WO2019225764A1 - Surface-treated steel plate - Google Patents
Surface-treated steel plate Download PDFInfo
- Publication number
- WO2019225764A1 WO2019225764A1 PCT/JP2019/020942 JP2019020942W WO2019225764A1 WO 2019225764 A1 WO2019225764 A1 WO 2019225764A1 JP 2019020942 W JP2019020942 W JP 2019020942W WO 2019225764 A1 WO2019225764 A1 WO 2019225764A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- coating film
- pigment
- plating layer
- alloy plating
- average
- Prior art date
Abstract
Description
(1)
鋼板、前記鋼板上の少なくとも片面に形成されたZn系合金めっき層、及び前記Zn系合金めっき層上に形成され、着色顔料と防錆顔料とバインダー樹脂とを含む平均厚さT1の塗膜を有し、
前記Zn系合金めっき層の化学組成が、質量%で、
Al:0.01~60%、
Mg:0.001~10%、及び
Si:0~2%であり、
前記塗膜中の前記着色顔料の平均濃度が、質量%で、5~15%であり、
前記塗膜の表面から塗膜の厚さ方向に幅T2の領域に存在する前記着色顔料の平均濃度CA1と、前記塗膜の前記Zn系合金めっき層側の界面から塗膜の厚さ方向に幅T2の領域に存在する前記着色顔料の平均濃度CA2との比CA1/CA2が0.2~0.9であり、
T2(μm)=0.1×T1(μm)+1.1μmであることを特徴とする、表面処理鋼板。
(2)
前記塗膜中の前記防錆顔料の平均濃度が、質量%で、3~12%であり、
前記塗膜の表面から塗膜の厚さ方向に幅T2の領域に存在する前記防錆顔料の平均濃度CB1と、前記塗膜の前記Zn系合金めっき層側の界面から塗膜の厚さ方向に幅T2の領域に存在する前記防錆顔料の平均濃度CB2との比CB1/CB2が1.3~4.0であり、
T2(μm)=0.1×T1(μm)+1.1μmであり、
前記防錆顔料が、Si、Mo、W及びBaの1種又は2種以上を含むことを特徴とする、(1)に記載の表面処理鋼板。
(3)
前記着色顔料が、5~30μmである長径X1と、1~30μmである短径X2と、0.0025μm以上である厚さX3とを有し、平均粒径=(X1+X2)/2、及び平均アスペクト比=(X1+X2)/2X3とした場合に、前記着色顔料の平均粒径が7~30μmであり、平均アスペクト比が20以上であることを特徴とする、(1)又は(2)に記載の表面処理鋼板。
(4)
前記塗膜の平均厚さT1が3~15μmであることを特徴とする、(1)~(3)のいずれか1つに記載の表面処理鋼板。
(5)
前記着色顔料の厚さが0.5T1以下である、(1)~(4)のいずれか1つに記載の表面処理鋼板。 The present invention has been made on the basis of the above findings, and the gist thereof is as follows.
(1)
A steel sheet, a Zn-based alloy plating layer formed on at least one surface of the steel sheet, and a coating film having an average thickness T 1 formed on the Zn-based alloy plating layer and containing a color pigment, a rust preventive pigment, and a binder resin Have
The chemical composition of the Zn-based alloy plating layer is mass%,
Al: 0.01 to 60%,
Mg: 0.001 to 10%, and Si: 0 to 2%,
The average concentration of the colored pigment in the coating film is 5 to 15% by mass%,
The average concentration C A1 of the color pigment present in the region of width T 2 in the thickness direction of the coating film from the surface of the coating film, and the thickness of the coating film from the interface on the Zn-based alloy plating layer side of the coating film The ratio C A1 / C A2 to the average concentration C A2 of the color pigment present in the region of width T 2 in the direction is 0.2 to 0.9;
A surface-treated steel sheet, wherein T 2 (μm) = 0.1 × T 1 (μm) +1.1 μm.
(2)
The average concentration of the anticorrosive pigment in the coating film is 3% to 12% by mass%,
The average concentration C B1 of the anticorrosive pigment existing in the region of the width T 2 in the thickness direction of the coating film from the surface of the coating film, and the thickness of the coating film from the interface on the Zn-based alloy plating layer side of the coating film The ratio C B1 / C B2 to the average concentration C B2 of the anticorrosive pigment existing in the width T 2 region in the lengthwise direction is 1.3 to 4.0,
T 2 (μm) = 0.1 × T 1 (μm) +1.1 μm,
The surface-treated steel sheet according to (1), wherein the rust preventive pigment contains one or more of Si, Mo, W and Ba.
(3)
The color pigment has a major axis X 1 of 5 to 30 μm, a minor axis X 2 of 1 to 30 μm, and a thickness X 3 of 0.0025 μm or more, and an average particle size = (X 1 + X 2 ) / 2 and average aspect ratio = (X 1 + X 2 ) / 2X 3 , the color pigment has an average particle diameter of 7 to 30 μm and an average aspect ratio of 20 or more. The surface-treated steel sheet according to (1) or (2).
(4)
The surface-treated steel sheet according to any one of (1) to (3), wherein an average thickness T 1 of the coating film is 3 to 15 μm.
(5)
The surface-treated steel sheet according to any one of (1) to (4), wherein the color pigment has a thickness of 0.5 T 1 or less.
