WO2013126183A1 - Compositions containing aromatic isocyanate functional components and aliphatic aromatic isocyanate functional components having improved cure speed - Google Patents
Compositions containing aromatic isocyanate functional components and aliphatic aromatic isocyanate functional components having improved cure speed Download PDFInfo
- Publication number
- WO2013126183A1 WO2013126183A1 PCT/US2013/023571 US2013023571W WO2013126183A1 WO 2013126183 A1 WO2013126183 A1 WO 2013126183A1 US 2013023571 W US2013023571 W US 2013023571W WO 2013126183 A1 WO2013126183 A1 WO 2013126183A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- isocyanate
- isocyanate functional
- weight
- composition
- groups
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
- C08G18/72—Polyisocyanates or polyisothiocyanates
- C08G18/721—Two or more polyisocyanates not provided for in one single group C08G18/73 - C08G18/80
- C08G18/725—Combination of polyisocyanates of C08G18/78 with other polyisocyanates
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
- C08G18/72—Polyisocyanates or polyisothiocyanates
- C08G18/77—Polyisocyanates or polyisothiocyanates having heteroatoms in addition to the isocyanate or isothiocyanate nitrogen and oxygen or sulfur
- C08G18/78—Nitrogen
- C08G18/79—Nitrogen characterised by the polyisocyanates used, these having groups formed by oligomerisation of isocyanates or isothiocyanates
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B37/00—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding
- B32B37/0038—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding involving application of liquid to the layers prior to lamination, e.g. wet laminating
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/08—Processes
- C08G18/10—Prepolymer processes involving reaction of isocyanates or isothiocyanates with compounds having active hydrogen in a first reaction step
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/08—Processes
- C08G18/16—Catalysts
- C08G18/18—Catalysts containing secondary or tertiary amines or salts thereof
- C08G18/20—Heterocyclic amines; Salts thereof
- C08G18/2045—Heterocyclic amines; Salts thereof containing condensed heterocyclic rings
- C08G18/2063—Heterocyclic amines; Salts thereof containing condensed heterocyclic rings having two nitrogen atoms in the condensed ring system
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/08—Processes
- C08G18/16—Catalysts
- C08G18/22—Catalysts containing metal compounds
- C08G18/24—Catalysts containing metal compounds of tin
- C08G18/242—Catalysts containing metal compounds of tin organometallic compounds containing tin-carbon bonds
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
- C08G18/40—High-molecular-weight compounds
- C08G18/48—Polyethers
- C08G18/4804—Two or more polyethers of different physical or chemical nature
- C08G18/482—Mixtures of polyethers containing at least one polyether containing nitrogen
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
- C08G18/40—High-molecular-weight compounds
- C08G18/48—Polyethers
- C08G18/4829—Polyethers containing at least three hydroxy groups
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
- C08G18/72—Polyisocyanates or polyisothiocyanates
- C08G18/73—Polyisocyanates or polyisothiocyanates acyclic
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
- C08G18/72—Polyisocyanates or polyisothiocyanates
- C08G18/74—Polyisocyanates or polyisothiocyanates cyclic
- C08G18/76—Polyisocyanates or polyisothiocyanates cyclic aromatic
- C08G18/7657—Polyisocyanates or polyisothiocyanates cyclic aromatic containing two or more aromatic rings
- C08G18/7685—Polyisocyanates or polyisothiocyanates cyclic aromatic containing two or more aromatic rings containing two or more non-condensed aromatic rings directly linked to each other
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
- C08G18/72—Polyisocyanates or polyisothiocyanates
- C08G18/77—Polyisocyanates or polyisothiocyanates having heteroatoms in addition to the isocyanate or isothiocyanate nitrogen and oxygen or sulfur
- C08G18/78—Nitrogen
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
- C08G18/72—Polyisocyanates or polyisothiocyanates
- C08G18/77—Polyisocyanates or polyisothiocyanates having heteroatoms in addition to the isocyanate or isothiocyanate nitrogen and oxygen or sulfur
- C08G18/78—Nitrogen
- C08G18/79—Nitrogen characterised by the polyisocyanates used, these having groups formed by oligomerisation of isocyanates or isothiocyanates
- C08G18/797—Nitrogen characterised by the polyisocyanates used, these having groups formed by oligomerisation of isocyanates or isothiocyanates containing carbodiimide and/or uretone-imine groups
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/34—Silicon-containing compounds
- C08K3/346—Clay
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J11/00—Features of adhesives not provided for in group C09J9/00, e.g. additives
- C09J11/02—Non-macromolecular additives
- C09J11/04—Non-macromolecular additives inorganic
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J175/00—Adhesives based on polyureas or polyurethanes; Adhesives based on derivatives of such polymers
- C09J175/04—Polyurethanes
- C09J175/08—Polyurethanes from polyethers
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B2255/00—Coating on the layer surface
- B32B2255/10—Coating on the layer surface on synthetic resin layer or on natural or synthetic rubber layer
Definitions
- the invention relates to curable compositions containing isocyanate functional components which exhibit improved cure speed and longer tack free time and to methods of bonding substrates together utilizing such compositions.
- compositions having isocyanate functional components are utilized in a variety of useful products such as adhesives, molded products and foams. Such compositions are utilized in construction, vehicle manufacture, assembly of electronic subassemblies and devices, toys and the like.
- the adhesives are used to bond substrates together and have found widespread use because they allow for reasonable processing conditions and exhibit good adhesion to many substrates.
- One common use of such compositions is to bond glass, often in the form of windows, into structures.
- Two-part polyisocyanate based adhesives comprise, in one part, a polyisocyanate or an isocyanate functional prepolymer and in a second part a curing agent and catalyst for the reaction of the curing agent with isocyanate groups.
- the curing agent is a compound having on average more than one active hydrogen atom, for instance an amine or hydroxyl moiety.
- Two part adhesives are often used for bonding parts to together or to other structures, for example bonding trim parts to vehicles or bonding replacement windows into vehicles. Examples of such adhesive systems include those disclosed in US 7,892,395; US 2009/0044907; US 6,965,008; EP 1433802 and EP 1578834, all incorporated herein by reference in their entirety.
- the adhesive starts to cure when the two parts are contacted.
- Two-part adhesives have the advantage that they cure much faster than one -part adhesives.
- the invention relates to a composition
- a composition comprising Part 1 : a) one or more isocyanate functional components having aromatic isocyanate functional groups; and b) one or more isocyanate functional components having aliphatic isocyanate functional groups; and Part 2: c) one or more compounds having more than one isocyanate reactive groups: wherein the ratio of aromatic functional groups to isocyanate reactive groups is from 0.95 to 1.05 and the ratio of aromatic isocyanate functional groups and aliphatic isocyanate functional groups (total isocyanate groups) to isocyanate reactive groups is from 1.10 to 1.30.
- the composition may further contain one or more fillers in one or both of Part 1 and Part 2. Exemplary fillers include one or more clays.
- the one or more isocyanate functional components having aromatic isocyanate functional groups may comprise one or more prepolymers having aromatic isocyanate functional groups.
- the one or more isocyanate functional components having aromatic isocyanate functional groups comprises one or more polyisocyanates having aromatic isocyanate functional groups and one or more isocyanate functional group containing prepolymers having in their backbones the residue of one or more chains of one or more polypropylene oxides, copolymers of ethylene oxide and propylene oxide or mixtures thereof wherein equivalent weight of the chains are predominantly greater than about 780 and having aromatic isocyanate functional groups; and the isocyanate reactive component comprises one or more polypropylene oxides, copolymers of ethylene oxide and propylene oxide or mixtures thereof having equivalent weights predominantly about 960 or greater and terminal groups which are reactive with isocyanate groups, and one or more low molecular weight compounds having two or more isocyanate reactive groups and a molecular weight of 120 or less.
- the invention relates to a method of bonding two or more substrates together comprising i) contacting Part 1 and Part 2 according to any embodiment of the invention; ii) contacting the mixture of step i) with one or more substrates; iii) contacting the substrates together with the mixture of step i) disposed between the substrates; iv) allowing the mixture of step i) to cure so as to bond the substrates together.
- the two part compositions as described herein may further comprise one or more known blowing agents.
- compositions are useful in any known use of curable compositions containing isocyanate functional components, such as coatings, adhesives, open and closed cell foams, molded products and the like.
- the curable compositions may be used as adhesives to bond substrates together.
- a variety of similar and dissimilar, porous and nonporous, substrates may be bonded together using the compositions, for instance, plastics, glass, wood, ceramics, metal, coated substrates and the like.
- the compositions are useful in bonding glass or coated plastic to substrates, i.e. windows into vehicles or buildings, or parts of modular components together, such as vehicle modular components, i.e. vehicle modules, such as door, window or body.
- the compositions of the invention exhibit rapid cure speeds with longer tack free times. DESCRIPTION OF THE DRAWINGS
- Figure 1 plots the lap shear strength against the cure time for the tested compositions.
- Figure 2 compares the tack free time of the three tested adhesive.
- One or more as used herein means that at least one, or more than one, of the recited components are present.
- Nominal functionality means the theoretical functionality, which can be calculated from the stoichiometry of the ingredients used. The actual functionality is different due to imperfections in raw materials, incomplete conversion of the reactants and formation of byproducts.
