WO2012024262A1 - Polyolefin-based solar backsheet - Google Patents

Polyolefin-based solar backsheet Download PDF

Info

Publication number
WO2012024262A1
WO2012024262A1 PCT/US2011/047863 US2011047863W WO2012024262A1 WO 2012024262 A1 WO2012024262 A1 WO 2012024262A1 US 2011047863 W US2011047863 W US 2011047863W WO 2012024262 A1 WO2012024262 A1 WO 2012024262A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
backsheet
layers
iii
cross
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2011/047863
Other languages
English (en)
French (fr)
Inventor
Andreas H. Graichen
Wolfgang G. Schoeppel
Michael JÜRGENS
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
3M Innovative Properties Co
Original Assignee
3M Innovative Properties Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Co filed Critical 3M Innovative Properties Co
Priority to CN2011800394703A priority Critical patent/CN103068575A/zh
Priority to KR1020137006390A priority patent/KR20130097185A/ko
Priority to US13/814,856 priority patent/US20130133726A1/en
Priority to JP2013524923A priority patent/JP2013535365A/ja
Publication of WO2012024262A1 publication Critical patent/WO2012024262A1/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/32—Layered products comprising a layer of synthetic resin comprising polyolefins
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B15/08—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/20—Layered products comprising a layer of metal comprising aluminium or copper
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/10009—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets
    • B32B17/10018—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets comprising only one glass sheet
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10788—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer containing ethylene vinylacetate
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/10807—Making laminated safety glass or glazing; Apparatus therefor
    • B32B17/10816—Making laminated safety glass or glazing; Apparatus therefor by pressing
    • B32B17/10825—Isostatic pressing, i.e. using non rigid pressure-exerting members against rigid parts
    • B32B17/10834—Isostatic pressing, i.e. using non rigid pressure-exerting members against rigid parts using a fluid
    • B32B17/10844—Isostatic pressing, i.e. using non rigid pressure-exerting members against rigid parts using a fluid using a membrane between the layered product and the fluid
    • B32B17/10853—Isostatic pressing, i.e. using non rigid pressure-exerting members against rigid parts using a fluid using a membrane between the layered product and the fluid the membrane being bag-shaped
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/06—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B27/08—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/12—Layered products comprising a layer of synthetic resin next to a fibrous or filamentary layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/18—Layered products comprising a layer of synthetic resin characterised by the use of special additives
    • B32B27/20—Layered products comprising a layer of synthetic resin characterised by the use of special additives using fillers, pigments, thixotroping agents
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/28—Layered products comprising a layer of synthetic resin comprising synthetic resins not wholly covered by any one of the sub-groups B32B27/30 - B32B27/42
    • B32B27/283—Layered products comprising a layer of synthetic resin comprising synthetic resins not wholly covered by any one of the sub-groups B32B27/30 - B32B27/42 comprising polysiloxanes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/30—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers
    • B32B27/302—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers comprising aromatic vinyl (co)polymers, e.g. styrenic (co)polymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/30—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers
    • B32B27/308—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers comprising acrylic (co)polymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/34—Layered products comprising a layer of synthetic resin comprising polyamides
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/36—Layered products comprising a layer of synthetic resin comprising polyesters
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/40—Layered products comprising a layer of synthetic resin comprising polyurethanes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/02—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by structural features of a fibrous or filamentary layer
    • B32B5/028—Net structure, e.g. spaced apart filaments bonded at the crossing points
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10F—INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION
    • H10F19/00—Integrated devices, or assemblies of multiple devices, comprising at least one photovoltaic cell covered by group H10F10/00, e.g. photovoltaic modules
    • H10F19/80—Encapsulations or containers for integrated devices, or assemblies of multiple devices, having photovoltaic cells
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10F—INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION
    • H10F19/00—Integrated devices, or assemblies of multiple devices, comprising at least one photovoltaic cell covered by group H10F10/00, e.g. photovoltaic modules
    • H10F19/80—Encapsulations or containers for integrated devices, or assemblies of multiple devices, having photovoltaic cells
    • H10F19/85—Protective back sheets
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
    • B32B2264/10—Inorganic particles
    • B32B2264/101—Glass
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
    • B32B2264/10—Inorganic particles
    • B32B2264/107—Ceramic
    • B32B2264/108—Carbon, e.g. graphite particles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/20—Properties of the layers or laminate having particular electrical or magnetic properties, e.g. piezoelectric
    • B32B2307/204—Di-electric
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/20—Properties of the layers or laminate having particular electrical or magnetic properties, e.g. piezoelectric
    • B32B2307/206—Insulating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/30—Properties of the layers or laminate having particular thermal properties
    • B32B2307/308—Heat stability
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/40—Properties of the layers or laminate having particular optical properties
    • B32B2307/402—Coloured
    • B32B2307/4023—Coloured on the layer surface, e.g. ink
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/40—Properties of the layers or laminate having particular optical properties
    • B32B2307/412—Transparent
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/50—Properties of the layers or laminate having particular mechanical properties
    • B32B2307/538—Roughness
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/50—Properties of the layers or laminate having particular mechanical properties
    • B32B2307/54—Yield strength; Tensile strength
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/70—Other properties
    • B32B2307/71—Resistive to light or to UV
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/70—Other properties
    • B32B2307/712—Weather resistant
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/70—Other properties
    • B32B2307/714—Inert, i.e. inert to chemical degradation, corrosion
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/70—Other properties
    • B32B2307/732—Dimensional properties
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/70—Other properties
    • B32B2307/732—Dimensional properties
    • B32B2307/734—Dimensional stability
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2323/00—Polyalkenes
    • B32B2323/04—Polyethylene
    • B32B2323/046—LDPE, i.e. low density polyethylene
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2457/00—Electrical equipment
    • B32B2457/12—Photovoltaic modules
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E10/00—Energy generation through renewable energy sources
    • Y02E10/50—Photovoltaic [PV] energy
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31855—Of addition polymer from unsaturated monomers
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31855—Of addition polymer from unsaturated monomers
    • Y10T428/31909—Next to second addition polymer from unsaturated monomers