本発明に係る表面処理鋼板は、鋼板、鋼板上の少なくとも片面に形成されたZn系合金めっき層、及びZn系合金めっき層上に形成され、着色顔料と防錆顔料とバインダー樹脂とを含む平均厚さT1の塗膜を有し、Zn系合金めっき層の化学組成が、質量%で、Al:0.01~60%、Mg:0.001~10%、及びSi:0~2%であり、塗膜中の着色顔料の平均濃度が、質量%で、5~15%であり、塗膜の表面から塗膜の厚さ方向に幅T2の領域に存在する着色顔料の平均濃度CA1と、塗膜のZn系合金めっき層側の界面から塗膜の厚さ方向に幅T2の領域に存在する着色顔料の平均濃度CA2との比CA1/CA2が0.2~0.9であり、T2(μm)=0.1×T1(μm)+1.1μmであることを特徴とする。以下、本発明に係る表面処理鋼板の構成要件について説明する。 [Surface treated steel sheet]
The surface-treated steel sheet according to the present invention is an average comprising a steel sheet, a Zn-based alloy plating layer formed on at least one surface of the steel sheet, and a Zn-based alloy plating layer, and including a color pigment, a rust preventive pigment, and a binder resin. The coating composition has a thickness of T 1 and the chemical composition of the Zn-based alloy plating layer is, by mass%, Al: 0.01 to 60%, Mg: 0.001 to 10%, and Si: 0 to 2% The average concentration of the colored pigment in the coating film is 5 to 15% by mass, and the average concentration of the coloring pigment existing in the region of the width T 2 from the surface of the coating film in the thickness direction of the coating film. a C A1, the ratio C A1 / C A2 between the average concentration C A2 of coloring pigment present from the interface of Zn alloy plating layer side of the coated film in a thickness direction of the width T 2 areas of the coating and 0.2 0.9, and T 2 (μm) = 0.1 × T 1 (μm) +1.1 μm. Hereinafter, the constituent requirements of the surface-treated steel sheet according to the present invention will be described.
本発明における鋼板(めっき原板)としては、特に限定されず、熱延鋼板、冷延鋼板などの一般的な鋼板を使用することができる。鋼種も、特に限定されず、例えばAlキルド鋼、Ti、Nbなどを含有した極低炭素鋼、及びこれらにP、Si、Mnなどの元素を含有した高張力鋼などを使用することが可能である。本発明における鋼板の板厚は、特に限定されないが、例えば、0.25~3.5mmであればよい。 <Steel plate>
It does not specifically limit as a steel plate (plating original plate) in this invention, General steel plates, such as a hot-rolled steel plate and a cold-rolled steel plate, can be used. The steel type is not particularly limited, and for example, Al-killed steel, ultra-low carbon steel containing Ti, Nb, etc., and high-tensile steel containing elements such as P, Si, Mn, etc. can be used. is there. The thickness of the steel plate in the present invention is not particularly limited, but may be, for example, 0.25 to 3.5 mm.
本発明におけるZn系合金めっき層は鋼板上に形成されている。このZn系合金めっき層は鋼板の片面に形成されていても、両面に形成されていてもよい。Zn系合金めっき層は、少なくともAlとMgとを含有するZn-Al-Mg合金めっき層であってもよく、さらにSiを含有するZn-Al-Mg-Si合金めっき層であってもよい。これらの各含有量(濃度)は、質量%で、Al:0.01~60%、Mg:0.001~10%、及びSi:0~2%であり、残部がZn及び不純物である。以下、Zn系合金めっき層の化学組成について単に「%」と記した場合は、「質量%」を意味するものとする。 <Zn-based alloy plating layer>
The Zn-based alloy plating layer in the present invention is formed on a steel plate. This Zn-based alloy plating layer may be formed on one side of the steel plate or on both sides. The Zn-based alloy plating layer may be a Zn—Al—Mg alloy plating layer containing at least Al and Mg, and may further be a Zn—Al—Mg—Si alloy plating layer containing Si. Each of these contents (concentrations) is, by mass, Al: 0.01 to 60%, Mg: 0.001 to 10%, and Si: 0 to 2%, with the balance being Zn and impurities. Hereinafter, when the chemical composition of the Zn-based alloy plating layer is simply described as “%”, it means “mass%”.
