WO2013100642A1 - 흡음재의 제조방법 및 흡음재 - Google Patents

흡음재의 제조방법 및 흡음재 Download PDF

Info

Publication number
WO2013100642A1
WO2013100642A1 PCT/KR2012/011596 KR2012011596W WO2013100642A1 WO 2013100642 A1 WO2013100642 A1 WO 2013100642A1 KR 2012011596 W KR2012011596 W KR 2012011596W WO 2013100642 A1 WO2013100642 A1 WO 2013100642A1
Authority
WO
WIPO (PCT)
Prior art keywords
absorbing material
sound
sound absorbing
sawdust
chaff
Prior art date
Application number
PCT/KR2012/011596
Other languages
English (en)
French (fr)
Inventor
강춘원
오승원
Original Assignee
전북대학교산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 전북대학교산학협력단 filed Critical 전북대학교산학협력단
Publication of WO2013100642A1 publication Critical patent/WO2013100642A1/ko

Abstract

본 발명은 흡음재의 제조방법 및 흡음재에 관한 것으로, 상기 흡음재의 제조방법은 톱밥 및 왕겨를 10 : 90 내지 40 : 60 중량비로 혼합하는 혼합단계, 상기 톱밥 및 왕겨 혼합물에 접착수지를 도포하는 접착단계, 및 상기 접착수지가 도포된 톱밥 및 왕겨 혼합물을 가압하여 성형시키는 가압성형단계를 포함한다. 상기 흡음재의 제조방법에 따라 제조된 흡음재는 흡음성능 및 강도를 향상시킬 뿐만 아니라, 친환경적이고, 자원활용도가 낮은 톱밥 및 왕겨를 이용한 것이므로 자원활용도가 높다.

