WO2018215065A1 - Alliage ferritique - Google Patents

Alliage ferritique Download PDF

Info

Publication number
WO2018215065A1
WO2018215065A1 PCT/EP2017/062567 EP2017062567W WO2018215065A1 WO 2018215065 A1 WO2018215065 A1 WO 2018215065A1 EP 2017062567 W EP2017062567 W EP 2017062567W WO 2018215065 A1 WO2018215065 A1 WO 2018215065A1
Authority
WO
WIPO (PCT)
Prior art keywords
ferritic alloy
alloy according
alloy
weight
ferritic
Prior art date
Application number
PCT/EP2017/062567
Other languages
English (en)
Inventor
Bo JÖNSSON
Original Assignee
Sandvik Intellectual Property Ab
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sandvik Intellectual Property Ab filed Critical Sandvik Intellectual Property Ab
Priority to JP2019564792A priority Critical patent/JP7267936B2/ja
Priority to EP17726608.7A priority patent/EP3631034A1/fr
Priority to CN201780091046.0A priority patent/CN110709529A/zh
Priority to US16/613,137 priority patent/US20200181745A1/en
Priority to PCT/EP2017/062567 priority patent/WO2018215065A1/fr
Priority to BR112019024471-9A priority patent/BR112019024471A2/pt
Priority to CA3062819A priority patent/CA3062819A1/fr
Publication of WO2018215065A1 publication Critical patent/WO2018215065A1/fr

Abstract

Cette invention concerne un alliage ferritique comprenant les éléments suivants en % en poids [% en poids] : C : 0,01 à 0,1 ; N : 0,001 à 0,1 ; O : ≤ 0,2 ; Cr : 4 à 15 ; Al : 2 à 6 ; Si : 0,5 à 3 ; Mn : ≤ 3.0 ; Mo + W ≤ 4 ; Y ≤ 1,0 ; Sc, Ce, et/ou La ≤ 0,2 ; Zr ≤ 0,40 ; RE ≤ 0,4 ; le reste étant du Fe et les inévitables impuretés et satisfaisant en outre l'équation suivante : 0,014 ≤ (Al + 0,5 SQ (Cr + 10 Si + 0,1) ≤ 0,022.
PCT/EP2017/062567 2017-05-24 2017-05-24 Alliage ferritique WO2018215065A1 (fr)

Priority Applications (7)

Application Number Priority Date Filing Date Title
JP2019564792A JP7267936B2 (ja) 2017-05-24 2017-05-24 フェライト合金
EP17726608.7A EP3631034A1 (fr) 2017-05-24 2017-05-24 Alliage ferritique
CN201780091046.0A CN110709529A (zh) 2017-05-24 2017-05-24 铁素体合金
US16/613,137 US20200181745A1 (en) 2017-05-24 2017-05-24 Ferritic alloy
PCT/EP2017/062567 WO2018215065A1 (fr) 2017-05-24 2017-05-24 Alliage ferritique
BR112019024471-9A BR112019024471A2 (pt) 2017-05-24 2017-05-24 Liga ferrítica
CA3062819A CA3062819A1 (fr) 2017-05-24 2017-05-24 Alliage ferritique

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/EP2017/062567 WO2018215065A1 (fr) 2017-05-24 2017-05-24 Alliage ferritique

Publications (1)

Publication Number Publication Date
WO2018215065A1 true WO2018215065A1 (fr) 2018-11-29

Family

ID=58800816

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2017/062567 WO2018215065A1 (fr) 2017-05-24 2017-05-24 Alliage ferritique

Country Status (7)

Country Link
US (1) US20200181745A1 (fr)
EP (1) EP3631034A1 (fr)
JP (1) JP7267936B2 (fr)
CN (1) CN110709529A (fr)
BR (1) BR112019024471A2 (fr)
CA (1) CA3062819A1 (fr)
WO (1) WO2018215065A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2021043913A1 (fr) * 2019-09-03 2021-03-11 Kanthal Ab Nouveau matériau de soudage