本発明における塗膜はZn系合金めっき層上に形成されている。塗膜中には、着色顔料の他、防錆顔料とバインダー樹脂とを含む。塗膜の平均厚さT1は、十分な耐食性及び耐黒変性が担保される限り如何なる値であってもよいが、例えば、3μm以上15μm以下であることが好ましい。塗膜の平均厚さT1が3μm未満であると、着色顔料の一部が塗膜から突出して腐食因子が合金めっき層に到達する可能性が増え、十分な耐食性を担保できなくなるおそれがある。さらに、塗膜中の着色顔料によりZn系合金めっき層を見えなくする効果を担保するには厚さが不十分となり、耐黒変性が悪化するおそれがある。また、塗膜の平均厚さT1が15μm超であると、塗膜の平均厚さを増やすことによる耐食性及び耐黒変性の向上の効果が飽和する。塗膜の平均厚さT1は、例えば、4μm以上、5μm以上又は6μm以上であってよく、また、12μm以下又は10μm以下であってよい。したがって、塗膜の平均厚さT1は、3μm以上12μm以下であることがより好ましい。なお、本明細書において「耐黒変性」とは、塗膜の下地のZn系合金めっき層の黒変の発生を抑制するという意味ではなく、当該Zn系合金めっき層に黒変が生じても、塗膜中の着色顔料により外部から黒変を見えないようにして、表面処理鋼板に外観上の変化を生じさせないことを意味する。 <Coating film>
The coating film in the present invention is formed on the Zn-based alloy plating layer. The coating film contains a rust preventive pigment and a binder resin in addition to the color pigment. The average thickness T 1 of the coating film may be any value as long as sufficient corrosion resistance and blackening resistance are ensured. For example, it is preferably 3 μm or more and 15 μm or less. If the average thickness T 1 of the coating film is less than 3 μm, there is a possibility that a part of the color pigment protrudes from the coating film and the corrosion factor reaches the alloy plating layer, so that sufficient corrosion resistance cannot be secured. . Furthermore, the thickness becomes insufficient to ensure the effect of making the Zn-based alloy plating layer invisible by the colored pigment in the coating film, and the blackening resistance may be deteriorated. Further, when the average thickness T 1 of the coating film is more than 15 μm, the effect of improving the corrosion resistance and blackening resistance by increasing the average thickness of the coating film is saturated. The average thickness T 1 of the coating film may be, for example, 4 μm or more, 5 μm or more, or 6 μm or more, and may be 12 μm or less or 10 μm or less. Therefore, the average thickness T 1 of the coating film is more preferably 3 μm or more and 12 μm or less. In this specification, “blackening resistance” does not mean to suppress the occurrence of blackening of the Zn-based alloy plating layer underlying the coating film, and even if blackening occurs in the Zn-based alloy plating layer. This means that the appearance of the surface-treated steel sheet is not changed by making the black pigment visible from the outside by the colored pigment in the coating film.
本発明における着色顔料としては、例えば、酸化チタン、酸化亜鉛、酸化鉄、酸化アルミニウム、硫酸バリウム、アルミニウム、又はカーボンブラックなどの一般的な着色顔料を用いることができる。好ましくは、着色顔料はアルミニウムである。ただし、アルミニウムは水と反応し溶出する。そのため、本発明のように、塗膜を形成するための塗料に水系塗料を用いる場合は、アルミニウムを酸化物や樹脂でコーティングする必要がある。 (Color pigment)
As the colored pigment in the present invention, for example, a general colored pigment such as titanium oxide, zinc oxide, iron oxide, aluminum oxide, barium sulfate, aluminum, or carbon black can be used. Preferably, the color pigment is aluminum. However, aluminum is eluted by reacting with water. Therefore, when a water-based paint is used as a paint for forming a coating film as in the present invention, it is necessary to coat aluminum with an oxide or a resin.
本発明における塗膜中で使用される防錆顔料としては、Si、Mo、W及びBaの1種又は2種以上を含むことができる。好ましくは、Si、Mo及びBaの1種又は2種以上を含む。これらの具体的な化合物としては、限定されないが、例えば、シリカ(Grace社製、MSK-8D)、カルシウム修飾シリカ(W.R.Grace社製、SHIELDEXC303)、ホウ酸バリウム(昭和化学社製試薬)、メタホウ酸バリウム(昭和化学社製試薬)、モリブデン酸亜鉛(和光純薬工業社製試薬)、モリブデン酸カルシウム(和光純薬工業社製試薬)、タングステン酸ナトリウム(関東化学社製試薬)、タングステン酸カルシウム(関東化学社製試薬)、酸化タングステン(関東化学社製試薬)などが挙げられる。好ましくは、防錆顔料はシリカである。さらに、防錆顔料は多孔質であることができる。多孔質とすることで比表面積が大きく、見かけの比重が低くなるため、より塗膜の表面側に濃化させやすくなる。例えば、防錆顔料としては、比表面積が20m2/g以上、例えば、50m2/g以上、100m2/g以上、又は200m2/g以上の防錆顔料(例えばシリカ)を使用することができる。防錆顔料の比表面積の上限は、特に限定されないが、例えば500m2/gであればよい。なお、本明細書において「見かけの比重」とは、防錆顔料自身と内部空隙を体積とした場合の密度のことであり、「防錆顔料自身の体積」と「内部空隙の体積」が含まれる。 (Anti-rust pigment)
As a rust preventive pigment used in the coating film in this invention, 1 type, or 2 or more types of Si, Mo, W, and Ba can be included. Preferably, one or more of Si, Mo and Ba are included. Specific examples of these compounds include, but are not limited to, silica (Grace, MSK-8D), calcium-modified silica (WR Grace, SHIELDEXC303), barium borate (Showa Chemicals Reagents). ), Barium metaborate (reagent manufactured by Showa Chemical Co., Ltd.), zinc molybdate (reagent manufactured by Wako Pure Chemical Industries, Ltd.), calcium molybdate (reagent manufactured by Wako Pure Chemical Industries, Ltd.), sodium tungstate (reagent manufactured by Kanto Chemical Co., Inc.), Examples thereof include calcium tungstate (a reagent manufactured by Kanto Chemical Co., Inc.) and tungsten oxide (a reagent manufactured by Kanto Chemical Co., Inc.). Preferably, the rust preventive pigment is silica. Furthermore, the rust preventive pigment can be porous. By making it porous, the specific surface area is large and the apparent specific gravity is low, so it is easier to concentrate on the surface side of the coating film. For example, as the rust preventive pigment, a rust preventive pigment (for example, silica) having a specific surface area of 20 m 2 / g or more, for example, 50 m 2 / g or more, 100 m 2 / g or more, or 200 m 2 / g or more is used. it can. Although the upper limit of the specific surface area of a rust preventive pigment is not specifically limited, For example, what is necessary is just 500 m < 2 > / g. In this specification, “apparent specific gravity” means the density when the rust preventive pigment itself and the internal voids are in volume, and includes “the volume of the rust preventive pigment itself” and “the volume of the internal voids”. It is.
