WO2021261824A1 - 메이크업 밀착력 강화 및 묻어남 방지를 위한 양이온성 화장료 조성물 - Google Patents

메이크업 밀착력 강화 및 묻어남 방지를 위한 양이온성 화장료 조성물 Download PDF

Info

Publication number
WO2021261824A1
WO2021261824A1 PCT/KR2021/007433 KR2021007433W WO2021261824A1 WO 2021261824 A1 WO2021261824 A1 WO 2021261824A1 KR 2021007433 W KR2021007433 W KR 2021007433W WO 2021261824 A1 WO2021261824 A1 WO 2021261824A1
Authority
WO
WIPO (PCT)
Prior art keywords
powder
cosmetic composition
positive charge
polyquaternium
makeup
Prior art date
Application number
PCT/KR2021/007433
Other languages
English (en)
French (fr)
Inventor
이지현
이준배
서은주
박명삼
Original Assignee
코스맥스 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 코스맥스 주식회사 filed Critical 코스맥스 주식회사
Priority to JP2022568443A priority Critical patent/JP2023525773A/ja
Priority to US17/924,330 priority patent/US20230181448A1/en
Priority to CN202180033777.6A priority patent/CN115551466A/zh
Publication of WO2021261824A1 publication Critical patent/WO2021261824A1/ko

Abstract

메이크업 피부 밀착력 강화 및 묻어남 방지를 위한 양전하 공여 물질을 포함하는 파우더 화장료 조성물을 제공한다. 상기 파우더 화장료 조성물은 특정 조합의 공여 물질을 포함함으로써 단독의 양전하 공여 물질을 포함하는 경우 보다 현저히 높은 양전하를 나타내어 메이크업의 피부 밀착력이 우수한 효과를 제공할 수 있다.

Description

메이크업 밀착력 강화 및 묻어남 방지를 위한 양이온성 화장료 조성물
메이크업 피부 밀착력 강화 및 묻어남 방지를 위한 양전하 공여 물질을 함유한 파우더를 포함하는 화장료 조성물에 관한 것이다.
미세먼지, 황사 등 대기오염 물질로부터 호흡기를 보호하기 위해 간헐적으로 착용하던 마스크는 최근 사스, 메르스 및 신종 코로나 바이러스 확산으로 인하여 그 중요도가 높아지고 또한 일상화되고 있다. 이렇게 마스크 착용 시간 및 빈도가 점점 증가하면서 마스크와의 접촉에 의해 메이크업이 무너지거나 마스크에 묻어나는 등 많은 문제점들이 발생하고 있다.
이처럼 메이크업　화장료에서 커버력 및 밀착력은 필수적으로 요구되는 요소이지만, 특히　파우더　제형은 제형적 특성으로 인해 밀착성을 향상시키기에는 한계가 있다. 또한,　파우더형 압축 제형은 케이킹 현상 또는 그레이징 현상 등이 발생할 수 있으며, 제품 도포 시 화장 뭉침 현상 또는 화장 들뜸 현상 등이 초래될 수 있다. 상기와 같이,　화장료의 밀착성과 커버력을 향상시키기 위해 다양한 방법들이 시도되고 있으나, 아직까지 실효성이 부족하며 소비자가 체감할 만큼의 효과는 발휘되지 않은 실정이다.
이와 관련하여, 기존 연구에 따르면 피부 표면은 음전하를 띠는 것으로 알려져 있다(J. Pharm. Sci, 76(10) (1987) 765-773; 및 J. Controlled Release 103 (2005) 123-136 참조). 따라서, 본 발명자들은 양전하를 띠는 파우더를 함유하는 메이크업 화장료 조성물을 도입할 경우, 정전기적 인력으로 인해 피부 표면과의 강한 밀착을 기대할 수 있고, 이를 통해 마스크에 묻어남을 방지할 수 있음을 확인하여, 본 발명을 완성하였다.
일 양상은 양전하 공여 물질을 함유한 파우더를 포함하는 화장료 조성물로서, 메이크업 묻어남이 방지되고, 피부 밀착력이 개선된 것인 화장료 조성물을 제공한다.
