Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08C—TREATMENT OR CHEMICAL MODIFICATION OF RUBBERS
  • C08C19/00—Chemical modification of rubber
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F210/00—Copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
  • C08F210/04—Monomers containing three or four carbon atoms
  • C08F210/06—Propene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F8/00—Chemical modification by after-treatment
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K13/00—Use of mixtures of ingredients not covered by one single of the preceding main groups, each of these compounds being essential
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
  • C08K3/20—Oxides; Hydroxides
  • C08K3/22—Oxides; Hydroxides of metals
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/0008—Organic ingredients according to more than one of the "one dot" groups of C08K5/01 - C08K5/59
  • C08K5/0025—Crosslinking or vulcanising agents; including accelerators
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/04—Oxygen-containing compounds
  • C08K5/09—Carboxylic acids; Metal salts thereof; Anhydrides thereof
  • C08K5/098—Metal salts of carboxylic acids
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/04—Oxygen-containing compounds
  • C08K5/14—Peroxides
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/16—Nitrogen-containing compounds
  • C08K5/34—Heterocyclic compounds having nitrogen in the ring
  • C08K5/3467—Heterocyclic compounds having nitrogen in the ring having more than two nitrogen atoms in the ring
  • C08K5/3477—Six-membered rings
  • C08K5/3492—Triazines
  • C08K5/34924—Triazines containing cyanurate groups; Tautomers thereof
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L27/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers
  • C08L27/02—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L27/12—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers not modified by chemical after-treatment containing fluorine atoms
  • C08L27/18—Homopolymers or copolymers or tetrafluoroethene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F214/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen
  • C08F214/18—Monomers containing fluorine
  • C08F214/26—Tetrafluoroethene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F214/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen
  • C08F214/18—Monomers containing fluorine
  • C08F214/26—Tetrafluoroethene
  • C08F214/262—Tetrafluoroethene with fluorinated vinyl ethers
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
  • C08K3/20—Oxides; Hydroxides
  • C08K3/22—Oxides; Hydroxides of metals
  • C08K2003/2217—Oxides; Hydroxides of metals of magnesium
  • C08K2003/222—Magnesia, i.e. magnesium oxide
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
  • C08K3/20—Oxides; Hydroxides
  • C08K3/22—Oxides; Hydroxides of metals
  • C08K2003/2296—Oxides; Hydroxides of metals of zinc

