WO2015175726A1 - Production of substantially spherical metal powers - Google Patents
Production of substantially spherical metal powers Download PDFInfo
- Publication number
- WO2015175726A1 WO2015175726A1 PCT/US2015/030669 US2015030669W WO2015175726A1 WO 2015175726 A1 WO2015175726 A1 WO 2015175726A1 US 2015030669 W US2015030669 W US 2015030669W WO 2015175726 A1 WO2015175726 A1 WO 2015175726A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- granules
- sintering
- titanium
- powder
- sintered
- Prior art date
Abstract
Description
Claims