WO2017135239A1 - Stratifié optique et dispositif d'affichage d'image dans lequel ledit stratifié optique est utilisé - Google Patents

Stratifié optique et dispositif d'affichage d'image dans lequel ledit stratifié optique est utilisé Download PDF

Info

Publication number
WO2017135239A1
WO2017135239A1 PCT/JP2017/003377 JP2017003377W WO2017135239A1 WO 2017135239 A1 WO2017135239 A1 WO 2017135239A1 JP 2017003377 W JP2017003377 W JP 2017003377W WO 2017135239 A1 WO2017135239 A1 WO 2017135239A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
optical laminate
polarizer
retardation
retardation layer
Prior art date
Application number
PCT/JP2017/003377
Other languages
English (en)
Japanese (ja)
Inventor
浩 角村
清水　享
慎悟 並木
優一 平見
Original Assignee
三菱ケミカル株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2017014146A external-priority patent/JP7044468B2/ja
Application filed by 三菱ケミカル株式会社 filed Critical 三菱ケミカル株式会社
Priority to CN201780009590.6A priority Critical patent/CN108603970B/zh
Priority to US16/072,771 priority patent/US20190079231A1/en
Priority to KR1020187022497A priority patent/KR102577635B1/ko
Priority to SG11201806359WA priority patent/SG11201806359WA/en
Publication of WO2017135239A1 publication Critical patent/WO2017135239A1/fr

Abstract

L'invention concerne un stratifié optique dans lequel une couche électroconductrice est formée directement sur une couche de déphasage, le stratifié optique étant très mince, ayant une fonction antireflet exceptionnelle, et étant en outre apte à présenter des caractéristiques d'affichage exceptionnelles même lorsqu'il est appliqué sur une partie incurvée d'un dispositif d'affichage d'image. Le stratifié optique comprend un polariseur, une couche de déphasage collée sur le polariseur, et une couche électroconductrice formée directement sur la couche de déphasage. La couche de déphasage présente un déphasage dans le plan Re(550) de 100 à 180 nm, et satisfait la relation Re(450) < Re(550) < Re(650), la température de transition vitreuse (Tg) étant de 150°C ou plus, et la valeur absolue du coefficient photo-élastique étant de 20×10-12(m2/N) ou inférieure. L'angle formé par l'axe lent de la couche de déphasage et l'axe d'absorption du polariseur est de 35° à 55°.
PCT/JP2017/003377 2016-02-05 2017-01-31 Stratifié optique et dispositif d'affichage d'image dans lequel ledit stratifié optique est utilisé WO2017135239A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
CN201780009590.6A CN108603970B (zh) 2016-02-05 2017-01-31 光学层叠体及使用了该光学层叠体的图像显示装置
US16/072,771 US20190079231A1 (en) 2016-02-05 2017-01-31 Optical laminate and image display device in which said optical laminate is used
KR1020187022497A KR102577635B1 (ko) 2016-02-05 2017-01-31 광학 적층체 및 해당 광학 적층체를 이용한 화상 표시 장치
SG11201806359WA SG11201806359WA (en) 2016-02-05 2017-01-31 Optical laminate and image display device in which said optical laminate is used

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2016-021299 2016-02-05
JP2016021299 2016-02-05
JP2017-014146 2017-01-30
JP2017014146A JP7044468B2 (ja) 2016-02-05 2017-01-30 光学積層体および該光学積層体を用いた画像表示装置

Publications (1)

Publication Number Publication Date
WO2017135239A1 true WO2017135239A1 (fr) 2017-08-10

Family

ID=59499846

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/003377 WO2017135239A1 (fr) 2016-02-05 2017-01-31 Stratifié optique et dispositif d'affichage d'image dans lequel ledit stratifié optique est utilisé

Country Status (1)

Country Link
WO (1) WO2017135239A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110873916A (zh) * 2018-08-29 2020-03-10 日东电工株式会社 相位差膜、带相位差层的偏振片及相位差膜的制造方法
CN113544552A (zh) * 2019-10-21 2021-10-22 日东电工株式会社 相位差膜及其制造方法以及使用了该相位差膜的圆偏振片及图像显示装置

