WO2013105699A1 - Manufacturing method of titanium alloy with high-strength and high-formability and its titanium alloy - Google Patents

Manufacturing method of titanium alloy with high-strength and high-formability and its titanium alloy Download PDF

Info

Publication number
WO2013105699A1
WO2013105699A1 PCT/KR2012/001952 KR2012001952W WO2013105699A1 WO 2013105699 A1 WO2013105699 A1 WO 2013105699A1 KR 2012001952 W KR2012001952 W KR 2012001952W WO 2013105699 A1 WO2013105699 A1 WO 2013105699A1
Authority
WO
WIPO (PCT)
Prior art keywords
temperature
titanium alloy
forming
strain
manufacturing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2012/001952
Other languages
English (en)
French (fr)
Inventor
Chan Hee Park
Chang Seok Oh
Jong Taek Yeom
Jae Keun Hong
Chong Soo Lee
Yong Taek Hyun
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Korea Institute of Machinery and Materials KIMM
Original Assignee
Korea Institute of Machinery and Materials KIMM
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Korea Institute of Machinery and Materials KIMM filed Critical Korea Institute of Machinery and Materials KIMM
Priority to US13/879,206 priority Critical patent/US9435017B2/en
Priority to JP2013553380A priority patent/JP5941070B2/ja
Publication of WO2013105699A1 publication Critical patent/WO2013105699A1/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/16—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of other metals or alloys based thereon
    • C22F1/18—High-melting or refractory metals or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/16—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of other metals or alloys based thereon
    • C22F1/18—High-melting or refractory metals or alloys based thereon
    • C22F1/183—High-melting or refractory metals or alloys based thereon of titanium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C14/00—Alloys based on titanium

