WO2013110798A1 - Acier pour la production de pièces destinées aux voies ferrées, aux croisements et aiguillages ferroviaires, et procédé destiné à la production desdites pièces - Google Patents

Acier pour la production de pièces destinées aux voies ferrées, aux croisements et aiguillages ferroviaires, et procédé destiné à la production desdites pièces Download PDF

Info

Publication number
WO2013110798A1
WO2013110798A1 PCT/EP2013/051517 EP2013051517W WO2013110798A1 WO 2013110798 A1 WO2013110798 A1 WO 2013110798A1 EP 2013051517 W EP2013051517 W EP 2013051517W WO 2013110798 A1 WO2013110798 A1 WO 2013110798A1
Authority
WO
WIPO (PCT)
Prior art keywords
railway
steel
rail
switches
crossings
Prior art date
Application number
PCT/EP2013/051517
Other languages
English (en)
Inventor
Lifen DENG
Vijay Jerath
Shreekant Jaiswal
Original Assignee
Tata Steel Uk Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tata Steel Uk Ltd filed Critical Tata Steel Uk Ltd
Priority to RU2014134530A priority Critical patent/RU2014134530A/ru
Priority to US14/373,741 priority patent/US20150028165A1/en
Priority to CN201380012280.1A priority patent/CN104160058A/zh
Priority to JP2014553744A priority patent/JP2015510548A/ja
Priority to MX2014008972A priority patent/MX2014008972A/es
Priority to AU2013213544A priority patent/AU2013213544A1/en
Priority to BR112014018242A priority patent/BR112014018242A2/pt
Priority to KR1020147023571A priority patent/KR20140119153A/ko
Priority to EP13702617.5A priority patent/EP2807283A1/fr
Publication of WO2013110798A1 publication Critical patent/WO2013110798A1/fr
Priority to HK15103913.1A priority patent/HK1203572A1/xx

Abstract

La présente invention concerne un acier forgé destiné à la production de pièces destinées aux voies ferrées, aux croisements ferroviaires ou aux aiguillages ferroviaires comprenant (pourcentage en poids) : - 0,01 - 0,15 % de carbone ; - au plus 0,5 % de silicium ; - 10 - 15 % de manganèse ; - au moins 0,6 à 3,95 % de molybdène ; - éventuellement un ou plusieurs parmi les éléments suivants i. 0,05 à 0,2 % de nickel et/ou ii. 0,05 à 0,2 % de cobalt et/ou iii. 0,02 à 0,30 % de Cr et/ou iv. 0,05 à 0,2 % de cuivre ; v. au plus 5 ppm d'H ; vi. au plus 0,20 % de V ; vii. au plus 0,10 % de Nb ; viii. au plus 0,20 % de Ti et/ou de Zr ; ix. au plus 50 ppm de B ; x. au plus 250 ppm de N ; xi. au plus 0,2 % d'Al ; xii. au plus 0,08 % de S ; xiii. au plus 0,08 % de P ; xiv. au plus 1,5 % de W ; - et le reste étant du fer et des impuretés inévitables. En outre, l'invention concerne un procédé de production de l'acier forgé et son utilisation.
PCT/EP2013/051517 2012-01-25 2013-01-25 Acier pour la production de pièces destinées aux voies ferrées, aux croisements et aiguillages ferroviaires, et procédé destiné à la production desdites pièces WO2013110798A1 (fr)

Priority Applications (10)