本発明における塗膜の成分として使用されるバインダー樹脂は、ポリエステル樹脂、ウレタン樹脂、又はアクリル樹脂であるとよい。本発明においては、これらの樹脂の硬化剤としてイミノ基型メラミン樹脂を使用することが重要である。好ましくは、本発明におけるバインダー樹脂はポリエステル樹脂である。また、本発明で使用されるポリエステル樹脂としては、-20~70℃のガラス転移温度Tgと、3000~30000の数平均分子量を有するものが好ましい。バインダー樹脂がウレタン樹脂の場合、Tgは0~50℃、数平均分子量は5000~25000のものが好ましい。バインダー樹脂がアクリル樹脂の場合、Tgは0~50℃、数平均分子量は3000~25000のものが好ましい。また、本発明においては、バインダー樹脂に対する溶媒には水性溶媒を用いる。 (Binder resin)
The binder resin used as a component of the coating film in the present invention is preferably a polyester resin, a urethane resin, or an acrylic resin. In the present invention, it is important to use an imino group type melamine resin as a curing agent for these resins. Preferably, the binder resin in the present invention is a polyester resin. The polyester resin used in the present invention preferably has a glass transition temperature Tg of −20 to 70 ° C. and a number average molecular weight of 3000 to 30000. When the binder resin is a urethane resin, it is preferable that Tg is 0 to 50 ° C. and the number average molecular weight is 5000 to 25000. When the binder resin is an acrylic resin, it is preferable that Tg is 0 to 50 ° C. and the number average molecular weight is 3000 to 25000. In the present invention, an aqueous solvent is used as a solvent for the binder resin.
本発明に係る表面処理鋼板の製造方法の例を以下で説明する。本発明に係る表面処理鋼板は、例えば、鋼板上に形成されたZn系合金めっき層上に、着色顔料及び防錆顔料を添加し、イミノ基型メラミン樹脂をバインダー樹脂の硬化剤として添加した水性塗料を塗布し、所定のヒートパターンにより加熱して塗料を硬化させることで製造することができる。 [Method for producing surface-treated steel sheet]
The example of the manufacturing method of the surface treatment steel plate which concerns on this invention is demonstrated below. The surface-treated steel sheet according to the present invention is, for example, an aqueous solution in which a coloring pigment and a rust preventive pigment are added to a Zn-based alloy plating layer formed on a steel sheet, and an imino group type melamine resin is added as a curing agent for the binder resin. It can be produced by applying a paint and heating it with a predetermined heat pattern to cure the paint.
鋼板としては、任意の板厚及び化学組成を有するものを使用することができる。例えば、板厚0.25~3.5mmの冷延鋼板を使用することができる。Zn系合金めっき層は、例えば鋼板上にZn-Al-Mg合金めっきを溶融めっきで1~30μmの厚さで形成することができる。溶融めっきは、例えば、各種金属を添加した400~550℃の溶融めっき浴で行うことができる。Al及びMg含有量は、質量%で、Al:0.01~60%、Mg:0.001~10%であり、残部は典型的にZn及び不純物である。また、上記のような化学組成に加えて、質量%で、Si:0.001~2%を含み、Zn-Al-Mg-Si合金めっき層を形成することもできる。 <Formation of Zn-based alloy plating layer>
As a steel plate, what has arbitrary board thickness and chemical composition can be used. For example, a cold rolled steel sheet having a thickness of 0.25 to 3.5 mm can be used. For example, the Zn-based alloy plating layer can be formed by hot-plating Zn—Al—Mg alloy plating on a steel plate to a thickness of 1 to 30 μm. The hot dipping can be performed, for example, in a hot dipping bath at 400 to 550 ° C. to which various metals are added. The contents of Al and Mg are, by mass, Al: 0.01 to 60%, Mg: 0.001 to 10%, and the balance is typically Zn and impurities. In addition to the chemical composition as described above, a Zn—Al—Mg—Si alloy plating layer containing Si: 0.001 to 2% by mass% can also be formed.
塗料は、溶媒に分散させたポリエステル樹脂(例えば、分子量:16000、Tg:10℃)等のバインダー樹脂とイミノ基型メラミン樹脂とを、固形分質量比100:10~100:30で混合し、次いで、その混合物に所定量の着色顔料及び防錆顔料を分散させることで得ることができる。また、溶媒としては、水性溶媒(例えば水)を使用する。 <Preparation of paint>
The paint is prepared by mixing a binder resin such as a polyester resin dispersed in a solvent (for example, molecular weight: 16000, Tg: 10 ° C.) and an imino group-type melamine resin at a solid content mass ratio of 100: 10 to 100: 30, Subsequently, it can obtain by disperse | distributing a predetermined amount of a coloring pigment and an antirust pigment to the mixture. As the solvent, an aqueous solvent (for example, water) is used.
