WO2019227872A1 - Fibre de purification de formaldéhyde et son procédé de préparation - Google Patents

Fibre de purification de formaldéhyde et son procédé de préparation Download PDF

Info

Publication number
WO2019227872A1
WO2019227872A1 PCT/CN2018/116866 CN2018116866W WO2019227872A1 WO 2019227872 A1 WO2019227872 A1 WO 2019227872A1 CN 2018116866 W CN2018116866 W CN 2018116866W WO 2019227872 A1 WO2019227872 A1 WO 2019227872A1
Authority
WO
WIPO (PCT)
Prior art keywords
fiber
polymer
formaldehyde
solution
formaldehyde purification
Prior art date
Application number
PCT/CN2018/116866
Other languages
English (en)
Chinese (zh)
Inventor
杜冰
赫法贵
陈家枢
高福
Original Assignee
深圳大学
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 深圳大学 filed Critical 深圳大学
Publication of WO2019227872A1 publication Critical patent/WO2019227872A1/fr

Abstract

L'invention concerne un procédé de préparation d'une fibre de purification de formaldéhyde, le procédé impliquant la dissolution d'un premier polymère dans un solvant organique pour formuler une première solution de filage et la réalisation d'un filage électrostatique et d'un séchage sous vide sur celle-ci, puis la mise en place du tout dans une solution de modification à la dopamine pour le trempage, et le lavage du tout de manière à obtenir une première fibre polymère ; ou la dissolution d'un second polymère dans un solvant organique pour formuler une seconde solution de filage, et la réalisation d'un filage électrostatique et d'un rayonnement UV sur celle-ci de façon à obtenir une seconde fibre polymère ; et la mise en place de la première fibre de polymère et/ou la seconde fibre de polymère dans une solution contenant des ions de métal noble pour le trempage de façon à combiner la première fibre de polymère et/ou la seconde fibre de polymère avec les ions de métal noble ; puis la mise en place du tout dans une solution de borohydrure de sodium pour le trempage de façon à convertir les ions de métal noble en une substance élémentaire de métal noble ou un composé de métal noble, puis le retrait et le lavage du tout pour obtenir la fibre de purification de formaldéhyde. La fibre présente une masse légère, une bonne perméabilité à l'air, une stabilité élevée et une capacité de charge élevée, et peut être utilisée comme catalyseur pour catalyser la conversion de formaldéhyde, et peut obtenir un taux de conversion de formaldéhyde élevé par absorption d'une petite quantité de composants actifs.
PCT/CN2018/116866 2018-05-31 2018-11-22 Fibre de purification de formaldéhyde et son procédé de préparation WO2019227872A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201810551037.1 2018-05-31
CN201810551037.1A CN108797107B (zh) 2018-05-31 2018-05-31 一种甲醛净化纤维及其制备方法

Publications (1)

Publication Number Publication Date
WO2019227872A1 true WO2019227872A1 (fr) 2019-12-05

Family

ID=64089755

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2018/116866 WO2019227872A1 (fr) 2018-05-31 2018-11-22 Fibre de purification de formaldéhyde et son procédé de préparation

Country Status (2)

Country Link
CN (1) CN108797107B (fr)
WO (1) WO2019227872A1 (fr)

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108797107B (zh) * 2018-05-31 2020-07-28 深圳大学 一种甲醛净化纤维及其制备方法
CN111501203B (zh) * 2019-01-30 2022-05-17 宁波方太厨具有限公司 一种催化纳米纤维膜的制备方法
CN111501347B (zh) * 2019-01-30 2021-12-24 宁波方太厨具有限公司 一种催化纳米纤维的制备方法
CN110316209A (zh) * 2019-08-06 2019-10-11 安阳安振环境高科有限公司 一种列车车厢空气净化系统
CN113509793A (zh) * 2020-04-09 2021-10-19 宁波方太厨具有限公司 去除甲醛的复合纳米纤维过滤膜制备方法
CN115888818B (zh) * 2022-07-29 2024-04-02 南京工业大学 一种微流控静电纺丝原位生长烟气脱硝催化剂及其制备方法和应用
CN115364639B (zh) * 2022-09-23 2024-02-27 三亚光远新型材料有限公司 一种水基量子点除醛功能添加剂及其制备方法

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103409940A (zh) * 2013-07-11 2013-11-27 东华大学 用于吸附La3+的多巴胺复合纳米纤维亲和膜的制备方法
CN105057003A (zh) * 2015-08-22 2015-11-18 北京化工大学 一种二氧化钛纳米复合薄膜制备方法
CN106807451A (zh) * 2017-01-18 2017-06-09 湖北工业大学 一种柔性铂甲醛室温氧化催化剂及其制备方法
CN106955740A (zh) * 2017-03-17 2017-07-18 广东工业大学 一种甲醛净化处理整体式催化剂及其制备方法与应用
CN107457002A (zh) * 2017-09-22 2017-12-12 江苏科来材料科技有限公司 一种宽光谱响应光催化膜的制备方法
CN107983320A (zh) * 2017-11-21 2018-05-04 上海纳米技术及应用国家工程研究中心有限公司 用于甲醛去除的双功能薄膜的制备方法及其产品和应用
CN108797107A (zh) * 2018-05-31 2018-11-13 深圳大学 一种甲醛净化纤维及其制备方法