Application Number Priority Date Filing Date Title
RU2014134530A RU2014134530A (ru) 2012-01-25 2013-01-25 Сталь для изготовления деталей железнодорожного пути, железнодорожных пересечений и стрелочных переводов и способ изготовления указанных деталей
US14/373,741 US20150028165A1 (en) 2012-01-25 2013-01-25 Steel for producing parts for railway, railway crossings and switches and method for producing said parts
CN201380012280.1A CN104160058A (zh) 2012-01-25 2013-01-25 用于生产轨道、轨道交叉口和转辙器的零件的钢以及生产所述零件的方法
JP2014553744A JP2015510548A (ja) 2012-01-25 2013-01-25 鉄道線路、鉄道線路クロッシング及びポイント用の部品を製造するための鋼、及び該部品の製造方法
MX2014008972A MX2014008972A (es) 2012-01-25 2013-01-25 Acero para producir partes para vias ferreas, desvios y cruces ferroviarios y metodo para producir dichas partes.
AU2013213544A AU2013213544A1 (en) 2012-01-25 2013-01-25 Steel for producing parts for railway, railway crossings and switches and method for producing said parts
BR112014018242A BR112014018242A2 (pt) 2012-01-25 2013-01-25 aço para produção de peças para ferrovias, cruzamentos de ferrovias e desvios e método para produção das ditas peças
KR1020147023571A KR20140119153A (ko) 2012-01-25 2013-01-25 레일, 레일 크로싱 및 스위치용 부품 제조용 강 및 이들 부품의 제조 방법
EP13702617.5A EP2807283A1 (fr) 2012-01-25 2013-01-25 Acier pour la production de pièces destinées aux voies ferrées, aux croisements et aiguillages ferroviaires, et procédé destiné à la production desdites pièces
HK15103913.1A HK1203572A1 (en) 2012-01-25 2015-04-22 Steel for producing parts for railway, railway crossings and switches and method for producing said parts

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
EP12152514 2012-01-25
EP12152514.1 2012-01-25
US201261595014P 2012-02-03 2012-02-03
US61/595,014 2012-02-03
EP12153948.0 2012-02-03
EP12153948 2012-02-03

Publications (1)

Publication Number Publication Date
WO2013110798A1 true WO2013110798A1 (fr) 2013-08-01

Family

ID=48872901

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2013/051517 WO2013110798A1 (fr) 2012-01-25 2013-01-25 Acier pour la production de pièces destinées aux voies ferrées, aux croisements et aiguillages ferroviaires, et procédé destiné à la production desdites pièces

Country Status (11)

Country Link
US (1) US20150028165A1 (fr)
EP (1) EP2807283A1 (fr)
JP (1) JP2015510548A (fr)
KR (1) KR20140119153A (fr)
CN (1) CN104160058A (fr)
AU (1) AU2013213544A1 (fr)
BR (1) BR112014018242A2 (fr)
HK (1) HK1203572A1 (fr)
MX (1) MX2014008972A (fr)
RU (1) RU2014134530A (fr)
WO (1) WO2013110798A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3088554A4 (fr) * 2013-12-24 2016-12-14 Posco Matériau à base d'acier ayant d'excellentes soudabilité et résistance au choc de la partie soudée

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11055942B2 (en) 2017-08-01 2021-07-06 The Chamberlain Group, Inc. System and method for facilitating access to a secured area
US10713869B2 (en) 2017-08-01 2020-07-14 The Chamberlain Group, Inc. System for facilitating access to a secured area
JP6801747B2 (ja) * 2018-06-28 2020-12-16 Ｊｆｅスチール株式会社 オーステナイト系レールの製造方法
CN113668299B (zh) * 2021-08-20 2023-04-25 宜兴市鑫煜科技有限公司 一种铁路轨道电车岔道用整铸型辙叉结构及其制备工艺

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB935814A (en) * 1961-10-21 1963-09-04 Huettenwerk Oberhausen Ag Improvements in and relating to the production of wear-resistant self-hardening homogeneous rails
GB2007257A (en) * 1977-11-03 1979-05-16 Creusot Loire Austenitic manganese steel for railway frogs
CN1208776A (zh) * 1998-06-19 1999-02-24 四川工业学院 高速准高速铁路道叉高性能耐磨钢
US6315844B1 (en) * 1997-08-14 2001-11-13 Bwg Butzbacher Weichenbau Gesellschaft Mbh & Co. Kg Method for producing high-strength track element and track element thus obtained
GB2385862A (en) * 2002-02-27 2003-09-03 Edgar Allen Ltd A Cast Austenitic Manganese-Nickel Steel

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS60128242A (ja) * 1983-12-15 1985-07-09 Nippon Steel Corp 非磁性ドリルカラ−用高マンガン鋼
JP2533935B2 (ja) * 1989-06-10 1996-09-11 株式会社神戸製鋼所 耐ＳＲ脆化特性が優れ、且つ高強度、高靭性を有する高Ｍｎ非磁性鋼の製造方法
CN100484701C (zh) * 2005-10-17 2009-05-06 大连交通大学 高锰钢辙叉心轨的锻造(轧制)生产方法
CN100463992C (zh) * 2007-06-12 2009-02-25 燕山大学 锻造(轧制)耐磨奥氏体高锰钢及其制造工艺

