WO2015108630A1

WO2015108630A1 - Vacuum interrupter with arc-resistant center shield

Info

Publication number: WO2015108630A1
Application number: PCT/US2014/068986
Authority: WO
Inventors: Louis Grant CAMPBELL; Stephen David Mayo
Original assignee: Eaton Corporation
Priority date: 2014-01-20
Filing date: 2014-12-08
Publication date: 2015-07-23
Also published as: ES2947223T3; CN105917434B; EP3097576A1; US9368301B2; JP7198571B2; JP2017508072A; CN105917434A; EP3097576B1; KR102320715B1; US20150206677A1; KR20160111926A

Abstract

The disclosed concept pertains to alloy compositions, methods and arc-resistant shields composed of the alloy compositions. The arc-resistant shields are positioned in vacuum interrupter chambers and demonstrate resistance to arc damage and ability to hold off high voltages after arcing, while providing a lower cost alternative to traditional alloy compositions used for producing arc-resistant shields. In certain embodiments, the alloy compositions include copper and/or an element chemically compatible to copper and another component, such as but not limited to, iron, stainless steel, niobium, molybdenum, vanadium, tungsten carbide, chromium carbide, vanadium carbide and chromium, and alloys and mixtures thereof.

Description

VACUUM INTERRUPTER WITH ARC-RESISTANT CENTER SHIELD

CROSS-REFERENCE TO RELATED APPLICATION

This application claims priority from and claims the benefit of L S.

Patent Application Serial No. 14/158,928, filed January 20, 2014, which is incorporated by reference herein.

BACKGROUND

Field

The disclosed concept pertains generally to vacuum circuit breakers and other types of vacuum switchgear and related components, such as vacuum interrupters and arc-resistant shields. In particular, the disclosed concept pertains to new alloy compositions for use in constructing internal arc-resistant shields employed in the vacuum interrupter chamber. Background Info ination

Vacuum interrupters are typically used to interrupt high voltage AC currents. The interrupters include a generally cylindrical vacuum envelope

surrounding a pair of coaxial ly aligned separable contact assemblies having opposing contact surfaces. The contact surfaces abut one another in a closed circuit position and are separated to open the circuit. Each electrode assembly is connected to a current carrying terminal post extending outside the vacuum envelope and connecting to an AC circuit.

An arc is typically formed between the contact, surfaces when the contacts are moved apart, to the open circuit position. The arcing continues until the current is interrupted. Metal from the contacts that is vaporized by the arc forms a neutral plasma durins arcinu and condenses back onto the contacts and also onto a vapor shield placed between the contact assemblies and the vacuum envelope after the current is extinguished.

The vacuum en velope of the interrupter typical ly incl udes a ceramic tubular insulating casing with a metal end cap or seal covering each end. The electrodes of the vacuum interrupter extend through the end caps into the vacuum envelope. At least one of the end caps is ri idly connected to the electrode and must be able to withstand relatively high dynamic forces during operation of the

interrupter.

Vacuum interrupters are key components of vacuum-type switchgear. It is typical for interrupters for vacuum-type circuit breakers using transverse magnetic field contacts to include the vapor shield, e.g., internal arc shield or arc- resistant shield, that is resistant to heavy arcing to restrict the outward dissemination of the arc and preserve the high voltage withstand of the interrupter after breaking the fault current.

It is customary for the shield to be constructed of copper, stainless steel, copper-chromium alloy or a combination thereof. In some cases, the shield may be constructed of one material in the arcing area and a second material may be used for the remainder of the shield. The copper-chromi am alloy material may be used for the highest fault current ratings because of its resistance to arc damage and its abi lit to hold off high voltages after the arcing has occurred. It is typical for the copper- chromium alloy to include about 10 to 25% by weight chromium and the balance copper.

