WO2022183797A1 - Carbon fiber fish bait rough blank and manufacturing method therefor - Google Patents
Carbon fiber fish bait rough blank and manufacturing method therefor Download PDFInfo
- Publication number
- WO2022183797A1 WO2022183797A1 PCT/CN2021/134702 CN2021134702W WO2022183797A1 WO 2022183797 A1 WO2022183797 A1 WO 2022183797A1 CN 2021134702 W CN2021134702 W CN 2021134702W WO 2022183797 A1 WO2022183797 A1 WO 2022183797A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- carbon fiber
- cloth
- rough
- mold
- mandrel
- Prior art date
Abstract
The present invention relates to a carbon fiber fish bait rough blank and a manufacturing method therefor. Said method comprises the following steps: step 1, adhering a carbon fiber cloth to the cavity of a mold; step 2, heating the carbon fiber cloth in the mold; step 3, blow molding; step 4, taking out the molded semi-finished rough blank, the semi-finished rough blank being divided into two halves, and gluing positions being reserved on the two halves; and step 5, installing accessories in the semi-finished rough blank, and gluing the two halves of a product together, so as to obtain a rough blank. The method of the present invention increases the strength of the rough blank by means of blow molding, and a vacuum contraction device and a mold are relatively cheap and easy to use.
Description
本发明涉及一种碳纤维鱼饵粗胚及其制作方法。The invention relates to a rough embryo of carbon fiber fishing lure and a preparation method thereof.
浮标最重要的是传达鱼讯,也就是鱼索饵的讯息。钓手如能正确且快速的掌握鱼讯那中鱼的数量就会比他人多。The most important thing for the buoy is to convey the message of the fish, that is, the message of the fish baiting. If the angler can grasp the fish information correctly and quickly, the number of fish will be more than others.
现有技术中的各种材质的浮标都有，最近也有使用碳纤维浮标。但是现有碳纤维浮标材质以下技术缺陷：(1)现有碳纤维浮标无法实现轻量化与高强度的最佳平衡；(2)现有碳纤维浮标制作需要高温固化，对设备要求更高并且生产效率不高。There are buoys of various materials in the prior art, and carbon fiber buoys are also used recently. However, the existing carbon fiber buoy materials have the following technical defects: (1) the existing carbon fiber buoy cannot achieve the best balance between light weight and high strength; (2) the existing carbon fiber buoy production requires high temperature curing, which requires higher equipment and low production efficiency. high.
发明内容SUMMARY OF THE INVENTION
本发明设计了一种碳纤维鱼饵粗胚及其制作方法，其解决的技术问题是：(1)现有碳纤维浮标无法实现轻量化与高强度的最佳平衡；(2)现有碳纤维浮标制作需要高温固化，对设备要求更高并且生产效率不高。The present invention designs a carbon fiber bait rough embryo and a manufacturing method thereof. The technical problems solved by the invention are as follows: (1) the existing carbon fiber buoy cannot achieve the optimal balance of light weight and high strength; (2) the existing carbon fiber buoy needs to be manufactured High temperature curing requires higher equipment and lower production efficiency.
为了解决上述存在的技术问题，本发明采用了以下方案：In order to solve the above-mentioned technical problem, the present invention adopts the following scheme:
一种碳纤维鱼饵粗胚的制作方法，包括以下步骤：步骤1、将碳纤维布贴在模具的型腔内；步骤2、将模具内的碳纤维布加热；步骤3、吹气成型；步骤4、成型好的粗胚半成品取出，粗胚半成品分为两半，两半预留胶合位；步骤5、在粗胚半成品中安装配件后，用胶将两半产品胶合在一起，得到粗胚。A method for producing carbon fiber bait rough embryos, comprising the following steps: step 1, sticking carbon fiber cloth in a cavity of a mold; step 2, heating the carbon fiber cloth in the mold; step 3, blow molding; step 4, molding The good rough embryo semi-finished product is taken out. The rough embryo semi-finished product is divided into two halves, and the two halves are reserved for gluing. Step 5. After installing the accessories in the rough embryo semi-finished product, glue the two halves together with glue to obtain the rough embryo.
优选地，步骤2中模具在真空热压罐内使得碳纤维布在真空状态加热收缩成型。Preferably, in step 2, the mold is in a vacuum autoclave to heat and shrink the carbon fiber cloth in a vacuum state.
优选地，步骤2中的加热温度为150℃，并且持续15分钟以上。Preferably, the heating temperature in step 2 is 150° C. and lasts for more than 15 minutes.