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107587268B (zh) * 2017-08-24 2020-08-11 东华大学 一种环保溶剂型静电纺防水透湿膜的制备方法

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103409940A (zh) * 2013-07-11 2013-11-27 东华大学 用于吸附La3+的多巴胺复合纳米纤维亲和膜的制备方法
CN105057003A (zh) * 2015-08-22 2015-11-18 北京化工大学 一种二氧化钛纳米复合薄膜制备方法
CN106807451A (zh) * 2017-01-18 2017-06-09 湖北工业大学 一种柔性铂甲醛室温氧化催化剂及其制备方法
CN106955740A (zh) * 2017-03-17 2017-07-18 广东工业大学 一种甲醛净化处理整体式催化剂及其制备方法与应用
CN107457002A (zh) * 2017-09-22 2017-12-12 江苏科来材料科技有限公司 一种宽光谱响应光催化膜的制备方法
CN107983320A (zh) * 2017-11-21 2018-05-04 上海纳米技术及应用国家工程研究中心有限公司 用于甲醛去除的双功能薄膜的制备方法及其产品和应用
CN108797107A (zh) * 2018-05-31 2018-11-13 深圳大学 一种甲醛净化纤维及其制备方法

Also Published As

Publication number Publication date
CN108797107A (zh) 2018-11-13
CN108797107B (zh) 2020-07-28

Similar Documents

Publication Publication Date Title
WO2019227872A1 (fr) Fibre de purification de formaldéhyde et son procédé de préparation
CN108772108B (zh) 一种可见光响应的二氧化钛纳米线/金属有机骨架/碳纳米纤维膜及其制备方法及应用
Yao et al. Electrospun Bi-decorated BixTiyOz/TiO2 flexible carbon nanofibers and their applications on degradating of organic pollutants under solar radiation
CN108714431B (zh) 一种纳米纤维素增强复合光催化剂及其制备方法和应用
CN107297204A (zh) 一种以活性炭纤维为载体的TiO2纳米棒光催化网的制备方法
CN109248680B (zh) 一种低能耗化学场驱动的有机污染物降解催化剂及其应用
CN111250056B (zh) 一种壳聚糖/石墨相氮化碳/二氧化钛纳米纤维膜及其制备方法和应用
CN106807451B (zh) 一种柔性铂甲醛室温氧化催化剂及其制备方法
Mehmood et al. Immobilizing a visible light-responsive photocatalyst on a recyclable polymeric composite for floating and suspended applications in water treatment
Zhao et al. Polypyrrole/cadmium sulfide hollow fiber with high performance contaminant removal and photocatalytic activity fabricated by layer-by-layer deposition and fiber-sacrifice template approach
Liu et al. Electrospinning synthesis of InVO 4/BiVO 4 heterostructured nanobelts and their enhanced photocatalytic performance
CN109794160A (zh) 一种用于分解甲醛的催化剂及其制备方法
Liu et al. The multiple promotion effects of ammonium phosphate-modified Ag3PO4 on photocatalytic performance
CN108940375B (zh) 一种甲醛净化纤维及其制备方法
Lan et al. Hierarchical polyurethane/RGO/BiOI fiber composite as flexible, self-supporting and recyclable photocatalysts for RhB degradation under visible light
Xue et al. Facile fabrication of three-dimensional nanofibrous foams of cellulose@ g-C3N4@ Cu2O with superior visible-light photocatalytic performance
CN110665533A (zh) 一种室温甲醛净化用非贵金属掺杂碳纤维膜及其制备方法和应用
Pascariu et al. New composite membranes based on PVDF fibers loaded with TiO2: Sm nanostructures and reinforced with graphene/graphene oxide for photocatalytic applications
CN113117418A (zh) 具有光催化解毒功能的纳米纤维过滤防护材料及其制备方法
CN108514885A (zh) 一种Cu（Ⅱ）修饰的BiOCl的制备方法及其应用
CN111411412A (zh) 石墨烯-聚丙烯腈基纳米复合材料及其制备方法和应用
CN112044417A (zh) 一种用于处理印染废水的吸附材料及其制备方法
CN107973367B (zh) 一种Fe掺杂包裹型TiO2光催化剂降解废水的工艺
Zheng et al. In-situ platinum nanoparticles loaded dialdehyde modified sisal fiber-based activated carbon fiber paper for formaldehyde oxidation
Ou et al. CdSNPs@ NPAN‐rGO‐PAN electrospinning film with enhanced photocatalytic activity via adjusting the fiber dimension

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18920214

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

32PN Ep: public notification in the ep bulletin as address of the adressee cannot be established

Free format text: NOTING OF LOSS OF RIGHTS PURSUANT TO RULE 112(1) EPC (EPO FORM 1205 DATED 02/02/2021)

122 Ep: pct application non-entry in european phase

Ref document number: 18920214

Country of ref document: EP

Kind code of ref document: A1