Definitions

  • This disclosure relates to backsheets for solar modules, in particular, crystalline solar modules and to solar modules containing the backsheets and to methods of making the backsheets.
  • the backsheets are based on poly-olefins selected from polyethenes (PE's) and polypropenes (PP's).
  • Wafer-based solar cells also referred to as crystalline solar cells or modules
  • Wafer-based solar cells contain crystalline silicon, for example monocrystalline silicon (c-Si), poly- or multi-crystalline silicon (poly-Si or mc-Si). They typically comprise a series of wafers soldered together, a so-called solar cell layer.
  • the wafers are generally about 180 and about 240 ⁇ thick.
  • the solar cell layer may further comprise electrical wirings connecting the individual cell units and bus bars having one end connected to the cells and the other exiting the module.
  • the solar cell layer is then further laminated to encapsulant layer(s) and protective layer(s) to form a weather resistant module.
  • a solar cell module derived from wafer-based solar cell(s) comprises, in order of position from the front light-receiving side to the back non-light-receiving side: (1 ) a top layer, (2) a top encapsulant layer, (3) a solar cell layer, (4) a back encapsulant layer, and (5) a backing layer, which commonly comprises a backsheet.
  • a top layer a top encapsulant layer
  • a solar cell layer (4) a back encapsulant layer
  • a backing layer which commonly comprises a backsheet.
  • the top layer is typically a glass sheet.
  • the encapsulant layers used in such solar cell modules are designed to encapsulate and protect the fragile solar cells and to adhere them to the top layer.
  • Typical encapusulant layers include ethylene vinylacetates (EVA) polymers.
  • the backing layer typically contains a protective backsheet, which is a multi-layered protective material.
  • the backsheet typically provides electrical insulation of the solar module and protects the solar module from influences from the environment, predominantly from moisture.
  • Backsheets typically contain multiple layers from different materials, wherein each material and layer may serve a different purpose. Most commonly at least one of the materials contains a fluoropolymer. In addition to fluoropolymers frequently used materials include polyethene terephthalate (PET) polymers or polyethene naphthalate (PEN) polymers. This set up presents an economical disadvantage because the ingredients are comparatively expensive. In many cases tie layers or other additional ingredients may have to be provided to achieve sufficient cohesion of the individual layers to bond to each other and to the encapsulant layers of the solar module, which further increases costs. Other commercial types of backsheets comprise layers of polyester and/or polyamides.
  • a disadvantage of many prior art materials is that the individual layers cannot be combined to a multi-layer backsheet in a single process step but instead have to be separately and subsequently bonded together, which further increases processing costs and may also lead to comparatively instable interlayer bonding in particular in view of long term stability requirements.
  • a multi-layered backsheet for solar modules comprising in this order
  • each layer there may or may not be one or more sublayers,
  • top layer (i), the insulating layer (ii) and the back layer (iii) contain a polyolefin as the major component, wherein the polyolefin is selected from polyethene homo- and copolymers (PE's) and polypropene homo- and copolymers (PP's).
  • PE's polyethene homo- and copolymers
  • PP's polypropene homo- and copolymers
  • a solar module comprising one or more solar cells and one or more encapsulating layer and further comprising the backsheet.
  • a method of making the backsheet comprising: providing compositions for making layers (i), (ii) and (iii)
  • compositions into a multi-layered article and optionally cross-linking in yet another aspect there is provided a method of making a solar module comprising vacuum laminating the backsheet to a solar module.
  • Figure 1 is a schematic cross-sectional view of a photovoltaic module.
  • Figure 2 is a schematic cross-sectional view of an embodiment of the backsheet according to the present disclosure.
  • Figure 3 is a schematic cross-sectional view of an embodiment of the backsheet according to the present disclosure.
  • Figure 4 is a schematic cross-sectional view of an embodiment of the backsheet according to the present disclosure.
  • Figure 5 is a schematic cross-sectional view of an embodiment of the backsheet according to the present disclosure.
  • Figure 6 is a schematic cross-sectional view of an embodiment of the backsheet according to the present disclosure.
  • Figure 7 is a schematic cross-sectional view of an embodiment of the backsheet according to the present disclosure.
  • Figure 8 is a schematic cross-sectional view of an embodiment of the backsheet according to the present disclosure.
  • Figure 9 is a schematic cross-sectional view of an embodiment of the backsheet according to the present disclosure.
  • Figure 10 is a schematic cross-sectional view of an embodiment of the backsheet according to the present disclosure.
  • the terms “comprises,” “comprising,” “includes,” “including,” “containing,” “characterized by,” “has,” “having” or any other variation thereof, are intended to cover a nonexclusive inclusion.
  • a process, method, article, or apparatus that comprises a list of elements is not necessarily limited to only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus and including equivalents.
  • “or” refers to an inclusive or and not to an exclusive or.
  • any numerical range recited herein is intended to include and to specifically disclose the end points specified and also all integers and fractions within that range.
  • a range of from 1 % to 50% is intended to be an abbreviation and to expressly disclose the values 1 % and 50% and also the values between 1 % and 50%, such as, for example, 2%, 40%, 10%, 30%, 1.5 %, 3.9 % and so forth.
  • copolymer is used to refer to polymers containing two or more monomers.
  • the present disclosure provides protective sheets for the back of solar modules, i.e., protective sheets for the side of a solar module that is opposite to its light-receiving side. Such sheets are referred to a backsheets.
  • the present disclosure also provides solar modules comprising the backsheets and methods of making them.
  • the protective sheet materials provide electrical insulation.
  • the backsheets have a dielectric breakdown voltage of at least 10 kV or at least 20 kV.
  • the backsheets also provide mechanical protection of the solar module.
  • the backsheets have an elongation at break of at least 50% and a tensile strength of at least 20 MPa.
  • a particular advantage of the backsheets provided herein is that they provide long term electrical and mechanical protection against heat and moisture exposure. It has been found that the mechanical and electrical properties of the backsheets provided herein do not degrade or only degrade to a comparatively low degree after exposure to extreme heat and moisture conditions, like pressure cooking for 100 hours as described, for example, in the experimental section.
  • the backsheets have a total thickness of about 0.22 mm to 0.80 mm 0.35 mm to about 0.70 mm, or from about 0.40 mm to about 0.65 mm. It is an advantage of the present disclosure that the backsheets with such a small thickness may already provide all or at least same of the properties described above and below.
  • the backsheets provided herein have a layered structure. When viewed from top (which is the side of the backsheet that is to be bonded to the solar module) it comprises the layers (i), (ii) and (iii) in this order. There may or there may not be other layers between the layers (i) and (ii), or (ii) and (iii), or (i), (ii) and (iii). They may also be or not be other layers covering the top of layers (i) or the back of layer (iii) or the top of layer (ii) in case the layer (i) is absent.
  • Layer (i) is referred to as the "top layer” and is an optional layer, although its presence is preferred.
  • Layer (ii) is referred to herein as an "insulating layer" by which is meant that this layer provides all or the major part of the electrical insulation of the backsheet. However, it is not meant that the other layers do not participate in providing electrical insulation, which in fact they may well do.
  • Layer (iii) is referred to herein as the "back layer”. Its major purpose is to protect the layer (ii) from degradation.
  • the backsheets may be surface treated or at least one side of the backsheet may be surface treated.
  • Surface treatment may be carried out to improve the compatibility or adhesion to another surface or to provide a functional or decorative pattern or structure.
  • the backsheets may have smooth or rough surfaces on one or both of its external sides.
  • Rough surfaces may facilitate deaeration during the lamination process when the backsheet is included in a solar cell module.
  • Rough surfaces can be created by mechanical embossing or by melt fracture during extrusion of the sheets followed by quenching so that surface roughness is retained during handling.
  • a typical example for surface treatment to improve adhesion of other substrates, such as for example, external components like junction boxes, or mounting materials involves a plasma treatment, like a Corona treatment.
  • Corona treatments may be carried out for example under air or nitrogen atmosphere or other suitable atmospheres.
  • the layers (i), (ii) and/or (iii) contain polyethene (PE) and/or polypropene (PP) polymers as their major component.
  • PE polyethene
  • PP polypropene
  • “Major component” denotes that this component is present at the highest amount as expressed by percentage by weight based on the weight of the layer.
  • the PE and/or PP polymers are preferably present in an amount of greater than 50% by weight or even greater than 75% by weight or even greater than 90% by weight. The weight percentages are based on the weight of the layer they are contained in.
  • Polyethene polymers include homo- and copolymers of ethene, i.e., polymers comprising repeating units derived from ethene.
  • the PE polymers typically contain more than 50% by mole, preferably more than 60% by mole or more than 80% by mole and more preferably at least 95% by mole or more than 99% by mole or 100% by mole of units derived from ethene.
  • Suitable comonomers include alkenes, in particular a-olefins such as but not limited to propene, 1-butene, 1 -hexene, 1 -octene and combinations thereof.
  • Alkenes as used herein above and below include hydrocarbons with one carbon-carbon double bond and hydrocarbons with two carbon-carbon double bonds.
  • the a-olefins may be branched or cyclic or linear. Further examples include 4-methyl-1-pentene, 1-decene, 1-dodecene, 1 -tetracene, 1 -hexadecene, 1 - octadecene.
  • Suitable a-olefins include in general hydrocarbons of the general formula (C n H 2 n) with a terminal carbon-carbon double bond of up to 20 carbon atoms.
  • the PE polymer is selected from PE homo- or copolymers comprising more than 99% by mole of repeating units derived from ethene, PE copolymers comprising at least 50% preferably at least 60%, more preferably at least 80 % and most preferably at least 95% by mole of repeating units derived from ethene and one or more comonomers selected from alkenes, in particular a-olefins.
  • Polypropene polymers include homo- and copolymers of propene, i.e., polymers comprising repeating units derived from propene.
  • the PP polymers typically contain more than 50% by mole, preferably more than 60% by mole or more than 80% by mole and more preferably at least 95% by mole or more than 99% by mole or 100% by mole of units derived from propene.
  • Suitable comonomers include alkenes, in particular a-olefins such as but not limited to ethene, 1-butene, 1 -hexene, 1 -octene and combinations thereof.
  • Alkenes as used herein above and below include hydrocarbons with one carbon-carbon double bond and hydrocarbons with two carbon-carbon double bonds.
  • the a-olefins may be branched or cyclic or linear. Further examples include 4-methyl-1-pentene, 1-decene, 1-dodecene, 1 -tetracene, 1 -hexadecene, 1 - octadecene.
  • the PP polymer is selected from PP homo- or copolymers comprising more than 99% by mole of repeating units derived from propene, PP copolymers comprising at least 50% preferably at least 60%, more preferably at least 80 % and most preferably at least 95% by mole of repeating units derived from propene and one or more comonomers selected from alkenes, in particular a-olefins.
  • the PE and PP polymers used in the preparation of the layers may have a melting point of at least 100°C.
  • the PE and PP polymers may be linear or branched.
  • the PE and PP polymers may also be graft polymers, blockpolymers, core-shell polymers or combinations thereof. Also blends thereof may be used.
  • Suitable PE polymers include but are not limited to UHMWPE, HDPE, MDPE, LDPE, LLDPE, VLDPE.
  • UHMWPE ultra high molecular weight polyethene
  • HDPE high density polyethene
  • MDPE medium density polyethene
  • LLDPE linear low density polyethene
  • LDPE low density polyethene
  • VLDPE very low density polyethene
  • LLDPE linear low density polyethene
  • one layer may be prepared by a linear material, like HDPE and another layer may be prepared by a non-linear material like LDPE.
  • polyethenes and polypropenes are inexpensive raw materials. Therefore, it is an advantage of the backsheets provided herein that they can be prepared at low raw material costs. Yet the backsheet has the desired mechanical properties like elongation at break and/or tensile strength, electrical insulation and/or long-term stability under moisture and heat as described herein.
  • Another advantage of the present backsheets is that several or even all of their layers can be prepared in principle from the same or at least the same chemical type of polymeric material (i.e., polyethene or polypropene polymers). This means the layers can be prepared from materials having the same or similar chemical composition and thus may have similar viscosity or density. Similar in this respect means a deviation of less than 10%.
  • the layers can be prepared by co-extrusion which may obviate the use of adhesives and the like.
  • the backsheets or major components (layers) thereof can be prepared in a single process step.
  • the layers (i) and (ii) or (ii) and (iii) or (i), (ii) and (iii) may be coextruded simultaneously. Therefore, in a preferred embodiment there are no other layers between layers (i) and (ii) or between layers (ii) and (iii) or layers (i), (ii) and (iii). In such embodiments the respective layers may form a continuous common interface.
  • a backsheet having some or all of the properties described herein may be prepared without requiring layers from other polymers or other materials. Therefore, the backsheets provided herein may be free of one or more or of all of the following polymers or polymer layers: fluoropolymers, polyester, polyamides,
  • polyterepthalates polyacetates, like polyvinylacetates. Or ethylvinylacetates, polycarbonates or polyacrylates.
  • the backsheet provided herein contains the polyethene polymers described above and is free of polypropene polymers.
