WO2021215240A1 - レジスト下層膜形成用組成物及び半導体基板の製造方法 - Google Patents

レジスト下層膜形成用組成物及び半導体基板の製造方法 Download PDF

Info

Publication number
WO2021215240A1
WO2021215240A1 PCT/JP2021/014642 JP2021014642W WO2021215240A1 WO 2021215240 A1 WO2021215240 A1 WO 2021215240A1 JP 2021014642 W JP2021014642 W JP 2021014642W WO 2021215240 A1 WO2021215240 A1 WO 2021215240A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
metal
underlayer film
forming
composition
Prior art date
Application number
PCT/JP2021/014642
Other languages
English (en)
French (fr)
Inventor
智昭 瀬古
酒井　達也
一憲 酒井
祐亮 庵野
Original Assignee
Jsr株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jsr株式会社 filed Critical Jsr株式会社
Priority to JP2022516941A priority Critical patent/JPWO2021215240A1/ja
Priority to KR1020227036364A priority patent/KR20230007332A/ko
Publication of WO2021215240A1 publication Critical patent/WO2021215240A1/ja
Priority to US17/961,611 priority patent/US20230069221A1/en

Abstract

電子線又は極端紫外線リソグラフィーにおける金属含有レジストの下層膜の形成に用いられ、金属含有レジストパターンの倒壊を抑制し、微細な金属含有レジストパターンを形成できるレジスト下層膜を形成することができる組成物等を提供する。本発明は、電子線又は極端紫外線リソグラフィーにおける金属含有レジスト膜の下層膜を形成するために用いられるレジスト下層膜形成用組成物であって、下記式（１）で表される第１構造単位を有するポリシロキサン化合物と、溶媒とを含有するレジスト下層膜形成用組成物である。

Description

レジスト下層膜形成用組成物及び半導体基板の製造方法
　本発明は、レジスト下層膜形成用組成物及び半導体基板の製造方法に関する。
　半導体基板の製造におけるパターン形成には、多層レジストプロセスが用いられることがある。多層レジストプロセスは、例えば、基板上に有機下層膜、ケイ素含有膜等のレジスト下層膜を介して積層されたレジスト膜を露光及び現像して得られたレジストパターン等をマスクとしてエッチングを行うことでパターニングされた基板を形成する（国際公開第２０１２／０３９３３７号参照）。
　最近では、半導体デバイスの高集積化がさらに進んでおり、より微細なパターンを形成するため、使用する露光光がＫｒＦエキシマレーザー（２４８ｎｍ）、ＡｒＦエキシマレーザー（１９３ｎｍ）等から、極端紫外線（１３．５ｎｍ、ＥＵＶ）へと短波長化される傾向にある。また、微細なパターンを形成するため、電子線を使用したリソグラフィーも行われることがある。
国際公開第２０１２／０３９３３７号
　多層レジストプロセスにおいては、レジスト下層膜であるケイ素含有膜上に金属含有レジスト膜を形成するための組成物（以下、「金属含有レジスト膜形成用組成物」ともいう）を用いて、微細な金属含有レジストパターンを形成できることが求められる。しかし、従来の電子線又は極端紫外線リソグラフィーにおいて、金属含有レジストパターンの倒壊を抑制し、微細な金属含有レジストパターンを良好な形状で形成することは困難である。特に、形成されるレジストパターンが微細なものになるほど、現像時等において金属含有レジストパターンの倒壊が生じ易くなる。
　本発明は、以上のような事情に基づいてなされたものであり、その目的は、電子線又は極端紫外線リソグラフィーにおける金属含有レジストの下層膜の形成に用いられ、金属含有レジストパターンの倒壊を抑制し、微細な金属含有レジストパターンを形成できるレジスト下層膜を形成することができるレジスト下層膜形成用組成物、及びこのようなレジスト下層膜形成用組成物を用いた半導体基板の製造方法を提供することにある。
　上記課題を解決するためになされた発明は、電子線又は極端紫外線リソグラフィーにおける金属含有レジストの下層膜を形成するために用いられるレジスト下層膜形成用組成物であって、下記式（１）で表される第１構造単位を有するポリシロキサン化合物（以下、「［Ａ］化合物」ともいう。）と、溶媒（以下、「［Ｂ］溶媒」ともいう。）とを含有するレジスト下層膜形成用組成物である。
Figure JPOXMLDOC01-appb-C000003
 （式（１）中、Ｘは、ヒドロキシ基、カルボニル基及びエーテル結合から選ばれる少なくとも１つの構造を有する有機基である。ａは、１～３の整数である。ａが２以上の場合、複数のＸは互いに同一又は異なる。Ｒ１は、炭素数１～２０の１価の有機基、ヒドロキシ基又はハロゲン原子である。但し、Ｒ１は、Ｘ以外の基である。ｂは、０～２の整数である。ｂが２の場合、２つのＲ１は互いに同一又は異なる。但し、ａ＋ｂは３以下である。）
　上記課題を解決するためになされた別の発明は、基板に直接又は間接にレジスト下層膜形成用組成物を塗工する工程と、上記レジスト下層膜形成用組成物塗工工程により形成されたレジスト下層膜に金属含有レジスト膜形成用組成物を塗工する工程と、上記金属含有レジスト膜形成用組成物塗工工程により形成された金属含有レジスト膜を電子線又は極端紫外線により露光する工程と、上記露光された金属含有レジスト膜を現像する工程とを備え、上記レジスト下層膜形成用組成物が、上述の当該レジスト下層膜形成用組成物である半導体基板の製造方法である。
　本発明によれば、電子線又は極端紫外線リソグラフィーにおける金属含有レジストの下層膜の形成に用いられ、金属含有レジストパターンの倒壊を抑制し、微細な金属含有レジストパターンを形成できるレジスト下層膜を形成することができるレジスト下層膜形成用組成物、及びこのようなレジスト下層膜形成用組成物を用いた半導体基板の製造方法を提供することができる。
　以下、本発明のレジスト下層膜形成用組成物及び半導体基板の製造方法について詳説する。
＜レジスト下層膜形成用組成物＞
　当該レジスト下層膜形成用組成物は、［Ａ］化合物と［Ｂ］溶媒とを含有する。当該レジスト下層膜形成用組成物は、本発明の効果を損なわない範囲において、［Ａ］化合物及び［Ｂ］溶媒以外のその他の添加剤（以下、「［Ｃ］添加剤」ともいう。）を含有していてもよい。
　当該レジスト下層膜形成用組成物は［Ａ］化合物と［Ｂ］溶媒とを含有することにより、電子線又は極端紫外線リソグラフィーにおいて、形成される金属含有レジスト下層膜上に、パターンの倒壊が抑制された、微細な金属含有レジストパターンを形成することができる。
　当該レジスト下層膜形成用組成物は、上述のような効果を奏するため、電子線又は極端紫外線リソグラフィーにおける金属含有レジスト膜の下層膜を形成するための組成物として好適に用いることができる。
　以下、当該レジスト下層膜形成用組成物が含有する各成分について説明する。
［［Ａ］化合物］
　［Ａ］化合物は、後述する下記式（１）で表される第１構造単位（以下、「構造単位（Ｉ）」ともいう。）を有するポリシロキサン化合物である。本明細書において「ポリシロキサン化合物」とは、シロキサン結合（－Ｓｉ－Ｏ－Ｓｉ－）を含む化合物を意味する。［Ａ］化合物は、本発明の効果を損なわない範囲において、上記構造単位（Ｉ）以外の他の構造単位を有していてもよい。他の構造単位としては、例えば後述する下記式（２）で表される第２構造単位（以下、「構造単位（ＩＩ）」ともいう。）、後述する下記式（３）で表される第３構造単位（以下、「構造単位（ＩＩＩ）」ともいう。）等が挙げられる。
　以下、［Ａ］化合物が有する各構造単位について説明する。
（構造単位（Ｉ））
　構造単位（Ｉ）は、下記式（１）で表される構造単位である。［Ａ］化合物は、１種又は２種以上の構造単位（Ｉ）を有することができる。
Figure JPOXMLDOC01-appb-C000004
