WO2020203389A1 - Film étiré, stratifié, vitrage et procédé de fabrication de film étiré - Google Patents

Film étiré, stratifié, vitrage et procédé de fabrication de film étiré Download PDF

Info

Publication number
WO2020203389A1
WO2020203389A1 PCT/JP2020/012601 JP2020012601W WO2020203389A1 WO 2020203389 A1 WO2020203389 A1 WO 2020203389A1 JP 2020012601 W JP2020012601 W JP 2020012601W WO 2020203389 A1 WO2020203389 A1 WO 2020203389A1
Authority
WO
WIPO (PCT)
Prior art keywords
stretched film
film
unit
semi
acid
Prior art date
Application number
PCT/JP2020/012601
Other languages
English (en)
Japanese (ja)
Inventor
篤 南谷
基 白神
英明 武田
Original Assignee
株式会社クラレ
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社クラレ filed Critical 株式会社クラレ
Priority to JP2021511465A priority Critical patent/JPWO2020203389A1/ja
Publication of WO2020203389A1 publication Critical patent/WO2020203389A1/fr

Abstract

La présente invention concerne un film étiré présentant d'excellentes propriétés de résistance à la chaleur et de transparence. Ce film étiré contient un polyamide semi-aromatique, le polyamide semi-aromatique comprenant un motif dicarboxylate et un motif diamine, le motif dicarboxylate comprenant un motif dicarboxylate de naphtalène, le motif diamine comprenant un motif diamine aliphatique comprenant de 4 à 12 atomes de carbone, et le coefficient de dilatation linéaire du film étiré à une température de 50 à 150 °C étant de -50×10-6/°C à 50×10-6/°C.
PCT/JP2020/012601 2019-03-29 2020-03-23 Film étiré, stratifié, vitrage et procédé de fabrication de film étiré WO2020203389A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2021511465A JPWO2020203389A1 (fr) 2019-03-29 2020-03-23

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019067440 2019-03-29
JP2019-067440 2019-03-29

Publications (1)

Publication Number Publication Date
WO2020203389A1 true WO2020203389A1 (fr) 2020-10-08

Family

ID=72668816

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/012601 WO2020203389A1 (fr) 2019-03-29 2020-03-23 Film étiré, stratifié, vitrage et procédé de fabrication de film étiré

Country Status (2)

Country Link
JP (1) JPWO2020203389A1 (fr)
WO (1) WO2020203389A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115884864A (zh) * 2021-03-31 2023-03-31 尤尼吉可株式会社 半芳香族聚酰胺膜及由其得到的层叠体

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012067172A1 (fr) * 2010-11-17 2012-05-24 ユニチカ株式会社 Film de polyamide semi-aromatique et son procédé de fabrication
JP2012515244A (ja) * 2009-01-16 2012-07-05 ディーエスエム アイピー アセッツ ビー．ブイ． フレキシブルプリント回路基板用ポリアミドフィルム
JP2013189495A (ja) * 2012-03-12 2013-09-26 Kurabo Ind Ltd プラスチックフィルムおよびその製造方法

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012515244A (ja) * 2009-01-16 2012-07-05 ディーエスエム アイピー アセッツ ビー．ブイ． フレキシブルプリント回路基板用ポリアミドフィルム
WO2012067172A1 (fr) * 2010-11-17 2012-05-24 ユニチカ株式会社 Film de polyamide semi-aromatique et son procédé de fabrication
JP2013189495A (ja) * 2012-03-12 2013-09-26 Kurabo Ind Ltd プラスチックフィルムおよびその製造方法

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115884864A (zh) * 2021-03-31 2023-03-31 尤尼吉可株式会社 半芳香族聚酰胺膜及由其得到的层叠体
US20230312847A1 (en) * 2021-03-31 2023-10-05 Unitika Ltd. Semiaromatic polyamide film and laminate obtained therefrom
CN115884864B (zh) * 2021-03-31 2024-04-09 尤尼吉可株式会社 半芳香族聚酰胺膜及由其得到的层叠体
US11965072B2 (en) * 2021-03-31 2024-04-23 Unitika Ltd. Semiaromatic polyamide film and laminate obtained therefrom

Also Published As

Publication number Publication date
JPWO2020203389A1 (fr) 2020-10-08

Similar Documents

Publication Publication Date Title
JP5881614B2 (ja) 半芳香族ポリアミドフィルム、およびその製造方法
JP7398288B2 (ja) 押出成形用組成物、そのフィルム、及び、フィルムの製造方法
JP6889966B1 (ja) 柔軟性ポリアミドフィルム
CN113825621B (zh) 半芳香族聚酰胺膜及其制造方法
KR101867495B1 (ko) 반방향족 폴리아미드 필름
KR20110114636A (ko) 투명 필름
JP2020180297A (ja) 半芳香族ポリアミドフィルム
JP6358837B2 (ja) 半芳香族ポリアミドフィルム
WO2020203389A1 (fr) Film étiré, stratifié, vitrage et procédé de fabrication de film étiré
JP7051181B1 (ja) ポリアミドおよびそれからなる成形体およびフィルムならびに該ポリアミドの製造方法
JP2019099626A (ja) 熱可塑性樹脂フィルムおよび積層体
WO2012173105A1 (fr) Film de polyamide copolymérisé
JP2009234131A (ja) 二軸延伸ポリアミド樹脂フィルムの製造方法
JP6474201B2 (ja) ポリアミドフィルム
JP7252602B2 (ja) 半芳香族ポリアミドフィルム
TWI856210B (zh) 柔軟性聚醯胺膜
CN115884864B (zh) 半芳香族聚酰胺膜及由其得到的层叠体
RU2786076C1 (ru) Пленка полуароматического полиамида и способ ее получения
TW202337977A (zh) 熱塑性樹脂膜
WO2023068121A1 (fr) Stratifié de film de polyamide
JP2024009620A (ja) 延伸ポリアミドフィルム

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20783850

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2021511465

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20783850

Country of ref document: EP

Kind code of ref document: A1