It is an object of the disclosed concept to develop new alloy compositions for use in constructing arc-resistant shields for interna! use in vacuum interrupters wherein the compositions are other than the conventional pure chromium and copper alloys, it is a further object to develop new alloy compositions wherein the amount of chromium is present in a reduced amount as compared to known copper-chromium compositions. I still a further object, chromium is absent from the compositions. Chromium is expensive to obtain and therefore, reducing or

eliminating the presence of chromium will provide a lower cost alternative to the conventional materials used in constructing arc-resistant shields. Further, it is believed employing materials or elements other than pure chromium and copper can result in alloy compositions which exhibit superior performance in arc-resistant SUMMARY

These needs and others are met by embodiments of the disclosed concept, which provide compositions and are-resistant shields constructed of these compositions.

In an aspect, the disclosed concept provides an alloy composition for constructing an arc- resistant shield positioned in a vacuum interrupter chamber. The allo composition includes a melting range of I00°C or greater between a solidiis temperature and a liquidus temperature, the solidus temperature of 900X or greater, a substantially multi-phase microstructure, and an ability to fbnn a substantially smooth surface when rapidly cooled following arc melting.

The composition can include a first component and a second component. The first component may include copper or a chemically compatible element to copper. The second component may be selected from the group consisting of iron, stainless steel, niobium, molybdenum, vanadium, chromium alloy, carbide, and alloys and mixtures thereof. In certain embodiments, the composition includes the copper component and ferrochrome. The ferrochrome may constitute about 70 weight percent chromium and about 30 weight percent iron.

The first component may be pure copper or a copper alloy, such as but not limited to cupronickel, copper-tin, nickel-copper, silver bearing copper, tin bronze and aluminum bronze. The first component can also include nickel, silver, gold, palladium, platinum, cobalt, rhodium, iridium, ruthenium, and alloys and mixtures thereof

The carbide may be selected from the group consisting of tungsten carbide, chromium carbide, vanadium carbide, molybdenum carbide, niobium carbide, tantalum carbide, titanium carbide, zirconium carbide, hafnium carbide, boron carbide, and silicon carbide.

In another aspect, the disclosed concept provides an arc -resistant shield composed of an alloy material including a first component and a. second component. The first component may include copper or a chemically compatible element to copper. The second component may be selected from the group consisting of iron, stainless steel, niobium, molybdenum, vanadium, chromium alloy, carbide, and their alloys and mixtures. The arc-resistant shield is an internal component of a vacuum interrupter.

In certain embodiments, the first component may include pure copper or copper alloy. In other embodiments, the first component may include nickel, silver, gold, palladium, platinum, cobalt, rhodium, iridium, ruthenium, and alloys and mixtures thereof.

In still another aspect, the disclosed concept provides a method for preparing an arc -resistant shield located in a vacuum interrupter. The method inc ludes obtaining a first component selected from the group consisting of pure copper, copper alloy, a chemically compatible element to copper and mixtures thereof; obtaining a second component selected from the group consisting of iron, stainless steel, niobium, molybdenum, vanadium, chromium alloy, carbide, and their alioys and mixtures; combining the first and second components to form a mixture, shaping the mixture into a selected shape; and machining to form the arc-resistant shield. The chromium alloy may be ierrochrome and the ferrochrome may be in the form of a pre-alloyed chromium-iron powder. Further, the forming of the mixture may be conducted by a technique selected from extruding, molding and combinations thereof.

BRIEF DESCRIPTION OF DRAWINGS

A full understanding of the disclosed concept can be gained from the following description of the preferred embodiments when read in conjunction with the accompanying drawing in which:

FIG. 1 is a sectional view of a vacuum interrupter including an arc- resistant shield, in accordance with the disclosed concept,

DET AILED DESCRIPTION OF PREFERRED EMBODIMEN TS

The disclosed concept includes alloy compositions, methods of prepar ing the compositions and methods of employing the compositions to prepare arc-resistant shields for use i vacuum interrupters. Vacuum interrupters are key internal components of vacuum sw.itch.gear, such as vacuum circuit breakers. The arc- resistant shields are traditionally constructed of copper, stainless steel or copper- chromium alloy, hi particular, copper-chromium alloys are known materials for use with highest fault current ratings because of their resistance to heavy arcing and their ability to preserve the high voltage withstand of the interrupter after arcing has occurred. Preferred copper-chromium alloys include from 10 to 25 weight percent chromium and the balance copper based on total weight of the alloy composition. One disadvantage of known copper-chromium alloys is the high cost associated with them, hi particular, pure chromium is an expensive element and therefore, its presence in an alloy composition can result in an expensive material. The cost of a material may be lowered by reducing the amount of chromium or producing the material in the absence of chromium. Thus, it is an object of this disclosed concept to provide suitable alloy compositions that are useful in forming arc-resistant shields. The alloy compositions should be capable of demonstrating resistance to arc damage and holding off high voltages after arcing, while providing lower cost alternati ves to traditional alloy compositions. FIG. 1 shows a vacuum interrupter 10 having a cylindrical insulating tube 12 which, in combination with end seals 51 and 52, forms a vacuum envelope 50, The insulating tube 12 supports a vapor shield 24 by means of a flange 25. An arc resistant vapor shield 24 surrounds a first electrode assembly 20 and a second electrode assembly 22 to prevent metal vapors from collecting on the insulating tube 12 and to prevent the arc from hitting the insulating tube 12. The insulating tube 12 is preferably made of a ceramic material such as alumina, zi.rco.nta or other oxide ceramics, but mav also be alass. The first and second electrode assemblies 20 and 22. respectively, are longitudinally aligned within the vacuum envelope 50. The first electrode assembly 20 includes a bellows 28, a first electrode contact 30, a first terminal post 3 1, and a first vapor shield 32, The second electrode assembly 22 includes a second electrode contact 34, a second terminal post 35, and a second vapor shield 36. While the vacuum envelope 50 shown in FIG. 1 is part of the vacuum interrupter 10, it is to be understood that the term "vacuum envelope" as used herein is intended to include any sealed component having a ceramic to metal seal which forms a substantially gas-tight enclosure. Such sealed enclosures may be maintained at sub-atmospheric, atmospheric or super-atmospheric pressures during operation. The first and second electrode assemblies 20 and 22, respectively, are axially movable with respect to each other for opening and closing the AC circuit. The bellows 28 mounted on the first electrode assembly 20 seals the interior of the vacuum envelope formed by the insulating tube 1.2 and end seals 51 and 52, while pennitting movement of the first electrode assembly 20 from a closed position as shown in FIG. 1 to an open circuit position (not shown). The first electrode contact 30 is connected to the generally cylindrical first terminal post 31 which extends out of the vacuum envelope 50 through a hole in the end seal 51. The first vapor shield 32 is mounted on the first terminal post 31 in order to keep metal vapors off the bellows 28. Likewise, the second electrode contact 34 is connected to the generally cylindrical second terminal post 35 which extends through the end seal 52. The second vapor shield 36 is mounted on the second terminal post 35 to protect the insulating tube 12 from metal vapors. The second terminal post 35 is rigidly and hermetically sealed to the end seal 52 by means such as, but not l imited to, welding or brazing. Preferably, said first and second electrode contacts 30 and 34, respectively, are composed of an alloy composition., e.g., copper-chromium.

In accordance with certain embodiments of the disclosed concept, suitable alloy compositions for producing an arc-resistant shield demonstrate one or more of the following characteristics or properties: (i) melting range or interval wherein solid and liquid phases simultaneously exist, e.g., a slurry, and wherein the melting range or interval is equal to or greater than 100°C between solidus and liquidus temperatures;

(ii) solidus temperature equal to or greater than 900°€;

(in) .substantially multi-phase microstructure with at least two phases; and

(iv) ability to form a substantially smooth surface when rapidly cooled a tie!' arc melting.