Definitions

  • the present invention relates to a method of manufacturing a titanium alloy with high strength and high formability, and more particularly a titanium alloy provided with ultrafine grains with high strength/high formability through rolling that gradually changes a forming temperature in accordance with the strain under relatively low strain(strain of 2.5 or less) without using severe plastic deformation known in the art, and a method of manufacturing the titanium alloy.
  • the present invention relates to a titanium alloy having ultrafine grains with high strength/high formability by making the final temperature, at which forming is finished, a plastic instability temperature or less of an initial lamellar structure (martensite) while gradually decreasing a forming temperature into an optimized condition, by using a principle that formability increases with an increase in a fine spheroidized structure during deformation, after starting deformation at the beta transformation temperature or less and the plastic instability temperature or more of an initial lamellar structure (martensite), without simply decreasing the forming temperature during forming, and a method of manufacturing the titanium alloy.
  • a titanium alloy is typical lightweight metal and has high specific strength and excellent corrosion resistance, so that it can be used for various fields, such as a material for the aerospace industry, a material for the chemical industry, a material for bio-implant, and a material of sports products. Since the titanium alloy has a superplastic property, it is possible to reduce the weight of a product and the machining cost by performing superplastic forming. Therefore, it is possible to create a large added value by applying the titanium alloy to industries.
  • the HPT machining is a method of generating shear deformation under a high pressure and has a problem in that machining can be performed with a high speed at a room temperature, while the size of the material is limited and the thickness and the fine structure of the material are not uniform.
  • the ECAP machining is a method of generating shear deformation of a material by putting in the material to an L-shaped channel and is economical because it is possible to perform forming with existing equipment and increase the scale. Further, since the cross-sectional area of the material does not decrease even if the amount of machining increases, it is possible to provide the material with a large amount of deformation.
  • An embodiment of the present invention is directed to providing a method of manufacturing a titanium alloy (Ti-6Al-4V,Ti-6Al-2Sn-4Zr-2Mo-0.1Si,Ti-6Al-4Fe-0.25Si) with high strength and high formability, which includes: rolling that changes a titanium alloy to have ultrafine grains by rolling the titanium alloy under a low-strain condition, where the strain is 2.5 or less under a predetermined temperature change condition, where the final temperature for finishing forming is lower than the plastic instability temperature of an initial lamellar structure (martensite), while gradually decreasing a forming temperature into an optimized condition, by using a principle that formability increases with an increase in a fine spheroidized structure during deformation, after starting deformation of the titanium alloy at the beta transformation temperature or less and the plastic instability temperature or more of an initial lamellar structure (martensite), without simply decreasing the forming temperature during forming, at a predetermined deformation speed after manufacturing the titanium alloy having a lamellar structure.
  • Another embodiment of the present invention is directed to providing titanium alloys (Ti-6Al-4V, Ti-6Al-2Sn-4Zr-2Mo-0.1Si, and Ti-6Al-4Fe-0.25Si) manufactured by the manufacturing method to have ultrafine grains of which the size is 1 ⁇ m or less.
  • the present invention provides a method of manufacturing a titanium alloy with high strength and high formability, which includes: preparing a material and equipment for manufacturing a titanium alloy; manufacturing a titanium alloy having a lamellar structure (martensite structure) by cooling the prepared material with water after performing heat treatment at the beta transformation temperature or more; and rolling that makes ultrafine grains by finishing forming of the titanium alloy at a plastic instability temperature by gradually decreasing the forming temperature in accordance with an increase of a strain after starting the forming at the plastic instability temperature of more, under a condition of a low strain in which the strain is 2.5 or less, after the manufacturing of a titanium alloy having a lamellar structure.
  • the initial forming start temperature for starting the forming is the plastic instability temperature or more of an initial lamellar structure
  • the final forming temperature for finishing the forming is the plastic instability temperature or less of an initial lamellar structure
  • the process is finished while maintaining the plastic instability temperature or less of the initial lamellar structure when the strain reaches 2.5 while decreasing the temperature along a predetermined drop curve in accordance with an increase in the strain after starting the forming at a forming temperature of the plastic instability temperature or more at the initial stage.
  • the present invention provides a method of manufacturing a titanium alloy (Ti-6Al-4V) with high strength and high formability, which includes: preparing a material and equipment for manufacturing a titanium alloy (Ti-6Al-4V); manufacturing a titanium alloy having a lamellar structure (martensite structure) by cooling the prepared material with water after performing heat treatment for one hour or more under the condition of a temperature of 1040°C at the beta transformation temperature (995°C) or more; and rolling that makes ultrafine grains by finishing forming of the titanium alloy at a plastic instability temperature or less by gradually decreasing the forming temperature in accordance with an increase of strain after starting the forming at the plastic instability temperature of more, under a condition of a low strain in which the strain is 1.4 or less, after the manufacturing of a titanium alloy having a lamellar structure.