- Isocyanate content means the weight percentage of isocyanate moieties based on the total weight of the isocyanate components.
- isocyanate-reactive compound as used herein includes any organic compound having nominally at least two isocyanate-reactive moieties.
- an active hydrogen containing moiety refers to a moiety containing a hydrogen atom which, because of its position in the molecule, displays significant activity according to the Zerewitinoff test described by Wohler in the Journal of the American Chemical Society, Vol. 49, p. 3181 (1927).
- active hydrogen moieties are -COOH, -OH, -NH 2 , -NH-, -CONH 2 , -SH, and -CONH-.
- Preferable isocyanate- reactive compounds include polyols, polyamines, polymercaptans and polyacids, more preferably, polyols.
- Aromatic isocyanate group means an isocyanate group covalently bonded to an aromatic carbon atom.
- Aliphatic isocyanate group means an isocyanate group covalently bonded to an aliphatic carbon atom.
- compositions of this invention are reactive systems containing isocyanate functional components which are curable.
- Reactive means herein that the curable composition (e.g. adhesive) contains components which react to form a polymeric matrix that is set irreversibly once cured.
- the curable systems are two-part systems, preferably useful as adhesives.
- Isocyanate based (polyurethane or polyurea forming) curable systems comprise two or more isocyanate functional components, one or more aromatic isocyanate functional components and one or more aliphatic isocyanate functional components.
- An isocyanate functional component contains one or more compounds having on average more than one isocyanate functional group per molecule.
- the isocyanate functional compounds can be any compounds which contain on average more than one isocyanate moiety.
- the isocyanate functional components can be in the form of isocyanate functional prepolymers, monomers or oligomers having on average greater than 1 isocyanate group, and preferably 2 or more isocyanate groups.
- the isocyanate prepolymers can by any prepolymers prepared by reaction of an isocyanate functional compound with one or more compounds having on average more than one isocyanate reactive functional groups, such as hydroxyl, amine, thiol, carboxyl and the like, under conditions such that the prepolymers prepared have on average more than one isocyanate moiety (group) per molecule.
- the isocyanate functional components are present in the curable composition in a sufficient amount to form a cured component when exposed to curing conditions.
- the isocyanate functional components when combined with isocyanate reactive compounds are capable of bonding substrates together in a manner that the substrates remain bound together when exposed to temperatures of -30°C to 100°C for long periods of time, such as 10 years; and up to temperatures of 180°C for short periods of up to 30 minutes.
- the isocyanate functional components contain a sufficient amount of aromatic isocyanate groups to speed the cure of the two components when contacted as measured by lap shear strength at certain designated times from contacting of the parts or contacting of the contacted parts with one or more substrates.
- the amount of the isocyanate functional components is chosen to provide a sufficient amount of aromatic isocyanate groups in relation the amount of isocyanate reactive groups in the curative.
- the amount of the isocyanate functional components is chosen to provide a sufficient amount of aromatic isocyanate groups such that the ratio of aromatic isocyanate groups in part A to the amount of isocyanate reactive groups in the part B fall within a preferably ratio range.
- the ratio of aromatic isocyanate groups in part A to the amount of isocyanate reactive groups in the part B is about 0.95: 1 or greater, more preferably about 0.97: 1 or greater and most preferably about 0.98: 1 or greater.
- the ratio of aromatic isocyanate groups in part A to the amount of isocyanate reactive groups in the part B is about 1.05: 1 or less, more preferably about 1.03 or less and most preferably about 1.02: 1 or less.
- the isocyanate functional components contain a sufficient amount of aliphatic isocyanate groups to improve the final cured strength typically measured after about 7 days from cure and adhesion to substrate surfaces.
- the amount of aliphatic isocyanate groups is expressed as the part of the total amount of isocyanate groups expressed as a ratio of total isocyanate groups in part A to the total amount of isocyanate reactive groups in part B.
- the amount of aliphatic isocyanate groups can be calculated from the ratio of aromatic isocyanate groups to isocyanate reactive groups and the ratio of total isocyanate groups in part A to isocyanate reactive groups in part B.
- the ratio of total isocyanate groups in part A to isocyanate reactive groups in part B is chosen to provide rapid cure, with longer tack free times and high overall final cure strength.
- the ratio of total isocyanate groups in part A to the amount of isocyanate reactive groups in the part B is about 1.10: 1 or greater and most preferably about 1.14: 1 or greater.
- the ratio of aromatic isocyanate groups in part A to the amount of isocyanate reactive groups in the part B is about 1.30: 1 or less, more preferably about 1.20: 1 or less and most preferably about 1.18: 1 or less.
- the aromatic isocyanate groups and aliphatic isocyanate groups may be located on the same isocyanate functional components or different isocyanate functional components, preferably different isocyanate functional components.
- Preferably a portion of the aromatic isocyanate groups are located on isocyanate functional prepolymers.
- the aliphatic isocyanate groups are located on polyisocyanates or addition products of polyisocyanates.
- the curable system is a two-part polyisocyanate component containing curable system.
- the two parts are reactive with one another and when contacted undergo cure.
- One part of the composition comprises, or contains, two or more isocyanate functional components as described hereinbefore, typically referred to as the resin side or A side.
- the other component comprises one or more isocyanate reactive components which comprises, or contains, one or more compounds, oligomers or prepolymers having on average more than one group reactive with isocyanate moieties, commonly known as the curative or B side.
- Compounds having on average one or more isocyanate reactive groups can be compounds, prepolymers, small chain compounds such as difunctional chain extenders or polyfunctional crosslinking agents known in the art or mixtures thereof.
- a catalyst as described hereinbefore may be utilized in the curative side.
- the reaction product is a cured product which is capable of performing the desired function, such as bonding certain substrates together.
- the isocyanate functional component is present in the curable composition in a sufficient amount to form a cured component when exposed to curing conditions.
- such prepolymers are present in sufficient quantity to provide cohesive strength, and in adhesive uses, adhesive character to the composition.
- Isocyanate functional prepolymers have an average isocyanate functionality sufficient to allow the preparation of a crosslinked polyurethane upon cure and not so high that the prepolymers are unstable.
- the prepolymers are prepared by reacting one or more polyisocyanates with one or more compounds containing on average more than one isocyanate reactive group per molecule.
- the isocyanate functional prepolymers are the reaction product of one or more polyisocyanates and one or more isocyanate reactive compounds wherein an excess of polyisocyanate is present on equivalent basis, preferably an excess of about 0.6 equivalents or greater.
- the prepolymer preferably has a free isocyanate content which facilitates acceptable strength in the compositions prepared from the prepolymers, preferably after 60 minutes.
- the isocyanate content of part 1 including all of the isocyanate function components is preferably about 5 percent by weight or greater and most preferably in the about 7 by weight or greater.
- the isocyanate content of the part 1 is preferably about 32 percent by weight or less, more preferably about 25 percent by weight or less and most preferably about 17 percent by weight or less.
- the prepolymers preferably exhibit a polydispersity of about 2.5 or less, more preferably about 2.3 or less and most preferably about 2.1 or less.
- Exemplary polyisocyanates useful in the invention and in preparing isocyanate functional prepolymers include any aliphatic, cycloaliphatic, araliphatic, heterocyclic or aromatic polyisocyanates, or mixtures thereof.
- the polyisocyanates used have an average isocyanate functionality of about 2.0 or greater and an equivalent weight of about 80 or greater.
- the isocyanate functionality of the polyisocyanates is about 2.0 or greater, more preferably about 2.2 or greater, and is most preferably about 2.4 or greater; and is preferably about 4.0 or less, more preferably about 3.5 or less, and most preferably about 3.0 or less.
- the equivalent weight of the polyisocyanates is about 80 or greater, more preferably about 1 10 or greater, and is most preferably about 120 or greater; and is preferably about 300 or less, more preferably about 250 or less, and most preferably about 200 or less.
- Exemplary aliphatic polyisocyanates include those disclosed by Wu, U.S. Pat. No. 6,512,033 at column 3, line 3 to line 49, incorporated herein by reference.
- More preferred aliphatic isocyanates include, isophorone diisocyanate, tetramethylxylene diisocyanate, 1 ,6-hexa-methylene diisocyanate and oligomeric or polymeric derivatives thereof, bis(4-isocyanato- cylohexyl)methane, and trimethyl hexamethylene diisocyanate.
- the most preferred aliphatic isocyanates are is hexamethylene diisocyanate and oligomeric and polymeric derivatives thereof.
- Examples of preferred aliphatic isocyanates include trimers of hexamethylene diisocyanate, such as those available from Bayer under the trademark and designation DESMODUR N3300, DESMODUR N3400, DESMODUR N- 100.
- Exemplary aromatic polyisocyanates include those disclosed by Wu, U.S. Pat. No. 6,512,033 at column 3, line 3 to line 49, incorporated herein by reference. More preferred aromatic isocyanates include diphenylmethane diisocyanate, toluene diisocyanate and polymeric derivatives thereof. The most preferred isocyanate is diphenylmethane diisocyanate.
- the amount of isocyanate containing compound used to prepare the prepolymer is that amount that gives the desired properties, the appropriate free isocyanate content and viscosities as discussed herein.
