WO2014081089A1 - Procédé de traitement de surface d'articles métalliques - Google Patents

Procédé de traitement de surface d'articles métalliques Download PDF

Info

Publication number
WO2014081089A1
WO2014081089A1 PCT/KR2013/002837 KR2013002837W WO2014081089A1 WO 2014081089 A1 WO2014081089 A1 WO 2014081089A1 KR 2013002837 W KR2013002837 W KR 2013002837W WO 2014081089 A1 WO2014081089 A1 WO 2014081089A1
Authority
WO
WIPO (PCT)
Prior art keywords
metal product
oxide film
film layer
washing
product
Prior art date
Application number
PCT/KR2013/002837
Other languages
English (en)
Korean (ko)
Inventor
윤주식
유재인
Original Assignee
주식회사 위스코하이텍
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from KR1020120134267A external-priority patent/KR101401365B1/ko
Priority claimed from KR1020120144595A external-priority patent/KR101401366B1/ko
Priority claimed from KR1020120147341A external-priority patent/KR101401363B1/ko
Priority claimed from KR1020130001449A external-priority patent/KR101461070B1/ko
Priority claimed from JP2013061656A external-priority patent/JP5657728B2/ja
Application filed by 주식회사 위스코하이텍 filed Critical 주식회사 위스코하이텍
Publication of WO2014081089A1 publication Critical patent/WO2014081089A1/fr

Abstract

La présente invention se rapporte à un procédé de traitement de surface d'articles métalliques, ledit procédé consistant à : éliminer des huiles de la surface d'un article métallique ; enlever et neutraliser un matériau pour enlever les huiles de la surface de l'article métallique ; et traiter la surface de l'article métallique lavé, le procédé permettant de traitement de surface d'un article métallique comprenant les étapes consistant à : pulvériser une solution, une solution de traitement de surface, ou un alcool, étant pulvérisée sur la surface de l'article métallique lavé et la solution de traitement de surface étant préparée par mélange de l'eau soit avec de l'éthanol (C2H5OH), soit avec de l'acétone (CH3COCH3) ; et produire une couche pelliculaire oxydée, une couche pelliculaire oxydée étant formée sur la surface de l'article métallique par combustion ou semi-combustion de l'article métallique traité au cours de l'étape de pulvérisation d'une solution. En outre, la solution de traitement de surface est préparée par mélange de l'éthanol (C2H5OH), de l'acétone (CH3COCH3) et d'eau, l'éthanol étant mélangé dans un volume faisant entre 1 et 50 fois le volume d'eau et l'acétone étant mélangé dans un volume faisant entre 0,05 et 1 fois le volume d'éthanol.
PCT/KR2013/002837 2012-11-26 2013-04-05 Procédé de traitement de surface d'articles métalliques WO2014081089A1 (fr)

Applications Claiming Priority (10)

Application Number Priority Date Filing Date Title
KR1020120134267A KR101401365B1 (ko) 2012-11-26 2012-11-26 표면 광택을 가진 마그네슘합금 제품의 표면처리방법
KR10-2012-0134267 2012-11-26
KR1020120144595A KR101401366B1 (ko) 2012-12-12 2012-12-12 마그네슘합금 제품의 표면코팅방법
KR10-2012-0144595 2012-12-12
KR10-2012-0147341 2012-12-17
KR1020120147341A KR101401363B1 (ko) 2012-12-17 2012-12-17 마그네슘합금 제품의 표면도장방법
KR10-2013-0001449 2013-01-07
KR1020130001449A KR101461070B1 (ko) 2013-01-07 2013-01-07 금속 제품의 표면처리방법
JP2013061656A JP5657728B2 (ja) 2012-11-26 2013-03-25 表面処理方法
JP2013-061656 2013-03-25

Publications (1)

Publication Number Publication Date
WO2014081089A1 true WO2014081089A1 (fr) 2014-05-30

Family

ID=50776243

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2013/002837 WO2014081089A1 (fr) 2012-11-26 2013-04-05 Procédé de traitement de surface d'articles métalliques

Country Status (1)

Country Link
WO (1) WO2014081089A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108117050A (zh) * 2017-11-21 2018-06-05 青岛国林环保科技股份有限公司 一种用于臭氧发生器的高压电极及其制造方法和应用
CN113136577A (zh) * 2021-04-06 2021-07-20 南通海高数控机械有限公司 一种c型钢自动化防锈处理生产线