Definitions

• the present invention relates to a composition, a crosslinked rubber and a method for producing the same.
• Crosslinked rubber obtained by cross-linking a fluoropolymer is excellent in heat resistance, chemical resistance, oil resistance, weather resistance, etc., and therefore, a sealing material (for example, O-ring, packing, oil seal, etc.) As a gasket) and a cushioning material, it is widely used in fields such as vehicles, ships, aircraft, general machinery, and construction.
• a sealing material for example, O-ring, packing, oil seal, etc.
• a gasket As a method for producing such a crosslinked rubber, Patent Document 1 includes a fluorine-containing copolymer having a unit based on tetrafluoroethylene and a unit based on propylene, an organic peroxide (crosslinking agent), a crosslinking aid and the like.
• a method of cross-linking a composition to obtain a cross-linked rubber is disclosed.
• transparent crosslinked rubber has been required in various fields.
• a member formed of transparent crosslinked rubber when a member formed of transparent crosslinked rubber is used, there is an advantage that visibility from the outside is improved, and detection of manufacturing abnormality and maintenance of equipment are facilitated.
• the crosslinked rubber when the crosslinked rubber is transparent, it can be used as a material for a microchannel device or the like in a biomimetic chip. This is because the microchannel device is required to have chemical resistance and softness like a living body, and also to be transparent for observing the state of cells from the outside.
• one of the rubber properties required for crosslinked rubber is that it has excellent tensile strength.
• the present inventor evaluated a crosslinked rubber as described in Patent Document 1, and found that the tensile strength was excellent depending on the composition of the composition used at the time of producing the crosslinked rubber. We found that there was room for improvement in transparency.
• the present invention has been made in view of the above problems, and an object of the present invention is to provide a crosslinked rubber having excellent tensile strength and transparency and a method for producing the same.
• the present inventors have determined the content of the cross-linking agent and the cross-linking aid in the composition of the cross-linked rubber in which the fluoro-containing copolymer is cross-linked in the composition.
• a crosslinked rubber having excellent tensile strength and transparency can be obtained by setting the content within a specific range, and have reached the present invention.
• a composition containing a fluorine-containing copolymer, a cross-linking agent, a cross-linking aid, and an antacid is a copolymer having a unit based on tetrafluoroethylene and a unit based on propylene.
• the content of the cross-linking agent in the composition is 0.03 to 1.5 parts by mass with respect to 100 parts by mass of the fluorine-containing copolymer.
• the composition is characterized in that the content of the cross-linking aid is 0.1 to 3.5 parts by mass with respect to 100 parts by mass of the fluorine-containing copolymer.
• RA represents an organic group having 10 to 30 carbon atoms
• n represents an integer of 2 or 3
• M represents an alkaline earth metal, Zn, Cd, Co, Sn, Cu, Pb, Ni or Al. Shown.
• the fluorine-containing copolymer has an iodine atom and has an iodine atom.
• the composition according to [1] or [2], wherein the mass ratio of the content of the iodine atom to the content of the cross-linking agent in the composition is 0.20 to 4.0.
• the fluorine-containing copolymer has an iodine atom and has an iodine atom.
• the cross-linked rubber according to any one of [1] to [4], wherein the mass ratio of the content of the cross-linking agent to the content of the cross-linking aid in the composition is 0.01 to 8.5. Manufacturing method.
• a crosslinked rubber which comprises crosslinking a fluorine-containing copolymer in a composition containing a fluorine-containing copolymer, a cross-linking agent, a cross-linking aid, and an acid-receiving agent to obtain a cross-linked rubber. It ’s a manufacturing method,
• the fluorine-containing copolymer is a copolymer having a unit based on tetrafluoroethylene and a unit based on propylene.
• the content of the cross-linking agent in the composition is 0.03 to 1.5 parts by mass with respect to 100 parts by mass of the fluorine-containing copolymer.
• the content of the cross-linking aid is 0.1 to 3.5 parts by mass with respect to 100 parts by mass of the fluorine-containing copolymer.
• a method for producing a crosslinked rubber, wherein the total light transmittance of the crosslinked rubber is 60 to 100%.
• the fluorine-containing copolymer is a copolymer having a unit based on tetrafluoroethylene and a unit based on perfluoro (alkyl vinyl ether).
• the content of the cross-linking agent in the composition is 0.03 to 0.7 parts by mass with respect to 100 parts by mass of the fluorine-containing copolymer.
• the composition is characterized in that the content of the cross-linking aid in the composition is 0.1 to 2.5 parts by mass with respect to 100 parts by mass of the fluorine-containing copolymer.
• the fluorine-containing copolymer has an iodine atom and has an iodine atom.
• composition according to [8] wherein the mass ratio of the content of the iodine atom to the content of the cross-linking agent in the composition is 0.3 to 1.2.
• the fluorine-containing copolymer has an iodine atom and has an iodine atom.
• the composition according to [8] or [9], wherein the mass ratio of the content of the iodine atom to the content of the cross-linking aid in the composition is 0.3 to 1.2.
• the total content of the components other than the fluorine-containing copolymer in the composition is 0.5 to 20 parts by mass with respect to 100 parts by mass of the fluorine-containing copolymer [8]. ] To [11]. [13] A crosslinked rubber in which the fluorine-containing copolymer in any of the compositions [8] to [12] is crosslinked. [14] A method for producing a crosslinked rubber, which comprises cross-linking a fluorine-containing copolymer in a composition containing a fluorine-containing copolymer, a cross-linking agent, and a cross-linking aid to obtain a cross-linked rubber.
• the fluorine-containing copolymer is a copolymer having a unit based on tetrafluoroethylene and a unit based on perfluoro (alkyl vinyl ether).
• the content of the cross-linking agent in the composition is 0.03 to 0.7 parts by mass with respect to 100 parts by mass of the fluorine-containing copolymer.
• the content of the cross-linking aid in the composition is 0.1 to 2.5 parts by mass with respect to 100 parts by mass of the fluorine-containing copolymer.
• a method for producing a crosslinked rubber, wherein the total light transmittance of the crosslinked rubber is 70 to 100%.
• the meanings of the terms in the present invention are as follows.
• the "unit” in the copolymer is an atomic group derived from one molecule of the monomer, which is directly formed by polymerizing a monomer, and an atomic group obtained by chemically converting a part of the atomic group. It is a general term for.
• the "unit based on a monomer” is also simply referred to as a “unit” below.
• Rubberer means rubber exhibiting properties as defined by JIS K 6200 (2008) and is distinguished from “resin”.
• the crosslinked rubber in the first embodiment of the present invention is a composition containing a fluorine-containing copolymer (hereinafter, also referred to as “copolymer A”), a crosslinking agent, a crosslinking aid, and an acid receiving agent (hereinafter, also referred to as “copolymer A”).
• a crosslinked rubber hereinafter, also referred to as “rubber A” obtained by cross-linking the copolymer A in the “composition A”
• the copolymer A is tetrafluoroethylene.
• the content of the cross-linking agent in the composition A is 0.03 to 1.5 parts by mass with respect to 100 parts by mass of the copolymer A.
• the content of the cross-linking aid is 0.1 to 3.5 parts by mass with respect to 100 parts by mass of the copolymer A, and the total light transmittance of the rubber A is 60 to 100. %.
• the crosslinked rubber of the first embodiment is excellent in tensile strength and transparency. The details of this reason have not been clarified, but it is presumed to be due to the following reasons. Fluorine-containing copolymers tend to be partially crystallized by cross-linking as compared with silicone resins and the like. Therefore, it is considered that if the number of crosslinked structures increases in the crosslinked rubber in which the fluorine-containing copolymer is crosslinked, microcrystalline portions are likely to be formed, and as a result, the crosslinked rubber looks opaque.
