WO2020218787A1 - 소성된 층상 이중 수산화물 및 폴리머를 포함하는 성형용 화장료 조성물 - Google Patents

소성된 층상 이중 수산화물 및 폴리머를 포함하는 성형용 화장료 조성물 Download PDF

Info

Publication number
WO2020218787A1
WO2020218787A1 PCT/KR2020/005198 KR2020005198W WO2020218787A1 WO 2020218787 A1 WO2020218787 A1 WO 2020218787A1 KR 2020005198 W KR2020005198 W KR 2020005198W WO 2020218787 A1 WO2020218787 A1 WO 2020218787A1
Authority
WO
WIPO (PCT)
Prior art keywords
cosmetic composition
molding
weight
double hydroxide
layered double
Prior art date
Application number
PCT/KR2020/005198
Other languages
English (en)
French (fr)
Inventor
지홍근
박영아
강유진
김자인
이종현
Original Assignee
주식회사 에이치엔에이파마켐
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 에이치엔에이파마켐 filed Critical 주식회사 에이치엔에이파마켐
Priority to CN202080030520.0A priority Critical patent/CN113710215A/zh
Priority to US17/603,376 priority patent/US20220211589A1/en
Priority to JP2021563137A priority patent/JP2022529840A/ja
Priority to EP20795429.8A priority patent/EP3960147A4/en
Publication of WO2020218787A1 publication Critical patent/WO2020218787A1/ko

Abstract

본 발명은 소성된 층상 이중 수산화물(layered double hydroxide) 및 폴리머를 포함하는 성형(molding)용 화장료 조성물에 관한 것으로, 보다 상세하게는 유효성분, 소성된 층상 이중 수산화물, 폴리머 및 용매를 포함하는 성형용 화장료 조성물, 및 이의 제조 방법에 관한 것이다.

Description

소성된 층상 이중 수산화물 및 폴리머를 포함하는 성형용 화장료 조성물
본 발명은 소성된 층상 이중 수산화물(layered double hydroxide) 및 폴리머를 포함하는 성형(molding)용 화장료 조성물에 관한 것으로, 보다 상세하게는 유효성분, 소성된 층상 이중 수산화물, 폴리머 및 용매를 포함하는 성형용 화장료 조성물, 및 이의 제조 방법에 관한 것이다.
기능성 재료의 개발로 인하여 화장품 원재료에 보다 높은 안정성을 부여할 수 있는 다양한 기능화 방법이 광범위하게 연구되고 있다. 특히, 빛, 열 및 공기중의 산소가 기능성 원재료의 생물학적 활성을 심각하게 감소시키는 것으로 잘 알려져 있다. 따라서 다양한 화장품 활성성분의 안정화를 위한 새로운 기능화 기술이 필요한 실정이다.
이러한 화장품 활성성분의 전달 시스템 중 하나로 주목받고 있는 것이 층상 이중 수산화물(layered double hydroxide, LDH)이다. 층상 이중 수산화물은 층상구조의 무기화합물로, 모양이 마치 지층의 엽편상과 같은 모습으로 층을 이루고 있다. LDH는 기본적으로 이산화탄소와 같은 작은 기체 분자에서부터 DNA 등과 같은 생체 고분자에 이르기 까지 다양한 음이온을 흡수할 수 있는 구조적 특성을 가지고 있는 무기재료이다. 또한, 층 안에 포집되어 있는 분자들은 무기 층과의 정전기적 상호 작용에 의해 에너지적으로 안정하게 유지될 수 있다. 음이온은 이온교환 방식으로 흡수되거나 방출되는 특성을 가지고 있다. 무기 층은 알카리 금속부터 전이 금속에 이르기 까지 다양한 조성으로 구성되기 때문에 촉매, 자성체, 전자 재료 등의 전구체 물질로 사용될 수 있다. 최근에는 특정한 분자 연결고리를 사용하여 LDH 나노재료를 자기조립 시키거나, 무기 층의 표면 반응을 선택적으로 유도하여 층 안 음이온이 특정한 환경에서 방출될 수 있도록 조절하는 메커니즘이 발견되면서 가스센서(gas-sensor)나 약물 전달(drug delivery) 재료로도 관심을 받고 있다. 특히, 층과 층 사이에 존재하는 정전기적 인력을 화학적으로 최소화하면 1 nm 두께의 나노층(nanolayer)으로 분리 할 수 있으며, 이는 LDH 재료의 응용성을 폭발적으로 증가시키는 기폭재가 되어, nanoelectronics, magento-optics, nanosensor 등의 분야에 적용되고 있다. 또한, 기능성 유기분자에 대한 흡착성능이 매우 우수한 LDH 나노층은 앞으로 화장품 유효성분의 흡착 성능 향상과 화학적 환경조절에 따른 방출제어 등의 기술 개발을 바탕으로 새로운 bioencapsulation 소재로 관심 받고 있다. 이러한 LDH를 활용한 예로, 대한민국 공개특허공보 제10-2018-0109205호에서는 리포좀을 층상 이중 수산화물과 혼합한 후 밀링하여 리포좀이 층상 이중 수산화물의 층 사이에 흡착된 캡슐을 형성함으로써 영여자 추출물을 2차적으로 안정화시킨, 영여자 추출물 및 층상 이중 수산화물을 포함하는 화장료 조성물을 개시하고 있다.