일 양상은 양전하 공여 물질을 함유한 파우더를 포함하는 화장료 조성물로서, 메이크업 묻어남이 방지되고, 피부 밀착력이 개선된 것인 화장료 조성물을 제공하는 것이다. 상기 화장료 조성물은 파우더 화장료 조성물일 수 있다.
본 명세서에서 사용되는 용어, "양전하 공여 물질(positive charge donor substance)"은 생리학적 pH와 같은 선택된 pH에서 양의 값의 순전하를 제공하는 물질을 의미하는 것으로, 상기 생리학적 pH는 6 내지 8, 구체적으로는 6.5 내지 8, 보다 구체적으로는 7.5의 pH를 의미하는 것일 수 있다.
상기 양전하 공여 물질 및 이를 포함하는 파우더의 제타 전위는 양의 전위를 나타낼 수 있고, 음전하의 피부에 밀착될 수 있는 어떤 크기의 양전하를 나타낼 수 있다. 예를 들어, 상기 양전하 공여 물질 또는 이를 포함하는 파우더의 제타 전위는 pH가 중성인 조건에서 5 내지 120 mV, 예를 들어, 5 내지 110 mV, 5 내지 100 mV, 5 내지 95 mV, 5 내지 90 mV, 10 내지 120 mV, 10 내지 110 mV, 10 내지 100 mV, 10 내지 95 mV, 10 내지 90 mV, 20 내지 120 mV, 20 내지 110 mV, 20 내지 100 mV, 20 내지 95 mV, 20 내지 90 mV, 30 내지 120 mV, 30 내지 110 mV, 30 내지 100 mV, 30 내지 95 mV, 30 내지 90 mV, 40 내지 120 mV, 40 내지 110 mV, 40 내지 100 mV, 40 내지 95 mV, 40 내지 90 mV, 45 내지 120 mV, 45 내지 110 mV, 45 내지 100 mV, 45 내지 95 mV, 45 내지 90 mV, 45 내지 80 mV, 또는 45 내지 70 mV일 수 있다. 일 구체예에 있어서, 양전하 공여 물질을 포함하지 않은 파우더는 제타 전위가 음의 값으로 측정된 반면에, 산화철, 폴리쿼터늄 또는 이들의 조합을 포함하는 혼합 파우더는 제타 전위가 양의 값으로 측정됨을 확인하였다.
상기 양전하 공여 물질은 양전하를 제공할 수 있는 어떤 종류의 물질도 사용될 수 있으나, 예를 들어, 산화철 (Iron-oxide), 폴리쿼터늄(예: 폴리쿼터늄-10 (Polyquaternium-10), 폴리쿼터늄-7 (Polyquaternium-7) 등), 구아하이드록시프로필트라이모늄클로라이드 (Guar Hydroxypropyltrimonium Chloride), 폴리라이신 (Poly-L-lysine) 또는 이들의 조합일 수 있다. 상기 산화철은 적색산화철, 황색산화철, 흑색산화철 또는 이들의 조합일 수 있으나, 이에 제한되지 않는다.
일 구체예에 있어서, 상기 양전하 공여 물질은 산화철 및 폴리쿼터늄-10의 조합일 수 있다. 따라서, 상기 파우더는 산화철 및 폴리쿼터늄-10을 함유한 혼합 파우더일 수 있다. 일 구체예에 있어서, 상기 양전하 공여 물질로서 산화철 및 폴리쿼터늄-10의 조합을 사용할 경우, 단독의 양전하 공여 물질 보다 높은 양전하를 나타내고, 이에 따른 피부 밀착력 개선 효과 및 메이크업 묻어남 방지 효과가 우수함을 확인하였다. 일 실시예에서, 산화철 또는 폴리쿼터늄-10을 단독으로 포함하는 파우더에 비해, 산화철 및 폴리쿼터늄-10의 조합을 포함하는 혼합 파우더는 더 높은 제타 전위를 나타냄을 확인하였다. 또한, 산화철 및 폴리쿼터늄-6의 조합을 포함하는 혼합 파우더에 비해, 산화철 및 폴리쿼터늄-10의 조합을 포함하는 혼합 파우더는 더 높은 제타 전위를 나타냄을 확인하였다.