优选地，步骤3是将碳纤维布包在芯模上，取出芯模或不取出芯模，向碳纤维布插入气袋，吹气使得加热后的碳纤维布成型，得到粗胚半成品。Preferably, step 3 is to wrap the carbon fiber cloth on the mandrel, take out the mandrel or not, insert an air bag into the carbon fiber cloth, and blow air to make the heated carbon fiber cloth to be formed to obtain a rough semi-finished product.
优选地，不取出芯模时，所述芯模为固定式芯模或EPS类收缩芯模。Preferably, when the mandrel is not taken out, the mandrel is a fixed mandrel or an EPS-type shrinking mandrel.
优选地，步骤5中的配件为卡环或/和响珠。Preferably, the accessories in step 5 are snap rings or/and snap beads.
一种碳纤维鱼饵粗胚的制作方法，包括以下步骤：A method for producing carbon fiber bait rough embryos, comprising the following steps:
步骤1、模具内壁喷透明胶衣；Step 1. Spray transparent gel coat on the inner wall of the mold;
步骤2、将干燥的碳纤布贴于模具内表面的透明胶衣上；Step 2. Paste the dry carbon fiber cloth on the transparent gel coat on the inner surface of the mold;
步骤3、在碳纤布上铺导流网、脱模布；Step 3. Lay the guide net and the release cloth on the carbon fiber cloth;
步骤4、套真空导流袋；Step 4. Set the vacuum diversion bag;
步骤5、真空导流袋抽真空后，导入树脂固化；Step 5. After the vacuum diversion bag is evacuated, the resin is introduced to cure;
步骤6、得到粗胚。Step 6. Obtain crude embryos.
优选地，步骤6中可以为常温固化或加热固化。Preferably, the step 6 may be room temperature curing or heating curing.
优选地，所述碳纤布为：1k、1.5K、3K、12K等各类碳纤维编织布，0-900UD布，玻纤及玻纤电镀布、编织布、纺沦、涤沦、克维拉纤维编织布，各类纤维类混编布、编织布、交叉布，以及各类含浸树脂的预浸布、编织布和未含浸树脂的干布。Preferably, the carbon fiber cloth is: 1k, 1.5K, 3K, 12K and other types of carbon fiber woven cloth, 0-900UD cloth, glass fiber and glass fiber electroplating cloth, woven cloth, spinning, polyester, Kevlar fiber Woven fabrics, various types of fiber blended fabrics, woven fabrics, crossed fabrics, and various types of resin-impregnated pre-impregnated fabrics, woven fabrics and non-resin-impregnated dry fabrics.
一种碳纤维鱼饵粗胚，其特征在于：使用上述任何一项制备方法制得。A carbon fiber bait rough embryo is characterized in that: it is prepared by any one of the above-mentioned preparation methods.
该碳纤维鱼饵粗胚及其制作方法具有以下有益效果：The carbon fiber bait rough embryo and the preparation method thereof have the following beneficial effects:
(1)本发明方法通过吹气成型可以增加粗胚的强度，并且真空收缩设备与模具相对便宜且更易操作。(1) The method of the present invention can increase the strength of the rough embryo through blow molding, and the vacuum shrinking equipment and the mold are relatively cheap and easier to operate.
(2)本发明方法真空导流为低温树脂，可常温固化，设备要求不高，效率会更高。(2) The vacuum diversion method of the present invention is a low-temperature resin, which can be cured at room temperature, and the equipment requirements are not high, and the efficiency will be higher.
(3)本发明制得鱼饵粗胚具有更加轻量化和强度更好的优点。(3) The rough embryo of the fishing bait prepared by the present invention has the advantages of lighter weight and better strength.
下面结合实施例，对本发明做进一步说明：Below in conjunction with embodiment, the present invention is further described:
实施例1：一种碳纤维鱼饵粗胚的制作方法，包括以下步骤：步骤1、将碳纤维布贴在模具的型腔内；步骤2、将模具内的碳纤维布加热；步骤3、吹气成型；步骤4、成型好的粗胚半成品取出，粗胚半成品分为两半，两半预留胶合位；步骤5、在粗胚半成品中安装配件后，用胶将两半产品胶合在一起，得到粗胚。Embodiment 1: a method for making a carbon fiber bait rough embryo, comprising the following steps: step 1, sticking carbon fiber cloth in the cavity of a mold; step 2, heating the carbon fiber cloth in the mold; step 3, blow molding; Step 4. Take out the formed rough embryo semi-finished product. The rough embryo semi-finished product is divided into two halves, and the two halves are reserved for gluing; embryo.