次いで、得られた塗料をZn系合金めっき層上に所定の厚さになるように、例えばロールコーター等で塗布し、所定のヒートパターンで焼付け、硬化させることができる。焼付けは、5~70℃/秒の加熱速度で最終的に180~230℃の鋼板温度になるように加熱する。具体的には、当該鋼板温度に加熱するプロセスにおいて、70~150℃、好ましくは100~150℃の間の温度において、1~5秒間、好ましくは1~3秒間、鋼板温度を保持することが重要である。すなわち、塗料をZn系合金めっき層上に塗布した後に、室温(例えば20℃)のめっき鋼板を一旦70~150℃に加熱し(第1加熱工程)、その温度で1~5秒間保持した後(温度保持工程)、さらに180~230℃に加熱する(第2加熱工程)ことで、本発明における塗膜が得られる。このようなヒートパターンは、2つの加熱炉で実現することができる。具体的には、塗料を塗布したZn系合金めっき鋼板の通板方向に対して、順番に、加熱炉A及び加熱炉Bを設置し、加熱炉Aと加熱炉Bとの間に加熱処理を行わない温度保持領域を設けるとよい。したがって、加熱炉Aで塗料を塗布しためっき鋼板を70~150℃の間の温度に昇温し、その温度において温度保持領域で1~5秒間保持した後、加熱炉Bで180~230℃の間の温度に昇温し、塗料を硬化させることができる。なお、上記ヒートパターンは、上述のように連続式に行ってもよいし、バッチ式に行ってもよい。 <Formation of coating film>
Next, the obtained paint can be applied on the Zn-based alloy plating layer with a predetermined thickness, for example, by a roll coater, and baked and cured with a predetermined heat pattern. The baking is performed at a heating rate of 5 to 70 ° C./second so that the steel plate temperature finally reaches 180 to 230 ° C. Specifically, in the process of heating to the steel plate temperature, the steel plate temperature can be maintained for 1 to 5 seconds, preferably 1 to 3 seconds at a temperature of 70 to 150 ° C., preferably 100 to 150 ° C. is important. That is, after applying the paint on the Zn-based alloy plating layer, the plated steel sheet at room temperature (for example, 20 ° C.) is once heated to 70 to 150 ° C. (first heating step) and held at that temperature for 1 to 5 seconds. (Temperature holding step) Further heating to 180 to 230 ° C. (second heating step) provides the coating film in the present invention. Such a heat pattern can be realized by two heating furnaces. Specifically, the heating furnace A and the heating furnace B are installed in order with respect to the sheet passing direction of the Zn-based alloy plated steel sheet coated with the paint, and the heat treatment is performed between the heating furnace A and the heating furnace B. It is preferable to provide a temperature holding region that is not performed. Accordingly, the temperature of the plated steel sheet coated with the paint in the heating furnace A is raised to a temperature of 70 to 150 ° C., held at that temperature in the temperature holding region for 1 to 5 seconds, and then heated to 180 to 230 ° C. in the heating furnace B. The paint can be cured by raising the temperature to between. The heat pattern may be performed continuously as described above, or may be performed batchwise.
(Zn系合金めっき層の形成)
厚さ1mmの冷延鋼板を、化学組成がAl:約11%、Mg:約3%、及びZn:約86%の約450℃の溶融めっき浴に3~5秒間浸漬し、冷延鋼板上に約10μmの厚さのZn-11%Al-3%Mg合金めっき層を形成した。また、溶解めっき浴の組成を変更し、同様の手順で冷延鋼板上に約10μmの厚さのZn-1%Al-1%Mg合金めっき層及びZn-40%Al-8%Mg合金めっき層を形成した。あるいは、厚さ1mmの冷延鋼板を、化学組成がAl:約11%、Mg:約3%、Si:約1%、及びZn:約85%の約450℃の溶融めっき浴に3~5秒間浸漬し、冷延鋼板上に約10μmの厚さのZn-11%Al-3%Mg-1%Si合金めっき層を形成した。また、溶解めっき浴の組成を変更し、同様の手順で冷延鋼板上に約10μmの厚さのZn-11%Al-3%Mg-0.4%Si合金めっき層及びZn-11%Al-3%Mg-1.5%Si合金めっき層を形成した。 <Preparation of surface-treated steel sheet sample>
(Formation of Zn-based alloy plating layer)
A cold-rolled steel sheet having a thickness of 1 mm is immersed in a hot-dip plating bath having a chemical composition of Al: about 11%, Mg: about 3%, and Zn: about 86% at about 450 ° C. for 3 to 5 seconds. A Zn-11% Al-3% Mg alloy plating layer having a thickness of about 10 μm was formed. Also, the composition of the dissolution plating bath was changed, and a Zn-1% Al-1% Mg alloy plating layer and Zn-40% Al-8% Mg alloy plating having a thickness of about 10 μm were applied on the cold-rolled steel sheet in the same procedure. A layer was formed. Alternatively, a cold rolled steel sheet having a thickness of 1 mm is placed in a hot-dip plating bath at about 450 ° C. with a chemical composition of Al: about 11%, Mg: about 3%, Si: about 1%, and Zn: about 85%. It was immersed for 2 seconds to form a Zn-11% Al-3% Mg-1% Si alloy plating layer having a thickness of about 10 μm on the cold-rolled steel sheet. In addition, the composition of the dissolution plating bath was changed, and a Zn-11% Al-3% Mg-0.4% Si alloy plating layer and Zn-11% Al having a thickness of about 10 μm were formed on the cold-rolled steel sheet in the same procedure. A −3% Mg—1.5% Si alloy plating layer was formed.