　上記式（１）中、Ｘは、ヒドロキシ基、カルボニル基及びエーテル結合からなる群から選ばれる少なくとも１つの構造を含む有機基である。ａは、１～３の整数である。ａが２以上の場合、複数のＸは互いに同一又は異なる。Ｒ１は、炭素数１～２０の１価の有機基、ヒドロキシ基又はハロゲン原子である。但し、Ｒ１は、Ｘ以外の基である。ｂは、０～２の整数である。ｂが２の場合、２つのＲ１は互いに同一又は異なる。但し、ａ＋ｂは３以下である。
　本明細書において、「有機基」とは、少なくとも１個の炭素原子を含む基を意味し、「炭素数」とは、基を構成する炭素原子数を意味する。
　Ｒ１で表される炭素数１～２０の１価の有機基としては、例えば炭素数１～２０の１価の炭化水素基、この炭化水素基の炭素－炭素結合間に２価のヘテロ原子含有基を含む基（以下、「基（α）」ともいう）、上記炭化水素基又は上記基（α）が有する水素原子の一部又は全部を１価のヘテロ原子含有基で置換した基（以下、「基（β）」ともいう）、上記炭化水素基、上記基（α）又は上記基（β）と２価のヘテロ原子含有基とを組み合わせた基（以下、「基（γ）」ともいう）等が挙げられる。なお、Ｒ１で表される炭素数１～２０の１価の有機基には、Ｘで表される基は含まれないものとする。
　本明細書において「炭化水素基」には、鎖状炭化水素基、脂環式炭化水素基及び芳香族炭化水素基が含まれる。この「炭化水素基」は、飽和炭化水素基でも不飽和炭化水素基でもよい。「鎖状炭化水素基」とは、環状構造を含まず、鎖状構造のみで構成された炭化水素基をいい、直鎖状炭化水素基及び分岐状炭化水素基の両方を含む。「脂環式炭化水素基」とは、環構造としては脂環構造のみを含み、芳香環構造を含まない炭化水素基をいい、単環の脂環式炭化水素基及び多環の脂環式炭化水素基の両方を含む。但し、脂環構造のみで構成されている必要はなく、その一部に鎖状構造を含んでいてもよい。「芳香族炭化水素基」とは、環構造として芳香環構造を含む炭化水素基をいう。但し、芳香環構造のみで構成されている必要はなく、その一部に鎖状構造や脂環構造を含んでいてもよい。
　炭素数１～２０の１価の炭化水素基としては、例えば炭素数１～２０の１価の鎖状炭化水素基、炭素数３～２０の１価の脂環式炭化水素基、炭素数６～２０の１価の芳香族炭化水素基が挙げられる。
　炭素数１～２０の１価の鎖状炭化水素基としては、例えばメチル基、エチル基、ｎ－プロピル基、ｉ－プロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ｉｓｏ－ブチル基、ｔｅｒｔ－ブチル基等のアルキル基、エテニル基、プロペニル基、ブテニル基等のアルケニル基、エチニル基、プロピニル基、ブチニル基等のアルキニル基などが挙げられる。
　炭素数３～２０の１価の脂環式炭化水素基としては、例えばシクロペンチル基、シクロヘキシル基等の単環の脂環式飽和炭化水素基、ノルボルニル基、アダマンチル基、トリシクロデシル基、テトラシクロドデシル基等の多環の脂環式飽和炭化水素基、シクロペンテニル基、シクロヘキセニル基等の単環の脂環式不飽和炭化水素基、ノルボルネニル基、トリシクロデセニル基、テトラシクロドデセニル基等の多環の脂環式不飽和炭化水素基などが挙げられる。
　炭素数６～２０の１価の芳香族炭化水素基としては、例えばフェニル基、トリル基、キシリル基、ナフチル基、アントリル基等のアリール基、ベンジル基、フェネチル基、ナフチルメチル基、アントリルメチル基等のアラルキル基などが挙げられる。
　２価又は１価のヘテロ原子含有基を構成するヘテロ原子としては、例えば酸素原子、窒素原子、硫黄原子、リン原子、ケイ素原子、ハロゲン原子等が挙げられる。ハロゲン原子としては、例えばフッ素原子、塩素原子、臭素原子、ヨウ素原子が挙げられる。
　２価のヘテロ原子含有基としては、例えば－Ｏ－、－Ｃ（＝Ｏ）－、－Ｓ－、－Ｃ（＝Ｓ）－、－ＮＲ’－、これらのうちの２つ以上を組み合わせた基等が挙げられる。Ｒ’は、水素原子又は１価の炭化水素基である。
　１価のヘテロ原子含有基としては、例えばハロゲン原子、ヒドロキシ基、カルボキシ基、シアノ基、アミノ基、スルファニル基等が挙げられる。
　Ｒ１で表されるハロゲン原子としては、フッ素原子、塩素原子、臭素原子、ヨウ素原子が挙げられる。
　Ｒ１としては、炭素数１～２０の１価の有機基が好ましく、１価の鎖状炭化水素基、１価の芳香族炭化水素基又は１価の炭化水素基の有する水素原子の一部若しくは全部を１価のヘテロ原子含有基で置換した１価の基がより好ましく、アルキル基又はアリール基がより好ましく、メチル基、エチル基又はフェニル基がさらに好ましい。
　ｂとしては、０又は１が好ましく、０がより好ましい。
　上記式（１）中のＸは、ヒドロキシ基、カルボニル基及びエーテル結合からなる群から選ばれる少なくとも１つの構造を有する有機基である。
　ヒドロキシ基を有する有機基としては、例えばヒドロキシメチル基、ヒドロキシエチル基等のヒドロキシアルキル基が挙げられる。
　カルボニル基を有する有機基としては、例えばエステル結合を有する有機基、カーボネート構造を有する有機基、アミド結合を有する有機基、アシル基を有する有機基、カルボン酸無水物基を有する有機基等が挙げられる。
　カルボニル基を有する有機基としては、下記式（１－１）、下記式（１－２）で表される基が挙げられる。
Figure JPOXMLDOC01-appb-C000005
　上記式（１－１）及び式（１－２）中、Ｒ２及びＲ４は、炭素数１～２０の１価の有機基である。ｎは、１又は２である。ｎが２の場合、複数のＲ２は互いに同一又は異なる。Ｒ３は、水素原子又は炭素数１～２０の１価の有機基である。Ｌは、単結合又は２価の連結基である。＊は、上記式（１）におけるケイ素原子との結合部位を示す。
　Ｒ２及びＲ４で表される炭素数１～２０の１価の有機基としては、例えば上述のＲ１で表される炭素数１～２０の１価の有機基として例示した基と同様の基等が挙げられる。
　Ｒ２及びＲ４は、炭素数１～２０の１価の鎖状炭化水素基又は炭素数６～２０の１価の芳香族炭化水素基が好ましく、炭素数１～２０の１価の鎖状炭化水素基がより好ましい。
　Ｌで表される２価の連結基としては、例えば炭素数１～２０の２価の有機基等が挙げられる。炭素数１～２０の２価の有機基としては、例えば上述のＲ１で表される炭素数１～２０の１価の有機基として例示した１価の有機基から１個の水素原子を除いた基等が挙げられる。
　Ｌとしては、炭素数１～２０の２価の炭化水素基が好ましく、炭素数１～２０の２価の鎖状炭化水素基がより好ましく、炭素数１～２０のアルカンジイル基がさらに好ましい。Ｌで表される基の炭素数としては、１～１２が好ましく、１～６がより好ましい。Ｌで表される基のより好ましい形態としては、－（ＣＨ２）ｍ－（ｍは、１から６の整数である。）で表される基が挙げられる。
　式（１）中のＸにおけるエーテル結合を有する有機基としては、例えばｔ－ブトキシメチル基、ｔ－ブトキシエチル基、アセタール構造を有する有機基が挙げられる。
　ａとしては、１又は２が好ましく、１がより好ましい。
　構造単位（Ｉ）としては、例えば下記式（１－１）～（１－１０）で表される化合物に由来する構造単位等が挙げられる。
Figure JPOXMLDOC01-appb-C000006
　［Ａ］化合物における構造単位（Ｉ）の含有割合の下限としては、［Ａ］化合物を構成する全構造単位に対して、０．１モル％が好ましく、１モル％がより好ましく、２モル％がさらに好ましく、３モル％がよりさらに好ましい。また、構造単位（Ｉ）の含有割合の上限としては、８０モル％が好ましく、５０モル％がより好ましく、２０モル％がさらに好ましい。構造単位（Ｉ）の含有割合が上記範囲であることにより、レジスト下層膜上に電子線又は極端紫外線リソグラフィーによりレジストパターンを形成する際に、断面形状の矩形性がより優れ、倒壊し難い、微細なレジストパターンを形成することができる。
（構造単位（ＩＩ））
　構造単位（ＩＩ）は、下記式（２）で表される構造単位である。［Ａ］化合物が構造単位（ＩＩ）を有する場合、当該レジスト下層膜形成用組成物により形成されるレジスト下層膜の酸素ガスエッチング耐性を向上させることができる。［Ａ］化合物は、１種又は２種以上の構造単位（ＩＩ）を有することができる。
Figure JPOXMLDOC01-appb-C000007
　上記式（２）中、Ｒ５は、置換若しくは非置換の炭素数１～２０の１価のアルコキシ基、ヒドロキシ基、又はハロゲン原子である。ｃは、０～３の整数である。ｃが２以上の場合、複数のＲ５は同一又は異なる。
　Ｒ５で表される置換若しくは非置換の炭素数１～２０の１価のアルコキシ基としては、例えばメトキシ基、エトキシ基、プロポキシ基等が挙げられる。
　Ｒ５で表されるハロゲン原子としては、例えばフッ素原子、塩素原子、臭素原子、ヨウ素原子が挙げられる。
