WO2022205031A1 - Matériau composite silicium-oxygène-carbone, son procédé de préparation et application associée - Google Patents
Matériau composite silicium-oxygène-carbone, son procédé de préparation et application associée Download PDFInfo
- Publication number
- WO2022205031A1 WO2022205031A1 PCT/CN2021/084273 CN2021084273W WO2022205031A1 WO 2022205031 A1 WO2022205031 A1 WO 2022205031A1 CN 2021084273 W CN2021084273 W CN 2021084273W WO 2022205031 A1 WO2022205031 A1 WO 2022205031A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- silicon
- carbon
- composite material
- negative electrode
- layer
- Prior art date
Abstract
La présente invention concerne un matériau composite silicium-oxygène-carbone, un procédé de préparation de celui-ci et une application associée. Le matériau composite silicium-oxygène-carbone comprend un matériau matriciel, qui comporte un matériau à structure tridimensionnelle et une couche de SiOC sur la surface du matériau à structure tridimensionnelle, la couche de SiOC contenant Si, O et C ; et une couche de carbone sur la surface du matériau matriciel. Le matériau composite silicium-oxygène-carbone de la présente invention présente des caractéristiques telles qu'une capacité élevée et de bonnes conductivités électrique et ionique, et permet d'améliorer efficacement les performances du cycle et d'autres qualités d'un dispositif électrochimique.
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN202180004690.6A CN114175309A (zh) | 2021-03-31 | 2021-03-31 | 硅氧碳复合材料及其制备方法和应用 |
PCT/CN2021/084273 WO2022205031A1 (fr) | 2021-03-31 | 2021-03-31 | Matériau composite silicium-oxygène-carbone, son procédé de préparation et application associée |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/CN2021/084273 WO2022205031A1 (fr) | 2021-03-31 | 2021-03-31 | Matériau composite silicium-oxygène-carbone, son procédé de préparation et application associée |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2022205031A1 true WO2022205031A1 (fr) | 2022-10-06 |
Family
ID=80489990
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/CN2021/084273 WO2022205031A1 (fr) | 2021-03-31 | 2021-03-31 | Matériau composite silicium-oxygène-carbone, son procédé de préparation et application associée |
Country Status (2)
Country | Link |
---|---|
CN (1) | CN114175309A (fr) |
WO (1) | WO2022205031A1 (fr) |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102214817A (zh) * | 2010-04-09 | 2011-10-12 | 清华大学 | 一种碳/硅/碳纳米复合结构负极材料及其制备方法 |
CN104412423A (zh) * | 2012-06-27 | 2015-03-11 | 捷恩智株式会社 | 二次电池用负极活性物质及其制造方法、使用其的负极以及锂离子电池 |
US20170062804A1 (en) * | 2015-08-28 | 2017-03-02 | Samsung Electronics Co., Ltd. | Composite, method of preparing the same, electrode including the composite, and lithium battery including the electrode |
CN107768607A (zh) * | 2016-08-15 | 2018-03-06 | 福建新峰二维材料科技有限公司 | 一种锂离子电池负极材料的制备方法 |
WO2020016280A1 (fr) * | 2018-07-17 | 2020-01-23 | Commissariat A L'energie Atomique Et Aux Energies Alternatives | Matériau d'électrode particulaire de sioc sphérique |
-
2021
- 2021-03-31 WO PCT/CN2021/084273 patent/WO2022205031A1/fr active Application Filing
- 2021-03-31 CN CN202180004690.6A patent/CN114175309A/zh active Pending
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102214817A (zh) * | 2010-04-09 | 2011-10-12 | 清华大学 | 一种碳/硅/碳纳米复合结构负极材料及其制备方法 |
CN104412423A (zh) * | 2012-06-27 | 2015-03-11 | 捷恩智株式会社 | 二次电池用负极活性物质及其制造方法、使用其的负极以及锂离子电池 |
US20170062804A1 (en) * | 2015-08-28 | 2017-03-02 | Samsung Electronics Co., Ltd. | Composite, method of preparing the same, electrode including the composite, and lithium battery including the electrode |
CN107768607A (zh) * | 2016-08-15 | 2018-03-06 | 福建新峰二维材料科技有限公司 | 一种锂离子电池负极材料的制备方法 |
WO2020016280A1 (fr) * | 2018-07-17 | 2020-01-23 | Commissariat A L'energie Atomique Et Aux Energies Alternatives | Matériau d'électrode particulaire de sioc sphérique |
Also Published As
Publication number | Publication date |
---|---|
CN114175309A (zh) | 2022-03-11 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN111403693B (zh) | 负极活性材料和使用其的负极极片、电化学装置和电子装置 | |
WO2022193123A1 (fr) | Matériau d'électrode négative et son procédé de préparation, dispositif électrochimique et dispositif électronique | |
WO2022205032A1 (fr) | Pièce polaire négative, dispositif électrochimique et dispositif électronique | |
WO2022193286A1 (fr) | Matériau d'électrode négative et son procédé de préparation, dispositif électrochimique et dispositif électronique | |
WO2021189339A1 (fr) | Plaque d'électrode négative, dispositif électrochimique et dispositif électronique | |
CN114982009B (zh) | 负极材料、负极极片及包含其的电化学装置及电子装置 | |
WO2023082245A1 (fr) | Électrode et son procédé de fabrication, dispositif électrochimique et dispositif électronique | |
WO2023082247A1 (fr) | Électrode et son procédé de préparation, dispositif électrochimique et dispositif électronique | |
WO2022140962A1 (fr) | Matériau d'électrode négative, dispositif électrochimique et appareil électronique | |
US20230343937A1 (en) | Silicon-carbon composite particle, negative electrode active material, and negative electrode, electrochemical apparatus, and electronic apparatus containing same | |
CN113196524B (zh) | 负极材料、负极极片、电化学装置和电子装置 | |
CN113066970A (zh) | 硅碳负极材料、电化学装置和电子装置 | |
Lou et al. | Graphite-like structure of disordered polynaphthalene hard carbon anode derived from the carbonization of perylene-3, 4, 9, 10-tetracarboxylic dianhydride for fast-charging lithium-ion batteries | |
WO2022204979A1 (fr) | Matériau composite à base de silicium, son procédé de préparation et application correspondante | |
US20230343943A1 (en) | Negative electrode material, negative electrode plate, and electrochemical apparatus and electronic apparatus containing such negative electrode plate | |
WO2022205031A1 (fr) | Matériau composite silicium-oxygène-carbone, son procédé de préparation et application associée | |
KR20220148303A (ko) | 음극 복합재 및 이의 응용 | |
WO2022140974A1 (fr) | Matériau composite de sioc, son procédé de préparation et ses applications | |
WO2023137708A1 (fr) | Dispositif electrochimique | |
WO2024050799A1 (fr) | Matériau actif d'électrode négative, son procédé de préparation, batterie secondaire, module de batterie, bloc-batterie et appareil électrique | |
WO2022205151A1 (fr) | Matériau actif d'électrode négative, appareil électrochimique et appareil électronique | |
WO2023082246A1 (fr) | Électrode et son procédé de préparation, dispositif électrochimique et dispositif électronique | |
WO2021217331A1 (fr) | Matériau d'électrode négative, et plaque d'électrode négative, dispositif électrochimique et dispositif électronique comprenant le matériau d'électrode négative | |
WO2023184125A1 (fr) | Dispositif électrochimique et appareil électronique | |
WO2023082248A1 (fr) | Électrode et son procédé de fabrication, dispositif électrochimique et dispositif électronique |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 21933710 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 21933710 Country of ref document: EP Kind code of ref document: A1 |