水中にバインダー樹脂としてポリエステル樹脂(分子量:16,000;ガラス転移点:10℃)をエマルジョンとして分散させ、pHが8.0~9.0となるように調整した。その中にイミノ基型メラミン樹脂を混合した。ポリエステル樹脂とイミノ基型メラミン樹脂との濃度の比は100:20であった。次いで、その混合物中に、着色顔料として平均粒径10μm・平均アスペクト比25(長径X1:12μm、短径X2:8μm、厚さX3:0.40μm)の樹脂コーティングアルミニウム、及び、防錆顔料として平均粒径3μmのSi化合物2種(シリカA:比表面積320m2/g、シリカB:比表面積180m2/g)、Ba化合物2種(ホウ酸バリウムA:比表面積40m2/g、ホウ酸バリウムB:比表面積4.2m2/g)、Mo化合物(モリブデン酸カルシウム:比表面積80m2/g)又はW化合物(酸化タングステン:比表面積40m2/g)のいずれかを添加して塗料を調製した。着色顔料及び防錆顔料の添加量は、後述するように、GD-OESを用いて測定した場合に塗膜中で所望の濃度が得られるように適宜調整した。添加した防錆顔料の種類を表1に示した(Si-AはシリカA、Si-BはシリカB、Ba-Aはホウ酸バリウムA、Ba-Bはホウ酸バリウムB、Moはモリブデン酸カルシウム、及びWは酸化タングステンを示す)。また、試料No.32は、防錆顔料を添加しなかった例であり、試料No.35は、イミノ基型メラミン樹脂の代わりにメチル化メラミン樹脂を用いた例である。なお、表1には記載していないが、イミノ基型メラミン樹脂の代わりにブチル化メラミン樹脂を用いた塗料も調製したが、調製時に塗料が固化したため塗膜を形成できなかった。表1では、イミノ基型メラミン樹脂を用いたものは「イミノ基型」、メチル化メラミン樹脂を用いたものは「メチル化」と示した。 (Preparation of paint)
A polyester resin (molecular weight: 16,000; glass transition point: 10 ° C.) as a binder resin was dispersed in water as an emulsion, and the pH was adjusted to 8.0 to 9.0. The imino group type melamine resin was mixed therein. The ratio of the concentration of the polyester resin and the imino group type melamine resin was 100: 20. Next, in the mixture, resin-coated aluminum having an average particle diameter of 10 μm and an average aspect ratio of 25 (major axis X 1 : 12 μm, minor axis X 2 : 8 μm, thickness X 3 : 0.40 μm) as a color pigment, and the average particle diameter 3μm of Si two compounds as rust pigment (silica a: a specific surface area of 320 m 2 / g, silica B: specific surface area of 180m 2 / g), Ba two compounds (barium borate a: a specific surface area of 40 m 2 / g , Barium borate B: specific surface area 4.2 m 2 / g), Mo compound (calcium molybdate: specific surface area 80 m 2 / g) or W compound (tungsten oxide: specific surface area 40 m 2 / g) A paint was prepared. As will be described later, the addition amounts of the color pigment and the rust preventive pigment were appropriately adjusted so that a desired concentration was obtained in the coating film when measured using GD-OES. Table 1 shows the types of anticorrosive pigments added (Si-A is silica A, Si-B is silica B, Ba-A is barium borate A, Ba-B is barium borate B, and Mo is molybdic acid. Calcium and W represent tungsten oxide). Sample No. No. 32 is an example in which no rust preventive pigment was added. 35 is an example in which a methylated melamine resin is used in place of the imino group type melamine resin. Although not described in Table 1, a paint using a butylated melamine resin instead of the imino group type melamine resin was also prepared, but a coating film could not be formed because the paint solidified at the time of preparation. In Table 1, those using an imino group type melamine resin are indicated as “imino group type”, and those using a methylated melamine resin are indicated as “methylation”.
