WO2016165835A1 - Couche de non-tissé pour textiles de protection contre la chaleur - Google Patents

Couche de non-tissé pour textiles de protection contre la chaleur Download PDF

Info

Publication number
WO2016165835A1
WO2016165835A1 PCT/EP2016/025033 EP2016025033W WO2016165835A1 WO 2016165835 A1 WO2016165835 A1 WO 2016165835A1 EP 2016025033 W EP2016025033 W EP 2016025033W WO 2016165835 A1 WO2016165835 A1 WO 2016165835A1
Authority
WO
WIPO (PCT)
Prior art keywords
nonwoven layer
holes
nonwoven fabric
air spaces
layer
Prior art date
Application number
PCT/EP2016/025033
Other languages
German (de)
English (en)
Inventor
Marc Jolly
Stuart Smith
André Lang
Andy SCHUFFENHAUER
Original Assignee
Norafin Industries (Germany) Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Norafin Industries (Germany) Gmbh filed Critical Norafin Industries (Germany) Gmbh
Publication of WO2016165835A1 publication Critical patent/WO2016165835A1/fr

Abstract

L'invention concerne une couche de non-tissé (1), destinée à des textiles de protection contre la chaleur, comprenant un matériau composite fibreux (4) qui est pourvue au moins partiellement de fibres intrinsèquement ignifuges, la couche de non-tissé (1) comportant, de façon répartie dans ses directions de surface (7) en vue de l'isolation thermique, une pluralité d'espaces d'air (5) qui s'étendent dans la direction de l'épaisseur (2), perpendiculaire aux directions de surface (7) de la couche de non-tissé (1), sur au moins 0,1 mm et qui parsèment la couche de non-tissé (1) dans la direction de l'épaisseur (2) mais seulement partiellement et une pluralité de trous (6) étant ménagés dans la couche de non-tissé (1) , en plus des espaces d'air (5), lesquels trous s'étendent d'un côté (3) de la couche de non-tissé (1) dans la direction de l'épaisseur (2) jusque dans la couche de non-tissé (1) et ont, dans les directions de surface (7), une section transversale d'ouverture respectives d'au moins 1 mm2 et au maximum de 15 mm2.
PCT/EP2016/025033 2015-04-15 2016-04-08 Couche de non-tissé pour textiles de protection contre la chaleur WO2016165835A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE102015004841.4 2015-04-15
DE102015004841.4A DE102015004841A1 (de) 2015-04-15 2015-04-15 Vliesstofflage für Hitzeschutztextilien

Publications (1)

Publication Number Publication Date
WO2016165835A1 true WO2016165835A1 (fr) 2016-10-20

Family

ID=55948782

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2016/025033 WO2016165835A1 (fr) 2015-04-15 2016-04-08 Couche de non-tissé pour textiles de protection contre la chaleur

Country Status (2)

Country Link
DE (1) DE102015004841A1 (fr)
WO (1) WO2016165835A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020004348A1 (en) * 2000-03-02 2002-01-10 Kelly Karl Dewayne Imaged nonwoven fire-retardant fiber blends and process for making same
WO2003054265A1 (fr) * 2001-12-21 2003-07-03 Carl Freudenberg Kg Matiere de doublure ignifuge pour vetements de protection contre les effets de la chaleur
DE102004030393A1 (de) * 2004-06-23 2006-01-26 Carl Freudenberg Kg Verfahren zur Herstellung eines dreidimensional geformten Vliesstoffes, Vorrichtung zur Benutzung in dem Verfahren, danach erhaltener dreidimensional geformter Vliesstoff und seine Verwendung
US20060183393A1 (en) * 2005-02-14 2006-08-17 Precision Fabrics Group, Inc. Drapeable and launderable light weight flame retardant barrier fabrics
US20140087129A1 (en) * 2012-09-25 2014-03-27 Pbi Performance Products, Inc. Thermal liner for protective garments

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020004348A1 (en) * 2000-03-02 2002-01-10 Kelly Karl Dewayne Imaged nonwoven fire-retardant fiber blends and process for making same
WO2003054265A1 (fr) * 2001-12-21 2003-07-03 Carl Freudenberg Kg Matiere de doublure ignifuge pour vetements de protection contre les effets de la chaleur
DE102004030393A1 (de) * 2004-06-23 2006-01-26 Carl Freudenberg Kg Verfahren zur Herstellung eines dreidimensional geformten Vliesstoffes, Vorrichtung zur Benutzung in dem Verfahren, danach erhaltener dreidimensional geformter Vliesstoff und seine Verwendung
US20060183393A1 (en) * 2005-02-14 2006-08-17 Precision Fabrics Group, Inc. Drapeable and launderable light weight flame retardant barrier fabrics
US20140087129A1 (en) * 2012-09-25 2014-03-27 Pbi Performance Products, Inc. Thermal liner for protective garments

Also Published As

Publication number Publication date
DE102015004841A1 (de) 2016-10-20

Similar Documents

Publication Publication Date Title
EP3054042B1 (fr) Procédé de fabrication d'un laminé et laminé
EP2547816B1 (fr) Structure textile multiaxiale suturée
DE3132068A1 (de) Nicht-gewebtes tuchartiges material
EP2668328A1 (fr) Minces feuilles polymères macroporeuses
DE2201105A1 (de) Verfahren zur Herstellung eines boucleartige Noppen,Rippen od.dgl. aufweisenden textilen Verbundstoffes
EP2911765B1 (fr) Matériau de filtre à durée d'utilisation accrue et élément filtrant contenant ce matériau de filtre
EP2635732A1 (fr) Tissu non tissé renforcé
DE10133773A1 (de) Regelmässig strukturierte Vliesstoffe, Verfahren zu deren Herstellung und deren Verwendung
EP2187161A1 (fr) Matériau rétractant la traversée
DE4244904C2 (de) Verfahren zur Herstellung eines großvolumigen Vliesstoffes
EP1838523B1 (fr) Structure textile plane multicouche
EP3771556B1 (fr) Stratifié non-tissé et procédé de fabrication d'un stratifié non-tissé
DE102018111164B4 (de) Abstandsgewirk und Verfahren zu dessen Herstellung
DE202015002765U1 (de) Vliesstofflage für Hitzeschutztextilien
EP2758580A1 (fr) Non-tissé pourvu d'une matrice contenant des filaments élémentaires
DE19804940B4 (de) Textiler Schichtverbundstoff und Verfahren zu dessen Herstellung
WO2016165835A1 (fr) Couche de non-tissé pour textiles de protection contre la chaleur
EP1099787B1 (fr) Mat de fibres
DE4114408C2 (de) Dämm- und Isolationsmaterial aus Glasfasern
DE19956368A1 (de) Verfahren zur Herstellung von schmelzgeblasenen Vliesstoffen, daraus hergestellte schmelzgeblasene Vliesstoffe und Verwendung der schmelzgeblasenen Vliesstoffe
DE202018004272U1 (de) Vliesstoffstruktur mit mehreren Lagen
DE102012011221A1 (de) Atmungsaktiver Textilverbund
DE10345953B4 (de) Vliesstoff und Verfahren zur seiner Herstellung
DE1560771A1 (de) Verformbares Faserflaechengebilde
DE10039983C2 (de) Vliesstoff-Träger für Klebebänder

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16721083

Country of ref document: EP

Kind code of ref document: A1

122 Ep: pct application non-entry in european phase

Ref document number: 16721083

Country of ref document: EP

Kind code of ref document: A1