WO2017186547A1 - Hitzeschild mit äusserster yttriumoxidbeschichtung, verfahren zur herstellung und produkt - Google Patents
Hitzeschild mit äusserster yttriumoxidbeschichtung, verfahren zur herstellung und produkt Download PDFInfo
- Publication number
- WO2017186547A1 WO2017186547A1 PCT/EP2017/059318 EP2017059318W WO2017186547A1 WO 2017186547 A1 WO2017186547 A1 WO 2017186547A1 EP 2017059318 W EP2017059318 W EP 2017059318W WO 2017186547 A1 WO2017186547 A1 WO 2017186547A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- heat shield
- yttrium oxide
- outermost
- substrate
- Prior art date
Abstract
Durch die Verwendung von Yttriumoxid auf Aluminiumoxid als Schicht oder Substratmaterial wird die Korrosions- und Erosionsbeständigkeit von keramischen Hitzeschildelementen verbessert.
Description
Hitzeschild mit äußerster Yttriumoxidbeschichtung, Verfahren zur Herstellung und Produkt
Die Erfindung betrifft Hitzeschilde, die eine Vollkeramik aufweisen oder die beschichtete metallische Substrate sowie eine äußerste Yttriumoxidschicht aufweisen, ein Verfahren zur Herstellung und ein Produkt.
Keramische Hitzeschilde können aus massiver Keramik herge¬ stellt werden und weisen dabei vorzugsweise Mullite als Mas¬ sivmaterial auf. Darüber hinaus kann eine weitere Beschich- tung wie Aluminiumoxid auf dem keramischen Substrat vorhanden sein .
Ebenso gibt es Hitzeschildelemente mit metallischem Substrat, bei dem auf einer metallischen Haftvermittlerschicht eine Aluminiumoxidschicht vorhanden ist, eine TBC, die zur Wärme¬ dämmung dient.
Jedoch kommt es je nach Porosität oder abrasivem Abtrag zu Erosion auf der ersten Stufe der nachgeschalteten Turbine des Verbrennungssystems, was unerwünscht ist.
Es ist daher Aufgabe der Erfindung o.g. Problem zu lösen. Die Aufgabe wird gelöst durch ein keramisches Hitzeschild ge¬ mäß Anspruch 1, ein Verfahren nach Anspruch 8 sowie ein Produkt nach Anspruch 9.
In den Unteransprüchen sind weitere vorteilhafte Maßnahmen aufgelistet, die beliebig miteinander kombiniert werden kön¬ nen, um weitere Vorteile zu erzielen.
Die keramischen Hitzeschildelemente aus massiver Keramik wei¬ sen auf, bestehen vorzugsweise aus Mullite (2Al203xSi02) und/oder Aluminiumoxid.
Die Mullitephasen weisen vorzugsweise Körner bis zu 1mm auf und sind in einer feinkörnigen Matrix verteilt. Die Mullite-
phase ist unter Heißgasbedingungen nicht stabil und zersetzt sich oberhalb Temperaturen von 1673K unter dem Einfluss von Wasserdampf zu Aluminiumoxid und Si(OH)4. Zum Schutz weisen daher die keramisch massiven Hitzeschilder (CHS) eine Erosionsschutzschicht (EBC) auf, die aus einer dünnen Lage von lOOym bis 400ym Aluminiumoxid besteht. Die Aluminiumoxid¬ schicht ist vorzugsweise durch einen Plasmaspritzprozess oder andere Spritzprozesse aufgebracht.
Durch die Verwendung von Yttriumoxid als äußerste Schutz¬ schicht auf dem Aluminiumoxid wird die Korrosions- und Ero¬ sionsbeständigkeit verbessert.
Das liegt daran, dass Yttriumoxid Yttriumaluminiumgarnat (YAG) bildet durch die starke Anbindung von Aluminiumoxid in dem CHS bzw. EBC-Schicht. Durch eine Wärmebehandlung oberhalb 1573K für vorzugsweise eine Stunde bildet sich eine hinrei¬ chend dicke Yttriumgarnat-Schicht (YAG-Schicht ) aus.
Es zeigen
Figur 1, 4 ein massives keramisches Hitzeschildelement,
Figur 2, 3 ein metallisches Hitzeschildelement.
Die Figuren und die Beschreibung stellen nur Ausführungsbeispiele der Erfindung dar.
In Figur 1 ist ein massives keramisches Hitzeschild 1 darge¬ stellt .
Das Substrat 4 besteht aus massiver Keramik wie oben be¬ schrieben und weist Mullite und/oder Aluminiumoxid oder vor¬ zugsweise auch nur Aluminiumoxid (AI2O3) auf (FIG 4: 4
1111) .
Auf dem Mullite oder auf dem Aluminiumoxid / Mullite des Sub¬ strats 4, 4xist eine Aluminiumoxidschicht 7 wie oben be¬ schrieben aufgebracht.