- Oligomeric aromatic polyisocyanates useful include those available from The Dow Chemical Company under the trademarks PAPI and VORANATE, such as VORANTE M220, PAPI 27 and PAPI 20 polymeric isocyanates.
- Preferable polyols useful in the preparation of the prepolymers include those disclosed in Wu, U.S. Pat. No. 6,512,033 at column 4, line 10 to line 64, incorporated herein by reference.
- Exemplary polyols include polyether polyols, polyester polyols, poly(alkylene carbonate)polyols, hydroxyl containing polythioethers and mixtures thereof.
- Preferred polyols are polyether polyols containing one or more alkylene oxide units in the backbone of the polyol.
- Preferred alkylene oxide units are ethylene oxide, propylene oxide, butylene oxide and mixtures thereof.
- the alkylene oxides can contain straight or branched chain alkylene units.
- the polyol contains propylene oxide units, ethylene oxide units or a mixture thereof. Where a mixture of alkylene oxide units is contained in a polyol, the different units can be randomly arranged or arranged in blocks of each alkylene oxide.
- the polyol comprises propylene oxide chains with ethylene oxide chains capping the polyol.
- the polyols are a mixture of diols and triols.
- the isocyanate -reactive compound has a functionality of about 1.9 or greater, more preferably about 1.95 or greater, and is most preferably about 2.0 or greater; and is preferably about 4.0 or less, more preferably about 3.5 or less, and is most preferably about 3.0 or less.
- the equivalent weight of the isocyanate -reactive compounds is about 200 or greater, more preferably about 500 or greater, and more preferably about 1,000 or greater; and is preferably about 5,000 or less, more preferably about 3,000 or less, and most preferably about 2,500 or less.
- the adhesive compositions may further comprise one or more isocyanate functional prepolymers or isocyanate reactive compounds in the form of prepolymers containing one or more organic based polymers dispersed therein or grafted to the backbone.
- the preferable organic base polymer containing triols are disclosed in Zhou, U.S. Pat. No. 6,709,539 at column 4, line 13 to column 6, line 18, incorporated herein by reference.
- the triols used to disperse or graft the organic particles is one or more polyether triols and more preferably one or more polyoxyalkylene based triols, which preferably comprise polyoxypropylene chains with a polyoxyethylene end caps.
- triols are ethylene oxide-capped polyols prepared by reacting glycerin with propylene oxide, followed by reacting the product with ethylene oxide.
- the organic particles comprise one or more of thermoplastic polymers, rubber- modified thermoplastic polymers or polyureas.
- prepolymers containing organic particles are contained in the adhesive in an amount of about 5 percent by weight or greater.
- prepolymers containing organic particles are contained in the adhesive in an amount of about 40 percent by weight or less.
- the isocyanate reactive compounds may be present in isocyanate functional prepolymers in an amount sufficient to react with most of the isocyanate groups of the isocyanates leaving enough isocyanate groups to correspond with the desired free isocyanate content of the prepolymer.
- the components containing active hydrogen groups are present in an amount of about 50 parts by weight or greater based on the prepolymer, more preferably about 65 parts by weight or greater and most preferably about 80 parts by weight or greater.
- the components containing active hydrogen groups are present in an amount of about 90 parts by weight or less based on the prepolymer and most preferably about 85 parts by weight or less.
- the prepolymers may be prepared by any suitable method, such as bulk polymerization and solution polymerization.
- the process may be carried out under anhydrous conditions, preferably under an inert atmosphere, such as a nitrogen blanket, to prevent crosslinking of the isocyanate groups by moisture.
- the reaction is preferably carried out at a temperature from about 0° C to about 150° C, more preferably from about 25° C to about 90° C, until the residual isocyanate content determined by titration of a sample is very close to the desired theoretical value.
- the reactions to prepare the prepolymer may be carried out in the presence of urethane catalysts, for example stannous salts of carboxylic acids, such as stannous octoate, stannous oleate, stannous acetate, and stannous laurate; dialkyltin dicarboxylates, such as dibutyltin dilaurate and dibutyltin diacetate; tertiary amines and tin mercaptides.
- the catalyst is stannous octoate.
- the amount of catalyst employed is generally from about 0.005 to about 5 parts by weight of the mixture catalyzed.
- the reaction is carried out in admixture with a plasticizer.
- a polyether diol having an effective functionality of at least about 1.9, preferably at least about 1.95 and a polyether triol, having an effective functionality of at least about 2.8, preferably at least about 2.9 are reacted with an aromatic polyisocyanate with a functionality of at least about 2.0.
- Preferred polyether diols have a molecular weight of about 1 ,000 or greater and more preferably about 3000 or greater.
- Preferred polyether diols have a molecular weight of about about 9,000 or less and more preferably about 6,000 as or less. Such molecular weight are calculated from the OH-number and functionality.
- the prepolymers or curing agents comprising copolymers of ethylene oxide and propylene oxide contain about 40 weight percent or less of ethylene oxide monomer units, even more preferably 25 weight percent or less of ethylene oxide monomer units, even more preferably about 15 weight percent or less of ethylene oxide monomer units and most preferably about 12 weight percent or less of ethylene oxide monomer units.
- ethylene monomer units are present, they are present in an amount of 5 percent by weight or greater and more preferably about 8 percent by weight or greater.
- the isocyanate functional prepolymers have in their backbone the residue of one or more chains of one or more polypropylene oxide, copolymers of ethylene oxide and propylene oxide or mixtures thereof which have chain lengths such that the glass transition temperature of the cured polymers containing such prepolymers is about -40°C or less, more preferably about -45°C or less and most preferably about -50°C or less.
- the isocyanate reactive group containing compounds utilized in part 2 comprise with one or more polypropylene oxide based polyols, copolymers of ethylene oxide and propylene oxide based polyols or mixtures thereof.
- the isocyanate functional prepolymer or the isocyanate reactive group containing compounds have in their backbones the residue of one or more chains of one or more polypropylene oxides, copolymers of ethylene oxide and propylene oxide or mixtures thereof which chains have equivalent weights of about 780 or greater, more preferably about 960 or greater, even more preferably about 1 ,000 or greater and most preferably about 1 ,500 or greater.
- the isocyanate functional prepolymer or the isocyanate reactive compounds have in their backbone the residue of one or more chains of one or more polypropylene oxides, copolymers of ethylene oxide and propylene oxide or mixtures thereof which chains have equivalent weights of about 4,000 or less, more preferably about 3,000 or less and most preferably about 2,000 or less.
- one or more of the isocyanate functional prepolymers or one or more of the isocyanate reactive compounds have in their backbone the residue of one or more polypropylene oxides, copolymers of ethylene oxide and propylene oxide or mixtures thereof wherein the chains of polypropylene oxides, copolymers of ethylene oxide and propylene oxide or mixtures thereof are predominantly greater than about 15 monomer units, more preferably about 20 monomer units or greater and most preferably 30 monomer units or greater. More preferably, the number of monomer units per chain in the chains of polypropylene oxides, copolymers of ethylene oxide and propylene oxide or mixture thereof is about 120 or less and most preferably about 60 monomer units or less.
- Predominantly means that the great majority of the chains of the one or more polypropylene oxides, copolymers of ethylene oxide and propylene oxide or mixtures thereof have equivalent weights or the recited monomer units as recited. More preferably, substantially all of the chains of the residue of the one or more polypropylene oxides, copolymers of ethylene oxide and propylene oxide or mixtures thereof exhibit equivalent weights or monomer units as described. “Substantially all” and "consists essentially of mean that there may be a minor amount of the polymer chains which do not meet the equivalent weight or monomer unit limitations but such minor amount does not have any impact on the properties of the cured composition of the invention.
- the isocyanate functional group containing prepolymers and/or the isocyanate reactive compounds consist of one or more prepolymers or isocyante reactive compounds having in their backbone chains of one or more polypropylene oxides, copolymers of ethylene oxide and propylene oxide or mixtures thereof wherein the chains exhibit an equivalent weight or monomer unit content as recited.
- the one or more isocyanate functional components have aromatic isocyanate functional groups which comprise one or more polyisocyanates having aromatic isocyanate functional groups and one or more isocyanate functional group containing prepolymers having in their backbones the residue of one or more chains of one or more polypropylene oxides, copolymers of ethylene oxide and propylene oxide or mixtures thereof wherein equivalent weight of the chains are predominantly greater than about 780 and having aromatic isocyanate functional groups; and the isocyanate reactive component comprises one or more polypropylene oxides, copolymers of ethylene oxide and propylene oxide or mixtures thereof having equivalent weights predominantly about 960 or greater and terminal groups which are reactive with isocyanate groups.
- Chains as used herein with respect to propylene oxides and copolymers of propylene oxides and ethylene oxide refer to polymer segments of only propylene oxide or propylene oxide and ethylene oxides and does not include the initiators.
- the weights and number of monomer units referred to herein relative to chains of propylene oxide or propylene oxide and ethylene oxide are quoted on an equivalents basis.
- the isocyanate group containing prepolymer does not contain chains of polypropylene oxide or copolymers of ethylene oxide and propylene oxide having equivalent weights of less than about 780, more preferably less than about 960, even more preferably less than about 1,000 and most preferably less than about 1,500.