상기 파우더는 상기 양전하 공여 물질을 피부 밀착력을 개선하고 메이크업 묻어남을 방지하는 효과를 얻을 수 있는 적절한 함량으로 포함할 수 있다.
상기 파우더는 파우더 전체 중량에 대해 상기 산화철을 0.05 내지 95 중량%, 예를 들어, 0.05 내지 90 중량%, 예를 들어, 0.5 내지 95 중량%, 예를 들어 0.5 내지 90 중량%, 예를 들어, 1 내지 95 중량%, 예를 들어, 1 내지 90 중량%, 예를 들어 5 내지 95 중량%, 예를 들어, 5 내지 90 중량%, 예를 들어 10 내지 95 중량%, 예를 들어, 10 내지 90 중량%, 예를 들어, 5 내지 85 중량%, 예를 들어, 10 내지 85 중량%, 예를 들어, 15 내지 95 중량%, 예를 들어, 15 내지 90 중량%, 예를 들어, 20 내지 95 중량%로 포함하는 것일 수 있다. 상기 범위에서 벗어나, 산화철의 함량이 증가하면, 화장료 조성물의 색상에 영향을 미치므로, 화장료 조성물의 원하는 조색이 어려운 문제가 있을 수 있고, 산화철의 함량이 감소하면, 피부 밀착력을 개선하고 메이크업 묻어남을 방지하는 효과가 미미할 수 있다.
상기 파우더는 파우더 전체 중량에 대해 상기 폴리쿼터늄-10을 1 내지 60 중량%, 예를 들어, 1 내지 55 중량%, 예를 들어, 1 내지 50 중량%, 예를 들어, 5 내지 60 중량%, 예를 들어, 5 내지 55 중량%, 예를 들어 5 내지 50 중량%, 예를 들어, 10 내지 60 중량%, 예를 들어, 10 내지 55 중량%, 예를 들어, 10 내지 50 중량%로 포함하는 것일 수 있다. 상기 범위를 벗어나, 폴리쿼터늄-10의 함량이 증가하면, 화장료 조성물의 점도가 높아져 화장료 조성물의 제형 및 사용감에 부정적 영향을 미칠 수 있고, 폴리쿼터늄-10의 함량이 감소하면, 피부 밀착력을 개선하고 메이크업 묻어남을 방지하는 효과가 미미할 수 있다.
상기 파우더는 일반적인　파우더　화장품에 포함되는　파우더들의 조합을 더 포함할 수 있으며, 종래에　파우더　화장료　조성물에 포함되는 어떠한　파우더류를 포함할 수 있다. 예를 들어, 탤크, 마이카, 합성운모, 세리사이트, 실리카, 이산화 티탄, 실리콘계　파우더, 보론　파우더, 징크옥사이드, 나일론　파우더, 폴리메타크릴레이트　파우더, 우레탄　파우더, 아크릴레이트 (코)폴리머, 폴리에틸렌 (코)폴리머, 유기계 색소안료, 무기계 색소 안료 및 진주 광택 안료로 구성된 군으로부터 선택된 하나 이상을 포함할 수 있다. 또한, 상기 파우더는 표면처리 되지 않을 수도 있으나, 실리콘, 금속염, 지방산, 아미노산, 라우로일라이신 또는 레시틴으로 표면처리 된 것일 수도 있다.
상기 화장료 조성물은 양전하 공여 물질을 함유한 파우더를 포함함으로써, 화장료 조성물의 피부 밀착력이 현저히 개선되어, 피부에 도포된 메이크업이 다른 표면, 예를 들어, 마스크에 묻어나는 문제점을 해결할 수 있다. 일 구체예에 있어서, 양전하 공여 물질로서 산화철 및 폴리쿼터늄-10을 파우더에 함유하고, 이를 포함한 화장료 조성물을 제조하여 메이크업이 묻어나는 정도를 평가한 결과, 상기 파우더를 포함하지 않는 화장료 조성물에 비해, 메이크업이 묻어나는 정도가 현저히 개선됨을 확인하였다.
