WO2014084318A1 - Siloxane compound, modified imide resin, thermosetting resin composition, prepreg, resin-equipped film, laminated plate, multilayer printed circuit board, and semiconductor package - Google Patents
Siloxane compound, modified imide resin, thermosetting resin composition, prepreg, resin-equipped film, laminated plate, multilayer printed circuit board, and semiconductor package Download PDFInfo
- Publication number
- WO2014084318A1 WO2014084318A1 PCT/JP2013/082072 JP2013082072W WO2014084318A1 WO 2014084318 A1 WO2014084318 A1 WO 2014084318A1 JP 2013082072 W JP2013082072 W JP 2013082072W WO 2014084318 A1 WO2014084318 A1 WO 2014084318A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- compound
- resin
- siloxane compound
- aromatic
- Prior art date
Abstract
Description
また、特許文献8に記載の熱硬化性ポリアゾメチン樹脂は、耐熱性や強靭性の改良が依然不足であり、これらを銅張積層板や層間絶縁材料として適用した場合も、耐熱性や信頼性、加工性等が不足する場合がある。
さらに、特許文献9に記載の熱硬化性ポリアゾメチン樹脂は、低硬化収縮性や低熱膨張率性の点で、満足出来ていなかった。 However, the polyazomethines described in Patent Documents 1 to 7 may lack heat resistance and moldability when applied as a copper clad laminate or an interlayer insulating material.
Further, the thermosetting polyazomethine resin described in Patent Document 8 still lacks improvement in heat resistance and toughness, and even when these are applied as a copper clad laminate or an interlayer insulating material, the heat resistance and reliability are also improved. , Workability and the like may be insufficient.
Furthermore, the thermosetting polyazomethine resin described in Patent Document 9 has not been satisfactory in terms of low curing shrinkage and low thermal expansion.
[2] さらに、芳香族アゾメチンを含む[1]に記載のシロキサン化合物。
[3] 1分子中に少なくとも2個の1級アミノ基を有する芳香族アミン化合物(A)、1分子中に少なくとも2個のアルデヒド基を有する芳香族アルデヒド化合物(B)、分子末端に少なくとも2個のアミノ基を有するシロキサン化合物(C)を反応させ得られる、[2]に記載のシロキサン化合物。
[4] 1分子中に少なくとも2個の1級アミノ基を有する芳香族アミン化合物(A)、1分子中に少なくとも2個のアルデヒド基を有する芳香族アルデヒド化合物(B)、を反応後、分子末端に少なくとも2個のアミノ基を有するシロキサン化合物(C)を反応させ得られる、[2]に記載のシロキサン化合物。
[5] 1分子中に少なくとも2個のアルデヒド基を有する芳香族アルデヒド化合物(B)、分子末端に少なくとも2個のアミノ基を有するシロキサン化合物(C)を反応後、1分子中に少なくとも2個の1級アミノ基を有する芳香族アミン化合物(A)を反応させて得られる、[2]に記載のシロキサン化合物。
[6] [1]~[5]のいずれかに記載のシロキサン化合物と、1分子中に少なくとも2個のN-置換マレイミド基を有するマレイミド化合物(D)とを反応させて得られる、芳香族アゾメチンを有する変性イミド樹脂。
[7] さらに、酸性置換基を有し、該酸性置換基が下記一般式(3)に示すアミン化合物(E)の酸性置換基に由来する[6]に記載の変性イミド樹脂。
[8] [1]~[5]のいずれかに記載のシロキサン化合物と、1分子中に少なくとも2個のN-置換マレイミド基を有するマレイミド化合物(D)とを含有する熱硬化性樹脂組成物。
[9] さらに、下記一般式(3)に示す酸性置換基を有するアミン化合物(E)を含有する[8]に記載の熱硬化性樹脂組成物。
[10] さらに、熱可塑性エラストマー(F)を含有する[8]又は[9]に記載の熱硬化性樹脂組成物。
[11] さらに、エポキシ樹脂及びシアネート樹脂から選ばれた少なくとも一種の熱硬化性樹脂(G)を含有する[8]~[10]のいずれかに記載の熱硬化性樹脂組成物。
[12] さらに、無機充填材(H)を含有する[8]~[11]のいずれかに記載の熱硬化性樹脂組成物。
[13] さらに、硬化促進剤(I)を含有する[8]~[12]のいずれかに記載の熱硬化性樹脂組成物。
[14] [8]~[13]のいずれかに記載の熱硬化性樹脂組成物を基材に含浸してなるプリプレグ。
[15] [8]~[13]のいずれかに記載の熱硬化性樹脂組成物を支持体上に層形成してなる樹脂付フィルム。
[16] [14]記載のプリプレグを積層成形し得られる積層板。
[17] [15]記載の樹脂付フィルムを積層成形して得られる積層板。
[18] [16]又は[17]記載の積層板を用いて製造される多層プリント配線板。
[19] [18]記載の多層プリント配線板に半導体素子を搭載してなる半導体パッケージ。
[2] The siloxane compound according to [1], further comprising an aromatic azomethine.
[3] An aromatic amine compound (A) having at least two primary amino groups in one molecule, an aromatic aldehyde compound (B) having at least two aldehyde groups in one molecule, and at least 2 at the molecular end The siloxane compound according to [2], which is obtained by reacting a siloxane compound (C) having an amino group.
[4] After reacting an aromatic amine compound (A) having at least two primary amino groups in one molecule and an aromatic aldehyde compound (B) having at least two aldehyde groups in one molecule, the molecule The siloxane compound according to [2], which can be obtained by reacting a siloxane compound (C) having at least two amino groups at its terminals.
[5] After reacting an aromatic aldehyde compound (B) having at least two aldehyde groups in one molecule and a siloxane compound (C) having at least two amino groups at the molecular ends, at least two in one molecule The siloxane compound according to [2], which is obtained by reacting the aromatic amine compound (A) having a primary amino group.
[6] An aromatic obtained by reacting the siloxane compound according to any one of [1] to [5] with a maleimide compound (D) having at least two N-substituted maleimide groups in one molecule. A modified imide resin having azomethine.
[7] The modified imide resin according to [6], further having an acidic substituent, wherein the acidic substituent is derived from the acidic substituent of the amine compound (E) represented by the following general formula (3).
[8] A thermosetting resin composition comprising the siloxane compound according to any one of [1] to [5] and a maleimide compound (D) having at least two N-substituted maleimide groups in one molecule. .
[9] The thermosetting resin composition according to [8], further including an amine compound (E) having an acidic substituent represented by the following general formula (3).
[10] The thermosetting resin composition according to [8] or [9], further comprising a thermoplastic elastomer (F).
[11] The thermosetting resin composition according to any one of [8] to [10], further containing at least one thermosetting resin (G) selected from an epoxy resin and a cyanate resin.
[12] The thermosetting resin composition according to any one of [8] to [11], further containing an inorganic filler (H).
[13] The thermosetting resin composition according to any one of [8] to [12], further comprising a curing accelerator (I).
[14] A prepreg obtained by impregnating a base material with the thermosetting resin composition according to any one of [8] to [13].
[15] A film with a resin obtained by forming a layer of the thermosetting resin composition according to any one of [8] to [13] on a support.
[16] A laminate obtained by laminate-molding the prepreg according to [14].
[17] A laminate obtained by laminating the film with resin according to [15].
[18] A multilayer printed wiring board produced using the laminated board according to [16] or [17].
[19] A semiconductor package comprising a semiconductor element mounted on the multilayer printed wiring board according to [18].
(シロキサン化合物)
本発明のシロキサン化合物は、下記一般式(1)及び下記一般式(2)に示す構造を含むものである。かかる構造は例えば、下記一般式(1)に示す構造を含む化合物と下記一般式(2)に示す構造を含む化合物とを反応させることで得られる。 Hereinafter, the present invention will be described in detail.
(Siloxane compound)
The siloxane compound of the present invention includes a structure represented by the following general formula (1) and the following general formula (2). Such a structure can be obtained, for example, by reacting a compound having a structure represented by the following general formula (1) with a compound having a structure represented by the following general formula (2).
また、本発明のシロキサン化合物は、芳香族アゾメチンを含むことが好ましい。
ここで、芳香族アゾメチンとは、シッフ塩基(-N=CH-)に少なくとも1つの芳香族が結合したものをいう。
Moreover, it is preferable that the siloxane compound of this invention contains aromatic azomethine.
Here, the aromatic azomethine means a compound in which at least one aromatic is bonded to a Schiff base (—N═CH—).
本発明のシロキサン化合物は、1分子中に少なくとも2個の1級アミノ基を有する芳香族アミン化合物(A)(以下、芳香族アミン化合物(A)と呼ぶことがある)、1分子中に少なくとも2個のアルデヒド基を有する芳香族アルデヒド化合物(B)(以下、芳香族アルデヒド化合物(B)と呼ぶことがある)、分子末端に少なくとも2個のアミノ基を有するシロキサン化合物(C)(以下、シロキサン化合物(C)と呼ぶことがある)を反応させて得られる。 Hereinafter, the siloxane compound of the present invention will be described in detail.
The siloxane compound of the present invention is an aromatic amine compound (A) having at least two primary amino groups in one molecule (hereinafter sometimes referred to as an aromatic amine compound (A)). Aromatic aldehyde compound (B) having two aldehyde groups (hereinafter sometimes referred to as aromatic aldehyde compound (B)), siloxane compound (C) having at least two amino groups at the molecular terminals (hereinafter, It may be obtained by reacting a siloxane compound (sometimes called a siloxane compound (C)).
一般式(2)の式中、nは1~100の整数であり、より好ましくは、2~50の整数である。 The siloxane compound (C) having at least two amino groups at the molecular ends of the present invention includes a structure represented by the following general formula (2).
In the general formula (2), n is an integer of 1 to 100, more preferably an integer of 2 to 50.
これらの中で、例えば、合成時の反応性が高く、低熱膨張性の点から、X-22-161A、X-22-161B、KF-8012、X-22-1660B-3、BY-16-853Bが好ましく、相溶性に優れ、高弾性率化できる点から、X-22-161A、X-22-161Bが特に好ましい。 A commercially available product may be used as the siloxane compound (C) having at least two amino groups at the molecular terminals. Examples of commercially available products include “KF-8010” (amino group equivalent 430), “X-22-161A” (amino group equivalent 800), “X-22-161B” (amino group equivalent 1500), “KF— 8012 "(amino group equivalent 2200)," KF-8008 "(amino group equivalent 5700)," X-22-9409 "(amino group equivalent 700)," X-22-1660B-3 "(amino group equivalent 2200) (Shin-Etsu Chemical Co., Ltd.), “BY-16-853U” (amino group equivalent 460), “BY-16-853” (amino group equivalent 650), “BY-16-853B” (amino group equivalent) 2200) (above, manufactured by Toray Dow Corning Co., Ltd.). These may be used alone or in admixture of two or more.
Among these, for example, from the viewpoint of high reactivity during synthesis and low thermal expansion, X-22-161A, X-22-161B, KF-8012, X-22-1660B-3, BY-16- 853B is preferable, and X-22-161A and X-22-161B are particularly preferable from the viewpoint of excellent compatibility and high elastic modulus.
反応温度は、例えば、70~150℃が好ましく、副生成物である水を除去しながら反応することが望ましく、反応温度は100~130がより好ましい。温度が70℃より低いと反応速度が遅くなり、温度が150℃以下であれば反応溶媒に高沸点の溶媒を必要とせず、プリプレグを製造する際、残溶剤を残しにくくなり耐熱性の低下を抑制することが出来る。 A siloxane compound (i) is obtained by charging the above raw materials, an organic solvent and, if necessary, a reaction catalyst into a reaction kettle and stirring for 0.1 to 10 hours while heating and keeping warm as necessary to cause a dehydration condensation reaction.
The reaction temperature is preferably 70 to 150 ° C., for example, and the reaction is desirably performed while removing water as a by-product, and the reaction temperature is more preferably 100 to 130. When the temperature is lower than 70 ° C., the reaction rate is slow, and when the temperature is 150 ° C. or lower, a high-boiling solvent is not required as a reaction solvent, and when producing a prepreg, it is difficult to leave a residual solvent and heat resistance is reduced. Can be suppressed.
反応方法bにおいて、反応に使用される有機溶媒及び必要により使用される反応触媒は、任意に反応方法aと同様のものを使用することができる。 Next, the reaction method b will be described in detail. In the reaction method b, first, an aromatic amine compound (A) having at least two primary amino groups in one molecule and an aromatic aldehyde compound (B) having at least two aldehyde groups in one molecule. To obtain an aromatic azomethine compound having at least one aldehyde group in one molecule. Subsequently, the modified siloxane compound (ii) having an aromatic azomethine can be obtained by reacting the compound with a siloxane compound (C) having at least two amino groups at the molecular terminals.
In reaction method b, the same organic solvent as used in reaction method a can be used as the organic solvent used in the reaction and, if necessary, the reaction catalyst.
