WO2021100816A1 - Particules de nitrure de bore, et composition de résine - Google Patents

Particules de nitrure de bore, et composition de résine Download PDF

Info

Publication number
WO2021100816A1
WO2021100816A1 PCT/JP2020/043237 JP2020043237W WO2021100816A1 WO 2021100816 A1 WO2021100816 A1 WO 2021100816A1 JP 2020043237 W JP2020043237 W JP 2020043237W WO 2021100816 A1 WO2021100816 A1 WO 2021100816A1
Authority
WO
WIPO (PCT)
Prior art keywords
boron nitride
nitride particles
less
resin
mass
Prior art date
Application number
PCT/JP2020/043237
Other languages
English (en)
Japanese (ja)
Inventor
祐輔 佐々木
建治 宮田
Original Assignee
デンカ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by デンカ株式会社 filed Critical デンカ株式会社
Priority to JP2021558448A priority Critical patent/JPWO2021100816A1/ja
Priority to CN202080073885.1A priority patent/CN114630808A/zh
Publication of WO2021100816A1 publication Critical patent/WO2021100816A1/fr

Abstract

Selon un aspect, l'invention concerne des particules de nitrure de bore qui présentent une surface spécifique BET supérieure ou égale à １０ｍ２／ｇ et inférieure ou égale à １６ｍ２／ｇ, et une quantité totale d'oxygène supérieure ou égale à ０,４% en masse et inférieure ou égale à ０,８% en masse.
PCT/JP2020/043237 2019-11-21 2020-11-19 Particules de nitrure de bore, et composition de résine WO2021100816A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2021558448A JPWO2021100816A1 (fr) 2019-11-21 2020-11-19
CN202080073885.1A CN114630808A (zh) 2019-11-21 2020-11-19 氮化硼粒子及树脂组合物

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019210788 2019-11-21
JP2019-210788 2019-11-21

Publications (1)

Publication Number Publication Date
WO2021100816A1 true WO2021100816A1 (fr) 2021-05-27

Family

ID=75980141

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/043237 WO2021100816A1 (fr) 2019-11-21 2020-11-19 Particules de nitrure de bore, et composition de résine

Country Status (4)

Country Link
JP (1) JPWO2021100816A1 (fr)
CN (1) CN114630808A (fr)
TW (1) TW202130577A (fr)
WO (1) WO2021100816A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022264324A1 (fr) * 2021-06-16 2022-12-22 デンカ株式会社 Poudre de nitrure de bore hexagonal ainsi que procédé de fabrication de celle-ci, produit cosmétique ainsi que procédé de fabrication de celui-ci, et procédé d'évaluation qualité

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010076955A (ja) * 2008-09-24 2010-04-08 Mitsui Chemicals Inc 金属箔付きシートおよび回路基板用積層体
WO2015122378A1 (fr) * 2014-02-12 2015-08-20 電気化学工業株式会社 Particules de nitrure de bore et leur procédé de production
WO2019073690A1 (fr) * 2017-10-13 2019-04-18 デンカ株式会社 Poudre de nitrure de bore, sa méthode de production et élément de dissipation thermique produit à l'aide de celle-ci
JP2019085446A (ja) * 2017-11-01 2019-06-06 デンカ株式会社 窒化ホウ素含有樹脂組成物

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010076956A (ja) * 2008-09-24 2010-04-08 Mitsui Chemicals Inc 窒化ホウ素粉末の評価方法
JP2015224264A (ja) * 2014-05-26 2015-12-14 株式会社Ｂｎ機能設計 樹脂添加用の複合粒子
KR102560615B1 (ko) * 2015-08-26 2023-07-27 덴카 주식회사 열전도성 수지 조성물

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010076955A (ja) * 2008-09-24 2010-04-08 Mitsui Chemicals Inc 金属箔付きシートおよび回路基板用積層体
WO2015122378A1 (fr) * 2014-02-12 2015-08-20 電気化学工業株式会社 Particules de nitrure de bore et leur procédé de production
WO2019073690A1 (fr) * 2017-10-13 2019-04-18 デンカ株式会社 Poudre de nitrure de bore, sa méthode de production et élément de dissipation thermique produit à l'aide de celle-ci
JP2019085446A (ja) * 2017-11-01 2019-06-06 デンカ株式会社 窒化ホウ素含有樹脂組成物

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022264324A1 (fr) * 2021-06-16 2022-12-22 デンカ株式会社 Poudre de nitrure de bore hexagonal ainsi que procédé de fabrication de celle-ci, produit cosmétique ainsi que procédé de fabrication de celui-ci, et procédé d'évaluation qualité

Also Published As

Publication number Publication date
CN114630808A (zh) 2022-06-14
TW202130577A (zh) 2021-08-16
JPWO2021100816A1 (fr) 2021-05-27

Similar Documents

Publication Publication Date Title
TWI833891B (zh) 球狀矽石粉末、含有其之樹脂薄片及其保存方法
JP7069314B2 (ja) 塊状窒化ホウ素粒子、窒化ホウ素粉末、窒化ホウ素粉末の製造方法、樹脂組成物、及び放熱部材
WO2017145869A1 (fr) Poudre de nitrure de bore hexagonal, son procédé de production, composition de résine, et feuille de résine
WO2019073690A1 (fr) Poudre de nitrure de bore, sa méthode de production et élément de dissipation thermique produit à l'aide de celle-ci
JP2019085446A (ja) 窒化ホウ素含有樹脂組成物
JP2019073409A (ja) 塊状窒化ホウ素粉末の製造方法及びそれを用いた放熱部材
WO2021100816A1 (fr) Particules de nitrure de bore, et composition de résine
WO2021111909A1 (fr) Particules de nitrure de bore et leur méthode de fabrication
WO2021100817A1 (fr) Particules de nitrure de bore, et composition de résine
WO2021100808A1 (fr) Particules de nitrure de bore, et composition de résine
WO2021193765A1 (fr) Particules de nitrure de bore et leur procédé de production, et composition de résine et récepteur contenant lesdites particules de nitrure de bore
WO2021111910A1 (fr) Particules de nitrure de bore et leur procédé de production
WO2021193764A1 (fr) Particule de nitrure de bore et composition de résine et récipient la comprenant
JP7289020B2 (ja) 窒化ホウ素粒子、その製造方法、及び樹脂組成物
WO2021200877A1 (fr) Particules de nitrure de bore agrégées et leur procédé de production
JP7289019B2 (ja) 窒化ホウ素粉末及び樹脂組成物
JP7124249B1 (ja) 放熱シート及び放熱シートの製造方法
JP2022125061A (ja) 凝集窒化ホウ素粒子、窒化ホウ素粉末、熱伝導性樹脂組成物及び放熱シート
CN117043099A (zh) 氮化硼粉末及树脂组合物

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20889061

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2021558448

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20889061

Country of ref document: EP

Kind code of ref document: A1