  • the backsheet provided herein contains the polypropene polymers described above and is free of polyethene polymers.
  • the backsheets may also be free of tie-layers.
  • Tie-layers are polymeric layers between two dissimilar polymers and binding the dissimilar polymer layers.
  • Dissimilar polymer layers are layers of two different chemical classes. Typically, the two dissimilar polymers would not or only poorly bind to each other, without the tie-layer.
  • Dissimilar polymers are polymers having the majority or repeating units derived from a different monomer, e.g., a polyamide versus a polyester.
  • Examples of tie-layer polymers include polymers modified to contain functional groups like hydroxyl, epoxy, or amine, carboxylic acid groups or anhydride groups.
  • the PE or PP polymers in layers (i) and/or (ii) and/or (iii) are preferably in cross-linked form in the assembled back sheet but may be used in non-cross-linked form in the preparation of the backsheet.
  • the layers may be prepared by non-cross-linked polymers but may be cross-linked afterwards either individually or combined.
  • layer (ii) and (iii) together or layers (i) and (ii) or, preferably layers (i), (ii) and (iii) are subjected to cross-linking.
  • the cross-linking may be carried out chemically or physically, the latter being preferred. In chemical cross-linking the composition contains a cross-linker as described below.
  • the cross-linker may be activated thermally, by chemical reaction or by irradiation, typically UV irradiation.
  • irradiation typically UV irradiation.
  • physical cross-linking the cross-linking is achieved by irradiating the polymers with ⁇ - or ⁇ -irradiation or e-beam irradiation.
  • a cross-linking agent is not required and may not be present.
  • the cross- linking is carried out by bulk irradiation of all layers (i.e., (ii) and (iii) or (i), (ii) and (iii)).
  • the layers may be cross-linked by the same or different cross-linking methods or cross-linkers and may be subjected by the same cross-linking process together or separately. A combination of physical and chemical crosslinking may also be used.
  • the layers (i), (ii) and (iii) all contain as a major component a polyethene polymer containing more than 75% by mole or more than 85% by mole or more than 95% by mole of units derived from ethene.
  • the layers are preferably cross-linked, for example by physical cross-linking, like but not limited to e-beam irradiation.
  • the dosages and/or acceleration voltages used can be optimized according to the desired performance and properties of the backsheet.
  • Typical total dosages that may be applied by single or multiple treatments may be between more than 10 Mrad or more than 16 Mrad, for example 20 Mrad, 25 Mrad, 30 Mrad, 39 Mrad, 40, Mrad, 43 Mrad, 47 Mrad, 50 Mrad, 56 Mrad.
  • the dosage may be less than 200 Mrad, e.g., 195 Mrad, 175, Mrad, 146 Mrad, 135 Mrad, 124 Mrad, 1 12 Mrad, 108 Mrad, 92 Mrad or 85 Mrad.
  • the dosage may be less than 80 Mrad, e.g., 73 Mrad, 62 Mrad or 51 Mrad.
  • Typical acceleration voltages may be between 50 and 500 kV, e.g., 70kV, 80kV, 90kV, 100kV, 1 10kV, 120kV, 130kV, 140kV, 150kV, 160kV, 170kV, 180kV, 190kV, 200kV, 210kV, 220kV, 230kV, 240kV, 250kV, 260kV, 270kV, 280kV, 290kV, 300kV, 310kV, 320kV, 330kV, 340kV, 350kV, 360kV, 370kV, 380kV, 390kV, 400kV, 410kV, 420kV, 430kV, 440kV, 450kV, 460kV, 470kV, 480kV, 490 kV.
  • the layers (i), (ii) and (iii) all contain as a major component a polypropene polymer containing more than 75% by mole or more than 85% by mole or more than 95% by mole of units derived from propene.
  • the layers are preferably cross-linked, for example by physical cross-linking, like but not limited to e-beam irradiation.
  • the combination of the layers (i), (ii) and (iii) or the individual layers (i), (ii) and (iii) may have a thickness effective to provide the electrical breakdown voltage of at least 10 kV or at least 20 kV and / or some or all of the mechanical properties as described herein. Typically a thickness of at least 210 ⁇ or at least 310 ⁇ may be sufficient.
  • the layers (i), (ii) and (iii) are bonded directly to each other.
  • the top layer is an optional layer. It is positioned at the top of the backsheet, i.e., the position which is to contact the encapsulant layer of the solar module or a surface of a layer or a plurality of layers covering it - for example adhesive layers or tie layers if required. More specifically, it is to contact the encapsulant layer that is opposite to the light-receiving side of the solar module (or a layer a surface of layer or a plurality of layers covering it).
  • layer (i) may be covered on its top face by other layers, for example intermediate layers as described below.
  • the layer may or may not be surface treated to provide a surface pattern or structure or to roughen the surface as described above or to increase adhesion to a substrate or surface as described above.
  • the top layer may be of the same polymer composition as layer (ii) or (iii) or of a different composition.
  • a top layer (i) may be desired, for example, to introduce a colour into the solar module or the backsheet or a coloured pattern representing information or decoration. Such colour or pattern can be introduced by printing it onto the top layer or by using a top layer containing pigments or a combination of pigments.
  • the top layer (i) contains white pigments and/or reflective particles.
  • the top layer (i) may be of white colour. It may also be non transparent.
  • the top layer is typically coloured or contains at least pigments.
  • Typical pigments include inorganic pigments, preferably white pigments.
  • white pigments include titanium oxides, like but not limited to Ti0 2 , or zinc oxides, like but not limited to ZnO, or combinations thereof.
  • Other pigments include pigments for green, red and blue.
  • the top layer may also be of black colour (i.e., it may contain black pigments or carbon particles).
  • the layer may contain up to 1 % by weight up to 4% by weight or up to 20% by weight of pigments or reflective particles.
  • Preferred reflective particles are reflective glass particles.
  • the top layer may in addition to the pigments also contain UV-stabilisers, for example those described below.
  • the top layer may in addition to the pigments also contain antioxidants, for example those described below.
  • the top layer may in addition to the pigments also contain cross-linking agents for example those described below.
  • the top layer may in addition to the pigment also contain flame retardants for example those described below.
  • the top layer may in addition also contain anti-dripping agents, for example those described below.
  • the top layer may typically have a thickness of from about 10 ⁇ to about 150 ⁇ , or from about 50 ⁇ to about 100 ⁇ .
  • the top layer may contain a cross-linked PE polymer, a non-cross-linked PE polymer, a cross- linked PP polymer or a non-cross-linked PP polymer.
  • the top layer contains a cross- linked PE polymer.
  • the PE polymer may be a high density PE, for example is consists of high density PE.
  • the PE polymer may be a low density PE, for example is consists of low density PE.
  • the top layer generally, is free of ionomers or acid copolymers.
  • the top layer may form a continuous interface with the insulating layer (ii), or it may be separated from layer (ii) by one or more intermediate layers.
  • the letter is less preferred. Insulating layer (layer (ii)):
  • the insulating layer may be the top outmost layer of the backsheet, in case there is no top layer (i) and in case of the backsheet is not attached to the solar module.
  • the layer may or may not be surface treated to create a pattern or structure or roughened surface as described above. If incorporated into a solar module the insulating layer may in this case be in direct contact with the back encapsulant layer of the solar module or it may be separated therefrom by one or more intermediate layers, for example optional intermediate layers, or adhesive layers and the like. If a top layer (i) is present the layer (ii) is placed between layer (i) and above layer (iii).
  • the insulating layer has sufficient thickness to provide a dielectric breakdown voltage of the backsheet of at least 10 kV or at least 20 kV.
  • the optimum thickness depends on the chemical composition of the layer. Typically the layer has a thickness of at least 150 mm, at least 210 ⁇ or at least 310 ⁇ or at least 350 ⁇ ..
  • the upper limit of the layer is determined by material costs and the mechanical properties of the backsheet but typically is less than 1 ,000 ⁇ .
  • the insulating layer typically comprises the PE polymers and PP polymers described above.
  • the polymer is cross-linked and most preferably the polymer is a cross-linked PE polymer.
  • the chemical composition of layer (ii) may be identical or different to that of layer (iii) and identical or different to that of (i).
  • the rheological property of layer (ii), for example its viscosity and/or density may be identical or different to that of layer (i) and/or (iii).
  • the layer (ii) may contain, for example, up to about 10 wt %, preferably up to about 5 wt %, and more preferably up to about 1 wt % of antioxidants based on the total weight of the layer.
  • the layer may contain, for example, up to about 10 wt %, preferably up to about 5 wt %, and more preferably up to about 1 wt % of UV-stabilizers based on the total weight of the layer.
  • the layer (ii) may contain anti-dripping agents like those described below. Typical amounts include up to 1 % wt, or up to %wt or up to 10% wt based on the weight of the layer.
  • the layer (ii) does not contain carbon particles (because this may reduce the insulating properties of the layer).
  • layer (ii) does not contain organic or inorganic pigments.
  • layer (ii) does not contain carbon particles and pigments.
  • layer (ii) is free of pigments as those described below.
  • layer (ii) is free of carbon particles or free of carbon particles and pigments. "Free of” as used herein means from 0 to less than 1 % wt or from 0 to less than 0.1 % wt or from 0 to less than 0.01 % wt based on the weight of the layer or 0% (within the detection limit).
  • layer (ii) does not contain any additives other than flame retardants and antioxidants as described below.
  • layer (ii) can contain up to 35% or up to 30% by weight based on the weight of the layer of flame retardant and yet has a dielectric break down voltage of at least 20 kV. Therefore, layer (ii) may contain up to 35 or up to 30% or up to 20% or up to 10% by weight based on the weight of the layer of flame retardants.
  • the layer may also contain anti-dripping agents. Therefore, another advantage of the backsheets provided herein is that they can be loaded to up to 20% or up to 30% by weight per layer with flame retardants or flame retardants and anti- dripping agents and thus has a good anti-burning behaviour but may still provide the
  • the backsheet may comprise multiple insulating layers as described above. It is also possible to use an insulating layer having one or more sublayers.
  • the insulating layer (ii) may contain one or more sublayer comprising the PE and/or PP polymers described above, which may be identical polymers or independently chosen and which make up a total thickness described above as desired thickness of the insulating layer (ii).
  • This layer protects the layer (ii) from the environment. It may contain the same or a different polyolefin than layer (ii).
  • Layer (iii) typically contains carbon particles. However, it is also possible that the layer (iii) contains pigment, for example white pigments as described above with respect to layer (i). It has been found that the material is resistant enough to only show little yellowing upon extensive heat, dampness or UV treatment.
  • the carbon particles may be modified, for example surface treated, coated or may contain functionalised groups (e.g., by chemical reaction with chemical modifiers or by adsorption of chemicals). Carbon particles include graphite, fullerenes, nanotubes, soot, carbon blacks (e.g., carbon black, acetylene black, ketjen black).
  • the layer (iii) may contain from about 1 % to about 6% or up to about 10% weight based on the weight of the layer of carbon particles.
  • the loading with carbon particles may be increased but in that case the layer may become electron conductive. In this case the layer may have to be earthed when it is incorporated into a solar module.
  • layer (iii) is of black colour due the presence of substantial amounts of carbon particles.
  • the layer can be of a different colour if pigments or paints are used.
  • layer (iii) may contain other additives.
  • additives include antioxidants, for example those described below.
  • Other additives include UV- absorbers, for example those described below, cross-linkers as described below and flame retardants, like those described below and anti dripping agents. The amount of these
  • ingredients may be individually or combined be from about 1 %wt to up to 10% wt.
  • the layer (iii) may have a thickness of about 50 to about 100 ⁇ .
  • the layer (iii) may be in direct contact with layer (ii) or it may be separated from layer (iii) by the presence of one or more intermediate layers. Preferably, it forms a continuous interface with layer (ii). This means that no tie-layer, primer or adhesive is placed between layer (ii) and (iii).
  • Layer (iii) may comprise a cross-linked PE or PP polymer, preferably a cross-linked PE polymer.
  • the PE polymer may be a high density PE, for example is consists of high density PE.
  • the PE polymer may be a low density PE, for example is consists of low density PE.
  • the layer (iii) may be prepared by non-cross linked polymers and are cross-linked during or after assembly.
  • layer (iii) can contain up to 35% or up to 30% by weight based on the weight of the layer of flame retardant and yet the backsheet has a dielectric break down voltage of at least 20 kV, when using the layer (ii) as described above. Therefore, layer (iii) may contain up to 35 or up to 30% or up to 20% or up to 10% by weight based on the weight of the layer of flame retardants.
  • layer (ii) and (iii) may each contain up to 10% or up to 20% or even up to 30% by weight of flame retardants based on the weight of the respective layer.
  • One or more optional layers may be introduced into the backsheet to introduce further desirable properties or to enhance the existing properties.
  • coloured layers or layers containing patterns displaying decoration or information may be introduced to the backsheet by introducing optional layers (iv), for example between layers (i) and (ii), between layer (ii) and (iii), or on top of layer (ii) in case layer (i) is absent or on the back of layer (iii).
  • optional layers for example between layers (i) and (ii), between layer (ii) and (iii), or on top of layer (ii) in case layer (i) is absent or on the back of layer (iii).
  • Such coloured layers may contain the polyolefins as described above and pigments or pattern displaying information or decoration printed thereon or introduced into the surface of that layer by surface-treatment.
  • the optional layer (iv) is a polyolefin layer and contains the same polyolefin as layer (ii), or as layer (iii) or as layer (ii) and (iii).
  • Optional layer (iv) may typically have a thickness of from about 5 to about 100 ⁇ .