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004057381A1 (fr) * 2002-12-20 2004-07-08 Teijin Limited Lamine conducteur transparent, ecran tactile et unite d'affichage a cristaux liquides dotee d'un ecran tactile
JP2006131789A (ja) * 2004-11-08 2006-05-25 Teijin Chem Ltd 位相差フィルム用ポリカーボネート共重合体
JP2015212818A (ja) * 2014-04-16 2015-11-26 三菱化学株式会社 位相差フィルム、円偏光板及び画像表示装置

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004057381A1 (fr) * 2002-12-20 2004-07-08 Teijin Limited Lamine conducteur transparent, ecran tactile et unite d'affichage a cristaux liquides dotee d'un ecran tactile
JP2006131789A (ja) * 2004-11-08 2006-05-25 Teijin Chem Ltd 位相差フィルム用ポリカーボネート共重合体
JP2015212818A (ja) * 2014-04-16 2015-11-26 三菱化学株式会社 位相差フィルム、円偏光板及び画像表示装置

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110873916A (zh) * 2018-08-29 2020-03-10 日东电工株式会社 相位差膜、带相位差层的偏振片及相位差膜的制造方法
CN113544552A (zh) * 2019-10-21 2021-10-22 日东电工株式会社 相位差膜及其制造方法以及使用了该相位差膜的圆偏振片及图像显示装置

Similar Documents

Publication Publication Date Title
JP6920047B2 (ja) 円偏光板およびそれを用いたフレキシブルな画像表示装置
JP7044468B2 (ja) 光学積層体および該光学積層体を用いた画像表示装置
JP6453746B2 (ja) 長尺状の光学積層体および画像表示装置
WO2017038416A1 (fr) Plaque de polarisation avec couches de compensation optique de forme allongée, et panneau électroluminescent organique mettant en œuvre celle-ci
JP6301885B2 (ja) 光学補償層付偏光板およびそれを用いた有機ｅｌパネル
JP6712335B2 (ja) 光学補償層付偏光板およびそれを用いた有機ｅｌパネル
WO2017098970A1 (fr) Plaque de polarisation circulaire et dispositif d&#39;affichage d&#39;image flexible l&#39;utilisant
TW202018339A (zh) 附相位差層之偏光板及使用了該附相位差層之偏光板的影像顯示裝置
CN112840245B (zh) 带相位差层的偏光板及使用其的图像显示装置
JP6797499B2 (ja) 位相差層付偏光板およびそれを用いた画像表示装置
JP6709637B2 (ja) 光学補償層付偏光板およびそれを用いた有機ｅｌパネル
JP2020064274A (ja) 位相差層付偏光板およびそれを用いた画像表示装置
JP2020064277A (ja) 位相差層付偏光板およびそれを用いた画像表示装置
WO2017135239A1 (fr) Stratifié optique et dispositif d&#39;affichage d&#39;image dans lequel ledit stratifié optique est utilisé
TWI832889B (zh) 附相位差層之偏光板及使用了該附相位差層之偏光板的影像顯示裝置
JP2020064280A (ja) 位相差層付偏光板およびそれを用いた画像表示装置
TWI827658B (zh) 附相位差層之偏光板及使用該附相位差層之偏光板的影像顯示裝置
JP2020115227A (ja) 位相差層付偏光板およびそれを用いた画像表示装置
TW202104390A (zh) 附相位差層之偏光板及使用其之影像顯示裝置
JP2020064298A (ja) 位相差層付偏光板およびそれを用いた画像表示装置
CN115236785B (zh) 带相位差层的偏光板及使用其的图像显示装置
TWI827659B (zh) 帶相位差層的偏光板及使用了該帶相位差層的偏光板的影像顯示裝置
JP2023073124A (ja) 位相差層付偏光板および該位相差層付偏光板を含む画像表示装置
JP2020064297A (ja) 位相差層付偏光板およびそれを用いた画像表示装置
JP2020064296A (ja) 位相差層付偏光板およびそれを用いた画像表示装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17747395

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 11201806359W

Country of ref document: SG

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17747395

Country of ref document: EP

Kind code of ref document: A1