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB935814A (en) * 1961-10-21 1963-09-04 Huettenwerk Oberhausen Ag Improvements in and relating to the production of wear-resistant self-hardening homogeneous rails
GB2007257A (en) * 1977-11-03 1979-05-16 Creusot Loire Austenitic manganese steel for railway frogs
US6315844B1 (en) * 1997-08-14 2001-11-13 Bwg Butzbacher Weichenbau Gesellschaft Mbh & Co. Kg Method for producing high-strength track element and track element thus obtained
CN1208776A (zh) * 1998-06-19 1999-02-24 四川工业学院 高速准高速铁路道叉高性能耐磨钢
GB2385862A (en) * 2002-02-27 2003-09-03 Edgar Allen Ltd A Cast Austenitic Manganese-Nickel Steel

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
FLETCHER; BEYNON: "Development of a machine for closely controlled rolling contact fatigue and wear testing", J. TEST. EVAL., vol. 28, 2000, pages 267 - 275

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3088554A4 (fr) * 2013-12-24 2016-12-14 Posco Matériau à base d'acier ayant d'excellentes soudabilité et résistance au choc de la partie soudée
US10301707B2 (en) 2013-12-24 2019-05-28 Posco Steel having excellent weldability and impact toughness of welding zone

Also Published As

Publication number Publication date
MX2014008972A (es) 2015-03-19
HK1203572A1 (en) 2015-10-30
EP2807283A1 (fr) 2014-12-03
RU2014134530A (ru) 2016-03-20
US20150028165A1 (en) 2015-01-29
BR112014018242A2 (pt) 2017-07-04
JP2015510548A (ja) 2015-04-09
AU2013213544A1 (en) 2014-08-28
CN104160058A (zh) 2014-11-19
KR20140119153A (ko) 2014-10-08

Similar Documents

Publication Publication Date Title
KR101988144B1 (ko) 재질 균일성이 우수한 후육 고인성 고장력 강판 및 그 제조 방법
US9945014B2 (en) High-manganese wear resistant steel having excellent weldability and method for manufacturing same
US20150028165A1 (en) Steel for producing parts for railway, railway crossings and switches and method for producing said parts
KR20130025947A (ko) 용접부 인성과 내지연 파괴 특성이 우수한 내마모 강판
AU2009216933B2 (en) Rail steel with an excellent combination of wear properties and rolling contact fatigue resistance
CA2886286A1 (fr) Procede de production d'acier fondu a haute resistance a l'usure et acier presentant lesdites caracteristiques
JP2021509144A (ja) 疲労亀裂伝播抑制特性に優れた構造用高強度鋼材及びその製造方法
EP2785890B1 (fr) Aciers pour rails avec excellente combinaison de propriétés d'usure, de résistance à la fatigue en contact roulant et de soudabilité
KR100361472B1 (ko) 내마모성과 내피로특성이 우수한 구조용 강 및 그 제조 방법
WO2020012297A1 (fr) Partie de voie en acier hypereutectoïde
JP5847330B2 (ja) 靭性及び溶接性に優れた耐摩耗鋼
JP5056634B2 (ja) 疲労特性に優れた溶接継手
KR20150077549A (ko) 원유탱크용 강재 및 그 제조 방법
KR101505278B1 (ko) 원유탱크용 강재 및 그 제조방법
KR20140042105A (ko) 원유탱크용 강재 및 그 제조 방법

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13702617

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 14373741

Country of ref document: US

ENP Entry into the national phase

Ref document number: 2014553744

Country of ref document: JP

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: MX/A/2014/008972

Country of ref document: MX

NENP Non-entry into the national phase

Ref country code: DE

REEP Request for entry into the european phase

Ref document number: 2013702617

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 2013702617

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 20147023571

Country of ref document: KR

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 2014134530

Country of ref document: RU

Kind code of ref document: A

REG Reference to national code

Ref country code: BR

Ref legal event code: B01A

Ref document number: 112014018242

Country of ref document: BR

ENP Entry into the national phase

Ref document number: 2013213544

Country of ref document: AU

Date of ref document: 20130125

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 112014018242

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20140724