WO2020175437A1 - Rouleau de chargement - Google Patents

Rouleau de chargement Download PDF

Info

Publication number
WO2020175437A1
WO2020175437A1 PCT/JP2020/007356 JP2020007356W WO2020175437A1 WO 2020175437 A1 WO2020175437 A1 WO 2020175437A1 JP 2020007356 W JP2020007356 W JP 2020007356W WO 2020175437 A1 WO2020175437 A1 WO 2020175437A1
Authority
WO
WIPO (PCT)
Prior art keywords
charging port
image
rubber
base material
particles
Prior art date
Application number
PCT/JP2020/007356
Other languages
English (en)
Japanese (ja)
Inventor
章吾 鈴木
池田　篤
麻実 植松
孝祐 大浦
智 福岡
佐々木　憲司
Original Assignee
Nok株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nok株式会社 filed Critical Nok株式会社
Publication of WO2020175437A1 publication Critical patent/WO2020175437A1/fr

Abstract

Ce rouleau de chargement comprend un matériau de noyau, un matériau de caoutchouc disposé sur la périphérie du matériau de noyau, et une couche de surface disposée sur la périphérie du matériau de caoutchouc. La rugosité moyenne en dix points Rz de la surface de la couche de surface est de 16,2-22,2 μｍ, inclus. La largeur moyenne des éléments de profil de rugosité RSm sur la surface de la couche de surface est de 87,0 à 106,2 µm inclus.
PCT/JP2020/007356 2019-02-27 2020-02-25 Rouleau de chargement WO2020175437A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019034895 2019-02-27
JP2019-034895 2019-02-27

Publications (1)

Publication Number Publication Date
WO2020175437A1 true WO2020175437A1 (fr) 2020-09-03

Family

ID=72240039

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/007356 WO2020175437A1 (fr) 2019-02-27 2020-02-25 Rouleau de chargement

Country Status (1)

Country Link
WO (1) WO2020175437A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11480886B2 (en) * 2019-02-27 2022-10-25 Nok Corporation Charging roll

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003316111A (ja) * 2002-04-19 2003-11-06 Canon Inc 帯電部材及び帯電装置
JP2012118510A (ja) * 2010-10-04 2012-06-21 Canon Inc 帯電部材、プロセスカートリッジ及び電子写真装置
US20150065607A1 (en) * 2013-08-27 2015-03-05 Lexmark International, Inc. Elastomeric Roll for an Electrophotographic Image Forming Device having Compressible Hollow Microparticles

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003316111A (ja) * 2002-04-19 2003-11-06 Canon Inc 帯電部材及び帯電装置
JP2012118510A (ja) * 2010-10-04 2012-06-21 Canon Inc 帯電部材、プロセスカートリッジ及び電子写真装置
US20150065607A1 (en) * 2013-08-27 2015-03-05 Lexmark International, Inc. Elastomeric Roll for an Electrophotographic Image Forming Device having Compressible Hollow Microparticles

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11480886B2 (en) * 2019-02-27 2022-10-25 Nok Corporation Charging roll

Similar Documents

Publication Publication Date Title
JP7394928B2 (ja) 帯電ロール
JP7337176B2 (ja) 帯電ロール
JP2022126823A (ja) 帯電ロール
JP7342209B2 (ja) 帯電ロール
WO2019044829A1 (fr) Rouleau électroconducteur
JP2019191519A (ja) 導電性ロール
WO2020175437A1 (fr) Rouleau de chargement
WO2020175436A1 (fr) Rouleau de chargement
WO2020175434A1 (fr) Rouleau de chargement
JP7337177B2 (ja) 帯電ロール
CN113242939B (zh) 带电辊
WO2020175433A1 (fr) Rouleau de charge
WO2020175431A1 (fr) Rouleau de chargement
WO2020175432A1 (fr) Rouleau de charge
WO2020175435A1 (fr) Rouleau de charge
CN114286968B (zh) 带电辊
WO2022163128A1 (fr) Rouleau de charge

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20762824

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20762824

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP