℃에서 벤팅될 수 있어 수납부에서 전지 외부로 가스를 배출 또는 배기할 수 있다. 특히, 상기 벤트 부재(15)는 100℃ 내지 120℃에서 1.5 atm 이상의 압력에서 벤팅될 수 있다. 상기 벤트 부재(15)가 전술한 온도 범위 및/또는 전술한 압력 조건에서 벤팅됨에 따라, 전지가 정상 작동할 때에는 전지의 밀봉이 가능하면서 전지의 이상 작동 시에만 가스 배출을 유도할 수 있다.
본 발명의 일 실시양태에서, 상기 벤트 부재(15)의 100℃ 이상에서의 최대 실링 강도가 6 kgf/15 mm 미만, 또는 5 kgf/15 mm 미만, 또는 4.5 kgf/15 mm 미만일 수 있다. 본 발명의 또 다른 실시양태에서, 상기 벤트 부재(15)의 100℃ 내지 120℃에서의 최대 실링 강도가 6 kgf/15 mm 미만, 또는 5 kgf/15 mm 미만, 또는 4.5 kgf/15 mm 미만일 수 있다. 본 발명의 또 다른 실시양태에서, 상기 벤트 부재(15)의 120℃ 이상에서의 최대 실링 강도가 3 kgf/15 mm 미만, 또는 2 kgf/15 mm 미만, 또는 1 kgf/15 mm 미만 또는 0.5 kgf/15 mm 미만일 수 있다. 상기 벤트 부재(15)가 전술한 온도 범위에서 전술한 실링 강도를 만족하는 경우, 고온, 예컨대 100℃ 이상에서 벤트 부재(15)가 삽입된 케이스(13) 부분의 실링 강도가 저하되어 벤트 특성이 구현되기 더욱 용이할 수 있다.
또한, 본 발명의 일 실시양태에서, 상기 벤트 부재(15)의 상온 내지 60℃에서의 최대 실링 강도가 6 kgf/15 mm 이상, 또는 8 kgf/15 mm 이상, 또는 10 kgf/15 mm 이상일 수 있다. 상기 벤트 부재(15)가 전술한 온도 범위에서 전술한 실링 강도를 만족하는 경우, 벤트 부재(15)가 삽입되어 있더라도, 전지의 정상 작동 시에 벤트 부재(15)가 삽입된 케이스(13) 부분이 우수한 실링 강도를 가져 전지의 밀봉성을 확보하기 용이할 수 있다.
본 발명의 일 실시양태에서, 상기 벤트 부재(15)의 100℃ 이상에서의 최대 실링 강도가 6 kgf/15 mm 미만이고, 상기 벤트 부재(15)의 상온 내지 60℃에서의 최대 실링 강도가 6 kgf/15 mm 이상일 수 있다. 상기 벤트 부재(15)가 전술한 실링 강도를 만족하는 경우, 고온, 예컨대 100℃ 이상에서 벤트 부재(15)가 삽입된 케이스(13) 부분의 실링 강도가 저하되어 벤트 특성이 구현되기 용이하면서, 전지의 정상적 작동 시에는 우수한 실링 강도를 가져 전지의 밀봉성을 확보하기 용이할 수 있다.
본 발명의 일 실시양태에서, 상기 벤트 부재(15)의 100℃ 이상에서의 평균 실링 강도가 4.5 kgf/15 mm 미만, 또는 3 kgf/15 mm 미만일 수 있다. 본 발명의 또 다른 실시양태에서, 상기 벤트 부재(15)의 100℃ 내지 120℃에서의 평균 실링 강도가 4.5 kgf/15 mm 미만, 또는 3 kgf/15 mm 미만일 수 있다. 본 발명의 또 다른 실시양태에서, 상기 벤트 부재(15)의 120℃ 이상에서의 평균 실링 강도가 2 kgf/15 mm 미만, 또는 1 kgf/15 mm 미만, 또는 0.5 kgf/15 mm 미만일 수 있다. 상기 벤트 부재(15)가 전술한 온도 범위에서 전술한 실링 강도를 만족하는 경우, 고온, 예컨대 100℃ 이상에서 벤트 부재(15)가 삽입된 케이스(13) 부분의 실링 강도가 저하되어 벤트 특성이 구현되기 더욱 용이할 수 있다.
본 발명의 일 실시양태에서, 상기 벤트 부재(15)의 상온 내지 60℃에서의 평균 실링 강도가 4.5 kgf/15 mm 이상, 또는 5 kgf/15 mm 이상, 또는 6 kgf/15 mm 이상, 또는 7 kgf/15 mm 이상일 수 있다. 상기 벤트 부재(15)가 전술한 온도 범위에서 전술한 실링 강도를 만족하는 경우, 벤트 부재(15)가 삽입되어 있더라도, 전지의 정상 작동 시에 벤트 부재(15)가 삽입된 케이스(13) 부분이 우수한 실링 강도를 가져 전지의 밀봉성을 확보하기 용이할 수 있다.