  • a metal layer (v) for example a metal foil, like an aluminium foil, may be incorporated into the backsheet, for example between layers (ii) and (iii). It also possible to provide the metal foil on the back of layer (iii), i.e., facing away from layer (ii).
  • the metal foil would be covered by one or more additional layers, which may also be a polyolefinic layer containing polyolefins as described above to protect the metal film from deterioration by weather and environment.
  • the thickness of this optional layer (v) may be in the range of 5 - 100 ⁇ based on the type of material used.
  • Another optional layer includes one or more external protection layers (vi). The protection layer faces the back side of the backsheet on its one side and the environment on its opposite side. If incorporated it may be exposed to the environment from the non-light-receiving side of the solar module.
  • This layer may comprise polyurethanes, polyarylates, silicones, fluoropolymers and combinations thereof, or it may contain the polyolefins like those used in layers (i), (ii) or (iii) as described above. It may contain additives which further increase the UV stability, thermal stability and resistance to oxidation or corrosion. It may contain flame retardants or it may provide anti-scratch properties or easy-to-clean properties. It may also be a coloured layer to provide the outside of the backsheet with another colour than black.
  • the thickness of this layer may typically be in the range of 1 - 500 ⁇ based on the type of material used.
  • One or more scrim or net layers may also be present to further increase dimensional stability and handling properties. These scrims or nets may be introduced between layers (i) and (ii) or (ii) and (iii) or all of them, for example by extrusion coating. The scrim or net layer may also be introduced between layer (iii) and another layer. Scrim or net type layers may also improve the anti dripping performance during burning. Scrim or net layers may be net-shaped or non-woven layers of a polymeric or plastic material or organic or inorganic fibers.
  • Chemical cross-linking agents may be activated thermally or by irradiation.
  • Typical chemical cross-linking agents include vinyl-silanes, such as but not limited to vinyl-tri-ethoxy or vinyl trimethoxy silane. They may be blended or copolymerised with the PE or PP polymers.
  • Other types of chemical cross-linkers include radical cross-linker which decompose to generate radicals. These radicals then lead to a cross-linking reaction. Examples include but are not limited to peroxides and azo-compounds. Examples for cross-linkers activated by irradiation include but are not limited to benzophenones.
  • cross-linkers are dispersed in the PE or PP polymers or blended with them.
  • Anti-oxidants are dispersed in the PE or PP polymers or blended with them.
  • Anti-oxidants can be chosen from a wide range of known anti-oxidants that are compatible with polyolefins. Examples include but are not limited to phenolic or phosphitic anti-oxidants, such as alkylated monophenols, alkylthiomethylphenols, hydroquinones, alkylated hydroquinones, tocopherols, hydroxylated thiodiphenyl ethers, alkylidenebisphenols, acylaminophenols.
  • phenolic or phosphitic anti-oxidants such as alkylated monophenols, alkylthiomethylphenols, hydroquinones, alkylated hydroquinones, tocopherols, hydroxylated thiodiphenyl ethers, alkylidenebisphenols, acylaminophenols.
  • the anti-oxidant is a member of the class of bis-phenolic antioxidants.
  • Suitable specific bis-phenolic antioxidants include 2,2'-ethylidenebis(4,6-di-t-butylphenol); 4,4'- butylidenebis(2-t-butyl-5-methylphenol); 2,2'-isobutylidenebis(6-t-butyl-4-methylphenol); and 2,2'-methylenebis(6-t-butyl-4-methylphenol).
  • Some commercially available bis-phenolic antioxidants include ANOX 29, LOWINOX 22M46, LOWINOX 44B25, and LOWINOX 22IB46.
  • UV-absorbers
  • UV absorbers include but are not limited to triazines, benzotriazoles, hydroxybenzophenones, hydroxyphenyltriazines, esters of benzoic acids, and mixtures of two or more thereof.
  • Further examples include cyclic amines. Examples include secondary, tertiary, acetylated, N-hydrocarbyloxy substituted, hydroxy substituted N-hydrocarbyloxy substituted, or other substituted cyclic amines which are further characterized by a degree of steric hindrance, generally as a result of substitution of an aliphatic group or groups on the carbon atoms adjacent to the amine function. Such compounds are commonly referred to as HALS (hindered amine light stabilizers).
  • HALS hinderedered amine light stabilizers
  • HALS also have anti-oxidative properties and can be used in addition or instead of anti-oxidants described above.
  • Specific examples of HALS include, but are not limited to, 4-hydroxy-2,2,6,6-tetramethylpiperidine, 1-allyl-4-hydroxy-2,2,6,6-tetramethylpiperidine, 1- benzyl-4-hydroxy -2,2,6,6-tetramethylpiperidine, bis(2,2,6,6-tetramethyl-4-piperidyl) sebacate, bis(2,2,6,6-tetramethyl-4-piperidyl) succinate, bis(1 ,2,2,6,6-pentamethyl-4-piperidyl) sebacate, bis(1-octyloxy-2,2,6,6-tetramethyl-4-piperidyl) sebacate, bis(1 ,2,2,6,6-pentamethyl-4-piperidyl)n -butyl-3,5-di-tert-butyl-4-hydroxybenzylmalonate, the condensate of
  • Examples for sterically hindered amines substituted on the N-atom by a hydroxy-substituted alkoxy group include but are not limited to 1 -(2-hydroxy-2-methylpropoxy)-4-octadecanoyloxy- 2,2,6,6-tetramethylpiperidine, 1 -(2-hydroxy-2-methylpropoxy)-4-hexadecanoyloxy-2, 2,6,6- tetramethylpiperidine, the reaction product of 1 -oxyl-4-hydroxy-2,2,6,6-tetramethylpiperidine with a carbon radical from t-amylalcohol, 1 -(2-hydroxy-2-methylpropoxy)-4-hydroxy-2, 2,6,6- tetramethylpiperidine, 1-(2-hydroxy-2-methylpropoxy)-4-oxo-2,2,6,6-tetramethylpiperidine, bis(1- (2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl) sebacate, bis(1-
  • Oxamides include, for example, 4,4'-dioctyloxyoxanilide, 2,2'-diethoxyoxanilide, 2,2'-dioctyloxy- 5,5'-di-tert-butoxanilide, 2,2'-didodecyloxy-5,5'-di-tert-butoxanilide, 2-ethoxy-2'-ethyloxanilide, N,N'-bis(3-dimethylaminopropyl)oxamide, 2-ethoxy-5-tert-butyl-2'-ethoxanilide and its mixture with 2-ethoxy-2'-ethyl-5,4'-di-tert-butoxanilide, mixtures of o- and p-methoxy-disubstituted oxanilides and mixtures of o- and p-ethoxy-disubstituted oxanilides.
  • Flame retardants are compounds that reduce or prevent flame propagation or increase the inflammability of a material.
  • flame retardants include but are not limited to halogenated aromatic compounds, like halogenated biphenyls or biphenyl ethers and bisphenols.
  • the halogenated materials are brominated or polybrominated. Specific examples include bisphenols like polybrominated biphenyl, penta-, octa and deca deca- brominated diphenyl ethers (BDE's), tetrabromobisphenol-A (TBBPA).
  • inorganic compounds like alumina trihydrate, antimony oxide, magnesium hydroxide, zinc borate, organic and inorganic phosphates, red phosphor and combinations thereof.
  • Anti-dripping agents are substances that reduce or prevent dripping of a polymer when being exposed to a flame.
  • dripping agents include fluoropolymers, such a
  • the dripping agents may be dispersed in or blended with the polymer making up the respective layer.
  • Commercial examples of dripping agents include MM5935EF from Dyneon LLC, ALGOFLON DF210 from Solvay-Solexis or ENTROPY TN3500 from Shanghai Entropy Chemical.
  • Pigments may be inorganic or organic. Pigments may be of green, blue, red, pink, purple and white colour. Most commonly used white pigments are inorganic pigments. Examples include but are not limited to zinck oxides and titanium oxides (like Ti0 2 ). The pigments may be dispersed, blended or dissolved (in which case the pigments are more appropriately referred to as dyes) in the layer or may be painted or printed onto a layer.
  • Carbon particles are not pigments in the meaning of this disclosure.
  • Reflective materials include glass particles or metal particles, with glass particles being preferred. They may be dispersed, blended or dissolved in a layer. Patterns displaying information.
  • the layers (i) or (iii) may contain patterns displaying information which may be laminated onto them or introduced into them by stamping. Such information may be, for example, a logo or instructions.
  • FIG. 1 shows a schematic cross-section of a solar module (1 ).
  • the solar module (1 ) contains a light-receiving side (2) (the top side) and a side (6) that is opposite to the light receiving side, which is the back side. Between the top and the back side there is a cell layer comprising an array of interconnected solar cells, i.e., devices that convert light into electrical energy.
  • the solar cell layer including its connectors is represented in figure 1 by layer (4).
  • the solar cell layer is encapsulated by one or more encapsulating layers (3) and (5). Instead of two separate layers (3) and (5) a single encapsulating layer may be used which then incorporates the solar cell layer (4).
  • the back side (6) typically contains a backsheet to protect the interior of the module from the environment.
  • FIGS 2 to 10 show various embodiments of the backsheets provided herein.
  • Figure 2 is a schematic representation of a cross-section of a backsheet (1 ) as prepared in example 1. It contains a top layer (i) represented by layer (2) in figure 2 which will face the encapsulant layer of the solar module (e.g., a layer (5) of figure 1 ) if incorporated into the solar cell.
  • the backsheet (1 ) further contains a middle layer (insulating layer) (ii) represented by layer (3) in figure 2 and a back layer (iii) represented by layer (4) in figure 2.
  • the top layer (i) is white and contains HDPE and white pigments.
  • Layer (iii) is black and contains HDPE and carbon black.
  • the layer (ii) contains LDPE.
  • All three layers contain UV stabilisers and have been coextruded, which means that layer (i) and (ii) and layer (ii) and (iii) form a continuous common interface. All layers have been subjected to a cross-linking treatment, which means that the polymers of the individual layers are cross-linked.
  • the cross-linking treatment was carried out by bulk cross-linking which means that also the neighbouring layers (i.e., layers (2) and (3) and/or (3) and (4)) may be cross-linked with each other.
  • the layers (i), or layer (ii) and/or layer (iii) may additionally contain UV stabilisers. They may also contain flame retardants and/or anti-dripping agents. They may also contain, although less preferred, cross-linker either as individual compounds or as comonomers. Layers (i) and/or (iii) may further contain antioxidants.
  • the multi-layer construction may also contain incorporated or added on top of (i) or to the back of (iii) or both a scrim layer.
  • FIG 3 a schematic cross section of another embodiment of a backsheet (1 ) is shown.
  • the backsheet (1 ) contains a top layer (i) of HDPE (which may contain pigments, in particular white pigments) and is represented by (2).
  • the insulating layer (ii) represented by (3) also contains HDPE.
  • Layer (3) does not contain pigments but may contain flame retardants and/or anti- dripping agents.
  • Back Layer (iii) represented by layer (4) also contains HDPE and carbon particles.
  • Layer (4) is black. Layer (4) may further contain flame retardants and/or anti-dripping agents and other additives like antioxidants, UV stabilisers and cross-linker.
  • All three layers have been coextruded, which means that layers (i) and (ii) and layers (ii) and (iii) form a continuous common interface.
  • all layers have been subjected to a cross- linking treatment, which means that the polymers of the individual layers are cross-linked.
  • the cross-linking treatment may be carried out by bulk cross-linking which means that also the neighbouring layers (i.e., layers (2) and (3) and/or (3) and (4)) may be cross-linked with each other.
  • the layer (i) may additionally contain flame retardants or cross-linker either as individual compounds or as comonomers and/or may contain antioxidants, UV stabilisers, flame retardants and anti-dripping agents.
  • the multi-layer construction may also contain incorporated or added on top of (i) or to the back of (iii) or both a scrim layer.
  • FIG 4 a schematic cross section of another embodiment of a backsheet (1 ) is shown.
  • the backsheet (1 ) contains a top layer (i) of LDPE (which may contain pigments, in particular white pigments) and is represented by (2).
  • the insulating layer (ii) represented by (3) also contains LDPE.
  • Layer (3) does not contain pigments but may contain flame retardants and/or anti-dripping agents and/or UV stabilisers.
  • Layer (iii) represented by layer (4) also contains LDPE and carbon particles.
  • Back Layer (4) is black. Layer (4) may further contain flame retardants and/or anti-dripping agents. All three layers have been coextruded, which means that layer (i) and (ii) and layer (ii) and (iii) form a continuous common interface.
  • all layers have been subjected to a cross-linking treatment, which means that the polymers of the individual layers are cross-linked.
  • the cross-linking treatment was carried out by bulk cross- linking which means that also the neighbouring layers (i.e., layers (2) and (3) and/or (3) and (4)) may be cross-linked with each other.
  • the layer (i) may additionally contain flame retardants and/or anti-dripping agents, or cross- linker either as individual compounds or as comonomers.
  • Layers (i) and/or (iii) may further contain antioxidants and/or UV stabilisers.
  • the multi-layer construction may also contain incorporated or added on top of (i) or to the back of (iii) or both a scrim layer.
  • FIG 5 a schematic cross section of another embodiment of a backsheet (1 ) is shown.
  • the backsheet (1 ) contains a top layer (i) of LDPE (which may contain pigments, in particular white pigments) and is represented by (2).
  • the insulating layer (ii) represented by (3) also contains HDPE.
  • Layer (3) does not contain pigments but may contain flame retardants and/or anti- dripping agents.
  • Back Layer (iii) represented by layer (4) also contains LDPE and carbon particles.
  • Layer (4) is black. Layer (4) may further contain flame retardants and/or anti-dripping agents. All three layers have been coextruded, which means that layer (i) and (ii) and layer (ii) and (iii) form a continuous common interface.
  • all layers have been subjected to a cross-linking treatment, which means that the polymers of the individual layers are cross-linked.
  • the cross-linking treatment may be carried out by bulk cross-linking which means that also the neighbouring layers (i.e., layers (2) and (3) and/or (3) and (4)) may be cross-linked with each other.
  • the layer (i) may additionally contain flame retardants and/or anti-dripping agents, or cross- linker either as individual compounds or as comonomers.
  • Layers (i) and/or (iii) may further contain antioxidants and/or UV stabilisers.
  • the multi-layer construction may also contain incorporated or added on top of (i) or to the back of (iii) or both a scrim layer.
  • FIG 6 a schematic cross section of another embodiment of a backsheet (1 ) is shown.
  • the backsheet (1 ) contains a top layer (i) of LDPE (which may contain pigments, in particular white pigments) and is represented by (2).
  • the insulating layer (ii) represented by (3) also contains HDPE.
  • Layer (3) does not contain pigments but may contain flame retardants and/or anti- dripping agents.
