WO2014044694A1 - Verfahren zur herstellung eines mit einem uv-gehärteten lack versehenen formteil aus kunststoff sowie selbiges formteil - Google Patents
Verfahren zur herstellung eines mit einem uv-gehärteten lack versehenen formteil aus kunststoff sowie selbiges formteil Download PDFInfo
- Publication number
- WO2014044694A1 WO2014044694A1 PCT/EP2013/069331 EP2013069331W WO2014044694A1 WO 2014044694 A1 WO2014044694 A1 WO 2014044694A1 EP 2013069331 W EP2013069331 W EP 2013069331W WO 2014044694 A1 WO2014044694 A1 WO 2014044694A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- molding
- cured
- injection
- molded part
- Prior art date
Abstract
Description
Claims