WO2016006624A1 - Film anti-condensation, et porte pour vitrine isolante contre le froid - Google Patents

Film anti-condensation, et porte pour vitrine isolante contre le froid Download PDF

Info

Publication number
WO2016006624A1
WO2016006624A1 PCT/JP2015/069605 JP2015069605W WO2016006624A1 WO 2016006624 A1 WO2016006624 A1 WO 2016006624A1 JP 2015069605 W JP2015069605 W JP 2015069605W WO 2016006624 A1 WO2016006624 A1 WO 2016006624A1
Authority
WO
WIPO (PCT)
Prior art keywords
water
film
test
antifogging
fogging
Prior art date
Application number
PCT/JP2015/069605
Other languages
English (en)
Japanese (ja)
Inventor
森　勇介
阿部　啓介
米田　貴重
Original Assignee
旭硝子株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 旭硝子株式会社 filed Critical 旭硝子株式会社
Publication of WO2016006624A1 publication Critical patent/WO2016006624A1/fr

Abstract

L'invention fournit un film anti-condensation permettant de conférer des propriétés anti-condensation à divers articles, et se révèle à la fois excellent en termes d'absorption d'eau et de résistance au pelage. Ce film anti-condensation est équipé : d'un film de résine ; et sur une des faces principales du film de résine, d'une couche d'absorption d'eau dont la durée de résistance à la condensation (T35) est supérieure ou égale à 200 secondes, lors d'un essai à la vapeur à 35°C mesurée à l'aide du procédé suivant. (Procédé de mesure de durée de résistance à la condensation (T35)) Un film PET (polyéthylène téréphtalate) de 100µm d'épaisseur possédant une couche d'absorption d'eau sur une de ses faces principales, est collé couche d'absorption d'eau apparente sur une des faces principales d'un corps de base en verre sodocalcique, et mis au repos pendant une heure sous un environnement à 23°C et à 50% d'humidité relative ; puis, une région carrée de 70mm×70mm est établie à la surface de la couche d'absorption d'eau, dans un état de fermeture hermétique tel que la distance depuis la surface d'eau chaude d'un bain d'eau chaude à 35°C est de 85mm, et la durée de résistance à la condensation (T35) [en secondes] depuis le début du repos jusqu'à ce qu'une condensation ou déformation due à une pellicule d'eau soit perceptible à l'œil, est ainsi mesurée.
PCT/JP2015/069605 2014-07-08 2015-07-08 Film anti-condensation, et porte pour vitrine isolante contre le froid WO2016006624A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014140911 2014-07-08
JP2014-140911 2014-07-08

Publications (1)

Publication Number Publication Date
WO2016006624A1 true WO2016006624A1 (fr) 2016-01-14

Family

ID=55064253

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2015/069605 WO2016006624A1 (fr) 2014-07-08 2015-07-08 Film anti-condensation, et porte pour vitrine isolante contre le froid

Country Status (1)

Country Link
WO (1) WO2016006624A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011004873A1 (fr) * 2009-07-10 2011-01-13 旭硝子株式会社 Article anti-buée, son procédé de production, et trousse de revêtement pour former un film anti-buée
JP2012086506A (ja) * 2010-10-22 2012-05-10 Konica Minolta Holdings Inc 防曇フィルム及び防曇ガラス
WO2013089165A1 (fr) * 2011-12-15 2013-06-20 旭硝子株式会社 Article anticondensation, procédé de fabrication de cet article, composition prévue pour la formation d'une couche absorbant l'eau, et article destiné à des dispositifs de transport

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011004873A1 (fr) * 2009-07-10 2011-01-13 旭硝子株式会社 Article anti-buée, son procédé de production, et trousse de revêtement pour former un film anti-buée
JP2012086506A (ja) * 2010-10-22 2012-05-10 Konica Minolta Holdings Inc 防曇フィルム及び防曇ガラス
WO2013089165A1 (fr) * 2011-12-15 2013-06-20 旭硝子株式会社 Article anticondensation, procédé de fabrication de cet article, composition prévue pour la formation d'une couche absorbant l'eau, et article destiné à des dispositifs de transport

Similar Documents

Publication Publication Date Title
JP6194892B2 (ja) 車両用フロントガラス
JP6123680B2 (ja) 防曇性物品およびその製造方法、吸水層形成用組成物ならびに輸送機器用物品
JPWO2015008672A1 (ja) 防曇性物品
CN107099215B (zh) 用于防雾涂层的组合物及包含防雾涂层的涂覆膜
JP6520922B2 (ja) 防曇性物品及びその製造方法
WO2011146188A1 (fr) Film et/ou stratifié traité en surface
WO2011004873A1 (fr) Article anti-buée, son procédé de production, et trousse de revêtement pour former un film anti-buée
JP2009529436A (ja) 安定化された赤外線吸収剤を含むポリマーフィルム
WO2012161330A1 (fr) Article antibuée et son procédé de production
JP2014001106A (ja) 防曇性ガラス物品その製造方法および輸送機器用物品
JP6443443B2 (ja) 防曇剤組成物並びに防曇性物品及びその製造方法
JP2016017013A (ja) 防曇性ガラス物品
JP6673361B2 (ja) 防曇性物品および自動車用ガラス
JP4359356B2 (ja) 防汚性赤外線遮蔽フィルム及びその製造方法
JP5307352B2 (ja) 軟質フィルム
JP2013244691A (ja) 防曇性物品
WO2016006624A1 (fr) Film anti-condensation, et porte pour vitrine isolante contre le froid
JP2001316626A (ja) コーティング剤
US20150152269A1 (en) Antifog sheet
WO2013183441A1 (fr) Article anticondensation
JP4736387B2 (ja) 耐擦傷性及び反射防止性を有する積層体
JP2012121760A (ja) 吸水性被膜を有する熱線反射ガラス
US20170015861A1 (en) Antifogging agent composition, antifogging article, and manufacturing method thereof
CN116023839A (zh) 涂层的制造方法、叠层结构、及涂层组成物
WO2015174373A1 (fr) Article antibuée et article pour machine de transport

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15819155

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15819155

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP