WO2014119311A1 - Procédé de fabrication de condensateur à électrolyte et condensateur à électrolyte - Google Patents
Procédé de fabrication de condensateur à électrolyte et condensateur à électrolyte Download PDFInfo
- Publication number
- WO2014119311A1 WO2014119311A1 PCT/JP2014/000474 JP2014000474W WO2014119311A1 WO 2014119311 A1 WO2014119311 A1 WO 2014119311A1 JP 2014000474 W JP2014000474 W JP 2014000474W WO 2014119311 A1 WO2014119311 A1 WO 2014119311A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- conductive polymer
- liquid composition
- capacitor element
- electrolytic capacitor
- aqueous solvent
- Prior art date
Abstract
La présente invention porte sur un procédé de fabrication d'un condensateur à électrolyte comprenant une étape de préparation d'un corps d'électrode positive comportant un film diélectrique, une étape de préparation d'une première composition liquide contenant un premier polymère conducteur, une étape d'imprégnation du corps d'électrode positive avec la première composition liquide, puis de séchage de celui-ci afin de former un élément condensateur qui comporte une couche d'électrolyte solide disposée sur la surface du film diélectrique et contenant le premier polymère conducteur, une étape de préparation d'une seconde composition liquide qui contient un solvant non aqueux et un second polymère conducteur dissous dans le solvant non aqueux, une étape d'imprégnation de l'élément condensateur avec la seconde composition, et une étape de logement de l'élément condensateur imprégné avec la seconde composition liquide dans un boîtier extérieur.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2014559583A JP6326633B2 (ja) | 2013-01-31 | 2014-01-30 | 電解コンデンサの製造方法および電解コンデンサ |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2013-017639 | 2013-01-31 | ||
JP2013017639 | 2013-01-31 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2014119311A1 true WO2014119311A1 (fr) | 2014-08-07 |
Family
ID=51262026
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2014/000474 WO2014119311A1 (fr) | 2013-01-31 | 2014-01-30 | Procédé de fabrication de condensateur à électrolyte et condensateur à électrolyte |
Country Status (2)
Country | Link |
---|---|
JP (1) | JP6326633B2 (fr) |
WO (1) | WO2014119311A1 (fr) |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN114730666A (zh) * | 2019-11-29 | 2022-07-08 | 松下知识产权经营株式会社 | 电解电容器用阴极箔、电解电容器、及它们的制造方法 |
Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH05144677A (ja) * | 1991-11-18 | 1993-06-11 | Rubycon Corp | アルミニウム電解コンデンサ |
JPH118161A (ja) * | 1997-06-18 | 1999-01-12 | Nitto Denko Corp | 固体電解コンデンサ及びその製造方法 |
-
2014
- 2014-01-30 WO PCT/JP2014/000474 patent/WO2014119311A1/fr active Application Filing
- 2014-01-30 JP JP2014559583A patent/JP6326633B2/ja active Active
Patent Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH05144677A (ja) * | 1991-11-18 | 1993-06-11 | Rubycon Corp | アルミニウム電解コンデンサ |
JPH118161A (ja) * | 1997-06-18 | 1999-01-12 | Nitto Denko Corp | 固体電解コンデンサ及びその製造方法 |
Also Published As
Publication number | Publication date |
---|---|
JPWO2014119311A1 (ja) | 2017-01-26 |
JP6326633B2 (ja) | 2018-05-23 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP7033705B2 (ja) | 電解コンデンサの製造方法 | |
JP6589142B2 (ja) | 電解コンデンサの製造方法 | |
US10121599B2 (en) | Method for producing electrolytic capacitor | |
WO2017163725A1 (fr) | Condensateur électrolytique et son procédé de fabrication | |
JP6803519B2 (ja) | 電解コンデンサの製造方法 | |
US10121598B2 (en) | Method for producing electrolytic capacitor | |
JP2016082053A (ja) | 電解コンデンサ | |
JP2019110322A (ja) | 電解コンデンサの製造方法 | |
JP6497563B2 (ja) | 電解コンデンサの製造方法 | |
WO2016157693A1 (fr) | Condensateur électrolytique | |
JP6868848B2 (ja) | 電解コンデンサ | |
JP6326633B2 (ja) | 電解コンデンサの製造方法および電解コンデンサ | |
JP6604497B2 (ja) | 電解コンデンサの製造方法 | |
WO2014132632A1 (fr) | Condensateur électrolytique et son procédé de fabrication | |
JP2017175091A (ja) | 電解コンデンサおよびその製造方法 | |
JP7407371B2 (ja) | 電解コンデンサ | |
JP2023029570A (ja) | 電解コンデンサ |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 14745678 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 2014559583 Country of ref document: JP Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 14745678 Country of ref document: EP Kind code of ref document: A1 |