Erfindungsgemäß wird eine Yttriumoxidschicht 10 als äußerste Schicht aufgebracht. Bei reinem Aluminiumoxidsubstrat (4λ) kann die Aluminiumodixschicht 7 (FIG 4) entfallen.
Figur 2 zeigt ein metallisches Hitzeschild 11 mit einem me¬ tallischen Substrat 40, auf dem eine metallische Haftver¬ mittlerschicht 42, insbesondere eine NiCoCrAlY-Legierung mit einer Aluminiumoxidschicht 70 vorhanden ist, die sich durch bewusste Oxidation einer metallischen Haftvermittlerschicht 42 und/oder unter Aufbringung einer Aluminiumoxidschicht gebildet hat bzw. vorhanden ist.
Als äußerste Schicht ist ebenfalls eine Yttriumoxidschicht 101 vorhanden.
Figur 3 zeigt ein weiteres Ausführungsbeispiel 111 der Erfin dung ausgehend von Figur 2, bei dem noch eine keramische Wär medämmschicht (TBC) 80 auf der metallischen Haftvermittlerschicht 42 mit einer Aluminiumoxidschicht 71 vorhanden ist, wie es von keramischen Schutzsystemen von Turbinenschaufeln bekannt ist. Darüber hinaus ist ebenfalls eine äußerste Yttriumoxidschicht 100 vorhanden.
Eine sich keramisch bildende Aluminiumoxidschicht (TGO) ist auch zwischen metallischer Haftvermittlerschicht 42 und TBC 80 vorhanden.
Die Yttriumoxidschicht 10, 100, 101 oder das Yttriumoxid weist vorzugsweise nur Yttriumoxid auf, insbesondere beste¬ hend daraus .
Das bedeutet, es ist kein Yttriumoxid als Stabilisator von ZrÜ2 wie ein Y2O3 - ZrÜ2.
Das Yttriumoxid oder die Yttriumoxidschicht 10, 10 0, 101 ist vorzugsweise direkt auf dem Aluminiumoxid oder auf der Alumi niumoxidschicht 7, 70, 71 aufgebracht.
Durch oben genannte Wärmebehandlung bildet sich eine Yttrium- garnatschicht aus (FIG 1 bis FIG 4) .
Claims
1. Hitzeschild (1, 11, 111, 1111),
aufweisend
Aluminiumoxid im Substrat (4, 4λ) oder als Schicht (7, 70, 71) auf einem Substrat (4, 40),
wobei Yttriumoxid,
insbesondere nur Yttriumoxid,
als äußerste Schicht (10, 100, 101) vorhanden ist,
insbesondere direkt auf dem Aluminiumoxid.
2. Massives keramisches Hitzeschild (1) nach Anspruch 1, bei dem das Material des Substrats (4) Mullite aufweist, mit einer zwischenliegenden Aluminiumoxidschicht (7) und einer äußersten Yttriumoxidschicht (10),
insbesondere direkt auf der Aluminiumoxidschicht (7), ganz insbesondere mit einer äußersten Schicht (10) nur aus Yttriumoxid.
Massives keramisches Hitzeschild (1) nach Anspruch 1 oder 2,
bei dem das Material des Substrats (4) Mullite und Alumini umoxid aufweist,
insbesondere daraus besteht.
Massives keramisches Hitzeschild (1111) nach Anspruch 1, bei dem das Material des Substrats (4λ) nur aus Aluminium¬ oxid besteht.
5. Hitzeschild (11, 111) nach Anspruch 1,
das zumindest aufweist
ein metallisches Substrat (40),
eine metallische Haftvermittlerschicht (42),
mit einer durch Oxidation gebildeten Aluminiumoxidschicht und/oder separat aufgebrachten Aluminiumoxidschicht (70, 71), auf der (70, 71) eine äußerste Yttriumoxidschicht (100, 101) aufgebracht ist,
insbesondere direkt auf der Aluminiumoxidschicht (70, 71), ganz insbesondere mit einer äußersten Schicht (100, 101) nur aus Yttriumoxid.
6. Hitzeschild nach Anspruch 5,
bei dem eine keramische Wärmedämmschicht (80),
insbesondere auf Zirkonoxidbasis ,
zwischen einer metallischen Haftvermittlerschicht (42) und Aluminiumoxidschicht (71) vorhanden ist.
7. Hitzeschild nach einem oder mehreren der Ansprüche 1 bis 6,
bei dem die Yttriumoxidschicht (100, 101) nur Yttriumoxid aufweist,
insbesondere daraus besteht,
und/oder nur Yttriumoxid verwendet wird.
8. Verfahren zur Herstellung eines Hitzeschilds (1, 11, 111, 1111),
bei dem ausgehend von einem Hitzeschild nach einem oder mehreren der Ansprüche 1, 2, 3, 4, 5, 6 oder 7 eine Wärme- behandlung bei mindestens 1573K,
insbesondere für mindestens eine Stunde,
durchgeführt wird.
9. Hitzeschild (1, 11, 111, 1111), hergestellt nach Anspruch 8.