WO2019069754A1 - Plaque polarisante, dispositif d'affichage d'image et procédé de production de plaque polarisante - Google Patents

Plaque polarisante, dispositif d'affichage d'image et procédé de production de plaque polarisante Download PDF

Info

Publication number
WO2019069754A1
WO2019069754A1 PCT/JP2018/035612 JP2018035612W WO2019069754A1 WO 2019069754 A1 WO2019069754 A1 WO 2019069754A1 JP 2018035612 W JP2018035612 W JP 2018035612W WO 2019069754 A1 WO2019069754 A1 WO 2019069754A1
Authority
WO
WIPO (PCT)
Prior art keywords
polarizing plate
based resin
stretching
polyester
polarizer
Prior art date
Application number
PCT/JP2018/035612
Other languages
English (en)
Japanese (ja)
Inventor
善則 南川
健太郎 池嶋
後藤　周作
咲美 ▲徳▼岡
Original Assignee
日東電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日東電工株式会社 filed Critical 日東電工株式会社
Priority to CN201880064514.XA priority Critical patent/CN111183379A/zh
Priority to KR1020207009169A priority patent/KR102640210B1/ko
Publication of WO2019069754A1 publication Critical patent/WO2019069754A1/fr

Abstract

L'invention concerne une plaque polarisante présentant un comportement de retrait thermique faible et dans laquelle le décollement est supprimé. La plaque polarisante selon l'invention comprend un matériau de base en résine polyester et un polariseur stratifié sur un côté du matériau de base en résine polyester. L'épaisseur du polariseur n'est pas supérieure à 10 µm. Si P(1340) représente l'intensité d'absorption à 1,340 cm–1 et P(1410) représente l'intensité d'absorption à 1,410 cm –1, tel que déterminé par des mesures de spectroscopie infrarouge à transformée de Fourier (FT-IR) par mise en oeuvre d'un procédé de réfléctance totale atténuée (ATR) non polarisée, le matériau de base en résine polyester présente une valeur P(1340)/(P(1410) d'au moins 0,60.
PCT/JP2018/035612 2017-10-03 2018-09-26 Plaque polarisante, dispositif d'affichage d'image et procédé de production de plaque polarisante WO2019069754A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201880064514.XA CN111183379A (zh) 2017-10-03 2018-09-26 偏振片、图像显示装置及偏振片的制造方法
KR1020207009169A KR102640210B1 (ko) 2017-10-03 2018-09-26 편광판, 화상 표시 장치 및 편광판의 제조 방법

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017-193273 2017-10-03
JP2017193273A JP7240089B2 (ja) 2017-10-03 2017-10-03 偏光板、画像表示装置、および偏光板の製造方法

Publications (1)

Publication Number Publication Date
WO2019069754A1 true WO2019069754A1 (fr) 2019-04-11

Family

ID=65994272

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/035612 WO2019069754A1 (fr) 2017-10-03 2018-09-26 Plaque polarisante, dispositif d'affichage d'image et procédé de production de plaque polarisante

Country Status (5)

Country Link
JP (1) JP7240089B2 (fr)
KR (1) KR102640210B1 (fr)
CN (1) CN111183379A (fr)
TW (1) TWI835751B (fr)
WO (1) WO2019069754A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115989138A (zh) * 2020-08-27 2023-04-18 日东电工株式会社 光学层叠体及使用了该光学层叠体的偏光板的制造方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2011053271A (ja) * 2009-08-31 2011-03-17 Teijin Dupont Films Japan Ltd 偏光子支持基材用フィルム
JP2015525900A (ja) * 2013-06-18 2015-09-07 エルジー・ケム・リミテッド 薄型偏光板及びその製造方法
JP2015225129A (ja) * 2014-05-26 2015-12-14 富士フイルム株式会社 ポリエステルフィルムおよびその製造方法、偏光板、画像表示装置、ハードコートフィルムならびにタッチパネル
KR101694258B1 (ko) * 2016-06-20 2017-01-09 에스케이씨 주식회사 편광자 보호 필름, 이를 포함하는 편광판, 및 이를 구비한 표시 장치
WO2017149909A1 (fr) * 2016-03-04 2017-09-08 日東電工株式会社 Plaque de polarisation

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4279944B2 (ja) 1999-06-01 2009-06-17 株式会社サンリッツ 偏光板の製造方法
KR100694258B1 (ko) * 2003-07-25 2007-03-14 엘지전자 주식회사 슬라이드 타입 휴대 단말기
JP2011000532A (ja) * 2009-06-18 2011-01-06 Daicel Chemical Industries Ltd アルコール脱水素反応用触媒、及びこれを用いたアルデヒドの製造方法
KR101833579B1 (ko) 2010-12-02 2018-02-28 닛토덴코 가부시키가이샤 편광판의 제조 방법
JP6086824B2 (ja) * 2013-06-14 2017-03-01 ヤマハ発動機株式会社 駆動ステージ及び駆動ステージを用いた部品実装装置

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2011053271A (ja) * 2009-08-31 2011-03-17 Teijin Dupont Films Japan Ltd 偏光子支持基材用フィルム
JP2015525900A (ja) * 2013-06-18 2015-09-07 エルジー・ケム・リミテッド 薄型偏光板及びその製造方法
JP2015225129A (ja) * 2014-05-26 2015-12-14 富士フイルム株式会社 ポリエステルフィルムおよびその製造方法、偏光板、画像表示装置、ハードコートフィルムならびにタッチパネル
WO2017149909A1 (fr) * 2016-03-04 2017-09-08 日東電工株式会社 Plaque de polarisation
KR101694258B1 (ko) * 2016-06-20 2017-01-09 에스케이씨 주식회사 편광자 보호 필름, 이를 포함하는 편광판, 및 이를 구비한 표시 장치

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115989138A (zh) * 2020-08-27 2023-04-18 日东电工株式会社 光学层叠体及使用了该光学层叠体的偏光板的制造方法

Also Published As

Publication number Publication date
TW201922480A (zh) 2019-06-16
KR20200066299A (ko) 2020-06-09
TWI835751B (zh) 2024-03-21
CN111183379A (zh) 2020-05-19
KR102640210B1 (ko) 2024-02-23
JP2019066714A (ja) 2019-04-25
JP7240089B2 (ja) 2023-03-15

Similar Documents

Publication Publication Date Title
JP6893762B2 (ja) 偏光板
TWI645224B (zh) Polarizer
WO2019069756A1 (fr) Plaque polarisante, dispositif d'affichage d'image et procédé de production de plaque polarisante
WO2019069757A1 (fr) Plaque polarisante, dispositif d'affichage d'image, et procédé de production de plaque polarisante
JP6921953B2 (ja) 積層体、積層体の製造方法、偏光板、および偏光板の製造方法
KR102640210B1 (ko) 편광판, 화상 표시 장치 및 편광판의 제조 방법
JP7240090B2 (ja) 偏光板、画像表示装置、および偏光板の製造方法
TWI857940B (zh) 偏光板、影像顯示裝置及偏光板之製造方法
KR102716823B1 (ko) 편광판, 화상 표시 장치 및 편광판의 제조 방법
KR102718408B1 (ko) 편광판, 화상 표시 장치 및 편광판의 제조 방법
CN115989138A (zh) 光学层叠体及使用了该光学层叠体的偏光板的制造方法
WO2019078050A1 (fr) Procédé de fabrication de stratifié optique

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18864081

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18864081

Country of ref document: EP

Kind code of ref document: A1