WO2021094228A1 - Composition, procédé de préparation et application associée - Google Patents

Composition, procédé de préparation et application associée Download PDF

Info

Publication number
WO2021094228A1
WO2021094228A1 PCT/EP2020/081409 EP2020081409W WO2021094228A1 WO 2021094228 A1 WO2021094228 A1 WO 2021094228A1 EP 2020081409 W EP2020081409 W EP 2020081409W WO 2021094228 A1 WO2021094228 A1 WO 2021094228A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
substrate
article
composition according
adsorbent
Prior art date
Application number
PCT/EP2020/081409
Other languages
English (en)
Inventor
Yingdan ZHU
Chen JIN
Miao TAN
Dongbo ZHAO
Original Assignee
Covestro Intellectual Property Gmbh & Co. Kg
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from CN201911111586.8A external-priority patent/CN112795298A/zh
Priority claimed from EP20151335.5A external-priority patent/EP3848423A1/fr
Application filed by Covestro Intellectual Property Gmbh & Co. Kg filed Critical Covestro Intellectual Property Gmbh & Co. Kg
Priority to CN202080078975.XA priority Critical patent/CN114829516A/zh
Priority to EP20800675.9A priority patent/EP4058523A1/fr
Publication of WO2021094228A1 publication Critical patent/WO2021094228A1/fr

Abstract

La présente invention concerne une composition, en particulier une composition ayant peu de COV et une faible odeur, une préparation et une application de la composition, un système à deux constituants comprenant la composition et son application, ainsi qu'un article revêtu ou collé par l'utilisation de la composition ou du système à deux constituants. La composition comprend au moins une dispersion aqueuse de polyuréthanne, au moins un adsorbant, et au moins un agent chélatant ; l'adsorbant étant un ou plusieurs des adsorbants suivants : un tamis moléculaire hydrophile et un tamis moléculaire amphiphile ; la dispersion aqueuse de polyuréthanne est présente en une quantité de 50 % en poids à 99 % en poids, l'adsorbant en une quantité de 0,1 % en poids à 3 % en poids, et l'agent chélatant en une quantité de 0,05 % en poids à 1 % en poids, dans chaque cas par rapport à la quantité de composition, correspondant à 100 % en poids.
PCT/EP2020/081409 2019-11-13 2020-11-09 Composition, procédé de préparation et application associée WO2021094228A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN202080078975.XA CN114829516A (zh) 2019-11-13 2020-11-09 一种组合物及其制备方法和应用
EP20800675.9A EP4058523A1 (fr) 2019-11-13 2020-11-09 Composition, procédé de préparation et application associée

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
CN201911111586.8A CN112795298A (zh) 2019-11-13 2019-11-13 一种组合物及其制备方法和应用
CN201911111586.8 2019-11-13
EP20151335.5 2020-01-13
EP20151335.5A EP3848423A1 (fr) 2020-01-13 2020-01-13 Composition, son procédé de préparation et son application

Publications (1)

Publication Number Publication Date
WO2021094228A1 true WO2021094228A1 (fr) 2021-05-20

Family

ID=73043287

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2020/081409 WO2021094228A1 (fr) 2019-11-13 2020-11-09 Composition, procédé de préparation et application associée

Country Status (3)

Country Link
EP (1) EP4058523A1 (fr)
CN (1) CN114829516A (fr)
WO (1) WO2021094228A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050131109A1 (en) * 2003-09-18 2005-06-16 Wolfgang Arndt Aqueous adhesive dispersions
CN103980814A (zh) 2014-05-21 2014-08-13 三棵树涂料股份有限公司 聚氨酯净味亚光耐磨清面漆及其制备方法
CN104151540A (zh) 2014-08-06 2014-11-19 山东蓝星东大化工有限责任公司 低voc含量高回弹聚氨酯泡沫用聚醚多元醇的制备方法
CN104592878A (zh) 2015-01-01 2015-05-06 宁波帝杨电子科技有限公司 一种环保水性漆及其制备方法
CN106009271A (zh) 2016-06-23 2016-10-12 神华集团有限责任公司 一种改性聚丙烯组合物及其制备方法

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN100467554C (zh) * 2008-03-25 2009-03-11 中华制漆（深圳）有限公司 具有抗菌和空气净化功能的涂料组合物
CN101348628B (zh) * 2008-09-17 2011-05-18 中国建筑材料科学研究总院 净化空气的厚质涂覆材料及其配制方法
CN108504078B (zh) * 2017-02-28 2022-04-19 科思创聚合物（中国）有限公司 一种组合物及其制备方法和应用

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050131109A1 (en) * 2003-09-18 2005-06-16 Wolfgang Arndt Aqueous adhesive dispersions
CN103980814A (zh) 2014-05-21 2014-08-13 三棵树涂料股份有限公司 聚氨酯净味亚光耐磨清面漆及其制备方法
CN104151540A (zh) 2014-08-06 2014-11-19 山东蓝星东大化工有限责任公司 低voc含量高回弹聚氨酯泡沫用聚醚多元醇的制备方法
CN104592878A (zh) 2015-01-01 2015-05-06 宁波帝杨电子科技有限公司 一种环保水性漆及其制备方法
CN106009271A (zh) 2016-06-23 2016-10-12 神华集团有限责任公司 一种改性聚丙烯组合物及其制备方法

Also Published As

Publication number Publication date
EP4058523A1 (fr) 2022-09-21
CN114829516A (zh) 2022-07-29

Similar Documents

Publication Publication Date Title
EP3589677B1 (fr) Composition, sa préparation et son utilisation
WO2018158278A1 (fr) Composition, sa production, et utilisation associée
US11965108B2 (en) Composition, preparation method and application thereof
EP3848423A1 (fr) Composition, son procédé de préparation et son application
WO2021094228A1 (fr) Composition, procédé de préparation et application associée
KR20220020812A (ko) 수성 폴리우레탄 분산액
EP3841139B1 (fr) Composition de polyuréthane, procédé de préparation et son application
CN112795298A (zh) 一种组合物及其制备方法和应用
CN113801554A (zh) 一种组合物及其制备方法和应用
EP3985042A1 (fr) Composition adhésive et son procédé de préparation et son utilisation
KR20240047382A (ko) 수성 폴리우레탄-우레아 분산액
EP4174100A1 (fr) Dispersion aqueuse de polyuréthane-urée
EP3640272A1 (fr) Composition, son procédé de préparation et son application
CN110857329A (zh) 一种聚氨酯组合物及其制备方法和应用
EP4029894A1 (fr) Dispersion aqueuse de polyuréthane-urée
US20240034828A1 (en) Aqueous Polyurethane Urea Dispersion
EP3795601A1 (fr) Dispersion aqueuse de polyuréthane
CN110857385A (zh) 一种组合物及其制备方法和应用
WO2022049226A1 (fr) Composition adhésive ainsi que son procédé de préparation et son utilisation
CN114605611A (zh) 水性聚氨酯脲分散体
EP4339216A1 (fr) Composition adhésive, son procédé de préparation et son utilisation
CN114149779A (zh) 粘结剂组合物及其制备方法和应用

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20800675

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2020800675

Country of ref document: EP

Effective date: 20220613