　Ｒ５としては、置換若しくは非置換の炭素数１～２０の１価のアルコキシ基が好ましく、メトキシ基、エトキシ基がより好ましい。
　ｃとしては、１又は２が好ましい。
　［Ａ］化合物が他の構造単位として構造単位（ＩＩ）を有する場合、構造単位（ＩＩ）の含有割合の下限としては、［Ａ］化合物を構成する全構造単位に対して、３０モル％が好ましく、４０モル％がより好ましく、５０モル％、６０モル％又は７０モル％がさらに好ましい場合もある。上記含有割合の上限としては、９５モル％が好ましく、９０モル％がより好ましく、８５モル％がさらに好ましい。
（構造単位（ＩＩＩ））
　構造単位（ＩＩＩ）は、下記式（３）で表される構造単位である。［Ａ］化合物が構造単位（ＩＩＩ）を有する場合、当該レジスト下層膜形成用組成物の保存安定性及び塗工性を向上させることができる。［Ａ］化合物は、１種又は２種以上の構造単位（ＩＩＩ）を有することができる。
Figure JPOXMLDOC01-appb-C000008
　上記式（３）中、Ｒ６は、置換又は非置換の炭素数１～２０の１価の炭化水素基である。ｄは、１～３の整数である。ｄが２の場合、２のＲ６は、同一又は異なる。Ｒ７は、置換若しくは非置換の炭素数１～２０の１価の有機基、ヒドロキシ基、又は、ハロゲン原子である。ｅは、０～２の整数である。ｅが複数の場合、複数のＲ３は、同一又は異なる。ただし、ｄ＋ｅは３以下である。
　Ｒ６で表される置換又は非置換の炭素数１～２０の１価の炭化水素基としては、例えば上述のＲ１で表される炭素数１～２０の１価の炭化水素基として例示した基と同様の基等が挙げられる。
　ｄとしては、１が好ましい。
　Ｒ７で表されるハロゲン原子としては、フッ素原子、塩素原子、臭素原子、ヨウ素原子が挙げられる。
　Ｒ７としては、置換若しくは非置換の炭素数１～２０の１価のアルコキシ基が好ましく、メトキシ基、エトキシ基がより好ましい。
　ｅとしては、０又は１が好ましい。
　［Ａ］化合物が他の構造単位として構造単位（ＩＩＩ）を有する場合、構造単位（ＩＩＩ）の含有割合の下限としては、［Ａ］化合物を構成する全構造単位に対して、０．１モル％が好ましく、１モル％がより好ましく、２モル％、３モル％又は５モル％がさらに好ましい場合もある。上記含有割合の上限としては、４０モル％が好ましく、３０モル％がより好ましく、２０モル％がさらに好ましい。
　［Ａ］化合物を構成する全構造単位に対する構造単位（Ｉ）、構造単位（ＩＩ）及び構造単位（ＩＩＩ）の合計含有割合の下限としては、８０モル％が好ましく、９０モル％がより好ましく、９５モル％又は９９モル％がさらに好ましい場合もある。上記合計含有割合の上限は１００モル％であってよい。
　当該レジスト下層膜形成用組成物における［Ａ］化合物の含有割合の下限としては、当該レジスト下層膜形成用組成物に含まれる全成分に対して、０．１質量％が好ましく、０．３質量％がより好ましく、０．５質量％がさらに好ましい。上記含有割合の上限としては、１０質量％が好ましく、５質量％がより好ましく、３質量％がさらに好ましく、２質量％がよりさらに好ましい。
　［Ａ］化合物は、重合体の形態であることが好ましい。本明細書において「重合体」とは、２以上の構造単位を有する化合物をいい、重合体において同一の構造単位が２以上連続する場合、この構造単位を「繰り返し単位」ともいう。［Ａ］化合物が重合体の形態である場合、［Ａ］化合物のゲルパーミエーションクロマトグラフィー（ＧＰＣ）によるポリスチレン換算重量平均分子量（Ｍｗ）の下限としては、１，０００が好ましく、１，２００がより好ましく、１，５００がさらに好ましい。上記Ｍｗの上限としては、１０，０００が好ましく、５，０００がより好ましく、３，０００がさらに好ましい。
　なお、本明細書において［Ａ］化合物のＭｗは、東ソー（株）のＧＰＣカラム（「Ｇ２０００ＨＸＬ」２本、「Ｇ３０００ＨＸＬ」１本及び「Ｇ４０００ＨＸＬ」１本）を使用し、以下の条件によるゲルパーミエーションクロマトグラフィー（ＧＰＣ）により測定される値である。
　溶離液：テトラヒドロフラン
　流量：１．０ｍＬ／分
　試料濃度：１．０質量％
　試料注入量：１００μＬ
　カラム温度：４０℃
　検出器：示差屈折計
　標準物質：単分散ポリスチレン
　［Ａ］化合物は、各構造単位を与える単量体を用い、常法により合成することができる。例えば構造単位（Ｉ）を与える単量体及び必要に応じて他の構造単位を与える単量体をシュウ酸等の触媒及び水の存在下、溶媒中で加水分解縮合させることにより合成することができる。加水分解縮合反応等により、各単量体は種類に関係なく［Ａ］化合物中に取り込まれると考えられる。したがって、合成された［Ａ］化合物における構造単位（Ｉ）及び他の構造単位の含有割合は、通常、合成反応に用いた各単量体の仕込み量の割合と同等になる。
［［Ｂ］溶媒］
　［Ｂ］溶媒としては特に制限されず、例えばアルコール系溶媒、ケトン系溶媒、エーテル系溶媒、エステル系溶媒、含窒素系溶媒等が挙げられる。［Ｂ］溶媒は、通常、有機溶媒である。当該レジスト下層膜形成用組成物は、１種又は２種以上の［Ｂ］溶媒を含有することができる。
　アルコール系溶媒としては、例えばメタノール、エタノール、ｎ－プロパノール、ｉｓｏ－プロパノール、ｎ－ブタノール、ｉｓｏ－ブタノール等のモノアルコール系溶媒、エチレングリコール、１，２－プロピレングリコール、ジエチレングリコール、ジプロピレングリコール等の多価アルコール系溶媒などが挙げられる。
　ケトン系溶媒としては、例えばアセトン、メチルエチルケトン、メチル－ｎ－プロピルケトン、メチル－ｉｓｏ－ブチルケトン、シクロヘキサノン、２－ヘプタノン等が挙げられる。
　エーテル系溶媒としては、例えばエチルエーテル、ｉｓｏ－プロピルエーテル、エチレングリコールジブチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールジエチルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノプロピルエーテル、テトラヒドロフラン等が挙げられる。
　エステル系溶媒としては、例えば酢酸エチル、γ－ブチロラクトン、酢酸ｎ－ブチル、酢酸エチレングリコールモノメチルエーテル、酢酸エチレングリコールモノエチルエーテル、酢酸ジエチレングリコールモノメチルエーテル、酢酸ジエチレングリコールモノエチルエーテル、酢酸プロピレングリコールモノメチルエーテル、酢酸プロピレングリコールモノエチルエーテル、酢酸ジプロピレングリコールモノメチルエーテル、酢酸ジプロピレングリコールモノエチルエーテル、プロピオン酸エチル、プロピオン酸ｎ－ブチル、乳酸メチル、乳酸エチル等が挙げられる。
　含窒素系溶媒としては、例えばＮ，Ｎ－ジメチルホルムアミド、Ｎ，Ｎ－ジメチルアセトアミド、Ｎ－メチルピロリドン等が挙げられる。
　これらの中でも、エーテル系溶媒又はエステル系溶媒が好ましく、成膜性に優れるため、グリコール構造を有するエーテル系溶媒又はグリコール構造を有するエステル系溶媒がより好ましい。
　グリコール構造を有するエーテル系溶媒及びグリコール構造を有するエステル系溶媒としては、例えばプロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノプロピルエーテル、酢酸プロピレングリコールモノメチルエーテル、酢酸プロピレングリコールモノエチルエーテル、酢酸プロピレングリコールモノプロピルエーテル等が挙げられる。これらの中でも、酢酸プロピレングリコールモノメチルエーテル又はプロピレングリコールモノエチルエーテルが好ましい。
　当該レジスト下層膜形成用組成物における［Ｂ］溶媒の含有割合の下限としては、当該レジスト下層膜形成用組成物に含まれる全成分に対して、９０質量％が好ましく、９２．５質量％がより好ましく、９５質量％がさらに好ましい。上記含有割合の上限としては、９９．９質量％が好ましく、９９．５質量％がより好ましく、９９質量％がさらに好ましい。
［［Ｃ］添加剤］
　［Ｃ］添加剤としては、例えば酸発生剤、塩基性化合物（塩基発生剤を含む）、ラジカル発生剤、界面活性剤、コロイド状シリカ、コロイド状アルミナ、有機ポリマー、水等が挙げられる。当該レジスト下層膜形成用組成物は、１種又は２種以上の［Ｃ］添加剤を含有することができる。
　当該レジスト下層膜形成用組成物が［Ｃ］添加剤を含有する場合、当該レジスト下層膜形成用組成物における［Ｃ］添加剤の含有割合としては、用いる［Ｃ］添加剤の種類に応じて、また本発明の効果を損なわない範囲において適宜決定することができる。
＜レジスト下層膜形成用組成物の調製方法＞
