WO2016068337A1 - Courroie de transmission par frottement et son procédé de fabrication - Google Patents

Courroie de transmission par frottement et son procédé de fabrication Download PDF

Info

Publication number
WO2016068337A1
WO2016068337A1 PCT/JP2015/080842 JP2015080842W WO2016068337A1 WO 2016068337 A1 WO2016068337 A1 WO 2016068337A1 JP 2015080842 W JP2015080842 W JP 2015080842W WO 2016068337 A1 WO2016068337 A1 WO 2016068337A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
polyvinyl alcohol
friction transmission
transmission belt
belt
Prior art date
Application number
PCT/JP2015/080842
Other languages
English (en)
Japanese (ja)
Inventor
裕司 勘場
宏貴 今井
Original Assignee
三ツ星ベルト株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2015208209A external-priority patent/JP6175113B2/ja
Application filed by 三ツ星ベルト株式会社 filed Critical 三ツ星ベルト株式会社
Priority to CN201580059231.2A priority Critical patent/CN107002818B/zh
Priority to EP15854588.9A priority patent/EP3214338B1/fr
Priority to US15/523,125 priority patent/US10508712B2/en
Publication of WO2016068337A1 publication Critical patent/WO2016068337A1/fr

Abstract

La présente invention porte sur une courroie de transmission par frottement utilisée pour entraîner des accessoires d'un moteur automobile, etc., et porte de façon spécifique sur une courroie de transmission par frottement, laquelle courroie stabilise les conditions de frottement d'une surface de transmission par frottement tout en maintenant les performances de la courroie, telles que des performances de réduction de consommation de carburant et des performances de résistance à l'usure, de façon à améliorer les performances de résistance à la génération de sons, et sur son procédé de fabrication. L'invention vise à procurer une courroie de transmission par frottement qui stabilise la condition de frottement d'une surface de transmission par frottement tout en maintenant les performances de la courroie, telles que les performances de réduction de consommation de carburant et les performances de résistance à l'usure, de façon à améliorer les performances de résistance à la génération de sons, et son procédé de fabrication. A cet effet, l'invention porte sur sur une courroie de transmission par frottement (10) dont une couche comprimée (2) contient une composition de caoutchouc qui contient un composant polymère et une résine à base de poly(alcool vinylique).
PCT/JP2015/080842 2014-10-31 2015-10-30 Courroie de transmission par frottement et son procédé de fabrication WO2016068337A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CN201580059231.2A CN107002818B (zh) 2014-10-31 2015-10-30 摩擦传动带及其制造方法
EP15854588.9A EP3214338B1 (fr) 2014-10-31 2015-10-30 Courroie de transmission par frottement et son procédé de fabrication
US15/523,125 US10508712B2 (en) 2014-10-31 2015-10-30 Friction transmission belt and manufacturing method thereof

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
JP2014223772 2014-10-31
JP2014-223772 2014-10-31
JP2014262804 2014-12-25
JP2014-262804 2014-12-25
JP2015208209A JP6175113B2 (ja) 2014-10-31 2015-10-22 摩擦伝動ベルト
JP2015-208209 2015-10-22

Publications (1)

Publication Number Publication Date
WO2016068337A1 true WO2016068337A1 (fr) 2016-05-06

Family

ID=55857669

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2015/080842 WO2016068337A1 (fr) 2014-10-31 2015-10-30 Courroie de transmission par frottement et son procédé de fabrication

Country Status (1)

Country Link
WO (1) WO2016068337A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3133207A1 (fr) * 2015-08-12 2017-02-22 Denka Company Limited Liant pour papier de verre
CN111207181A (zh) * 2019-08-21 2020-05-29 宁波丰茂远东橡胶有限公司 一种彩色磨楔带及其制备方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004162897A (ja) * 2002-07-30 2004-06-10 Mitsuboshi Belting Ltd Ｖリブドベルト及びその製造方法
JP2008082538A (ja) * 2006-09-01 2008-04-10 Mitsuboshi Belting Ltd 動力伝動ベルト及び動力伝動ベルトの製造方法
JP2008156806A (ja) * 2006-11-27 2008-07-10 Central Glass Co Ltd ガラス繊維被覆用塗布液およびそれを用いたゴム補強用ガラス繊維
JP2014167347A (ja) * 2013-01-30 2014-09-11 Mitsuboshi Belting Ltd 摩擦伝動ベルト

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004162897A (ja) * 2002-07-30 2004-06-10 Mitsuboshi Belting Ltd Ｖリブドベルト及びその製造方法
JP2008082538A (ja) * 2006-09-01 2008-04-10 Mitsuboshi Belting Ltd 動力伝動ベルト及び動力伝動ベルトの製造方法
JP2008156806A (ja) * 2006-11-27 2008-07-10 Central Glass Co Ltd ガラス繊維被覆用塗布液およびそれを用いたゴム補強用ガラス繊維
JP2014167347A (ja) * 2013-01-30 2014-09-11 Mitsuboshi Belting Ltd 摩擦伝動ベルト

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3133207A1 (fr) * 2015-08-12 2017-02-22 Denka Company Limited Liant pour papier de verre
US11673979B2 (en) 2015-08-12 2023-06-13 Denki Kagaku Kogyo Kabushiki Kaisha Binder for glass paper
CN111207181A (zh) * 2019-08-21 2020-05-29 宁波丰茂远东橡胶有限公司 一种彩色磨楔带及其制备方法

Similar Documents

Publication Publication Date Title
US10508712B2 (en) Friction transmission belt and manufacturing method thereof
JP5997712B2 (ja) 摩擦伝動ベルト
JP6553687B2 (ja) Ｖリブドベルト及びその用途
JP6055430B2 (ja) 伝動用ベルト
WO2013133378A1 (fr) Courroie d'entraînement par friction et son procédé de fabrication
JP6674061B2 (ja) Ｖリブドベルト及びその用途
JP6291470B2 (ja) 摩擦伝動ベルト及びその製造方法
US20190390047A1 (en) Transmission Belt
JP5926543B2 (ja) 摩擦伝動ベルト及びその製造方法
JP6175113B2 (ja) 摩擦伝動ベルト
JP2018076968A (ja) 摩擦伝動ベルト
WO2017110784A1 (fr) Courroie d'entraînement par frottement
JPWO2009150803A1 (ja) 摩擦伝動ベルト及びそれを用いたベルト伝動装置
WO2016068337A1 (fr) Courroie de transmission par frottement et son procédé de fabrication
JP6748002B2 (ja) 摩擦伝動ベルト及びその製造方法
JP2017116100A (ja) 摩擦伝動ベルト
WO2018043355A1 (fr) Courroie à nervures en v et son utilisation
WO2019208740A1 (fr) Courroie à nervures en v et son application
WO2021060532A1 (fr) Composition de caoutchouc et courroie de transmission à friction

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15854588

Country of ref document: EP

Kind code of ref document: A1

REEP Request for entry into the european phase

Ref document number: 2015854588

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 15523125

Country of ref document: US

NENP Non-entry into the national phase

Ref country code: DE