WO2017064592A1 - Manchon pour fonderies ou aciéries - Google Patents

Manchon pour fonderies ou aciéries Download PDF

Info

Publication number
WO2017064592A1
WO2017064592A1 PCT/IB2016/055957 IB2016055957W WO2017064592A1 WO 2017064592 A1 WO2017064592 A1 WO 2017064592A1 IB 2016055957 W IB2016055957 W IB 2016055957W WO 2017064592 A1 WO2017064592 A1 WO 2017064592A1
Authority
WO
WIPO (PCT)
Prior art keywords
sleeve
chambers
hot top
molten metal
mould
Prior art date
Application number
PCT/IB2016/055957
Other languages
English (en)
Inventor
Giorgio PIANTONI
Original Assignee
Faprosid S.R.L.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Faprosid S.R.L. filed Critical Faprosid S.R.L.
Publication of WO2017064592A1 publication Critical patent/WO2017064592A1/fr

Abstract

L'invention concerne un manchon pour fonderies ou aciéries permettant, par rapport à un manchon classique, l'obtention de masselottes ou de lingots présentant un volume inférieur ou encore l'obtention d'un module de masselotte plus grand à un volume de masselotte équivalent. Le manchon comprend une paroi latérale externe délimitant un volume interne destiné à recevoir le métal fondu à solidifier sous forme de masselotte. Le volume interne est subdivisé en deux chambres ou plus, de manière telle que le rapport de la surface que le métal fondu peut mouiller au volume correspondant est maximisé.
PCT/IB2016/055957 2015-10-12 2016-10-05 Manchon pour fonderies ou aciéries WO2017064592A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
IT612015004597 2015-10-12
IT102015000060661(UB2015A004597) 2015-10-12

Publications (1)

Publication Number Publication Date
WO2017064592A1 true WO2017064592A1 (fr) 2017-04-20

Family

ID=58517173

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2016/055957 WO2017064592A1 (fr) 2015-10-12 2016-10-05 Manchon pour fonderies ou aciéries

Country Status (1)

Country Link
WO (1) WO2017064592A1 (fr)

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US969015A (en) * 1909-12-13 1910-08-30 Edwin C Washburn Riser-lining for molding devices.
GB1071668A (en) * 1963-04-03 1967-06-14 Eduard Baur Feeder body for providing a feeding space in a casting mould
US4081020A (en) * 1975-08-08 1978-03-28 Foseco International Limited Mould assemblies for use in casting molten metals
JPS54102525U (fr) * 1977-12-28 1979-07-19
DE2907301A1 (de) * 1979-02-24 1980-09-04 Eduard Dr Ing Baur Geschlossener speiser fuer giessformen
JPS57190749A (en) * 1981-05-20 1982-11-24 Takada Seikosho:Kk Solid exothermic and heat insulating material for riser
US4694884A (en) * 1985-05-17 1987-09-22 Foseco International Limited Molten metal casting and feeder sleeves for use therein
FR2608477A1 (fr) * 1986-12-23 1988-06-24 Languedoc Acieries Haut Elements isolants pour masselottes de pieces metalliques
CN1084790A (zh) * 1992-09-30 1994-04-06 福塞科国际有限公司 有浇口单元并垂直分离的模型
EP1422004A1 (fr) * 2002-11-22 2004-05-26 Peugeot Citroen Automobiles S.A. Masselotte utilisee pour la fonderie

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US969015A (en) * 1909-12-13 1910-08-30 Edwin C Washburn Riser-lining for molding devices.
GB1071668A (en) * 1963-04-03 1967-06-14 Eduard Baur Feeder body for providing a feeding space in a casting mould
US4081020A (en) * 1975-08-08 1978-03-28 Foseco International Limited Mould assemblies for use in casting molten metals
JPS54102525U (fr) * 1977-12-28 1979-07-19
DE2907301A1 (de) * 1979-02-24 1980-09-04 Eduard Dr Ing Baur Geschlossener speiser fuer giessformen
JPS57190749A (en) * 1981-05-20 1982-11-24 Takada Seikosho:Kk Solid exothermic and heat insulating material for riser
US4694884A (en) * 1985-05-17 1987-09-22 Foseco International Limited Molten metal casting and feeder sleeves for use therein
FR2608477A1 (fr) * 1986-12-23 1988-06-24 Languedoc Acieries Haut Elements isolants pour masselottes de pieces metalliques
CN1084790A (zh) * 1992-09-30 1994-04-06 福塞科国际有限公司 有浇口单元并垂直分离的模型
EP1422004A1 (fr) * 2002-11-22 2004-05-26 Peugeot Citroen Automobiles S.A. Masselotte utilisee pour la fonderie

Similar Documents

Publication Publication Date Title
AU601315B2 (en) Moulds for metal casting and sleeves containing filters for use therein
US6289969B1 (en) Metal casting
US8770265B2 (en) Method and system for manufacturing railcar couplers
US9718124B2 (en) Device for producing a cylinder crankcase using the low-pressure or gravity casting method
US10688555B2 (en) Method and casting mould for the manufacture of cast parts, in particular cylinder blocks and cylinder heads, with a functional feeder connection
CN106232262B (zh) 单晶铸造用模具
WO2017064592A1 (fr) Manchon pour fonderies ou aciéries
US4938802A (en) Reusable ceramic mold
US5291938A (en) Vertically parted mould having a feeder unit therein
CN212191123U (zh) 浇口杯
JPH07155897A (ja) 鋳型構造及び鋳造方法
JP5729642B2 (ja) 柱状インゴットの鋳造装置
ITUB20154597A1 (it) Manicotto per fonderia o acciaieria
JP5748123B2 (ja) 柱状インゴットの鋳造方法
CN217666238U (zh) 浇注铸造高温合金力学试棒用模壳
CN212945276U (zh) 一种阀体配件连接件的熔模铸造结构
RU2245213C1 (ru) Изложница
CN115519080A (zh) 一种高温合金铸锭材料的熔模精密铸造方法
RU1782191C (ru) Способ производства фасонных отливок и литейна форма дл его осуществлени
CA1304561C (fr) Tube avec filtre pour la coulee de metaux
CN110252953A (zh) 一种用于重力铸造浇注的硬模冒口及其铸造方法
RU2003431C1 (ru) Форма дл центробежного лить прокатных валков
US2080961A (en) Billet mold
JPS55153650A (en) Production of hollow casting
CA1304562C (fr) Tube avec filtre pour la coulee de metaux

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16795409

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16795409

Country of ref document: EP

Kind code of ref document: A1