　当該レジスト下層膜形成用組成物の調製方法としては特に限定されず、常法に従って調製することができる。例えば［Ａ］化合物の溶液と、［Ｂ］溶媒と、必要に応じて［Ｃ］添加剤とを所定の割合で混合し、好ましくは得られた混合溶液を孔径０．２μｍ以下のフィルター等でろ過することにより調製することができる。
＜半導体基板の製造方法＞
　当該半導体基板の製造方法は、基板に直接又は間接にレジスト下層膜形成用組成物を塗工する工程（以下、「レジスト下層膜形成用組成物塗工工程」ともいう。）と、上記レジスト下層膜形成用組成物塗工工程により形成されたレジスト下層膜に直接又は間接に金属含有レジスト膜形成用組成物を塗工する工程（以下、「金属含有レジスト膜形成用組成物塗工工程」ともいう）と、上記金属含有レジスト膜形成用組成物塗工工程により形成された金属含有レジスト膜を電子線又は極端紫外線により露光する工程（以下、「露光工程」ともいう）と、上記露光された金属含有レジスト膜を現像する工程（以下、「現像工程」ともいう）とを備える。当該半導体基板の製造方法では、レジスト下層膜形成用組成物として上述の当該レジスト下層膜形成用組成物を用いる。
　当該半導体基板の製造方法は、必要に応じて、上記レジスト下層膜形成用組成物塗工工程後、金属含有レジスト膜形成用組成物塗工工程前に、上記レジスト下層膜形成用組成物塗工工程により形成された塗工膜を加熱する工程（以下、「加熱工程」ともいう。）をさらに備えていてもよい。
　当該半導体基板の製造方法は、必要に応じて、上記レジスト下層膜形成用組成物塗工工程前に、上記基板に直接又は間接に有機下層膜を形成する工程（以下、「有機下層膜形成工程」ともいう）をさらに備えていてもよい。
　また、当該半導体基板の製造方法は、現像工程後、形成されたレジストパターン等をマスクとしてエッチングを行う工程（以下、「エッチング工程」ともいう）を備えていてよい。このエッチング工程により、基板自体に微細なパターンが形成される。
　当該半導体基板の製造方法によれば、レジスト下層膜の形成に上述の当該レジスト下層膜形成用組成物を用い、電子線又は極端紫外線による露光を行うため、金属含有レジスト下層膜上に微細なレジストパターンを形成することができる。従って、当該半導体基板の製造方法によれば、微細なパターンが形成された半導体基板を効率的に製造することができる。なお、当該製造方法における「半導体基板」とは、半導体デバイス（半導体素子）に用いられる基板をいい、材質が半導体である基板に限定されるものではない。
　当該製造方法において形成されるレジストパターン及び基板パターン（基板に形成されたパターン）のサイズは、例えば線幅１００ｎｍ以下、５０ｎｍ以下、３０ｎｍ以下、２０ｎｍ以下又は１５ｎｍ以下の部分を有するものであることが好ましい。形成されるレジストパターンの最小の線幅は例えば２ｎｍ、５ｎｍ又は１０ｎｍであってよい。
　以下、当該半導体基板の製造方法が備える各工程について説明する。
［有機下層膜形成工程］
　本工程では、後述するレジスト下層膜形成用組成物塗工工程前に、後述する基板に直接又は間接に有機下層膜を形成する。本工程は、任意の工程である。本工程により、基板に直接又は間接に有機下層膜が形成される。なお、「上記レジスト下層膜形成用組成物塗工工程前」とは、レジスト下層膜形成用組成物塗工工程の直前のみを意味するのではなく、レジスト下層膜形成用組成物塗工工程よりも川上の時点を意味する。したがって、本工程とレジスト下層膜形成用組成物塗工工程との間にその他の任意の工程を備えていてもよい。
　有機下層膜は、例えば有機下層膜形成用組成物の塗工等により形成することができる。有機下層膜を有機下層膜形成用組成物の塗工により形成する方法としては、例えば有機下層膜形成用組成物を基板に直接又は間接に塗工して形成された塗工膜を加熱や露光を行うことにより硬化等させる方法等が挙げられる。上記有機下層膜形成用組成物としては、例えばＪＳＲ（株）の「ＨＭ８００６」等を用いることができる。加熱や露光の諸条件については、用いる有機下層膜形成用組成物の種類等に応じて適宜決定することができる。
　基板に間接に有機下層膜を形成する場合としては、例えば基板上に形成された低誘電絶縁膜上に有機下層膜を形成する場合等が挙げられる。
［レジスト下層膜形成用組成物塗工工程］
　本工程では、基板に直接又は間接にレジスト下層膜形成用組成物を塗工する。本工程により、基板上に直接又は間接にレジスト下層膜形成用組成物の塗工膜が形成される。本工程では、レジスト下層膜形成用組成物として上述の当該レジスト下層膜形成用組成物を用いる。
　基板としては、例えば酸化シリコン、窒化シリコン、酸窒化シリコン、ポリシロキサン等の絶縁膜、樹脂基板などが挙げられる。また、基板としては、配線溝（トレンチ）、プラグ溝（ビア）等のパターニングが施された基板であってもよい。
　レジスト下層膜形成用組成物の塗工方法としては特に制限されず、例えば回転塗工法等が挙げられる。
　基板に間接にレジスト下層膜形成用組成物を塗工する場合としては、例えば基板上に形成された他の膜上にレジスト下層膜形成用組成物を塗工する場合等が挙げられる。基板上に形成された他の膜としては、例えば上述の有機下層膜形成工程により形成される有機下層膜、反射防止膜、低誘電体絶縁膜等が挙げられる。
［加熱工程］
　本工程では、上記レジスト下層膜形成用組成物塗工工程後、後述する金属含有レジスト膜形成用組成物塗工工程前に、上記レジスト下層膜形成用組成物塗工工程により形成された塗工膜を加熱する。この加熱により、塗工膜が硬化することなどにより、レジスト下層膜が形成される。
　塗工膜の加熱を行う際の雰囲気としては特に制限されず、例えば大気下、窒素雰囲気下等が挙げられる。通常、塗工膜の加熱は大気下で行われる。塗工膜の加熱を行う場合の加熱温度、加熱時間等の諸条件については適宜決定することができる。加熱温度の下限としては、例えば１５０℃であってよいが、２００℃が好ましく、２１０℃又は２２０℃がより好ましい。加熱温度を上記下限以上とすることで、アミノ基を十分に生じさせることができる。加熱温度の上限としては、５５０℃が好ましく、４５０℃がより好ましく、３００℃がさらに好ましい。加熱時間の下限としては、１５秒が好ましく、３０秒がより好ましい。加熱時間の上限としては、１，２００秒が好ましく、６００秒がより好ましい。
　レジスト下層膜形成用組成物が［Ｃ］添加剤として酸発生剤を含有し、この酸発生剤が露光により酸を発生する酸発生剤である場合には、加熱と露光とを組み合わせることにより、レジスト下層膜の形成を促進させることができる。また、酸発生剤が加熱により酸を発生する酸発生剤である場合には、上記加熱により酸が発生し、硬化反応を促進させることができる。
　本工程により形成されるレジスト下層膜の平均厚みの下限としては、１ｎｍが好ましく、３ｎｍがより好ましく、５ｎｍがさらに好ましい。上記平均厚みの上限としては、３００ｎｍが好ましく、１００ｎｍがより好ましく、５０ｎｍがさらに好ましく、２０ｎｍがよりさらに好ましい。
［金属含有レジスト膜形成用組成物塗工工程］
　本工程では、上記工程により形成されたレジスト下層膜に直接又は間接に金属含有レジスト膜形成用組成物を塗工する。本工程により、レジスト下層膜上に直接又は間接に金属含有レジスト膜が形成される。
　金属含有レジスト膜形成用組成物の塗工方法としては特に制限されず、例えば回転塗工法等が挙げられる。
　本工程をより詳細に説明すると、例えば形成される金属含有レジスト膜が所定の厚みとなるようにレジスト組成物を塗工した後、プレベーク（以下、「ＰＢ」ともいう）することによって塗工膜中の溶媒を揮発させることにより、金属含有レジスト膜を形成する。
　ＰＢ温度及びＰＢ時間は、使用される金属含有レジスト膜形成用組成物の種類等に応じて適宜決定することができる。ＰＢ温度の下限としては、３０℃が好ましく、５０℃がより好ましい。ＰＢ温度の上限としては、２００℃が好ましく、１５０℃がより好ましい。ＰＢ時間の下限としては、１０秒が好ましく、３０秒がより好ましい。ＰＢ時間の上限としては、６００秒が好ましく、３００秒がより好ましい。
　本工程において用いる金属含有レジスト膜形成用組成物としては、金属原子を含む化合物（以下、「［Ｐ］金属含有化合物」ともいう）を含有する金属含有レジスト膜形成用組成物等が挙げられる。
［金属含有レジスト膜形成用組成物］
　金属含有レジスト膜形成用組成物は、［Ｐ］金属含有化合物を固形分換算で５０質量％以上含有する。金属含有レジスト膜形成用組成物は、［Ｑ］溶媒をさらに含有することが好ましく、その他の成分をさらに含有してもよい。金属含有レジスト膜形成用組成物は、［Ｐ］金属含有化合物を固形分換算で５０質量％以上含有するため、エッチング耐性に優れるレジスト膜を形成できる。
（［Ｐ］金属含有化合物）