  • the forming is started at 800°C, which is an initial forming start temperature, above a plastic instability temperature of an initial lamellar structure and is finished at 600 °C, which is a final forming temperature, under the plastic instability temperature of the initial lamellar structure.
  • the forming temperature initially starts from 800°C, is decreased along a predetermined drop curve as the strain increases, and the process is finished while the temperature at 600°C when strain reaches 1.4.
  • the present invention provides a titanium alloy (Ti-6Al-4V) manufactured by the method to have ultrafine grains of which the size is 1 ⁇ m or less.
  • the present invention provides a method of manufacturing a titanium alloy (Ti-6Al-2Sn-4Zr-2Mo-0.1Si) with high strength and high formability, which includes: preparing a material and equipment for manufacturing a titanium alloy (Ti-6Al-2Sn-4Zr-2Mo-0.1Si); manufacturing a titanium alloy having a lamellar structure (martensite structure) by cooling the prepared material with water after performing heat treatment for one hour or more under the condition of a temperature of 1040°C at the beta transformation temperature (995°C) or more; and rolling that makes ultrafine grains by finishing forming of the titanium alloy at a plastic instability temperature or less by gradually decreasing the forming temperature in accordance with an increase of strain after starting the forming at the plastic instability temperature of more, under a condition of a low strain in which the strain is 1.4 or less, after the manufacturing of a titanium alloy having a lamellar structure.
  • the forming is started at 850°C, which is an initial forming start temperature, above a plastic instability temperature of an initial lamellar structure and is finished at 650 °C, which is a final forming temperature, under the plastic instability temperature of the initial lamellar structure.
  • the present invention provides a titanium alloy (Ti-6Al-2Sn-4Zr-2Mo-0.1Si) manufactured by the method to have ultrafine grains of which the size is 1 ⁇ m or less.
  • the present invention provides a method of manufacturing a titanium alloy (Ti-6Al-4Fe-0.25Si) with high strength and high formability, which includes: preparing a material and equipment for manufacturing a titanium alloy (Ti-6Al-4Fe-0.25Si); manufacturing a titanium alloy having a lamellar structure (martensite structure) by cooling the prepared material with water after performing heat treatment for one hour or more under the condition of a temperature of 1040°C at the beta transformation temperature (995°C) or more; and rolling that makes ultrafine grains by finishing forming of the titanium alloy at a plastic instability temperature or less by gradually decreasing the forming temperature in accordance with an increase of strain after starting the forming at the plastic instability temperature of more, under a condition of a low strain in which the strain is 1.4 or less, after the manufacturing of a titanium alloy having a lamellar structure.
  • the forming is started at 800°C, which is an initial forming start temperature, above a plastic instability temperature of an initial lamellar structure and is finished at 600 °C, which is a final forming temperature, under the plastic instability temperature of the initial lamellar structure.
  • Another embodiment of the present invention is directed to providing a titanium alloy (Ti-6Al-4Fe-0.25Si) manufactured by the method to have ultrafine grains of which the size is 1 ⁇ m or less.
  • titanium alloys Ti-6Al-4V,Ti-6Al-2Sn-2Mo-0.1Si, and Ti-6Al-4Fe-0.25Si
  • Ti-6Al-4V,Ti-6Al-2Sn-2Mo-0.1Si, and Ti-6Al-4Fe-0.25Si having ultrafine grains (1 ⁇ m or less) by using a small amount of energy consumption under a low strain (strain of 2.5 or less) when using the method of manufacturing a titanium alloy according to an embodiment of the present invention, not a manufacturing method using general severe plastic deformation.
  • the titanium alloys (Ti-6Al-4V, Ti-6Al-2Sn-2Mo-0.1Si, and Ti-6Al-4Fe-0.25Si) having ultrafine grains which are manufactured, as described above, can also be provided with high strength/high formability in comparison to the existing titanium alloys.
  • Fig. 1 is a flowchart illustrating a method of manufacturing a titanium alloy (Ti-6Al-4V) with high strength and high formability according to the present invention.
  • Fig. 2A is a picture showing a microstructure of a titanium alloy (Ti-6Al-4V) having an early equiaxed structure that is used for the method of manufacturing a titanium alloy (Ti-6Al-4V) with high strength and high formability according to the present invention
  • Fig. 2B is a picture of a microstructure of a titanium alloy (Ti-6Al-4V) having a lamellar (martensite) structure.
  • Figs. 3A to 3C are graphs showing true stress (MPa) according to a deformation temperature and a strain in rolling.
  • Fig. 4A is microstructure of titanium manufactured by the comparative example shown in Fig. 3B and Fig. 4B is microstructure of a titanium alloy (Ti-6Al-4V) formed by the present invention as in Fig. 3C.
  • Ti-6Al-4V titanium alloy
  • Fig. 5 is a graph showing true stress (MPa) according to a deformation temperature and a strain in compressing of Ti-6Al-2Sn-4Zr-2Mo-0.1Si that is another titanium alloy.
  • Fig. 6A is a picture showing an early structure of Ti-6Al-2Sn-4Zr-2Mo-0.1Si
  • Fig. 6B is a picture of a microstructure of a titanium alloy (Ti-6Al-2Sn-4Zr-2Mo-0.1Si) manufactured by another embodiment of the present invention.
  • Fig. 7 is a graph showing true stress (MPa) according to a deformation temperature and a strain in compressing of Ti-6Al-4Fe-0.25Si that is another titanium alloy.