상기 화장료 조성물은 상기 파우더를 피부 밀착력을 개선하고 메이크업 묻어남을 방지하는 효과를 얻을 수 있는 적절한 함량으로 포함할 수 있다. 상기 화장료 조성물은 조성물 전체 중량에 대해 상기 파우더를 0.0001 내지 20 중량%, 0.0001 내지 10 중량%, 0.0001 내지 5 중량%, 0.001 내지 20 중량%, 0.001 내지 10 중량%, 0.001 내지 5 중량%, 0.01 내지 20 중량%, 0.01 내지 10 중량%, 0.01 내지 5 중량%, 0.1 내지 20 중량%, 0.1 내지 10 중량%, 0.1 내지 5 중량%, 1 내지 20 중량%, 1 내지 10 중량%, 또는 1 내지 5 중량%로 포함할 수 있다. 상기 파우더의 함량이 상기 범위를 벗어나면 원하는 화장료 제형을 얻을 수 없거나, 피부 밀착력을 개선하고 메이크업 묻어남을 방지하는 효과가 미미할 수 있다.
상기 화장료 조성물의 제형은 통상적인 화장료의 제형이라면 제한되지 않지만, 예컨대 압축 파우더, 압축 팩트, 파우더 파운데이션 또는 파우더 팩트 등으로, 일정한 접시에 화장료를 성형시켜 만든 제형일 수 있다. 상기 파우더의 성형성을 향상시키기 위해 오일 바인더를 포함할 수 있고, 상기 오일 바인더는 에스터계 오일, 탄화수소계 오일 및 실리콘 오일 등이 사용될 수 있다.
상기 화장료 조성물은 보존제, 안정화제, 계면활성제, 용해제, 보습제, 에몰리언트제, 자외선 흡수제, 방부제, 살균제, 산화 방지제, pH 조정제, 유기 및 무기 안료, 향료, 냉감제 또는 제한제 등을 더 포함할 수 있다. 상기 보습제 등의 추가 성분의 배합량은 본 발명의 목적 및 효과를 손상시키지 않는 범위 내에서 당업자가 용이하게 선정 가능하다.
일 양상에 따른 파우더 화장료 조성물은 양전하 공여 물질을 포함함으로써, 메이크업이 묻어나는 문제를 해결하고, 피부 밀착력이 개선된 효과를 제공할 수 있다.
다른 양상에 따른 파우더 화장료 조성물은 특정 조합의 양전하 공여 물질을 포함함으로써 단독의 양전하 공여 물질을 포함하는 경우 보다 현저히 높은 양전하를 나타내어 메이크업의 피부 밀착력이 우수한 효과를 제공할 수 있다.
도 1은 비교예 1에 따른 파우더의 표면 전위 (mV) 측정 값을 나타낸 그래프이다.
도 2는 비교예 2에 따른 파우더의 표면 전위 (mV) 측정 값을 나타낸 그래프이다.
도 3은 비교예 3에 따른 파우더의 표면 전위 (mV) 측정 값을 나타낸 그래프이다.
도 4는 실시예 1에 따른 혼합 파우더의 표면 전위 (mV) 측정 값을 나타낸 그래프이다.
도 5는 실시예 2에 따른 혼합 파우더의 표면 전위 (mV) 측정 값을 나타낸 그래프이다.
도 6은 비교예 4에 따른 파우더의 표면 전위 (mV) 측정 값을 나타낸 그래프이다.
도 7은 실시예 3에 따른 파우더의 표면 전위 (mV) 측정 값을 나타낸 그래프이다.
도 8은 양이온성 파우더를 함유한 화장료 조성물의 피부 밀착력 개선 및 마스크 묻어남 방지 효과를 확인한 이미지이다.
이하 실시예를 통하여 보다 상세하게 설명한다. 그러나, 이들 실시예는 예시적으로 설명하기 위한 것으로 본 발명의 범위가 이들 실시예에 한정되는 것은 아니다.