　［Ｐ］金属含有化合物は、金属原子を含有する化合物である。［Ｐ］金属含有化合物は、１種単独で又は２種以上を組み合わせて用いることができる。また、［Ｐ］金属含有化合物を構成する金属原子は、１種単独で又は２種以上を組み合わせて用いることができる。ここで「金属原子」とは、半金属、すなわちホウ素、ケイ素、ゲルマニウム、ヒ素、アンチモン及びテルルを含む概念である。
　［Ｐ］金属含有化合物を構成する金属原子としては、特に限定されず、例えば第３族～第１６族の金属原子等が挙げられる。上記金属原子の具体例としては、例えばチタン、ジルコニウム、ハフニウム等の第４族の金属原子、タンタル等の第５族の金属原子、クロム、タングステン等の第６族の金属原子、鉄、ルテニウム等の第８族の金属原子、コバルト等の第９族の金属原子、ニッケル等の第１０族の金属原子、銅等の第１１族の金属原子、亜鉛、カドミウム、水銀等の第１２族の金属原子、ホウ素、アルミニウム、ガリウム、インジウム、タリウム等の第１３族の金属原子、ゲルマニウム、スズ、鉛等の第１４族の金属原子、アンチモン、ビスマス等の第１５族の金属原子、テルル等の第１６族の金属原子などが挙げられる。
　［Ｐ］金属含有化合物を構成する金属原子は、周期表において第４族、第１２族又は第１４族に属し、かつ第４周期、第５周期又は第６周期に属する第１金属原子を含むとよい。すなわち、上記金属原子は、チタン、ジルコニウム、ハフニウム、亜鉛、カドミウム、水銀、ゲルマニウム、スズ及び鉛のうち少なくとも１種を含むとよい。このように、［Ｐ］金属含有化合物が第１金属原子を含むことで、レジスト膜の露光部における二次電子の放出や、この二次電子等による［Ｐ］金属含有化合物の現像液に対する溶解性の変化がより促進される。その結果、パターン倒れをより確実に抑制することができる。第１金属原子としては、スズ又はジルコニウムが好ましい。
　［Ｐ］金属含有化合物は、金属原子以外の他の原子をさらに有することが好ましい。上記他の原子としては、例えば炭素原子、水素原子、酸素原子、窒素原子、リン原子、硫黄原子、ハロゲン原子等が挙げられ、これらの中で炭素原子、水素原子及び酸素原子が好ましい。［Ｐ］金属含有化合物における他の原子は、１種単独で又は２種以上を組み合わせて用いることができる。
　レジスト膜形成用感放射線性組成物における［Ｐ］金属含有化合物の固形分換算での含有量の下限としては、７０質量％が好ましく、９０質量％がより好ましく、９５質量％がさらに好ましい。また、上記含有量は、１００質量％であってもよい。ここで、レジスト膜形成用感放射線性組成物における固形分とは、後述する［Ｑ］溶媒以外の成分をいう。
（［Ｐ］金属含有化合物の合成方法）
　［Ｐ］金属含有化合物は、例えば金属原子及び加水分解性基を有する金属化合物、この金属化合物の加水分解物、上記金属化合物の加水分解縮合物又はこれらの組み合わせに対し、加水分解縮合反応、配位子交換反応等を行う方法により得ることができる。上記金属化合物は、１種単独で又は２種以上組み合わせて使用できる。
　［Ｐ］金属含有化合物としては、下記式（４）で表される金属原子及び加水分解性基を有する金属化合物（以下、「金属化合物（１）」ともいう）に由来するものが好ましい。このような金属化合物（１）を用いることで、安定な［Ｐ］金属含有化合物を得ることができる。
Figure JPOXMLDOC01-appb-C000009
　上記式（４）中、Ｍは、金属原子である。Ｌ１は、配位子又は炭素数１～２０の１価の有機基である。ａ１は、０～６の整数である。ａ１が２以上の場合、複数のＬ１は同一でも異なっていてもよい。Ｙは、１価の加水分解性基である。ｂ１は、２～６の整数である。複数のＹは同一でも異なっていてもよい。なお、Ｌ１はＹに該当しない配位子又は有機基である。
　Ｍで表される金属原子としては、第１金属原子が好ましく、スズがより好ましい。
　Ｙで表される加水分解性基としては、Ｍで表される金属原子にあわせて適宜変更可能であるが、例えば置換又は非置換のエチニル基、ハロゲン原子、アルコキシ基、アシロキシ基、置換又は非置換のアミノ基等が挙げられる。
　Ｙで表される置換又は非置換のエチニル基、及び置換又は非置換のアミノ基における置換基としては、炭素数１～２０の１価の炭化水素基が好ましく、鎖状炭化水素基がより好ましく、アルキル基がさらに好ましい。
　Ｙで表されるハロゲン原子としては、例えばフッ素原子、塩素原子、臭素原子、ヨウ素原子等が挙げられる。これらの中で、塩素原子が好ましい。
　Ｙで表されるアルコキシ基としては、例えばメトキシ基、エトキシ基、ｎ－プロポキシ基、ｉ－プロポキシ基、ｎ－ブトキシ基等が挙げられる。これらの中で、エトキシ基、ｉ－プロポキシ基、ｎ－ブトキシ基が好ましい。
　Ｙで表されるアシロキシ基としては、例えばホルミル基、アセトキシ基、エチリルオキシ基、プロピオニルオキシ基、ｎ－ブチリルオキシ基、ｔ－ブチリルオキシ基、ｔ－アミリルオキシ基、ｎ－ヘキサンカルボニロキシ基、ｎ－オクタンカルボニロキシ基等が挙げられる。これらの中で、アセトキシ基が好ましい。
　Ｙで表される置換又は非置換のアミノ基としては、例えばアミノ基、メチルアミノ基、ジメチルアミノ基、ジエチルアミノ基、ジプロピルアミノ基等が挙げられる。これらの中で、ジメチルアミノ基及びジエチルアミノ基が好ましい。
　以下、Ｍで表される金属原子と、Ｙで表される加水分解性基との好適な組み合わせを説明する。Ｍで表される金属原子がスズである場合、Ｙで表される加水分解性基としては、置換又は非置換のエチニル基、ハロゲン原子、アルコキシ基、アシロキシ基及び置換又は非置換のアミノ基が好ましく、ハロゲン原子がより好ましい。Ｍで表される金属原子がゲルマニウムである場合、Ｙで表される加水分解性基としては、ハロゲン原子、アルコキシ基、アシロキシ基、及び置換又は非置換のアミノ基が好ましい。Ｍで表される金属原子がハフニウム、ジルコニウム及びチタンである場合、Ｙで表される加水分解性基としては、ハロゲン原子、アルコキシ基及びアシロキシ基が好ましい。
　Ｌ１で表される配位子としては、単座配位子及び多座配位子が挙げられる。
　上記単座配位子としては、例えばヒドロキソ配位子、ニトロ配位子、アンモニア等が挙げられる。
　上記多座配位子としては、例えばヒドロキシ酸エステル、β－ジケトン、β－ケトエステル、α位の炭素原子が置換されていてもよいマロン酸ジエステル及びπ結合を有する炭化水素、又はこれらの化合物に由来する配位子や、ジホスフィン等が挙げられる。
　上記ジホスフィンとしては、例えば１，１－ビス（ジフェニルホスフィノ）メタン、１，２－ビス（ジフェニルホスフィノ）エタン、１，３－ビス（ジフェニルホスフィノ）プロパン、２，２’－ビス（ジフェニルホスフィノ）－１，１’－ビナフチル、１，１’－ビス（ジフェニルホスフィノ）フェロセン等が挙げられる。
　Ｌ１で表される１価の有機基としては、例えば上記式（１）においてＲ１で表される炭素数１～２０の１価の有機基として例示した基と同様のもの等が挙げられる。Ｌ１で表される１価の有機基の炭素数の下限としては、２が好ましく、３がより好ましい。一方、上記炭素数の上限としては、１０が好ましく、５がより好ましい。Ｌ１で表される１価の有機基としては、置換又は非置換の炭化水素基が好ましく、置換若しくは非置換の鎖状炭化水素基又は置換若しくは非置換の芳香族炭化水素基がより好ましく、置換若しくは非置換のアルキル基又は置換若しくは非置換のアラルキル基がさらに好ましく、ｉ－プロピル基又はベンジル基基が特に好ましい。
　ａ１としては、１及び２が好ましく、１がより好ましい。
　ｂ１としては、２～４の整数が好ましい。ｂ１を上記数値とすることで、［Ｐ］金属含有化合物における金属原子の含有割合を高め、［Ｐ］金属含有化合物による二次電子の発生をより効果的に促進できる。その結果、パターン倒れをより確実に抑制することができる。
　金属化合物（１）としては、ハロゲン化金属化合物が好ましく、イソプロピルスズ三塩化物又はベンジルスズ三塩化物がより好ましい。
　金属化合物（１）に対して加水分解縮合反応を行う方法としては、例えば必要に応じて用いられるテトラメチルアンモニウムヒドロキシド等の塩基存在下、水、又は水を含む溶媒中で金属化合物（１）を撹拌する方法等が挙げられる。この場合、必要に応じて加水分解性基を有する他の化合物を添加してもよい。この加水分解縮合反応に用いる水の量の下限としては、金属化合物（１）等が有する加水分解性基に対し、０．２倍モルが好ましく、１倍モルがより好ましく、３倍モルがさらに好ましい。加水分解縮合反応における水の量を上記範囲とすることで、容易かつ確実に［Ｐ］金属含有化合物を得ることができる。
　［Ｐ］金属含有化合物の合成反応の際、金属化合物（１）以外にも、上記式（４）の化合物におけるＬ１で表される多座配位子になり得る化合物や架橋配位子になり得る化合物等を添加してもよい。上記架橋配位子になり得る化合物としては、例えばヒドロキシ基、イソシアネート基、アミノ基、エステル基、アミド基等の配位可能な基を２以上有する化合物等が挙げられる。
