WO2010088327A2 - Catalyst for producing ammonia from hydrocarbon and nitrogen oxides - Google Patents
Catalyst for producing ammonia from hydrocarbon and nitrogen oxides Download PDFInfo
- Publication number
- WO2010088327A2 WO2010088327A2 PCT/US2010/022316 US2010022316W WO2010088327A2 WO 2010088327 A2 WO2010088327 A2 WO 2010088327A2 US 2010022316 W US2010022316 W US 2010022316W WO 2010088327 A2 WO2010088327 A2 WO 2010088327A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- catalyst
- silver
- hydrocarbon
- ammonia
- alumina
- Prior art date
Abstract
Description
Claims