비교예 1 내지 3, 및 실시예 1 및 2. 양전하 공여물질을 함유한 혼합 파우더의 제조
양전하를 갖는 파우더를 제조하기 위해, 하기 표 1에 나타낸 비교예 및 실시예의 조성으로 파우더를 혼합하여 제조하였다. 구체적으로, 비교예 1 내지 3은 산화철, 실리카, 또는 폴리쿼터늄-10을 각각 함유하도록 제조하였고, 실시예 1 및 2는 산화철, 실리카, 및 폴리쿼터늄-10을 함유하도록 제조하였다.
함량 (중량 %)
성분 비교예1 비교예2 비교예3 실시예1 실시예2
산화철 - 100 - 90 10
실리카 100 - - 1 50
폴리쿼터늄-10 - - 100 9 40
비교예 4 및 실시예 3. 양전하 공여물질을 함유한 혼합 파우더의 제조
양전하를 갖는 파우더를 제조하기 위해, 하기 표 2에 나타낸 비교예 및 실시예의 조성으로 파우더를 혼합하여 제조하였다. 구체적으로, 비교예 4는 흑색산화철 및 폴리쿼터늄-6을 함유하도록 제조하였고, 실시예 1은 황색산화철 및 폴리쿼터늄-10을 함유하도록 제조하였다.
함량 (중량 %)
성분 비교예4 실시예3
흑색산화철 90 -
황색산화철 - 90
실리카 1 1
폴리쿼터늄-10 - 9
폴리쿼터늄-6 9 -
실험예 1. 표면 전위 (제타 전위) 확인
1.1 입자 크기 및 제타 전위 확인
양전하 공여물질을 함유한 혼합 파우더와 표면전위 측정을 아래와 같이 실시하였다. 표면전위는 입도 및 표면전위를 측정할 수 있는 동적광산란장치(HORIBA, SZ-100, Dynamic Light Scattering, DLS)를 이용하여 파우더의 표면전위를 측정하였다. 혼합 파우더에 대한 표면전위 측정에 앞서 먼저 증류수에 대한 표면전위 측정을 시행하였고, 표면전위가 0임을 확인하였다. 혼합 파우더의 표면전위 측정방법은 혼합 파우더를 물에 균일하게 분산한 후, SZ-100 분석기기를 이용하여 표면전위 측정을 수행하였다. 비교예 1 내지 3, 및 실시예 1 및 2의 파우더의 측정된 제타 전위 값은 도 1 내지 도 5 및 하기 표 3에 나타내었다. 또한, 비교예 4 및 실시예 3의 파우더의 측정된 제타 전위 값은 도 6 내지 도 7 및 하기 표 4에 나타내었다.
실험항목 비교예1 비교예2 비교예3 실시예1 실시예2
Zeta potential(mV) -46.8 13.9 41.4 67.9 49.3
-47.5 18.8 40.8 65.8 50.2
-51.7 16.1 39.9 68.8 49.0
-54.0 13.8 41.1 67.5 48.2
-51.8 12.9 40.7 67.6 51.6
평균 -50.4 15.1 40.8 67.5 49.7
실험항목 비교예4 실시예3
Zeta potential(mV) 14.8 66.1
17.7 67.5
22.5 67.7
평균 18.3 67.1
그 결과, 도 1 내지 도 5 및 표 3에 나타낸 바와 같이, 양전하 공여 물질을 포함하지 않는 비교예 1의 파우더는 음전하를 나타낸 반면, 양전하 공여 물질인 산화철 및 폴리쿼터늄-10을 단독으로 포함하는 비교예 2 및 3의 파우더는 각각 평균적으로 15.1 mV 및 40.8 mV로, 중간 정도의 양전하를 나타내었다.
특히, 양전하 공여 물질인 산화철 및 폴리쿼터늄-10을 혼합하여 포함하는 실시예 1 및 2의 파우더는 각각 평균적으로 67.5 mV 및 49.7 mV로, 양전하 공여 물질을 포함하지 않는 비교예 1의 파우더뿐만 아니라, 양전하 공여 물질을 단독으로 포함하는 비교예 2 및 3의 파우더에 비해서도, 현저히 증가된 양전하를 나타내었다.
또한, 도 6 내지 도 7 및 표 4에 나타낸 바와 같이, 산화철 및 폴리쿼터늄-6의 조합을 포함하는 비교예 4의 혼합 파우더에 비해, 산화철 및 폴리쿼터늄-10의 조합을 포함하는 실시예 3의 혼합 파우더가 현저히 강한 양전하를 나타내었다.