　［Ｐ］金属含有化合物の合成反応の温度の下限としては、０℃が好ましく、１０℃がより好ましい。上記温度の上限としては、１５０℃が好ましく、１００℃がより好ましく、５０℃がさらに好ましい。
　［Ｐ］金属含有化合物の合成反応の時間の下限としては、１分が好ましく、１０分がより好ましく、１時間がさらに好ましい。上記時間の上限としては、１００時間が好ましく、５０時間がより好ましく、２４時間がさらに好ましく、４時間が特に好ましい。
（［Ｑ］溶媒）
　［Ｑ］溶媒としては、有機溶媒が好ましい。この有機溶媒の具体例としては、例えば上述のレジスト下層膜形成用組成物において［Ｂ］溶媒として例示したものと同様のもの等が挙げられる。
　［Ｑ］溶媒としては、アルコール系溶媒が好ましく、モノアルコール系溶媒がより好ましく、４－メチル－２－ペンタノールがさらに好ましい。
［その他の任意成分］
　レジスト膜形成用感放射線性組成物は、［Ｐ］金属含有化合物及び［Ｑ］溶媒以外にも、配位子となり得る化合物、界面活性剤等のその他の任意成分を含有してもよい。
［配位子となり得る化合物］
　上記配位子となり得る化合物としては、例えば多座配位子又は架橋配位子となり得る化合物等が挙げられ、具体的には［Ｐ］金属含有化合物の合成方法において例示した多座配位子又は架橋配位子となり得る化合物と同様のもの等が挙げられる。
［界面活性剤］
　界面活性剤は塗布性、ストリエーション等を改良する作用を示す成分である。界面活性剤としては、例えばポリオキシエチレンラウリルエーテル、ポリオキシエチレンステアリルエーテル、ポリオキシエチレンオレイルエーテル、ポリオキシエチレンｎ－オクチルフェニルエーテル、ポリオキシエチレンｎ－ノニルフェニルエーテル、ポリエチレングリコールジラウレート、ポリエチレングリコールジステアレート等のノニオン系界面活性剤の他、以下商品名として、ＫＰ３４１（信越化学工業社）、ポリフローＮｏ．７５、同Ｎｏ．９５（以上、共栄社化学社）、エフトップＥＦ３０１、同ＥＦ３０３、同ＥＦ３５２（以上、トーケムプロダクツ社）、メガファックＦ１７１、同Ｆ１７３（以上、大日本インキ化学工業社）、フロラードＦＣ４３０、同ＦＣ４３１（以上、住友スリーエム社）、アサヒガードＡＧ７１０、サーフロンＳ－３８２、同ＳＣ－１０１、同ＳＣ－１０２、同ＳＣ－１０３、同ＳＣ－１０４、同ＳＣ－１０５、同ＳＣ－１０６（以上、旭硝子社）等が挙げられる。
（レジスト膜形成用感放射線性組成物の調製方法）
　レジスト膜形成用感放射線性組成物は、例えば［Ｐ］金属含有化合物と、必要に応じて［Ｑ］溶媒等のその他の任意成分とを所定の割合で混合し、好ましくは、得られた混合物を孔径０．２μｍ程度のメンブランフィルターで濾過することにより調製できる。レジスト膜形成用感放射線性組成物が［Ｑ］溶媒を含有する場合、レジスト膜形成用感放射線性組成物の固形分濃度の下限としては、０．１質量％が好ましく、０．５質量％がより好ましく、１質量％がさらに好ましく、２質量％が特に好ましい。一方、上記固形分濃度の上限としては、５０質量％が好ましく、３０質量％がより好ましく、１５質量％がさらに好ましく、４質量％が特に好ましい。
［露光工程］
　本工程では、上記金属含有レジスト膜形成用組成物塗工工程により形成された金属含有レジスト膜を電子線又は極端紫外線（波長１３．５ｎｍ等、「ＥＵＶ」ともいう）により露光する。具体的には、例えば所定のパターンを有するマスクを介して、電子線又は極端紫外線を金属含有レジスト膜に照射する。本工程により、金属含有レジスト膜における露光部と非露光部との間で現像液への溶解性に差異が生じる。露光条件は、用いる金属含有レジスト膜形成用組成物の種類等に応じて適宜決定することができる。
　本工程では、上記露光後、解像度、パターンプロファイル、現像性等の金属含有レジスト膜の性能を向上させるために、ポストエクスポージャーベーク（以下、「ＰＥＢ」ともいう）を行うことができる。ＰＥＢ温度及びＰＥＢ時間としては、使用される金属含有レジスト膜形成用組成物の種類等に応じて適宜決定することができる。ＰＥＢ温度の下限としては、５０℃が好ましく、７０℃がより好ましい。ＰＥＢ温度の上限としては、２００℃が好ましく、１５０℃がより好ましい。ＰＥＢ時間の下限としては、１０秒が好ましく、３０秒がより好ましい。ＰＥＢ時間の上限としては、６００秒が好ましく、３００秒がより好ましい。
［現像工程］
　本工程では、上記露光された金属含有レジスト膜を現像する。この現像に用いる現像液としては、アルカリ水溶液（アルカリ現像液）、有機溶媒含有液（有機溶媒現像液）等が挙げられる。例えばアルカリ現像液を用いたポジ型の場合、金属含有レジスト膜における露光部のアルカリ水溶液への溶解性が高まっていることから、アルカリ現像を行うことで露光部が除去されることにより、ポジ型のレジストパターンが形成される。また、有機溶媒現像液を用いたネガ型の場合、金属含有レジスト膜における露光部の有機溶媒への溶解性が低下していることから、有機溶媒現像を行うことで有機溶媒への溶解性が相対的に高い非露光部が除去されることにより、ネガ型のレジストパターンが形成される。
　アルカリ水溶液（アルカリ現像液）としては、例えば水酸化ナトリウム、水酸化カリウム、炭酸ナトリウム、けい酸ナトリウム、メタけい酸ナトリウム、アンモニア水、エチルアミン、ｎ－プロピルアミン、ジエチルアミン、ジ－ｎ－プロピルアミン、トリエチルアミン、メチルジエチルアミン、エチルジメチルアミン、トリエタノールアミン、テトラメチルアンモニウムヒドロキシド（ＴＭＡＨ）、ピロール、ピペリジン、コリン、１，８－ジアザビシクロ－［５．４．０］－７－ウンデセン、１，５－ジアザビシクロ－［４．３．０］－５－ノネン等のアルカリ性化合物の少なくとも１種を溶解したアルカリ性水溶液等が挙げられる。
　アルカリ水溶液におけるアルカリ性化合物の含有割合の下限としては、０．１質量％が好ましく、０．５質量％がより好ましく、１質量％がさらに好ましい。上記含有割合の上限としては、２０質量％が好ましく、１０質量％がより好ましく、５質量％がさらに好ましい。
　アルカリ水溶液としては、ＴＭＡＨ水溶液が好ましく、２．３８質量％ＴＭＡＨ水溶液がより好ましい。
　有機溶媒含有液（有機溶媒現像液）が含有する有機溶媒としては、有機溶媒現像に用いられる公知の有機溶媒を用いることができる。例えば、上述の当該レジスト下層膜形成用組成物における［Ｂ］溶媒として例示したものと同様のもの等が挙げられる。
　有機溶媒としては、エステル系溶媒、エーテル系溶媒、アルコール系溶媒、ケトン系溶媒及び／又は炭化水素系溶媒が好ましく、ケトン系溶媒がより好ましく、２－ヘプタノンが特に好ましい。
　有機溶媒含有液における有機溶媒の含有割合の下限としては、８０質量％が好ましく、９０質量％がより好ましく、９５質量％がさらに好ましく、９９質量％が特に好ましい。
　これらの現像液は、１種単独又は２種以上を組み合わせて用いてもよい。なお、現像後は、洗浄し、乾燥することが一般的である。
［エッチング工程］
　本工程は、レジストパターン等をマスクとしてエッチングを行う工程である。エッチングの回数としては１回でも、複数回、すなわちエッチングにより得られるパターンをマスクとして順次エッチングを行ってもよいが、より良好な形状のパターンを得る観点からは、複数回が好ましい。複数回のエッチングを行う場合、例えば、上記有機下層膜を有さない場合はレジスト下層膜、基板の順に順次エッチングし、上記有機下層膜を有する場合はレジスト下層膜、有機下層膜、基板の順に順次エッチングを行う。エッチングの方法としては、ドライエッチング、ウエットエッチング等が挙げられる。これらの中で、基板のパターンの形状をより良好なものとする観点から、ドライエッチングが好ましい。エッチングガスとしては、フッ素系ガス、酸素系ガス等が、マスク及びエッチングされる層の材質に応じて適宜選択される。例えば、レジストパターンをマスクとしたレジスト下層膜（ケイ素含有膜）のドライエッチングには、通常フッ素系ガスが用いられ、これに酸素系ガスと不活性ガスとを混合したものが好適に用いられる。レジスト下層膜（ケイ素含有膜）パターンをマスクとした有機下層膜のドライエッチングには、通常、酸素系ガスが用いられる。有機下層膜パターンをマスクとした基板のドライエッチングには、レジスト下層膜（ケイ素含有膜）のドライエッチングと同様のガス等が用いられる。上記エッチングの後、所定のパターンを有するパターニング基板が得られる。
　以下、実施例を説明する。なお、以下に示す実施例は、本発明の代表的な実施例の一例を示したものであり、これにより本発明の範囲が狭く解釈されることはない。