ここで、1分子中に少なくとも2個の1級アミノ基を有する芳香族アミン化合物(A)と1分子中に少なくとも2個のアルデヒド基を有する芳香族アルデヒド化合物(B)の使用量は、例えば、芳香族アミン化合物(A)の一級アミノ基数〔芳香族アミン化合物(A)の使用量/芳香族アミン化合物(A)の一級アミノ基当量〕が、芳香族アルデヒド化合物(B)のアルデヒド基数〔芳香族アルデヒド化合物(B)の使用量/芳香族アルデヒド化合物(B)のアルデヒド基当量〕の0.1倍~5.0倍の範囲になるように使用することが好ましい。0.1倍以上とすることにより、本反応により得られる芳香族アゾメチン化合物の分子量の低下が抑制される傾向にある。また、5.0倍以下とすることにより、溶媒への溶解性の低下が抑制される。 First, an aromatic amine compound (A) having at least two primary amino groups per molecule and an aromatic aldehyde compound (B) having at least two aldehyde groups per molecule in an organic solvent. By performing dehydration condensation reaction, an aromatic azomethine compound having at least one aldehyde group in one molecule is obtained.
Here, the use amount of the aromatic amine compound (A) having at least two primary amino groups in one molecule and the aromatic aldehyde compound (B) having at least two aldehyde groups in one molecule is, for example, The number of primary amino groups of the aromatic amine compound (A) [the amount of the aromatic amine compound (A) used / the primary amino group equivalent of the aromatic amine compound (A)] is the number of aldehyde groups of the aromatic aldehyde compound (B) [ The amount used of the aromatic aldehyde compound (B) / the aldehyde group equivalent of the aromatic aldehyde compound (B)] is preferably 0.1 to 5.0 times. By setting it to 0.1 times or more, a decrease in the molecular weight of the aromatic azomethine compound obtained by this reaction tends to be suppressed. Moreover, the fall of the solubility to a solvent is suppressed by setting it as 5.0 times or less.
反応温度は、例えば、70~150℃が好ましく、00~130℃がより好ましい。また、副生成物である水を除去しながら反応することが好ましい。1温度が70℃以上であれば、反応速度が遅くなりすぎない傾向にある。反応温度が150℃以下であれば反応溶媒に高沸点の溶媒を必要とせず、プリプレグを製造する際、残溶剤を残しにくくなり、耐熱性の低下を抑制することができる。 At least one aldehyde per molecule is prepared by charging the above raw materials, organic solvent, and if necessary, a reaction catalyst in a reaction kettle, and stirring and dehydrating condensation reaction for 0.1 to 10 hours while heating and holding as necessary. An aromatic azomethine compound having a group is obtained.
The reaction temperature is, for example, preferably 70 to 150 ° C, more preferably 00 to 130 ° C. Moreover, it is preferable to react, removing the water which is a by-product. If 1 temperature is 70 degreeC or more, it exists in the tendency for reaction rate not to become too slow. If the reaction temperature is 150 ° C. or lower, a high-boiling solvent is not required for the reaction solvent, and when the prepreg is produced, it is difficult to leave a residual solvent, and a decrease in heat resistance can be suppressed.
ここで、芳香族アゾメチン化合物とシロキサン化合物(C)の使用量は、例えば、シロキサン化合物(C)の一級アミノ基数〔シロキサン化合物(C)の使用量/シロキサン化合物(C)の一級アミノ基当量〕が、芳香族アゾメチン化合物のアルデヒド基数〔芳香族アゾメチン化合物の使用量/芳香族アゾメチン化合物のアルデヒド基当量〕の1.0~10.0倍の範囲になるように使用されることが好ましい。1.0倍以上とすることにより、溶媒への溶解性の低下が抑制される傾向にある。また、10.0倍以下とすることにより、芳香族アゾメチンを有する変性シロキサン化合物(ii)を含有する熱硬化性樹脂の弾性率の低下が抑制される傾向にある。 Next, a dehydration condensation reaction of the aromatic azomethine compound having at least one aldehyde group in one molecule obtained by the above reaction and the siloxane compound (C) having at least two amino groups at the molecular ends in an organic solvent. By doing so, a modified siloxane compound (ii) having an aromatic azomethine can be obtained.
Here, the amount of the aromatic azomethine compound and the siloxane compound (C) used is, for example, the number of primary amino groups of the siloxane compound (C) [the amount of siloxane compound (C) used / the primary amino group equivalent of the siloxane compound (C)]. However, it is preferably used in a range of 1.0 to 10.0 times the number of aldehyde groups of the aromatic azomethine compound [amount of aromatic azomethine compound used / aldehyde group equivalent of aromatic azomethine compound]. By setting it to 1.0 times or more, a decrease in solubility in a solvent tends to be suppressed. Moreover, it is in the tendency for the fall of the elasticity modulus of the thermosetting resin containing the modified siloxane compound (ii) which has aromatic azomethine to be suppressed by setting it as 10.0 times or less.
反応温度は、例えば、70~150℃が好ましく、100~130℃がより好ましい。また、副生成物である水を除去しながら反応することが好ましい。反応温度が70℃以上であると、反応速度が遅くなりすぎない傾向にある。反応温度が150℃以下であれば、反応溶媒に高沸点の溶媒を必要とせず、プリプレグを製造する際、残溶剤を残しにくくなり耐熱性の低下を抑制することが出来る。 A modified siloxane compound having an aromatic azomethine (ii) is prepared by charging the above raw materials, an organic solvent and, if necessary, a reaction catalyst in a reaction kettle and stirring and dehydrating and condensing for 0.1 to 10 hours while heating and keeping heat as necessary. ) Is obtained.
The reaction temperature is, for example, preferably 70 to 150 ° C, more preferably 100 to 130 ° C. Moreover, it is preferable to react, removing the water which is a by-product. When the reaction temperature is 70 ° C. or higher, the reaction rate tends not to be too slow. If reaction temperature is 150 degrees C or less, a high boiling point solvent is not required for a reaction solvent, and when manufacturing a prepreg, it will become difficult to leave a residual solvent and it can suppress a heat resistant fall.
反応方法cにおいて、反応に使用される有機溶媒及び必要により使用される反応触媒は、任意に反応方法a及びbと同様のものを使用することができる。 Next, the reaction method c will be described in detail. In the reaction method c, first, an aromatic aldehyde compound (B) having at least two aldehyde groups in one molecule and a siloxane compound (C) having at least two amino groups at the molecular ends are reacted. A modified siloxane compound having at least one aldehyde group and azomethine group (—N═CH—) in one molecule is obtained. Next, the modified siloxane compound (iii) having an aromatic azomethine can be obtained by reacting the compound with an aromatic amine compound (A) having at least two primary amino groups in one molecule.
In the reaction method c, the organic solvent used in the reaction and the reaction catalyst used as necessary can be the same as those used in the reaction methods a and b.
ここで、1分子中に少なくとも2個のアルデヒド基を有する芳香族アルデヒド化合物(B)と、分子末端に少なくとも2個のアミノ基を有するシロキサン化合物(C)の使用量は、例えば、シロキサン化合物(C)の一級アミノ基数〔シロキサン化合物(C)の使用量/シロキサン化合物(C)の一級アミノ基当量〕が、芳香族アルデヒド化合物(B)のアルデヒド基数〔芳香族アルデヒド化合物(B)の使用量/芳香族アルデヒド化合物(B)のアルデヒド基当量〕の0.1倍~5.0倍の範囲になるように使用することが好ましい。0.1倍以上とすることにより、溶媒への溶解性の低下が抑制される。また、5.0倍以下とすることにより、本反応により得られる1分子中に少なくとも1個のアルデヒド基とアゾメチン基(-N=CH-)を有する変性シロキサン化合物の分子量の低下が抑制される。 An aromatic aldehyde compound (B) having at least two aldehyde groups in one molecule and a siloxane compound (C) having at least two amino groups at the molecular ends are subjected to a dehydration condensation reaction in an organic solvent. A modified siloxane compound having at least one aldehyde group and azomethine group (—N═CH—) in the molecule is obtained.
Here, the amount of the aromatic aldehyde compound (B) having at least two aldehyde groups in one molecule and the amount of the siloxane compound (C) having at least two amino groups at the molecular ends are, for example, siloxane compound ( C) number of primary amino groups [amount of siloxane compound (C) used / primary amino group equivalent of siloxane compound (C)] is the number of aldehyde groups of aromatic aldehyde compound (B) [amount of aromatic aldehyde compound (B) used] / Aldehyde group equivalent of aromatic aldehyde compound (B)] is preferably used in a range of 0.1 to 5.0 times. By making it 0.1 times or more, a decrease in solubility in a solvent is suppressed. In addition, when the ratio is 5.0 times or less, a decrease in the molecular weight of the modified siloxane compound having at least one aldehyde group and azomethine group (—N═CH—) in one molecule obtained by this reaction is suppressed. .
反応温度は、例えば、70~150℃が好ましく、100~130℃がより好ましい。また、副生成物である水を除去しながら反応することが好ましい。反応温度が70℃以上であると、反応速度が遅くなりすぎない傾向がある。反応温度が150℃以下であれば反応溶媒に高沸点の溶媒を必要とせず、プリプレグを製造する際、残溶剤を残しにくくなり耐熱性の低下を抑制することが出来る。 At least one aldehyde per molecule is prepared by charging the above raw materials, organic solvent, and if necessary, a reaction catalyst in a reaction kettle, and stirring and dehydrating condensation reaction for 0.1 to 10 hours while heating and holding as necessary. A modified siloxane compound having an azomethine group (—N═CH—) is obtained.
The reaction temperature is, for example, preferably 70 to 150 ° C, more preferably 100 to 130 ° C. Moreover, it is preferable to react, removing the water which is a by-product. When the reaction temperature is 70 ° C. or higher, the reaction rate tends not to be too slow. When the reaction temperature is 150 ° C. or lower, a high-boiling solvent is not required as the reaction solvent, and when the prepreg is produced, it is difficult to leave a residual solvent, and a decrease in heat resistance can be suppressed.
ここで、変性シロキサン化合物と芳香族アミン化合物(A)の使用量は、例えば、芳香族アミン化合物(A)の一級アミノ基数〔芳香族アミン化合物(A)の使用量/芳香族アミン化合物(A)の一級アミノ基当量〕が、変性シロキサン化合物のアルデヒド基数〔変性シロキサン化合物の使用量/変性シロキサン化合物のアルデヒド基当量〕の1.0~10.0倍の範囲になるように使用されることが好ましい。1.0倍以上とすることにより、芳香族アゾメチンを有する変性シロキサン化合物(iii)を含有する熱硬化性樹脂の低熱膨張性の低下が抑制される傾向にある。また、10.0倍以下とすることにより、溶媒への溶解性の低下が抑制される傾向にある。 Next, a modified siloxane compound having at least one aldehyde group and azomethine group (—N═CH—) in one molecule obtained by the above reaction, and an aromatic having at least two primary amino groups in one molecule. A modified siloxane compound (iii) having an aromatic azomethine can be obtained by subjecting the aromatic amine compound (A) to a dehydration condensation reaction in an organic solvent.
Here, the usage amount of the modified siloxane compound and the aromatic amine compound (A) is, for example, the number of primary amino groups of the aromatic amine compound (A) [the usage amount of the aromatic amine compound (A) / the aromatic amine compound (A). ) Primary amino group equivalent] is 1.0 to 10.0 times the number of aldehyde groups of the modified siloxane compound [amount of modified siloxane compound used / aldehyde group equivalent of the modified siloxane compound]. Is preferred. By setting it to 1.0 times or more, there is a tendency that a decrease in low thermal expansion of the thermosetting resin containing the modified siloxane compound (iii) having an aromatic azomethine is suppressed. Moreover, it exists in the tendency for the fall of the solubility to a solvent to be suppressed by setting it as 10.0 times or less.
反応温度は、例えば、70~150℃が好ましく、100~130℃がより好ましい。また、副生成物である水を除去しながら反応することが好ましい。反応温度が70℃以上であると、反応速度が遅くなりすぎない傾向にある。反応温度が150℃以下であれば、反応溶媒に高沸点の溶媒を必要とせず、プリプレグを製造する際、残溶剤を残しにくくなり、耐熱性の低下を抑制することができる。 A modified siloxane compound having an aromatic azomethine is prepared by charging the above raw materials, an organic solvent and, if necessary, a reaction catalyst into a reaction kettle and stirring and dehydrating and condensing for 0.1 to 10 hours while heating and holding as necessary. iii) is obtained.
The reaction temperature is, for example, preferably 70 to 150 ° C, more preferably 100 to 130 ° C. Moreover, it is preferable to react, removing the water which is a by-product. When the reaction temperature is 70 ° C. or higher, the reaction rate tends not to be too slow. If reaction temperature is 150 degrees C or less, it will become difficult to leave a residual solvent when manufacturing a prepreg, without requiring a high boiling point solvent as a reaction solvent, and a heat resistant fall can be suppressed.