The disclosed concept relates to an alloy composition having a first component and a second component. In certain embodiments, the first component is copper, including pure copper, copper alloy or mixtures thereof. In certain embodiments, instead of or in addition to, the first component ma include any compatible element. For example, an element that is chemically compatible to copper. Thai is, an element that may serve as a replacement for copper. Suitable compatible elements include but are not limited to nickel, silver, gold, palladium, platinum, cobalt, rhodium, iridium, ruthenium, and alloys and mixtures thereof. The second component may include iron, stainless steel, niobium, molybdenum, vanadium, chromium, carbide and alloys and mixtures thereof. The carbide may include tungsten carbide, chromium carbide, vanadium carbide, molybdenum carbide, niobium carbide, tantalum carbide, titanium carbide, zirconium carbide, hafnium carbide, boron carbide and silicon carbide, in certain embodiments, the second component is chromium alloy.

Non-limiting examples of alloy compositions that are suitable for use in the disclosed concept include a copper componen with another component such as, iron, stainless steel, niobium, molybdenum, vanadium, chromium, their alloys or mixtures, and carbide. In certain embodiments of the disclosed concept, the alloy compositions include copper-iron, copper-stainless steel, copper-niobium, copper- molybdenum, copper- vanadium, copper-chromium alloy, copper-ferrochrome, copper-ferrovanadium, copper-ferromobium, and copper-X-carbide wherein X represents tungsten, chromium, vanadium, tantalum, molybdenum, niobium, silicon, boron, or any common carbide former. Further, in certain embodiments, the copper alloy can include euproniekel, copper-tin, nickel-copper, silver bearing copper, tin bronze and aluminum bronze.

The disclosed concept relates to alloy compositions for producing the arc-resistant shield that incl ude components other than pure chromium since the use of pure chromium can result in an expensive material. In certain embodim ents, the compositions include copper, e.g., in the form of pure copper and/or copper alloy, and a chromium alloy wherein the chromium alloy is ferrochrorne. The amount of each of these components can vary. The ferrochrorne ma constitute from about 5 to about 60 weight percent based on total weight of the composition. The copper may c onstitute the balance. The ferrochrorne component is a chromium-iron alloy wherei the amount of each of the chromium and iron can van'. The chromium may constitute about 70 weight percent and the iron may constitute about 30 weight percent based on total weight of the ferrochrome component.

In general, the alloy compositions of the disclosed concept are subjected to one or more of known powder metallurgy, extrusion, forging and casting processes in order to form an arc-resistant shield. Traditional powder metallurgy techniques include but are not limited to pressing and sintering, extrusion, e.g., binder-assisted extrusion, powder injection molding and powder forging. Extrusion includes hot or cold extrusion and forging includes hot forging or cold forming.

Casting includes vacuum induction melting, sand casting, and other conventional casting methods.

in accordance with certain embodiments of the disclosed concept, each of the copper and ferrochrome components may be in dry form, e.g., powder. In these embodiments, the composition is prepared by mixing together copper powder and ferrochrome powder. The ferrochrome powder constitutes a pre-alloyed chromium- iron powder. The amounts of copper and ferrochrome, and the amounts of chromium and iron can be within the weight ranges specified above. The copper and

ferrochrome powders may be atomized, chemically reduced, electrolytically formed, ground or formed by any other known powder production process. The powder morphology may be spherical, acicular, or irregular. The copper-ferrochrome powder mixture is pressed to shape and sintered. The shaping and sintering can be conducted in accordance with conventional shaping and sintering apparatus and processes known in the art. The shaped, sintered article forms an arc -resistant shield. Optionally, machining of the shaped, sintered artic le may be necessary to finalize the form of t he shield.