한편, 화장품의 발전으로 다양하게 눈에 보이는 화장품에 대하여 관심이 증가되고 있다. 화장품의 활성성분(유효성분) 등에 따른 효능이나 효과도 중시되지만, 소비자가 사용전에 외관상으로 보이는 형태를 보고 나서 구매하는 경우도 많아지고 있다. 특히, 눈에 보이는 캡슐 제형의 에센스나 크림 등의 다양한 형태의것도 판매되고 있고, 동결건조로 히아루론산, 콜라겐 등을 눈에 보여주는 형태의 것들도 나오고 있다. 이러한 시대의 변화에 따라 소비자들을 시각적으로 만족시킬 수 있는 다양한 모양의 화장품에 대한 지속적인 요구가 있다.
[선행기술문헌]
[특허문헌]
대한민국 공개특허공보 제10-2018-0109205호
이에 본 발명은 활성성분을 안정한 상태에서 피부 내로 효율적으로 전달할 수 있을 뿐만 아니라 뛰어난 성형성으로 다양한 형태의 모양으로 자유롭게 성형 가능한 화장료(cosmetic) 조성물을 제공하는 것을 그 기술적 과제로 한다.
또한, 본 발명은 상기 성형용 화장료 조성물을 효과적으로 제조하기 위한 제조 방법을 제공하는 것을 다른 기술적 과제로 한다.
상기 과제를 해결하기 위하여 본 발명은 활성성분, 소성된 층상 이중 수산화물, 폴리머 및 용매를 포함하는 성형(molding)용 화장료 조성물을 제공한다.
또한, 본 발명은 i) 층상 이중 수산화물을 400 내지 1,200°C의 온도에서 6시간 내지 16시간 동안 소성한 다음 냉각하고, ii) 활성성분 및 폴리머를 용매에 용해시키고, 상기 소성된 층상 이중 수산화물과 혼합하여 교반하는 것을 포함하는 성형용 화장료 조성물의 제조 방법을 제공한다.
이하에서 본 발명에 대하여 상세히 설명한다.
본 발명의 일 측면에 따르면, 활성성분, 소성된 층상 이중 수산화물, 폴리머 및 용매를 포함하는 성형용 화장료 조성물이 제공된다.
본 발명의 성형용 화장료 조성물은 활성성분을 바람직하게는 0.01 내지 50 중량%, 더 바람직하게는 0.1 내지 48 중량%, 더 바람직하게는 1 내지 45 중량% 포함한다. 본 발명의 성형용 화장료 조성물에서 활성성분이 0.01 중량% 미만으로 포함될 경우 이에 따른 효능이 제대로 발휘되지 않을 수 있고, 50 중량%를 초과하여 포함될 경우 화장료 조성물의 성형시 문제가 있을 수 있다.
본 발명에서 활성성분에 따른 특별한 제한은 없다. 본 발명에서 활성성분은 예를 들면, 보습제, 미백제, 주름개선제, 자외선 차단제, 육모제, 비타민 또는 그 유도체, 아미노산 또는 펩타이드, 항염증제, 여드름 치료제, 살균제, 여성호르몬제, 각질박리용해제 및 천연물로 이루어진 그룹으로부터 선택되는 하나 이상일 수 있으나 이에 제한되는 것은 아니다.