また、使用カラムとしては、東ソー株式会社製TSKgel SuperHZ2000,2300を使用でき、測定条件としては、測定温度40℃、流量0.5ml/min、溶媒テトラヒドロフランとすることで、測定可能である。 The modified siloxane compound of the present invention obtained by the above reaction methods a, b and c can be confirmed by performing IR measurement. The IR measurement, to confirm that the peak of 1620 cm -1 attributable to the azomethine group (-N = CH-) appears, also, at 3,440 cm -1 due to the primary amino group, and 3370cm peak around -1 By confirming the presence, it can be confirmed that the reaction proceeds well and the desired compound is obtained. Further, the weight average molecular weight (Mw) is, for example, preferably 1000 to 300000, and particularly preferably 6000 to 150,000. If the weight average molecular weight (Mw) is not less than the lower limit, low curing shrinkage and low thermal expansion are improved, and if it is not more than the upper limit, compatibility and elastic modulus are improved. The weight average molecular weight (Mw) is measured by gel permeation chromatography (GPC) and converted by a calibration curve produced using standard polystyrene. For example, it can be performed under the following conditions. As a measuring device, an auto sampler (AS-8020 manufactured by Tosoh Corporation), a column oven (860-C0 manufactured by JASCO Corporation), an RI detector (830-RI manufactured by JASCO Corporation), a UV / VIS detector ( JASCO Corporation 870-UV) and HPLC pump (JASCO Corporation 880-PU) are used.
In addition, TSKgel SuperHZ2000, 2300 manufactured by Tosoh Corporation can be used as the column used, and measurement can be performed by using a measurement temperature of 40 ° C., a flow rate of 0.5 ml / min, and a solvent tetrahydrofuran.
本発明の変性イミド樹脂は、既述の本発明のアミノ変性シロキサン化合物と、1分子中に少なくとも2個のN-置換マレイミド基を有するマレイミド化合物(C)とを反応させて得られるものである。 (Modified imide resin)
The modified imide resin of the present invention is obtained by reacting the aforementioned amino-modified siloxane compound of the present invention with a maleimide compound (C) having at least two N-substituted maleimide groups in one molecule. .
なお、アミン化合物(D)のさらなる詳細については後述する。また、「アミン化合物(D)の酸性置換基に由来するもの」とは、アミン化合物(D)の酸性置換基そのもの、及び、当該酸性置換基を含むものをいう。 Further, the modified imide resin preferably has an acidic substituent, and the acidic substituent is derived from the acidic substituent of the amine compound (D) represented by the following general formula (3). The acidic substituent can be introduced by reacting the amine compound (D). By having such an acidic substituent, good low thermal expansibility can be obtained.
Further details of the amine compound (D) will be described later. The term “derived from the acidic substituent of the amine compound (D)” refers to the acidic substituent itself of the amine compound (D) and the one containing the acidic substituent.
本発明の熱硬化性樹脂組成物は、本発明の変性シロキサン化合物と、1分子中に少なくとも2個のN-置換マレイミド基を有するマレイミド化合物(D)を含有してなるものである。
1分子中に少なくとも2個のN-置換マレイミド基を有するマレイミド化合物(D)(以下、マレイミド化合物(D)と呼ぶことがある)としては、例えば、ビス(4-マレイミドフェニル)メタン、ポリフェニルメタンマレイミド、ビス(4-マレイミドフェニル)エーテル、ビス(4-マレイミドフェニル)スルホン、3,3-ジメチル-5,5-ジエチル-4,4-ジフェニルメタンビスマレイミド、4-メチル-1,3-フェニレンビスマレイミド、m-フェニレンビスマレイミド、2,2-ビス(4-(4-マレイミドフェノキシ)フェニル)プロパン等が挙げられる。これらのマレイミド化合物は、単独で用いても2種類以上を混合して用いてもよい。 (Thermosetting resin composition)
The thermosetting resin composition of the present invention comprises the modified siloxane compound of the present invention and a maleimide compound (D) having at least two N-substituted maleimide groups in one molecule.
Examples of maleimide compounds (D) having at least two N-substituted maleimide groups in one molecule (hereinafter sometimes referred to as maleimide compounds (D)) include bis (4-maleimidophenyl) methane, polyphenyl Methanemaleimide, bis (4-maleimidophenyl) ether, bis (4-maleimidophenyl) sulfone, 3,3-dimethyl-5,5-diethyl-4,4-diphenylmethane bismaleimide, 4-methyl-1,3-phenylene Examples thereof include bismaleimide, m-phenylene bismaleimide, 2,2-bis (4- (4-maleimidophenoxy) phenyl) propane, and the like. These maleimide compounds may be used alone or in admixture of two or more.
マレイミド化合物(D)の使用量は、例えば、樹脂成分の総和100質量部当たり、30~99質量部とすることが好ましく、40~95質量部とすることが、低熱膨張性、高弾性率の点からより好ましい In the thermosetting resin composition of the present invention, the amount (blending amount) of the siloxane compound of the present invention is preferably, for example, 1 to 30 parts by mass per 100 parts by mass of the total resin components. It is more preferable to set it as a mass part from the point of copper foil adhesiveness and chemical resistance.
The amount of maleimide compound (D) used is, for example, preferably 30 to 99 parts by weight, and 40 to 95 parts by weight per 100 parts by weight of the total resin components. More preferable in terms
有機溶媒中で変性シロキサン化合物、マレイミド化合物(D)を反応させる際の反応温度は、例えば、70~150℃であることが好ましく、100~130℃であることがより好ましい。反応時間は、例えば、0.1~10時間であることが好ましく、1~6時間であることがより好ましい。 In this pre-reaction, it is preferable to synthesize a modified imide resin by reacting the siloxane compound of the present invention and the maleimide compound (D) while heating and keeping in an organic solvent.
The reaction temperature when reacting the modified siloxane compound and maleimide compound (D) in an organic solvent is preferably, for example, 70 to 150 ° C., more preferably 100 to 130 ° C. The reaction time is, for example, preferably 0.1 to 10 hours, and more preferably 1 to 6 hours.
併用する硬化剤としては、例えば、ジシアンジアミドや、4,4’-ジアミノジフェニルメタン、4,4’-ジアミノ-3,3’-ジエチル-ジフェニルメタン、4,4’-ジアミノジフェニルスルホン、フェニレンジアミン、キシレンジアミン等の芳香族アミン類、ヘキサメチレンジアミン、2,5-ジメチルヘキサメチレンジアミン等の脂肪族アミン類、メラミン、ベンゾグアナミン等のグアナミン化合物類などが挙げられる。
また、上記ラジカル開始剤としては、特に制限されないが、例えば、アシル過酸化物、ハイドロパーオキサイド、ケトン過酸化物、t-ブチル基を有する有機過酸化物、クミル基を有する過酸化物等の有機過酸化物などが使用できる。これらは単独で、あるいは2種類以上を混合して使用してもよい。これらの中で、例えば、良好な反応性や耐熱性の点から、芳香族アミン類が好ましい。 A thermosetting resin composition comprising the siloxane compound of the present invention and a maleimide compound (D) having at least two N-substituted maleimide groups in one molecule, and an aromatic obtained by pre-reacting the above compound The modified imide resin having azomethine alone has good thermosetting reactivity, but if necessary, a curing agent and a radical initiator may be used in combination. By using a curing agent and a radical initiator, heat resistance, adhesiveness, and mechanical strength can be improved.
Examples of the curing agent used in combination include dicyandiamide, 4,4′-diaminodiphenylmethane, 4,4′-diamino-3,3′-diethyl-diphenylmethane, 4,4′-diaminodiphenylsulfone, phenylenediamine, and xylenediamine. Aromatic amines such as hexamethylenediamine and 2,5-dimethylhexamethylenediamine, and guanamine compounds such as melamine and benzoguanamine.
The radical initiator is not particularly limited, and examples thereof include acyl peroxides, hydroperoxides, ketone peroxides, organic peroxides having a t-butyl group, and peroxides having a cumyl group. Organic peroxides can be used. These may be used alone or in admixture of two or more. Among these, for example, aromatic amines are preferable from the viewpoint of good reactivity and heat resistance.
有機溶媒中で本発明のシロキサン化合物、マレイミド化合物(D)、酸性置換基を有するアミン化合物(E)を反応させる際の反応温度は、例えば、70~150℃であることが好ましく、100~130℃であることがより好ましい。反応時間は、例えば、0.1~10時間であることが好ましく、1~6時間であることがより好ましい。 In this pre-reaction, a modified imide resin having an acidic substituent is synthesized by reacting the siloxane compound of the present invention, a maleimide compound (D), and an amine compound (E) having an acidic substituent while being heated and kept in an organic solvent. It is preferable to do.
The reaction temperature when the siloxane compound of the present invention, maleimide compound (D), and amine compound (E) having an acidic substituent are reacted in an organic solvent is preferably 70 to 150 ° C., for example, and preferably 100 to 130. More preferably, it is ° C. The reaction time is, for example, preferably 0.1 to 10 hours, and more preferably 1 to 6 hours.
また、プレ反応における酸性置換基を有するアミン化合物(E)の使用量は、例えば、本発明のシロキサン化合物の樹脂成分100質量部に対して1~1000質量部が好ましく、5~500質量部がより好ましい。1質量部以上とすることにより耐熱性の低下を抑制可能であり、また、1000質量部以下とすることにより低熱膨張性を良好に保つことができる。 The amount of the maleimide compound (D) used in the pre-reaction is preferably 50 to 3000 parts by weight, for example, 100 to 1500 parts per 100 parts by weight of the resin component of the siloxane compound of the present invention while maintaining the above relationship. Part by mass is more preferable. By setting it to 50 parts by mass or more, a decrease in heat resistance can be suppressed. Moreover, low thermal expansibility can be kept favorable by setting it as 3000 mass parts or less.
The amount of the amine compound (E) having an acidic substituent in the pre-reaction is, for example, preferably 1 to 1000 parts by weight, and preferably 5 to 500 parts by weight with respect to 100 parts by weight of the resin component of the siloxane compound of the present invention. More preferred. By setting it as 1 mass part or more, a heat resistant fall can be suppressed, and low thermal expansion can be kept favorable by setting it as 1000 mass parts or less.
また、上記ラジカル開始剤としては、例えば、アシル過酸化物、ハイドロパーオキサイド、ケトン過酸化物、t-ブチル基を有する有機過酸化物、クミル基を有する過酸化物等の有機過酸化物などが使用できる。これらは単独で、あるいは2種類以上を混合して使用してもよい。これらの中で、例えば、良好な反応性や耐熱性の点から、芳香族アミン類が好ましい。 Examples of the curing agent used in combination include dicyandiamide, 4,4′-diaminodiphenylmethane, 4,4′-diamino-3,3′-diethyl-diphenylmethane, 4,4′-diaminodiphenylsulfone, phenylenediamine, and xylenediamine. Aromatic amines such as hexamethylenediamine and 2,5-dimethylhexamethylenediamine, and guanamine compounds such as melamine and benzoguanamine.
Examples of the radical initiator include organic peroxides such as acyl peroxides, hydroperoxides, ketone peroxides, organic peroxides having a t-butyl group, and peroxides having a cumyl group. Can be used. These may be used alone or in admixture of two or more. Among these, for example, aromatic amines are preferable from the viewpoint of good reactivity and heat resistance.
熱可塑性エラストマー(F)としては、例えば、スチレン系エラストマー、オレフィン系エラストマー、ウレタン系エラストマー、ポリエステル系エラストマー、ポリアミド系エラストマー、アクリル系エラストマー、シリコーン系エラストマーやその誘導体が挙げられる。これらは、ハードセグメント成分とソフトセグメント成分を含んでおり、一般に前者が耐熱性及び強度に、後者が柔軟性及び強靭性に寄与している。これらは、1種を単独で又は2種以上を混合して使用できる。 Furthermore, the thermosetting resin composition of the present invention can contain a thermoplastic elastomer (F).
Examples of the thermoplastic elastomer (F) include styrene elastomers, olefin elastomers, urethane elastomers, polyester elastomers, polyamide elastomers, acrylic elastomers, silicone elastomers and derivatives thereof. These include a hard segment component and a soft segment component. In general, the former contributes to heat resistance and strength, and the latter contributes to flexibility and toughness. These can be used individually by 1 type or in mixture of 2 or more types.
エポキシ樹脂としては、例えば、ビスフェノールA型エポキシ樹脂、ビスフェノールF型エポキシ樹脂、ビスフェノールS型エポキシ樹脂、フェノールノボラック型エポキシ樹脂、クレゾールノボラック型エポキシ樹脂、ビスフェノールAノボラック型エポキシ樹脂、ビスフェノールFノボラック型エポキシ樹脂、スチルベン型エポキシ樹脂、トリアジン骨格含有エポキシ樹脂、フルオレン骨格含有エポキシ樹脂、トリフェノールフェノールメタン型エポキシ樹脂、ビフェニル型エポキシ樹脂、キシリレン型エポキシ樹脂、ビフェニルアラルキル型エポキシ樹脂、ナフタレン型エポキシ樹脂、ジシクロペンタジエン型エポキシ樹脂、脂環式エポキシ樹脂、多官能フェノール類及びアントラセン等の多環芳香族類のジグリシジルエーテル化合物及びこれらにリン化合物を導入したリン含有エポキシ樹脂などが挙げられる。これらは単独で、あるいは2種類以上を混合して使用してもよい。これらの中で、例えば、耐熱性、難燃性の点からビフェニルアラルキル型エポキシ樹脂及びナフタレン型エポキシ樹脂が好ましい。 Furthermore, the thermosetting resin composition of the present invention can contain at least one thermosetting resin (G) selected from an epoxy resin and a cyanate resin.