In a preferred method of fabricating the arc-resistant shield for the vacuum circuit interrupter, the steps of fabricating incl ude pouring a copper- ferrochrome blend into a die cavity, tapping to level powder, applying a pressure of about 80,000 to about 150,000 psi to form a shield, sintering the shield in a reducing or vacuum furnace at a temperature of about 950° C to about 1 1.00° C for about 0.5 to about 10 hours, and machining and forming a hollow shield.

in preferred method, the steps include initially prefabricating a cylindrical shel l container or tube container of copper, or copper alloy, pouring copper-ferrochrome powder, leveling by tapping or pressing, outgassing the container containing the powder at a temperature of about 125° C to about 400° C, sealing the container by welding a top cover of the container vacuum weld or welding the top; evacuating through a port and seal, hoi extruding the container at a temperature from about 400° C to about 900° C, removing the container and machining the shields. I another form of the method, the container is hot isostatieaiSy pressed in the range of about 700° C to about 1080° C between about 10,000 psi to about 30,000 psi for about 0.25 hours to about. 6 hours.

Various processes for the fabrication of the shield include the following:

Process 1

1. Pour a copper-ferroclirome blend into a die cavity and tap t level powder;

2. Apply a pressure of about 80,000 to about 150,000 psi to fabricate a shield pre-form;

3. Sinter in a reducing or vacuum furnace in a range of about 950° C to about 1 100° C for about 0.5 to about 10 hours; and

4. Machine the shield by boring out the center.

Process #2

1. Same as Process #1 except that a core is used in the die during pressing to form a hollow tube pre-form;

2. Sinter in a reducing or vacuum furnace in a range of about 950° C to about 1 100° C for about 0.5 to about 10 ^'hours; and

3. M achme the shield.

Process #3

1 . Same as Processes #1 and #2 except that a rubber bag is used as the die and a cold isostatic press is used to apply isostatic pressure in a range of about 60,000 psi to about 120,000 psi;

2. Sinter in a reducing or vacuum furnace in a range of about 950° C to about 1 100° C for about 0.5 to about 10 hours; and Machine the shield.

Process #4

1. Place a prefabricated copper or copper-ferrochrome pipe;

2. Plasma, laser deposit, thermal spray, or cold spray a layer of copper-ferrochrome on the internal diameter of the pipe; and

3. Machine the shield.

Process #5

1. Place a sacrificial or re-usable .mandrel;

2. Plasma, laser deposit, thermal spray, or cold spray a layer of copper-ferrochrome on the outside diameter of the mandrel;

4. Remove the mandrel by machiniiig (or chemically if sacrificial), or withdraw the mandrel from the deposited material if re-usable; and

3. Machine the shield.

Process #6

1. Form a slurry of copper powder, ferrochrome powder; and a suitable liquid carrying agent (binder) that substantially solidifies when dried or eentrifugaiiy separated;

2. Pour the slurry into a hollow pipe;

3. Spin the pipe to force the slurry against the inner diameter of the pipe;

4. Dry the spun mixture;

5. Remove the solidified mixture from the pipe;

7. Sinter the eentrifugaiiy formed cylindrical powder mixture; and

8. Machine the shield from the cylindrical sintered part.

Process #7

1. Melt an appropriate mixture of copper and ferrochrome using vacuum induction melt or other technique;

2. Pour the melt into a mold with a central core; 3. Break out the mold to remove the casting; and

4. Machine the casting to form a shield.

Process #S

1. Melt an appropriate mixture of copper and ferrochrome using vacuum induction me!t or other technique;

2. Pour the melt into a mold with a centrifugal caster and cast the shield; and

3. Machine the shield.

Process #9

1. Prepare a solid or cylindrical blank of copper and ferrochrome by powder metallurgy sintering, powder metallurgy infiltration, or casting;

2. Heat the blank to a temperature at which it may he extruded; 3. Extrude the blank into a cylindrical shape, e.g., using an extrusion press; and

4. Machine the shield from the extruded cylindrical shape, if necessary. Process #10

1. Mix dry copper and ferrochrome powder with a suitable plastic binder system;

2. Heat the powder/binder mixture to a temperature at which it may be molded;

3 , Extrude or powder injection mold the powder/hinder mixture into a cylindrical shape;