보습제로는, 예를 들면 크레아틴, 폴리글루탐산, 젖산 나트륨, 하이드로 프로린, 2-피로리돈-5-카르본산나트륨, 히아루론산, 히아루론산 나트륨, 세라마이드, 피토스테릴, 콜레스테롤, 씨토스테롤, 풀루란, 프로테오글리칸 등이 있으나 이에 제한되는 것은 아니다. 미백제로는, 예를 들면 알부틴 및 알부틴 유도체, 코직산, 비사보놀, 나이이신아마이드, 비타민 C 및 비타민 C 유도체, 프라센타, 알란토인 등이 있으나 이에 제한되는 것은 아니다. 주름개선제로는, 예를 들면 레티놀, 레티놀 유도체, 아데노신, 감초 추출물, 홍삼 추출물, 인삼 추출물 등이 있으나 이에 제한되는 것은 아니다. 자외선 차단제로는, 예를 들면 벤조페논 유도체, 파라아미노안식향산 유도체, 메톡시계피산 유도체, 살리실산 유도체 등이 있으나 이에 제한되는 것은 아니다. 육모제로는 특별한 제한은 없다고 할 것이나, 혈행촉진제 및/또는 국소자극제가 바람직하고, 혈행촉진제로는 예를 들면 월견초 추출물, 세파란틴, 비타민 E 및 그 유도체, 감마 오리자놀 등이 있으나 이에 제한되는 것은 아니며, 국소 자극제로는 고추 틴크, 생강 틴크, 칸타리스 틴크, 니코틴산 벤질에스테르 등이 있으나 이에 제한되는 것은 아니다. 비타민 또는 그 유도체로는, 예를 들면 비타민 A(레티놀) 및 그 유도체, 비타민 B1, B2, B6, 비타민 E 및 그 유도체, 비타민 D, 비타민 H, 비타민 K, 판토텐산 및 그 유도체, 비오틴, 판테놀, 코엔자임 Q10, 이데베논 등이 있으나 이에 제한되는 것은 아니다. 아미노산 또는 펩타이드로는, 예를 들면 시스테인, 메티오닌, 세린, 라이신, 트립토판, 아미노산 엑기스, 상피세포성장인자(EGF), 인슐린유사 성장인자(IGF), 섬유아세포 성장인자(FGF), 쿠퍼 펩타이드, 쿠퍼 트리펩타이드-1, 트리펩타이드-29, 트리펩타이드-1, 아세틸 헥사펩타이드-8, 니코티노일 트리펩타이드-35, 헥사펩타이드-12, 헥사펩타이드-9. 팔미토일 펜타펩타이드-4, 팔미토일 테트라펩타이드-7, 팔미토일 트리펩타이드-29, 팔미토일 트리펩타이드-1, 노나펩타이드-7, 트리펩타이드-10 시트룰린(citrulline), sh-폴리펩타이드-15, 팔미토일 트리펩타이드-5, 디아미노프로피오일 트리펩타이드-33, r-스파이더(spider) 폴리펩타이드-1 등이 있으나 이에 제한되는 것은 아니다. 항염증제로는, 예를 들면 베타-글리틸리틴산, 글리틸리탄산 유도체, 아미노카프론산, 하이드로코티손, 베타글루칸, 감초 등이 있으나 이에 제한되는 것은 아니다. 여드름 치료제로는, 예를 들면 에스트라디올, 에스트로겐, 에티닐 에스트라리올, 트리크로산, 아젤릭산 등이 있으나 이에 제한되는 것은 아니다. 살균제로는, 예를 들면 염화 벤잘코늄, 염화 벤제토니움(benzethonium chloride), 하로칼반 등이 있으나 이에 제한되는 것은 아니다. 여성호르몬제로는 특별한 제한은 없다고 할 것이나, 에스트로겐이 적합하며, 에스트로겐으로서는 에스트라디올, 에티닐 에스트라디올, 식물성 에스트로겐인 이소플라본 등이 바람직하다. 각질박리용해제로는, 예를 들면 유황, 살리실산, 아하(AHA), 바하(BHA), 레소르신 등이 있으나 이에 제한되는 것은 아니다. 천연물의 추출 엑기스나 그들로부터 얻어진 성분으로, 예를 들면 풍년화, 광대수염, 백화, 대황, 감초, 알로에, 카모마일, 로즈힙, 마로니에, 인삼, 수세미, 오이, 김, 미역, 마, 달팽이, 영여자 등의 추출물이나 히노키티올, 베타카로틴 등이 있으나 이에 제한되는 것은 아니다. 그 외에 효모 추출물, 콜라겐, 에라스틴, DHA, EPA, 향 성분 등도 있다.
본 발명의 성형용 화장료 조성물은 소성된 층상 이중 수산화물(layered double hydroxide, LDH)을 바람직하게는 10 내지 60 중량%, 더 바람직하게는 15 내지 55 중량%, 더 바람직하게는 20 내지 50 중량% 포함한다. 본 발명의 성형용 화장료 조성물에서 소성된 층상 이중 수산화물이 10 중량% 미만으로 포함될 경우 유효성분을 피부내로 전달하는 효율이 낮아질 수 있고, 60 중량%를 초과하여 포함될 경우 화장료 조성물의 성형시 문제가 있을 수 있다.
본 발명에서 LDH의 조성은 [M2+ 1-x M3+ x(OH)2]x+(An-)x/n·mH2O의 구조식으로 표현된다. 상기 구조식에서, M2+와 M3+는 금속 양이온으로 수활석(brucite)의 팔면체 자리를 차지하고 있고, An-는 층 사이에 위치한 음이온을 나타내며, M2+ = Ca2+, Mg2+, Zn2+, Ni2+, Mn2+, Co2+, Fe2+ 등이고, M3+ = Al3+, Cr3+, Mn3+, Fe3+, Ga3+, Co3+, Ni3+ 등이며, An-는 OH-, F-, Cl-, Br-, I-, NO3 -, CO3 2-, SO4 2- 등이고, 고정된 조성물 상태에서 0.2 ≤ x ≤ 0.33이며, n은 1 또는 2이고, m은 일반적으로 0.5 내지 4이다.
