WO2016183761A1 - 磁性材料局部机磁耦合系数测试方法 - Google Patents
磁性材料局部机磁耦合系数测试方法 Download PDFInfo
- Publication number
- WO2016183761A1 WO2016183761A1 PCT/CN2015/079149 CN2015079149W WO2016183761A1 WO 2016183761 A1 WO2016183761 A1 WO 2016183761A1 CN 2015079149 W CN2015079149 W CN 2015079149W WO 2016183761 A1 WO2016183761 A1 WO 2016183761A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- magnetic
- magnetic material
- coupling coefficient
- test method
- curve
- Prior art date
Abstract
Description
Claims (7)
- 如权利要求1所述的测试方法,其特征在于,在步骤1)和2)中,将磁性材料放置在两块永磁体之间,通过调整两块永磁体的距离实现对磁性材料所施加的磁场强度的调节。
- 如权利要求2所述的测试方法,其特征在于,步骤1)和2)利用霍尔探头测量所施加的磁场强度。
- 如权利要求1所述的测试方法,其特征在于,步骤1)和2)用一个与压电驱动器连接的压头压入磁性材料,在压痕加载和卸载过程中,同时通过载荷传感器和位移传感器分别测量压痕的载荷信号和深度信号。
- 如权利要求1所述的测试方法,其特征在于,所述磁性材料是为非均质磁性材料。
- 如权利要求5所述的测试方法,其特征在于,所述磁性材料是层状电磁复合材料。
- 如权利要求1所述的测试方法,其特征在于,所述磁性材料是纳米级磁性薄膜材料。