4. Remove the plastic binder system by solvent process, thermal process, or a combination thereof, such that the powder remains in its formed cylindrical shape;

5. Sinter the cylindrical shape; and

6. Machine the shield, if necessary. EXAMPLES

Example 1,

In one experiment, arc resistant shields were made by mixing 36 wt % high carbon ferrochrome powder and 64 wt% copper powder, pressing in a cylindrical die, sintering the part, and machining the final shield shape. The composition of the high carbon feirochrome powder was 67-71 wt% chromium. 8-9.5% carbon, with the balance iron. The high carbon ferrochrome powder was ground to a size of -100 mesh. The copper powder was water atomized pure copper, at a size of «140 mesh. Pressing of the parts was performed with a dual-action powder compaction press. The tooling elements used to press the cylindrical parts consisted of a holl ow cylindric al upper punch, hollow cylindrical lower punch, hollow cylindrical die body, and a solid cylindrical core rod. Powder was fed into the cylindrical cavity using an automatic powder shoe. Compaction was performed at pressures of 45,000 to 1 16,000 psi. Parts were then vacimm sintered at 950 to 1 50°C for 6 hours and machined on a lathe to final shape.

B mple 2

In another experiment, arc resistant shields were made by mixing 60 wt % high carbon ierrochrome powder and 40 wt% copper powder, pressing in a cylindrical die, sintering the part, and machining the final shield shape. The composition of the high carbon ferrochrome powder was 67-71 wt% chromium, 8- 9,5% carbon, with the balance iron. The high carbon ferrochrome powder was ground to a size of -100 mesh. The copper powder was water atomized pure copper, at a size of -140 mesh . Pressing of the parts was performed with a dual -ac tion powder compaction press. The tooling elements used to press the cylindrical parts consisted of a hollow cylindrical upper punch, hollow cylindrical lower punch, hollow cylindrical die body, and a solid cylindrical core rod. Powder was fed into the cylindrical cavity using an automatic powder shoe. Compaction was performed at pressures of 60,000 to 160,000 psi. Parts were then vacuum sintered at 950 to 1050°C for 6 hours, and machined on a lathe to final shape. in another experiment, are resistant shields were made by mixing 36 wt % lo carbon ferroehrome powder and 64 wt% copper powder, pressing in a cylindrical die, sintering the part, and machining the final shield shape. The composition of the high carbon ferroehrome powder was 70 wt% chromium with the balance iron. The high carbon ferroehrome powder was ground to a size of -80 mesh. The copper powder was water atomized pure copper, at a size of -140 mesh. Pressing of the parts was performed with a dual-action powder compaction press. The tooling elements used to press the cylindrical parts consisted of a hollow cylindrical upper punch, hollow cylindrical lower punch, hollow cylindrical die body, and a solid cylindrical core rod. Powder was fed into the cylindrical ca v ity using an automatic powde shoe. Compaction was performed at pressures of 43,000 to 1 19,000 psi. Parts were then vacuum sintered at 950 to 1050°C for 6 hours, and machined on a lathe to fin l shape.

In another experiment, arc resistant shields were made by mixing 60 wt % low carbon ferroehrome powder and 40 wt% copper powder, pressing in a cylindrical die, sintering the part, and machining the final shield shape. The composition of the high carbon ferroehrome powder was 70 wt% chromium with the balance iron. The high carbon ferroehrome powder was ground to a size of -80 mesh. The copper powder was water atomized pure copper, at a size of -140 mesh. Pressing of the parts was performed with a dual-action powder compaction press. The tooling elements used to press the cylindrical parts consisted of a hollow cylindrical upper punch, hollow cylindrical lower punch, hollow cylindrical die body, and a solid cylindrical core rod. Powder was fed into the cylindrical cavity using an automatic powder shoe. Compaction was performed at pressures of 50,000 to 1 12,000 psi. Parts were then vacuum sintered at 950 to 1050°C for 6 hours, and machined on a lathe to final shape.