LDH 구조의 층 사이에 위치한 음이온은 쉽게 교체될 수 있어 할로겐 이온부터 DNA와 같은 음전하를 가지는 생체 고분자뿐 아니라 콜라겐 트리펩타이드와 같은 바이오 물질 및 Ag, Au, Pt 등을 함유하는 고체 나노입자도 인터칼레이션(intercalation)할 수 있다. LDH의 기본적인 층상 구조와 가능한 금속 양이온 및 음이온의 예를 도 1에 나타낸다. LDH의 제조는 당 분야에 공지된 방법, 예를 들면 수열방법, 대류순환법, 초음파법 등으로 합성을 할 수 있다.
본 발명에서 LDH의 소성(calcination)은 당 분야에 공지된 방법에 따라 수행될 수 있고 이에 따른 특별한 제한은 없다. 본 발명에 따른 일 구체예에서 LDH의 소성은 LDH를 노(furnace)에서 약 400 내지 1,200°C의 온도, 더 바람직하게는 약 500 내지 1,100°C의 온도로, 약 6시간 내지 16시간, 더 바람직하게는 약 8시간 내지 14시간 가열하여 수행한다.
본 발명에 따른 일 구체예에서, LDH의 금속 수산화물 표면은 다양한 물질로 표면 작용화 및 표면 개질이 가능하다. 예를 들면 도데실 설페이트(dodecyl sulfate), 스테아레이트(stearate) 등과 같은 물질로 개질이 가능하다.
본 발명의 성형용 화장료 조성물은 폴리머를 바람직하게는 0.5 내지 20 중량%, 더 바람직하게는 1 내지 18 중량%, 더 바람직하게는 2 내지 15 중량% 포함한다. 본 발명의 성형용 화장료 조성물에서 폴리머가 0.5 중량% 미만으로 포함되거나 20 중량%를 초과하여 포함될 경우 화장료 조성물의 성형시 문제가 있을 수 있다.
본 발명에서 폴리머는 예를 들면, 셀룰로오스, 메틸셀룰로오스, 하이드록시에틸셀룰로오스, 미결정 셀룰로오스(microcrystalline cellulose), 나노셀룰로오스, 전분(starch), 폴리메틸 메타크릴레이트(poly(methyl methacylate), PMMA), 폴리아크릴산(polyacrylic acid), 아크릴레이트/C10-30 알킬 아크릴레이트 크로스폴리머(acrylates/C10-30 alkyl acrylate crosspolymer), 폴리비닐알코올(PVA), 폴리비닐피롤리돈(PVP), 폴리글리콜라이드(PGA), 잔탄검, 아카시아검(아라비아검), 구아검, 카라기난검, 젤란검(gellan gum), 카라야검(karaya gum), 로커스트빈검(locust bean gum), 히알루론산, 풀루란(pullulan), 알긴산나트륨, 키토산, 한천(agar), 젤라틴 및 콜라겐으로부터 선택되는 하나 이상이 사용될 수 있으나 이에 제한되는 것은 아니다.
본 발명의 성형용 화장료 조성물은 용매를 바람직하게는 10 내지 60 중량%, 더 바람직하게는 15 내지 55 중량%, 더 바람직하게는 20 내지 50 중량% 포함한다. 본 발명의 성형용 화장료 조성물에서 용매가 10 중량% 미만으로 포함되거나 60 중량%를 초과하여 포함될 경우 화장료 조성물의 성형시 문제가 있을 수 있다.
본 발명에서 용매는 예를 들면, 물, 글리세린, 프로필렌 글리콜, 부틸렌 글리콜, 디글리세린, 디프로필렌 글리콜 및 이의 혼합물이 사용될 수 있으나 이에 제한되는 것은 아니다.
본 발명의 성형용 화장료 조성물은 그 필요에 따라 안정화제, 산화방지제, 윤활제 등의 성분을 추가로 포함할 수 있다.
본 발명의 다른 측면에 따르면, i) 층상 이중 수산화물을 400 내지 1,200°C의 온도에서 6시간 내지 16시간 동안 소성한 다음 냉각하고, ii) 활성성분 및 폴리머를 용매에 용해시키고, 상기 소성된 층상 이중 수산화물과 혼합하여 교반하는 것을 포함하는 성형용 화장료 조성물의 제조 방법이 제공된다.
상기 제조 방법의 (i) 단계에서, 층상 이중 수산화물의 조성은 상기에서 정의한 바와 같고, 소성은 바람직하게는 500 내지 1,100°C의 온도에서 8시간 내지 14시간 동안 수행된다.
상기 제조 방법의 (ii) 단계에서, 활성성분에 따른 특별한 제한은 없고, 예를 들면, 보습제, 미백제, 주름개선제, 자외선 차단제, 육모제, 비타민 또는 그 유도체, 아미노산 또는 펩타이드, 항염증제, 여드름 치료제, 살균제, 여성호르몬제, 각질박리용해제 및 천연물로 이루어진 그룹으로부터 선택되는 하나 이상일 수 있으나 이에 제한되는 것은 아니다.