• the present inventors have reduced the content of the cross-linking agent and the cross-linking aid used for cross-linking the fluorine-containing copolymer as compared with the conventional case, thereby maintaining excellent tensile strength and excellent transparency.
• rubber can be obtained. That is, by reducing the content of the cross-linking agent and the cross-linking aid to the extent that the characteristics as a rubber are not lost, the microcrystal portion in the cross-linked rubber remains a cross-linking point to the extent that excellent tensile strength is maintained. It is presumed that a crosslinked rubber having excellent transparency was obtained.
• the composition used for producing the crosslinked rubber will be described, and then the crosslinked rubber and the method for producing the crosslinked rubber will be described.
• composition A contains a copolymer A, a cross-linking agent, a cross-linking aid, and an acid-receiving agent.
• the copolymer A is a copolymer having a tetrafluoroethylene (hereinafter, also referred to as “TFE”) unit and a propylene (hereinafter, also referred to as “P”) unit.
• TFE tetrafluoroethylene
• P propylene
• the copolymer A may have a unit based on a monomer other than TFE and P, and as a specific example thereof, a unit based on a monomer represented by the following formula (A1) (hereinafter, "" Formula (A1) unit ”), monomer-based unit represented by the following formula (A2) (hereinafter, also referred to as“ formula (A2) unit ”), perfluoro (alkyl vinyl ether) (hereinafter, hereafter.
• PAVE vinylidene fluoride
• HFP hexafluoropropylene
• CTFE chlorotrifluoroethylene
• R 1 , R 2 and R 3 independently represent a hydrogen atom, a fluorine atom or a methyl group
• a represents an integer of 2 to 6
• R 4 is an a-valent carbon number of carbon 1
• 2 or 3 is preferable for a, and 2 is particularly preferable.
• the plurality of R 1 , the plurality of R 2 and the plurality of R 3 may be the same or different from each other, and it is particularly preferable that they are the same as each other.
• R 1, R 2 and R 3 is a fluorine atom or a hydrogen atom, all of R 1, R 2 and R 3 are a fluorine atom It is more preferable that some or all of them are hydrogen atoms, and it is particularly preferable that all of R 1 , R 2 and R 3 are fluorine atoms.
• R 4 may be linear, branched chain, or cyclic, preferably linear or branched chain, and particularly preferably linear.
• the carbon number of R 4 is preferably 2 to 8, more preferably 3 to 7, further preferably 3 to 6, and particularly preferably 3 to 5.
• the number of etheric oxygen atoms in R 4 is preferably 0-3, 1 or 2 are particularly preferred. It is preferred that one or two etheric oxygen atoms are present at the ends of the perfluoroalkylene group. When R 4 is in these suitable ranges, the tensile strength of the rubber A is superior and the compression set at a high temperature is small.
• a vinyl group or a trifluoro is attached to each of both ends of a perfluoroalkylene group having 1 to 10 carbon atoms with or without etheric oxygen.
• examples thereof include compounds to which a vinyl group is bonded.
• the copolymer A has at least one of the units based on these monomers, the crosslinkability is excellent, the crosslinked rubber A is excellent in tensile strength, and the compression set at high temperature is small.
• R f represents a perfluoroalkyl group containing an ethereal oxygen atom having 1 to 8 carbon atoms.
• the carbon number of R f is preferably 1 to 6, and particularly preferably 1 to 5.
• monomer represented by the formula (A2) include perfluoro (3,6-dioxa-1-heptene), perfluoro (3,6-dioxa-1-octene), and perfluoro (5-). Methyl-3,6-dioxa-1-nonene).
• R f1 represents a perfluoroalkyl group having 1 to 8 carbon atoms.
• the carbon number of R f1 is preferably 1 to 6, and particularly preferably 1 to 5.
• PAVE perfluoro (methyl vinyl ether) (hereinafter, also referred to as “PMVE”), perfluoro (ethyl vinyl ether) (hereinafter, also referred to as “PVE”), and perfluoro (propyl vinyl ether) (hereinafter, also referred to as “PVE”).
• PMVE perfluoro (methyl vinyl ether)
• PVE perfluoro (ethyl vinyl ether)
• PVE perfluoro (propyl vinyl ether)
• PPVE perfluoro (propyl vinyl ether)
• the content of TFE units is preferably 30 to 70 mol%, particularly preferably 40 to 60 mol%, based on all the units of the copolymer A.
• the content thereof is preferably 0.03 to 0.5 mol%, preferably 0.05 to 0.4 mol%, based on all the units of the copolymer A.
• % Is more preferable, and 0.1 to 0.3 mol% is particularly preferable.
• it is at least the lower limit of the above range the cross-linking reactivity is excellent, the rubber A is excellent in tensile strength, and the compression set at high temperature is smaller.
• the content thereof is preferably 1 to 40 mol%, particularly preferably 10 to 30 mol%, based on all the units of the copolymer A.
• the content thereof is preferably 5 to 50 mol%, particularly preferably 10 to 30 mol%, based on all the units of the copolymer A.
• the total content of the TFE unit and the content of the P unit is preferably 40 to 100 mol%, particularly preferably 60 to 100 mol%, based on all the units of the copolymer A.
• Combination 1 Combination of TFE unit and P unit
• Combination 2 Combination of TFE unit, P unit and PAVE unit (preferably, formula (A3) unit, particularly preferably PPVE unit or PMVE unit)
• Combination 3 Combination of TFE unit, P unit and formula (A1) unit
• Combination 4 TFE unit, P unit, formula (A1) unit and PAVE unit (preferably formula (A3) unit, particularly preferably , PPVE unit or PMVE unit)
• Combination 5 Combination of TFE unit, P unit, formula (A1) unit, and VdF unit Among these, combination 1 and combination 2 in terms of elongation at cutting. , Combination 3 is preferable, and Combination 1 and Combination 3 are particularly preferable.
• the copolymerization composition in the combinations 1 to 5 is preferably the following molar ratio.
• the molar ratio is as follows, the cross-linking reactivity of the copolymer is further excellent, and the mechanical properties, heat resistance, chemical resistance, oil resistance, and weather resistance of rubber A are further excellent.
• the copolymer composition in Combination 3 is more preferably the following molar ratio.
• the copolymer composition in combination 4 is more preferably the following molar ratio.
• Combination 4: TFE unit / P unit / formula (A1) unit / PAVE unit 40 to 58/40 to 50/0.01 to 2/10 to 20 (molar ratio)
• the copolymer composition in combination 5 is more preferably the following molar ratio.
• the copolymer A may have a unit based on a monomer other than the above.
• examples of other monomers include fluorine-containing monomers and non-fluorine monomers.
• non-fluorinated monomer examples include ⁇ -olefins such as isobutylene and penten, vinyl ethers such as methyl vinyl ether, ethyl vinyl ether, propyl vinyl ether and butyl vinyl ether, vinyl acetate, vinyl propionate, vinyl butyrate and vinyl caproate. , Vinyl esters such as vinyl caprylate.
• the content thereof is preferably 0.001 to 2.0 mol%, preferably 0.01 to 1 with respect to all the units of the copolymer A. 0.0 mol% is more preferable, and 0.01 to 0.5 mol% is particularly preferable.
• a monomer having an iodine atom may be used as another monomer.
• an iodine atom can be easily introduced into the side chain of the copolymer A.
• Specific examples of the monomer having an iodine atom include iodoethylene, 4-iodo-3,3,4,5-tetrafluoro-1-butene, 2-iodo-1,1,2,2-tetrafluoro-.
• the copolymer A has a unit based on a monomer having an iodine atom, the content thereof is preferably 0.001 to 2.0 mol%, preferably 0.01, based on all the units of the copolymer A. ⁇ 1.0 mol% is more preferable, and 0.01 to 0.5 mol% is particularly preferable.
• the copolymer A preferably has an iodine atom, and particularly preferably has an iodine atom at the end of the copolymer A (polymer chain).
• the terminal means both the end of the main chain and the end of the branched chain of the copolymer A.
• the iodine atom include an iodine atom derived from an iodine compound that functions as a chain transfer agent described later, and an iodine atom in a unit based on the above-mentioned monomer having an iodine atom, which is an iodine atom derived from an iodine compound. Is preferable.
• the content thereof is preferably 0.01 to 5.0% by mass, more preferably 0.05 to 2.0% by mass, based on the total mass of the copolymer A. It is preferable, and 0.05 to 1.0% by mass is particularly preferable.
• the content of iodine atoms is in the above range, the cross-linking reactivity of the copolymer A is more excellent, and the mechanical properties of the rubber A are more excellent.
• the mass ratio of the iodine atom content to the content of the cross-linking agent (described later) in the composition A is 0.