Description

흡음재의 제조방법 및 흡음재
본 발명은 흡음재의 제조방법 및 흡음재에 관한 것이다. 보다 상세하게는 폐기시 부가적인 오염이 발생하지 않고, 재활용이 가능하여 친환경적일 뿐만 아니라, 우수한 방음성능을 나타내는 흡음재의 제조방법 및 흡음재에 관한 것이다.
산업이 발달하고 운송수단이 발달함에 따라, 인간의 주위환경 요소중에 소음원이 증가하게 되었고, 이를 효율적으로 저감시킬 수 있는 방법이 여러 가지로 형태로 시도되고 있다.
일반적으로 극장, 음악실, 녹음실, 연주회장 등에서는 소음이 외부로 전달되거나 외부의 소리가 유입되는 것을 차단하고, 소리에 의한 음향이 반사되어 발생되는 공진현상을 제거하기 위해 흡음 및 방음 설비를 갖고 있으며, 일반 가정에서도 실내의 소음이 외부로 전달되지 않도록 하기 위해 흡음 및 방음 설비를 설치하는 경우가 증가하고 있다.
나아가 최근 정부는 2005년 7월부터 공동주택은 바닥충격음이 최소 기준 50㏈을 충족하도록 규제하고 있어, 흡음 및 방음 설비의 역할은 더욱 증대되고 있다.
이러한 흡음 및 방음 설비는 소음원의 주위에 흡음재를 사용하는 방법이 많이 사용되는데, 이렇게 사용되는 흡음재의 종류에는 크게 무기계와 유기계 재료가 사용되고 있으며, 무기계 재료로는 암면, 글라스 울, 유리섬유 등이 있고, 유기계 재료에는 폴리에스터 섬유를 이용하여 제조한 흡음보드, 우레탄, 폴리프로필렌, 폴리에틸렌 등의 수지를 발포시킨 재료가 사용되고 있다.
그러나, 상기 흡음 및 방음 설비는 주요 구성으로 스폰지를 포함하는 것이 일반적이므로 완전한 방음의 구현에 어려움이 있다. 또한 상기 유기계 및 무기계 흡음재는 폐기시에 오염원이 될 수 있을 뿐만 아니라, 재활용이 곤란하다는 문제점이 있다.
구체적인 선행기술을 보면, 특허문헌1(KR10-2003-0013495 A)은 폐타이어 고무칩과 콜크분말을 이용한 공동주택층간의 흡음재 제조방법 및 그 제품에 대하여 개시하고 있으며, 상기 특허문헌 1에 따른 발명은 흡음재의 제조시 고무칩과 콜크분말을 일정 비율로 배합하고, 금형에서 프레스로 몰딩하는 방법을 사용하고 있다. 그러나 이러한 제조방법으로 흡음재를 제조하는 경우, 고무칩과 콜크분말이 일체로 성형되기 때문에 상기 흡음재의 재활용이 어렵다는 단점이 있다.
특허문헌2(KR10-2003-0008801 A)는 "폐 에틸렌비닐아세테이트를 포함한 건축자재물 및 그 제조방법"에 대하여 설명하고 있으며, 발포 에틸렌 비닐 아세테이트 50 내지 85 중량%, 폴리우레탄 15 내지 50 중량%을 포함하여 차음 및 제진재를 제조하고 있다. 그러나 이렇게 제조된 차음 및 제진재는 성형방법이 각기 다른 두 고분자 물질의 혼합이 작업공정에 어려움을 줄 수 있으며, 상기 차음 및 제진재는 재활용이 어려울 뿐만 아니라, 이를 폐기하는 경우 물성이 다른 고분자 물질의 혼합에 따라 유독가스나 오염물질이 배출될 수 있다는 단점이 있다.
본 발명의 목적은 자원활용도가 낮은 톱밥 및 왕겨를 이용하여 자원활용도 및 친환경성을 높일 뿐만 아니라 흡음성능 및 강도를 향상시킨 흡음재의 제조방법을 제공하는 것이다.
본 발명의 다른 목적은 상기 흡음재의 제조방법에 따른 흡음재를 제공한다.
상기 목적을 달성하기 위하여, 본 발명의 일 실시예에 따른 흡음재의 제조방법은 톱밥 및 왕겨를 10 : 90 내지 40 : 60 중량비로 혼합하는 혼합단계, 상기 톱밥 및 왕겨 혼합물에 접착수지를 도포하는 접착단계, 및 상기 접착수지가 도포된 톱밥 및 왕겨 혼합물을 가압하여 성형시키는 가압성형단계를 포함한다.
상기 가압성형단계는 170 내지 200℃에서 가압성형 하는 것일 수 있다.
상기 가압성형단계는 35 내지 45kg/cm2으로 가압하는 1차 가압성형단계, 25 내지 35kg/cm2으로 가압하는 2차 가압성형단계, 및 15 내지 25 kg/cm2으로 가압하는 3차 가압성형단계를 포함하는 것일 수 있다.
본 발명의 다른 일 실시예에 따른 흡음재는 상기 흡음재의 제조방법으로 제조된 것이다.
상기 흡음재는 비중이 0.4 내지 0.5인 것일 수 있다.
이하, 본 발명을 더욱 상세하게 설명한다.
본 발명의 일 실시예에 따른 흡음재의 제조방법은 톱밥 및 왕겨를 10 : 90 내지 40 : 60 중량비로 혼합하는 혼합단계, 상기 톱밥 및 왕겨 혼합물에 접착수지를 도포하는 접착단계, 및 상기 접착수지가 도포된 톱밥 및 왕겨 혼합물을 가압하여 성형시키는 가압성형단계를 포함한다.
도 1은 흡음재의 제조방법을 나타내는 공정도이다. 이하, 도 1을 참조하여 상기 흡음재의 제조방법에 대하여 설명한다.
우선, 톱밥 및 왕겨를 10 : 90 내지 40 : 60 중량비로 혼합한다(S10).
상기 톱밥은 톱으로 켜거나 자를 때에 나무 따위에서 쓸려 나오는 가루를 말하며, 상기 왕겨는 벼의 겉겨를 말한다. 상기 톱밥의 함량이 상기 중량비를 초과하는 경우 접착수지의 사용량이 증가하고, 흡음성이 저하되며, 가압시간이 늘어나는 문제가 있다. 또한, 상기 왕겨의 함량이 상기 중량비를 초과하는 경우 흡음재의 강도가 저하되는 문제가 있다.
상기 톱밥 및 왕겨는 건조된 것을 사용하는 것이 바람직하다. 상기 톱밥 및 왕겨의 건조는 자연건조, 열풍건조 및 기타 일반적인 건조방법을 모두 사용할 수 있다.
상기 건조된 톱밥 및 왕겨는 수분함량이 5 중량% 이하인 것일 수 있다. 톱밥 및 왕겨의 수분 함량이 5 중량%를 초과하는 경우 높은 경우 접착수지의 성능이 저하되며, 흡음재의 강도가 저하되는 문제가 있다.
다음으로, 상기 톱밥 및 왕겨 혼합물에 접착수지를 도포하였다(S20).
상기 접착 수지는 흡음재 제조에 사용되는 일반적인 접착제를 사용할 수 있으며, 구체적으로는 에틸렌 초산비닐 공중합체(EVA), 폴리아미드, 폴리에스테르, 폴리우레탄, 페놀 수지 접착제(phenol resin adhesive) 및 이들의 혼합으로 이루어진 군에서 선택한 어느 하나를 사용할 수 있다. 또한, 바람직하게는 상기 접착 수지는 페놀 수지 접착제일 수 있다. 페놀 수지 접착제를 사용하는 경우 상온 경화성이 우수하고, 상기 톱밥 및 왕겨에 대한 접착 효과가 우수하다.