- the isocyanate functional group containing component does not contain prepolymers having in its backbone chains of polypropylene oxides, copolymers of ethylene oxide and propylene oxide having equivalent weights of greater than about 4,000, more preferably about greater than about 3,000 or greater and most preferably greater than about 2,000 or greater.
- the isocyanate containing component does not contain a chain of polypropylene oxide or copolymers of ethylene oxide and propylene oxide having less than about 15 monomer units, more preferably less than about 20 monomer units and most preferably less than about 30 monomer units. In a preferred embodiment, the isocyanate containing component does not contain a chain of polypropylene oxide copolymers of ethylene oxide and propylene oxide having greater than about 120 monomer units per chain and most preferably greater than about 60 monomer units per chain.
- the aromatic isocyanate functional component may be present in the composition in a sufficient amount such that the curable compositions exhibit rapid cure rates, especially as measured by lap shear strength at 1 and 4 hours from contacting the two parts, and the cured composition has sufficient strength for its designed purpose, in the case of adhesive systems such that the adhesive is capable of bonding substrates together and to provide the desired cohesive and adhesive strengths.
- the aromatic isocyanate functional component is present in an amount of about 10 percent by weight or greater based on the weight of the composition, more preferably about 30 percent by weight or greater and most preferably about 50 percent by weight or greater.
- the aromatic isocyanate functional component is present in an amount of about 65 percent by weight or less based on the weight of the composition, more preferably about 60 percent by weight or less and most preferably about 55 percent by weight or less.
- the percentages stated are selected such that the ratios of equivalents of aromatic isocyanate groups to isocyanate reactive groups meet the requirements stated hereinbefore.
- the aliphatic isocyanate functional component may be present in the composition in a sufficient amount such that the curable compositions exhibit sufficient strength for its designed purpose, in the case of adhesive systems such that the adhesive is capable of bonding substrates together and to provide the desired cohesive and adhesive strengths.
- the aliphatic isocyanate functional component is present in an amount of about 1 percent by weight or greater based on the weight of the composition, more preferably about 3 percent by weight or greater and most preferably about 5 percent by weight or greater.
- the aliphatic isocyanate functional component is present in an amount of about 20 percent by weight or less based on the weight of the composition, more preferably about 15 percent by weight or less and most preferably about 10 percent by weight or less.
- the percentages stated are selected such that the ratios of equivalents of aliphatic and aromatic isocyanate groups to isocyanate reactive groups meet the requirements stated hereinbefore.
- compositions may comprise one or more curing agents located in the second part.
- Curing agents are comounds that contains greater than one isocyanate reactive group, preferably hydroxyl or amine functional groups.
- the curing agents can be one or more chain extenders, crosslinking agents, polyols or polyamines, or prepolymers as described herein having isocyanate reactive groups. Polyols as described hereinbefore can be utilized as curing agents.
- the prepolymers can be prepared by the reaction of polyisocyanates with compounds containing isocyanate reactive compounds utilizing excess equivalents of isocyanate reactive groups such that the resulting prepolymers contain isocyanate reactive groups.
- the isocyanate functional curable compositions may further comprise one or more low molecular weight compounds having two or more isocyanate reactive groups and a hydrocarbon backbone wherein the backbone may further comprise one or more heteroatoms.
- Such low molecular weight compounds may be chain extenders, such compounds are difunctional, or crosslinkers, having greater than two active hydrogen groups per compound.
- the heteroatoms in the backbone can be oxygen, sulfur, nitrogen or a mixture thereof, wherein oxygen, nitrogen or a mixture thereof is more preferred and oxygen is most preferred.
- the molecular weight of the low molecular weight compound is about 120 or less and more preferably about 100 or less.
- the low molecular weight compound comprises one or more multifunctional alcohols, multifunctional alkanol amines, one or more adducts of multifunctional alcohol and an alkylene oxide, one or more adducts of a multifunctional alkanol amine and an alkylene oxide or a mixture thereof.
- multifunctional alcohols and multifunctional alkanol amines are ethane diol, propane diol, butane diol, hexane diol, heptane diol, octane diol, glycerine, trimethylol propane, pentaerythritol, neopentyl glycol, ethanol amines (diethanol amine, triethanol amine) and propanol amines (di-isopropanol amine, tri-isopropanol amine) and the like. Blends of various low molecular weight compounds may be used.
- the low molecular weight compound is used in a sufficient amount to obtain the desired G-Modulus (E- Modulus).
- the low molecular compound may be located in the resin side, the curative side or both, preferably, the curative side.
- the low molecular weight compound is present in composition in an amount of about 2 percent by weight or greater, more preferably about 3 percent by weight or greater and most preferably about 4.0 percent by weight or greater.
- the low molecular weight compound is present in the composition in an amount of about 16 percent by weight or less, more preferably about 12 percent by weight or less and most preferably about 10 percent by weight or less.
- the curative part may further comprise polyoxyalkylene polyamine having 2 or greater amines per polyamine.
- the polyoxyalkylene polyamine has 2 to 4 amines per polyamine and most preferably 2 to 3 amines per polyamine.
- the polyoxyalkylene polyamine has a weight average molecular weight of about 200 or greater and most preferably about 400 or greater.
- the polyoxyalkylene polyamine has a weight average molecular weight of about 5,000 or less and most preferably about 3,000 or less.
- polyoxyalkylene polyamines are JEFF AMINETM D-T-403 polypropylene oxide triamine having a molecular weight of about 400 and JEFF AMINETM D-400 polypropylene oxide diamine having a molecular weight of about 400.
- the polyoxyalkylene polyamines are present in a sufficient amount to prevent the composition from sagging once mixed and applied.
- the polyoxyalkylene polyamine is present in the curable composition in an amount of about 0.2 percent by weight or greater, more preferably about 0.3 percent by weight or greater and most preferably about 0.5 percent by weight or greater.
- the polyoxyalkylene polyamine is present in the curable composition in an amount of about 6 percent by weight or less, more preferably about 4 percent by weight or less and most preferably about 2 percent by weight or less.
- the prepolymers useful in the invention and the compositions of the invention may further comprise a plasticizer commonly used in polyurethane compositions.
- the composition may contain plasticizers in both components.
- the plasticizer is present in an amount sufficient to disperse the prepolymer in the final adhesive composition.
- the plasticizer can be added to the adhesive either during preparation of the prepolymer or during compounding of the adhesive composition.
- plasticizers include straight and branched alkylphthalates, such as diisononyl phthalate, dioctyl phthalate and dibutyl phthalate, a partially hydrogenated terpene commercially available as "HB-40", trioctyl phosphate, alkylsulfonic acid esters of phenol, toluene-sulfamide, adipic acid esters, castor oil, xylene, l-methyl-2-pyrrolidinone and toluene.
- plasticizers are branched plasticizers, such as branched chain alkyl phthalates for example di-isononyl phthalates (available under the Trademark PLATINOL N from BASF.
- the amount of plasticizer used is that amount sufficient to give the desired rheological properties and disperse the components in the curable composition.
- the plasticizer is present in about 1 percent by weight or greater of the composition, more preferably about 5 percent by weight or greater and most preferably about 10 percent by weight or greater.
- the plasticizer is present in about 50 percent by weight or less of the composition and more preferably about 40 percent by weight or less.
- the composition may comprise components to control the rheology, viscosity, pumpability and the sag characteristics.
- the materials included in the composition for these purposes include one or more fillers, one or more isocyanate functional polyester based prepolymers, or a mixture thereof. These materials are added in a sufficient amount such that the composition exhibits the desired rheology, viscosity and the sag characteristics.
- these components are added such that the composition exhibits a press flow viscosity (at room temperature, 4 bar pressure 2 mm nozzle, 18 mm length) of about 10 grams per minute or higher, more preferably about 15 grams per minute or higher and most preferably about 20 grams per minute or higher to allow for application by a manual dispensing gun.
- the composition may comprises one or more fillers.
- Fillers are added for a variety of reasons as described hereinbefore and one or more types of fillers may be utilized in the composition of this invention. Fillers may be added to reinforce the composition, to impart the appropriate viscosity and rheology and to strike a balance between cost and the desired properties of the composition and the parts of the composition.
- Preferred classes of fillers comprise one or more reinforcing fillers, such as one or more carbon blacks, one or more clays or non-pigmented fillers, one or more thixotropes or combinations thereof.
- the fillers comprise one of more reinforcing carbon blacks and one or more clays.
- fillers that impart a balance of cost and viscosity to each part and comprise clays and non-pigmented fillers. Such fillers are used in a sufficient amount to impart an acceptable balance of viscosity and cost to the formulation and to achieve the desired properties of the composition.
- fillers useful for this purpose are clays, untreated and treated talc, and calcium carbonates.
- Preferred clays useful in the invention include kaolin, surface treated kaolin, calcined kaolin, aluminum silicates and surface treated anhydrous aluminum silicates.
- Kaolin is also known as Kaolinite and comprises compounds represented by the chemical formula Al 2 Si 2 O 5 (OH) 4 , and it most often occurs as clay-sized, platelike, hexagonally shaped crystals.