• the copolymer A has an iodine atom
• the mass ratio of the iodine atom content to the content of the cross-linking aid (described later) in the composition A is determined. It is preferably 0.05 to 2.5, more preferably 0.15 to 1.6, even more preferably 0.20 to 1.5, and particularly preferably 0.30 to 1.3.
• the crosslinking reaction is likely to proceed, and when it is at least the upper limit of the above range, the tensile strength is more excellent.
• the content of the copolymer A is preferably 75 to 99% by mass, more preferably 85 to 99% by mass, further preferably 95 to 99% by mass, and 97 to 99% by mass with respect to the total mass of the composition A. Is particularly preferable.
• An example of a method for producing the copolymer A is a method of copolymerizing the above-mentioned monomers in the presence of a chain transfer agent and a radical polymerization initiator.
• the chain transfer agent is preferably an iodine compound, and particularly preferably an iodine compound represented by the formula RI 2 .
• R preferably represents an alkylene group or a perfluoroalkylene group having 3 or more carbon atoms, more preferably 3 to 8 carbon atoms.
• Specific examples of the iodine compound represented by the formula RI 2 include 1,3-diiodopropane, 1,4-diiodobutane, 1,6-diiodohexane, 1,8-diiodooctane, and 1,3-di.
• Examples thereof include iodoperfluoropropane, 1,4-diiodoperfluorobutane, 1,6-diiodoperfluorohexane, and 1,8-diiodoperfluorooctane.
• the iodine compound an iodine compound having a perfluoroalkylene group is preferable, and 1,4-diiodoperfluorobutane is particularly preferable.
• an iodine atom can be introduced into the main chain terminal of the copolymer A.
• the end of the polymer chain having an iodine atom may be the end of the main chain or the end of the branched chain.
• a water-soluble polymerization initiator and a redox polymerization initiator are preferable.
• the water-soluble polymerization initiator include persulfates such as ammonium persulfate, sodium persulfate and potassium persulfate, and organic polymerization initiators such as disuccinic acid peroxide and azobisisobutylamidine dihydrochloride. Among these, persulfates are preferable, and ammonium persulfate is more preferable.
• the redox polymerization initiator include a polymerization initiator that is a combination of persulfates and a reducing agent.
• a polymerization initiator capable of polymerizing each monomer in a polymerization temperature range of 0 to 60 ° C. is preferable.
• the persulfate constituting the redox polymerization initiator include alkali metal salts of persulfate such as ammonium persulfate, sodium persulfate, and potassium persulfate, and ammonium persulfate is preferable.
• the reducing agent to be combined with persulfates include thiosulfate, sulfite, hydrogen sulfite, pyrosulfite, and hydroxymethanesulfinate, preferably hydroxymethanesulfinate, and sodium hydroxymethanesulfinate. Salt is particularly preferred.
• the cross-linking agent is used to cross-link the copolymer A.
• an organic peroxide is preferable because the cross-linking reactivity of the copolymer A is more excellent.
• organic peroxides include dialkyl peroxides, ⁇ , ⁇ '-bis (tert-butylperoxy) -p-diisopropylbenzene, ⁇ , ⁇ '-bis (tert-butylperoxy) -m-.
• Classes, ⁇ , ⁇ '-bis (tert-butylperoxy) -p-diisopropylbenzene, ⁇ , ⁇ '-bis (tert-butylperoxy) -m-diisopropylbenzene are preferable.
• dialkyl peroxides include 1,1-di (tert-butylperoxy) -3,3,5-trimethylcyclohexane, 2,5-dimethylhexane-2,5-dihydroxyperoxide, and tert-butyl.
• Peroxymaleic acid tert-butyl peroxyisopropyl carbonate, tert-butyl peroxide, 2,5-dimethyl-2,5-di (tert-butylperoxy) hexane, 2,5-dimethyl-2,5- Examples thereof include di (tert-butylperoxy) -3-hexine, and as the dialkyl peroxides, dicumylperoxide and 2,5-dimethyl-2,5-di (tert-butylperoxy) hexane are preferable.
• the cross-linking agent may contain only one type or two or more types.
• the content of the cross-linking agent in the composition A is 0.03 to 1.5 parts by mass, preferably 0.03 to 0.7 parts by mass, with respect to 100 parts by mass of the copolymer A. 1 to 0.6 parts by mass is more preferable, and 0.3 to 0.5 parts by mass is particularly preferable. When it is at least the lower limit of the above range, the tensile strength of the rubber A is more excellent, and when it is at least the upper limit of the above range, the transparency of the rubber A is more excellent.
• the cross-linking aid is used to improve the cross-linking reactivity of the copolymer A.
• the cross-linking aid is preferably a compound having two or more reactive functional groups in the same molecule.
• Specific examples of the reactive functional group include a carbon-carbon double bond-containing group, a halogen atom, an acid anhydride residue, a carboxy group, an amino group, a cyano group, and a hydroxyl group.
• the plurality of reactive functional groups present in the same molecule of the cross-linking aid may be the same or different from each other.
• the carbon-carbon double bond-containing group examples include an alkenyl group such as a vinyl group, an allyl group and a metalyl group, an unsaturated acyl group such as an acryloyl group and a methacryloyl group, and a maleimide group.
• the carbon-carbon double bond-containing group is preferably an alkenyl group having 2 to 4 carbon atoms, and particularly preferably an allyl group.
• the cross-linking aid include triallyl cyanurate, triallyl isocyanurate, trimetalyl isocyanurate, 1,3,5-triacrylloylhexahydro-1,3,5-triazine, triallyl trimellitate, m.
• -Phenylenediamine bismaleimide p-quinonedioxime, p, p'-dibenzoylquinonedioxime, dipropargyl terephthalate, diallyl phthalate, N, N', N'', N''-tetraallyl terephthalamide
• vinyl group-containing siloxane oligomers polymethylvinylsiloxane, polymethylphenylvinylsiloxane, etc.
• triallyl cyanurate, triallyl isocyanurate, and trimetalyl isocyanurate are preferable, and triallyl isocyanurate is particularly preferable.
• the cross-linking aid may contain only one type or two or more types.
• the content of the cross-linking aid is 0.1 to 3.5 parts by mass, preferably 0.1 to 2.5 parts by mass, based on 100 parts by mass of the copolymer A. 0.1 to 2.0 parts by mass is more preferable, and 0.15 to 1.5 parts by mass is particularly preferable.
• the tensile strength of the rubber A is more excellent
• the transparency of the rubber A is more excellent.
• the mass ratio of the content of the cross-linking agent to the content of the cross-linking aid is preferably 0.01 to 8.5, preferably 0.4. ⁇ 7 is more preferable, 0.4 to 7.0 is further preferable, 0.4 to 5.0 is even more preferable, and 0.5 to 2.0 is particularly preferable. Within the above range, unreacted cross-linking aid is unlikely to remain, and the cross-linking reaction proceeds satisfactorily, so that transparency is more excellent.
• the total content of the cross-linking agent and the cross-linking aid is preferably 5.0 parts by mass or less, more preferably 2.0 parts by mass or less, based on 100 parts by mass of the copolymer A. It is more preferably 1.8 parts by mass or less, and particularly preferably 1.5 parts by mass or less. If it is equal to or less than the above value, the transparency of the rubber A is more excellent.
• the total content of the cross-linking agent and the cross-linking aid is preferably 0.1 part by mass or more, particularly preferably 0.5 parts by mass or more, based on 100 parts by mass of the copolymer A. When it is equal to or more than the above value, the tensile strength of the rubber A is more excellent.
• the antacid is used to improve the cross-linking reactivity of the copolymer A.
• the acid receiving agent is preferably a monovalent or divalent metal oxide, a monovalent or divalent metal hydroxide, or a fatty acid metal salt.
• Specific examples of the monovalent or divalent metal oxide include zinc oxide, magnesium oxide, sodium oxide, calcium oxide, barium oxide, lead oxide, and copper oxide.
• Specific examples of the monovalent or divalent metal hydroxide include magnesium hydroxide, aluminum hydroxide, and calcium hydroxide. Hydrotalcite is also preferably used as an antacid.
• the fatty acid metal salt include a fatty acid metal salt represented by the following formula (A4).
• the acid receiving agent is preferably at least one selected from the group consisting of zinc oxide, magnesium oxide and a fatty acid metal salt represented by the following formula (A4) from the viewpoint of further improving the cross-linking reactivity.
• RA represents an organic group having 10 to 30 carbon atoms
• n represents an integer of 2 or 3
• M represents an alkaline earth metal, Zn, Cd, Co, Sn, Cu, Pb, Ni or Al.
