WO2011092401A2 - Procede de realisation d'une cellule photovoltaique avec preparation de surface d'un substrat en silicium cristallin - Google Patents
Procede de realisation d'une cellule photovoltaique avec preparation de surface d'un substrat en silicium cristallin Download PDFInfo
- Publication number
- WO2011092401A2 WO2011092401A2 PCT/FR2011/000049 FR2011000049W WO2011092401A2 WO 2011092401 A2 WO2011092401 A2 WO 2011092401A2 FR 2011000049 W FR2011000049 W FR 2011000049W WO 2011092401 A2 WO2011092401 A2 WO 2011092401A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- substrate
- silicon oxide
- layer
- thin film
- silicon
- Prior art date
Abstract
Description
Claims