WO2013181375A1 - Tissue repair devices and scaffolds - Google Patents
Tissue repair devices and scaffolds Download PDFInfo
- Publication number
- WO2013181375A1 WO2013181375A1 PCT/US2013/043336 US2013043336W WO2013181375A1 WO 2013181375 A1 WO2013181375 A1 WO 2013181375A1 US 2013043336 W US2013043336 W US 2013043336W WO 2013181375 A1 WO2013181375 A1 WO 2013181375A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- scaffold
- bone
- tissue repair
- repair device
- scaffolds
- Prior art date
Abstract
Description
Claims