• the organic group represented by RA may be saturated or unsaturated, and an aliphatic hydrocarbon group is preferable, a linear aliphatic hydrocarbon group is more preferable, and a saturated linear aliphatic hydrocarbon group is particularly preferable.
• the organic group represented by RA has 10 to 30 carbon atoms, preferably 10 to 25, more preferably 10 to 20, and particularly preferably 12 to 18.
• the metal salt represented by the formula (A4) is a metal salt of a higher fatty acid generally known as a processing aid.
• the fatty acid may be a naturally derived component such as an animal fatty acid or an artificially synthesized component. Further, it may be a mixture of fatty acids having two or more kinds of carbon atoms.
• the metal salt represented by the formula (A4) include calcium stearate, zinc stearate, barium stearate, magnesium stearate, aluminum stearate, cadmium stearate, cobalt stearate, tin stearate, and lead stearate. , Copper stearate, nickel stearate, lithium stearate, calcium ricinolate, zinc palmitate, aluminum myristate.
• the metal salt represented by the formula (A4) calcium stearate, zinc stearate, barium stearate, magnesium stearate, aluminum stearate are preferable, calcium stearate and aluminum stearate are more preferable, and calcium stearate is preferable.
• the antacid may contain only one type or two or more types.
• the content of the antacid in the composition A is preferably 0.01 to 1.5 parts by mass, more preferably 0.03 to 1.0 parts by mass with respect to 100 parts by mass of the copolymer A. 0.05 to 0.6 parts by mass is particularly preferable. When it is at least the lower limit of the above range, the tensile strength of the rubber A is more excellent, and when it is at least the upper limit of the above range, the transparency of the rubber A is more excellent.
• composition A may contain components other than the above as long as the effects of the present invention are not impaired.
• processing aids eg, fatty acid esters
• fillers and reinforcing agents eg, carbon black, barium sulfate, calcium metasilicate, calcium carbonate, titanium oxide, silicon dioxide, clay, talc.
• Sulfurizer, scorch retarder eg, phenolic hydroxyl group-containing compounds such as orthophenylphenol, bisphenol A, quinones such as hydroquinone, 2,4-di (3-isopropylphenyl) -4-methyl-1- ⁇ -Methylstyrene dimers such as pentene
• scorch retarder eg, phenolic hydroxyl group-containing compounds such as orthophenylphenol, bisphenol A, quinones such as hydroquinone, 2,4-di (3-isopropylphenyl) -4-methyl-1- ⁇ -Methylstyrene dimers such as pentene
• composition A may contain the above-mentioned other components, but it is preferable that the composition A does not substantially contain the other components from the viewpoint of the more excellent transparency of the rubber A.
• composition A does not substantially contain other components means that the total content of the other components in the composition A is 0, based on 100 mass of the copolymer A. It means that it is 1 part by mass or less, preferably 0.01 part by mass or less, and particularly preferably 0 part by mass.
• composition A is substantially free of other components, it is easy to make the total light transmittance of the rubber A in the range of 60 to 100%.
• the refractive index of the crosslinked rubber a obtained by cross-linking the composition a composed of only the fluorine-containing copolymer, the cross-linking agent, the cross-linking aid and the acid-receiving agent, and the refractive index of other components are different.
• the contents are equivalent, the content of other components may be outside the above range. This is because when the refractive index of the crosslinked rubber a and the refractive index of other components are the same, it is presumed that the total light transmittance of the rubber A is unlikely to decrease and the influence on the transparency of the rubber A is small.
• the total content of the other components in the composition A is 20 parts by mass or less with respect to 100 mass by mass of the copolymer A. It is preferably 15 parts by mass or less, more preferably 10 parts by mass or less, and particularly preferably 5 parts by mass or less.
• the total content of the components other than the copolymer A in the composition A, that is, the cross-linking agent, the cross-linking aid, the acid-receiving agent and the other components is 0.5 to 100 parts by mass of the copolymer A. 20 parts by mass is preferable, 0.5 to 10 parts by mass is more preferable, 0.5 to 1.8 parts by mass is further preferable, and 0.5 to 1.5 parts by mass is particularly preferable. When it is at least the lower limit of the above range, the tensile strength of the rubber A is more excellent, and when it is at least the upper limit of the above range, the transparency of the rubber A is more excellent.
• Examples of the method for preparing the composition A include a method of mixing the above components. Mixing of each component can be carried out using a rubber mixing device such as a roll, a kneader, a Banbury mixer or an extruder. Further, after obtaining a mixture obtained by mixing each of the above components, the mixture may be molded. That is, the composition A may be a molded product. Specific examples of the molding method of the mixture include compression molding, injection molding, extrusion molding, calendar molding, or a method of dissolving the mixture in a solvent and dipping or coating it.
• the rubber A is obtained by cross-linking the copolymer A in the composition A.
• a method for cross-linking the copolymer A in the composition A a method of heating the composition A is preferable.
• Specific examples of the heating method include heat press crosslinking, steam crosslinking, and hot air crosslinking, which can be appropriately selected in consideration of the shape and use of the composition A.
• the heating conditions are preferably 100 to 400 ° C. for 1 second to 24 hours.
• the rubber formed by heating the composition A and primary cross-linking may be further heated and secondary cross-linked.
• Secondary cross-linking can stabilize or improve the mechanical properties, compression set, and other properties of rubber.
• the heating conditions for the secondary cross-linking are preferably 100 to 300 ° C. for 30 minutes to 48 hours.
• Examples of the cross-linking method other than heating the copolymer A in the composition A include a method of irradiating the composition A with radiation to cross-link the composition A.
• Specific examples of the radiation to be irradiated include electron beams and ultraviolet rays.
• the rubber A Since the rubber A is obtained from the composition A, it exhibits high transparency. As an index showing the transparency of the rubber A, the total light transmittance can be mentioned.
• the total light transmittance (%) means the transmittance of light including all of the parallel component and the diffusing component among the light transmitted when the test piece is exposed to light.
• the total light transmittance of the rubber A is 60 to 100%, and from the viewpoint that the transparency of the rubber A is more excellent, 70% or more is preferable, 73% or more is more preferable, 75% or more is particularly preferable, and rubber. From the viewpoint of more excellent tensile strength of A, 99% or less is preferable, 95% or less is more preferable, and 93% or less is particularly preferable.
• the total light transmittance of rubber A in the present invention is a value measured in accordance with JIS K7361-1: 1997 using a plate-shaped molded product (thickness 2 mm) of rubber A.
• the parallel light transmittance means the transmittance of the parallel component excluding the diffusion component among the light transmitted by irradiating the test piece with light. It can be said that the higher the parallel light transmittance, the more excellent the transparency of the rubber A.
• the parallel light transmittance of the rubber A is preferably 5 to 100%, more preferably 30% or more, further preferably 40% or more, particularly preferably 45% or more, and particularly preferably 45% or more, because the transparency of the rubber A is more excellent. From the viewpoint of more excellent tensile strength, 99% or less is more preferable, 95% or less is further preferable, and 90% or less is particularly preferable.
• the parallel light transmittance of the rubber A in the present invention is a value measured according to JIS K7361-1: 1997 using a plate-shaped molded product (thickness 2 mm) of the rubber A.
• a haze value can be mentioned as an index showing the transparency of the rubber A.
• the haze value (%) is the diffused light excluding the parallel component with respect to the transmittance (total light transmittance Tt) of the light beam transmitted by irradiating the test piece with light and including all the parallel component and the diffused component. It means the ratio (100 ⁇ Td / Tt [%]) of the transmittance (diffusion transmittance Td) of.