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN117403138B (zh) * 2023-10-24 2024-05-14 上海交通大学 一种耐腐蚀氧化物弥散强化钢及其制备方法

Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1262588A (en) * 1968-06-28 1972-02-02 Allegheny Ludlum Ind Inc Improvements in or relating to ferritic stainless steel resistant to oxidation at elevated temperatures
US4261739A (en) * 1979-08-06 1981-04-14 Armco Inc. Ferritic steel alloy with improved high temperature properties
EP0091526A2 (fr) 1982-04-12 1983-10-19 Allegheny Ludlum Corporation Alliage fer-chrome-aluminium, article réalisé avec cet alliage et procédé pour sa fabrication
EP0475420A1 (fr) 1990-09-12 1992-03-18 Kawasaki Steel Corporation Feuille mince d'alliages fer-chrome-aluminium, obtenue par solidification rapide et résistant à l'oxydation
JPH0741917A (ja) * 1993-07-27 1995-02-10 Nippon Steel Corp 自動車排気系用鋼
JPH0741905A (ja) * 1993-07-27 1995-02-10 Nippon Steel Corp 自動車排気系用鋼
JPH07157852A (ja) * 1993-10-15 1995-06-20 Kawasaki Steel Corp 高温塩害特性に優れたフェライト系ステンレス鋼
JP2000273592A (ja) * 1999-03-19 2000-10-03 Sanyo Special Steel Co Ltd 冷間鍛造用電磁ステンレス鋼及びその製造方法
JP2001164317A (ja) * 1999-12-09 2001-06-19 Nippon Steel Corp 耐酸化性に優れた自動車排気系鋼管の製造方法
FR2806940A1 (fr) * 2000-03-29 2001-10-05 Usinor Feuillard en acier inoxydable ferritique contenant de l'aluminium, utilisable notamment pour un support de catalyseur d'echappement de vehicule automobile et procede de fabrication dudit feuillard
JP2009167443A (ja) * 2008-01-11 2009-07-30 Nisshin Steel Co Ltd フェライト系ステンレス鋼及びその製造方法
JP2011162863A (ja) * 2010-02-12 2011-08-25 Nippon Steel & Sumikin Stainless Steel Corp 耐酸化性と電気伝導性に優れたＡｌ含有フェライト系ステンレス鋼
WO2017182188A1 (fr) * 2016-04-22 2017-10-26 Sandvik Intellectual Property Ab Alliage ferritique

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5541290B2 (fr) * 1973-11-02 1980-10-23
JPS5911660B2 (ja) * 1979-10-31 1984-03-16 日新製鋼株式会社 燃焼機器熱吸収放射体用ステンレス鋼
JPS5915974B2 (ja) * 1980-04-18 1984-04-12 住友金属工業株式会社 石油、石炭化学プラント用フエライト鋼