上記のように調製した塗料を、形成される塗膜の平均厚さT1が5μmになるようにZn系合金めっき層上にロールコーターで塗布し、焼付けることで硬化させた。焼付けは、表1に記載したような条件(到達温度A、加熱時間A、加熱速度A、保持時間、到達温度B、加熱時間B、加熱速度B)で行った。具体的には、まず、上記のZn系合金めっき層を形成しためっき鋼板の焼付け開始時の温度を20℃に維持し、当該めっき鋼板に上記の塗料を塗布後、表1に記載されるように加熱炉Aで到達温度Aまで加熱速度Aで昇温し、到達温度Aで所定の保持時間保持した後、加熱炉Bで到達温度Bまで加熱速度Bで昇温した。焼付けの際の加熱速度と鋼板の到達温度と保持時間との組み合わせを変更して、表面処理鋼板の試料の比CA1/CA2及び/又は比CB1/CB2を調整した。 (Formation of coating film)
The coating material prepared as described above was applied on a Zn-based alloy plating layer with a roll coater so that the average thickness T 1 of the coating film to be formed was 5 μm and cured by baking. Baking was performed under the conditions as described in Table 1 (attainment temperature A, heating time A, heating rate A, holding time, attainment temperature B, heating time B, heating rate B). Specifically, first, the temperature at the start of baking of the plated steel sheet on which the Zn-based alloy plating layer is formed is maintained at 20 ° C., and the coating material is applied to the plated steel sheet, as described in Table 1. Then, the temperature was raised at the heating rate A to the ultimate temperature A in the heating furnace A, held at the ultimate temperature A for a predetermined holding time, and then heated at the heating rate B to the ultimate temperature B in the heating furnace B. The ratio C A1 / C A2 and / or the ratio C B1 / C B2 of the sample of the surface-treated steel sheet was adjusted by changing the combination of the heating rate at the time of baking, the ultimate temperature of the steel sheet, and the holding time.
上記のように表面処理鋼板の試料を作成し、表1に示したようなめっき化学組成、着色顔料及び防錆顔料の濃度及び濃度分布並びに防錆顔料の種類を有する各試料について、以下のように耐食性及び耐黒変性の評価試験を行った。 <Evaluation of surface-treated steel sheet sample>
Samples of the surface-treated steel sheet were prepared as described above, and for each sample having the plating chemical composition, the concentration and concentration distribution of the color pigment and the rust preventive pigment, and the type of the rust preventive pigment as shown in Table 1, An evaluation test of corrosion resistance and blackening resistance was conducted.
それぞれの試料について、耐食性の評価試験として塩水噴霧試験(JASO M609-91法に準拠)を行った。この塩水噴霧試験は、(1)塩水噴霧2時間(5%NaCl、35℃);(2)乾燥4時間(60℃);及び(3)湿潤2時間(50℃、湿度95%以上)を1サイクルとして合計120サイクル(合計960時間)実施した。端面からの腐食を防ぐため、各試料の端面をテープによりシールして試験した。各試料は幅50mm、長さ100mmとした。 (Evaluation test for corrosion resistance)
Each sample was subjected to a salt spray test (based on the JASO M609-91 method) as an evaluation test for corrosion resistance. This salt spray test consists of (1) salt spray 2 hours (5% NaCl, 35 ° C.); (2) drying 4 hours (60 ° C.); and (3) wet 2 hours (50 ° C., humidity 95% or more). A total of 120 cycles (total 960 hours) were performed as one cycle. In order to prevent corrosion from the end face, the end face of each sample was sealed with a tape and tested. Each sample had a width of 50 mm and a length of 100 mm.
評点8:Z=0%
評点7:0%<Z≦5%
評点6:5%<Z≦10%
評点5:10%<Z≦20%
評点4:20%<Z≦30%
評点3:30%<Z≦40%
評点2:40%<Z≦50%
評点1:50%<Z The corrosion resistance was evaluated by observing the surface (planar portion) of the sample after 960 hours of the salt spray test with an optical microscope and determining the rust generation area ratio Z. Specifically, first, the surface of the sample was read with a scanner. Then, the area | region where rust generate | occur | produced was selected using image editing software, and the rust generation | occurence | production area ratio was calculated | required. This procedure was performed on five samples, and the “rust generation area ratio Z” was determined by averaging the rust generation area ratio. Based on the “rust generation area ratio Z” determined for each sample as described above, the score of each sample was determined in eight stages as follows. A score of 3 or higher was regarded as a passing score for corrosion resistance.
Score 8: Z = 0%
Score 7: 0% <Z ≦ 5%
Score 6: 5% <Z ≦ 10%
Score 5: 10% <Z ≦ 20%
Score 4: 20% <Z ≦ 30%
Score 3: 30% <Z ≦ 40%
Score 2: 40% <Z ≦ 50%
Score 1: 50% <Z
それぞれの試料について、耐黒変性の評価試験として、サンシャイン・カーボン・アーク灯式耐候性試験(SWOM)(JIS D0205に準拠)を行った。試験は、60分間のアークランプ噴射時間中に水を12分間噴射し、これを合計500時間行った。各試料は幅50mm、長さ50mmとした。 (Evaluation test for blackening resistance)
Each sample was subjected to a sunshine carbon arc lamp weather resistance test (SWOM) (based on JIS D0205) as an evaluation test for blackening resistance. The test was carried out for a total of 500 hours, spraying water for 12 minutes during an arc lamp spraying time of 60 minutes. Each sample had a width of 50 mm and a length of 50 mm.
評点8:ΔL*≦1
評点7:1<ΔL*≦2
評点6:2<ΔL*≦3
評点5:3<ΔL*≦4
評点4:4<ΔL*≦5
評点3:5<ΔL*≦6
評点2:6<ΔL*≦7
評点1:7<ΔL* The evaluation of blackening resistance was determined by measuring “color change ΔL * ” (lightness L of the sample after the test−lightness L of the sample before the test) on the surface of the sample before and after performing the weather resistance test. ΔL * was determined by color tone measurement (JIS Z8729) based on the CIE color system (L * a * b * color system) using a spectrocolorimeter (Suga Test Instruments Co., Ltd .: SC-T45). . According to the measured ΔL * , the score was determined in 8 steps as follows. A score of 3 or higher was considered acceptable for blackening resistance.