Examples of the epoxy resin include bisphenol A type epoxy resin, bisphenol F type epoxy resin, bisphenol S type epoxy resin, phenol novolac type epoxy resin, cresol novolak type epoxy resin, bisphenol A novolak type epoxy resin, bisphenol F novolak type epoxy resin. , Stilbene type epoxy resin, Triazine skeleton containing epoxy resin, Fluorene skeleton containing epoxy resin, Triphenolphenol methane type epoxy resin, Biphenyl type epoxy resin, Xylylene type epoxy resin, Biphenyl aralkyl type epoxy resin, Naphthalene type epoxy resin, Dicyclopentadiene -Type epoxy resin, alicyclic epoxy resin, polyfunctional phenols and diglycidyl ether compounds of polycyclic aromatics such as anthracene Beauty These and phosphorus-containing epoxy resin obtained by introducing a phosphorus compound is mentioned. These may be used alone or in admixture of two or more. Among these, for example, biphenyl aralkyl type epoxy resins and naphthalene type epoxy resins are preferable from the viewpoint of heat resistance and flame retardancy.
また、樹脂組成物に無機充填材を配合するに際しては、例えば、該無機充填材をシラン系、チタネート系等のカップリング剤、シリコーンオリゴマー等の表面処理剤で前処理、あるいはインテグラルブレンド処理することも好ましい。 The content of the inorganic filler is, for example, preferably 20 to 500 parts by mass and more preferably 50 to 350 parts by mass with respect to 100 parts by mass of the total resin components. By setting the content of the inorganic filler to 20 to 500 parts by mass with respect to 100 parts by mass of the total of the resin components, the moldability and low thermal expansion of the resin composition can be kept good.
In addition, when an inorganic filler is blended in the resin composition, for example, the inorganic filler is pretreated with a silane or titanate coupling agent, a surface treatment agent such as a silicone oligomer, or an integral blend treatment. It is also preferable.
これらの中で、例えば、促進効果と保存安定性の点から、ナフテン酸亜鉛、イミダゾール誘導体、ホスホニウム塩が好ましい。 The thermosetting resin composition of the present invention can contain a curing accelerator (I). Examples of the curing accelerator include zinc metal naphthenate, cobalt naphthenate, tin octylate, cobalt octylate, bisacetylacetonate cobalt (II), trisacetylacetonate cobalt (III) and the like, imidazoles and Examples thereof include organic phosphorus compounds such as phosphines and phosphonium salts, secondary amines, tertiary amines, and quaternary ammonium salts. These 1 type can be used individually or in mixture of 2 or more types.
Among these, for example, zinc naphthenate, imidazole derivatives, and phosphonium salts are preferable from the viewpoint of the promoting effect and the storage stability.
これらの中で、例えば、溶解性の点からメチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン、メチルセロソルブ、プロピレングリコールモノメチルエーテルが好ましく、低毒性である点からメチルイソブチルケトン、シクロヘキサノン、プロピレングリコールモノメチルエーテルがより好ましい。 Examples of the organic solvent used here include alcohol solvents such as methanol, ethanol, propanol, butanol, methyl cellosolve, butyl cellosolve, propylene glycol monomethyl ether, ketone solvents such as acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, and butyl acetate. Ester solvents such as propylene glycol monomethyl ether acetate, ether solvents such as tetrahydrofuran, aromatic solvents such as toluene, xylene and mesitylene, nitrogen atom-containing solvents such as dimethylformamide, dimethylacetamide and N-methylpyrrolidone, dimethyl sulfoxide And a sulfur atom-containing solvent. These can be used individually by 1 type or in mixture of 2 or more types.
Among these, for example, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, methyl cellosolve, and propylene glycol monomethyl ether are preferable from the viewpoint of solubility, and methyl isobutyl ketone, cyclohexanone, and propylene glycol monomethyl ether are more preferable from the viewpoint of low toxicity.
本発明のプリプレグは、前記した本発明の熱硬化性樹脂組成物を、基材に含浸してなるものである。以下、本発明のプリプレグについて詳述する。
本発明のプリプレグは、本発明の熱硬化性樹脂組成物を、基材に含浸し、加熱等により半硬化(Bステージ化)して製造することができる。本発明の熱硬化性樹脂組成物を基材に含浸させる方法として特に限定されないが、例えば、基材を樹脂ワニスに浸漬する方法、各種コーターにより塗布する方法、スプレーによる吹き付ける方法等が挙げられる。これらの中でも、基材を樹脂ワニスに浸漬する方法が好ましい。これにより、基材に対する樹脂組成物の含浸性を向上することができる。
本発明の基材としては、例えば、各種の電気絶縁材料用積層板に用いられている周知のものが使用できる。その材質の例としては、Eガラス、Dガラス、Sガラス及びQガラス等の無機物繊維、ポリイミド、ポリエステル及びテトラフルオロエチレン等の有機繊維、並びにそれらの混合物などが挙げられる。他の用途では、例えば、繊維強化基材であれば、炭素繊維等を用いることも可能である。 (Prepreg)
The prepreg of the present invention is obtained by impregnating a base material with the above-described thermosetting resin composition of the present invention. Hereinafter, the prepreg of the present invention will be described in detail.
The prepreg of the present invention can be produced by impregnating the thermosetting resin composition of the present invention into a substrate and semi-curing (B-stage) by heating or the like. Although it does not specifically limit as a method to make a base material impregnate the thermosetting resin composition of this invention, For example, the method of immersing a base material in a resin varnish, the method of apply | coating with various coaters, the method of spraying, etc. are mentioned. Among these, the method of immersing the base material in the resin varnish is preferable. Thereby, the impregnation property of the resin composition with respect to a base material can be improved.
As a base material of this invention, the well-known thing used for the laminated board for various electrical insulation materials can be used, for example. Examples of the material include inorganic fibers such as E glass, D glass, S glass and Q glass, organic fibers such as polyimide, polyester and tetrafluoroethylene, and mixtures thereof. In other applications, for example, carbon fiber or the like can be used in the case of a fiber reinforced base material.
本発明の樹脂付フィルムは、本発明の熱硬化性樹脂組成物を支持体上に層形成してなるものである。本発明で得られる熱硬化性樹脂組成物を支持体上に層形成する方法として特に限定されないが、例えば、本発明で得られる熱硬化性樹脂組成物をワニスの状態にし、各種コーターを用いて支持体に塗布し、更に加熱、あるいは熱風吹きつけ等により乾燥させて樹脂組成物層を形成させることができる。このように加熱等により半硬化(Bステージ化)して本発明の樹脂付フィルムを製造することができる。この半硬化状態は、樹脂付きフィルムと回路基板を積層し、硬化する際に、樹脂付きフィルムの樹脂組成物層と回路基板との接着力が確保される状態で、また、回路基板への埋めこみ性(流動性)が確保される状態であることが好ましい。 (Film with resin)
The film with a resin of the present invention is obtained by forming a layer of the thermosetting resin composition of the present invention on a support. Although it does not specifically limit as a method of carrying out layer formation of the thermosetting resin composition obtained by this invention on a support body, For example, the thermosetting resin composition obtained by this invention is made into a varnish state, and various coaters are used. The resin composition layer can be formed by applying to a support and further drying by heating or blowing hot air. Thus, the resin-coated film of the present invention can be produced by being semi-cured (B-staged) by heating or the like. This semi-cured state is a state in which the adhesive force between the resin composition layer of the resin-coated film and the circuit board is secured when the film with resin and the circuit board are laminated and cured, and embedded in the circuit board. It is preferable that the property (fluidity) is ensured.
樹脂付きフィルムは、ロール状に巻き取って貯蔵することもできる。 The thickness of the support is, for example, preferably 10 to 150 μm, more preferably 25 to 50 μm. A protective film according to the support can be further laminated on the surface of the resin composition layer where the support is not provided. The thickness of the protective film is, for example, 1 to 40 μm. By laminating the protective film, foreign matter can be prevented from being mixed.
The film with resin can also be wound and stored in a roll.
本発明の積層板は、前述の樹脂付フィルムを積層成形して得られるものである。例えば、樹脂付フィルムを、真空ラミネーターを用いて、回路基板、プリプレグ及び基材等の片面又は両面にラミネートし、必要に応じ、加熱により硬化することで製造することができる。回路基板に用いられる基板としては、例えば、ガラスエポキシ基板、金属基板、ポリエステル基板、ポリイミド基板、BTレジン基板、熱硬化型ポリフェニレンエーテル基板等が挙げられる。なお、ここで回路基板とは、上記のような基板の片面又は両面に回路パターンが形成されたものをいう。また導体層と絶縁層とを交互に複数積層してなるプリント配線板において、該プリント配線板の最外層の片面又は両面に回路パターンが形成されたものも、ここでいう回路基板に含まれる。なお導体層表面には、黒化処理等により予め粗化処理が施されていてもよい。 (Laminated board)
The laminated board of the present invention is obtained by laminating the above-mentioned resin-coated film. For example, it can be manufactured by laminating a film with resin on one side or both sides of a circuit board, a prepreg, a base material and the like using a vacuum laminator and curing by heating as necessary. Examples of the substrate used for the circuit substrate include a glass epoxy substrate, a metal substrate, a polyester substrate, a polyimide substrate, a BT resin substrate, a thermosetting polyphenylene ether substrate, and the like. In addition, a circuit board means here that the circuit pattern was formed in the one or both surfaces of the above boards. In addition, a printed wiring board in which a plurality of conductor layers and insulating layers are alternately laminated and having a circuit pattern formed on one side or both sides of the outermost layer of the printed wiring board is also included in the circuit board here. The surface of the conductor layer may be subjected to a roughening process in advance by a blackening process or the like.
積層板を製造する際の成形条件は、例えば、電気絶縁材料用積層板及び多層板の手法が適用でき、例えば多段プレス、多段真空プレス、連続成形、オートクレーブ成形機等を使用し、温度100~250℃、圧力0.2~10MPa、加熱時間0.1~5時間の範囲で成形することができる。また、本発明のプリプレグと内層用配線板とを組合せ、積層成形して、積層板を製造することもできる。 The laminate of the present invention is obtained by laminating the above-described prepreg of the present invention. The prepreg of the present invention can be produced, for example, by laminating 1 to 20 sheets and laminating and forming a metal foil such as copper or aluminum on one or both sides thereof.
As the molding conditions for producing the laminate, for example, a laminate plate for an electrical insulating material and a multilayer plate method can be applied. For example, a multistage press, a multistage vacuum press, continuous molding, an autoclave molding machine, etc. are used, and Molding can be performed at 250 ° C., pressure of 0.2 to 10 MPa, and heating time of 0.1 to 5 hours. Further, the prepreg of the present invention and the inner layer wiring board can be combined and laminated to produce a laminated board.
本発明の多層プリント配線板は、前記積層板を用いて製造される。例えば、本発明の積層板の導体層を通常のエッチング法によって配線加工し回路基板を得ることが出来る。そして、前述のプリプレグを介して配線加工した積層板を複数積層し、加熱プレス加工することによって一括して多層化する。その後、ドリル加工、レーザー加工によるスルーホール又はブラインドビアホールの形成と、メッキ又は導電性ペーストによる層間配線の形成を経て多層プリント配線板を製造することができる。 (Multilayer printed wiring board)
The multilayer printed wiring board of this invention is manufactured using the said laminated board. For example, the circuit board can be obtained by wiring processing the conductor layer of the laminate of the present invention by an ordinary etching method. Then, a plurality of laminated boards processed by wiring through the above-described prepreg are laminated and subjected to hot press processing to be multi-layered at once. Thereafter, a multilayer printed wiring board can be manufactured through formation of a through hole or blind via hole by drilling or laser processing, and formation of an interlayer wiring by plating or conductive paste.
本発明の半導体パッケージは、前記多層プリント配線板に半導体素子を搭載してなるものである。本発明の半導体パッケージは、前記プリント配線板の所定の位置に半導体チップやメモリ等の半導体素子を搭載し製造される。 (Semiconductor package)
The semiconductor package of the present invention is obtained by mounting a semiconductor element on the multilayer printed wiring board. The semiconductor package of the present invention is manufactured by mounting a semiconductor element such as a semiconductor chip or a memory at a predetermined position of the printed wiring board.
なお、各実施例及び比較例で得られた樹脂板を用いて硬化収縮率、ならびに銅張積層板を用いて、ガラス転移温度、熱膨張率、銅箔接着性、銅付きはんだ耐熱性、曲げ弾性率、誘電特性について以下の方法で測定し、評価した。 Next, the present invention will be described in more detail with reference to the following examples, but these examples do not limit the present invention.
In addition, curing shrinkage using the resin plate obtained in each Example and Comparative Example, and using copper-clad laminate, glass transition temperature, coefficient of thermal expansion, copper foil adhesiveness, solder heat resistance with copper, bending The elastic modulus and dielectric properties were measured and evaluated by the following methods.
5mm角の樹脂板(厚さ1mm)を作製し、TMA試験装置(TAインスツルメント社製、Q400)を用いて圧縮法で熱機械分析を行った。樹脂板を前記装置にZ方向に装着後、荷重5g、昇温速度45℃/分とし、20℃(5分保持)~260℃(2分保持)~20℃(5分保持)の温度プロファイルにて測定した。樹脂板の初期寸法と昇温開始前の20℃及び昇温後の20℃での寸法変化量から樹脂板の硬化収縮率を評価した。
具体的には、以下の式を用いて、樹脂板の硬化収縮率を算出した。
硬化収縮率(%)={(昇温開始前20℃の寸法(mm)-昇温後20℃の寸法(mm))/昇温開始前20℃の寸法(mm)}×100 (1) Measurement of cure shrinkage rate of resin plate A 5 mm square resin plate (thickness 1 mm) was prepared, and thermomechanical analysis was performed by a compression method using a TMA test apparatus (TA Instruments, Q400). . After mounting the resin plate in the Z direction on the device, the temperature profile is 20 ° C (5 minutes hold) to 260 ° C (2 minutes hold) to 20 ° C (5 minutes hold) with a load of 5 g and a heating rate of 45 ° C / min. Measured with The cure shrinkage rate of the resin plate was evaluated from the initial dimension of the resin plate and the dimensional change at 20 ° C. before starting the temperature increase and 20 ° C. after the temperature increase.
Specifically, the curing shrinkage rate of the resin plate was calculated using the following formula.
Curing shrinkage rate (%) = {(20 ° C. dimension before starting temperature rise (mm) −20 ° C. dimension after temperature rise (mm)) / 20 ° C. dimension before temperature rise (mm)} × 100
銅張積層板を銅エッチング液に浸漬することにより銅箔を取り除いた5mm角の評価基板を作製し、TMA試験装置(TAインスツルメント社製、Q400)を用いて圧縮法で熱機械分析をおこなった。評価基板を前記装置にZ方向に装着後、荷重5g、昇温速度10℃/分の測定条件にて連続して2回測定した。2回目の測定における熱膨張曲線の異なる接線の交点で示されるTgを求め、耐熱性を評価した。 (2) Measurement of glass transition temperature (Tg) A 5-mm square evaluation board from which copper foil was removed by immersing a copper-clad laminate in a copper etching solution was prepared, and a TMA test apparatus (TA Instruments, Q400) was prepared. ) Was used for thermomechanical analysis by the compression method. After mounting the evaluation substrate on the apparatus in the Z direction, the measurement substrate was measured twice continuously under the measurement conditions of a load of 5 g and a heating rate of 10 ° C./min. The Tg indicated by the intersection of tangents with different thermal expansion curves in the second measurement was determined, and the heat resistance was evaluated.
銅張積層板を銅エッチング液に浸漬することにより銅箔を取り除いた5mm角の評価基板を作製し、TMA試験装置(TAインスツルメント社製、Q400)を用いて圧縮法で熱機械分析をおこなった。評価基板を前記装置にX方向に装着後、荷重5g、昇温速度10℃/分の測定条件にて連続して2回測定した。2回目の測定における30℃から100℃までの平均熱膨張率を算出し、これを熱膨張率の値とした。 (3) Measurement of coefficient of thermal expansion A 5-mm square evaluation board from which copper foil was removed by immersing a copper clad laminate in a copper etching solution was prepared, and a TMA test apparatus (TA Instruments, Q400) was used. The thermomechanical analysis was performed by the compression method. After mounting the evaluation substrate on the apparatus in the X direction, the measurement substrate was measured twice continuously under the measurement conditions of a load of 5 g and a heating rate of 10 ° C./min. The average coefficient of thermal expansion from 30 ° C. to 100 ° C. in the second measurement was calculated and used as the value of the coefficient of thermal expansion.
銅張積層板を銅エッチング液に浸漬することにより3mm幅の銅箔を形成して評価基板を作製し、引張り試験機を用いて銅箔の接着性(ピール強度)を測定した。 (4) Evaluation of copper foil adhesion (copper foil peel strength) A copper-clad laminate is immersed in a copper etching solution to form a copper foil having a width of 3 mm to produce an evaluation substrate, and copper is tested using a tensile tester. The adhesion (peel strength) of the foil was measured.
銅張積層板から25mm角の評価基板を作製し、温度288℃のはんだ浴に、120分間評価基板をフロートし、外観を観察することにより銅付きはんだ耐熱性を評価した。 (5) Evaluation of solder heat resistance with copper Solder heat resistance with copper by preparing a 25 mm square evaluation board from a copper clad laminate, floating the evaluation board in a solder bath at a temperature of 288 ° C. for 120 minutes, and observing the appearance Sex was evaluated.
銅張積層板を銅エッチング液に浸漬することにより銅箔を取り除いた25mm×50mmの評価基板を作製し、オリエンテック社製5トンテンシロンを用い、クロスヘッド速度1mm/min、スパン間距離20mmで測定した。 (6) Flexural modulus A copper-clad laminate was immersed in a copper etching solution to produce a 25 mm × 50 mm evaluation board from which the copper foil was removed, using a 5-ton tensilon manufactured by Orientec Co., Ltd., and a crosshead speed of 1 mm / min. Measured at a span distance of 20 mm.
銅張積層板を銅エッチング液に浸漬することにより銅箔を取り除いた100mm×2mmの評価基板を作製し、空洞共振機装置(株式会社関東電子応用開発製)を用いて、周波数1GHzでの比誘電率及び誘電正接を測定した。 (7) Dielectric properties (dielectric constant and dielectric loss tangent)
A 100 mm × 2 mm evaluation board from which copper foil was removed by immersing a copper clad laminate in a copper etching solution was used, and a cavity resonator device (manufactured by Kanto Electronics Application Development Co., Ltd.) was used to obtain a ratio at a frequency of 1 GHz. The dielectric constant and dielectric loss tangent were measured.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、3,3’-ジメチル-4,4’-ジアミノビフェニル:0.27g、テレフタルアルデヒド:0.33g、X-22-161B:199.4g、プロピレングリコールモノメチルエーテル:300.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(i-1)含有溶液(Mw:30000、樹脂成分:90質量%)を得た。 Production Example 1: Production of Siloxane Compound (i-1) Into a reaction vessel with a volume of 2 liters capable of being heated and cooled, equipped with a thermometer, a stirrer, and a moisture meter with a reflux condenser, 3,3′-dimethyl- 4,4′-diaminobiphenyl: 0.27 g, terephthalaldehyde: 0.33 g, X-22-161B: 199.4 g, propylene glycol monomethyl ether: 300.0 g were added and reacted at 115 ° C. for 4 hours. The mixture was heated to 0 ° C. and dehydrated by atmospheric concentration to obtain a modified siloxane compound (i-1) -containing solution (Mw: 30000, resin component: 90% by mass) having aromatic azomethine.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、4,4'-ジアミノベンズアニリド:0.27g、テレフタルアルデヒド:0.31g、X-22-161B:199.4g、プロピレングリコールモノメチルエーテル:300.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(i
-2)含有溶液(Mw:31000、樹脂成分:90質量%)を得た。 Production Example 2: Production of Siloxane Compound (i-2) 4,4′-Diaminobenze was placed in a reaction vessel with a volume of 2 liters capable of being heated and cooled, equipped with a thermometer, a stirrer, and a moisture meter with a reflux condenser. Anilide: 0.27 g, terephthalaldehyde: 0.31 g, X-22-161B: 199.4 g, propylene glycol monomethyl ether: 300.0 g were added, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. Modified siloxane compound (i) dehydrated by atmospheric concentration and having aromatic azomethine
-2) A contained solution (Mw: 31000, resin component: 90% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、4-アミノフェニル-4’-アミノベンゾエート:0.27g、テレフタルアルデヒド:0.31g、X-22-161B:199.4g、プロピレングリコールモノメチルエーテル:300.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(i-3)含有溶液(Mw:31000、樹脂成分:90質量%)を得
た。 Production Example 3 Production of Siloxane Compound (i-3) 4-aminophenyl-4 ′ was placed in a 2 liter reaction vessel equipped with a thermometer, a stirrer and a moisture meter with a reflux condenser and capable of heating and cooling. -Aminobenzoate: 0.27 g, terephthalaldehyde: 0.31 g, X-22-161B: 199.4 g, propylene glycol monomethyl ether: 300.0 g, reacted at 115 ° C for 4 hours, then heated to 130 ° C Then, it was dehydrated by concentration under normal pressure to obtain a modified siloxane compound (i-3) -containing solution having aromatic azomethine (Mw: 31000, resin component: 90% by mass).
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、4,4’-ジアミノアゾベンゼン:0.27g、テレフタルアルデヒド:0.31g、X-22-161B:199.4g、プロピレングリコールモノメチルエーテル:300.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(i-4)含有溶液(Mw:30000、樹脂成分:90質量%)を得た。 Production Example 4 Production of Siloxane Compound (i-4) 4,4′-Diaminoazobenzene was placed in a reaction vessel having a volume of 2 liters capable of being heated and cooled, equipped with a thermometer, a stirrer, and a moisture meter with a reflux condenser. : 0.27 g, terephthalaldehyde: 0.31 g, X-22-161B: 199.4 g, propylene glycol monomethyl ether: 300.0 g were added, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. Dehydration was performed by pressure concentration to obtain a modified siloxane compound (i-4) -containing solution having aromatic azomethine (Mw: 30000, resin component: 90% by mass).
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、3,3’-ジエチル-4,4’-ジアミノジフェニルメタン:0.18g、テレフタルアルデヒド:0.19g、KF-8012:199.6g、プロピレングリコールモノメチルエーテル:300.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(i-5)含有溶液(Mw:50000、樹脂成分:90質量%)を得た。 Production Example 5: Production of Siloxane Compound (i-5) 3,3′-Diethyl-into a reaction vessel having a thermometer, a stirrer, a moisture meter with a reflux condenser and a heat-coolable volume of 2 liters. 4,4′-diaminodiphenylmethane: 0.18 g, terephthalaldehyde: 0.19 g, KF-8012: 199.6 g, propylene glycol monomethyl ether: 300.0 g were added, reacted at 115 ° C. for 4 hours, and then to 130 ° C. The temperature was raised and dehydration was performed by concentration under atmospheric pressure to obtain a modified siloxane compound (i-5) -containing solution (Mw: 50000, resin component: 90% by mass) having an aromatic azomethine.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、3,3’-ジエチル-4,4’-ジアミノジフェニルメタン:12.9g、テレフタルアルデヒド:17.1g、プロピレングリコールモノメチルエーテル:45.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチン化合物含有溶液(樹脂成分:60質量%)を得た。
次に、上記反応溶液に、X-22-161B:325.5g、プロピレングリコールモノメチルエーテル:513.3gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(ii-1)含有溶液(Mw:30000、樹脂成分:90質量%)を得た。 Production Example 6 Production of Siloxane Compound (ii-1) 3,3′-Diethyl-into a reaction vessel having a thermometer, a stirrer, and a water quantifier equipped with a reflux condenser with a volume of 2 liters capable of heating and cooling. 4,4′-diaminodiphenylmethane: 12.9 g, terephthalaldehyde: 17.1 g, propylene glycol monomethyl ether: 45.0 g were added, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and concentrated at atmospheric pressure. Dehydration gave an aromatic azomethine compound-containing solution (resin component: 60% by mass).
Next, X-22-161B: 325.5 g and propylene glycol monomethyl ether: 513.3 g were added to the above reaction solution, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and dehydrated by normal pressure concentration. Thus, a modified siloxane compound (ii-1) -containing solution having an aromatic azomethine (Mw: 30000, resin component: 90% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、2,5-ジメチル-1,4-ジアミノベンゼン:8.7g、テレフタルアルデヒド:21.3g、プロピレングリコールモノメチルエーテル:45.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチン化合物含有溶液(樹脂成分:60質量%)を得た。
次に、上記反応溶液に、X-22-161B:413.8g、プロピレングリコールモノメチルエーテル:645.7gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(ii-2)含有溶液(Mw:25000樹脂成分:90質量%)を得た。 Production Example 7: Production of siloxane compound (ii-2) 2,5-dimethyl-1 was placed in a 2 liter reaction vessel having a thermometer, a stirrer, and a water quantifier with a reflux condenser and capable of heating and cooling. , 4-diaminobenzene: 8.7 g, terephthalaldehyde: 21.3 g, propylene glycol monomethyl ether: 45.0 g, reacted at 115 ° C. for 4 hours, heated to 130 ° C. and dehydrated by normal pressure concentration An aromatic azomethine compound-containing solution (resin component: 60% by mass) was obtained.
Next, X-22-161B: 413.8 g and propylene glycol monomethyl ether: 645.7 g are added to the above reaction solution, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and dehydrated by normal pressure concentration. Thus, a modified siloxane compound (ii-2) -containing solution having an aromatic azomethine (Mw: 25000 resin component: 90% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、4,4'-ジアミノベンズアニリド:12.1g、テレフタルアルデヒド:17.9g、プロピレングリコールモノメチルエーテル:45.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチン化合物含有溶液(樹脂成分:60質量%)を得た。
次に、上記反応溶液に、X-22-161B:342.1g、プロピレングリコールモノメチルエーテル:538.1gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(ii-3)含有溶液(Mw:31000、樹脂成分:90質量%)を得た。 Production Example 8 Production of Siloxane Compound (ii-3) 4,4′-Diaminobenz was placed in a reaction vessel having a volume of 2 liters capable of being heated and cooled, equipped with a thermometer, a stirrer, and a moisture meter with a reflux condenser. Anilide: 12.1 g, terephthalaldehyde: 17.9 g, propylene glycol monomethyl ether: 45.0 g were added, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and dehydrated by atmospheric concentration, and aromatic azomethine A compound-containing solution (resin component: 60% by mass) was obtained.
Next, X-22-161B: 342.1 g and propylene glycol monomethyl ether: 538.1 g were added to the reaction solution, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and dehydrated by concentration at normal pressure. Thus, a modified siloxane compound (ii-3) -containing solution having an aromatic azomethine (Mw: 31000, resin component: 90% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、4-アミノフェニル-4’-アミノベンゾエート:12.2g、テレフタルアルデヒド:17.9g、プロピレングリコールモノメチルエーテル:45.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチン化合物含有溶液(樹脂成分:60質量%)を得た。
次に、上記反応溶液に、X-22-161B:341.6g、プロピレングリコールモノメチルエーテル:537.3gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(ii-4)含有溶液(Mw:31000、樹脂成分:90質量%)を得た。 Production Example 9 Production of Siloxane Compound (ii-4) In a reaction vessel with a volume of 2 liters that can be heated and cooled, equipped with a thermometer, a stirrer, and a moisture meter with a reflux condenser, 4-aminophenyl-4 ′ -Aminobenzoate: 12.2 g, terephthalaldehyde: 17.9 g, propylene glycol monomethyl ether: 45.0 g, reacted at 115 ° C for 4 hours, heated to 130 ° C, dehydrated by concentration at normal pressure, aroma Group azomethine compound-containing solution (resin component: 60% by mass) was obtained.
Next, X-22-161B: 341.6 g and propylene glycol monomethyl ether: 537.3 g were added to the above reaction solution, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and dehydrated by concentration at normal pressure. Thus, a modified siloxane compound (ii-4) -containing solution having aromatic azomethine (Mw: 31000, resin component: 90% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、4,4’-ジアミノアゾベンゼン:11.6g、テレフタルアルデヒド:18.4g、プロピレングリコールモノメチルエーテル:45.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチン化合物含有溶液(樹脂成分:60質量%)を得た。
次に、上記反応溶液に、X-22-161B:352.1g、プロピレングリコールモノメチルエーテル:553.1gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(ii-5)含有溶液(Mw:30000、樹脂成分:90質量%)を得た。 Production Example 10 Production of Siloxane Compound (ii-5) 4,4′-Diaminoazobenzene was placed in a reaction vessel with a volume of 2 liters capable of being heated and cooled, equipped with a thermometer, a stirrer, and a moisture meter with a reflux condenser. : 11.6 g, terephthalaldehyde: 18.4 g, propylene glycol monomethyl ether: 45.0 g, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and dehydrated by atmospheric concentration, aromatic azomethine compound A containing solution (resin component: 60% by mass) was obtained.
Next, X-22-161B: 352.1 g and propylene glycol monomethyl ether: 553.1 g were added to the reaction solution, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and dehydrated by concentration at normal pressure. Thus, a modified siloxane compound (ii-5) -containing solution having aromatic azomethine (Mw: 30000, resin component: 90% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、テレフタルアルデヒド:5.2g、X-22-161A:24.8g、プロピレングリコールモノメチルエーテル:45.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、アルデヒド基とアゾメチン基を有する変性シロキサン化合物含有溶液(樹脂成分:60質量%)を得た。
次に、上記反応溶液に、ビス(4-(4-アミノフェノキシ)フェニル)プロパン:13.0g、プロピレングリコールモノメチルエーテル:44.4gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(iii-1)含有溶液(Mw:40000、樹脂成分:90質量%)を得た。 Production Example 11 Production of Siloxane Compound (iii-1) In a reaction vessel with a thermometer, a stirrer, a moisture meter with a reflux condenser and a heat-coolable volume of 2 liters, terephthalaldehyde: 5.2 g, X-22-161A: 24.8 g and propylene glycol monomethyl ether: 45.0 g were added and reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and dehydrated by concentration under normal pressure to remove aldehyde groups and azomethine groups. A modified siloxane compound-containing solution (resin component: 60% by mass) was obtained.
Next, bis (4- (4-aminophenoxy) phenyl) propane: 13.0 g and propylene glycol monomethyl ether: 44.4 g were added to the above reaction solution, reacted at 115 ° C. for 4 hours, and then raised to 130 ° C. The mixture was heated and dehydrated by normal pressure concentration to obtain a modified siloxane compound (iii-1) -containing solution (Mw: 40000, resin component: 90% by mass) having an aromatic azomethine.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、テレフタルアルデヒド:3.0g、X-22-161B:27.0g、プロピレングリコールモノメチルエーテル:45.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、アルデヒド基とアゾメチン基を有する変性シロキサン化合物含有溶液(60質量%)を得た。
次に、上記反応溶液に、3,3’-ジエチル-4,4’-ジアミノジフェニルメタン:4.6g、プロピレングリコールモノメチルエーテル:31.9gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(iii-2)含有溶液(Mw:70000、樹脂成分:90質量%)を得た。 Production Example 12: Production of siloxane compound (iii-2) In a reaction vessel with a thermometer, a stirrer, and a moisture meter with a reflux condenser and a heat-coolable volume of 2 liters, terephthalaldehyde: 3.0 g, X-22-161B: 27.0 g and propylene glycol monomethyl ether: 45.0 g were added and reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and dehydrated by concentration under normal pressure to remove aldehyde groups and azomethine groups. A modified siloxane compound-containing solution (60% by mass) was obtained.
Next, 4.6 g of 3,3′-diethyl-4,4′-diaminodiphenylmethane and 31.9 g of propylene glycol monomethyl ether are added to the above reaction solution and reacted at 115 ° C. for 4 hours. The temperature was raised and dehydration was performed by concentration at atmospheric pressure to obtain a modified siloxane compound (iii-2) -containing solution (Mw: 70000, resin component: 90% by mass) having aromatic azomethine.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、テレフタルアルデヒド:3.0g、X-22-161B:27.0g、プロピレングリコールモノメチルエーテル:45.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、アルデヒド基とアゾメチン基を有する変性シロキサン化合物含有溶液(樹脂成分:60質量%)を得た。
次に、上記反応溶液に、4,4'-ジアミノベンズアニリド:4.1g、プロピレングリコールモノメチルエーテル:31.2gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(iii-3)含有溶液(Mw:69000、樹脂成分:90質量%)を得た。 Production Example 13 Production of Siloxane Compound (iii-3) In a reaction vessel with a thermometer, a stirrer, a moisture meter with a reflux condenser and a heat-coolable volume of 2 liters, terephthalaldehyde: 3.0 g, X-22-161B: 27.0 g and propylene glycol monomethyl ether: 45.0 g were added and reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and dehydrated by concentration under normal pressure to remove aldehyde groups and azomethine groups. A modified siloxane compound-containing solution (resin component: 60% by mass) was obtained.
Next, 4.1 g of 4,4′-diaminobenzanilide and 31.2 g of propylene glycol monomethyl ether were added to the reaction solution, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and normal pressure. The solution was dehydrated by concentration to obtain a modified siloxane compound (iii-3) -containing solution having aromatic azomethine (Mw: 69000, resin component: 90% by mass).
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、テレフタルアルデヒド:3.0g、X-22-161B:27.0g、プロピレングリコールモノメチルエーテル:45.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、アルデヒド基とアゾメチン基を有する変性シロキサン化合物含有溶液(樹脂成分:60質量%)を得た。
次に、上記反応溶液に、4-アミノフェニル-4’-アミノベンゾエート:4.5g、プロピレングリコールモノメチルエーテル:31.2gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(iii-4)含有溶液(Mw:69000、樹脂成分:90質量%)を得た。 Production Example 14 Production of Siloxane Compound (iii-4) In a reaction vessel with a thermometer, a stirrer, a moisture meter with a reflux condenser and a heat-coolable volume of 2 liters, terephthalaldehyde: 3.0 g, X-22-161B: 27.0 g and propylene glycol monomethyl ether: 45.0 g were added and reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and dehydrated by concentration under normal pressure to remove aldehyde groups and azomethine groups. A modified siloxane compound-containing solution (resin component: 60% by mass) was obtained.
Next, 4-aminophenyl-4′-aminobenzoate: 4.5 g and propylene glycol monomethyl ether: 31.2 g were added to the above reaction solution, reacted at 115 ° C. for 4 hours, and then heated to 130 ° C. Dehydration was performed by concentration under normal pressure to obtain a modified siloxane compound (iii-4) -containing solution having aromatic azomethine (Mw: 69000, resin component: 90% by mass).
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、テレフタルアルデヒド:3.0g、X-22-161B:27.0g、プロピレングリコールモノメチルエーテル:45.0gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、アルデヒド基とアゾメチン基を有する変性シロキサン化合物含有溶液(樹脂成分:60質量%)を得た。
次に、上記反応溶液に、4,4’-ジアミノアゾベンゼン:3.9g、プロピレングリコールモノメチルエーテル:30.8gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮により脱水し、芳香族アゾメチンを有する変性シロキサン化合物(iii-5)含有溶液(Mw:68000、樹脂成分:90質量%)を得た。 Production Example 15 Production of Siloxane Compound (iii-5) In a reaction vessel with a thermometer, a stirrer, a moisture meter with a reflux condenser and a heat-coolable volume of 2 liters, terephthalaldehyde: 3.0 g, X-22-161B: 27.0 g and propylene glycol monomethyl ether: 45.0 g were added and reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and dehydrated by concentration under normal pressure to remove aldehyde groups and azomethine groups. A modified siloxane compound-containing solution (resin component: 60% by mass) was obtained.
Next, 3.9 g of 4,4′-diaminoazobenzene and 30.8 g of propylene glycol monomethyl ether are added to the above reaction solution, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and concentrated at normal pressure. To obtain a modified siloxane compound (iii-5) -containing solution having aromatic azomethine (Mw: 68000, resin component: 90% by mass).