  • Back Layer (iii) represented by layer (4) also contains LDPE and carbon particles.
  • Layer (4) is black. Layer (4) may further contain flame retardants and/or anti-dripping agents. All three layers have been coextruded, which means that layer (i) and (ii) and layer (ii) and (iii) form a continuous common interface.
  • all layers have been subjected to a cross-linking treatment, which means that the polymers of the individual layers are cross-linked.
  • the cross-linking treatment may be carried out by bulk cross-linking which means that also the neighbouring layers (i.e., layers (2) and (3) and/or (3) and (4)) may be cross-linked with each other.
  • the layer (i) may additionally contain flame retardants and/or anti-dripping agents, or cross- linker either as individual compounds or as comonomers.
  • Layers (i) and/or (iii) may further contain antioxidants and/or UV stabilisers.
  • the multi-layer construction may also contain incorporated or added on top of (i) or to the back of (iii) or both a scrim layer.
  • FIG 7 a schematic cross section of another embodiment of a backsheet (1 ) is shown.
  • the backsheet (1 ) contains a top layer (i) of HDPE (which may contain pigments, in particular white pigments) and is represented by (2).
  • the insulating layer (ii) represented by (3) also contains HDPE.
  • Layer (3) does not contain pigments but may contain flame retardants and/or anti- dripping agents.
  • Back Layer (iii) represented by layer (4) contains LDPE and carbon particles.
  • Layer (4) is black. Layer (4) may further contain flame retardants and/or anti dripping agents. All three layers have been coextruded, which means that layer (i) and (ii) and layer (ii) and (iii) form a continuous common interface.
  • all layers have been subjected to a cross- linking treatment, which means that the polymers of the individual layers are cross-linked.
  • the cross-linking treatment may be carried out by bulk cross-linking which means that also the neighbouring layers (i.e., layers (2) and (3) and/or (3) and (4)) may be cross-linked with each other.
  • the layer (i) may additionally contain flame retardants or cross-linker either as individual compounds or as comonomers.
  • Layers (i) and (iii) may further contain antioxidants and UV stabilisers.
  • the multi-layer construction may also contain incorporated or added on top of (i) or to the back of (iii) or both a scrim layer.
  • FIG 8 a schematic cross section of another embodiment of a backsheet (1 ) is shown.
  • the backsheet (1 ) contains a top layer (i) represented by (2), an insulating layer (ii) represented by (3) and a back layer (iii) represented by layer (4). Layers (i), (ii) and (iii) may be as described herein or as shown in figures 2 to 7.
  • the embodiment shown in figure 8 further contains an optional layer (iv) represented by (5).
  • the embodiment may further contain one or more scrim layers.
  • FIG 9 a schematic cross section of another embodiment of a backsheet (1 ) is shown.
  • the backsheet (1 ) contains a top layer (i) represented by (2), an insulating layer (ii) represented by (3) and a back layer (iii) represented by layer (4).
  • Layers (i), (ii) and (iii) may be as described herein or as shown in figures 2 to 8.
  • the embodiment shown in figure 9 further contains an optional layer (vi) represented by (5).
  • the embodiment may also contain one or more scrim layers.
  • FIG 10 a schematic cross section of another embodiment of a backsheet (1 ) is shown.
  • the backsheet (1 ) contains a top layer (i) represented by (2), an insulating layer (ii) represented by (3) and a back layer (iii) represented by layer (4).
  • Layers (i), (ii) and (iii) may be as described herein or as shown in figures 2 to 7.
  • the embodiment shown in figure 10 further contains an optional layer (v) represented by (5) and at least one external protective layer (vi) represented by (6).
  • the embodiment may also contain one or more scrim layers.
  • PP backsheets provided herein can be represented by figures 2 to 10 in which layers (i), (ii), (iii) are replaced by PP polymers of different molecular weight, copolymer content or density.
  • the backsheets can be produced by any suitable process.
  • a pre-formed multilayer sheet may be produced by first separately preparing each of the component layer sheets through any suitable process and then laminating or bonding the layers to form the multi-layer sheet.
  • the layers may also be glued together.
  • it is an advantage of the present backsheets that they can be produced directly by a co-extrusion process or that at least some of their layers can be produced by co-extrusion.
  • layers (ii) and (iii) or layers (i) and (ii) or (i), (ii) and (iii) are coextruded.
  • the compositions making up the layers are prepared by mixing the ingredients.
  • compositions are then extruded in molten form through the respective sheet-shaping dies.
  • the dies and feedblocks are shaped such that the extrudates leaving the dies form the multilayered article upon cooling.
  • the compositions can generally be extruded at a temperature of about 130°C to 250°C or 160 °C to about 280°C.
  • coextruded layers also have the advantage of being more homogenous and contain fewer air bubble inclusions and or particle inclusions. This may further increase the electrical properties and long-term performance of the backsheets.
  • the coextrusion may also be carried out by cast film extrusion or blown film extrusion.
  • the layers may be cross-linked individually or combined as described above.
  • the layer (i), (ii) and (iii) are combined and then cross-linked simultaneously.
  • the invention further provides a solar cell module comprising at least one backsheet as described above.
  • a solar module comprises at least one solar cell layer.
  • the solar cells have a light-receiving side and a side opposite to it, which is referred to as the non-light-receiving side.
  • the solar cells are electrically interconnected and/or arranged in a flat plane.
  • the solar cell layer may further comprise electrical wirings, such as cross ribbons and bus bars.
  • solar cell is meant to include any article which can convert light into electrical energy.
  • Preferred are wafer-based solar cells (e.g., c-Si or mc-Si based solar cells).
  • the solar module further contains one or more encapsulant layers.
  • the solar module contains at least one encapsulant layer or a part of an encapsulant layer adjacent to the non-light- receiving side of the solar cell layer.
  • this encapsulant layer also has a light-receiving side which is the part of the layer facing the non-light-receiving side of the solar cells and a non-light- receiving side, which is the part opposite to its light-receiving part.
  • the backsheet is laminated to the non-light-receiving part of the encapsulant layer (or part thereof) facing the non light-receiving side of the solar cells.
  • the topsheet described above is laminated to the encapsulant layer.
  • This encapsulant layer may comprise any suitable polymeric material.
  • suitable polymeric materials include acid copolymers, ionomers, poly(ethylene vinyl acetates), polyvinyl acetals), polyurethanes, polyvinyl chlorides), polyethylenes (e.g., linear low density polyethylenes), polyolefin block elastomers, copolymers of an ⁇ -olefin and an ⁇ , ⁇ -ethylenically unsaturated carboxylic acid ester (e.g., ethylene methyl acrylate copolymer and ethylene butyl acrylate copolymer), silicone elastomers, epoxy resins, and combinations of two or more thereof.
  • the encapsulant layer comprises poly(ethylene vinyl acetates)(EVA).
  • the solar cell module may further comprise an incident layer serving as the outermost layer(s) of the module at the light-receiving side.
  • the outermost layers may be formed of any suitable transparent sheets or films. Suitable sheets may be glass or plastic sheets, such as
  • polycarbonates acrylic polymers (i.e., thermoplastic polymers or copolymers of acrylic acid, methacrylic acid, esters of these acids, or acrylonitrile), polyacrylates, cyclic polyolefins (e.g., ethylene norbornene polymers), polystyrenes (preferably metallocene-catalyzed polystyrenes), polyamides, polyesters, fluoropolymers, or combinations of two or more thereof.
  • the outmost layers are made of glass.
  • glass includes not only window glass, plate glass, silicate glass, sheet glass, low iron glass, tempered glass, tempered CeO-free glass, and float glass, but also colored glass, specialty glass (such as those types of glass containing ingredients to control solar heating), coated glass (such as those sputtered with metals (e.g., silver or indium tin oxide) for solar control purposes), E-glass, Toroglass, SOLEX glass (PPG Industries, Pittsburgh, Pa, USA.) and STARPHIRE glass (PPG Industries). It is understood, however, that the type of glass to be selected for a particular module depends on the intended use.
  • the solar cell module may further comprise other functional film or sheet layers (e.g., dielectric layers or barrier layers) embedded within the module, although this may not be required.
  • functional layers may comprise polymeric films that are coated with additional functional coatings.
  • poly(ethylene terephthalate) films coated with a metal oxide coating may function as additional oxygen and moisture barrier layers in the modules but are not required.
  • the solar module or the backsheet do not contain such a barrier film.
  • a layer of nonwoven glass fiber may also be included between the solar cell layers and the encapsulant layers to facilitate deaeration during the lamination process or to serve as reinforcement for the encapsulants.
  • a surface of the encapsulant layer may be treated prior to the lamination process to incorporate the backsheet to enhance the adhesion of the backsheet to the encapsulant layer.
  • This adhesion enhancing treatment may take any form known within the art and may include flame treatments, plasma treatments, electron beam treatments, oxidation treatments, corona discharge treatments, chemical treatments, chromic acid treatments, hot air treatments, ozone treatments, ultraviolet light treatments, sand blast treatments, solvent treatments, and combinations of two or more thereof.
  • flame treatments plasma treatments, electron beam treatments, oxidation treatments, corona discharge treatments, chemical treatments, chromic acid treatments, hot air treatments, ozone treatments, ultraviolet light treatments, sand blast treatments, solvent treatments, and combinations of two or more thereof.
  • it is an advantage of the backsheets provided herein that they can be satisfyingly bonded to the encapsulant layer, in particular when the encapsulant layer contains EVA, by lamination, in particular vacuum lamination.
  • Solar modules may be prepared by stacking the component layers of the solar cell module in a desired order to form a pre-lamination assembly.
  • the assembly may then placed into a bag capable of sustaining a vacuum ("a vacuum bag"), the air is drawn out of the bag by a vacuum line or other means, the bag is sealed while the vacuum is maintained and the sealed bag is placed in an autoclave at a pressure and temperature sufficient to provide lamination.
  • a vacuum ring may be substituted for the vacuum bag.
  • the air in the autoclave may be cooled without introducing additional gas to maintain pressure in the autoclave. The excess air pressure is vented and the laminates are removed from the autoclave.
  • the pre-lamination assembly may be heated in an oven after which the heated assembly is passed through a set of nip rolls so that the air in the void spaces between the individual layers may be squeezed out, and the edge of the assembly sealed.
  • the assembly at this stage is referred to as a pre-press.
  • the pre-press may then be placed in an air autoclave subjected to an appropriate temperature and pressure regime to achieve laminated products.
  • the solar cell modules may also be produced through non-autoclave processes.
  • the non-autoclave processes include heating the pre-lamination assembly and the application of vacuum, pressure or both.
  • the assembly may be successively passed through heating ovens and nip rolls.
  • the edges of the solar cell module may be sealed.
  • Suitable materials useful in sealing the solar cell module edges include, but are not limited to, butyl rubber, polysulfide, silicone, polyurethane, polypropylene elastomers, polystyrene elastomers, block elastomers, styrene- ethylene-butylene-styrene (SEBS), and the like. It is another advantage of the backsheets provided herein that they are compatible with the sealants described above and can thus provide good sealing of the interface of the backsheet and encapsulant layer of the solar module.
  • Multi-layered backsheet for solar modules comprising in this order
  • each layer there may or may not be one or more sublayers,
  • the top layer (i), the insulating layer (ii) and the back layer (iii) contain a polyolefin as the major component, wherein the polyolefin is selected from polyethene homo- and copolymers (PE's) and polypropene homo- and copolymers (PP's).
  • the insulating layer (ii) has a thickness of at least 210 or at least 310 ⁇ .
  • the backsheet of 1 wherein at least the layers (ii) and (iii) and preferably also layer (i) contain independently from each other as the major component a polyethene.
  • the backsheet of any one of 1 to 3 having a dielectric breakdown voltage of at least 20 kV. 5.
  • the backsheet of any one of 1 to 4 having a thickness of at least 0.25 and up to 0.7 mm.
  • a solar module comprising one or more solar cells and one or more encapsulating layer and further comprising a backsheet according to any one of 1 to 16.
  • the solar module of 17 being a crystalline solar module.
  • each layer there may or may not be one or more sublayers,
  • the insulating layer (ii) and the back layer (iii) contains a polyolefin selected from cross- linked polyethene homo- and copolymers (PE's) as the major component wherein the PE copolymers are selected from
  • PE copolymers comprising more than 99% by mole of repeating units derived from ethene and
  • PE copolymers comprising at least 50% preferably at least 60%, more preferably at least 80 % and most preferably at least 95% by mole of repeating units derived from ethene and further comprising one or more comonomers selected from alkenes, in particular a-olefins.
  • layer (i) contains a polyolefin selected from cross-linked polyethene homo- and copolymers (PE's) as the major component and wherein the comonomers are as defined in 20.
  • PE's cross-linked polyethene homo- and copolymers
  • the backsheet of any one of 20 to 24 having a thickness of at least 0.25 and up to 0.7 mm.
  • the backsheet of any one of 20 to 36 having a reduction of dielectric break down voltage of less than 1 %.
  • the backsheet of any one of 20 to 38 having a reduction in tensile strength of less than 20% after being exposed to water steam at a temperature of 121 °C and a pressure of 1 bar for 100 hours.
  • the backsheet of any one of 20 to 39 having a reduction in elongation at break and tensile strength of less than 20% after being exposed to water steam at a temperature of 121 °C and a pressure of 1 bar for 100 hours.
  • the backsheet of any one of 20 to 40 having a reduction in elongation at break and tensile strength of less than 20% after being exposed to water steam at a temperature of 121 °C and a pressure of 1 bar for 100 hours and a having a reduction of dielectric break down voltage of less than 1 %.