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000345370A (ja) * 1999-06-07 2000-12-12 Ueda Alumite Kogyo Kk マグネシウム又はマグネシウム合金の表面処理方法
JP2006063392A (ja) * 2004-08-26 2006-03-09 Seiko Epson Corp 酸化膜形成方法、酸化膜、部品および電子機器
JP2007302922A (ja) * 2006-05-09 2007-11-22 Yazaki Corp マグネシウム部材の表面処理方法
KR20090012640A (ko) * 2007-07-31 2009-02-04 (주) 태양기전 마그네슘 제품의 표면처리방법
KR20110025384A (ko) * 2009-09-04 2011-03-10 주식회사 위스코하이텍 마그네슘합금 제품의 직화식 표면처리방법

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000345370A (ja) * 1999-06-07 2000-12-12 Ueda Alumite Kogyo Kk マグネシウム又はマグネシウム合金の表面処理方法
JP2006063392A (ja) * 2004-08-26 2006-03-09 Seiko Epson Corp 酸化膜形成方法、酸化膜、部品および電子機器
JP2007302922A (ja) * 2006-05-09 2007-11-22 Yazaki Corp マグネシウム部材の表面処理方法
KR20090012640A (ko) * 2007-07-31 2009-02-04 (주) 태양기전 마그네슘 제품의 표면처리방법
KR20110025384A (ko) * 2009-09-04 2011-03-10 주식회사 위스코하이텍 마그네슘합금 제품의 직화식 표면처리방법

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108117050A (zh) * 2017-11-21 2018-06-05 青岛国林环保科技股份有限公司 一种用于臭氧发生器的高压电极及其制造方法和应用
CN113136577A (zh) * 2021-04-06 2021-07-20 南通海高数控机械有限公司 一种c型钢自动化防锈处理生产线

Similar Documents

Publication Publication Date Title
JP5657728B2 (ja) 表面処理方法
KR20070009884A (ko) 알루미늄 표면의 다중칼라 형성방법
TW201420792A (zh) 一種塑膠基材全幹法拉絲處理的方法
KR101045864B1 (ko) 마그네슘합금 제품의 직화식 표면처리방법
WO2014081089A1 (fr) Procédé de traitement de surface d'articles métalliques
JP2006511698A (ja) マグネシウム化成被覆組成物およびその使用方法
US20080156652A1 (en) Cyanide-free pre-treating solution for electroplating copper coating layer on zinc alloy surface and a pre-treating method thereof
KR101461070B1 (ko) 금속 제품의 표면처리방법
JP2017061719A (ja) 有色シリコン薄膜の形成方法
KR101401366B1 (ko) 마그네슘합금 제품의 표면코팅방법
KR101401363B1 (ko) 마그네슘합금 제품의 표면도장방법
KR101401365B1 (ko) 표면 광택을 가진 마그네슘합금 제품의 표면처리방법
US2437441A (en) Coloring metal surfaces
CN108300990B (zh) 一种不锈钢丝网的环保型着色工艺
CN109628980A (zh) 一种镁合金外观件的电泳涂装工艺
IT201800010168A1 (it) Inibitore di metallizzazione per attrezzature di trattamenti galvanici
CN109628918A (zh) 一种镁合金的彩色化学氧化工艺
CN102127734B (zh) 一种镜面铝表面直接镀膜方法
CH634602A5 (de) Verfahren zum stromlosen katalytischen abscheiden von aluminium.
KR20190034910A (ko) 마그네슘계 금속의 표면 처리 방법
CN112323054B (zh) 一种具有黑色镀层的金属铝齿拉链的制备方法
RU2058352C1 (ru) Способ удаления лакокрасочного покрытия
Upton The effect of the sealers on increase of corrosion resistance of chromate-free passivates on zinc and zinc alloys [J]
EP3127966B1 (fr) Composition de revêtement de protection pour surfaces de chrome
EP3192854A1 (fr) Article dont la surface est traitee avec un agent de couplage a caractere oleophobe et/ou hydrophobe

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13856252

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13856252

Country of ref document: EP

Kind code of ref document: A1