WO2011132147A1 - Novel metal-organic frameworks as electrode material for lithium ion accumulators - Google Patents
Novel metal-organic frameworks as electrode material for lithium ion accumulators Download PDFInfo
- Publication number
- WO2011132147A1 WO2011132147A1 PCT/IB2011/051696 IB2011051696W WO2011132147A1 WO 2011132147 A1 WO2011132147 A1 WO 2011132147A1 IB 2011051696 W IB2011051696 W IB 2011051696W WO 2011132147 A1 WO2011132147 A1 WO 2011132147A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- electrode material
- metal
- lithium ion
- lithium
- porous metal
- Prior art date
Abstract
Description
Claims