- the clays can be used in any form which facilitates formulation of a composition having the desired properties, for example a composition that can be utilized a hand- dispensable adhesive.
- the clay is admixed in the form of pulverized powder, spray- dried beads or finely ground particles.
- the clays or non-pigmented fillers are present in an amount sufficient to render the rheology of the composition suitable to function as desired, such as an adhesive applicable by hand-gun.
- the clays or non-pigmented fillers may be used in an amount of about 0 percent by weight or greater of the composition, more preferably about 3 percent by weight or greater, and even more preferably about 5 percent by weight or greater, even more preferably about 10 percent by weight or greater and most preferably about 16 percent by weight or greater.
- the clays or non-pigmented fillers may be used in an amount of about 60 percent by weight or less of the composition of the invention and more preferably about 50 percent by weight or less.
- the composition may further comprise a reinforcing filler which is present in a sufficient amount to improve the strength and rheology of the composition.
- the preferred class of reinforcing fillers comprises one or more forms of carbon black.
- the reinforcing filler is present in an amount such that the compositions is nonconductive, exhibiting an impedance of the composition of at least 10 10 Ohm-cm. If too much of certain reinforcing fillers, such as one or more forms of carbon black are present, the composition may be conductive.
- the carbon black used may be a standard carbon black, which is not specifically surface treated or oxidized to render it nonconductive.
- One or more nonconductive carbon blacks which may be specifically surface treated or oxidized to render it nonconductive, may be used in conjunction with the standard carbon black.
- the amount of standard carbon black in the composition is that amount which provides the desired color, viscosity, sag resistance and strength. If non conductivity is desired, standard carbon black may be utilized at a level at which the composition is nonconductive.
- reinforcing filler is a high surface area carbon black.
- high surface area carbon black is carbon black that exhibits an oil absorption of about 1 10 cc/l OOg or greater and preferably about 1 15 cc/100 g or greater.
- high surface area carbon black is carbon black that exhibits an iodine number of about 130 mg/g or greater and preferably about 150 mg/g or greater.
- the high surface area carbon black exhibits both of the defined oil absorbtion and iodine properties.
- Preferred high surface area carbon blacks include ELFTEXTM57100, MONARCH RAVENTM 1040 and RAVENTM 1060 carbon blacks.
- the reinforcing filler is preferably present in the composition, based on the weight of the composition, in an amount by about 0 percent by weight or greater, more preferably by about 10 percent by weight or greater and most preferably about 14 percent by weight or greater.
- the reinforcing filler based on the weight of the composition, in an amount of about 20 percent by weight or less, more preferably about 18 percent by weight or less, and most preferably about 16 percent by weight or less. If conductive carbon black is used and a non- conductive composition is desired, attention must be paid to keep the concentration below about 18 percent by weight to prevent the impedance of the composition to be above 10 10 Ohm-cm. Standard carbon blacks are well known in the art and include RAVENTM 790, RAVENTM 450, RAVENTM 500, RAVENTM 430, RAVENTM 420 and RAVENTM 410 carbon blacks available from Colombian and CSXTM carbon blacks available from Cabot, and PRINTEXTM30 carbon black available from Degussa. Nonconductive carbon blacks include RAVENTM 1040 and RAVENTM 1060 carbon black available from Colombian.
- the adhesive composition may further comprise fillers which functions as a thixotrope (rheological additive).
- thixotropes are well known to those skilled in the art and include fumed silica and the like.
- Preferred fumed silicas include organically modified fumed silicas.
- the thixotrope may be added to the composition in a sufficient amount to give the desired rheological properties.
- the thixotrope is present in an amount of about 0 percent by weight or greater based on the weight of the composition, preferably about 2.0 percent by weight or greater.
- the optional thixotrope is present in an amount of about 10 percent by weight or less based on the weight of the composition and more preferably about 8 percent by weight, most preferably about 6 or less.
- the isocyanate functional component may further comprise one or more isocyanate functional prepolymers containing one or more polyester based polyols which are solid at ambient temperature, about 23° C.
- the polyester based polyols have melting points such that the prepolymer provides sufficient green strength to prevent the substrates from moving in relation to one another due to gravitational forces at ambient temperatures. In terms of installing a window in a vehicle or building, the polyester based prepolymer prevents the window from sliding after installation.
- the polyester polyols have melting points of about 40° C or greater, even more preferably about 45° C or greater and most preferably about 50° C or greater.
- the polyester polyols exhibit melting points of about 85° C or less, even more preferably about 70° C or less and most preferably about 60° C or less.
- the polyester polyol based isocyanate prepolymer is present in the adhesive composition in sufficient amount to support the needed green strength and the desired rheology of the composition. If the amount is too high, an adhesive composition is not hand gun applicable at ambient temperature.
- the polyester polyol based isocyanate prepolymer is present in the adhesive composition in an amount of about 0 percent by weight or greater based on the weight of the adhesive composition, more preferably about 1 percent by weight or greater and most preferably about 2 percent by weight or greater.
- the polyester polyol based isocyanate prepolymer is present in the adhesive composition in an amount of about 10 percent by weight or less, even more preferably about 5 percent by weight or less and most preferably about 3 percent by weight or less.
- the polyester polyol can be any polyester composition that meets the property requirements defined, which is crystalline at ambient temperatures and melts in the desired temperature range.
- Preferred polyester polyols are available from Creanova under the trade name DYNACOL and the designations 7381, 7360 and 7330, with 7381, most preferred.
- the isocyanate functional component may further comprise a polyfunctional isocyanate for the purpose of improving the modulus of the composition in the cured form.
- Polyfunctional as used in the context of the isocyanates refers to isocyanates having a functionality of 2.4 or greater.
- the polyisocyanates can be any having a nominal functionality of about 2.4 or greater, more preferably about 2.7 or greater.
- the polyfunctional isocyanates have a nominal functionality of about 5 or less, even more preferably about 4.5 or less and most preferably about 4.2 or less.
- the polyfunctional isocyanates can be any isocyanates which are reactive with the isocyanate polyisocyanate prepolymers used in the composition and which improve the modulus of the cured composition.
- the polyisocyanates can be monomeric; trimeric isocyanurates or biurets of monomeric isocyanates; oligomeric or polymeric, the reaction product of several units of one or more monomeric isocyanates and can be aliphatic or aromatic.
- Examplary aliphatic polyfunctional isocyanates include trimers of hexamethylene diisocyanate, such as those available from Bayer under the trademark and designation DESMODUR N3300, DESMODUR N3400, DESMODUR N-100.
- Examplary d aromatic polyfunctional isocyanates include polymeric isocyanates such as polymeric MDI (methylene diphenyl diisocyanates) such as those marketed by The Dow Chemical Company under the trademark of PAPI or VORANATE, including VORANATE M220, PAPI 20 and PAPI 27 polymeric isocyanates.
- the polyfunctional isocyanates are present in a sufficient amount to impact the modulus of the cured compositions of the invention. If too much is used, the cure rate of the composition is unacceptably slowed down. If too little is used, the desired modulus levels are not achieved.
- the polyfunctional isocyanates are preferably present in an amount of about 0.5 percent by weight or greater based on the weight of the composition.
- the polyfunctional isocyanates are preferably present in an amount of about 35 percent by weight or less, based on the weight of the composition, more preferably about 25 percent by weight or less and most preferably about 20 percent by weight or less.
- compositions may also contain one or more catalysts which catalyzes the reaction of isocyanate moieties with isocyanate reactive moieties, i.e. water or an active hydrogen containing compound.
- catalysts are organotin compounds, metal alkanoates, and tertiary amines. Mixtures of classes of catalysts may be used, such as a mixture of a tertiary amine and one or more of organotin compounds and metal alkanoates. Even more preferred are tertiary amines, such as dimorpholino diethyl ether, and a metal alkanoate, such as bismuth octoate.
- organotin compounds include alkyl tin oxides, stannous alkanoates, dialkyl tin carboxylates and tin mercaptides.
- Stannous alkanoates include stannous octoate.
- Alkyl tin oxides include dialkyl tin oxides, such as dibutyl tin oxide and its derivatives.
- Preferred organotin compounds are dialkyltin dicarboxylates and dialkyltin dimercaptides. Dialkyl tin dicarboxylates with lower total carbon atoms are preferred as they are more active catalysts in the compositions.
- Preferred dialkyl dicarboxylates include 1, 1-dimethyltin dilaurate, 1 , 1 -dibutyltin diacetate and 1,1 -dimethyl dimaleate.
- Preferred metal alkanoates include bismuth octoate or bismuth neodecanoate.
- the organo tin compounds or metal alkanoates may be present in an amount of about 60 parts per million or greater based on the weight of the composition, more preferably 120 parts by million or greater.
- the organo tin compounds or metal alkanoates may be present in an amount of about 1.0 percent or less based on the weight of the composition, more preferably 0.5 percent by weight or less and most preferably 0.2 percent by weight or less.
- Exemplary tertiary amine catalysts include dimorpholinodialkyl ether, a di((dialkyl- morpholino)alkyl)ether, bis-(2-dimethylaminoethyl)ether, triethylene diamine, pentamethyldi- ethylene triamine, N,N-dimethylcyclohexylamine, ⁇ , ⁇ -dimethyl piperazine 4-methoxyethyl mor- pholine, N-methylmorpholine, N-ethyl morpholine, diazabicyclo compounds and mixtures thereof.