  • fluoropolymers polyesters, polyamides, polyacetates. 43.
  • Multi-layered backsheet for solar modules comprising in this order
  • each layer there may or may not be one or more sublayers,
  • the insulating layer (ii) and the back layer (iii) contain a polyolefin as the major component, wherein the polyolefin is selected from cross-linked polypropene homo- and copolymers (PP's), wherein the PP-copolymers are selected from
  • PP copolymers comprising at least 50%, preferably at least 60%, more preferably at least 80 %, and most preferably at least 95%, by mole of repeating units derived from propene, and further comprising one or more comonomers selected from alkenes, in particular, a-olefins.
  • PP's cross-linked polypropene homo- and copolymers
  • the backsheet of any one of 53 to 56 having a thickness of at least 0.25 and up to 0.7 mm.
  • the backsheet of any one of 53 to 69 having a reduction in elongation at break of less than 20% after being exposed to water steam at a temperature of 121 °C and a pressure of 1 bar for 100 hours.
  • 71 The backsheet of any one of 53 to 70 having a reduction in tensile strength of less than 20% after being exposed to water steam at a temperature of 121 °C and a pressure of 1 bar for 100 hours.
  • the backsheet of any one of 53 to 71 having a reduction in elongation at break and tensile strength of less than 20% after being exposed to water steam at a temperature of 121 °C and a pressure of 1 bar for 100 hours.
  • the backsheet of any one of 53 to 72 having a reduction in elongation at break and tensile strength of less than 20% after being exposed to water steam at a temperature of 121 °C and a pressure of 1 bar for 100 hours and a having a reduction of dielectric break down voltage of less than 1 %.
  • fluoropolymers polyesters, polyamides, polyacetates.
  • the layer (i) of the backsheet contains white pigments and UV stabilisers, preferably UV stabilisers based on cyclic amines.
  • each layer there may or may not be one or more sublayers,
  • the insulating layer (ii) and the top layer (i) contain a polyolefin selected from cross- linked polyethene homo- and copolymers (PE's) as the major component wherein the PE copolymers are selected from
  • PE copolymers comprising more than 99% by mole of repeating units derived from ethene and
  • PE copolymers comprising at least 50% preferably at least 60%, more preferably at least 80 % and most preferably at least 95% by mole of repeating units derived from ethene and further comprising one or more comonomers selected from alkenes, in particular, a-olefins.
  • PE's cross-linked polyethene homo- and copolymers
  • the backsheet of any one of 85 to 89 having a thickness of at least 0.25 and up to 0.7 mm. 91 .
  • the backsheet according to any one of 85 to 99 wherein the layers (i), (ii,) or (iii) or the layers (i) and (ii), or the layers (i) and (iii), or the layers (ii) and (iii) or the layers (i), (ii) and (iii) contain flame retardants.
  • the backsheet of any one of 85 to 101 having a reduction of dielectric break down voltage of less than 1 %.
  • the backsheet of any one of 85 to 102 having a reduction in elongation at break of less than 20% after being exposed to water steam at a temperature of 121 °C and a pressure of 1 bar for 100 hours.
  • the backsheet of any one of 85 to 103 having a reduction in tensile strength of less than 20% after being exposed to water steam at a temperature of 121 °C and a pressure of 1 bar for 100 hours.
  • the backsheet of any one of 85 to 104 having a reduction in elongation at break and tensile strength of less than 20% after being exposed to water steam at a temperature of 121 °C and a pressure of 1 bar for 100 hours.
  • fluoropolymers polyesters, polyamides, polyacetates.
  • a solar module comprising one or more solar cells and one or more encapsulating layer and further comprising a backsheet according to any one of 1 to 19, 20 to 52 or 53 to 84 or 85 to 1 17.
  • the solar module of 1 18 being a crystalline solar module.
  • a method of making a backsheet according to any one of 1 to 1 17 said method comprising providing compositions for making layers (i), (ii) and (iii)
  • a method of making a backsheet according to any one of 1 to 1 17 said method comprising a) providing layers (i), (ii) and (iii),
  • HALS Hostavin N30 stencally hindered amine light stabiliser (HALS), UV stabilizer,
  • Polybatch UV 1952 stabilizer masterbatch containing 10 % wt. of a hindered amine light stabilizer, A.Schulman GmbH, Kerpen, Germany.
  • Polywhite NG 8270 W white masterbatch containing 60% wt. titanium dioxide (rutile) in polyethylene, A.Schulman GmbH, Kerpen, Germany.
  • Polyblack 1423 black masterbatch, containing 40% wt. carbon black in
  • a three layer polyethylene backsheet was prepared by first preparing the compositions for the individual layers.
  • the top layer composition (layer (i)) was prepared by blending 2,000 g of Polywhite NG 8270 W with 7,500 g of Hostalen HD 9550 F and with 500 g of Polybatch UV 1952 in a tumble mixer at room temperature.
  • composition for the back layer was prepared by blending 1 ,000 g of Polyblack 1423 with 8,500 g Hostalen HD 9550 F and with 500 g of Polybatch UV 1952 in a tumble mixer at room temperature.
  • the composition of the middle layer (layer (ii) was prepared by blending 9,500 g Lupolen 3020K with 500 g of Polybatch UV 1952 in a tumble mixer at room temperature.
  • the white (solar facing) layer (i) was metered by a KTron Gravimetric Feeder, commercially available from KTron, Germany, into a twin screw extruder, commercially available from Werner & Pfleiderer, Germany, with a screw diameter of 25 mm and a length of 45 times the screw diameter.
  • the middle layer (ii) was melted with a single screw extruder commercially available from Chang Maschinenbau, Germany with a screw diameter of 45 mm and a length of 30 times the screw diameter.
  • the black (backside facing) layer (iii) was melted with a single screw extruder commercially available from Extrudex, USA with a screw diameter of 30 mm and a length of 30 times the screw diameter.
  • the melt stream was fed through a slot die, commercially available from EDI.
  • the coextruded examples were made while casting from a slot die directly between a chilled stainless steel roll and a rubber roll without significant draw. The cooled layers were wound into a roll.
  • the three-layer product was subjected to e-beam radiation to cross-link the material using an e-beam unit commercially available from Polymer Physics, using 295 kV with a beam current of 4 mA at a line speed of 3m/min and beam width of 30 cm. The samples were treated 4 times. A 50 cm x 20 cm wide sample was cut from the sheet for further testing.
  • C1 A backsheet containing polyamide layers (lcosolar AAA 3554, Isovolta AG, Wiener Neudorf, Austria);
  • a backsheet comprising a PET/PET/EVA composition (DYMAT PYE, Coveme, San Lazzaro di Savena, Italy);
  • a backsheet containing a PVF/PET/PVF composition (lcosolar 2442, Isolvolta AG);
  • C4 A backsheet containing a PVF/PET/PVF composition (AKASOL PTL 3HR 700V, Krempel, Vaihingen/Enz, Germany).
  • the materials were subjected to a pressure cooker test DIN EN 60749-33 to test their hydrolytic stability and ageing properties. Test conditions were cooking the materials at 121 °C at 1 bar pressure for 100 hours in presence of steam. Test was done with tap water. Test samples were placed on an aluminium tray which was placed above the water reservoir generating the steam. The mechanical and electrical properties of the materials were tested before and after the pressure cooker test.
  • the dielectric breakdown voltage was determined according to ASTM D149, method A. The tests were carried on with type 2 electrodes and a voltage rate-of-rise of 500V/sec in a
  • Hypotronics Type 970 dielectric breakdown strength tester The tests were done in oil. The tensile strength and elongation at break were determined according to ASTM D-882 on a tensile tester, commercially available from Zwick, Germany with a 500 N load cell and a test speed of 100 mm/min. The mechanical properties of the materials before the pressure cooker test were as indicated in table 1 and compared with the properties after the pressure cooker test as indicated in table 2. Table 2 also indicates the degree of deterioration (expressed as reduction in %) of the property before and after the test.
  • Table 2 properties after pressure cooker test and degree of deterioration (reduction in original properties).
  • Example 1 was repeated but using various amounts of flame retardant (Polybatch PR 1049 DC).
  • the flame retardant was added to layer (ii) by 15 % by weight.
  • the resulting backsheet had a break down voltage of 23.18 kV.
  • the flame retardant was added to layer (ii) by 30% by weight.
  • the resulting backsheet had a break down voltage of 23.64 kV.
  • example 4 was repeated by also adding the flame retardant by 30% by weight to layer (iii).
  • the resulting backsheet had a breakdown voltage of 24.80 kV.
  • a three layer backsheet was prepared as described in example 1 with the following differences: layer (i): 250 g HOSTAVIN N30 masterbatch (20% wt of HOSTAVIN N30) were used instead of POLYBATCH UV 1952. The amount of Hostalen used was 7,750 g.
  • HOSTAVIN N30 masterbatch 250 g HOSTAVIN N30 masterbatch were used instead of POLYBATCH UV 1952.
  • the amount of HOSTALEN was 9,250 g.
  • the backsheet was subjected to a damp heat test and placed into a humidity chamber at 80% r.h. and 85 °C for 2,000 hours and tested for colour degradation of the white front side by determining the Yellowness index according to ASTM E313-1 . The index increased moderately from -5.8 to -3.2 after 2,000h treatment.
  • the backsheet of example 5 was subjected to a cycled UV- exposure.
  • the backside (layer (iii)) was irradiated with UV light (340 nm), 1.3 W/m 2 nm for 12 hour interval at 75°C, then the UV irradiation was stopped for 4 hours.
  • the cycle was repeated for the time intervals indicated below.
  • the dielectric breakdown, tensile strength and elongation at break of the backsheet material were determined as described above.
  • the electric breakdown voltage remained between 23 and 24 kV after exposure for 500 h, 1 ,000 h and 1 ,500 h.
  • the breakdown voltage slightly increased to values 25 and 27 kV after exposure for 2,000 h and 3,000 h, respectively.
  • Example 7 and comparative example C7 The elongation at break remained between 330% and 350% after exposure to 500 h, 1000 h, 2000 h and 3000 h. The yield strength (tensile) decreased from 28 MPa to 27 MPa after exposure of 3000h.
  • Example 7 and comparative example C7
  • the backsheet of example 5 was subjected to oven storage at various temperatures.
  • the yield strength (tensile) of the backsheet was determined at various time intervals (437 and 1 175 hours, and compared to the initial value and the reduction of the initial value was calculated (example 7).
  • the test was repeated with Melinex D 243 from DuPont Teijin, Germany,
  • the tensile strength of the backsheet according to example 7 was reduced by less than 10%.
  • the tensile strength of C7 was reduced by about 20%.
  • Example 8 theoretical example for making a PP backsheet:
  • a three layer polypropene backsheet may be prepared by first preparing the compositions for the individual layers.
  • the top layer composition (layer (i)) may be prepared by blending 2,000 g of Polypropene masterbatch containing 10% white pigments, 7,500 g polypropene and with 500 g of PP masterbatch comprising 10% wt of UV stabiliser (HALS) in a tumble mixer at room temperature.
  • HALS UV stabiliser
  • composition for the back layer (layer iii)) can be prepared by blending 1 ,000 g of a PP masterbatch containing 10% carbon black with 8,500 g propylene and with 500 g of a PP masterbatch containing 10% UV stabiliser (HALS) in a tumble mixer at room temperature.
  • HALS UV stabiliser
  • composition of the middle layer (layer (ii) may be prepared by blending 9,500 g
  • polypropene with 500 g of PP masterbatch containing 10% UV stabiliser (HALS) in a tumble mixer at room temperature.
  • HALS UV stabiliser
  • the white (solar facing) layer (i) may be metered by a KTron Gravimetric Feeder, commercially available from KTron, Germany, into a twin screw extruder, commercially available from Werner & Pfleiderer, Germany, with a screw diameter of 25 mm and a length of 45 times the screw diameter.
  • the middle layer (ii) may be metered with a single screw extruder commercially available from Chang Maschinenbau, Germany with a screw diameter of 45 mm and a length of 30 times the screw diameter.
  • the black (backside facing) layer (iii) may be metered with a single screw extruder commercially available from Extrudex, USA with a screw diameter of 30 mm and a length of 30 times the screw diameter.
  • All 3 extruders may fed the polymers into a Cloeren 3-layer-feed block to feed the molten stream into the positions i-ii-iii in the final melt stream.
  • the melt stream may be fed through a slot die, commercially available from EDI.
  • the coextruded examples may be made while casting from a slot die directly onto a chilled stainless steel roll without significant draw.
  • the cooled layers may be wound into a roll.
  • the three-layer product may be subjected to e-beam radiation to cross-link the material using an e-beam unit commercially available from Polymer Physics, using a treatment as described above.
  • Example 9
  • a two layer polyethylene backsheet was prepared by first preparing the compositions for the individual layers.
  • the top layer composition (layer (i)) was prepared by blending 2,000 g of Polywhite NG 8270 W with 7,500 g of Hostalen HD 9550 F and with 500 g of Polybatch UV 1952 in a tumble mixer at room temperature.
  • composition for the back layer was prepared by blending 1 ,000 g of Polyblack 1423 with 8,500 g Hostalen HD 9550 F and with 500 g of Polybatch UV 1952 in a tumble mixer at room temperature.
  • the white (solar facing) layer (i) was metered by a KTron Gravimetric Feeder, commercially available from KTron, Germany, into a twin screw extruder, commercially available from Werner & Pfleiderer, Germany, with a screw diameter of 25 mm and a length of 45 times the screw diameter.
  • the black (backside facing) layer (iii) was melted with a single screw extruder commercially available from Extrudex, USA with a screw diameter of 30 mm and a length of 30 times the screw diameter.
  • Both extruders fed the polymers into a Cloeren 3-layer-feed block to feed the molten stream into the positions i-ii-iii in the final melt stream.
  • the melt stream was fed through a slot die, commercially available from EDI.
  • the coextruded examples were made while casting from a slot die directly between a chilled stainless steel roll and a rubber roll without significant draw. The cooled layers were wound into a roll.
  • the three-layer product was subjected to e-beam radiation to cross-link the material using an e-beam unit commercially available from Polymer Physics, using 295 kV with a beam current of 4 mA at a line speed of 3m/min and beam width of 30 cm. The samples were treated 4 times.
  • the sample was tested for Yellowing Index.
  • the top layer (i) showed initial yellowing of (-0.8).
  • After 36 h at 125°C the white side showed a yellowing index of 13.