  • Fig. 8A is a picture showing an early structure of Ti-6Al-4Fe-0.25Si and Fig. 8B is a picture of a microstructure of a titanium alloy (Ti-6Al-4Fe-0.25Si) manufactured by another embodiment of the present invention.
  • Fig. 9 is a graph showing a room-temperature tension property of a titanium alloy (Ti-6Al-4V) with high strength and high formability which is formed by an embodiment of the present invention.
  • Fig. 10 is a graph showing a high-temperature tension property of a titanium alloy (Ti-6Al-4V) with high strength and high formability which is formed by an embodiment of the present invention.
  • Fig. 1 is a flowchart illustrating a method of manufacturing a titanium alloy (Ti-6Al-4V) with high strength and high formability according to the present invention.
  • Fig. 2A is a picture showing a microstructure of a titanium alloy (Ti-6Al-4V) having an early equiaxed structure that is used for the method of manufacturing a titanium alloy (Ti-6Al-4V) with high strength and high formability according to the present invention
  • Fig. 2B is a picture of a microstructure of a titanium alloy (Ti-6Al-4V) having a lamellar (martensite) structure.
  • a method of manufacturing a titanium alloy with high strength and high formability includes: preparing a material and equipment for manufacturing a titanium alloy; manufacturing a titanium alloy having a lamellar structure (martensite structure) by cooling the prepared material with water after performing heat treatment at the beta transformation temperature or more; and rolling that makes ultrafine grains by finishing forming of the titanium alloy at a plastic instability temperature by gradually decreasing the forming temperature in accordance with an increase of a strain after starting the forming at the plastic instability temperature of more, under a condition of a low strain in which the strain is 2.5 or less, after the manufacturing of a titanium alloy having a lamellar structure.
  • the initial forming start temperature for starting the forming is the plastic instability temperature or more of an initial lamellar structure
  • the final forming temperature for finishing the forming is the plastic instability temperature or less of an initial lamellar structure
  • the process is finished while maintaining the plastic instability temperature or less of the initial lamellar structure when the strain reaches 2.5 while decreasing the temperature along a predetermined drop curve in accordance with an increase in the strain after starting the forming at a forming temperature of the plastic instability temperature or more at the initial stage.
  • the method of manufacturing a titanium alloy (Ti-6Al-4V) includes: preparing a material and equipment for manufacturing a titanium alloy (Ti-6Al-4V); manufacturing a titanium alloy having a lamellar structure (martensite structure) by cooling the prepared material with water after performing heat treatment for one hour or more at a temperature condition of 1040°C above the beta transformation temperature (995°C); and rolling that makes ultrafine grains by rolling the titanium alloy under the condition of a low strain, in which the strain is 1.4 or less under a predetermined temperature change condition, at a predetermined deformation speed after the manufacturing of a titanium alloy having a lamellar structure.
  • a titanium alloy material for forming is prepared in the preparation process of a titanium alloy.
  • the titanium alloy may be a titanium alloy with aluminum (Al) and vanadium (V) added to increase strength and ductility.
  • the titanium alloy of the embodiment is a so-called Ti-6Al-4V alloy containing aluminum of about 6 wt% and vanadium of about 4 wt%.
  • the Ti-6Al-4V alloy can be used in various industries because it is light and has high strength, and super plastic property is also excellent.
  • the present invention is not limited thereto and various titanium alloys other than the Ti-6Al-4V alloy may be used, which is also included in the scope of the present invention.
  • the titanium alloy may be formed in a lamellar (martensite) structure having a prior beta grain boundary of about 400 ⁇ m and an acicular thickness of about 0.3 ⁇ m by cooling the material (with water) after performing heat treatment for one hour at 1040°C above the beta transformation temperature (about 995°C).
  • Fig. 2 shows a picture of a titanium alloy having the martensite structure.
  • the titanium alloy may have a fine basket weave.
  • the basket weave has machinability that is not excellent more than an equiaxed structure, beta phases are more finely distributed than the equiaxed structure.
  • beta phases are segmented by a dynamic spheroidizing mechanism in the rolling of a titanium alloy of the embodiment, so that the alpha phases and the beta phases can be more finely and uniformly distributed after the rolling, as coMPared with an equiaxed structure is used at the initial stage.
  • the sizes of the alpha phases and the beta phases distributed in the initial martensite structure or fine basket weave are very small, they can be more finely controlled after the rolling.
  • the titanium alloy starts to be rolled at a temperature of 800°C at a strain rate of 0.1/sec and the rolling keeps performed while gradually reducing the temperature to 600°C after starting the rolling.
  • Dynamic spheroidization is sufficiently generated by rolling the titanium alloy in this condition, and recrystallizing and annealing that were performed for dynamic spheroidization after the rolling in the related art may not be performed in the embodiment.
  • torsion is generated in the early alpha phases having a lamellar structure and shear stress gradually concentrates into the alpha phases, so that equiaxed alpha phases having a grain boundary are formed at the portions where the shear stress is exerted.
  • the deformation temperature in the rolling of a titanium alloy is determined in consideration of the size of the grains after the dynamic spheroidization and rolling. Further, the more the strain, the more the degree of the dynamic spheroidization increases. As described above, torsion is generated in the alpha phases in the first step for the dynamic spheroidization, which is considered because torsion is generated in more alpha phases, as the strain increases.