• the haze value indicates the turbidity (cloudiness) of the object to be measured, and it can be said that the smaller the haze value, the smaller the turbidity and the more excellent the transparency of the rubber A.
• the haze value of the rubber A is preferably 0 to 90%, more preferably 65% or less, further preferably 50% or less, particularly preferably 41% or less, and rubber A from the viewpoint of more excellent transparency of the rubber A. From the viewpoint of more excellent tensile strength, 0.5% or more is more preferable, 0.7% or more is further preferable, and 1% or more is particularly preferable. When the haze value is 90% or less, the transparency when observing the rubber A is more excellent.
• the haze value of rubber A in the present invention is a value measured in accordance with JIS K7136: 2000 using a plate-shaped molded product (thickness 2 mm) of rubber A.
• cross-linking degree As an index of the cross-linking property of the rubber A, MH - ML (hereinafter, also referred to as “cross-linking degree”) measured by the method of Examples described later can be mentioned. It can be said that the larger the value of the degree of cross-linking, the more the cross-linked structure of the rubber A, and the more microcrystal portions are present in the rubber A. Therefore, when the value of the degree of cross-linking is small, it can be said that the transparency of the rubber A is excellent, and when the value of the degree of cross-linking is large, it can be said that the rubber property of the rubber A is excellent (for example, the tensile strength is high).
• the degree of cross-linking of the rubber A is preferably 3 to 70 dNm, more preferably 3 to 50 dNm, more preferably 3 to 45 dNm, and particularly preferably 5 to 40 dNm.
• the degree of cross-linking of rubber A is within the above range, both rubber properties and transparency can be achieved at a high level.
• the hardness (Shore-A) of the rubber A is preferably 40 to 70, more preferably 40 to 64, and particularly preferably 45 to 60. When it is equal to or higher than the lower limit of the above range, the performance as a sealing material is sufficiently exhibited. When it is not more than the upper limit value in the above range, the amount of microcrystalline portions present in the rubber A is sufficiently small, and the transparency is excellent.
• the hardness (Shore-A) of rubber A is a value measured using a plate-shaped molded product (thickness 2 mm) of rubber A and a type A durometer in accordance with JIS K6253-3: 2012. ..
• the tensile strength of the rubber A is preferably 1 to 25 MPa, particularly preferably 1 to 15 MPa. When the tensile strength of the rubber A is within the above range, the rubber properties and transparency of the rubber A are more excellent.
• the 100% modulus of rubber A is preferably 0.2 to 5.0 MPa, particularly preferably 0.5 to 2.0 MPa, from the viewpoint of excellent rubber characteristics.
• the elongation rate of the rubber A at the time of cutting is preferably 250 to 1000%, particularly preferably 350 to 1000%, from the viewpoint of excellent rubber characteristics.
• the tensile strength, 100% modulus, and elongation at cutting of rubber A were measured in accordance with JIS K6251: 2017 using a sample obtained by punching a plate-shaped molded product (thickness 2 mm) of rubber A with a No. 3 dumbbell. Value.
• Rubber A is suitable for materials such as O-rings, sheets, gaskets, oil seals, diaphragms, and V-rings.
• materials such as O-rings, sheets, gaskets, oil seals, diaphragms, and V-rings.
• heat-resistant and chemical-resistant sealing materials heat-resistant and oil-resistant sealing materials, wire coating materials, sealing materials for semiconductor devices, corrosion-resistant rubber paints, sealing materials for urea-based greases, rubber paints, adhesive rubbers, hoses, tubes, etc.
• Calendar sheet (roll), sponge, rubber roll, oil drilling member, heat dissipation sheet, solution cross-linking body, rubber sponge, bearing seal (urea grease resistant, etc.), lining (chemical resistant), automotive insulating sheet, insulation for electronic devices Sheets, rubber bands for watches, packing for endoscopes (amine resistant), bellows hose (processed from calendar sheets), water heater packing / valves, fenders (marine civil engineering, ships), fibers / non-woven fabrics (protective clothing, etc.) ), Base sealant, rubber gloves, uniaxial eccentric screw pump stator, urea SCR system parts, vibration isolator, vibration damping agent, sealant, additive to other materials, toy applications. Since rubber A has excellent transparency, it is particularly suitable for applications that require visibility from the outside. Specific examples of applications that require transparency include materials for forming flow paths of microchannel devices in biomimetic chips.
• the crosslinked rubber in the second embodiment of the present invention is a composition containing a fluorine-containing copolymer (hereinafter, also referred to as “copolymer B”), a crosslinking agent, and a crosslinking aid (hereinafter, “composition”).
• a crosslinked rubber (hereinafter, also referred to as “rubber B”) obtained by cross-linking the copolymer B in (also referred to as “B”), wherein the copolymer B is a tetrafluoroethylene unit and perfluoro (alkyl).
• the content of the cross-linking agent in the composition B is 0.03 to 0.7 parts by mass with respect to 100 parts by mass of the copolymer B.
• the content of the cross-linking aid is 0.1 to 2.5 parts by mass with respect to 100 parts by mass of the copolymer B, and the total light transmittance of the rubber B is 70 to 100. %.
• the crosslinked rubber obtained by the method for producing a crosslinked rubber of the second embodiment is excellent in tensile strength and transparency. The reason for this is the same as in the first embodiment.
• the components used for producing the rubber B, the method for producing the rubber B, the physical properties of the rubber B, and the like are the same as those of the rubber A described in the first embodiment, and the description thereof will be omitted. .. In the following, the points different from the rubber A described in the first embodiment will be mainly described.
• composition B contains a copolymer B, a cross-linking agent, and a cross-linking aid.
• the composition B is different from the composition A in at least the first embodiment in that the copolymer B is used instead of the copolymer A and that it is not essential to contain an antacid.
• the copolymer B is different from the copolymer A in the first embodiment in that it essentially has a TFE unit and a PAVE unit. Specific examples of the PAVE unit are as described in the copolymer A in the first embodiment.
• the copolymer B preferably does not contain P units.
• the copolymer B may have a unit based on a monomer other than TFE and PAVE, and the above-mentioned formula (A1) unit and the above-mentioned formula (A2) unit are preferable.
• the lower limit of the content of TFE units is preferably 40 mol% or more, more preferably 50 mol% or more, and particularly preferably 60 mol% or more, based on all the units of the copolymer B.
• the upper limit of the content of TFE units is preferably 90 mol% or less, more preferably 80 mol% or less, further preferably less than 69 mol%, and particularly preferably 68 mol% or less, based on all the units of the copolymer B. preferable.
• the content of PAVE units is preferably 10 to 60 mol%, more preferably 20 to 50 mol%, further preferably 31 to 50 mol%, and 32 to 50 mol% with respect to all the units of the copolymer B.
• the content thereof is preferably 0.03 to 0.5 mol%, preferably 0.05 to 0.3 mol%, based on all the units of the copolymer B. % Is particularly preferable.
• the content thereof is preferably 5 to 50 mol%, particularly preferably 10 to 30 mol%, based on all the units of the copolymer B.
• the total content of the TFE unit and the content of the PAVE unit is preferably 50 to 100 mol%, more preferably 80 to 100 mol%, based on all the units of the copolymer B.
• Combination 6 Combination of TFE unit and PAVE unit (preferably formula (A3) unit, particularly preferably PPVE unit or PMVE unit)
• Combination 7 TFE unit and PAVE unit (preferably formula (A3) unit) , Particularly preferably, a combination of PPVE units or PMVE units) and the unit of formula (A1).
• the copolymerization composition of the combinations 6 and 7 is preferably the following molar ratio.
• the molar ratio is as follows, the cross-linking reactivity of the copolymer is further excellent, and the mechanical properties, heat resistance, chemical resistance, oil resistance, and weather resistance of rubber B are further excellent.