다음으로, 상기 접착수지가 도포된 톱밥 및 왕겨 혼합물을 가압하고 성형시킨다(S30).
바람직하게 상기 가압성형은 판상(板
Figure 72c0
) 형태로 성형되는 것일 수 있으며, 따라서 상기 톱밥 및 왕겨의 접착성과 성형된 흡음재의 강성 향상을 위해 상기 가압성형은 접착수지가 도포된 톱밥 및 왕겨 혼합물을 상하 방향의 양쪽에서 가압하는 방법을 사용할 수 있다.
상기 가압성형은 열압방식으로서, 170 내지 200℃에서 이루어지는 것일 수 있다. 상기 온도 범위에서 가압성형이 이루어지는 경우 상기 톱밥 및 왕겨의 접착성능 및 성형된 흡음재의 강성이 우수하다.
상기 온도 범위에서 가압성형이 이루어지는 경우 상기 가압성형은 10분 내지 20분 동안 이루어지는 것일 수 있다. 이는 상기 성형된 흡음재의 비중을 흡음성 및 강성이 가장 우수한 범위로 조절하기 위함이다.
상기 가압성형은 35 내지 45kg/cm2으로 가압하는 1차 가압성형단계, 25 내지 35kg/cm2으로 가압하는 2차 가압성형단계, 및 15 내지 25 kg/cm2으로 가압하는 3차 가압성형단계를 포함하는 것일 수 있다.
상기 가압성형이 상기 3단계의 가압성형단계를 포함하는 경우 상기 성형된 흡음재의 표면경도가 우수하고, 상기 톱밥 및 왕겨의 기공이 다양한 크기로 형성되기 때문에 흡음성이 향상된다.
상기 가압성형단계 이후 성형된 흡음재는 선택적으로 강성 및 내구성 향상을 위해 추가적인 건조단계를 더 포함할 수 있다.
본 발명의 다른 일 실시예에 따른 흡음재는 상기 흡음재의 제조방법으로 제조된 것이다.
상기 흡음재는 비중이 0.4 내지 0.5인 것일 수 있다.
상기 흡음재의 비중이 0.4 미만인 경우 상기 흡음재의 강성 및 표면경도가 저하되고, 비중이 0.5를 초과하는 경우 흡음성능 급격하게 저하되기 때문이다.
본 발명에 따른 흡음재의 제조방법에 따라 제조된 흡음재는 흡음성능 및 강도를 향상시킬 뿐만 아니라, 친환경적이고, 자원활용도가 낮은 톱밥 및 왕겨를 이용한 것이므로 자원활용도가 높은 장점이 있다.
도 1은 본 발명에 따른 흡음재의 제조방법을 나타내는 공정도이다.
도 2는 본 발명에 따른 실시예에 따라 제조된 흡음재에 대한 사진이다.
도 3은 본 발명에 따른 실시예 1 내지 7에 따라 제조된 흡음재의 흡음성능을 나타내는 그래프이다.
도 4는 본 발명에 따른 실시예 1 및 비교예 1 내지 2에 따라 제조된 흡음재의 흡음성능을 나타내는 그래프이다.
이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예에 대하여 첨부한 도면을 참고로 하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다.
[제조예 : 흡음재의 제조]
하기의 표 1와 같은 톱밥 및 왕겨의 조성에 따라 흡음재를 제조하였고, 제조된 각 실시예에 대한 흡음재의 비중을 측정하였다. 도 2는 상기 실시예에 따라 제조된 흡음재에 대한 사진이다.
표 1
실시예1 실시예2 실시예3 실시예4 실시예5 실시예6 실시예7
톱밥(중량%) 10 10 10 10 20 30 40
왕겨(중량%) 90 90 90 90 80 70 60
흡음재 비중 0.4 0.5 0.6 0.7 0.5 0.5 0.5
- 상기 흡음재는 190℃에서 40kg/cm2으로 가압하는 1차 가압성형단계, 30kg/cm2으로 가압하는 2차 가압성형단계, 및 20kg/cm2으로 가압하는 3차 가압성형단계로 진행하였다.
[실험예 : 흡음재의 흡음성능 실험]
상기 실시예에 대한 흡음성 성능을 실험하였고, 상기 실시예에 따른 흡음성능을 비교하기 위해 두께 6mm의 석고보드(비교예 1) 및 두께 11mm의 석고보드(비교예 2)에 대한 흡음성능을 측정하였다.
도 3은 상기 실시예 1 내지 7에 따라 제조된 흡음재의 흡음성능을 나타내는 그래프이다. 상기 그래프에서 가로축은 주파수이고, 세로축은 흡음성능을 나타내는 것으로 각 주파수 별로 세로축의 값이 높을수록 우수한 흡음성능을 가지는 것이다.
상기 도 3의 그래프를 참조하면, 본 발명에 따른 실시예에서 제조된 흡음재는 전반적으로 흡음성이 우수함을 확인할 수 있다. 특히 실시예 1의 경우 거의 모든 주파수 범위에서 40% 이상의 높은 흡음성을 나타낸다는 것을 확인하였다. 또한, 실시예 1 내지 4를 참조할 때, 상기 흡음재의 비중이 0.4 내지 0.5인 경우 넓은 주파수 범위에 걸쳐 흡음성능이 가장 우수하고, 이를 벗어나는 경우 흡음성능이 감소하는 것을 확인할 수 있다.
또한, 톱밥 함량을 변화시킨 실시예 5 내지 7을 참조할 때, 톱밥의 함량이 커질수록 흡음성능이 향상됨을 확인할 수 있었다. 특히 톱밥을 40 중량%로 포함하는 실시예 7이 고른 주파수 범위에서 흡음성능이 우수하다는 것을 알 수 있다.
도 4는 실시예 1 및 비교예 1 내지 2에 따라 제조된 흡음재의 흡음성능을 나타내는 그래프이다. 상기 그래프에서 가로축은 주파수이고, 세로축은 흡음성능을 나타내는 것으로 각 주파수 별로 세로축의 값이 높을수록 우수한 흡음성능을 가지는 것이다.
상기 도 4의 그래프를 참조하면, 본 발명에 따른 실시예 1은 비교예 1에 비하여 흡음성능이 넓은 주파수 범위에서 우수하다는 것을 알 수 있고, 두께가 11mm로 상대적으로 두꺼운 석고보드인 비교예 2에 비하여도 흡음성능이 넓은 주파수 범위에서 상대적으로 우수하다는 것을 알 수 있다.
이상에서 본 발명의 바람직한 실시예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고 다음의 청구범위에서 정의하고 있는 본 발명의 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태 또한 본 발명의 권리범위에 속하는 것이다.
본 발명은 자원활용도가 낮은 톱밥 및 왕겨를 이용하여 흡음성능 및 강도를 향상시킨 흡음재의 제조방법 및 그에 따른 흡음재로서 흡음재 생산 산업에 이용가능하다.