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、芳香族アゾメチンを有する変性シロキサン化合物(i-1)含有溶液(樹脂成分:90質量%):62.4g、2,2-ビス(4-(4-マレイミドフェノキシ)フェニル)プロパン:243.9g、プロピレングリコールモノメチルエーテル:443.8gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮し、芳香族アゾメチンを有する変性イミド樹脂(j-1)含有溶液(樹脂成分:60質量%)を得た。 Production Example 16 Production of Modified Imide Resin (j-1) Having Aromatic Azomethine In a reaction vessel with a volume of 2 liters capable of being heated and cooled, equipped with a thermometer, a stirrer, and a moisture meter with a reflux condenser, Modified siloxane compound (i-1) -containing solution having a group azomethine (resin component: 90% by mass): 62.4 g, 2,2-bis (4- (4-maleimidophenoxy) phenyl) propane: 243.9 g, propylene 443.8 g of glycol monomethyl ether was added, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and concentrated at normal pressure, and a modified imide resin (j-1) -containing solution containing aromatic azomethine (resin component: 60% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、芳香族アゾメチンを有する変性シロキサン化合物(i-2)含有
溶液(樹脂成分:90質量%):62.5g、2,2-ビス(4-(4-マレイミドフェノキシ)フェニル)プロパン:243.8g、プロピレングリコールモノメチルエーテル:443.8gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮し、芳香族アゾメチンを有する変性イミド樹脂(j-2)含有溶液(樹脂成分:60質量%)を得た。 Production Example 17: Production of Modified Imide Resin (j-2) Having Aromatic Azomethine Into a reaction vessel having a volume of 2 liters capable of being heated and cooled, equipped with a thermometer, a stirrer, and a moisture meter with a reflux condenser, Modified siloxane compound (i-2) -containing solution having a group azomethine (resin component: 90% by mass): 62.5 g, 2,2-bis (4- (4-maleimidophenoxy) phenyl) propane: 243.8 g, propylene 443.8 g of glycol monomethyl ether was added, reacted at 115 ° C. for 4 hours, heated to 130 ° C. and concentrated at normal pressure, and a modified imide resin (j-2) -containing solution containing aromatic azomethine (resin component: 60% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、芳香族アゾメチンを有する変性シロキサン化合物(ii-1)含有溶液(樹脂成分:90質量%):62.5g、2,2-ビス(4-(4-マレイミドフェノキシ)フェニル)プロパン:243.7g、プロピレングリコールモノメチルエーテル:443.8gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮し、芳香族アゾメチンを有する変性イミド樹脂(j-3)含有溶液(樹脂成分:60質量%)を得た。 Production Example 18 Production of Modified Imide Resin (j-3) Having Aromatic Azomethine In a reaction vessel with a volume of 2 liters capable of being heated and cooled, equipped with a thermometer, a stirrer, and a moisture meter with a reflux condenser, Modified siloxane compound (ii-1) -containing solution having a group azomethine (resin component: 90% by mass): 62.5 g, 2,2-bis (4- (4-maleimidophenoxy) phenyl) propane: 243.7 g, propylene 443.8 g of glycol monomethyl ether was added, reacted at 115 ° C. for 4 hours, heated to 130 ° C. and concentrated at normal pressure, and a modified imide resin (j-3) -containing solution containing aromatic azomethine (resin component: 60% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、芳香族アゾメチンを有する変性シロキサン化合物(ii-3)含有溶液(樹脂成分:90質量%):62.3g、2,2-ビス(4-(4-マレイミドフェノキシ)フェニル)プロパン:243.9g、プロピレングリコールモノメチルエーテル:443.8gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮し、芳香族アゾメチンを有する変性イミド樹脂(j-4)含有溶液(樹脂成分:60質量%)を得た。 Production Example 19 Production of Modified Imide Resin (j-4) Having Aromatic Azomethine In a reaction vessel with a volume of 2 liters capable of being heated and cooled, equipped with a thermometer, a stirrer, and a moisture meter with a reflux condenser, Modified siloxane compound (ii-3) -containing solution having a group azomethine (resin component: 90% by mass): 62.3 g, 2,2-bis (4- (4-maleimidophenoxy) phenyl) propane: 243.9 g, propylene 443.8 g of glycol monomethyl ether was added, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and concentrated at normal pressure, and a modified imide resin (j-4) -containing solution containing aromatic azomethine (resin component: 60% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、芳香族アゾメチンを有する変性シロキサン化合物(iii-2)含有溶液(樹脂成分:90質量%):62.5g、2,2-ビス(4-(4-マレイミドフェノキシ)フェニル)プロパン:243.8g、プロピレングリコールモノメチルエーテル:443.8gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮し、芳香族アゾメチンを有する変性イミド樹脂(j-5)含有溶液(樹脂成分:60質量%)を得た。 Production Example 20 Production of Modified Imide Resin (j-5) Having Aromatic Azomethine Into a reaction vessel having a volume of 2 liters capable of being heated and cooled, equipped with a thermometer, a stirrer, and a moisture meter with a reflux condenser, Modified siloxane compound (iii-2) -containing solution having a group azomethine (resin component: 90% by mass): 62.5 g, 2,2-bis (4- (4-maleimidophenoxy) phenyl) propane: 243.8 g, propylene 443.8 g of glycol monomethyl ether was added, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and concentrated at normal pressure, and a modified imide resin (j-5) -containing solution containing aromatic azomethine (resin component: 60% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、芳香族アゾメチンを有する変性シロキサン化合物(iii-3)含有溶液(樹脂成分:90質量%):61.7g、2,2-ビス(4-(4-マレイミドフェノキシ)フェニル)プロパン:244.4g、プロピレングリコールモノメチルエーテル:443.8gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮し、芳香族アゾメチンを有する変性イミド樹脂(j-6)含有溶液(樹脂成分:60質量%)を得た。 Production Example 21 Production of Modified Imide Resin (j-6) Having Aromatic Azomethine Into a reaction vessel with a volume of 2 liters capable of being heated and cooled, equipped with a thermometer, a stirrer, and a moisture meter with a reflux condenser, Modified siloxane compound (iii-3) -containing solution having a group azomethine (resin component: 90% by mass): 61.7 g, 2,2-bis (4- (4-maleimidophenoxy) phenyl) propane: 244.4 g, propylene 443.8 g of glycol monomethyl ether was added, reacted at 115 ° C. for 4 hours, heated to 130 ° C. and concentrated at normal pressure, and a modified imide resin (j-6) -containing solution containing aromatic azomethine (resin component: 60% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、芳香族アゾメチンを有する変性シロキサン化合物(i-1)含有溶液(樹脂成分:90質量%):62.5g、2,2-ビス(4-(4-マレイミドフェノキシ)フェニル)プロパン:238.1g、p-アミノフェノール:5.7g、プロピレングリコールモノメチルエーテル:443.8gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮し、酸性置換基と芳香族アゾメチンを有する変性イミド樹脂(k-1)含有溶液(樹脂成分:60質量%)を得た。 Production Example 22 Production of Modified Imide Resin (k-1) Having Acid Substituent and Aromatic Azomethine Reaction of 2 liters in volume capable of heating and cooling with thermometer, stirrer, moisture meter with reflux condenser In a container, a modified siloxane compound (i-1) -containing solution having an aromatic azomethine (resin component: 90% by mass): 62.5 g, 2,2-bis (4- (4-maleimidophenoxy) phenyl) propane: 238 0.1 g, p-aminophenol: 5.7 g, and propylene glycol monomethyl ether: 443.8 g, reacted at 115 ° C. for 4 hours, heated to 130 ° C. and concentrated at normal pressure, acidic substituent and aromatic A modified imide resin (k-1) -containing solution having azomethine (resin component: 60% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、芳香族アゾメチンを有する変性シロキサン化合物(i-2)含有溶液(樹脂成分:90質量%):62.6g、2,2-ビス(4-(4-マレイミドフェノキシ)フェニル)プロパン:238.0g、p-アミノフェノール:5.7g、プロピレングリコールモノメチルエーテル:443.7gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮し、酸性置換基と芳香族アゾメチンを有する変性イミド樹脂(k-2)含有溶液(樹脂成分:60質量%)を得た。 Production Example 23 Production of Modified Imide Resin (k-2) Having Acid Substituent and Aromatic Azomethine Reaction with a volume of 2 liters capable of being heated and cooled with a thermometer, a stirrer, and a moisture meter with a reflux condenser In a container, a modified siloxane compound (i-2) -containing solution having an aromatic azomethine (resin component: 90% by mass): 62.6 g, 2,2-bis (4- (4-maleimidophenoxy) phenyl) propane: 238 0.0 g, p-aminophenol: 5.7 g, and propylene glycol monomethyl ether: 443.7 g, reacted at 115 ° C. for 4 hours, heated to 130 ° C. and concentrated at normal pressure, acid substituent and aromatic A modified imide resin (k-2) -containing solution (resin component: 60% by mass) having azomethine was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、芳香族アゾメチンを有する変性シロキサン化合物(ii-1)含有溶液(樹脂成分:90質量%):62.5g、2,2-ビス(4-(4-マレイミドフェノキシ)フェニル)プロパン:238.0g、p-アミノフェノール:5.7g、プロピレングリコールモノメチルエーテル:443.8gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮し、酸性置換基と芳香族アゾメチンを有する変性イミド樹脂(k-3)含有溶液(樹脂成分:60質量%)を得た。 Production Example 24 Production of Modified Imide Resin (k-3) Having Acid Substituent and Aromatic Azomethine Reaction of 2 liters capable of heating and cooling with thermometer, stirrer, moisture meter with reflux condenser In a container, a solution containing a modified siloxane compound (ii-1) having an aromatic azomethine (resin component: 90% by mass): 62.5 g, 2,2-bis (4- (4-maleimidophenoxy) phenyl) propane: 238 0.0 g, p-aminophenol: 5.7 g, and propylene glycol monomethyl ether: 443.8 g, reacted at 115 ° C. for 4 hours, heated to 130 ° C. and concentrated at normal pressure, acid substituent and aromatic A modified imide resin (k-3) -containing solution having azomethine (resin component: 60% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、芳香族アゾメチンを有する変性シロキサン化合物(ii-3)含有溶液(樹脂成分:90質量%):62.3g、2,2-ビス(4-(4-マレイミドフェノキシ)フェニル)プロパン:238.2g、p-アミノフェノール:5.7g、プロピレングリコールモノメチルエーテル:443.8gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮し、酸性置換基と芳香族アゾメチンを有する変性イミド樹脂(k-4)含有溶液(樹脂成分:60質量%)を得た。 Production Example 25: Production of Modified Imide Resin (k-4) Having Acid Substituent and Aromatic Azomethine Reaction of 2 liters capable of heating and cooling with thermometer, stirrer, moisture meter with reflux condenser In a container, a modified siloxane compound (ii-3) -containing solution having an aromatic azomethine (resin component: 90% by mass): 62.3 g, 2,2-bis (4- (4-maleimidophenoxy) phenyl) propane: 238 .2 g, p-aminophenol: 5.7 g, propylene glycol monomethyl ether: 443.8 g, reacted at 115 ° C. for 4 hours, heated to 130 ° C. and concentrated at normal pressure, acid substituent and aromatic A modified imide resin (k-4) -containing solution having azomethine (resin component: 60% by mass) was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、芳香族アゾメチンを有する変性シロキサン化合物(iii-2)含有溶液(樹脂成分:90質量%):62.6g、2,2-ビス(4-(4-マレイミドフェノキシ)フェニル)プロパン:238.0g、p-アミノフェノール:5.7g、プロピレングリコールモノメチルエーテル:443.7gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮し、酸性置換基と芳香族アゾメチンを有する変性イミド樹脂(k-5)含有溶液(樹脂成分:60質量%)を得た。 Production Example 26 Production of Modified Imide Resin (k-5) Having Acid Substituent and Aromatic Azomethine Reaction of 2 liters capable of heating and cooling with thermometer, stirrer, moisture meter with reflux condenser In a container, a solution containing a modified siloxane compound (iii-2) having an aromatic azomethine (resin component: 90% by mass): 62.6 g, 2,2-bis (4- (4-maleimidophenoxy) phenyl) propane: 238 0.0 g, p-aminophenol: 5.7 g, and propylene glycol monomethyl ether: 443.7 g, reacted at 115 ° C. for 4 hours, then heated to 130 ° C. and concentrated at normal pressure, acid substituent and aromatic A modified imide resin (k-5) -containing solution (resin component: 60% by mass) having azomethine was obtained.
温度計、攪拌装置、還流冷却管付き水分定量器の付いた加熱及び冷却可能な容積2リットルの反応容器に、芳香族アゾメチンを有する変性シロキサン化合物(iii-3)含有溶液(樹脂成分:90質量%):61.8g、2,2-ビス(4-(4-マレイミドフェノキシ)フェニル)プロパン:238.6g、p-アミノフェノール:5.7g、プロピレングリコールモノメチルエーテル:443.8gを入れ、115℃で4時間反応した後、130℃まで昇温して常圧濃縮し、酸性置換基と芳香族アゾメチンを有する変性イミド樹脂(k-6)含有溶液(樹脂成分:60質量%)を得た。 Production Example 27 Production of Modified Imide Resin (k-6) Having Acid Substituent and Aromatic Azomethine Reaction of 2 liters capable of heating and cooling with thermometer, stirrer, moisture meter with reflux condenser In a container, a modified siloxane compound (iii-3) -containing solution having aromatic azomethine (iii-3) -containing solution (resin component: 90% by mass): 61.8 g, 2,2-bis (4- (4-maleimidophenoxy) phenyl) propane: 238 .6 g, p-aminophenol: 5.7 g, and propylene glycol monomethyl ether: 443.8 g, reacted at 115 ° C. for 4 hours, heated to 130 ° C. and concentrated at normal pressure, acid substituent and aromatic A modified imide resin (k-6) -containing solution containing azomethine (resin component: 60% by mass) was obtained.
製造実施例1~15で得られた芳香族アゾメチンを有する変性シロキサン化合物(i-1~i-5、ii-1~ii-5、iii-1~iii-5)含有溶液、製造実施例16~21で得られた芳香族アゾメチンを有する変性イミド樹脂(j-1~j-6)含有溶液、及び製造実施例22~27で得られた酸性置換基と芳香族アゾメチンを有する変性イミド樹脂含有溶液と、以下に示す芳香族アミン化合物(A)、芳香族アルデヒド化合物(B)、シロキサン化合物(C)、マレイミド化合物(D)、酸性置換基を有するアミン化合物(E)、熱可塑性エラストマー(F)、熱硬化性樹脂(G)、無機充填材(H)、硬化促進剤(I)、及び希釈溶剤にメチルエチルケトンを使用して、第1表~第9表に示した配合割合(質量部)で混合して樹脂分65質量%のワニスを得た。 Examples 1 to 39 and Comparative Examples 1 to 12
Solutions containing the modified siloxane compounds (i-1 to i-5, ii-1 to ii-5, iii-1 to iii-5) having aromatic azomethine obtained in Production Examples 1 to 15, Production Example 16 Modified imide resin (j-1 to j-6) containing aromatic azomethine obtained in ~ 21 and modified imide resin containing acidic substituent and aromatic azomethine obtained in Production Examples 22 ~ 27 Solution, aromatic amine compound (A), aromatic aldehyde compound (B), siloxane compound (C), maleimide compound (D), amine compound (E) having an acidic substituent, thermoplastic elastomer (F ), Thermosetting resin (G), inorganic filler (H), curing accelerator (I), and methyl ethyl ketone as diluent solvent, and the blending ratios (parts by mass) shown in Tables 1 to 9 Mixed with To obtain a fat content of 65% by weight of the varnish.