Landscapes

  • Laminated Bodies (AREA)
  • Photovoltaic Devices (AREA)
PCT/US2011/047863 2010-08-16 2011-08-16 Polyolefin-based solar backsheet Ceased WO2012024262A1 (en)

Priority Applications (4)

Application Number Priority Date Filing Date Title
CN2011800394703A CN103068575A (zh) 2010-08-16 2011-08-16 基于聚烯烃的太阳能背板
KR1020137006390A KR20130097185A (ko) 2010-08-16 2011-08-16 폴리올레핀-기반의 태양광 백시트
US13/814,856 US20130133726A1 (en) 2010-08-16 2011-08-16 Polyolefin-Based Solar Backsheet
JP2013524923A JP2013535365A (ja) 2010-08-16 2011-08-16 ポリオレフィンに基づくソーラーバックシート

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP20100172956 EP2390093B1 (en) 2010-08-16 2010-08-16 Polyolefin-based solar backsheet
EP10172956.4 2010-08-16

Publications (1)

Publication Number Publication Date
WO2012024262A1 true WO2012024262A1 (en) 2012-02-23

Family

ID=43466850

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2011/047863 Ceased WO2012024262A1 (en) 2010-08-16 2011-08-16 Polyolefin-based solar backsheet

Country Status (7)

Country Link
US (1) US20130133726A1 (enExample)
EP (2) EP2617568A1 (enExample)
JP (1) JP2013535365A (enExample)
KR (1) KR20130097185A (enExample)
CN (1) CN103068575A (enExample)
TW (1) TW201213126A (enExample)
WO (1) WO2012024262A1 (enExample)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102642364A (zh) * 2012-04-24 2012-08-22 云南云天化股份有限公司 一种太阳能电池背板及其生产方法
CN102832282A (zh) * 2012-08-31 2012-12-19 苏州中来光伏新材股份有限公司 一种玻纤基降冰片烯共聚物改性太阳电池背膜及其加工工艺
US9276151B2 (en) 2011-11-04 2016-03-01 3M Innovative Properties Company Polyolefin adhesive material for use in solar modules
US9379263B2 (en) 2011-11-04 2016-06-28 3M Innovative Properties Company Durable polyolefin adhesive material for solar modules
US12433039B2 (en) 2019-11-22 2025-09-30 Endurance Solar Solutions Inc. Photovoltaic module backsheet comprising polyolefin layers