步骤2中模具在真空热压罐内使得碳纤维布在真空状态加热收缩成型。步骤2中的加热温度可以为150℃，并且持续15分钟以上。上述加热时间和温度可以进行调整。In step 2, the mold is in a vacuum autoclave to heat and shrink the carbon fiber cloth in a vacuum state. The heating temperature in step 2 may be 150° C. and last for more than 15 minutes. The above heating time and temperature can be adjusted.
步骤3是将碳纤维布包在芯模上，取出芯模或不取出芯模，向碳纤维布插入气袋，吹气使得加热后的碳纤维布成型，得到粗胚半成品。不取出芯模时，所述芯模为固定式芯模或EPS类收缩芯模。Step 3 is to wrap the carbon fiber cloth on the mandrel, take out the mandrel or not, insert an air bag into the carbon fiber cloth, blow air to make the heated carbon fiber cloth to be formed, and obtain a rough semi-finished product. When the mandrel is not taken out, the mandrel is a fixed mandrel or an EPS-type shrinking mandrel.
步骤5中的配件为卡环或/和响珠。The accessories in step 5 are snap rings or/and snap beads.
实施例2：一种碳纤维鱼饵粗胚的制作方法，包括以下步骤：步骤1、模具内壁喷透明胶衣；步骤2、将干燥的碳纤布贴于模具内表面的透明胶衣上；步骤3、在碳纤布上铺导流网、脱模布；步骤4、套真空导流袋；步骤5、真空导流袋抽真空后，导入树脂固化；步骤6、得到粗胚。Embodiment 2: a method for making a carbon fiber bait rough embryo, comprising the following steps: step 1, spraying a transparent gel coat on the inner wall of the mold; step 2, sticking the dry carbon fiber cloth on the transparent gel coat on the inner surface of the mold; step 3, A guide net and a mold release cloth are laid on the carbon fiber cloth; step 4, cover a vacuum guide bag; step 5, after the vacuum guide bag is evacuated, introduce resin to solidify; step 6, obtain a rough embryo.
步骤6中可以为常温固化或加热固化。具体来说，可以为常温1小时固化或加热到400℃，35分钟固化。In step 6, it can be curing at room temperature or curing by heating. Specifically, it can be cured at room temperature for 1 hour or heated to 400°C for 35 minutes.
所述碳纤布为：1k、1.5K、3K、12K等各类碳纤维编织布，0-900UD布，玻纤及玻纤电镀布、编织布、纺沦、涤沦、克维拉纤维编织布，各类纤维类混编布、编织布、交叉布，以及各类含浸树脂的预浸布、编织布和未含浸树脂的干布。The carbon fiber cloth is: 1k, 1.5K, 3K, 12K and other types of carbon fiber woven cloth, 0-900UD cloth, glass fiber and glass fiber electroplating cloth, woven cloth, woven cloth, polyester, Kevlar fiber woven cloth, Various types of fiber blended fabrics, woven fabrics, crossed fabrics, and various types of resin-impregnated pre-impregnated fabrics, woven fabrics and non-resin-impregnated dry fabrics.
上面结合实施例对本发明进行了示例性的描述，显然本发明的实现并不受上述方式的限制，只要 采用了本发明的方法构思和技术方案进行的各种改进，或未经改进将本发明的构思和技术方案直接应用于其它场合的，均在本发明的保护范围内。The present invention has been exemplarily described above in conjunction with the embodiments. Obviously, the implementation of the present invention is not limited by the above-mentioned methods, as long as various improvements made by the method concept and technical solutions of the present invention are adopted, or the present invention is not modified without improvement. It is within the protection scope of the present invention that the ideas and technical solutions of the invention are directly applied to other occasions.
Claims (10)
- 一种碳纤维鱼饵粗胚的制作方法，包括以下步骤：A method for producing carbon fiber bait rough embryos, comprising the following steps:步骤1、将碳纤维布贴在模具的型腔内；Step 1. Paste the carbon fiber cloth in the cavity of the mold;步骤2、将模具内的碳纤维布加热；Step 2. Heat the carbon fiber cloth in the mold;步骤3、吹气成型；Step 3, blow molding;步骤4、成型好的粗胚半成品取出，粗胚半成品分为两半，两半预留胶合位；Step 4. Take out the formed rough embryo semi-finished product, divide the rough embryo semi-finished product into two halves, and reserve a gluing position for the two halves;步骤5、在粗胚半成品中安装配件后，用胶将两半产品胶合在一起，得到粗胚。Step 5. After installing the accessories in the rough embryo semi-finished product, glue the two half products together with glue to obtain the rough embryo.