상기 제조 방법의 (ii) 단계에서, 폴리머는 예를 들면, 셀룰로오스, 메틸셀룰로오스, 하이드록시에틸셀룰로오스, 미결정 셀룰로오스, 나노셀룰로오스, 전분, 폴리메틸 메타크릴레이트, 폴리아크릴산, 아크릴레이트/C10-30 알킬 아크릴레이트 크로스폴리머, 폴리비닐알코올, 폴리비닐피롤리돈, 폴리글리콜라이드, 잔탄검, 아카시아검, 구아검, 카라기난검, 젤란검, 카라야검, 로커스트빈검, 히알루론산, 풀루란, 알긴산나트륨, 키토산, 한천, 젤라틴 및 콜라겐으로 이루어진 그룹으로부터 선택되는 하나 이상이 사용될 수 있으나 이에 제한되는 것은 아니다.
상기 제조 방법의 (ii) 단계에서, 용매는 예를 들면, 물, 글리세린, 프로필렌 글리콜, 부틸렌 글리콜, 디글리세린, 디프로필렌 글리콜 및 이의 혼합물이 사용될 수 있으나 이에 제한되는 것은 아니다.
상기 제조 방법의 (ii) 단계에서, 활성성분, 폴리머, 용매 및 소성된 층상 이중 수산화물의 중량비는 바람직하게는 각각 0.01 내지 50 중량%, 0.5 내지 20 중량%, 10 내지 60 중량% 및 10 내지 60 중량%; 더 바람직하게는 각각 0.1 내지 48 중량%, 1 내지 18 중량%, 15 내지 55 중량% 및 15 내지 55 중량%; 더 바람직하게는 각각 1 내지 45 중량%, 2 내지 15 중량%, 20 내지 50 중량% 및 20 내지 50 중량%이다.
본 발명에 따른 성형용 화장료 조성물의 성형은 당 분야에 공지된 방법에 따라 수행되어 다양한 모양(둥근볼, 큐빅, 조개 모양, 꽃 모양, 별 모양, 하트 모양, 알파벳 모양, 일반적 판상모양 등)으로 제조될 수 있고 이에 따른 특별한 제한은 없다. 예를 들면, 본 발명에 따른 성형용 화장료 조성물을 원하는 모양의 금형에 투입부을 통하여 투입 후 압축을 한 다음 분리하여 건조함으로써 제조할 수 있다.
또한, 본 발명에 따른 성형용 화장료 조성물은 그 활성성분에 따라 클렌징(cleansing), 목욕용 발포제, 에센스, 바디워시(body wash) 등의 다양한 제형의 화장품을 제공할 수 있다.
본 발명의 성형용 화장료 조성물은 활성성분을 매우 안정한 형태로 피부 내로 효율적으로 전달할 뿐만 아니라 뛰어난 성형성으로 다양한 모양을 갖는 심미적으로 우수하고, 보관이나 휴대가 편리한 화장품을 제공할 수 있다.
도 1은 층상 이중 수산화물(LDH)의 층상 구조와 조성을 나타낸 모식도이다.
도 2는 실시예 11에서 본 발명의 성형용 화장료 조성물을 다양한 모양으로 성형한 다음 촬영한 사진이다.
도 3은 비교예의 성형용 화장료 조성물을 성형한 다음 촬영한 사진이다.
도 4는 실시예 1에서 제조된 조성물의 제타포텐셜을 Photal, ELS-Z를 사용하여 측정한 결과이다.
도 5는 실시예 1에서 제조된 조성물의 안정도를 Turbiscan으로 측정한 결과이다.
도 6은 실시예 1에서 제조된 조성물을 동결 전자현미경을 사용하여 확대 촬영한 사진이다.
이하, 실시예를 통하여 본 발명을 보다 구체적으로 설명한다. 그러나 하기 실시예는 본 발명의 이해를 돕기 위하여 예시하는 것일 뿐, 본 발명의 범위가 이에 의하여 한정되는 것은 아니다.
제조예 1: 알루미늄/마그네슘 하이드록사이드 스테아레이트(aluminum/magnesium hydroxide stearate)의 합성
시판되고 있는 제품을 태산화학(한국)으로부터 구매하여 사용하였다.
제조예 2: ZnAl-층상 이중 수산화물(ZnAl-LDH)의 합성
카보네이트(carbonate) 이온을 함유하는 ZnAl-LDH를 다음과 같이 공침법(coprecipitation)으로 합성하였다. 0.2M Zn(NO3)2와 0.1M의 Al(NO3)3의 혼합용액에 최종 pH가 7.0 정도가 될 때까지 1M의 Na2CO3 용액을 서서히 첨가하였다. 혼합용액을 약 70°C의 오븐에 하루정도 보관 후, 필터한 다음 증류수와 에탄올로 세척하고 나서 진공펌프를 이용하여 건조하였다. 합성된 c-LDH의 가능한 구조식은 다음과 같다: [Zn4Al2(OH)12]CO3·xH2O.