While example systems, methods, and the like have been illustrated by describing examples, and while the examples have been described in considerable detail, it is not the intention of the applicants to restrict or in any way limit the scope of the appended claims to such detail. It is, of course, not possible to describe every conceivable combination of components or methodologies for purposes of describing the systems, methods, and so on described herein. Therefore, the disclosed concept is not limited to the specific details, the representative apparatus, and illustrative examples shown and described. Thus, this application is intended to embrace alieraiions. modi fications, and variations that fall within the scope of the appended claims.

Claims

What is Claimed Is:

! . An alloy composition for constructing an arc-resistant shield (24) positioned in a vacuum interrupter (10) chamber, the ailoy composition comprising:

a melting range of 100°€ or greater between a soii us temperature and a liquidus temperature;

the soiidus temperature of 900°C or greater:

a substantially multi-phase microstruciure; and

an abilit to form a. substantially smooth surface when rapidly cooled following arc -melting.

2. The composition of claim 1 , wherein the composition comprises two components, comprising:

a first component; and

a second component selected from the group consisting of iron , stainless steel, niobium, molybdenum, vanadium, chromium ailoy, carbide, and alloys and mixtures thereof.

3. The composition of claim 2, wherein the first component is selected from the group consisting of pure copper, copper ailoy, a chemically compatible element to copper, and mixtures thereof,

4. The composition of claim 3, wherein the copper alloy is cupronickel, copper-tin, nickel-copper, silver bearing copper, tin bronze, and aluminum bronze,

5. The composition of claim 2, wherein the carbide is selected from the group consisting of tungsten carbide, chromium carbide, vanadium carbide, molybdenum carbide, niobium carbide, tantalum carbide, titanium carbide, zirconium carbide, hafnium carbide, boron carbide, and silicon carbide.

6 The composition of claim 2, wherein the chromium alloy is ferrochrome.

7. The composition of claim 6, wherein the ferrochrome constitutes from about 5 to about 60 weight percent based on total weight of the composition.

8. The composition of claim 6„ wherem the feiTochrome is in a form of pre- alloyed powder.

9. The composition of claim 6, wherein the ferrochrome constitutes from about 70 weight percent chromium and about 30 weight percent iron based on total weight of the ferrochrome component.

10. The composition of claim 3. wherein the chemically compatible element is selected from the group consisting of nickel, silver, gold, palladium, platinum, cobalt, rhodium, iridium,, ruthenium,, and alloys and mixtures thereof

1 1. An arc-resistant shield (24) composed of an al loy material comprising;

a first component selected from t e group consisting of pure copper, copper alloy, a chemically compatible element t copper, and mixtures thereof; and

a second component; selected from the group consisting of iron , stainless steel, niobium, molybdenum, vanadium, chromium alloy, carbide, and alloys and mixtures thereof,

wherein, the arc-resistant shield (24) is an internal component of a vacuum interrupter (10).

12. A method for preparing an arc- esistant shield (24) located in a vacuum switchgear chamber, the method comprising.: obtaining a first component selected from the grou consisting of pure copper, copper alloy, a chemically compatible element to copper, and mixtures thereof;

obtaining a second component selected from the group consisting of iron, stainless steel, niobium, molybdenum, vanadi um, chromi um alloy, carbide, aad alloys and mixtures thereof;

combining the first and. second components to form a mixture; shaping the mixture into a selected shape; and machining to form the arc-resistant shield (24).

13. The method of claim 12, wherein t he chromium allo is ferrochrome.

14. The method of claim 13, wherein the ferrochrome is in a form of pre- alioyed chromium-iron powder.

15. The method of claim 12, wherein the forming of the mixture is conducted by a technique selected from the group consisting of extruding, molding and

combinations thereof.