본 발명의 일 실시양태에서, 상기 벤트 부재(15)가 100℃ 이상에서의 평균 실링 강도가 4.5 kgf/15 mm 미만이고, 상기 벤트 부재(15)의 상온 내지 60℃에서의 평균 실링 강도가 4.5 kgf/15 mm 이상일 수 있다. 상기 벤트 부재(15)가 전술한 온도 범위를 가지는 경우, 고온, 예컨대 100℃ 이상에서 벤트 부재(15)가 삽입된 케이스(13) 부분의 실링 강도가 저하되어 벤트 특성이 구현되기 용이할 수 있다. 또한, 케이스(13)가 전지의 정상 작동 시에 우수한 실링 강도를 가져 전지의 밀봉성을 확보하기 용이할 수 있다.
온도에 따른 벤트 부재(15)의 실링 강도는 벤트 부재(15)가 삽입된 부분의 케이스(13)를 폭 15mm, 길이 5cm로 재단한 뒤, 양 끝을 180°로 벌려 UTM 지그에 물린 뒤, 5 mm/min의 속도로 인장 테스트를 실시하여 측정할 수 있다.
이 때, 최대 실링 강도는 케이스(13)가 파단될 때의 최대값을 의미하며, 평균 실링 강도는 최대 실링 강도가 4.5 kgf/15 mm 이상인 경우에는 4.5 kgf/15 mm에서 케이스(13)가 8 mm 만큼 연신되었을 때의 평균값을 의미하고, 최대 실링 강도가 4.5 kgf/15 mm 미만인 경우에는 최대 실링 강도에서 케이스(13)가 8 mm 만큼 연신되었을 때의 평균값을 의미한다.
본 발명의 일 실시양태에서, 상기 벤트 부재(15)는 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌을 포함할 수 있다. 상기 벤트 부재(15)가 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌을 포함함에 따라, 정상 온도 범위, 예컨대 상온에서 60℃에서는 케이스(13)의 밀봉성이 우수하면서, 고온, 예컨대 100℃ 이상에서 벤트 부재(15)가 삽입된 케이스의 실링 강도가 저하되어 벤팅을 실현하거나 유발할 수 있다.
본 발명의 일 실시양태에서, 상기 벤트 부재(15)가 탄소수 6 내지 8의 코모노머를 가지는 선형 저밀도 폴리에틸렌을 포함할 수 있다.
본 발명의 일 실시양태에서, 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌이 메탈로센 촉매의 존재 하에 중합된 것일 수 있다. 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌이 메탈로센 촉매의 존재 하에 중합된 것인 경우, 지글러-나타 촉매의 존재 하에 중합된 경우보다 실링 강도 및 물성 측면에서 더욱 유리할 수 있다.
본 발명의 일 실시양태에서, 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌에서의 상기 탄소수 6 이상의 코모노머의 함량이 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌 100 중량% 대비 15 중량% 이하, 또는 12 중량% 이하, 또는 11.8 중량% 이하, 또는 10 중량% 이하, 또는 9 중량% 이하, 또는 8 중량% 이하, 또는 7.6 중량% 이하일 수 있다. 동시에, 상기 탄소수 6 이상의 코모노머의 함량이 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌 100 중량% 대비 5 중량% 이상, 또는 7.6 중량% 이상, 또는 8 중량% 이상, 또는 9.0 중량% 이상, 또는 10 중량% 이상, 또는 11.8 중량% 이상, 또는 12 중량% 이상일 수 있다. 탄소수 6 이상의 코모노머의 함량이 전술한 범위를 만족하는 경우, 분자 간 패킹 밀도가 감소하여 전지의 정상 작동 시에 실링 강도가 낮아지는 문제를 방지하기 용이할 수 있다.
상기 탄소수 6 이상의 코모노머의 함량은 H-NMR로 측정할 수 있다. 예컨대, 시료 약 10 mg을 트리클로로에틸렌 용매 약 0.6 mL에 히터 건(heat gun)을 사용하여 완전히 녹인 후, NMR 튜브에 샘플링하고, 1H-NMR을 이용하여 측정할 수 있다.
본 발명의 일 실시양태에서, 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 중량평균분자량이 10만 g/mol 내지 40만 g/mol, 또는 20만 g/mol 내지 35만 g/mol, 또는 23만 g/mol 내지 30만 g/mol일 수 있다. 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 중량평균분자량이 전술한 범위를 만족하는 경우, 전지의 정상 작동 시에 실링 강도가 더욱 향상될 수 있다.
