WO2017057188A1 - Composition d'encre argentée, son procédé de production, et produit feuilleté - Google Patents

Composition d'encre argentée, son procédé de production, et produit feuilleté Download PDF

Info

Publication number
WO2017057188A1
WO2017057188A1 PCT/JP2016/078013 JP2016078013W WO2017057188A1 WO 2017057188 A1 WO2017057188 A1 WO 2017057188A1 JP 2016078013 W JP2016078013 W JP 2016078013W WO 2017057188 A1 WO2017057188 A1 WO 2017057188A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
silver
ink composition
silver ink
carbon atoms
Prior art date
Application number
PCT/JP2016/078013
Other languages
English (en)
Japanese (ja)
Inventor
久美 廣瀬
Original Assignee
トッパン・フォームズ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by トッパン・フォームズ株式会社 filed Critical トッパン・フォームズ株式会社
Priority to JP2017543212A priority Critical patent/JP6802798B2/ja
Publication of WO2017057188A1 publication Critical patent/WO2017057188A1/fr

Abstract

La présente invention concerne une composition d'encre argentée qui est obtenue en mélangeant : un carbonate d'argent; un ou plusieurs composés azotés choisis dans le groupe constitué par des composés amines en C25 et des composés amines comprenant moins d'atomes de carbone et des sels d'ammonium quaternaire, de l'ammoniac, et des sels d'ammonium obtenus par la réaction de l'un quelconque des composés amines ou de l'ammoniac avec un acide; un ou plusieurs agents réducteurs choisis dans le groupe constitué par l'acide oxalique, l'hydrazine, et des composés représentés par la formule générale suivante (5); et un composé alcool acétylénique en C9 ou comprenant plus d'atomes de carbone représenté par la formule générale suivante (20). H-C(=O)-R21 (5)
PCT/JP2016/078013 2015-09-29 2016-09-23 Composition d'encre argentée, son procédé de production, et produit feuilleté WO2017057188A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2017543212A JP6802798B2 (ja) 2015-09-29 2016-09-23 銀インク組成物、その製造方法及び積層体

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2015191853 2015-09-29
JP2015-191853 2015-09-29

Publications (1)

Publication Number Publication Date
WO2017057188A1 true WO2017057188A1 (fr) 2017-04-06

Family

ID=58423696

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/078013 WO2017057188A1 (fr) 2015-09-29 2016-09-23 Composition d'encre argentée, son procédé de production, et produit feuilleté

Country Status (2)

Country Link
JP (1) JP6802798B2 (fr)
WO (1) WO2017057188A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017115090A (ja) * 2015-12-25 2017-06-29 トッパン・フォームズ株式会社 銀インク組成物

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS63139964A (ja) * 1986-12-01 1988-06-11 Canon Inc インクジエツト用インク及びそれを用いたインクジエツト記録方法
JP2002309130A (ja) * 2001-04-06 2002-10-23 Seiko Epson Corp 水性インク組成物
WO2007138345A1 (fr) * 2006-05-26 2007-12-06 Johnson Matthey Public Limited Company Procédé de production de nanoparticules métalliques stabilisées
US20100255201A1 (en) * 2009-04-01 2010-10-07 E.I. Du Pont De Nemours And Company Ink jet ink and ink set
WO2014051066A1 (fr) * 2012-09-28 2014-04-03 トッパン・フォームズ株式会社 Composition d'encre à base d'argent, conducteur et dispositif de communication
WO2014051083A1 (fr) * 2012-09-28 2014-04-03 トッパン・フォームズ株式会社 Composition d'encre argentée et produit de traitement thermique

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS63139964A (ja) * 1986-12-01 1988-06-11 Canon Inc インクジエツト用インク及びそれを用いたインクジエツト記録方法
JP2002309130A (ja) * 2001-04-06 2002-10-23 Seiko Epson Corp 水性インク組成物
WO2007138345A1 (fr) * 2006-05-26 2007-12-06 Johnson Matthey Public Limited Company Procédé de production de nanoparticules métalliques stabilisées
US20100255201A1 (en) * 2009-04-01 2010-10-07 E.I. Du Pont De Nemours And Company Ink jet ink and ink set
WO2014051066A1 (fr) * 2012-09-28 2014-04-03 トッパン・フォームズ株式会社 Composition d'encre à base d'argent, conducteur et dispositif de communication
WO2014051083A1 (fr) * 2012-09-28 2014-04-03 トッパン・フォームズ株式会社 Composition d'encre argentée et produit de traitement thermique

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017115090A (ja) * 2015-12-25 2017-06-29 トッパン・フォームズ株式会社 銀インク組成物

Also Published As

Publication number Publication date
JP6802798B2 (ja) 2020-12-23
JPWO2017057188A1 (ja) 2018-07-12

Similar Documents

Publication Publication Date Title
WO2014051066A1 (fr) Composition d'encre à base d'argent, conducteur et dispositif de communication
US20150259557A1 (en) Silver ink composition, conductor and communication device
JP6289841B2 (ja) 銀インク組成物の製造方法
JP6863715B2 (ja) 積層体及び積層体の製造方法
JP6821422B2 (ja) 金属薄膜基材の製造方法
WO2017057188A1 (fr) Composition d'encre argentée, son procédé de production, et produit feuilleté
JP6712949B2 (ja) 金属銀、金属銀の製造方法及び積層体
JPWO2015147124A1 (ja) 積層体
JP6421383B2 (ja) 積層体及び電子機器
JP6604468B2 (ja) 金属銀の製造方法
JP6346486B2 (ja) 積層体、データ受送信体、通信機器及び透明導電膜
JP6650295B2 (ja) 配線板
JP6644998B2 (ja) アンテナ構造体
JP2016005908A (ja) 積層体及び電子機器
JP6678475B2 (ja) 金属インク組成物、配線板及び配線の形成方法
JP6432096B2 (ja) 積層体及び電子機器
JP6081120B2 (ja) 積層体、データ受送信体及び通信機器
JP6322019B2 (ja) 積層体及び電子機器
JP6596783B2 (ja) 積層体、データ受送信体及び電子機器
WO2017110787A1 (fr) Corps stratifié et procédé de fabrication d'un corps stratifié
JP2017226798A (ja) 銀インク組成物
JP6501300B2 (ja) 積層体の製造方法
JP6289988B2 (ja) 銀インク組成物の製造方法
JP6393951B2 (ja) 金属銀の製造方法
JP2014087967A (ja) 積層体、データ受送信体及び通信機器

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16851362

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2017543212

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16851362

Country of ref document: EP

Kind code of ref document: A1