WO2013158581A1 - Improved photovoltaic modules for use in vehicle roofs, and/or methods of making the same - Google Patents
Improved photovoltaic modules for use in vehicle roofs, and/or methods of making the same Download PDFInfo
- Publication number
- WO2013158581A1 WO2013158581A1 PCT/US2013/036685 US2013036685W WO2013158581A1 WO 2013158581 A1 WO2013158581 A1 WO 2013158581A1 US 2013036685 W US2013036685 W US 2013036685W WO 2013158581 A1 WO2013158581 A1 WO 2013158581A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- module
- holes
- solar cells
- example embodiments
- glass
- Prior art date
Abstract
Description
Claims