また,上記ワニスを厚さ0.1mmのEガラスクロスに含浸塗工し,160℃で10分加熱乾燥して樹脂含有量48質量%のプリプレグを得た。
このプリプレグを4枚重ね,12μmの電解銅箔を上下に配置し,圧力3.0MPa、温度240℃で60分間プレスを行って,銅張積層板を得た。
得られた樹脂板及び銅張積層板の測定、評価結果を第1表~第9表に示す。 This resin powder was put into a mold of a Teflon (registered trademark) sheet, the glossy surface of 12 μm electrolytic copper foil was placed up and down, and pressed at a pressure of 2.0 MPa and a temperature of 240 ° C. for 60 minutes. The foil was removed to obtain a resin plate.
The varnish was impregnated with 0.1 mm thick E glass cloth and dried by heating at 160 ° C. for 10 minutes to obtain a prepreg having a resin content of 48 mass%.
Four prepregs were stacked, 12 μm electrolytic copper foils were placed one above the other, and pressed at a pressure of 3.0 MPa and a temperature of 240 ° C. for 60 minutes to obtain a copper-clad laminate.
Tables 1 to 9 show the measurement and evaluation results of the obtained resin plates and copper-clad laminates.
・KAYAHARD A-A:3,3’-ジエチル-4,4’-ジアミノジフェニルメタン〔日本化薬株式会社製、商品名〕
・4,4'-ジアミノベンズアニリド〔東京化成工業株式会社製、商品名〕
・4-アミノフェニル-4’-アミノベンゾエート〔常州市陽光薬業有限公司製、商品名〕 Aromatic amine compound (A)
KAYAHARD AA: 3,3′-diethyl-4,4′-diaminodiphenylmethane [manufactured by Nippon Kayaku Co., Ltd., trade name]
・ 4,4'-Diaminobenzanilide (trade name, manufactured by Tokyo Chemical Industry Co., Ltd.)
・ 4-Aminophenyl-4'-aminobenzoate (Changzhou Yoko Pharmaceutical Co., Ltd., trade name)
・TPAL:テレフタルアルデヒド〔東レ・ファインケミカル株式会社製、商品名〕 Aromatic aldehyde compound (B)
・ TPAL: terephthalaldehyde (trade name, manufactured by Toray Fine Chemical Co., Ltd.)
・X-22-161B:両末端アミノ変性シロキサン〔信越化学工業株式会社製、商品名〕 Siloxane compound (C)
X-22-161B: Amino-modified siloxane at both ends (trade name, manufactured by Shin-Etsu Chemical Co., Ltd.)
・BMI:ビス(4-マレイミドフェニル)メタン〔ケイ・アイ化成株式会社製、商品名〕
・BMI-4000:2,2-ビス(4-(4-マレイミドフェノキシ)フェニル)プロパン〔大和化成工業株式会社製、商品名〕 Maleimide compound (D)
・ BMI: Bis (4-maleimidophenyl) methane (trade name, manufactured by Kay Kasei Co., Ltd.)
BMI-4000: 2,2-bis (4- (4-maleimidophenoxy) phenyl) propane (trade name, manufactured by Daiwa Kasei Kogyo Co., Ltd.)
・p-アミノフェノール〔関東化学株式会社製、商品名〕 Amine compound having acidic substituent (E)
・ P-Aminophenol (trade name, manufactured by Kanto Chemical Co., Inc.)
・タフテックH1043:水添スチレン-ブタジエン共重合樹脂〔旭化成ケミカルズ株式会社製、商品名〕
・エポフレンドCT-310:エポキシ変性スチレン-ブタジエン共重合樹脂〔株式会社ダイセル製、商品名〕 Thermoplastic elastomer (F)
・ Tuftec H1043: Hydrogenated styrene-butadiene copolymer resin (trade name, manufactured by Asahi Kasei Chemicals Corporation)
・ Epofriend CT-310: Epoxy-modified styrene-butadiene copolymer resin (trade name, manufactured by Daicel Corporation)
・PT-30:ノボラック型シアネート樹脂〔ロンザジャパン株式会社製、商品名〕
・NC-7000L:α-ナフトール/クレゾールノボラック型エポキシ樹脂〔日本化薬株式会社製、商品名〕 Thermosetting resin (G)
PT-30: Novolac-type cyanate resin (Lonza Japan Co., Ltd., trade name)
NC-7000L: α-naphthol / cresol novolac type epoxy resin (trade name, manufactured by Nippon Kayaku Co., Ltd.)
・SC2050-KNK:溶融シリカ〔株式会社アドマテックス製、商品名〕
・モリブデン酸亜鉛〔シャーウィン・ウィリアムズ社製、商品名:KEMGARD1100〕 Inorganic filler (H)
SC2050-KNK: fused silica [manufactured by Admatechs, product name]
・ Zinc molybdate [manufactured by Sherwin Williams, trade name: KEMGARD1100]
・ナフテン酸亜鉛(II)8%ミネラルスピリット溶液〔東京化成工業株式会社製、商品名〕
・G-8009L:イソシアネートマスクイミダゾール〔第一工業製薬株式会社製、商品名〕
・TPP-MK:テトラフェニルホスホニウムテトラ-p-トリルボレート〔北興化学工業株式会社製、商品名〕 Curing accelerator (I)
・ Zinc (II) naphthenate 8% mineral spirit solution [Tokyo Chemical Industry Co., Ltd., trade name]
G-8809L: Isocyanate mask imidazole [Daiichi Kogyo Seiyaku Co., Ltd., trade name]
TPP-MK: Tetraphenylphosphonium tetra-p-tolylborate [made by Hokuko Chemical Co., Ltd., trade name]
メチンを有する変性イミド樹脂(j-1)~(j-6)含有溶液、及び酸性置換基と芳香族アゾメチンを有する変性イミド樹脂(k-1)~(k-6)含有溶液の配合量(質量部)は、樹脂成分の固形分換算の値を示すものである。 Hereinafter, solutions containing siloxane compounds (i-1) to (iii-5) in Tables 1 to 4, solutions containing modified imide resins (j-1) to (j-6) having aromatic azomethine, and acidic substituents The blending amount (part by mass) of the solution containing the modified imide resins (k-1) to (k-6) having an aromatic azomethine indicates a value in terms of solid content of the resin component.
一方、比較例は、樹脂板の硬化収縮率が大きく、また、積層板の特性においても、熱膨張率、銅箔接着性、弾性率、誘電特性において実施例と比較し、いずれかの特性に劣っている。 As is apparent from Tables 1 to 9, in the examples of the present invention, the curing shrinkage rate of the resin plate is small and excellent in low cure shrinkage. Also in the characteristics of the laminated plate, the thermal expansion rate, the copper foil Excellent adhesion, elastic modulus and dielectric properties.
On the other hand, the comparative example has a large curing shrinkage rate of the resin plate, and also in the characteristics of the laminated plate, the thermal expansion coefficient, the copper foil adhesiveness, the elastic modulus, and the dielectric characteristics are any of the characteristics. Inferior.
Claims (19)
- 下記一般式(1)及び下記一般式(2)に示す構造を含むシロキサン化合物。
- さらに、芳香族アゾメチンを含む請求項1に記載のシロキサン化合物。 Furthermore, the siloxane compound of Claim 1 containing aromatic azomethine.
- 1分子中に少なくとも2個の1級アミノ基を有する芳香族アミン化合物(A)、1分子中に少なくとも2個のアルデヒド基を有する芳香族アルデヒド化合物(B)、分子末端に少なくとも2個のアミノ基を有するシロキサン化合物(C)を反応させ得られる、請求項2に記載のシロキサン化合物。 An aromatic amine compound (A) having at least two primary amino groups in one molecule, an aromatic aldehyde compound (B) having at least two aldehyde groups in one molecule, and at least two amino compounds at the molecular terminals The siloxane compound according to claim 2, which is obtained by reacting a siloxane compound (C) having a group.
- 1分子中に少なくとも2個の1級アミノ基を有する芳香族アミン化合物(A)、1分子中に少なくとも2個のアルデヒド基を有する芳香族アルデヒド化合物(B)、を反応後、分子末端に少なくとも2個のアミノ基を有するシロキサン化合物(C)を反応させ得られる、請求項2に記載のシロキサン化合物。 After reacting the aromatic amine compound (A) having at least two primary amino groups in one molecule and the aromatic aldehyde compound (B) having at least two aldehyde groups in one molecule, at least at the molecular terminal The siloxane compound according to claim 2, which can be obtained by reacting a siloxane compound (C) having two amino groups.
- 1分子中に少なくとも2個のアルデヒド基を有する芳香族アルデヒド化合物(B)、分子末端に少なくとも2個のアミノ基を有するシロキサン化合物(C)を反応後、1分子中に少なくとも2個の1級アミノ基を有する芳香族アミン化合物(A)を反応させて得られる、請求項2に記載のシロキサン化合物。 After reacting an aromatic aldehyde compound (B) having at least two aldehyde groups in one molecule and a siloxane compound (C) having at least two amino groups at the molecular ends, at least two primary compounds in one molecule The siloxane compound according to claim 2, obtained by reacting an aromatic amine compound (A) having an amino group.
- 請求項1~5のいずれか1項に記載のシロキサン化合物と、1分子中に少なくとも2個のN-置換マレイミド基を有するマレイミド化合物(D)とを反応させて得られる、芳香族アゾメチンを有する変性イミド樹脂。 An aromatic azomethine obtained by reacting the siloxane compound according to any one of claims 1 to 5 with a maleimide compound (D) having at least two N-substituted maleimide groups in one molecule. Modified imide resin.
- さらに、酸性置換基を有し、該酸性置換基が下記一般式(3)に示すアミン化合物(E)の酸性置換基に由来する請求項6に記載の変性イミド樹脂。
- 請求項1~5のいずれか1項に記載のシロキサン化合物と、1分子中に少なくとも2個のN-置換マレイミド基を有するマレイミド化合物(D)とを含有する熱硬化性樹脂組成物。 A thermosetting resin composition comprising the siloxane compound according to any one of claims 1 to 5 and a maleimide compound (D) having at least two N-substituted maleimide groups in one molecule.
- さらに、下記一般式(3)に示す酸性置換基を有するアミン化合物(E)を含有する請求項8に記載の熱硬化性樹脂組成物。
- さらに、熱可塑性エラストマー(F)を含有する請求項8又は9に記載の熱硬化性樹脂組成物。 Furthermore, the thermosetting resin composition of Claim 8 or 9 containing a thermoplastic elastomer (F).
- さらに、エポキシ樹脂及びシアネート樹脂から選ばれた少なくとも一種の熱硬化性樹脂(G)を含有する請求項8~10のいずれか1項に記載の熱硬化性樹脂組成物。 The thermosetting resin composition according to any one of claims 8 to 10, further comprising at least one thermosetting resin (G) selected from an epoxy resin and a cyanate resin.
- さらに、無機充填材(H)を含有する請求項8~11のいずれか1項に記載の熱硬化性樹脂組成物。 The thermosetting resin composition according to any one of claims 8 to 11, further comprising an inorganic filler (H).
- さらに、硬化促進剤(I)を含有する請求項8~12のいずれか1項に記載の熱硬化性樹脂組成物。 The thermosetting resin composition according to any one of claims 8 to 12, further comprising a curing accelerator (I).
- 請求項8~13のいずれか1項に記載の熱硬化性樹脂組成物を基材に含浸してなるプリプレグ。 A prepreg obtained by impregnating a base material with the thermosetting resin composition according to any one of claims 8 to 13.
- 請求項8~13のいずれか1項に記載の熱硬化性樹脂組成物を支持体上に層形成してなる樹脂付フィルム。 A film with a resin, wherein the thermosetting resin composition according to any one of claims 8 to 13 is layered on a support.
- 請求項14記載のプリプレグを積層成形し得られる積層板。 A laminate obtained by laminating the prepreg according to claim 14.
- 請求項15記載の樹脂付フィルムを積層成形して得られる積層板。 A laminate obtained by laminating the film with resin according to claim 15.
- 請求項16又は17記載の積層板を用いて製造される多層プリント配線板。 A multilayer printed wiring board manufactured using the laminated board according to claim 16 or 17.
- 請求項18記載の多層プリント配線板に半導体素子を搭載してなる半導体パッケージ。 A semiconductor package comprising a semiconductor element mounted on the multilayer printed wiring board according to claim 18.