• Combination 6: TFE unit / PAVE unit 40 to 90/10 to 60 (molar ratio)
• Combination 7: TFE unit / PAVE unit / formula (A1) unit 40 to 90/10 to 60 / 0.03 to 0.5 (molar ratio)
• the copolymer composition of the combinations 6 and 7 is more preferably the following molar ratio.
• TFE unit / PAVE unit 69-90 / 10-31 (molar ratio)
• TFE unit / PAVE unit / formula (A1) unit 40 to 89.5 / 10 to 59.5 / 0.03 to 0.5 (molar ratio)
• the copolymer B preferably has an iodine atom, and particularly preferably has an iodine atom at the end of the copolymer B (polymer chain).
• the iodine atom include an iodine atom derived from an iodine compound that functions as a chain transfer agent and an iodine atom in a unit based on a monomer having an iodine atom, and an iodine atom derived from the iodine compound is preferable.
• Specific examples of the iodine compound and the monomer having an iodine atom are as described in the first embodiment.
• the content thereof is preferably 0.01 to 5.0% by mass, more preferably 0.05 to 2.0% by mass, based on the total mass of the copolymer B. It is preferable, and 0.05 to 1.0% by mass is particularly preferable.
• the content of iodine atoms is in the above range, the cross-linking reactivity of the copolymer B is more excellent, and the mechanical properties of the rubber B are more excellent.
• the mass ratio of the iodine atom content to the content of the cross-linking agent (described later) in the composition B is 0.
• the copolymer B has an iodine atom
• the mass ratio of the iodine atom content to the content of the cross-linking aid (described later) in the composition B is determined. It is preferably 0.3 to 1.2, more preferably 0.3 to 1.0, and particularly preferably 0.35 to 0.70.
• the crosslinking reaction is likely to proceed, and when it is at least the upper limit of the above range, the tensile strength is more excellent.
• the content of the copolymer B is preferably 75 to 99% by mass, more preferably 85 to 99% by mass, further preferably 96 to 99% by mass, and 97 to 99% by mass with respect to the total mass of the composition B. Is particularly preferable.
• An example of a method for producing the copolymer B is a method of copolymerizing the above-mentioned monomers in the presence of a chain transfer agent and a radical polymerization initiator.
• Specific examples of the chain transfer agent and the radical polymerization initiator used in the production of the copolymer B are the same as those of the chain transfer agent and the radical polymerization initiator in the first embodiment.
• cross-linking agent in the composition B are the same as those of the cross-linking agent in the first embodiment.
• the content of the cross-linking agent in the composition B is 0.03 to 0.7 parts by mass, preferably 0.1 to 0.6 parts by mass, with respect to 100 parts by mass of the copolymer B. 1 to 0.5 parts by mass is particularly preferable.
• the tensile strength of the rubber B is more excellent, and when it is at least the upper limit of the above range, the transparency of the rubber B is more excellent.
• cross-linking aid in the composition B are the same as those in the first embodiment.
• the content of the cross-linking aid in the composition B is 0.1 to 2.5 parts by mass, preferably 0.1 to 2.0 parts by mass, and 0, based on 100 parts by mass of the copolymer B. .1 to 1.0 parts by mass is particularly preferable.
• the tensile strength of the rubber B is more excellent, and when it is at least the upper limit of the above range, the transparency of the rubber is more excellent.
• the mass ratio of the content of the cross-linking agent to the content of the cross-linking aid (content of the cross-linking agent / content of the cross-linking aid) in the composition B is preferably 0.4 to 7, preferably 0.4 to 7. 0 is more preferable, 0.4 to 5.0 is even more preferable, and 0.5 to 2.0 is particularly preferable. Within the above range, unreacted cross-linking aid is unlikely to remain, and the cross-linking reaction proceeds satisfactorily, so that transparency is more excellent.
• the total content of the cross-linking agent and the cross-linking aid in the composition B is preferably 2.0 parts by mass or less, more preferably 1.8 parts by mass or less, based on 100 parts by mass of the copolymer B.
• the total content of the cross-linking agent and the cross-linking aid in the composition B is preferably 0.10 parts by mass or more, particularly preferably 0.15 parts by mass or more, based on 100 parts by mass of the copolymer B. When it is equal to or more than the above value, the tensile strength of the rubber B is more excellent.
• the composition B may contain the above-mentioned antacid or the above-mentioned other components as long as the effects of the present invention are not impaired.
• the other components are the same as the components that may be contained in the composition A.
• the composition B may contain the above-mentioned antacid and other components, but the composition B is substantially free of the antacid and other components because the rubber B is more transparent. Is preferable.
• composition B substantially does not contain an antacid and other components means that the total content of the antacid and other components in composition B is 100 of the copolymer B.
• the composition B is 0.1 part by mass or less with respect to the mass, preferably 0.01 part by mass or less, and particularly preferably 0 part by mass.
• the composition B is substantially free of antacids and other components, it is easy to have the total light transmittance of the rubber B in the range of 70 to 100%.
• the refractive index of the crosslinked rubber b obtained by cross-linking the composition b consisting only of the fluorine-containing copolymer, the cross-linking agent and the cross-linking aid, and the refractive index of the acid-receiving agent and other components are different. If they are equivalent, the content of the acid-receiving agent and other components may be outside the above range.
• the refractive index of the crosslinked rubber b is the same as the refractive index of the acid receiving agent and other components, it is presumed that the total light transmittance of the rubber B is unlikely to decrease and the influence on the transparency of the rubber B is small. Because.
• the refractive index of the crosslinked rubber b and the refractive index of the acid receiving agent and other components are equivalent, the total content of the acid receiving agent and other components in the composition B is 100 of the copolymer B.
• the mass it is preferably 20 parts by mass or less, more preferably 15 parts by mass or less, further preferably 10 parts by mass, and particularly preferably 5 parts by mass or less.
• the total content of the components other than the copolymer B in the composition B is 0.5 with respect to 100 parts by mass of the copolymer B. It is preferably from 20 parts by mass, more preferably 0.5 to 10 parts by mass, more preferably 0.5 to 1.8 parts by mass, and particularly preferably 0.5 to 1.2 parts by mass. When it is at least the lower limit of the above range, the tensile strength of the rubber B is more excellent, and when it is at least the upper limit of the above range, the transparency of the rubber B is more excellent.
• the method for preparing the composition B is the same as the method for preparing the composition A in the first embodiment. Further, after obtaining a mixture obtained by mixing each of the above components, the mixture may be molded. That is, the composition B may be a molded product. Specific examples of the molding method are as described in the first embodiment.
• Rubber B manufacturing method The rubber B is obtained by cross-linking the copolymer B in the composition B.
• the method and conditions for cross-linking the copolymer B in the composition B are the same as the method and conditions for cross-linking the copolymer A in the composition A in the first embodiment.
• the rubber B Since the rubber B is obtained by using the composition B, it exhibits high transparency. As an index showing the transparency of the rubber B, the total light transmittance can be mentioned.
• the total light transmittance of the rubber B is 70 to 100%, and from the viewpoint that the transparency of the rubber B is more excellent, 73% or more is preferable, 75% or more is particularly preferable, and the tensile strength of the rubber B is more excellent. From the point of view, 99% or less is preferable, 95% or less is more preferable, and 93% or less is particularly preferable. Since the rubber B is obtained by using the composition B, it satisfies the above-mentioned total light transmittance. Here, if the total light transmittance is 60% or more, the transparency when observing the crosslinked rubber is excellent, but since the total light transmittance of rubber B is 70% or more, when observing rubber B, It can be said that the transparency is better.
