WO2013009219A1 - Procédé pour créer un masque à la surface d'un substrat - Google Patents

Procédé pour créer un masque à la surface d'un substrat Download PDF

Info

Publication number
WO2013009219A1
WO2013009219A1 PCT/RU2012/000562 RU2012000562W WO2013009219A1 WO 2013009219 A1 WO2013009219 A1 WO 2013009219A1 RU 2012000562 W RU2012000562 W RU 2012000562W WO 2013009219 A1 WO2013009219 A1 WO 2013009219A1
Authority
WO
WIPO (PCT)
Prior art keywords
resist
substrate
laser
heating
heat treatment
Prior art date
Application number
PCT/RU2012/000562
Other languages
English (en)
Russian (ru)
Inventor
Игорь Георгиевич РУДОЙ
Аркадий Матвеевич СОРОКА
Мойше Самуилович КИТАЙ
Original Assignee
Rudoy Igor Georgievich
Soroka Arkadij Matveevich
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rudoy Igor Georgievich, Soroka Arkadij Matveevich filed Critical Rudoy Igor Georgievich
Publication of WO2013009219A1 publication Critical patent/WO2013009219A1/fr

Abstract

L'invention concerne la lithographie et notamment des procédés de création d'un masque de résine à la surface du substrat et notamment d'un substrat semi-conducteur. Le résultat technique de l'invention est une meilleure productivité de la lithographie à très haute résolution et notamment de la lithographie par UV extrêmes. Le résultat technique est réalisé en ce que le procédé de création d'un masque à la surface de la résine comprend l'application à la surface d'un substrat de résine polymère constitué de cycles monomères à base de molécules organiques, l'exposition de la résine, le traitement thermique de la résine exposée puis le développement de la structure créée dans la résine; on inclut dans la composition d'au moins 50% des cycles monomères au moins un atome de fluor, et le traitement thermique de la résine comprend son réchauffement par au moins une impulsion laser, la longueur d'onde du rayonnement étant sélectionnée sur la base de la condition selon laquelle le coefficient d'absorption du rayonnement laser par la résine dépasse le coefficient d'absorption du rayonnement laser par le substrat.
PCT/RU2012/000562 2011-07-12 2012-07-11 Procédé pour créer un masque à la surface d'un substrat WO2013009219A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
RU2011128761 2011-07-12
RU2011128761/28A RU2471263C1 (ru) 2011-07-12 2011-07-12 Способ создания маски на поверхности подложки

Publications (1)

Publication Number Publication Date
WO2013009219A1 true WO2013009219A1 (fr) 2013-01-17

Family

ID=47506292

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/RU2012/000562 WO2013009219A1 (fr) 2011-07-12 2012-07-11 Procédé pour créer un masque à la surface d'un substrat

Country Status (2)

Country Link
RU (1) RU2471263C1 (fr)
WO (1) WO2013009219A1 (fr)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
RU2764486C1 (ru) * 2020-12-25 2022-01-17 Публичное акционерное общество "Пермская научно-производственная компания" (ПАО "ПНППК") Способ улучшения характеристик интегрально-оптической схемы (варианты)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0165686A2 (fr) * 1984-06-20 1985-12-27 Gould Inc. Procédé pour la réparation des photomasques par dégradation du polymère induite par laser
JPH1124272A (ja) * 1997-06-30 1999-01-29 Fujitsu Ltd 放射線感光材料及びパターン形成方法
US6902859B2 (en) * 2001-04-10 2005-06-07 Fujitsu Limited Chemically amplified resist composition and method for forming patterned film using same
RU2008100283A (ru) * 2008-01-15 2009-07-20 Мойше Самуилович Китай (RU) Способ создания маски на поверхности подложки

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0165686A2 (fr) * 1984-06-20 1985-12-27 Gould Inc. Procédé pour la réparation des photomasques par dégradation du polymère induite par laser
JPH1124272A (ja) * 1997-06-30 1999-01-29 Fujitsu Ltd 放射線感光材料及びパターン形成方法
US6902859B2 (en) * 2001-04-10 2005-06-07 Fujitsu Limited Chemically amplified resist composition and method for forming patterned film using same
RU2008100283A (ru) * 2008-01-15 2009-07-20 Мойше Самуилович Китай (RU) Способ создания маски на поверхности подложки

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
S. V. ZELENTSOV ET AL.: "Sovremennaya fotolitografiya. Uchebno-metodicheski materialy po programme povysheniya kvalifikatsii ''Novye materialy elektroniki i optoelektroniki dlya informatsionno-telekommunikatsionnykh sistem''. Federalnoe agenstvo po obrazovaniju. Nizhegorodsky gosudarstvenny universitet im. N. .", LOBACHEVSKOGO. NIZHNY NOVGOROD, 2006, pages 56 *

Also Published As

Publication number Publication date
RU2471263C1 (ru) 2012-12-27

Similar Documents

Publication Publication Date Title
TW200842515A (en) Laser produced plasma EUV light source
WO2011055376A1 (fr) Source ponctuelle de rayons x laser plasma biologique
WO2007121142A2 (fr) Source lumineuse amelioree utilisant un plasma produit par laser
TWI644177B (zh) 用於產生輻射之方法及裝置
Lippert et al. Novel applications for laser ablation of photopolymers
NL2022769A (en) Spatial modulation of a light beam
Juha et al. Ablation of poly (methyl methacrylate) by a single pulse of soft X-rays emitted from Z-pinch and laser-produced plasmas
Juha et al. Short-wavelength ablation of molecular solids: pulse duration and wavelength effects
RU2471263C1 (ru) Способ создания маски на поверхности подложки
TWI358074B (en) Reducing fast ions in a plasma radiation source
KR100745704B1 (ko) 극자외선을 얻는 방법, 광선의 소스 및 리소그라피 공정에의 사용
RU2450384C1 (ru) Способ создания маски на поверхности подложки
Epstein Reduction of time-averaged irradiation speckle nonuniformity in laser-driven plasmas due to target ablation
US5175757A (en) Apparatus and method to enhance X-ray production in laser produced plasmas
Lippert et al. Structure property relations of photoreactive polymers designed for laser ablation
Ishino et al. Soft x-ray laser beamline for surface processing and damage studies
Bäuerle et al. Nanosecond-laser ablation
Lewis et al. Use of a random phase plate as a KrF laser beam homogenizer for thin film deposition applications
JP2009298911A (ja) ブロック共重合体および基板の加工方法
Kozawa et al. Basic aspects of acid generation processes in chemically amplified resists for electron beam lithography
Lippert et al. Polymers designed for laser applications: fundamentals and applications
Burian et al. Subthreshold erosion of an organic polymer induced by multiple shots of an X-ray free-electron laser
Bartnik et al. Low temperature plasmas induced in SF6 by extreme ultraviolet (EUV) pulses
Grisham et al. Materials modification with intense extreme ultraviolet pulses from a compact laser
WO2023199659A1 (fr) Matériau de réserve, procédé de production de motif de réserve et motif de réserve

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12811594

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 12811594

Country of ref document: EP

Kind code of ref document: A1