- a preferred dimorpho-linodialkyl ether is dimorpholinodiethyl ether.
- a preferred di((dialkylmorpholino)alkyl)ether is (di-(2-(3,5-dimethylmorpholino)ethyl)-ether).
- Diazabicyclo compounds are compounds which have diazobicyclo structures.
- Preferred diazabicyclo compounds include diazabicycloalkanes and diazabicyclo alkene salts.
- the catalyst may comprise one or more diazabicycloalkanes and one or more diazabicyclo alkene salts.
- the mole ratio of the one or more diazabicycloalkanes to the one or more diazabicycloalkene salts is preferably about 1 :9 or greater; more preferably about 2:8 or greater; and most preferably about 4:6 or greater.
- the mole ratio of the one or more diazabicycloalkanes to the one or more diazabicycloalkene salts is preferably about 9: 1 or less; more preferably about 8:2 or less; and most preferably about 6:4 or less.
- Preferred diazabicycloalkanes include diazabicyclooctane, available from Air Products under the trademark and designations, DABCO, DAB CO WT, DAB CO DC 1, DAB CO DC 2, and DABCO DC 21.
- Preferred diazabicycloalkene salts include diazabicycloundecene in the phenolate, ethylhexoate, oleate and formiate salt forms, available from Air Products under the trademark and designations, POLYCAT SA 1, POLYCAT SA 1/10, POLYCAT SA 102 and POLYCAT SA 610.
- one or more diazabicyclo compounds and one or more organo tin or metal alkanoate compounds and/or tertiary amine catalysts are present in the adhesive system.
- Tertiary amines are preferably employed in an amount, based on the weight of the composition of about 0.01 percent by weight or greater, more preferably about 0.05 percent by weight or greater, even more preferably about 0.1 percent by weight or greater and most preferably about 0.2 percent by weight or greater and about 2.0 percent by weight or less, more preferably about 1.5 percent by weight or less, and most preferably about 1.2 percent by weight or less.
- the composition of this invention may further comprise stabilizers, which function to protect the adhesive composition from moisture, thereby inhibiting advancement and preventing premature crosslinking of the isocyanates in the curable composition.
- Stabilizers known to the skilled artisan for moisture curing adhesives may be used preferably herein. Included among such stabilizers are diethylmalonate, alkylphenol alkylates, paratoluene sulfonic isocyanates, benzoyl chloride, phosphoric acid and orthoalkyl formates.
- Such stabilizers are preferably used in an amount of about 0.1 parts by weight or greater based on the total weight of the curable composition, preferably about 0.5 parts by weight or greater and more preferably about 0.8 parts by weight or greater.
- Such stabilizers are used in an amount of about 5.0 parts by weight or less based on the weight of the curable composition, more preferably about 2.0 parts by weight or less and most preferably about 1.4 parts by weight or less.
- the composition may further comprise an adhesion promoter, such as those disclosed in Mahdi, U.S. Patent Publication 2002/0100550 paragraphs 0055 to 0065 and Hsieh, U.S. 6,015,475 column 5, line 27 to column 6, line 41 incorporated herein by reference.
- the adhesion promoter contains a silane present in some form.
- Preferable methods of including silane functionality in the compositions are disclosed in Wu et al., U.S. Patent 6,512,033 at column 5, line 38 to column 7, line 27; U.S. Patents 5,623,044; 4,374,237; 4,345,053 and 4,625,012, relevant portions incorporated herein by reference.
- the silane may be blended with the prepolymer.
- such silane is a mercapto-silane or an amino- silane and more preferably is a mercapto-trialkoxy-silane or an amino-trialkoxy silane.
- the silanes having, active hydrogen atoms reactive with isocyanate moieties can be reacted with the terminal isocyanate moieties of the prepolymer.
- Such reaction products are disclosed in U.S. Pat. No.
- silanes having reactive hydrogen moieties reactive with isocyanate moieties can be reacted into the backbone of the prepolymer by reacting such silane with the starting materials during the preparation of the prepolymer.
- the process for the preparation of prepolymers containing silane in the backbone is disclosed in U.S. Pat. No. 4,625,012, relevant portions incorporated herein by reference.
- Such silane having active hydrogen moieties, can be reacted with a polyisocyanate to form an adduct which is blended with the prepolymer reacted with a polyurethane prepolymer or reacted with a polyisocyanate and a compound having on average more than one moiety reactive with an isocyanate moiety.
- the adduct is a reaction product of a secondary amino- or mercapto-alkoxy silane and a polyisocyanate, the adduct having an average of at least one silane group and at least one isocyanate group per molecule (hereinafter "adduct").
- Exemplary polyisocyanates for use in preparing the adduct include those described above as suitable for use in preparing the prepolymer, particularly including isophorone diisocyanate, polymethyl-ene polyphenyliso- cyanates, and aliphatic polyisocyanate such as hexamethylene diisocyanate.
- Exemplary organo functional silanes useful as adhesion promoters or to prepare adducts include amino- or mercapto- alkoxy silanes, isocyanato alkoxy silanes, methacryloxy silanes, epoxy alkoxy silanes, alkenyl alkoxy silanes and the like.
- Examples of such compounds include: N,N-bis[(3-triethoxysilyl) propylamine; ⁇ , ⁇ -bis [(3-tripropoxy-silyl) propylamine; N-(3-trimethoxy-silyl) propyl-3-[N-(3- trimethoxysilyl)-propyl amino]propionamide; N-(3 -triethoxysilyl)propyl-3 - [N-3 -triethoxysilyl)- propylamino]propionamide; N-(3 -trimethoxysilyl)propyl-3 - [N-3 -triethoxy-silyl)-propylamino] - pro-pionamide; 3-trimethoxysilylpropyl 3-[N-(3-trimethoxysilyl)propylamino]-2-methyl propionate; 3-triethoxysilyl propyl 3-[N-(3-triethoxysilyl)-propy
- the organo functional silane is gamma-mercaptopropyl-trimethoxysilane (available as A189 from Union Carbide) or N,N'-bis((3-trimethoxysilyl) propylamine.
- the amount of adhesion promoter present is that amount which enhances the adhesion of the adhesive to the substrate surface.
- the amount of adhesion promoter present is preferably about 0.1 percent by weight or greater based on the weight of the adhesive and most preferably about 0.5 percent by weight or greater.
- the amount of adhesion promoter used is preferably about 10 percent by weight or less and most preferably about 2.0 percent by weight or less.
- the adhesion promoter can be located in either or both parts of a two part adhesive or in a one part adhesive.
- compositions of this invention may be used in the compositions of this invention. Such materials are well known to those skilled in the art and may include ultraviolet stabilizers and antioxidants and the like. As used herein all parts by weight relative to the components of the curable composition are based on 100 total parts by weight of the curable composition.
- the compositions may further comprise components commonly used in molding parts such as mold release agents, fillers, conductive components and the like.
- compositions used to form foams such compositions may further comprise ingredients commonly used in foam forming compositions, such as blowing agents, mold release agents, skin forming agents and the like.
- the composition may be formulated by blending the components together using means well known in the art. Generally, the components are blended in a suitable mixer. Such blending is preferably conducted in an inert atmosphere in the absence of oxygen, for instance under vacuum, and atmospheric moisture to prevent premature reaction. It may be advantageous to add plasticizers to the reaction mixture for preparing the isocyanate functional prepolymers so that such mixtures may be easily mixed and handled. Alternatively, the plasticizers can be added during blending of all the components. Preferably, the materials are blended under vacuum or an inert gas, such as nitrogen or argon. The ingredients are blended for a sufficient time to prepare a well blended mixture, preferably from about 10 to about 60 minutes.
- the aliphatic isocyanate containing component may be added to the reaction mixture utilized to prepare a prepolymer, such as a prepolymer containing aromatic isocyanate groups, after formation of the prepolymer is complete. This may be achieved without cooling the reaction mixture or can be achieved after the reaction mixture cools.
- the prepolymers are prepared prior to blending the components to form the two parts of the curable composition. The two parts of the composition are blended separately. Once the composition is formulated, it is packaged in a suitable container such that it is protected from moisture and oxygen to prevent premature crosslinking of the prepolymers containing isocyanate groups.
- compositions may be used to bond a variety of substrates together as described hereinbefore.
- the two parts are contacted.
- the contacted composition is applied to a substrate and the composition on the first substrate is thereafter contacted with a second substrate.
- the surfaces to which the composition is applied are cleaned and/or activated and/or primed prior to application; see for example, U.S. Patents 4,525,51 1 ; 3,707,521 and 3,779,794, all are incorporated herein by reference in their entirety.
- Curing can be accelerated by applying heat to the curing composition by means of convection heat, impingement heat, IR heating, induction heating, microwave heating and the like.
- the adhesive composition is formulated to provide an open time of at least about 3 minutes or greater more preferably about 5 minutes or greater.
- Open time is understood to mean the time after application of the composition to a first substrate until it starts to become a high viscous paste and is not subject to deformation during assembly to conform to the shape of the second substrate and to adhere to it.