• the parallel light transmittance of the rubber B is preferably 20 to 100%, more preferably 40% or more, further preferably 50% or more, particularly preferably 55% or more, and particularly preferably 55% or more, because the transparency of the rubber B is more excellent. From the viewpoint of more excellent tensile strength, 99% or less is more preferable, 95% or less is further preferable, and 90% or less is particularly preferable. When the parallel light transmittance is 20% or more, the transparency when observing the rubber B is more excellent.
• the haze value of the rubber B is preferably 0 to 75%, more preferably 63% or less, further preferably 50% or less, particularly preferably 30% or less, and particularly preferably 30% or less, because the transparency of the rubber B is more excellent. From the viewpoint of more excellent tensile strength, 0.5% or more is more preferable, 0.7% or more is further preferable, and 1% or more is particularly preferable. When the haze value is 75% or less, the transparency when observing the rubber B is more excellent.
• the degree of cross-linking of the rubber B is preferably 5 to 70 dNm, more preferably 10 to 60 dNm, more preferably 20 to 55 dNm, and particularly preferably 40 to 50 dNm.
• the degree of cross-linking of rubber B is within the above range, both rubber properties and transparency can be achieved at a high level.
• the hardness (Shore-A) of rubber B is preferably 40 to 70, more preferably 45 to 64, and particularly preferably 50 to 60. When it is equal to or higher than the lower limit of the above range, the performance as a sealing material is sufficiently exhibited. When it is not more than the upper limit value in the above range, the amount of microcrystalline portions present in the rubber B is sufficiently small, and the transparency is excellent.
• the tensile strength of the rubber B is preferably 1 to 21 MPa, particularly preferably 5 to 15 MPa. When the tensile strength of the rubber B is within the above range, the rubber properties and transparency of the rubber A are more excellent.
• the 100% modulus of rubber B is preferably 0.2 to 5.0 MPa, particularly preferably 0.5 to 2.0 MPa, from the viewpoint of excellent rubber characteristics.
• the elongation rate of the rubber B during cutting is preferably 100 to 300%, particularly preferably 200 to 250%, from the viewpoint of excellent rubber characteristics.
• Examples 1-1 to 1-14 and Examples 2-1 to 2-3 are examples, and Examples 1-15 to 1-18 and Examples 2-4 to 2-9 are comparative examples. However, the present invention is not limited to these examples.
• the blending amount of each component in the table described later indicates a mass standard.
• the content of each unit in the copolymer was calculated by nuclear magnetic resonance (NMR) analysis.
• the content of iodine atoms in the copolymer was calculated by a device combining an automatic sample combustion device, an ion chromatograph pretreatment device (manufactured by Mitsubishi Chemical Analytech Co., Ltd., AQF-100 type) and an ion chromatograph.
• Total light transmittance, parallel light transmittance The total light transmittance and the parallel light transmittance are based on JIS K7361-1: 1997 using a cross-linked rubber plate-shaped molded product (thickness 2 mm), and a haze meter (manufactured by Nippon Denshoku Co., Ltd., NDH5000) is used. It was measured. When the total light transmittance is 60% or more, it can be said that the crosslinked rubber is excellent in transparency. When the total light transmittance is 70% or more, it can be said that the transparency of the crosslinked rubber is superior.
• the haze value was measured according to JIS K7136: 2000 using a plate-shaped molded product (thickness 2 mm) of crosslinked rubber.
• Tensile strength, 100% modulus and elongation at cutting use a tensile tester with data processing (Quick Leader) TS-2530 (manufactured by Ueshima Seisakusho), and hardness uses Digitest Shore A (manufactured by H. Burleys tester). The measurement was performed. When the tensile strength is 1 MPa or more, it can be said that the crosslinked rubber is excellent in tensile strength.
• Copolymer A1 was produced with reference to the method of Example 5 of International Publication No. 2017/057512.
• the content of iodine atoms in the copolymer A1 was 0.37% by mass.
• copolymer A2 was produced with reference to the method of Example 1 of International Publication No. 2009/112022.
• the content of iodine atoms in the copolymer A2 was 0.26% by mass.
• copolymer B1 The copolymer B1 was produced with reference to the method of Comparative Example 1 of International Publication No. 2010/082633.
• the content of iodine atoms in the copolymer B1 was 0.20% by mass.
• copolymer B2 Except for changing PBDVE to C3DVE, the copolymer B2 was produced with reference to the method of Example 1 of International Publication No. 2010/082633.
• the content of iodine atoms in the copolymer B2 was 0.20% by mass.
• Example 1-1 to Example 1-18 and Example 2-1 to Example 2-9 The ingredients and blending amounts shown in the table were mixed, and the mixture was kneaded with two rolls at room temperature for 10 minutes to obtain a mixed composition.
• the obtained composition is hot-pressed (primary cross-linking) under the cross-linking conditions shown in the table below to carry out sheet-like cross-linking of Examples 1-1 to 1-14 and Examples 2-1 to 2-9. Rubber (crosslinked rubber sheet) was obtained.
• the compositions of Examples 1-15 to 1-18 the compositions were not crosslinked, and a crosslinked rubber was not obtained.
• the various physical properties described above were measured using the obtained composition and the crosslinked rubber. The measurement results are shown in the table.
• R8200 Product name "AEROSIL (registered trademark) R8200", manufactured by Nippon Aerosil Co., Ltd., reinforcing agent Parkadox 14: Product name, manufactured by Kayaku Akzo Corporation, ⁇ , ⁇ '-bis (tert-butylperoxy) -p-diisopropyl Benzene, cross-linking agent (organic peroxide) Perhexa 25B: Trade name, manufactured by NOF CORPORATION, 2,5-dimethyl-2,5-bis (tert-butylperoxy) hexane, cross-linking agent (organic peroxide) TAIC: Product name, manufactured by Mitsubishi Chemical Corporation, triallyl isocyanate, cross-linking aid Ca stearate: calcium stearate, antacid
• the obtained crosslinked rubber has excellent transparency (total light transmittance of 60% or more) and also excellent tensile strength (tensile strength 1.
• Example 1-1 to Example 1-14 It was confirmed (0 MPa or more) (Example 1-1 to Example 1-14). Further, in Examples 1-8 and 1-10 to 1-12, the amount of the antacid was larger than that of Example 1-7, the cross-linking reaction proceeded evenly, and further, as compared with Example 1-9. It is considered that the softness was superior to that of Examples 1-7 and 1-9 because the amount of the acid receiving agent was small and it was difficult for microcrystals to be formed. On the other hand, as shown in Table 1, when copolymer A (copolymer A1 or copolymer A2) which is a fluorine-containing copolymer is used, the composition is crosslinked unless an acid receiving agent is used in combination. It could not be used as a rubber, and it was impossible to measure various physical properties (Examples 1-15 to 1-18).
• the composition contains,
• the content of the cross-linking agent is 0.03 to 0.7 parts by mass with respect to 100 parts by mass of the fluoropolymer, and the content of the cross-linking aid is 0 with respect to 100 parts by mass of the fluoropolymer. .1 to 2.5 parts by mass, the obtained crosslinked rubber has better transparency (total light transmittance of 70% or more) and also excellent tensile strength (tensile strength of 5.0 MPa or more).

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• General Chemical & Material Sciences (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Processes Of Treating Macromolecular Substances (AREA)

Priority Applications (5)

Applications Claiming Priority (2)

Related Child Applications (1)

Publications (1)

Family

ID=72427572

Family Applications (1)

Country Status (6)

Cited By (4)

Citations (6)

Family Cites Families (1)

• 2020
  • 2020-03-06 EP EP20770598.9A patent/EP3936528A1/en not_active Withdrawn
  • 2020-03-06 CN CN202080018932.2A patent/CN113544159A/zh active Pending
  • 2020-03-06 KR KR1020217026077A patent/KR20210139227A/ko not_active Withdrawn
  • 2020-03-06 JP JP2021505022A patent/JPWO2020184429A1/ja active Pending
  • 2020-03-06 WO PCT/JP2020/009661 patent/WO2020184429A1/ja not_active Ceased
• 2021
  • 2021-08-25 US US17/445,839 patent/US20210388121A1/en not_active Abandoned

Patent Citations (6)

Also Published As

Similar Documents

Legal Events