- 根据权利要求1所述的碳纤维鱼饵粗胚的制作方法，其特征在于：步骤2中模具在真空热压罐内使得碳纤维布在真空状态加热收缩成型。The method for producing carbon fiber bait rough embryos according to claim 1, wherein in step 2, the mold is in a vacuum autoclave to heat and shrink the carbon fiber cloth in a vacuum state.
- 根据权利要求2所述的碳纤维鱼饵粗胚的制作方法，其特征在于：步骤2中的加热温度为150℃，并且持续15分钟以上。The method for making rough embryos of carbon fiber fishing lures according to claim 2, wherein the heating temperature in step 2 is 150° C. and lasts for more than 15 minutes.
- 根据权利要求1所述的碳纤维鱼饵粗胚的制作方法，其特征在于：步骤3是将碳纤维布包在芯模上，取出芯模或不取出芯模，向碳纤维布插入气袋，吹气使得加热后的碳纤维布成型，得到粗胚半成品。The manufacturing method of carbon fiber fishing lure rough embryo according to claim 1, it is characterized in that: step 3 is to wrap carbon fiber cloth on the mandrel, take out the mandrel or not, insert an air bag into the carbon fiber cloth, and blow air to make The heated carbon fiber cloth is formed to obtain a semi-finished product of rough embryo.
- 根据权利要求4所述的碳纤维鱼饵粗胚的制作方法，其特征在于：不取出芯模时，所述芯模为固定式芯模或EPS类收缩芯模。The method for producing a rough embryo of carbon fiber fishing lure according to claim 4, wherein when the mandrel is not taken out, the mandrel is a fixed mandrel or an EPS type shrinking mandrel.
- 根据权利要求1所述的碳纤维鱼饵粗胚的制作方法，其特征在于：步骤5中的配件为卡环或/和响珠。The method for making rough embryos of carbon fiber fishing lures according to claim 1, wherein the accessories in step 5 are snap rings or/and ring beads.
- 一种碳纤维鱼饵粗胚的制作方法，包括以下步骤：A method for producing carbon fiber bait rough embryos, comprising the following steps:步骤1、模具内壁喷透明胶衣；Step 1. Spray transparent gel coat on the inner wall of the mold;步骤2、将干燥的碳纤布贴于模具内表面的透明胶衣上；Step 2. Paste the dry carbon fiber cloth on the transparent gel coat on the inner surface of the mold;步骤3、在碳纤布上铺导流网、脱模布；Step 3. Lay the guide net and the release cloth on the carbon fiber cloth;步骤4、套真空导流袋；Step 4. Set the vacuum diversion bag;步骤5、真空导流袋抽真空后，导入树脂固化；Step 5. After the vacuum diversion bag is evacuated, the resin is introduced to cure;步骤6、得到粗胚。Step 6. Obtain crude embryos.
- 根据权利要求7所述的碳纤维鱼饵粗胚的制作方法，其特征在于：步骤6中可以为常温固化或加热固化。The method for producing the rough embryo of carbon fiber fishing lure according to claim 7, characterized in that: in step 6, it can be solidified at room temperature or solidified by heating.
- 根据权利要求7所述的碳纤维鱼饵粗胚的制作方法，其特征在于：所述碳纤布为：1k、1.5K、3K、12K等各类碳纤维编织布，0-900UD布，玻纤及玻纤电镀布、编织布、纺沦、涤沦、克维拉纤维编织布，各类纤维类混编布、编织布、交叉布，以及各类含浸树脂的预浸布、编织布和未含浸树脂的干布。The method for making the rough embryo of carbon fiber fishing lure according to claim 7, wherein the carbon fiber cloth is: 1k, 1.5K, 3K, 12K and other types of carbon fiber woven cloth, 0-900UD cloth, glass fiber and glass fiber Electroplating cloth, woven cloth, spun, polyester, Kevlar fiber woven cloth, all kinds of fiber blended cloth, woven cloth, cross cloth, and all kinds of resin-impregnated pre-impregnated cloth, woven cloth and non-resin-impregnated cloth dry cloth.
- 一种碳纤维鱼饵粗胚，其特征在于：使用权利要求1-9中任何一项制备方法制得。A carbon fiber bait rough embryo is characterized in that: using any one of the preparation methods in claims 1-9 to make.