  • the strain may be 0.9 or more such that the dynamic spheroidization can be uniformly generated. Considering that it is practically difficult to give a large strain over 2.0, the strain may be 0.9 to 2.0.
  • the strain is set to 1.4 or less to allow grains to be made ultrafine with a low strain (1.5 or less), so that it is possible to produce a titanium alloy having ultrafine grains by using rolling/extruding/forging equipment widely used in industry.
  • the strain rate in the rolling of a titanium alloy may be 0.1/sec in the embodiment.
  • Figs. 3A to 3C are graphs showing true stress (MPa) according to a deformation temperature and a strain in rolling.
  • Fig. 3A is a graph of a comparative example 1 showing the result of a test compressing the lamellar structure of Fig. 2B to a strain of 1.4 under the condition of a strain rate of 0.1/sec at a temperature of 600°C.
  • Fig. 3B is a graph showing the result of a test of compressing the lamellar structure of Fig. 2B to a strain of 1.4 under the condition of a strain rate of 0.1/sec at a temperature of 800°C according to a comparative example 2. It can be seen from the test result that breaking did not finally occur and forming was performed well.
  • Fig. 3C is a graph showing the result of a test that compressing the lamellar structure of Fig. 2B to a strain of 1.4 while gradually decreasing the forming temperature from 800°C to 600°C, under the condition of a strain rate of 0.1/sec, as an embodiment of the present invention.
  • FIG. 3C An embodiment of the present invention shown in Fig. 3C and a comparative example 2 shown in Fig. 3B are described more.
  • dynamic spheroidization occurs in a titanium alloy having an initial lamellar (martensite) structure at a temperature of 775°C to 975°C.
  • the deformation temperature is too low, less than 775°C, dynamic spheroidization does not occur and fine cracks are generated or shear bands are formed between the alpha phases.
  • the deformation temperature when the deformation temperature is over 975°C, that is, it is the beta transformation temperature (about 977°C) or more, beta recrystallization having a prior beta grain boundary occurs, so that dynamic spheroidization is difficult. Further, when the deformation temperature is high, the grains may be increased in size by grain growth.
  • the dynamic spheroidization fraction is generally in proportion to the strain and in inverse proportion to the deformation speed and deformation temperature. Therefore, the deformation temperature is generally set at 875°C or less.
  • the main conception of the present invention relates to a titanium alloy having ultrafine grains with high strength/high formability by making the final temperature, at which forming is finished, a plastic instability temperature or less of a lamellar structure (martensite) while gradually decreasing a forming temperature into an optimized condition, by using a principle that formability increases with an increase in a fine spheroidized structure during machining, after starting machining at the plastic instability temperature or more of an initial lamellar structure (martensite), not simply decreasing the forming temperature during forming, and a method of manufacturing the titanium alloy.
  • the plastic instability section is a section where cracks, shear bands, pores, or breaking is formed during deformation, which is generally about 750°C to 650°C when a titanium alloy has an initial lamellar structure (martensite).
  • the temperature changes from 800°C to 750°C under the condition that the strain is 0.1 to 0.2
  • the temperature changes from 750°C to 700°C under the condition that the strain is 0.3 to 0.4
  • the temperature changes from 700°C to 650°C under the condition that the strain is 0.6 to 0.7
  • a temperature of 600°C is maintained under the condition that the strain is 0.9 to 1.4.
  • Figs. 4A and 4B are microstructures of titanium manufactured by the comparative example 2 shown in Fig. 3B and titanium alloy (Ti-6Al-4V) formed by the method of manufacturing a titanium alloy (Ti-6Al-4V) according to an embodiment of the present invention.
  • Fig. 4A is an inverse pole figure of comparative example 2, in which the size of grains of a titanium alloy formed under the forming conditions of comparative example 2 is about 2 ⁇ m.
  • Fig. 4B is an inverse pole figure of grains of the titanium alloy (Ti-6Al-4V) formed through the rolling according to an embodiment of the present invention, in which the size of the grains is about 0.5 ⁇ m. Forming of the titanium alloy (Ti-6Al-4V) having ultrafine grains with the sizes of grains described above was generally possible only under a large strain of 4 to 8 in the related art.
  • Ti-6Al-4V titanium alloy having ultrafine grains, as shown in Fig. 4B, under the condition of a strain of about 1.4, using the method of manufacturing a titanium alloy (Ti-6Al-4V) according to an embodiment of the present invention.
  • Fig. 5 shows a graph illustrating another embodiment of the present invention.
  • Fig. 5 is a graph showing true stress (MPa) according to a deformation temperature and a strain in compressing of Ti-6Al-2Sn-4Zr-2Mo-0.1Si that is another titanium alloy.
  • the comparative example 3 shown in Fig. 5A shows the result of a test that makes Ti-6Al-2Sn-4Zr-2Mo-0.1Si have a lamellar structure first, and then performs compression to a strain of 1.4 with a strain rate of 0.1/sec at a forming temperature of 650°C.
  • Fig. 5B is a graph showing forming conditions in the rolling of the method of manufacturing a titanium alloy (Ti-6Al-2Sn-2Mo-0.1Si) according to another embodiment of the present invention.
  • test was performed by making a lamellar (martensite) structure first and then decreasing the forming temperature step by step from 850°C to 650°C during compression to a strain of 1.4 at a strain rate of 0.1/sec.