제조예 3: MgAl-층상 이중 수산화물(MgAl-LDH)의 합성
카보네이트(carbonate) 이온을 함유하는 MgAl-LDH를 다음과 같이 공침법(coprecipitation)으로 합성하였다. 0.2M Mg(NO3)2와 0.1M의 Al(NO3)3의 혼합용액에 최종 pH가 7.0 정도가 될 때까지 1M의 Na2CO3 용액을 서서히 첨가하였다. 혼합용액을 약 70°C의 오븐에 하루정도 보관 후, 필터한 다음 증류수와 에탄올로 세척하고 나서 진공펌프를 이용하여 건조하였다. 합성된 c-LDH의 가능한 구조식은 다음과 같다: [Mg4Al2(OH)12]CO3·xH2O.
제조예 4: 알루미늄/마그네슘 실리케이트(aluminum/magnesium silicate)의 합성
시판되고 있는 제품을 BYK-Chemie GmbH(독일)로부터 구매하여 사용하였다.
실시예 1: 비타민 함유 성형용 조성물 제조
다음의 표 1의 조성으로, 제조예 1에서 얻은 알루미늄/마그네슘 하이드록사이드 스테아레이트를 노(furnace)에서 1,000°C의 온도에서 12시간 동안 가열을 한 다음 20°C까지 냉각하였다. 활성성분으로 레티놀과 폴리머로서 키토산을 물에 용해시킨 후 이에 상기 소성된 알루미늄/마그네슘 하이드록사이드 스테아레이트를 혼합하고 20분간 믹서로 교반하여 성형용 조성물을 제조하였다.
[표 1]
Figure PCTKR2020005198-appb-I000001
실시예 2: 펩타이드 함유 성형용 조성물 제조
다음의 표 2의 성분 및 조성을 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 성형용 조성물을 제조하였다.
[표 2]
Figure PCTKR2020005198-appb-I000002
실시예 3: 미백제 함유 성형용 조성물 제조
다음의 표 3의 성분 및 조성을 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 성형용 조성물을 제조하였다.
[표 3]
Figure PCTKR2020005198-appb-I000003
실시예 4: 천연 추출물 함유 성형용 조성물 제조
다음의 표 4의 성분 및 조성을 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 성형용 조성물을 제조하였다.
[표 4]
Figure PCTKR2020005198-appb-I000004
실시예 5: 클렌징 제형의 성형용 조성물의 제조 1
다음의 표 5의 성분 및 조성을 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 성형용 조성물을 제조하였다.
[표 5]
Figure PCTKR2020005198-appb-I000005
실시예 6: 클렌징 제형의 성형용 조성물의 제조 2
다음의 표 6의 성분 및 조성을 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 성형용 조성물을 제조하였다.
[표 6]
Figure PCTKR2020005198-appb-I000006
실시예 7: 클렌징 제형의 성형용 조성물의 제조 3
다음의 표 7의 성분 및 조성을 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 성형용 조성물을 제조하였다.
[표 7]
Figure PCTKR2020005198-appb-I000007
실시예 8: 목욕용 발포제 제형의 성형용 조성물의 제조 1
다음의 표 8의 성분 및 조성을 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 성형용 조성물을 제조하였다.
[표 8]
Figure PCTKR2020005198-appb-I000008
실시예 9: 목욕용 발포제 제형의 성형용 조성물의 제조 2
다음의 표 9의 성분 및 조성을 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 성형용 조성물을 제조하였다.
[표 9]
Figure PCTKR2020005198-appb-I000009
실시예 10: 에센스 제형의 성형용 조성물의 제조
다음의 표 10의 성분 및 조성을 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 성형용 조성물을 제조하였다.
[표 10]
Figure PCTKR2020005198-appb-I000010
실시예 11: 성형용 조성물의 성형
실시예 1 내지 10에서 얻은 성형용 조성물을 다양한 모양으로 성형틀에 넣어서 성형한 다음 건조기에서 50 내지 60°C의 온도에서 6시간 동안 건조하였다(도 2).
비교예
소성 과정을 거치지 않은 층상 이중 수산화물을 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 비타민 함유 성형용 조성물을 제조한 다음 성형하였다(도 3).
실험예 1: 제타포텐셜의 측정
실시예 1에서 제조된 조성물의 제타포텐셜을 Photal, ELS-Z를 사용하여 측정한 결과 -52.58 mV 임을 알 수 있었다(도 4).
실험예 2: 안정도 측정
실시예 1에서 제조된 조성물의 안정도 측정을 위해 Turbiscan(조건: 40℃, 6시간, 70 scans)을 사용해서 측정한 결과 시간이 지남에 따라 △T, △BS 변화가 거의 없어 에멀전이 안정함을 알 수 있었다(도 5).
실험예 3: 동결 전자현미경 촬영
실시예 1에서 제조된 조성물을 동결 전자현미경(JEM 1010, JEOL사, 일본)을 이용하여 촬영하였다(도 6).
