WO2014109824A1 - Dispositif médical pourvu d'un revêtement lubrifiant formant avec des composés hydrophiles un réseau d'interpénétration - Google Patents

Dispositif médical pourvu d'un revêtement lubrifiant formant avec des composés hydrophiles un réseau d'interpénétration Download PDF

Info

Publication number
WO2014109824A1
WO2014109824A1 PCT/US2013/069223 US2013069223W WO2014109824A1 WO 2014109824 A1 WO2014109824 A1 WO 2014109824A1 US 2013069223 W US2013069223 W US 2013069223W WO 2014109824 A1 WO2014109824 A1 WO 2014109824A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating
cross
polymer
hydrophilic
lubricious coating
Prior art date
Application number
PCT/US2013/069223
Other languages
English (en)
Inventor
Tung-Liang Lin
Jeong S. Lee
Original Assignee
Abbott Cardiovascular Systems Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US13/736,667 external-priority patent/US20130123664A1/en
Application filed by Abbott Cardiovascular Systems Inc. filed Critical Abbott Cardiovascular Systems Inc.
Priority to JP2015551672A priority Critical patent/JP2016503689A/ja
Priority to EP13793048.3A priority patent/EP2900290A1/fr
Publication of WO2014109824A1 publication Critical patent/WO2014109824A1/fr

Abstract

L'invention concerne, d'une part un dispositif médical garni d'un revêtement lubrifiant sur l'un au moins de ses segments, et d'autre part un procédé de revêtement d'un dispositif médical. Ce revêtement lubrifiant est constitué d'un réseau de composés hydrophiles à chaînes courtes et chaînes longues réticulés entre eux, en interpénétration avec un réseau de monomère ou de polymère multifonctionnel réticulé polymérisé. Le revêtement peut comporter un ou plusieurs agents qui confèrent au revêtement une meilleure adhésion sur le dispositif, ou qui confèrent au revêtement une hydratation plus rapide et/ou un meilleur pouvoir lubrifiant. En outre, le revêtement lubrifiant peut être pourvu d'un ou de plusieurs agents thérapeutiques ou de diagnostic, et, dans un mode de réalisation, dès l'hydratation du revêtement, l'agent s'élue relativement rapidement du revêtement lubrifiant en une émanation concentrée.
PCT/US2013/069223 2013-01-08 2013-11-08 Dispositif médical pourvu d'un revêtement lubrifiant formant avec des composés hydrophiles un réseau d'interpénétration WO2014109824A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2015551672A JP2016503689A (ja) 2013-01-08 2013-11-08 絡み合った網目構造中に親水性化合物を含む潤滑性被覆物を有する医療装置
EP13793048.3A EP2900290A1 (fr) 2013-01-08 2013-11-08 Dispositif médical pourvu d'un revêtement lubrifiant formant avec des composés hydrophiles un réseau d'interpénétration

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US13/736,667 US20130123664A1 (en) 2007-08-06 2013-01-08 Medical device having a lubricious coating with a hydrophilic compound in an interlocking network
US13/736,667 2013-01-08

Publications (1)

Publication Number Publication Date
WO2014109824A1 true WO2014109824A1 (fr) 2014-07-17

Family

ID=49622916

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2013/069223 WO2014109824A1 (fr) 2013-01-08 2013-11-08 Dispositif médical pourvu d'un revêtement lubrifiant formant avec des composés hydrophiles un réseau d'interpénétration

Country Status (3)

Country Link
EP (1) EP2900290A1 (fr)
JP (1) JP2016503689A (fr)
WO (1) WO2014109824A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016181245A1 (fr) * 2015-05-08 2016-11-17 Koninklijke Philips N.V. Revêtement hydrophile pour dispositifs intravasculaires
CN106730247A (zh) * 2017-02-04 2017-05-31 成都鼎信致远科技有限公司 一种血管介入导管
WO2020257830A1 (fr) * 2019-06-21 2020-12-24 Wismed Pl Sp Z.O.0. A Company Incorporated In Poland; Number Krs 0000751368 Fil-guide à élution médicamenteuse
CN114748700A (zh) * 2022-04-22 2022-07-15 华南理工大学 一种用于tpu包覆导丝的超亲水涂层及其制备方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5041570A (en) 1988-08-03 1991-08-20 Toyo Gosei Kogyo Co., Ltd. Photosensitive 4,4'-diazidostilbene derivative
US20070043160A1 (en) * 2003-04-17 2007-02-22 Medtronic Vascular, Inc. Coating for biomedical devices
US20090041923A1 (en) * 2007-08-06 2009-02-12 Abbott Cardiovascular Systems Inc. Medical device having a lubricious coating with a hydrophilic compound in an interlocking network