Claims (5)

  1. 톱밥 및 왕겨를 10 : 90 내지 40 : 60 중량비로 혼합하는 혼합단계,
    상기 톱밥 및 왕겨 혼합물에 접착수지를 도포하는 접착단계, 및
    상기 접착수지가 도포된 톱밥 및 왕겨 혼합물을 가압하여 성형시키는 가압성형단계
    를 포함하는 것인 흡음재의 제조방법.
  2. 제 1항에 있어서,
    상기 가압성형단계는 170 내지 200℃에서 가압성형 하는 것인 흡음재의 제조방법.
  3. 제 1항에 있어서,
    상기 가압성형단계는
    35 내지 45kg/cm2으로 가압하는 1차 가압성형단계,
    25 내지 35kg/cm2으로 가압하는 2차 가압성형단계, 및
    15 내지 25 kg/cm2으로 가압하는 3차 가압성형단계
    를 포함하는 것인 흡음재의 제조방법.
  4. 제1항 내지 제4항 중 어느 한 항에 기재된 흡음재의 제조방법으로 제조된 것인 흡음재.
  5. 제4항에 있어서,
    상기 흡음재는 비중이 0.4 내지 0.5인 것인 흡음재.
PCT/KR2012/011596 2011-12-29 2012-12-27 흡음재의 제조방법 및 흡음재 WO2013100642A1 (ko)