실험예 4: 경피 흡수촉진 효과 실험
인공피부인 Strat-M® Membrane (Transdermal Diffusion Test Model)을 사용하여 Franz-type diffusion cell(Transdermal Semi-Auto Diffusion Cell, LOGAN Instruments, USA)에 장착하여 실험하였다. Franz-type diffusion cell의 receptor 용기(5 ㎖)에 50 mM 인산염 완충액(pH 7.4, 0.1M NaCl)을 넣어준 후, diffusion cell을 32℃, 600 rpm으로 혼합, 분산시켜 주었으며, 실시예 1의 조성물 50 ㎕를 donor용기에 넣어 주었다. 예정한 시간에 따라 흡수 확산시켜 주었으며, 흡수 확산이 일어나는 피부는 0.64 cm2가 되게 하였다. 유효성분의 흡수확산이 끝난 후에는 건조된 킴와이프스(kimwipes) 또는 10 ㎖의 에탄올로 흡수되지 못하고 피부에 남아 있는 유화물을 씻어주고, 팁-타입 균질기(homogenizer)를 사용하여 유효성분이 흡수 확산되어 있는 피부를 갈아준 후, 피부 내부로 흡수된 레티놀을 4 ㎖의 디클로로메탄을 사용하여 추출하였다. 이후 추출액을 0.45 ㎛ 나일론 멤브레인(nylon membrane) 여과막으로 여과하고, 다음 조건으로 HPLC법으로 레티놀의 함량을 측정한 결과 경피 흡수량은 0.364 μg으로 효율적으로 피부 내로 전달되는 것을 알 수 있었다.
- 컬럼: C18 (4.6 × 200 mm, 5 μm)
- 이동상: 메탄올 : 헥산= 2 : 1
- 유속: 0.8 ml/min
- 검출기: UV 275 nm

Claims (22)

  1. 활성성분, 소성된 층상 이중 수산화물(layered double hydroxide), 폴리머 및 용매를 포함하는 성형(molding)용 화장료 조성물.
  2. 제1항에 있어서, 0.01 내지 50 중량%의 활성성분, 10 내지 60 중량%의 소성된 층상 이중 수산화물, 0.5 내지 20 중량%의 폴리머 및 10 내지 60 중량%의 용매를 포함하는 것을 특징으로 하는 성형용 화장료 조성물.
  3. 제2항에 있어서, 0.1 내지 48 중량%의 활성성분, 15 내지 55 중량%의 소성된 층상 이중 수산화물, 1 내지 18 중량%의 폴리머 및 15 내지 55 중량%의 용매를 포함하는 것을 특징으로 하는 성형용 화장료 조성물.
  4. 제3항에 있어서, 1 내지 45 중량%의 활성성분, 20 내지 50 중량%의 소성된 층상 이중 수산화물, 2 내지 15 중량%의 폴리머 및 20 내지 50 중량%의 용매를 포함하는 것을 특징으로 하는 성형용 화장료 조성물.
  5. 제1항에 있어서, 상기 활성성분이 보습제, 미백제, 주름개선제, 자외선 차단제, 육모제, 비타민 또는 그 유도체, 아미노산 또는 펩타이드, 항염증제, 여드름 치료제, 살균제, 여성호르몬제, 각질박리용해제 및 천연물로 이루어진 그룹으로부터 선택되는 하나 이상인 것을 특징으로 하는 성형용 화장료 조성물.
  6. 제1항에 있어서, 상기 소성된 층상 이중 수산화물이 다음의 구조식을 갖는 것을 특징으로 하는 성형용 화장료 조성물:
    [M2+ 1-x M3+ x(OH)2]x+(An-)x/n·mH2O
    상기 구조식에서,
    M2+와 M3+는 금속 양이온이고,
    An-는 음이온이며,
    0.2 ≤ x ≤ 0.33이고,
    n은 1 또는 2이며,
    m은 0.5 내지 4이다.
  7. 제6항에 있어서, M2+는 Ca2+, Mg2+, Zn2+, Ni2+, Mn2+, Co2+ 또는 Fe2+이고, M3+는 Al3+, Cr3+, Mn3+, Fe3+, Ga3+, Co3+ 또는 Ni3+이며, An-는 OH-, F-, Cl-, Br-, I-, NO3 -, CO3 2- 또는 SO4 2-인 것을 특징으로 하는 성형용 화장료 조성물.
  8. 제1항에 있어서, 상기 소성된 층상 이중 수산화물이 400 내지 1,200°C의 온도에서 소성되는 것을 특징으로 하는 성형용 화장료 조성물.
  9. 제8항에 있어서, 상기 소성된 층상 이중 수산화물이 500 내지 1,100°C의 온도에서 소성되는 것을 특징으로 하는 성형용 화장료 조성물.
  10. 제1항에 있어서, 상기 소성된 층상 이중 수산화물이 6시간 내지 16시간 동안 소성되는 것을 특징으로 하는 성형용 화장료 조성물.
  11. 제10항에 있어서, 상기 소성된 층상 이중 수산화물이 8시간 내지 14시간 동안 소성되는 것을 특징으로 하는 성형용 화장료 조성물.