- the compositions preferably exhibit tack free times of about 3 minutes or greater and most preferably about 5 minutes or greater.
- the compositions preferably exhibit lap shear strengths after one hour of about 0.5 MPa or greater, more preferably about 1.0 MPa or greater and most preferably about 3.5 MPa or greater.
- compositions preferably exhibit lap shear strengths after four hours of about 3.0 MPa or greater, more preferably about 5.0 MPa or greater and most preferably about 9.0 MPa or greater.
- the compositions preferably exhibit lap shear strengths after seven days of about 8.0 MPa or greater and more preferably about 15.0 MPa or greater.
- the components of two-part compositions are mixed.
- the volume ratio at which the two parts are combined is preferably a convenient whole number.
- Such dispensers with static mixing are shown in U.S. Patent Numbers 4,538,920 and 5,082, 147 (incorporated herein by reference) and are available from Conprotec, Inc. (Salem, New Jersey) under the trade name MIXPAC or SULZERTM QUADRO of Sulzer Ltd., Switzerland.
- these dispensers use a pair of tubular receptacles arranged side-by-side with each tube being intended to receive one of the two parts of the polymerizable composition.
- Two plungers, one for each tube are simultaneously advanced (e.g., manually or by a hand-actuated ratcheting mechanism) to evacuate the contents of the tubes into a common, hollow, elongated mixing chamber that may also contain a static mixer to facilitate blending of the two parts.
- the blended polymerizable composition is extruded from the mixing chamber onto a substrate.
- electrically-driven equipment dynamic mixing may be used.
- the volumetric ratio at which the two parts of the polymerizable composition are combined is controlled by the diameter of the tubes. (Each plunger is sized to be received within a tube of fixed diameter, and the plungers are advanced into the tubes at the same speed.)
- a single dispenser is often intended for use with a variety of different two-part polymerizable compositions and the plungers are sized to deliver the two parts of the polymerizable composition at a convenient mix ratio.
- Some common mix ratios are 1 : 1, 2: 1, 4: 1 and 10: 1 and can also be odd ratios.
- the two parts are blended at a mix ratio of about 1 : 1.
- the mixed two-part compositions of the invention have a suitable viscosity to allow application without dripping.
- the viscosities of the two individual components should be of the same order of magnitude.
- the components prior to cure have a viscosity of about 10 Pa.S (10,000 centipoises) or greater, more preferably about 20 Pa.S (20,000 centipoises) or greater and most preferably about 40 Pa.S (40,000 centipoises) or greater.
- the two parts of the compositions have a viscosity prior to contacting of about 300 Pa.S (300,000 centipoises) or less, more preferably about 200 Pa.S (200,000 centipoises) or less and most preferably about 150 Pa.S (150,000 centipoises) or less.
- "Viscosities" as used in this passage are determined at a shear rate of 1 reciprocal second measured with a cone plate rheometer of 20 mm diameter and 4° angle and a temperature of about 25 °C. Higher viscosities require dynamic mixing. For lower viscosities, the components may require gelling agent known in the art to prevent sag of the uncured adhesive system. Two-part adhesive compositions start to cure upon mixing the two parts.
- Molecular weights as described herein are number average molecular weights, unless otherwise specified, which may be determined by Gel Permeation Chromatography (also referred to as SEC). For polyurethane prepolymers, it is also possible to calculate approximate number average molecular weight from the equivalent ratio of the isocyanate compounds and of the polyol compounds with which they are reacted as known to the persons skilled in the art.
- Three part 1 compositions are prepared using the materials and amounts disclosed in Table 1, which are blended using the under vacuum at 60 °C for about 45 minutes so as to form an aromatic isocyanate containing prepolymer. After the prepolymer is formed, where utilized, the hexamethylene di-isocyanate based trimer is added after blending all of the other components under vacuum without cooling the mixture.
- Part 2 is prepared by blending the materials and amounts listed in Table 2 under a vacuum at ambient temperatures for about 45 minutes.
- Lap shear samples are prepared using steel substrates of 100 x 25 x 1 mm.
- the adhesive area is 25 mm x 10 mm x 2 mm.
- Part 2 is contacted separately with the Part 1 samples and applied to one of the steel surfaces using an air driven dual cartridge gun with a static Sulzer Quadro 8.7 x 24 mixer at a 1.0 to 1.0 volume mixing ratio.
- the samples are cured at ambient temperature for the recited cure time and tested for lap shear strength using a tensile testing machine according to test method DIN 1465 and pull rate of 10 mm/min.
- Voranol CP 4610 polyol having a molecular weight of 4500.
- Glycerin initiated polyglycol amine Jeffamine 400 polyamine, having a molecular weight of 400.
- Monoethylene glycol Monoethylene glycol
- Lap shear samples are tested as described before.
- the tack free time is tested according to following procedure: A bead of sample material (approx. 30 - 50 cm of length and 10 mm wide; approx. 0.5 g/mm) is applied on the PE-foil. In short intervals, the sample is touched lightly with the wooden spatula until no material is pulled of the bead. The difference between the start and the final time is the tack free time. E-Modulus, tensile strength and elongation are tested according to DIN 53304. The results are compiled in Table 3.
- Table 3 illustrates the physical properties and the curing behavior depending on aromatic and total Isocyanate index.
- Figure 1 plots the lap shear strength against the cure time.
- Figure 2 compares the tack free time of the adhesives containing the three resins.
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Inorganic Chemistry (AREA)
- Dispersion Chemistry (AREA)
- Polyurethanes Or Polyureas (AREA)
- Adhesives Or Adhesive Processes (AREA)
Priority Applications (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
BR112014019936A BR112014019936A8 (pt) | 2012-02-21 | 2013-01-29 | Composição e método para colar dois ou mais substratos |
CN201380010315.8A CN104136473B (zh) | 2012-02-21 | 2013-01-29 | 具有改良固化速度的含有芳族异氰酸酯官能组分和脂族芳族异氰酸酯官能组分的组合物 |
EP13703278.5A EP2817346B1 (en) | 2012-02-21 | 2013-01-29 | Compositions containing aromatic isocyanate functional components and aliphatic aromatic isocyanate functional components having improved cure speed |
US14/379,644 US9493604B2 (en) | 2012-02-21 | 2013-01-29 | Compositions containing aromatic isocyanate functional components and aliphatic aromatics isocyanate functional components having improved cure speed |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201261601189P | 2012-02-21 | 2012-02-21 | |
US61/601,189 | 2012-02-21 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2013126183A1 true WO2013126183A1 (en) | 2013-08-29 |
Family
ID=47679098
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2013/023571 WO2013126183A1 (en) | 2012-02-21 | 2013-01-29 | Compositions containing aromatic isocyanate functional components and aliphatic aromatic isocyanate functional components having improved cure speed |
Country Status (5)
Country | Link |
---|---|
US (1) | US9493604B2 ( ) |
EP (1) | EP2817346B1 ( ) |
CN (1) | CN104136473B ( ) |
BR (1) | BR112014019936A8 ( ) |
WO (1) | WO2013126183A1 ( ) |
Families Citing this family (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN107000311A (zh) * | 2014-10-16 | 2017-08-01 | 陶氏环球技术有限责任公司 | 增材制造方法 |
KR102578732B1 (ko) * | 2015-06-18 | 2023-09-15 | 다우 글로벌 테크놀로지스 엘엘씨 | 적외선으로 경화된 잠재적 2-성분 폴리우레탄 접착제 |
DE102016222129A1 (de) * | 2016-11-10 | 2018-05-17 | Sig Technology Ag | Verfahren zum Bedrucken eines Laminats zum Herstellen formstabiler Nahrungsmittelbehälter mit Aufbringen einer Grundierung mit Überdosierung von Isocyanatgruppen |
US20210238341A1 (en) * | 2018-04-13 | 2021-08-05 | Covestro Intellectual Property Gmbh & Co. Kg | Adducts of amine catalysts for producing isocyanurate polymers |
US11859109B2 (en) | 2018-07-02 | 2024-01-02 | Ddp Specialty Electronic Materials Us, Llc | Primerless polyurethane adhesive compositions |
CA3115106A1 (en) * | 2018-10-23 | 2020-04-30 | Presidium Usa, Inc. | Polyol compositions |
JP7523477B2 (ja) * | 2019-06-18 | 2024-07-26 | ダウ グローバル テクノロジーズ エルエルシー | レトルト接着剤組成物 |
Citations (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3707521A (en) | 1970-03-05 | 1972-12-26 | Essex Chemical Corp | Polyurethane sealant-primer system isocyanate-reactive surface primer composition for polyurethane sealants |
US3779794A (en) | 1970-03-05 | 1973-12-18 | Essex Chemical Corp | Polyurethane sealant-primer system |