비교예 5 및 실시예 4. 양전하 공여 물질을 함유하는 파운데이션 제조
양전하 공여물질 혼합 파우더의 함유 여부가 메이크업 화장료 조성물의 묻어남 방지에 미치는 영향을 알아보고자, 표면 전위가 가장 높은 상기 실시예 1의 혼합 파우더 함유 여부를 달리하여 비교예 5 및 실시예 4의 파운데이션 화장료 조성물을 제조하였다.
구체적으로, 하기 표 5에 기재된 각 성분과 함량에 따라 각 원료를 비이커에 계량한 후 75~80℃의 온도에서 디스퍼(disper)를 이용하여 1000rpm으로 5분간 균일하게 혼합하였다. 혼합 후 같은 온도에서 분체를 투입 후 1000rpm으로 3분간 균일하게 혼합하였다. 그 다음 기포를 제거하고 냉각하여 각 화장료 조성물을 제조하였다. 하기 표 5에 비교예 5 및 실시예 4의 화장료 조성물의 구체적인 성분 및 함량을 나타내었다.
성분 함량 (중량%)
비교예5 실시예4
라우릴피이지-10트리스(트리메칠실록시)실릴에칠디메치콘 3.0 3.0
페닐트리메치콘 10.0 10.0
사이클로펜타실록산 21.0 21.0
에칠헥실메톡시신나메이트 7.0 7.0
에칠헥실살리실레이트 5.0 5.0
디스테아디모늄헥토라이트 0.5 0.5
미립자티타늄디옥사이드 7.0 7.0
티타늄디옥사이드 9.0 9.0
황색산화철 1.0 1.0
정제수 To 100 To 100
디소듐이디티에이 0.02 0.02
마그네슘설페이트 0.7 0.7
글리세린 5.0 5.0
페녹시에탄올 0.7 0.7
양전하 공여물질을 함유한 혼합 파우더(실시예1) - 3.0
실험예 2. 메이크업 묻어남 평가
상기 실시예 4와 비교예 5의 파운데이션 화장료 조성물에 대하여 마스크 착용시 메이크업 묻어남 정도를 평가하였다.
구체적으로, 세안 후, 항온 및 항습 조건에서 10분 대기 후, 실시예 4 및 비교예 5의 화장료 조성물을 각각 얼굴 우측과 좌측에 도포한 뒤, 5분 동안 제품을 고정시켰다. 이후, 마스크를 착용하고, 2시간 동안 일상 생활을 한 후, 착용하였던 마스크의 얼굴과 닿았던 면의 이미지를 촬영하였다.
그 결과, 도 8에 나타낸 바와 같이, 비교예 5의 조성물에 비해, 실시예 4의 조성물은 피부에 도포한 경우에 마스크 묻어남이 현저히 적게 나타남을 확인하였다. 상기 결과로부터, 실시예 4의 조성물은 비교예 5의 조성물에 비해, 양전하 공여물질을 함유한 혼합 파우더를 더 포함함으로써, 화장료 조성물의 피부 밀착력이 증가하여, 마스크에 묻어나는 문제를 방지할 수 있음을 확인할 수 있다.
실험예 3. 피부 안전성 평가
상기 실시예 4와 비교예 5의 파운데이션 화장료 조성물의 피부 안전성에 대한 평가를 수행하였다.
구체적으로, 피부 질환이 없는 성인 남녀 20명을 대상으로 하여 상기 실시예 4 및 비교예 5의 화장료 조성물의 자극 정도를 평가하였다. 시험자들의 팔 전반에 20 μL의 시료를 도포한 후, 시험 부위를 밀폐한 후 24시간 동안 첩포하였다. 첩포를 제거한 후 30분과 24시간 후에 피부에서의 반응을 CTFA 가이드라인에 제시된 용어(terminology)에 의거하여 검사하였다. 판정 기준에 의해 얻어진 시험자들의 피부자극지수(PII) 점수를 평균하여 1 미만이면 저자극, 2 미만이면 경자극, 3.5 미만이면 중자극, 3.5 이상이면 강자극으로 평가하였다. 실시예 4 및 비교예 5의 화장료 조성물의 피부 자극 지수는 하기 표 6에 나타내었다.