　本実施例における［Ａ］化合物の重量平均分子量（Ｍｗ）の測定、［Ａ］化合物の溶液中の濃度の測定、及び膜の平均厚みの測定はそれぞれ以下の方法により行った。
［重量平均分子量（Ｍｗ）の測定］
　［Ａ］化合物の重量平均分子量（Ｍｗ）は、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）により、東ソー（株）のＧＰＣカラム（「Ｇ２０００ＨＸＬ」２本、「Ｇ３０００ＨＸＬ」１本及び「Ｇ４０００ＨＸＬ」１本）を使用し以下の条件により測定した。
　溶離液：テトラヒドロフラン
　流量：１．０ｍＬ／分
　試料濃度：１．０質量％
　試料注入量：１００μＬ
　カラム温度：４０℃
　検出器：示差屈折計
　標準物質：単分散ポリスチレン
［［Ａ］化合物の溶液中の濃度］
　［Ａ］化合物の溶液０．５ｇを２５０℃で３０分間焼成して得られた残渣の質量を測定し、この残渣の質量を［Ａ］化合物の溶液の質量で除することにより、［Ａ］化合物の溶液の濃度（単位：質量％）を算出した。
［膜の平均厚み］
　膜の平均厚みは、分光エリプソメータ（Ｊ．Ａ．ＷＯＯＬＬＡＭ社の「Ｍ２０００Ｄ」）を用いて測定した。
＜［Ａ］化合物の合成＞
　［Ａ］化合物の合成に使用した単量体（以下、「単量体（Ｍ－１）～（Ｍ－１３）」ともいう。）を以下に示す。以下の合成例、皮革合成例及び参考合成例においては特に断りのない限り、質量部は使用した単量体の合計質量を１００質量部とした場合の値を意味し、モル％は使用した単量体の合計モル数を１００モル％とした場合の値を意味する。
Figure JPOXMLDOC01-appb-C000010
［合成例１］（化合物（Ａ－１）の合成）
　反応容器において、上記単量体（Ｍ－１）及び単量体（Ｍ－４）（合計１００質量部）をモル比率が９０／１０（モル％）となるようプロピレングリコールモノエチルエーテル５３質量部に溶解し、単量体溶液を調製した。上記反応容器内を５℃とし、撹拌しながら、９．１質量％シュウ酸水溶液４９質量部を２０分間かけて滴下した。滴下終了後、反応容器内を４０℃に加熱し、反応を４時間実施した。反応終了後、水を９８質量部加え、攪拌を１時間実施した。攪拌終了後、反応容器内を３０℃以下に冷却した。冷却した反応溶液にプロピレングリコールモノエチルエーテルを３７５質量部加えた後、エバポレーターを用いて、水、反応により生成したアルコール類及び余剰のプロピレングリコールモノエチルエーテルを除去して、化合物（Ａ－１）のプロピレングリコールモノエチルエーテル溶液を得た。化合物（Ａ－１）のＭｗは１，８００であった。化合物（Ａ－１）の上記プロピレングリコールモノエチルエーテル溶液中の濃度は、１０．０質量％であった。
［合成例２～１２及び比較合成例１～２］（化合物（Ａ－２）～（Ａ－１２）及び化合物（ａ－１）～（ａ－２）の合成）
　下記表１に示す種類及び使用量（モル％）の各単量体を使用した以外は、合成例１と同様にして、化合物（Ａ－２）～（Ａ－１２）及び化合物（ａ－１）～（ａ－２）のプロピレングリコールモノエチルエーテル溶液を得た。得られた［Ａ］化合物のＭｗ及び［Ａ］化合物の上記プロピレングリコールモノエチルエーテル溶液中の濃度（質量％）を下記表１に合わせて示す。下記表１における「－」は、該当する単量体を使用しなかったことを示す。
Figure JPOXMLDOC01-appb-T000011
［参考合成例１］（化合物（ａ－３）の合成）
　窒素置換した反応容器に、マグネシウム１８．６１質量部及びテトラヒドロフラン３５質量部を加え、２０℃で撹拌した。次に、ジブロモメタン、トリクロロメチルシラン及びトリクロロヒドロシラン（合計１００質量部）をモル比率が５０／１５／３５（モル％）となるようテトラヒドロフラン３５５質量部に溶解し、単量体溶液を調製した。反応容器内を２０℃とし、攪拌しながら上記単量体溶液を１時間かけて滴下した。滴下終了時を反応の開始時間とし、４０℃で１時間、その後６０℃で３時間反応させた後、テトラヒドロフラン２１３質量部を添加し、１０℃以下に冷却し、重合反応液を得た。次いで、この重合反応液にトリエチルアミン９６．８４質量部を加えた後、撹拌しながら、メタノール３０．６６質量部を１０分かけて滴下した。滴下終了時を反応の開始時間とし、２０℃で１時間反応させた後、反応液をジイソプロピルエーテル７００質量部中に投入し、析出した塩をろ別した。次に、エバポレーターを用いて、ろ液中のテトラヒドロフラン、余剰のトリエチルアミン及び余剰のメタノールを除去した。得られた残渣をジイソプロピルエーテル１８０質量部中に投入し、析出した塩をろ別し、ろ液にジイソプロピルエーテルを添加することで２２３ｇのポリカルボシラン（ａａ－３）のジイソプロピルエーテル溶液を得た。ポリカルボシラン（ａａ－３）のＭｗは７００であった。
　反応容器に、上記ポリカルボシラン（ａａ－３）のジイソプロピルエーテル溶液２２３質量部のうち１００質量部及びメタノール９０質量部を加えた。上記反応容器内を３０℃とし、撹拌しながら３．２質量％シュウ酸水溶液８質量部を２０分間かけて滴下した。滴下終了時を反応の開始時間とし、４０℃で４時間反応させた後、反応容器内を３０℃以下に冷却した。次に、この反応容器に、ジイソプロピルエーテル９９質量部及び水１９８質量部を加え、分液抽出を行った後、得られた有機層にシュウ酸二水和物０．２６質量部及び酢酸プロピレングリコールモノメチルエーテル３９６質量部を加え、エバポレーターを用いて、水、ジイソプロピルエーテル、反応により生成したアルコール類及び余剰の酢酸プロピレングリコールモノメチルエーテルを除去した。次いで、得られた溶液に脱水剤としてのオルトギ酸トリメチル１９．８２質量部を加え、４０℃で１時間反応させた後、反応容器内を３０℃以下に冷却した。この反応容器に、酢酸プロピレングリコールモノメチルエーテル９９質量部を加えた後、エバポレーターを用いて、反応により生成したアルコール類、エステル類、オルトギ酸トリメチル及び余剰の酢酸プロピレングリコールモノメチルエーテルを除去し、化合物（ａ－３）の酢酸プロピレングリコールモノメチルエーテル溶液を得た。化合物（ａ－３）のＭｗは２，５００であった。この化合物（ａ－３）の酢酸プロピレングリコールモノメチルエーテル溶液の濃度は５質量％であった。
［参考合成例２］（化合物（ａ－４）の合成）
　上記参考合成例１におけるジブロモメタン、トリクロロメチルシラン及びトリクロロヒドロシラン（モル比率：５０／１５／３５（モル％）、合計１００質量部）をジブロモメタン、テトラクロロシラン、トリクロロメチルシラン及びトリクロロヒドロシラン（モル比率：５０／５／１５／３０（モル％）、合計１００質量部）とした以外は、上記参考合成例１と同様にして、化合物（ａ－４）の酢酸プロピレングリコールモノメチルエーテル溶液を得た。化合物（ａ－４）のＭｗは２，１００であった。この化合物（ａ－４）の酢酸プロピレングリコールモノメチルエーテル溶液の濃度は５質量％であった。
＜レジスト下層膜形成用組成物の調製＞
　レジスト下層膜形成用組成物の調製に用いた［Ｂ］溶媒及び［Ｃ］添加剤について以下に示す。
［［Ｂ］溶媒］
　Ｂ－１：プロピレングリコールモノエチルエーテル
　Ｂ－２：酢酸プロピレングリコールモノメチルエーテル
［［Ｃ］添加剤］
　Ｃ－１：下記式（Ｃ－１）で表される化合物
　Ｃ－２：下記式（Ｃ－２）で表される化合物
　Ｃ－３：下記式（Ｃ－３）で表される化合物
Figure JPOXMLDOC01-appb-C000012
［実施例１－１］
　［Ａ］化合物としての（Ａ－１）０．５質量部（但し、溶媒を除く）、［Ｂ］溶媒としての（Ｂ－１）９５．５質量部（［Ａ］化合物の溶液に含まれる溶媒としての（Ｂ－１）も含む）及び水４質量部（［Ａ］化合物の溶液に含まれる水も含む）を混合し、得られた溶液を孔径０．２μｍのＰＴＦＥ（ポリテトラフルオロエチレン）フィルターでろ過して、レジスト下層膜形成用組成物（Ｊ－１）を調製した。
［実施例１－２～１－１４、比較例１－１～１－２及び参考例１－１～１－２］
　下記表２に示す種類及び配合量の各成分を用いた以外は、実施例１と同様に操作して、組成物（Ｊ－２）～（Ｊ－１４）及び（ｊ－１）～（ｊ－４）を調製した。下記表２中の「－」は、該当する成分を使用しなかったことを示す。
Figure JPOXMLDOC01-appb-T000013
＜金属含有レジスト膜形成用組成物の調製＞
［化合物の合成］
　金属含有レジスト膜形成用組成物の調製に用いる化合物（Ｓ－１）～（Ｓ－４）を、以下に示す手順により合成した。
［合成例２－１］（化合物（Ｓ－１）の合成）