Patent Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1262588A (en) * 1968-06-28 1972-02-02 Allegheny Ludlum Ind Inc Improvements in or relating to ferritic stainless steel resistant to oxidation at elevated temperatures
US4261739A (en) * 1979-08-06 1981-04-14 Armco Inc. Ferritic steel alloy with improved high temperature properties
EP0091526A2 (fr) 1982-04-12 1983-10-19 Allegheny Ludlum Corporation Alliage fer-chrome-aluminium, article réalisé avec cet alliage et procédé pour sa fabrication
EP0475420A1 (fr) 1990-09-12 1992-03-18 Kawasaki Steel Corporation Feuille mince d'alliages fer-chrome-aluminium, obtenue par solidification rapide et résistant à l'oxydation
JPH0741917A (ja) * 1993-07-27 1995-02-10 Nippon Steel Corp 自動車排気系用鋼
JPH0741905A (ja) * 1993-07-27 1995-02-10 Nippon Steel Corp 自動車排気系用鋼
JPH07157852A (ja) * 1993-10-15 1995-06-20 Kawasaki Steel Corp 高温塩害特性に優れたフェライト系ステンレス鋼
JP2000273592A (ja) * 1999-03-19 2000-10-03 Sanyo Special Steel Co Ltd 冷間鍛造用電磁ステンレス鋼及びその製造方法
JP2001164317A (ja) * 1999-12-09 2001-06-19 Nippon Steel Corp 耐酸化性に優れた自動車排気系鋼管の製造方法
FR2806940A1 (fr) * 2000-03-29 2001-10-05 Usinor Feuillard en acier inoxydable ferritique contenant de l'aluminium, utilisable notamment pour un support de catalyseur d'echappement de vehicule automobile et procede de fabrication dudit feuillard
JP2009167443A (ja) * 2008-01-11 2009-07-30 Nisshin Steel Co Ltd フェライト系ステンレス鋼及びその製造方法
JP2011162863A (ja) * 2010-02-12 2011-08-25 Nippon Steel & Sumikin Stainless Steel Corp 耐酸化性と電気伝導性に優れたＡｌ含有フェライト系ステンレス鋼
WO2017182188A1 (fr) * 2016-04-22 2017-10-26 Sandvik Intellectual Property Ab Alliage ferritique

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2021043913A1 (fr) * 2019-09-03 2021-03-11 Kanthal Ab Nouveau matériau de soudage

Also Published As

Publication number Publication date
US20200181745A1 (en) 2020-06-11
JP7267936B2 (ja) 2023-05-02
EP3631034A1 (fr) 2020-04-08
CA3062819A1 (fr) 2018-11-29
CN110709529A (zh) 2020-01-17
JP2020521051A (ja) 2020-07-16
BR112019024471A2 (pt) 2020-06-16

Similar Documents

Publication Publication Date Title
JP2024079699A (ja) フェライト合金
EP2479302B1 (fr) Alliage thermorésistant à base de Ni, composant de turbine à gaz et turbine à gaz
KR20120137520A (ko) 오스테나이트계 스테인리스강
WO1990010722A1 (fr) Alliages de ferrure d'aluminium ayant des proprietes ameliorees pour des applications a temperatures elevees
EP3318653B1 (fr) Acier inoxydable ferritique
JPH0885849A (ja) 高Ｃｒフェライト系耐熱鋼
EP3118341B1 (fr) Acier inoxydable ferritique
US20200181745A1 (en) Ferritic alloy
US5296054A (en) Austenitic steel
JPWO2018066573A1 (ja) オーステナイト系耐熱合金およびそれを用いた溶接継手
JP2003171745A (ja) 熱交換器用オーステナイト系ステンレス鋼板
JP5554180B2 (ja) オーステナイト系ステンレス鋼
JPH1096038A (ja) 高Ｃｒオーステナイト系耐熱合金
JPH0835043A (ja) 熱間加工性フェライト系ステンレス鋼合金
JP2005144488A (ja) 連続鋳造ロール肉盛用溶接材料およびロール
JP3367216B2 (ja) 高Ｃｒフェライト系耐熱鋼
WO2021043913A1 (fr) Nouveau matériau de soudage
JP2024088135A (ja) フェライト系ステンレス鋼
WO2004087980A1 (fr) Acier inoxydable pour applications a hautes temperatures
JPH0813071A (ja) 高温度で鍛造可能な合金
JP2001220636A (ja) ニッケルアルミナイド系超耐熱合金

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17726608

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 3062819

Country of ref document: CA

ENP Entry into the national phase

Ref document number: 2019564792

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

REG Reference to national code

Ref country code: BR

Ref legal event code: B01A

Ref document number: 112019024471

Country of ref document: BR

WWE Wipo information: entry into national phase

Ref document number: 2017726608

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 2017726608

Country of ref document: EP

Effective date: 20200102

ENP Entry into the national phase

Ref document number: 112019024471

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20191121