Families Citing this family (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2517258A4 (en) * 2009-12-23 2014-11-26 Madico Inc HIGH-PERFORMANCE BACK-UP FOIL FOR PHOTOVOLTAIC APPLICATIONS AND METHOD FOR THE PRODUCTION THEREOF
EP2572877A3 (en) * 2011-09-20 2013-05-29 RENOLIT Belgium N.V. Photovoltaic modules comprising a backsheet and electrical insulating layer(s) which are highly permeable to corrosive degradation by-products
DE102012100184B4 (de) * 2012-01-11 2015-03-12 Hanwha Q.CELLS GmbH Verfahren zur Herstellung einer Halbleiterwafer-Solarzelle und eines Solarmoduls
CN102569469A (zh) * 2012-03-26 2012-07-11 深圳市金恒晟科技有限公司 一种新型太阳能背板
WO2014128581A1 (en) * 2013-02-25 2014-08-28 Sabic Innovative Plastics Ip B.V. Photovoltaic module assembly
JPWO2015045673A1 (ja) * 2013-09-25 2017-03-09 パナソニックＩｐマネジメント株式会社 太陽電池モジュールの製造方法
AT14193U1 (de) * 2013-10-22 2015-05-15 Isovoltaic Ag Verbundfolie für ein Photovoltaikmodul
CN104842620A (zh) * 2014-02-18 2015-08-19 常州百佳薄膜科技有限公司 一种耐析出无卤阻燃聚丙烯流延片材及其制备方法
ES2745557T3 (es) 2014-03-07 2020-03-02 Saudi Basic Ind Corp Cubierta de tejado modular
NL2012989B1 (en) 2014-06-12 2016-07-04 Olympic Holding B V Photovoltaic panels.
DE102015103045A1 (de) 2015-03-03 2016-09-08 Bischof + Klein Gmbh & Co. Kg Rückseitenfolie für Solarmodule
WO2016157041A2 (en) * 2015-03-27 2016-10-06 Tata Power Solar Systems Limited Dielectric coating formulation for metal integrated solar panel
EP3139417A1 (en) 2015-09-03 2017-03-08 Borealis AG Polyethylene composition for a layer element of a photovoltaic module
CN105882094B (zh) * 2016-04-06 2018-02-16 广东东立新材料科技有限公司 太阳能板耐高温抗紫外线自粘膜
CN105895722B (zh) * 2016-05-25 2018-01-23 苏州固泰新材股份有限公司 单面磨砂高反射太阳能背板用pvdf薄膜及制备方法
DE102016009020A1 (de) 2016-07-23 2018-01-25 Aluminium Féron GmbH & Co. KG Mehrschichtige Rückseitenfolie für Solarmodule, Solarmodul sowie Verfahren zur Herstellung der Folie und des Moduls
WO2018061036A1 (en) * 2016-10-02 2018-04-05 Roshan Shah A backsheet for a photovoltaic module
CN108075006A (zh) * 2016-11-15 2018-05-25 上海海优威新材料股份有限公司 多层结构的太阳能电池背板
US20180313079A1 (en) * 2017-04-26 2018-11-01 Robert D. Russell Multi-Layered Metalized Film For Use In Agriculture
WO2019201646A1 (en) 2018-04-16 2019-10-24 Borealis Ag A process for producing a multilayer laminate
FR3086461B1 (fr) 2018-09-22 2023-10-27 Total Sa Laminat de cellules photovoltaiques et procede de fabrication associe
FR3098994A1 (fr) 2019-07-17 2021-01-22 Total Sa Laminât de cellules photovoltaïques et procédé de fabrication associé
CN112928176B (zh) * 2021-02-08 2023-02-28 浙江中聚材料有限公司 一种三层共挤无胶透明太阳能光伏背板及其制备工艺
WO2022221874A1 (en) 2021-04-15 2022-10-20 H.B. Fuller Company Hot melt composition in the form of a film for use in thin film photovoltaic modules
EP4348719A4 (en) * 2021-05-28 2025-02-26 Dow Global Technologies LLC REFLECTIVE GRID FOR PHOTOVOLTAIC MODULE FILM AND METHOD
US12074237B2 (en) * 2022-05-16 2024-08-27 Maxeon Solar Pte. Ltd. Photovoltaic laminate comprising single polymer composite
DE102022123726A1 (de) 2022-09-16 2024-03-21 Rkw Se Rückseitenfolie auf Polyolefinbasis für Photovoltaikmodule

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1999004971A2 (en) * 1997-07-24 1999-02-04 Evergreen Solar, Inc. Encapsulant material for solar cell module and laminated glass applications
JP2004223925A (ja) * 2003-01-23 2004-08-12 Mitsubishi Plastics Ind Ltd 積層シート、太陽電池用裏面保護シート、並びに太陽電池及び太陽電池モジュール
EP1898470A1 (en) * 2006-08-30 2008-03-12 Keiwa Inc. Back sheet for photovoltaic modules and photovoltaic module using the same
US20080078445A1 (en) * 2006-09-20 2008-04-03 Patel Rajen M Electronic Device Module Comprising Polyolefin Copolymer
US20100108128A1 (en) * 2008-11-06 2010-05-06 Lih-Long Chu Co-Extruded, Multilayered Polyolefin-Based Backsheet for Electronic Device Modules

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2147684A1 (de) * 1971-09-24 1973-03-29 Licentia Gmbh Verfahren zur erhoehung der elektrischen festigkeit von polymeren (polyaethylen)
DE10393252T5 (de) * 2002-09-06 2005-09-08 Dai Nippon Printing Co., Ltd. Rückseitenschutzschicht für ein Solarzellenmodul und Solarzellenmodul unter Verwendung derselben
US20060057392A1 (en) * 2003-10-07 2006-03-16 Smillie Benjamin A Multi-layer sheet having a weatherable surface layer
TWI335269B (en) * 2005-11-25 2011-01-01 Mitsui Chemicals Inc Composite sheet and use thereof
JP2007150084A (ja) * 2005-11-29 2007-06-14 Dainippon Printing Co Ltd 太陽電池モジュール用裏面保護シート、太陽電池モジュール用裏面積層体、および、太陽電池モジュール
JP4783865B2 (ja) * 2008-10-30 2011-09-28 三井・デュポンポリケミカル株式会社 多層シート、太陽電池素子用封止材、及び太陽電池モジュール
FR2941887B1 (fr) * 2009-02-06 2011-03-25 Arkema France Utilisation d'un film a base de polyolefine dans un module photovoltaique
JP2013504205A (ja) * 2009-09-01 2013-02-04 ダウ グローバル テクノロジーズ エルエルシー リジッドな光起電力モジュール用のバックシート

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1999004971A2 (en) * 1997-07-24 1999-02-04 Evergreen Solar, Inc. Encapsulant material for solar cell module and laminated glass applications
JP2004223925A (ja) * 2003-01-23 2004-08-12 Mitsubishi Plastics Ind Ltd 積層シート、太陽電池用裏面保護シート、並びに太陽電池及び太陽電池モジュール
EP1898470A1 (en) * 2006-08-30 2008-03-12 Keiwa Inc. Back sheet for photovoltaic modules and photovoltaic module using the same
US20080078445A1 (en) * 2006-09-20 2008-04-03 Patel Rajen M Electronic Device Module Comprising Polyolefin Copolymer
US20100108128A1 (en) * 2008-11-06 2010-05-06 Lih-Long Chu Co-Extruded, Multilayered Polyolefin-Based Backsheet for Electronic Device Modules

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9276151B2 (en) 2011-11-04 2016-03-01 3M Innovative Properties Company Polyolefin adhesive material for use in solar modules
US9379263B2 (en) 2011-11-04 2016-06-28 3M Innovative Properties Company Durable polyolefin adhesive material for solar modules
US9837569B2 (en) 2011-11-04 2017-12-05 3M Innovative Properties Company Polyolefin adhesive material for use in solar modules
CN102642364A (zh) * 2012-04-24 2012-08-22 云南云天化股份有限公司 一种太阳能电池背板及其生产方法
CN102832282A (zh) * 2012-08-31 2012-12-19 苏州中来光伏新材股份有限公司 一种玻纤基降冰片烯共聚物改性太阳电池背膜及其加工工艺
US12433039B2 (en) 2019-11-22 2025-09-30 Endurance Solar Solutions Inc. Photovoltaic module backsheet comprising polyolefin layers

Also Published As

Publication number Publication date
TW201213126A (en) 2012-04-01
CN103068575A (zh) 2013-04-24
EP2390093B1 (en) 2013-04-17
EP2390093A1 (en) 2011-11-30
KR20130097185A (ko) 2013-09-02
EP2617568A1 (en) 2013-07-24
JP2013535365A (ja) 2013-09-12
US20130133726A1 (en) 2013-05-30

Similar Documents

Publication Publication Date Title
US20130133726A1 (en) Polyolefin-Based Solar Backsheet
EP2346686B1 (en) Co-extruded, multilayered polyolefin-based backsheet for electronic device modules
JP5300743B2 (ja) 高メルトフローアイオノマー組成物を含む物品
EP2473345B1 (en) Backsheet for rigid photovoltaic modules
CN101983433B (zh) 包含高熔体流动速率的聚(乙烯醇缩丁醛)包封材料的太阳能电池模块
EP2599626A1 (en) Solar modules containing a backsheet with a polyolefin bonding layer
CN102272221A (zh) 包括乙烯共聚物共混物包封片材的太阳能电池模块
KR102030357B1 (ko) 열가소성 폴리올레핀 코폴리머 라미네이션 필름, 라미네이트 구조물 및 그의 제조방법
KR20130047696A (ko) 태양 전지용 백시트 및 태양 전지 모듈
KR101954164B1 (ko) 태양전지용 백 시트
JP2010278428A (ja) 太陽電池用シート及び太陽電池モジュール
EP2600425A1 (en) Solar modules containing a single-layer polyolefin-based backsheet
EP2600424A1 (en) Solar modules containing a backsheet with a polyolefin bonding layer
WO2013077874A1 (en) Integrated films for use in solar modules
US20230203288A1 (en) Multilayer assembly comprising silane-grafted polyolefin
KR101955622B1 (ko) 태양전지용 백 시트
WO2015168174A1 (en) Protective sheet for a photovoltaic module
WO2019076913A1 (en) ELECTROCONDUCTIVE BACK SHEET FOR SOLAR CELL MODULES

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201180039470.3

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11745911

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 13814856

Country of ref document: US

ENP Entry into the national phase

Ref document number: 2013524923

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20137006390

Country of ref document: KR

Kind code of ref document: A

122 Ep: pct application non-entry in european phase