US4345053A (en) | 1981-07-17 | 1982-08-17 | Essex Chemical Corp. | Silicon-terminated polyurethane polymer |
US4374237A (en) | 1981-12-21 | 1983-02-15 | Union Carbide Corporation | Silane-containing isocyanate-terminated polyurethane polymers |
US4525511A (en) | 1984-04-06 | 1985-06-25 | Essex Specialty Products, Inc. | Method and compositions for improving bonding to painted surfaces |
US4538920A (en) | 1983-03-03 | 1985-09-03 | Minnesota Mining And Manufacturing Company | Static mixing device |
US4625012A (en) | 1985-08-26 | 1986-11-25 | Essex Specialty Products, Inc. | Moisture curable polyurethane polymers |
US5082147A (en) | 1988-02-29 | 1992-01-21 | Richard Jacobs | Composition dispensing system |
US5143996A (en) * | 1987-08-20 | 1992-09-01 | Ashland Oil, Inc. | Primerless adhesive for fiberglass reinforced polyester substrates |
US5623044A (en) | 1992-10-13 | 1997-04-22 | Essex Specialty Products, Inc. | Polyurethane sealant compositions |
US6015475A (en) | 1997-01-29 | 2000-01-18 | Essex Specialty Products, Inc. | Polyurethane sealant compositions |
US20020100550A1 (en) | 1998-04-27 | 2002-08-01 | Mahdi Syed Z. | Method of bonding a window to a substrate using a silane functional adhesive composition |
US6512033B1 (en) | 1999-02-05 | 2003-01-28 | Essex Specialty Products Inc. | Polyurethane sealant compositions |
US6709539B2 (en) | 2000-08-07 | 2004-03-23 | Dow Global Technologies Inc. | One-part moisture curable polyurethane adhesive |
EP1433802A1 (en) | 2002-12-23 | 2004-06-30 | Dow Automotive AG | Polyurethane reactive composition |
WO2009015149A1 (en) * | 2007-07-23 | 2009-01-29 | Dow Global Technologies Inc. | Two part polyurethane curable composition having substantially consistent g-modulus across the range of use temperatures |
US7892395B2 (en) | 2006-12-21 | 2011-02-22 | Dow Global Technologies Inc. | Composition useful as an adhesive for installing vehicle windows |
Family Cites Families (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0195975A3 (de) | 1985-03-25 | 1987-06-03 | L. GIVAUDAN & CIE Société Anonyme | Bicyclisches Keton, Verfahren zu dessen Herstellung und Riech- und/oder Geschmackstoffkompositionen mit einem Gehalt an diesem bicyclischen Keton |
US5041517A (en) | 1989-06-12 | 1991-08-20 | W. R. Grace & Co.-Conn. | Two-component polyurethane adhesive |
US5951796A (en) | 1997-06-23 | 1999-09-14 | Polyfoam Products, Inc. | Two component polyurethane construction adhesive and method of using same |
US6423810B1 (en) | 2001-02-05 | 2002-07-23 | Lord Corporation | High strength, long-open time structural polyurethane adhesive and method of use thereof |
EP1524282A1 (de) | 2003-10-15 | 2005-04-20 | Sika Technology AG | Zweikomponentige Polyurethanzusammensetzung mit hoher Frühfestigkeit |
EP1854817A1 (de) | 2006-05-09 | 2007-11-14 | Sika Technology AG | Zweikomponentige Polyurethanzusammensetzung mit hoher Frühfestigkeit |
EP2011808A1 (de) | 2007-07-03 | 2009-01-07 | Bayer MaterialScience AG | Medizinische Klebstoffe für die Chirurgie |
-
2013
- 2013-01-29 WO PCT/US2013/023571 patent/WO2013126183A1/en active Application Filing
- 2013-01-29 US US14/379,644 patent/US9493604B2/en active Active
- 2013-01-29 EP EP13703278.5A patent/EP2817346B1/en active Active
- 2013-01-29 BR BR112014019936A patent/BR112014019936A8/pt not_active IP Right Cessation
- 2013-01-29 CN CN201380010315.8A patent/CN104136473B/zh active Active
Patent Citations (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3707521A (en) | 1970-03-05 | 1972-12-26 | Essex Chemical Corp | Polyurethane sealant-primer system isocyanate-reactive surface primer composition for polyurethane sealants |
US3779794A (en) | 1970-03-05 | 1973-12-18 | Essex Chemical Corp | Polyurethane sealant-primer system |
US4345053A (en) | 1981-07-17 | 1982-08-17 | Essex Chemical Corp. | Silicon-terminated polyurethane polymer |
US4374237A (en) | 1981-12-21 | 1983-02-15 | Union Carbide Corporation | Silane-containing isocyanate-terminated polyurethane polymers |
US4538920A (en) | 1983-03-03 | 1985-09-03 | Minnesota Mining And Manufacturing Company | Static mixing device |
US4525511A (en) | 1984-04-06 | 1985-06-25 | Essex Specialty Products, Inc. | Method and compositions for improving bonding to painted surfaces |
US4625012A (en) | 1985-08-26 | 1986-11-25 | Essex Specialty Products, Inc. | Moisture curable polyurethane polymers |
US5143996A (en) * | 1987-08-20 | 1992-09-01 | Ashland Oil, Inc. | Primerless adhesive for fiberglass reinforced polyester substrates |
US5082147A (en) | 1988-02-29 | 1992-01-21 | Richard Jacobs | Composition dispensing system |
US5623044A (en) | 1992-10-13 | 1997-04-22 | Essex Specialty Products, Inc. | Polyurethane sealant compositions |
US6015475A (en) | 1997-01-29 | 2000-01-18 | Essex Specialty Products, Inc. | Polyurethane sealant compositions |
US20020100550A1 (en) | 1998-04-27 | 2002-08-01 | Mahdi Syed Z. | Method of bonding a window to a substrate using a silane functional adhesive composition |
US6512033B1 (en) | 1999-02-05 | 2003-01-28 | Essex Specialty Products Inc. | Polyurethane sealant compositions |
US6709539B2 (en) | 2000-08-07 | 2004-03-23 | Dow Global Technologies Inc. | One-part moisture curable polyurethane adhesive |
EP1433802A1 (en) | 2002-12-23 | 2004-06-30 | Dow Automotive AG | Polyurethane reactive composition |
EP1578834A1 (en) | 2002-12-23 | 2005-09-28 | Dow Global Technologies Inc. | Polyurethane reactive composition |
US6965008B2 (en) | 2002-12-23 | 2005-11-15 | Dow Global Technologies Inc. | Polyurethane reactive composition |
US7892395B2 (en) | 2006-12-21 | 2011-02-22 | Dow Global Technologies Inc. | Composition useful as an adhesive for installing vehicle windows |
WO2009015149A1 (en) * | 2007-07-23 | 2009-01-29 | Dow Global Technologies Inc. | Two part polyurethane curable composition having substantially consistent g-modulus across the range of use temperatures |
US20090044907A1 (en) | 2007-07-23 | 2009-02-19 | Dow Global Technologies Inc. | Two part polyurethane curable composition having substantially consistent g-modulus across the range of use temperatures |
Non-Patent Citations (1)
Title |
---|
WOHLER, JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, vol. 49, 1927, pages 3181 |
Also Published As
Publication number | Publication date |
---|---|
BR112014019936A8 (pt) | 2017-07-11 |
US20150013904A1 (en) | 2015-01-15 |
CN104136473A (zh) | 2014-11-05 |
US9493604B2 (en) | 2016-11-15 |
CN104136473B (zh) | 2016-12-07 |
BR112014019936A2 ( ) | 2017-06-20 |
EP2817346A1 (en) | 2014-12-31 |
EP2817346B1 (en) | 2017-04-26 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP2655459B1 (en) | Curable compositions containing isocyanate functional components and having improved durability in the cured state | |
US8399595B2 (en) | Two part polyurethane curable composition having substantially consistent G-modulus across the range of use temperatures | |
EP2118162B1 (en) | Adhesive useful for installing vehicle windows | |
EP2817346B1 (en) | Compositions containing aromatic isocyanate functional components and aliphatic aromatic isocyanate functional components having improved cure speed | |
US11180686B2 (en) | Accelerate cure of moisture curable polyurethane adhesive compositions useful for bonding glass | |
EP2382254B1 (en) | Adhesive useful for installing vehicle windows providing rapid drive away time | |
US11732080B2 (en) | Compositions containing hydrophobic modified isocyanate functional prepolymer containing adhesives | |
EP3688061A1 (en) | Isocyanate functional adhesive wihich bonds primerless to silanated acrylic polyol based coating | |
EP2904039B1 (en) | Accelerated bonding of isocyanate functional adhesive to fiber reinforced plastics | |
EP3746493B1 (en) | Adhesive useful for installing vehicle windows | |
EP3746495B1 (en) | Adhesive useful for installing vehicle windows | |
US20220228045A1 (en) | Accelerate cure polyurethane adhesive composition |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 13703278 Country of ref document: EP Kind code of ref document: A1 |
|
DPE1 | Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101) | ||
ENP | Entry into the national phase |
Ref document number: 2014557669 Country of ref document: JP Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 14379644 Country of ref document: US |
|
REEP | Request for entry into the european phase |
Ref document number: 2013703278 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2013703278 Country of ref document: EP |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
REG | Reference to national code |
Ref country code: BR Ref legal event code: B01A Ref document number: 112014019936 Country of ref document: BR |
|
NENP | Non-entry into the national phase |
Ref country code: JP |
|
ENP | Entry into the national phase |
Ref document number: 112014019936 Country of ref document: BR Kind code of ref document: A2 Effective date: 20140812 |