Score 8: ΔL * ≦ 1
Score 7: 1 <ΔL * ≦ 2
Score 6: 2 <ΔL * ≦ 3
Score 5: 3 <ΔL * ≦ 4
Score 4: 4 <ΔL * ≦ 5
Score 3: 5 <ΔL * ≦ 6
Score 2: 6 <ΔL * ≦ 7
Score 1: 7 <ΔL *
Claims (5)
- 鋼板、前記鋼板上の少なくとも片面に形成されたZn系合金めっき層、及び前記Zn系合金めっき層上に形成され、着色顔料と防錆顔料とバインダー樹脂とを含む平均厚さT1の塗膜を有し、
前記Zn系合金めっき層の化学組成が、質量%で、
Al:0.01~60%、
Mg:0.001~10%、及び
Si:0~2%であり、
前記塗膜中の前記着色顔料の平均濃度が、質量%で、5~15%であり、前記塗膜の表面から塗膜の厚さ方向に幅T2の領域に存在する前記着色顔料の平均濃度CA1と、前記塗膜の前記Zn系合金めっき層側の界面から塗膜の厚さ方向に幅T2の領域に存在する前記着色顔料の平均濃度CA2との比CA1/CA2が0.2~0.9であり、
T2(μm)=0.1×T1(μm)+1.1μmであることを特徴とする、表面処理鋼板。 A steel sheet, a Zn-based alloy plating layer formed on at least one surface of the steel sheet, and a coating film having an average thickness T 1 formed on the Zn-based alloy plating layer and containing a color pigment, a rust preventive pigment, and a binder resin Have
The chemical composition of the Zn-based alloy plating layer is mass%,
Al: 0.01 to 60%,
Mg: 0.001 to 10%, and Si: 0 to 2%,
The average concentration of the colored pigment in the coating film is 5 to 15% by mass, and the average concentration of the coloring pigment existing in the region of the width T 2 from the surface of the coating film in the thickness direction of the coating film. and concentration C A1, the ratio of the Zn-based alloy plating layer side of the interface of the coating and the average concentration C A2 of the coloring pigment present in the region having a width T 2 in the thickness direction of the coating film C A1 / C A2 Is 0.2 to 0.9,
A surface-treated steel sheet, wherein T 2 (μm) = 0.1 × T 1 (μm) +1.1 μm. - 前記塗膜中の前記防錆顔料の平均濃度が、質量%で、3~12%であり、
前記塗膜の表面から塗膜の厚さ方向に幅T2の領域に存在する前記防錆顔料の平均濃度CB1と、前記塗膜の前記Zn系合金めっき層側の界面から塗膜の厚さ方向に幅T2の領域に存在する前記防錆顔料の平均濃度CB2との比CB1/CB2が1.3~4.0であり、
T2(μm)=0.1×T1(μm)+1.1μmであり、
前記防錆顔料が、Si、Mo、W及びBaの1種又は2種以上を含むことを特徴とする、請求項1に記載の表面処理鋼板。 The average concentration of the anticorrosive pigment in the coating film is 3% to 12% by mass%,
The average concentration C B1 of the anticorrosive pigment existing in the region of the width T 2 in the thickness direction of the coating film from the surface of the coating film, and the thickness of the coating film from the interface on the Zn-based alloy plating layer side of the coating film The ratio C B1 / C B2 to the average concentration C B2 of the anticorrosive pigment existing in the width T 2 region in the lengthwise direction is 1.3 to 4.0,
T 2 (μm) = 0.1 × T 1 (μm) +1.1 μm,
The surface-treated steel sheet according to claim 1, wherein the rust-preventing pigment contains one or more of Si, Mo, W, and Ba. - 前記着色顔料が、5~30μmである長径X1と、1~30μmである短径X2と、0.0025μm以上である厚さX3とを有し、平均粒径=(X1+X2)/2、及び平均アスペクト比=(X1+X2)/2X3とした場合に、前記着色顔料の平均粒径が7~30μmであり、平均アスペクト比が20以上であることを特徴とする、請求項1又は2に記載の表面処理鋼板。 The color pigment has a major axis X 1 of 5 to 30 μm, a minor axis X 2 of 1 to 30 μm, and a thickness X 3 of 0.0025 μm or more, and an average particle size = (X 1 + X 2 ) / 2 and average aspect ratio = (X 1 + X 2 ) / 2X 3 , the color pigment has an average particle diameter of 7 to 30 μm and an average aspect ratio of 20 or more. The surface-treated steel sheet according to claim 1 or 2.
- 前記塗膜の平均厚さT1が3~15μmであることを特徴とする、請求項1~3のいずれか1項に記載の表面処理鋼板。 The surface-treated steel sheet according to any one of claims 1 to 3, wherein an average thickness T 1 of the coating film is 3 to 15 µm.
- 前記着色顔料の厚さが0.5T1以下である、請求項1~4のいずれか1項に記載の表面処理鋼板。 The surface-treated steel sheet according to any one of claims 1 to 4, wherein the color pigment has a thickness of 0.5 T 1 or less.