  • Fig. 6A is a picture showing an early structure of Ti-6Al-2Sn-4Zr-2Mo-0.1Si and Fig. 6B is a picture of a fine structure of a titanium alloy (Ti-6Al-2Sn-4Zr-2Mo-0.1Si) manufactured by another embodiment of the present invention.
  • Fig. 6A is a picture showing the state of grains of an early fine structure of a Ti-6Al-2Sn-4Zr-2Mo-0.1Si alloy, from which it can be seen that the grains have a size of about 13 ⁇ m.
  • Fig. 6B shows a fine picture of grains of a titanium alloy (Ti-6Al-2Sn-4Zr-2Mo-0.1Si) that has undergone the rolling of the method of manufacturing a titanium alloy (Ti-6Al-2Sn-4Zr-2Mo-0.1Si) according to another embodiment of the present invention.
  • the grains of the titanium alloy (Ti-6Al-2Sn-4Zr-2Mo-0.1Si) according to another embodiment of the present invention are ultrafine grains having a size of about 0.4 ⁇ m in Fig. 6B.
  • Ti-6Al-2Sn-4Zr-2Mo-0.1Si having ultrafine grains, as shown in Fig. 6B, under the condition of a strain of about 1.4, using the method of manufacturing a titanium alloy (Ti-6Al-2Sn-4Zr-2Mo-0.1Si) according to another embodiment of the present invention.
  • Fig. 7 shows a graph illustrating another embodiment of the present invention.
  • Fig. 7 is a graph showing true stress (MPa) according to a deformation temperature and a strain in compressing of Ti-6Al-4Fe-0.25Si that is another titanium alloy.
  • the comparative example shown in Fig. 7A shows the result of a test that makes Ti-6Al-4Fe-0.25Si have a lamellar structure first, and then performs compression to a strain of 1.4 with a strain rate of 0.1/sec at a forming temperature of 600°C.
  • Fig. 7B is a graph showing forming conditions in the rolling of the method of manufacturing a titanium alloy (Ti-6Al-4Fe-0.25Si) according to another embodiment of the present invention.
  • test was performed by making a lamellar (martensite) structure first and then decreasing the forming temperature step by step from 800°C to 600°C during compression to a strain of 1.4 at a strain rate of 0.1/sec.
  • Fig. 8A is a picture showing an early structure of Ti-6Al-4Fe-0.25Si and Fig. 8B is a picture of a fine structure of a titanium alloy (Ti-6Al-4Fe-0.25Si) manufactured by another embodiment of the present invention.
  • Fig. 8A is a picture showing the state of grains of an early fine structure of a Ti-6Al-4Fe-0.25Si alloy, from which it can be seen that the sizes of the grains are not uniform.
  • Fig. 8B shows a fine picture of grains of a titanium alloy (Ti-6Al-4Fe-0.25Si) that has undergone the rolling of the method of manufacturing a titanium alloy (Ti-6Al-4Fe-0.25Si) according to another embodiment of the present invention.
  • the grains of the titanium alloy (Ti-6Al-4Fe-0.25Si) according to another embodiment of the present invention are ultrafine grains having a size of about 0.7 ⁇ m in Fig. 8B.
  • Ti-6Al-4Fe-0.25Si having ultrafine grains, as shown in Fig. 8B, under the condition of a strain of about 1.4, using the method of manufacturing a titanium alloy (Ti-6Al-4Fe-0.25Si) according to another embodiment of the present invention.
  • Fig. 9 is a graph showing a room-temperature tension property of a titanium alloy (Ti-6Al-4V) with high strength and high formability which is formed by an embodiment of the present invention.
  • Fig. 10 is a graph showing a high-temperature tension property of a titanium alloy (Ti-6Al-4V) with high strength and high formability which is formed by an embodiment of the present invention.
  • a titanium alloy (Ti-6Al-4V) formed by the method of manufacturing a titanium alloy (Ti-6Al-4V) according to an embodiment of the present invention and an early titanium alloy it can be seen that the yield strength and tensile strength of the titanium alloy (Ti-6Al-4V) formed by the manufacturing method according to an embodiment of the present invention were improved in comparison to the yield strength and tensile strength of the early titanium alloy.
  • titanium alloys Ti-6Al-4V and Ti-6Al-2Sn-2Mo-0.1Si having ultrafine grains (1 ⁇ m or less) by using a small amount of energy consumption under a relatively low strain (strain of 2.5 or less) when using the method of manufacturing a titanium alloy according to an embodiment of the present invention, not a manufacturing method using general severe plastic deformation.
  • the main conception of the present invention relates to a titanium alloy having ultrafine grains with high strength/high formability by making the final temperature, at which forming is finished, a plastic instability section or less of a lamellar structure (martensite) while gradually decreasing a forming temperature into an optimized condition, by using a principle that formability increases with an increase in a fine spheroidized structure during machining, after starting machining at the plastic instability section or more of an initial lamellar structure (martensite), not simply decreasing the forming temperature during forming, and a method of manufacturing the titanium alloy.
  • the titanium alloys (Ti-6Al-4V and Ti-6Al-2Sn-2Mo-0.1Si,Ti-6Al-4Fe-0.25Si) having ultrafine grains which are manufactured, as described above, can also be provided with high strength/high formability in comparison to the existing titanium alloys.
  • the spirit of the present invention may be applied to titanium alloys having different compositions other than the compositions of the titanium alloys described herein.
  • the present invention relates to a method of manufacturing a titanium alloy with high strength and high formability, and more particularly a titanium alloy provided with ultrafine grains with high strength/high formability through rolling that gradually changes a forming temperature in accordance with the strain under relatively low strain(strain of 2.5 or less) without using severe plastic deformation known in the art, and a method of manufacturing the titanium alloy.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Metal Rolling (AREA)
  • Forging (AREA)
PCT/KR2012/001952 2012-01-11 2012-03-19 Manufacturing method of titanium alloy with high-strength and high-formability and its titanium alloy Ceased WO2013105699A1 (en)