실험항목 비교예 5 실시예 4
피부자극지수(PII) 무자극 무자극
그 결과, 표 6에 나타낸 바와 같이, 비교예 5 및 실시예 4의 조성물 모두 무자극으로 화장료 조성물로서 안전하게 사용 가능함을 확인하였다. 상기 결과로부터, 양전하 공여 물질을 함유한 혼합 파우더를 더 포함하더라도, 이에 의해 피부 안전성에 부정적 영향을 미치는 것이 아님을 확인하였다.
실험예 4. 관능 평가
상기 실시예 4 및 비교예 5의 파운데이션 화장료 조성물에 대하여 관능 평가(5점 척도법)을 수행하였다.
구체적으로, 사용감, 밀착감, 전반적인 만족도에 대하여 매우 좋음 5점, 좋음 5점, 보통 3점, 나쁨 2점, 매우 나쁨 1점으로 평가하였다. 실시예 4 및 비교예 5의 화장료 조성물의 관능 평가 결과는 하기 표 7에 나타내었다.
항목 비교예 5 실시예 4
사용감 4.0 4.0
밀착감 3.0 4.5
전반적인 만족도 3.7 4.4
그 결과, 상기 표 7에 나타낸 바와 같이, 실시예 4의 화장료 조성물은 사용감에 있어 우수한 정도로 비교예 5의 조성물과 유사하게 유지되었고, 밀착감 및 전반적인 만족도에 있어서는 비교예 5의 조성물에 현저히 개선됨을 확인하였다. 상기 결과로부터, 실시예 4의 조성물은 비교예 5의 조성물에 비해, 양전하 공여 물질을 함유한 혼합 파우더를 포함함으로써, 사용감에 있어 부정적인 영향을 미치지 않으면서도, 현저히 개선된 메이크업 밀착감 및 전반적인 만족도를 나타냄을 확인할 수 있다. 이상의 결과로부터, 상기 양전하 공여물질을 포함하는 화장료 조성물은 양전하 공여물질을 포함함으로써, 특히, 산화철 및 폴리쿼터늄-10을 조합하여 포함함으로써, 피부 밀착력이 현저히 증가하고, 메이크업이 묻어나는 문제를 해결할 수 있음을 확인하였다.

Claims (7)

  1. 양전하 공여 물질을 함유한 파우더를 포함하는 화장료 조성물로서, 메이크업 묻어남이 방지되고, 피부 밀착력이 개선된 것을 특징으로 하는 화장료 조성물.
  2. 청구항 1에 있어서, 상기 양전하 공여 물질은 산화철(Iron-oxide), 폴리쿼터늄-10(Polyquaternium-10), 폴리쿼터늄-7(Polyquaternium-7), 구아하이드록시프로필트라이모늄클로라이드(Guar Hydroxypropyltrimonium Chloride), 폴리라이신(Poly-L-lysine) 또는 이들의 조합인 것인 화장료 조성물.
  3. 청구항 1에 있어서, 상기 파우더는 산화철 및 폴리쿼터늄-10를 함유한 혼합 파우더인 것인 화장료 조성물.
  4. 청구항 3에 있어서, 상기 파우더는 상기 산화철을 0.05 내지 95 중량%로 포함하는 것인 화장료 조성물.
  5. 청구항 3에 있어서, 상기 파우더는 상기 폴리쿼터늄-10을 1 내지 50 중량%로 포함하는 것인 화장료 조성물.
  6. 청구항 1에 있어서, 상기 파우더는 40 내지 120 mV의 제타 전위를 나타내는 것인 화장료 조성물.
  7. 청구항 1에 있어서, 조성물 전체 중량에 대해 상기 파우더를 0.0001 내지 20 중량%로 포함하는 것인 화장료 조성물.
PCT/KR2021/007433 2020-06-25 2021-06-15 메이크업 밀착력 강화 및 묻어남 방지를 위한 양이온성 화장료 조성물 WO2021261824A1 (ko)