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7160515B2 (en) * 2000-12-05 2007-01-09 The Procter & Gamble Company Volatile material-containing article
US7534495B2 (en) * 2004-01-29 2009-05-19 Boston Scientific Scimed, Inc. Lubricious composition
JP5499321B2 (ja) * 2006-09-13 2014-05-21 ディーエスエム アイピー アセッツ ビー．ブイ． 医療コーティングのためのコーティング調合物

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5041570A (en) 1988-08-03 1991-08-20 Toyo Gosei Kogyo Co., Ltd. Photosensitive 4,4'-diazidostilbene derivative
US20070043160A1 (en) * 2003-04-17 2007-02-22 Medtronic Vascular, Inc. Coating for biomedical devices
US20090041923A1 (en) * 2007-08-06 2009-02-12 Abbott Cardiovascular Systems Inc. Medical device having a lubricious coating with a hydrophilic compound in an interlocking network

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016181245A1 (fr) * 2015-05-08 2016-11-17 Koninklijke Philips N.V. Revêtement hydrophile pour dispositifs intravasculaires
JP2018519006A (ja) * 2015-05-08 2018-07-19 コーニンクレッカ フィリップス エヌ ヴェＫｏｎｉｎｋｌｉｊｋｅ Ｐｈｉｌｉｐｓ Ｎ．Ｖ． 導管内デバイスのための親水性コーティング
JP2020099720A (ja) * 2015-05-08 2020-07-02 コーニンクレッカ フィリップス エヌ ヴェＫｏｎｉｎｋｌｉｊｋｅ Ｐｈｉｌｉｐｓ Ｎ．Ｖ． 導管内デバイスのための親水性コーティング
CN106730247A (zh) * 2017-02-04 2017-05-31 成都鼎信致远科技有限公司 一种血管介入导管
WO2020257830A1 (fr) * 2019-06-21 2020-12-24 Wismed Pl Sp Z.O.0. A Company Incorporated In Poland; Number Krs 0000751368 Fil-guide à élution médicamenteuse
CN114748700A (zh) * 2022-04-22 2022-07-15 华南理工大学 一种用于tpu包覆导丝的超亲水涂层及其制备方法

Also Published As

Publication number Publication date
JP2016503689A (ja) 2016-02-08
EP2900290A1 (fr) 2015-08-05

Similar Documents

Publication Publication Date Title
EP2543400B1 (fr) Dispositif médical doté d'un revêtement lubrifiant avec un composé hydrophile dans un réseau interverrouillé
AU2012348360B2 (en) Medical device having a lubricious coating with a hydrophilic compound in an interlocking network
US8747940B2 (en) Manufacturing processes for making medical devices having a coating gradient
US20130123664A1 (en) Medical device having a lubricious coating with a hydrophilic compound in an interlocking network
US6221425B1 (en) Lubricious hydrophilic coating for an intracorporeal medical device
EP1858438B1 (fr) Revetements polymeres elastiques pour articles medicaux inserables
JP2705852B2 (ja) 潤滑性カテーテル
JP2834582B2 (ja) 潤滑性流動方向性カテーテル
EP1615677B1 (fr) Enrobage de dispositifs biomedicaux
US20080057298A1 (en) Low friction particulate coatings
WO2014109824A1 (fr) Dispositif médical pourvu d'un revêtement lubrifiant formant avec des composés hydrophiles un réseau d'interpénétration
KR20230013057A (ko) 코팅 조성물, 기재 상에 친수성 코팅을 형성하는 방법, 및 이러한 코팅을 포함하는 의료 장치
CN105530966A (zh) 光滑涂层组合物
JP6781220B2 (ja) 基板用コーティング
JP2007267757A (ja) ガイドワイヤ

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13793048

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2015551672

Country of ref document: JP

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 2013793048

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: DE