Priority Applications (2)

Application Number Priority Date Filing Date Title
US13/879,206 US9435017B2 (en) 2012-01-11 2012-03-19 Manufacturing method of titanium alloy with high-strength and high-formability and its titanium alloy
JP2013553380A JP5941070B2 (ja) 2012-01-11 2012-03-19 高強度及び高成形性を有するチタン合金の製造方法及びこれによるチタン合金

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR10-2012-0003287 2012-01-11
KR1020120003287A KR101414505B1 (ko) 2012-01-11 2012-01-11 고강도 및 고성형성을 가지는 티타늄 합금의 제조방법 및 이에 의한 티타늄 합금

Publications (1)

Publication Number Publication Date
WO2013105699A1 true WO2013105699A1 (en) 2013-07-18

Family

ID=48781629

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2012/001952 Ceased WO2013105699A1 (en) 2012-01-11 2012-03-19 Manufacturing method of titanium alloy with high-strength and high-formability and its titanium alloy

Country Status (4)

Country Link
US (1) US9435017B2 (enExample)
JP (1) JP5941070B2 (enExample)
KR (1) KR101414505B1 (enExample)
WO (1) WO2013105699A1 (enExample)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103938139A (zh) * 2014-04-26 2014-07-23 南昌航空大学 一种经过两相区高温变形tc4-dt钛合金获得三态组织的热处理工艺方法
CN108474064A (zh) * 2015-09-16 2018-08-31 宝山钢铁股份有限公司 粉末冶金钛合金

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112974700B (zh) * 2021-02-19 2022-07-26 西北工业大学 一种实现近β型钛合金薄壁结构件组织细晶化的成形方法
CN113618082B (zh) * 2021-07-16 2022-09-13 南京理工大学 仿贝壳结构的高抗压钛合金构件和真空高能束流增材制造方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20080302451A1 (en) * 2006-07-06 2008-12-11 Vladimir Vasilievich Astanin Method of Manufacturing Semi-Finished Sheet Products From Titanium Alloy
KR20110026153A (ko) * 2009-09-07 2011-03-15 포항공과대학교 산학협력단 저 변형량에서의 나노 결정립 티타늄 합금의 제조 방법
JP2011068955A (ja) * 2009-09-25 2011-04-07 Nhk Spring Co Ltd ナノ結晶チタン合金およびその製造方法
US20110179848A1 (en) * 2008-10-22 2011-07-28 Ruslan Zufarovich Valiev Nanostructured commercially pure titanium for biomedicine and a method for producing a rod therefrom

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4442004B2 (ja) 2000-08-09 2010-03-31 大同特殊鋼株式会社 耐熱Ｔｉ合金の製造方法