　反応容器内において、１５０ｍＬの０．５Ｎ水酸化ナトリウム水溶液を攪拌しながら、イソプロピルスズ三塩化物６．５質量部を添加し、反応を２時間実施した。析出した沈殿物をろ取し、５０質量部の水で２回洗浄した後、乾燥させ、化合物（Ｓ－１）を得た。化合物（Ｓ－１）は、イソプロピルスズ三塩化物の加水分解物の酸化水酸化物生成物（ｉ－ＰｒＳｎＯ（３／２－ｘ／２）（ＯＨ）ｘ（０＜ｘ＜３）を構造単位とする）である。
［合成例２－２］（化合物（Ｓ－２）の合成）
　反応容器内において、１００ｍＬの０．５Ｍ水酸化テトラメチルアンモニウム水溶液を攪拌しながら、ベンジルスズ三塩化物３．１６質量部を添加し、反応を２時間実施した。析出した沈殿物をろ取し、５０質量部の水で２回洗浄した後、乾燥させ、化合物（Ｓ－２）を得た。化合物（Ｓ－２）は、（（ＰｈＣＨ２）ＳｎＯ３／２）で表される構造単位を有する化合物である。
［合成例２－３］（化合物（Ｓ－３）の合成）
　反応容器内において、テトラブトキシスズ（ＩＶ）２０．０質量部、テトラヒドロフラン１００質量部及びメタクリル酸１００質量部を添加し、反応を６５℃で２０分間実施した。次に、水１０．６質量部を１０分間かけて滴下し、反応を６５℃で１８時間実施した。次いで、水１０．６質量部を１０分かけて滴下し、２時間撹拌した。冷却した反応液に水４００質量部を添加し、析出物を得た。得られた析出物を遠心分離した後、アセトン５０質量部に溶解し、水４００質量部を添加し、析出物を得た。得られた析出物を遠心分離した後、乾燥させ、化合物（Ｓ－３）を得た。化合物（Ｓ－３）は、スズの金属酸化物を主成分とし、メタクリル酸を含む粒子である。
［合成例２－４］（化合物（Ｓ－４）の合成）
　反応容器内において、テトライソプロポキシジルコニウム（ＩＶ）２０．０質量部、テトラヒドロフラン１００質量部及びメタクリル酸１００質量部を添加し、反応を６５℃で２０分間実施した。次に、水１０．６質量部を１０分間かけて滴下し、反応を６５℃で１８時間実施した。次いで、水１０．６質量部を１０分かけて滴下し、２時間撹拌した。冷却した反応液に水４００質量部を添加し、析出物を得た。得られた析出物を遠心分離した後、アセトン５０質量部に溶解し、水４００質量部を添加し、析出物を得た。得られた析出物を遠心分離した後、乾燥させ、化合物（Ｓ－４）を得た。化合物（Ｓ－４）は、ジルコニウムの金属酸化物を主成分とし、メタクリル酸を含む粒子である。
［金属含有レジスト膜形成用組成物の調製］
［調製例２－１］
　上記合成した化合物（Ｓ－１）２質量部と、プロピレングリコールモノエチルエーテル９８質量部とを混合し、得られた混合物を活性化４Åモレキュラーシーブにより残留水を除去した後、孔径０．２μｍのフィルターでろ過して、金属含有レジスト膜形成用組成物（Ｋ－１）を調製した。
［調製例２－２］
　上記合成した化合物（Ｓ－２）２質量部と、プロピレングリコールモノエチルエーテル９８質量部とを混合し、得られた溶液を孔径０．２μｍのフィルターでろ過して、金属含有レジスト膜形成用組成物（Ｋ－２）を調製した。
［調製例２－３］
　上記合成した化合物（Ｓ－３）２質量部と、プロピレングリコールモノエチルエーテル９８質量部、Ｎ－トリフルオロメタンスルホニルオキシ－５－ノルボルネン－２，３－ジカルボキシイミド０．２質量部とを混合し、得られた溶液を孔径０．２μｍのフィルターでろ過して、金属含有レジスト膜形成用組成物（Ｋ－３）を調製した。
［調製例２－４］
　上記合成した化合物（Ｓ－４）２質量部と、プロピレングリコールモノエチルエーテル９８質量部と、Ｎ－トリフルオロメタンスルホニルオキシ－５－ノルボルネン－２，３－ジカルボキシイミド０．２質量部とを混合し、得られた溶液を孔径０．２μｍのフィルターでろ過して、金属含有レジスト膜形成用組成物（Ｋ－４）を調製した。
＜評価＞
［実施例２－１～２－２９、比較例２－１～比較例２－８及び参考例１－１～１－２］
　調製した各レジスト下層膜形成用組成物及び調製した各金属含有レジスト膜形成用組成物を用いて、以下の方法により、レジストパターンの倒壊抑制性を評価した。評価結果を下記表３に示す。
［レジストパターンの倒壊抑制性］
　１２インチシリコンウェハ上に、有機下層膜形成用材料（ＪＳＲ（株）の「ＨＭ８００６」）をスピンコーター（東京エレクトロン（株）の「ＣＬＥＡＮ　ＴＲＡＣＫ　ＡＣＴ１２」）による回転塗工法により塗工した後、２５０℃で６０秒間加熱を行うことにより平均厚み１００ｎｍの有機下層膜を形成した。この有機下層膜上に、上記調製したレジスト下層膜形成用組成物を塗工し、２２０℃で６０秒間加熱した後、２３℃で３０秒間冷却することにより平均厚み１０ｎｍのレジスト下層膜を形成した。このレジスト下層膜上に、下記表３に示す金属含有レジスト膜形成用組成物を、上記スピンコーターによる回転塗工法により塗工してから、所定の時間経過後に、９０℃で６０秒間加熱してから、２３℃で３０秒間冷却することにより平均厚み３５ｎｍの金属含有レジスト膜を形成した。　ＥＵＶスキャナー（ＡＳＭＬ社の「ＴＷＩＮＳＣＡＮ　ＮＸＥ：３３００Ｂ」（ＮＡ０．３、シグマ０．９、クアドルポール照明、ウェハ上寸法が線幅２５ｎｍの１対１ラインアンドスペースのマスク）を用いて金属含有レジスト膜に露光を行った。露光後、基板を１１０℃で６０秒間加熱し、次いで２３℃で６０秒間冷却した。その後、２－ヘプタノン（２０～２５℃）を用い、パドル法により現像した後、乾燥することにより、レジストパターンが形成された評価用基板を得た。上記評価用基板のレジストパターンの測長及び観察には走査型電子顕微鏡（（株）日立ハイテクの「ＣＧ－６３００」）を用いた。
　レジストパターン倒壊抑制性は、
　線幅１８ｎｍのラインのレジストパターンの倒壊が確認されなかった場合は「Ａ」（極めて良好）と、
　線幅１８ｎｍのラインのレジストパターンの倒壊が確認されたが、線幅２４ｎｍのラインのレジストパターンの倒壊が確認されなかった場合は「Ｂ」（良好）と、
　線幅２４ｎｍのラインのレジストパターンの倒壊が確認された場合は「Ｃ」（不良）と評価した。
Figure JPOXMLDOC01-appb-T000014
　上記表３の結果から明らかなように、実施例の各レジスト下層膜形成用組成物はレジストパターン倒壊抑制性が良好であった。
　本発明のレジスト下層膜形成用組成物は、半導体基板の製造等に好適に用いることができる。

Claims (5)

  1. 　電子線又は極端紫外線リソグラフィーにおける金属含有レジスト膜の下層膜を形成するために用いられるレジスト下層膜形成用組成物であって、
    　下記式（１）で表される第１構造単位を有するポリシロキサン化合物と、
    　溶媒と
    　を含有するレジスト下層膜形成用組成物。
    Figure JPOXMLDOC01-appb-C000001
     （式（１）中、Ｘは、ヒドロキシ基、カルボニル基及びエーテル結合からなる群から選ばれる少なくとも１つの構造を有する有機基である。ａは、１～３の整数である。ａが２以上の場合、複数のＸは互いに同一又は異なる。Ｒ１は、炭素数１～２０の１価の有機基、ヒドロキシ基又はハロゲン原子である。但し、Ｒ１は、Ｘ以外の基である。ｂは、０～２の整数である。ｂが２の場合、２つのＲ１は互いに同一又は異なる。但し、ａ＋ｂは３以下である。）
  2. 　上記ポリシロキサン化合物が下記式（２）で表される第２構造単位をさらに有する請求項１に記載のレジスト下層膜形成用組成物。
    Figure JPOXMLDOC01-appb-C000002
     （上記式（２）中、Ｒ５は、置換若しくは非置換の炭素数１～２０の１価のアルコキシ基、ヒドロキシ基、又は、ハロゲン原子である。ｃは、０～３の整数である。ｃが２以上の場合、複数のＲ５は、同一又は異なる。）
  3. 　上記ポリシロキサン化合物を構成する全構造単位に対する上記第１構造単位の含有割合が１モル％以上４０モル％以下である請求項１又は請求項２に記載のレジスト下層膜形成用組成物。
  4. 　基板に直接又は間接に請求項１、請求項２又は請求項３に記載のレジスト下層膜形成用組成物を塗工する工程と、
    　上記レジスト下層膜形成用組成物塗工工程により形成されたレジスト下層膜に金属含有レジスト膜形成用組成物を塗工する工程と、
    　上記金属含有レジスト膜形成用組成物塗工工程により形成された金属含有レジスト膜を電子線又は極端紫外線により露光する工程と、
    　上記露光された金属含有レジスト膜を現像する工程と
    　を備える、半導体基板の製造方法。
  5. 　上記レジスト下層膜形成用組成物塗工工程前に、
    　上記基板に直接又は間接に有機下層膜を形成する工程
    　をさらに備える請求項４に記載の半導体基板の製造方法。
PCT/JP2021/014642 2020-04-23 2021-04-06 レジスト下層膜形成用組成物及び半導体基板の製造方法 WO2021215240A1 (ja)