  12. 제1항에 있어서, 상기 폴리머가 셀룰로오스, 메틸셀룰로오스, 하이드록시에틸셀룰로오스, 미결정 셀룰로오스, 나노셀룰로오스, 전분, 폴리메틸 메타크릴레이트, 폴리아크릴산, 아크릴레이트/C10-30 알킬 아크릴레이트 크로스폴리머, 폴리비닐알코올, 폴리비닐피롤리돈, 폴리글리콜라이드, 잔탄검, 아카시아검, 구아검, 카라기난검, 젤란검, 카라야검, 로커스트빈검, 히알루론산, 풀루란, 알긴산나트륨, 키토산, 한천, 젤라틴 및 콜라겐으로 이루어진 그룹으로부터 선택되는 하나 이상인 것을 특징으로 하는 성형용 화장료 조성물.
  13. 제1항에 있어서, 상기 용매가 물, 글리세린, 프로필렌 글리콜, 부틸렌 글리콜, 디글리세린, 디프로필렌 글리콜 및 이의 혼합물로부터 선택되는 것을 특징으로 하는 성형용 화장료 조성물.
  14. i) 층상 이중 수산화물을 400 내지 1,200°C의 온도에서 6시간 내지 16시간 동안 소성한 다음 냉각하고,
    ii) 활성성분 및 폴리머를 용매에 용해시키고, 상기 소성된 층상 이중 수산화물과 혼합하여 교반하는 것을 포함하는 성형용 화장료 조성물의 제조 방법.
  15. 제14항에 있어서, 상기 층상 이중 수산화물이 다음의 구조식을 갖는 것을 특징으로 하는 성형용 화장료 조성물의 제조 방법:
    [M2+ 1-x M3+ x(OH)2]x+(An-)x/n·mH2O
    상기 구조식에서,
    M2+와 M3+는 금속 양이온이고,
    An-는 음이온이며,
    0.2 ≤ x ≤ 0.33이고,
    n은 1 또는 2이며,
    m은 0.5 내지 4이다.
  16. 제15항에 있어서, M2+는 Ca2+, Mg2+, Zn2+, Ni2+, Mn2+, Co2+ 또는 Fe2+이고, M3+는 Al3+, Cr3+, Mn3+, Fe3+, Ga3+, Co3+ 또는 Ni3+이며, An-는 OH-, F-, Cl-, Br-, I-, NO3 -, CO3 2- 또는 SO4 2-인 것을 특징으로 하는 성형용 화장료 조성물의 제조 방법.
  17. 제14항에 있어서, 상기 층상 이중 수산화물을 500 내지 1,100°C의 온도에서 소성하는 것을 특징으로 하는 성형용 화장료 조성물의 제조 방법.
  18. 제14항에 있어서, 상기 층상 이중 수산화물을 8시간 내지 14시간 동안 소성하는 것을 특징으로 하는 성형용 화장료 조성물의 제조 방법.
  19. 제14항에 있어서, 상기 활성성분이 보습제, 미백제, 주름개선제, 자외선 차단제, 육모제, 비타민 또는 그 유도체, 아미노산 또는 펩타이드, 항염증제, 여드름 치료제, 살균제, 여성호르몬제, 각질박리용해제 및 천연물로 이루어진 그룹으로부터 선택되는 하나 이상인 것을 특징으로 하는 성형용 화장료 조성물의 제조 방법.
  20. 제14항에 있어서, 상기 폴리머가 셀룰로오스, 메틸셀룰로오스, 하이드록시에틸셀룰로오스, 미결정 셀룰로오스, 나노셀룰로오스, 전분, 폴리메틸 메타크릴레이트, 폴리아크릴산, 아크릴레이트/C10-30 알킬 아크릴레이트 크로스폴리머, 폴리비닐알코올, 폴리비닐피롤리돈, 폴리글리콜라이드, 잔탄검, 아카시아검, 구아검, 카라기난검, 젤란검, 카라야검, 로커스트빈검, 히알루론산, 풀루란, 알긴산나트륨, 키토산, 한천, 젤라틴 및 콜라겐으로 이루어진 그룹으로부터 선택되는 하나 이상인 것을 특징으로 하는 성형용 화장료 조성물의 제조 방법.
  21. 제14항에 있어서, 상기 용매가 물, 글리세린, 프로필렌 글리콜, 부틸렌 글리콜, 디글리세린, 디프로필렌 글리콜 및 이의 혼합물로부터 선택되는 것을 특징으로 하는 성형용 화장료 조성물의 제조 방법.
  22. 제14항에 있어서, 상기 단계 (ii)에서 활성성분, 폴리머, 용매 및 소성된 층상 이중 수산화물의 중량비가 각각 0.01 내지 50 중량%, 0.5 내지 20 중량%, 10 내지 60 중량% 및 10 내지 60 중량%인 것을 특징으로 하는 성형용 화장료 조성물의 제조 방법.
PCT/KR2020/005198 2019-04-23 2020-04-20 소성된 층상 이중 수산화물 및 폴리머를 포함하는 성형용 화장료 조성물 WO2020218787A1 (ko)