본 발명의 일 실시양태에서, 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 다분산성 지수(Poly Dispersity Index; PDI)가 4 이하, 또는 3.8 이하, 또는 3.796 이하, 또는 3.5 이하, 또는 3.023 이하, 또는 3 이하, 또는 2.7 이하, 또는 2.674 이하일 수 있다. 또한, 다분산성 지수(Poly Dispersity Index; PDI)가 1.0 이상일 수 있다. 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 다분산성 지수가 전술한 범위를 만족하는 경우, 분자량 분포가 좁아 전지의 정상 작동 시에 실링 강도 및 물성이 더욱 우수할 수 있다.
탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 중량평균분자량 및 다분산성 지수는 겔 투과 크로마토그래피(GPC: gel permeation chromatography)로 하기의 조건에서 측정한 것일 수 있다.
- 컬럼: Tosoh社 HLC-8321 GPC/HT
- 용매: TCB(Trichlorobenzene) + 0.04% BHT(after drying with 0.1% CaCl2)
- 유속: 1.0 ml/min
- 시료농도: 1.5 mg/ml
- 주입량: 300 ㎕
- 컬럼온도: 160℃
- Detector: RI detector
- Standard: Polystyrene (3차 함수로 보정)
본 발명의 일 실시양태에서, 상기 실란트 수지의 결정화 온도와 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 결정화 온도가 비슷할 수 있다. 예컨대, 상기 실란트 수지의 결정화 온도와 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 결정화 온도의 차이가 10℃ 이하, 또는 5℃ 이하일 수 있다. 또한, 상기 실란트 수지의 결정화 온도와 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 결정화 온도의 차이가 0.1℃ 이상일 수 있다. 상기 실란트 수지의 결정화 온도와 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 결정화 온도의 차이가 전술한 범위를 만족하는 경우, 상기 실란트 수지와 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 전지의 정상 작동 시의 융착 특성이 더욱 우수할 수 있다.
본 발명의 일 실시양태에서, 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 결정화 온도가 90℃ 내지 115℃, 또는 95℃ 내지 110℃, 또는 100℃ 내지 110℃, 또는 105℃ 내지 110℃일 수 있다. 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 결정화 온도가 전술한 범위를 만족하는 경우, 상기 실란트 수지와 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 융착 특성이 더욱 우수할 수 있다.
본 발명의 일 실시양태에서, 상기 실란트 수지의 결정화 온도와 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 결정화 온도의 차이가 10℃ 이하이고, 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 결정화 온도가 90℃ 내지 115℃일 수 있다.
상기 결정화 온도는 시차 주사 열량계(Differential scanning calorimeter; DSC)를 이용하여 측정할 수 있다. 예컨대, 시료의 온도를 30℃로부터 10℃/min으로 280℃까지 증가시킨 후, 280℃에서 10분 간 유지하고, 10℃/min으로 30℃까지 냉각한 후, 30℃에서 10분간 유지할 수 있다. 이후, 시료의 온도를 30℃로부터 10℃/min으로 280℃까지 증가시킨 후 온도를 280℃에서 10분간 유지하여 결정화 온도를 측정할 수 있다.
본 발명의 일 실시양태에서, 상기 벤트 부재(15)는 가스가 벤트 영역으로 향하기 쉽도록 다양한 형상을 가질 수 있다. 예컨대, 벤트 부재(15)가 필름 형상을 가질 수 있다.
상기 벤트 부재(15)는 기 설정된 크기의 소정의 두께를 갖도록 형성될 수 있다. 아울러, 상기 벤트 부재(15)는 설계에 따라, 삽입 길이를 다르게 하거나 또는 벤팅 압력 및 위치 제어가 가능할 수 있게 상기 케이스(13)에 삽입될 수 있다. 여기서, 상기 벤트 부재(15)의 삽입 길이는 전극 리드(11)의 돌출 방향을 기준으로 벤트 부재(15)의 일단과 타단 사이의 거리의 최대값을 의미한다.
본 발명의 일 실시양태에서, 상기 벤트 부재(15)는 보다 더 원활한 안착을 위해 접착층을 더 포함할 수 있다.
본 발명의 일 실시양태에서, 상기 이차전지는 원통형, 각형, 또는 파우치형 이차전지일 수 있다. 그 중에서도, 상기 이차전지가 파우치형 이차전지일 수 있다.
이하, 본 발명의 이해를 돕기 위하여 실시예를 들어 상세하게 설명하기로 한다. 그러나, 본 발명에 따른 실시예들은 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 하기 실시예에 한정되는 것으로 해석되어서는 안 된다. 본 발명의 실시예들은 당업계에서 평균적인 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해 제공되는 것이다.

Claims (22)

  1. 전극 조립체; 상기 전극 조립체를 수납하는 케이스; 및 벤트 부재를 포함하고,
    상기 벤트 부재가 상기 케이스 외부로 돌출되고, 상기 케이스 외부로 돌출된 벤트 부재의 일단이 상기 케이스 외측에 접합되는 것을 특징으로 하는 이차전지.