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20080302451A1 (en) * 2006-07-06 2008-12-11 Vladimir Vasilievich Astanin Method of Manufacturing Semi-Finished Sheet Products From Titanium Alloy
US20110179848A1 (en) * 2008-10-22 2011-07-28 Ruslan Zufarovich Valiev Nanostructured commercially pure titanium for biomedicine and a method for producing a rod therefrom
KR20110026153A (ko) * 2009-09-07 2011-03-15 포항공과대학교 산학협력단 저 변형량에서의 나노 결정립 티타늄 합금의 제조 방법
JP2011068955A (ja) * 2009-09-25 2011-04-07 Nhk Spring Co Ltd ナノ結晶チタン合金およびその製造方法

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
CHAN HEE PARK ET AL.: "Enhanced superplasticity utilizing dynamic globurizati on of Ti-6A1-4V alloy", MATERIALS SCIENCE AND ENGINEERING A, vol. 496, 2008, pages 150 - 158, XP025432763, DOI: doi:10.1016/j.msea.2008.05.001 *

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103938139A (zh) * 2014-04-26 2014-07-23 南昌航空大学 一种经过两相区高温变形tc4-dt钛合金获得三态组织的热处理工艺方法
CN108474064A (zh) * 2015-09-16 2018-08-31 宝山钢铁股份有限公司 粉末冶金钛合金
US11008639B2 (en) 2015-09-16 2021-05-18 Baoshan Iron & Steel Co., Ltd. Powder metallurgy titanium alloys

Also Published As

Publication number Publication date
JP2014506302A (ja) 2014-03-13
KR101414505B1 (ko) 2014-07-07
JP5941070B2 (ja) 2016-06-29
US9435017B2 (en) 2016-09-06
KR20130082215A (ko) 2013-07-19
US20140305554A1 (en) 2014-10-16

Similar Documents

Publication Publication Date Title
Ditta et al. Effect of hot extrusion and optimal solution treatment on microstructure and properties of spray-formed Al-11.3 Zn-2.65 Mg-1Cu alloy
WO2013105699A1 (en) Manufacturing method of titanium alloy with high-strength and high-formability and its titanium alloy
JP7282106B2 (ja) 耐疲労破壊性を向上させた７ｘｘｘシリーズアルミ合金プレート製品の製造方法
WO2012070870A2 (ko) 상온성형성이 우수한 마그네슘 합금 판재 및 그 제조방법
CN104046934B (zh) 制备超细晶镁锌锰合金的方法
Demirtas et al. Room temperature superplaticity in fine/ultrafine grained materials subjected to severe plastic deformation
WO2020032785A1 (ko) 연질 열처리 시간 단축형 냉간 압조용 선재 및 그 제조 방법
WO2017082684A1 (ko) 냉간단조성이 우수한 선재 및 그 제조방법
JPS6046358A (ja) α＋β型チタン合金の製造方法
US20170306467A1 (en) Methods for finishing extruded titanium products
WO2021215666A1 (ko) 고물성 마그네슘 합금 가공재 및 그 제조방법
WO2020067704A1 (ko) 마그네슘 합금 판재 및 이의 제조방법
CN109079067A (zh) 高强度铝合金环件轧制成形方法
WO2021025499A1 (ko) 고강도 고성형성 베타 타이타늄 합금
WO2018117632A1 (ko) 내식성이 우수한 마그네슘 합금 및 그 제조방법
WO2018079945A1 (ko) 핫스탬핑 알루미늄 케이스의 제조방법 및 그 방법에 의해 제조된 핫스탬핑 알루미늄 케이스
CN107236887A (zh) 一种高强度高塑性变形镁合金材料及制备方法
CN106676341A (zh) 一种微合金铝基复合材料的轧制工艺
CN115233061A (zh) 一种超高塑性稀土变形镁合金板材及其制备方法
KR100768568B1 (ko) 마그네슘 재료의 상온 ｅｃａｐ 방법
WO2024225720A1 (ko) 고강도 알루미늄-아연-마그네슘-구리 합금 후판 및 그 제조방법
CN109022857B (zh) 一种提高铝合金再结晶温度的方法
WO2016117768A1 (ko) 소성 가공용 마그네슘 합금 빌렛의 제조방법 및 이를 포함하는 고강도 마그네슘 합금 가공재의 제조방법
WO2018117713A1 (ko) 난연성이 우수한 고강도 마그네슘 합금 및 그 제조방법
CN110904371A (zh) 一种航空航天用超强耐蚀铝合金型材及其制造方法

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2013553380

Country of ref document: JP

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 13879206

Country of ref document: US

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12865106

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 12865106

Country of ref document: EP

Kind code of ref document: A1