  2. 제1항에 있어서,
    상기 벤트 부재가 케이스 외부로 돌출된 부분이 절곡되어 상기 케이스 외부로 돌출된 벤트 부재의 일단이 상기 케이스 외측에 접합되는 것을 특징으로 하는 이차전지.
  3. 제1항에 있어서,
    상기 케이스는 상기 전극 조립체를 수납하는 수납부 및 실란트 수지를 포함하고 상기 전극 조립체를 밀봉하기 위해 형성된 실링부를 구비하고,
    상기 케이스 외부로 돌출된 벤트 부재의 일단이 상기 수납부 내에서 전극 조립체가 위치하지 않는 부분과 대응하는 케이스 외측에 접합되는 것을 특징으로 하는 이차전지.
  4. 제3항에 있어서,
    상기 벤트 부재의 타단이 상기 실링부에 위치하는 것을 특징으로 하는 이차전지.
  5. 제4항에 있어서,
    상기 전극 조립체에 전극 리드가 부착되어 있고,
    상기 벤트 부재의 타단이 상기 전극 리드가 외부로 노출되는 측의 실링부에 위치하는 것을 특징으로 하는 이차전지.
  6. 제4항에 있어서,
    상기 전극 조립체에 전극 리드가 부착되어 있고,
    상기 벤트 부재의 타단이 상기 전극 리드가 외부로 노출되는 측의 코너 측 실링부에 위치하는 것을 특징으로 하는 이차전지.
  7. 제3항에 있어서,
    상기 벤트 부재의 융점이 상기 실란트 수지의 융점보다 낮은 것을 특징으로 하는 이차전지.
  8. 제1항에 있어서,
    상기 벤트 부재가 100℃ 내지 120℃에서 벤팅되는 것을 특징으로 하는 이차전지.
  9. 제8항에 있어서,
    상기 벤트 부재가 1.5 atm 이상의 압력에서 벤팅되는 것을 특징으로 하는 이차전지.
  10. 제1항에 있어서,
    상기 벤트 부재의 100℃ 이상에서의 최대 실링 강도가 6 kgf/15 mm 미만인 것을 특징으로 하는 이차전지.
  11. 제1항에 있어서,
    상기 벤트 부재의 100℃ 이상에서의 평균 실링 강도가 4.5 kgf/15 mm 미만인 것을 특징으로 하는 이차전지.
  12. 제1항에 있어서,
    상기 벤트 부재의 상온 내지 60℃에서의 최대 실링 강도가 6 kgf/15 mm 이상인 것을 특징으로 하는 이차전지.
  13. 제1항에 있어서,
    상기 벤트 부재의 상온 내지 60℃에서의 평균 실링 강도가 4.5 kgf/15 mm 이상인 것을 특징으로 하는 이차전지.
  14. 제1항에 있어서,
    상기 벤트 부재가 탄소수 6 이상의 코모노머(comonomer)를 가지는 선형 저밀도 폴리에틸렌을 포함하는 것을 특징으로 하는 이차전지.
  15. 제14항에 있어서,
    상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌이 메탈로센 촉매의 존재 하에 중합된 것을 특징으로 하는 이차전지.
  16. 제14항에 있어서,
    상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌에서 상기 탄소수 6 이상의 코모노머의 함량이 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌 100 중량% 대비 15 중량% 이하인 것을 특징으로 하는 이차전지.
  17. 제14항에 있어서,
    상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 다분산성 지수(Poly Dispersity Index; PDI)가 4 이하인 것을 특징으로 하는 이차전지.
  18. 제14항에 있어서,
    상기 케이스는 실란트 수지를 포함하고 상기 전극 조립체를 밀봉하기 위해 형성된 실링부를 구비하고,
    상기 실란트 수지의 결정화 온도와 상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 결정화 온도의 차이가 10℃ 이하인 것을 특징으로 하는 이차전지.
  19. 제18항에 있어서,
    상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 결정화 온도가 90℃ 내지 115℃인 것을 특징으로 하는 이차전지.
  20. 제14항에 있어서,
    상기 탄소수 6 이상의 코모노머를 가지는 선형 저밀도 폴리에틸렌의 중량평균분자량이 10만 g/mol 내지 40만 g/mol인 것을 특징으로 하는 이차전지.
  21. 제1항에 있어서,
    상기 벤트 부재가 100℃ 내지 130℃의 융점을 가지는 것을 특징으로 하는 이차전지.
  22. 제1항에 있어서,
    상기 이차전지는 파우치형 이차전지인 것을 특징으로 하는 이차전지.
PCT/KR2022/005502 2021-04-15 2022-04-15 이차전지 WO2022220655A1 (ko)